By R. G. Davies, P. Beardmore, T. L. Johnston

The flow stress of a series of Ni-Cr-A1 alloys consisting of a dispersion of y' (based on Ni3Al) in a rnatrix of nickel-base solid solution y has been measured at temperatures up to 950°C as a fwzction of the volume fraction of y'. At high temperatures the flow stress is controlled by the amount of Y' in the alloy, i.e., the higher the volume fraction of y', the greater is the flow stress. This simple relationship is not obeyed at low temperatures in so far as a peak in the flow stress-volume fraction relation occurs at about 25 pct y'. The variation in the mechanical properlies of these alloys as a function of both temperature and volume fraction of y' has been correlated with changes in distribution of both the dislocations and y'. The results are interpreted on the basis that at low temperatures the y matrix is strengthened significantly bv the presence of a hyperfine y' precipitate due to decomposition on cooling; at high temperatures the y matrix is a single phase of low strength. It is clearly recognized that the high temperature strength of most nickel-base superalloys depends upon a dispersion of the ordered fcc phase y', based on Ni3A1, in a fcc solid solution matrix y based on nickel. Although the volume fraction of y' varies widely from about 0.2 in Nimonic 80A to about 0.6 in Mar-M200, all such nickel-base alloys manifest an unusual insensi-tivity of the flow stress with respect to temperature. In Mar-M200 for example, the 0.2 pct flow stress remains essentially constant from room temperature to 750°C. The conclusion has been drawn1 that the characteristically low temperature dependence of the flow stress of y-y' nickel-base alloys is obtained when the state of dispersion of y' is such that dislocations are forced to cut through the y' particles at the onset of yielding. When the spacing between the y' particles is so large that the flow stress is controlled by dislocation bowing between particles, then the initial flow stress decreases progressively with an increase in temperature at a rate determined by changes in elastic properties. The same conclusion is inherent in the detailed, mechanistic model of the deformation process in commercial superalloys which has been developed by Copley and ear' in which the temperature independent flow stress is attributed primarily to the contribution of the antiphase boundary energy created in the y' particles during deformation. In this theory the temperature insensitivity of the flow stress is a reflection of the constant antiphase boundary energy as a function of temperature. An important microstructural parameter that is relevant to the explanations that have been suggested' to account for the temperature insensitivity of the flow stress is the volume fraction of y'. To vary the latter to any significant extent in a given commercial alloy is clearly difficult. However, it is possible in a relatively simple Ni-Al-Cr ternary system which manifests analogous microstructures in terms of the distribution of y' in y and contains specific alloys which have flow properties that depend on temperature in a manner quite similar to their more complex commercial counterparts. Hornbogen et . have studied precipitation phenomena and deformation mechanisms in such alloys but only where the y' volume fraction was small (less than 0.2) and the y' particle size varied from less than 100A up to a maximum of -1000A. In the present study, a series of alloys was prepared in which the volume percent of y' at 900°C was varied from 0 to 100 pct with the y' particle size (of the order 0.5 p) comparable to the sizes obtained in commercial superalloys. Particular attention has been given to the relationship between variations in the volume fraction and distribution of y' and the temperature dependence of the flow stress EXPERIMENTAL TECHNIQUES The Ni-Cr-Al system was selected because it is well characterized, bears a close relationship to commercial alloys, and offers the advantage of an extra degree of freedom over a binary system. In the present investigation, a series of alloys across the tie line between NisA1 and Ni3Cr (Ni3Cr is not an in-termetallic compound, the nomenclature is only used to designate the composition) were vacuum cast. The pseudobinary6 and the composition of the alloys used are shown in Fig. 1. It is important to note that the compositions of the y phase and the y' phase in the two-phase alloys was always the same. Alloy compositions were selected from the binary diagram, Fig. 1, in order that aging at 900°C would produce from 0 (100 pct y) to 100 pct y' by volume percent. (The size of the y' particles produced during the equilibrium aging treatment increased as the volume fraction of y' increased, ranging from about 0.2 p at low volume fractions up to about 0.8 p at the highest volume fraction.) The y' phase is based on the inter-metallic compound Ni,A1 which has the fcc LIZ type superlattice structure, and chromium substitutes for aluminum in the structure. The y phase is a disordered fcc solid solution. The alloys were heat treated at 1150°C for 2 hr, air cooled to room temperature, and finally annealed for 16 hr at 900°C. The rods were then centerless ground to 0.25 in. diam and cut into compression samples 0.5 in. long. The compression tests were made on an In-stron machine at a strain rate of 7 x 10"4 sec-'. A rapid heating radiant heat furnace was used which minimized the heating and temperature stabilization time to 10 min for the highest testing temperature. All the tests were stopped after 5 pct plastic strain.

Jan 1, 1970

By Charles H. Behre

This paper deals with recent geologic studies in the slate belt of Northampton, Lehigh and Berks counties, Pennsylvania. The work was conducted under the auspices of the Pennsylvania Topographic and Geologic Survey. Three years have now been spent in detailed consideration of the economic geology of this region. In the field, particular attention was paid to the bearing of geology on quarry development and property valuation and the object of this paper is to summarize the results from that viewpoint. Excellent studies of a somewhat similar nature have already been carried out by Bowles,' but with the emphasis upon the details of quarrying and fabricating methods, rather than upon the geologic relations. The Northampton-Lehigh-BeRks District Location The region here discussed lies in east-central Pennsylvania and extends southwestward from Delaware River, on the New Jersey line, to the Schuylkill in north-central Berks County. It is an elongated belt occupying the northern sections of the three counties mentioned and lying along the southern edge of Blue Mountain. Its length is about 50 miles and its average width five or six, though in places it attains a maximum of 10 miles. There are no large cities in the region, but about 10 miles south are Reading, Allentown, Bethlehem and Easton. Railroads serving the slate belt are the Delaware, Lackawanna and Western, and the Pennsylvania along the Delaware River, the Lehigh Valley and Central of New Jersey along the Lehigh, and the Pennsylvania and Philadelphia and Reading on the Schuylkill. In addition, two railroads—the Philadelphia and Reading and the Lehigh and New England—cut obliquely through the slate region to reach the more isolated communities. Transportation facilities are thus excellent. The slate deposits of these three counties are conspicuously unified, both economically and geologically. In general type of marketable

Jan 1, 1928

By W. S. Owen, T. Bell

The variation ox the M, temperature with nitrogen concentration has been determined experinzentally. The free-energy difference between martensite and the parent y Phase at the M, temperature,is computed for Fe-C and Fe-N alloys using recent solubility data fm the Fe-N system and new data for the variatim of the activity of the interstitial solute in the y phase with concentration. The "geometric model" is considered also, and the importance of Zener ordering is noted. It is shown that, although at any chosen concentration the M, temperature and the activity are significantly different in the two alloy systems, the free-energy duference is the same within the limits of experimental error, thus Providing further evidence of the very close similarity between the martensite transformations in Fe-C and Fe-N alloys. TO estimate the free-energy change accompanying the martensite transformation in binary interstitial alloys it is necessary to know the variation of the Ms temperature with interstitial solute concentration and some thermodynamic data. To date, only the Fe-C system has been discussed because this was the only system for which relevant experimental measurements had been made, but even in this case the data available are insufficient to permit the free-energy change to be calculated without the assumption of a thermodynamic model for the y and a solid solutions. The last comprehensive discussion of the topic was by Kaufman, Radcliffe, and Cohen in 1.960.' Since that time Ellis, Davidson, and Bodsworth2 have redeter mined the activity of carbon in y iron as a function of carbon content and Atkinson3 has measured the activity of nitrogen in Fe-N austenite. The M, temperature of Fe-N is reported in the present paper. Thus, it is now possible to assess the free-energy change accompanying the martensite transformation in Fe-N alloys on the same basis as that used to assess the change in Fe-C alloys. This comparison is of interest because it has been shown recently4 that the structure of the martensite formed in Fe-N alloys changes with nitrogen content in a manner exactly parallel to the changes in structure in the Fe-C series and that the strain associated with the distortion of the iron lattice in either the y or the a phase by a nitrogen atom is the same as that produced by a carbon atom. The work to be described tests whether or not this close similarity between the two systems extends to the thermodynamics of the martensitic transformations. THE Ms TEMPERATURES FOR Fe-N MARTENSITE Bose and Hawkes5 found the M, temperature of a eutectoid Fe-N alloy (2.35 wt pct N) to be 35°C. This single determination appears to be the only reported measurement of the M, temperature of an Fe-N alloy. In the present work a series of more than fifteen different specimens containing between 0 and 2.7 wt pct N were prepared by controlled nitriding of pure iron wire 0.010 in. diam. The iron was supplied by B.I.S.R.A. and was designated ACN2. The nitriding procedure, all aspects of which are critical, has been described in detail elsewhere.' Each specimen was quenched from the austenitizing temperature into brine at 20°C without removing the specimen from the ammonia-hydrogen atmosphere in which it was ni-trided. Alloys containing up to 0.7 wt pct N were fully martensitic. More concentrated alloys contained progressively more retained austenite. At 2.34 wt pct N the specimen was completely austenitic after quenching to 20°C. The M, temperature of specimens with M, temperature above 20°C (those containing less than 2.35 wt pct N) was determined by a thermal arrest technique. For the more concentrated alloys (2.35 to 2.70 wt pct N) the variation of electrical resistance with temperature down to -196°C was used. Unlike Fe-C alloys, Fe-N alloys cannot be reaus-tenitized in vacuum or in an inert atmosphere because excessive loss of nitrogen occurs, even in short times, at high temperatures. Consequently, the alloys were reaustenitized in the ammonia-hydrogen mixture corresponding to nitrogen equilibrium at the temperatures used. The specimens were quenched in a blast of cold hydrogen gas and the temperature, measured by a thermocouple welded to the 2.5-in.-long specimen, was recorded on a high-speed recorder. In the first experiments 0.002-in.-diam chromel-alumel wire thermocouples were used but it was found that these gave erroneous readings due to contamination by nitrogen pickup. Pt-Pt 13 pct Rh wires of 0.002 in. diam were found to be satisfactory. Further details of the experiments are available in the original thesis.7 The cooling rate was controlled between 400° and 4000°C per sec by adjusting the hydrogen pressure. At least three cooling curves were obtained for each composition. Each specimen was analyzed for nitrogen after quenching. To aid in the accurate location of the martensite arrest points a series of cooling curves of 0.010-in.-diam platinum wire were recorded and these, which did not contain an arrest, were used as comparison standards. Four specimens, each in the form of a 3-in. loop, were prepared from each of the four alloys containing more than 2.35 wt pct N. One specimen was used for nitrogen analysis, one for X-ray diffraction, and two for resistance measurements below 20°C. The latter specimens were quenched from 20°C into constant-temperature baths at selected lower temperatures.

Jan 1, 1968

By D. L. Creighton, S. A. Hoenig

The field-emission microscope has been adapted for the study of microcrack growth during the early stages of fracture in metal wires. Cracks as small as 6 1 in length can be detected and their growth can be followed to specimen failure. The system is quite useful in searching for microcracks since only sharp-edged surface defects will emit electrons under the experimental conditions. THE conditions leading to brittle fracture were discussed a number of years ago by Griffith1 and the term Griffith Cracks is often used for the small surface cracks which are responsible for brittle fracture. Griffith's theory has been modified by stroh2 and more recent results on metals are discussed by Allen,3 pp. 123-40. At present the phenomenon is not completely understood but there is general agreement that at least in certain materials the sequence leading to brittle fracture involves several stages. The initial microcracks are present because of cooling or working stresses, Hahn et al.,3 p. 95. When a stress is applied to the specimen the cracks grow slowly until the release of stored elastic energy is large enough to accelerate the crack and provide the necessary surface energy for crack growth. At this point the growth rate appears to increase rapidly to some new equilibrium velocity, and failure occurs. Since the microcracks are usually about the size of a single metallic grain (Ref. 3, p. 99) it is not easy to find them and it is very difficult to follow their growth under stress. This paper will report on the use of a cylindrical field-emission microscope for observation of the formation and growth of microcracks. I) THE FIELD-EMISSION MICROSCOPE The field-emission microscope (FEM) has a high magnification and resolution and is almost uniquely suited for observations of microcracks. Since the FEM is relatively new as a metallurgical instrument, a short description will be given here. Normally metals at room temperature do not emit electrons; however in the presence of a strong electric-field gradient, electrons can tunnel out through the reduced potential barrier. Since this tunneling is a function of the local field gradient and the local work function, the emitted electrons can be used to produce a highly magnified image of the surface by allowing them to strike a phosphor screen. Because the electron emission is dependent upon the local field gradient, smooth surfaces emit few electrons except at very high fields. On the other hand cracks, extrusions, or other surface defects, having sharp edges, emit strongly since the field gradient is very high in the vicinity of these defects. This indicates that the FEM should be most useful for detection of microcracks on otherwise smooth surfaces. A field-emission microscope was first used by Muller4 in 1936 for observation of metal surfaces, and recent reviews have been given by Muller5 and Gomer.6 The instrument has been used for metallurgical studies in the area of surface diffusion,= recrystallization,7 and grain growth 8 (Ref. 8 is directed specifically at metallurgists). In the work of Muller4,5 and Gomer 6 the specimen was in the form of a sharp metal point at the center of a phosphor-coated glais sphere. The impact of the emitted electrons on the phosphor produced a highly magnified image of the specimens. Such a system is not practical for applying a controlled stress to the specimen and a cylindrical geometry has been used in this investigation. This allowed the application of a controlled tensile stress to the wire specimen. Normally a cylindrical FEM geometry produces magnification only in the radial direction. This is the case because a smooth wire at the center of a cylinder produces a purely radial electrical field. However, if there is a break in the smooth surface of the inner cylinder, the field near the break becomes three-dimensional and the area of the break is highly magnified. The reason for this is clear if it is recalled that the field gradient depends on the relative radii of the inner and outer cylinders; if a crack forms, its edge radii are of atomic dimensions and a very high field gradient is formed near these crack edges. Since the electrons receive most of their acceleration near the crack edge and are always traveling perpendicular to the field lines, they tend to spread out and produce the magnified image observed in the cylindrical field-emission microscope. 11) BRITTLE-FRACTURE STUDIES A) Experimental Apparatus. The geometrical arrangement chosen was that used earlier by Gifford

Jan 1, 1965

By R. C. Buehl, J. P. Morris

F. D. Richardson—The authors are to be congratulated on this further contribution to our knowledge of the thermodynamics of the interaction between sulphur and carbon and silicon in liquid iron. As the authors state, the influence of carbon and silicon on the activity coefficient of sulphur in liquid iron is clearly of great importance in the blast furnace, since it must cause a three to fourfold improvement in the partition of sulphur between slag and metal. The influence of increasing temperature in further increasing the activity coefficient of the sulphur in the metal in the blast furnace by increasing the carbon content is also of interest. This effect, however, is probably only part of the reason for the general observation in blast furnace practice, that the sulphur content of the metal is lowered by increasing temperature. Other contributing factors are the lowering of the oxygen potential in the presence of carbon by increasing temperature and the probable increase in the activity coefficient of the lime in the slag for the same reason. The former of these effects, which works via the (CaO) + [S] = (CaS) + [O] equilibrium, might possibly account for a 70 pct improvement in the sulphur partition and the latter might give a further 50 pct improvement. C. Sherman—I would like to compliment the authors on their very careful research. If I may, I would like to show results of calculations on the carbon-sulphur-iron system similar to the ones that were shown in our paper for the silicon-sulphur-iron system. For Fe-S-C ternary system k=PHgs/PH2 x 1/(f1°) (f2°) (%S) where fs = sulphur activity coefficient fs' = fs for Fe-S system of equal pct S f3° = f2/f2 for Fe-S-C ternary system This same analysis has been used on other systems, but the results shown in fie.- 7 are for carbon and silicon. L. S. Darken—I would like to make two brief comments in addition to complimenting the authors on an apparently very precise and accurate investigation. The first is that the present work is in agreement with a calculation by Larsen and myself." Our calculation (much less precise than the present work) was based on: (1) Unpublished work on the sulphur content of molten iron (1.5 pct at 1500°C) in equilibrium with graphite and an iron sulphide slag; (2) the distribution coefficient of sulphur between slag and carbon-free liquid iron. We expressed the result in a form equivalent to log 7. = 0.18 [%C] which gives an activity coefficient (?s.) of sulphur only slightly higher than the authors find and certainly within the precision of the earlier work. My second comment concerns the correlation of the thermodynamic findings with atomistics. A rough pic- ture of the atomic arrangement in the liquid solution is rather easily conceived for this particular liquid solution containing iron, carbon, and sulphur. Carbon has a very much stronger affinity for iron than for sulphur. Hence we may conclude that a sulphur atom will but seldom be adjacent to a carbon atom—since this would be a position of high energy. From the metallic radii of iron and carbon we know that six iron atoms pack neatly around one carbon atom. Thus each carbon atom in retaining this shell of iron atoms (which latter may not be replaced by sulphur on account of the high energy requirement) decreases the available positions for each sulphur atom by six. Hence each atomic percent of carbon decreases the equilibrium sulphur content by 6 pct (of itself). Or, at low concentration each atomic percent of carbon increases the activity coefficient of sulphur by 6 pct. This is in good agreement with the observed increase (6 or 7 pct at low carbon content). It is indeed gratifying to find a case where, by such simple reasoning, quantitative agreement is found between precise data and the modern picture of the atomistics of the metallic state. J. P. Morris (authors' reply)—We would like to point out that there is an error in the equation on p. 322 of the paper. The third equation should read: ½S2 (gas) + H2 (gas) = H2S (gas) The authors wish to thank everyone for the interest they have shown in the paper. In regard to the general observation in blast furnace practice, that the sulphur content of the metal is lowered by increasing the temperature, Dr. Richardson is correct in stating that the cause can be attributed only in part to the increase in activity coefficient of sulphur resulting from the rise in carbon plus silicon content of the metal with rise in temperature. However, this factor is probably an important one. The results of one experiment, performed since this report was written, indicate that at a constant temperature the addition of silicon to a melt saturated with carbon causes an increase in the activity coefficient of sulphur even though the carbon solubility is lowered. In this test, 2.5 pct silicon was added to a melt saturated with carbon and maintained at 1400°C. Although the carbon content dropped from 4.85 to 4.1 pct, the activity coefficient of sulphur was increased by about 20 pct.

Jan 1, 1951

By A. E. Deruyttere, J. Van der Planken, M. Laurent, Van den Bergen

FahRENHORST and schmid1 observed that zinc single crystals work hardened less rapidly when strained in liquid air (- 185°C)than in a bath at -82°C, whereas at higher temperatures the rate of work hardening decreased with increasing temperature, as would be expected. Cadmium and magnesium showed no such decrease at -185°C. At that time the observed anomaly for zinc at liquid air temperature probably seemed insignificant. However it later was confirmed2 by experiments in liquid nitrogen (-196°C) and in the mixture solid carbon dioxide-acetone (-77"C) and therefore appeared to be real. seeger3 then suggested that the anomaly might be due to the different wetting of the zinc crystals by the cooling media. Recently a new confirmation was obtained,4 however the cooling media again were different: the rate of strain hardening was found to be lower in liquid nitrogen and liquid oxygen than in pentane cooled to various temperatures down to -126°C. Ekperiments will now be reported in which the medium surrounding the specimen at the different temperatures was the same, namely gaseous air. The single crystals were made from "Overcor 99.99" zinc. They were grown in a vertical traveling furnace on seeds of nearly the same orientations. The diameter of the crystals was 5 mm and the length between shoulders 140 mm. The brass shoulders were stuck to the crystals by means of araldite. A thin steel wire was fixed to each shoulder and served to fasten the specimen to a Houns-field tensile testing machine. The crystals with the shoulders and part of the wires were surrounded by two concentric cylindrical containers. The coolant. either liquid air or ground solid carbon dioxide, was poured into the outer container only. During cooling the containers rested on a support which was removed when the straining was started. In order to check the temperature which the crystals would attain inside the inner container, a hollow bar of zinc in which a thermocouple was fitted was first mounted in the apparatus as a substitute for a crystal. It appeared that a constant temperature, respectively - 183° and -72°C, was attained inside the bar, if a soaking time of the order of 1 hr was allowed and if the outer container was constantly kept filled. Accordingly, this procedure was adopted for every tensile test. To take account of the large scatter, fourteen tensile tests were performed with liquid air and seven with solid carbon dioxide. The orientation of the crystals and the results are presented in the table, in which the symbols have the following meaning: 1 : temperature x : initial angle between basal plane and specimen axis : initial angle between slip direction and specimen axis a : shear strain at fracture 0: average rate of strain hardening = —-——- 100 t0 and Te representing respectively the critical shear stress and the shear stress at fracture. Despite the scatter of the a- and 8— values which is of the same order of magnitude as in the work reported by Seeger and Trzuble,4 it is evident that the strain hardening rate is significantly lower at -183°C thanat-72°C. The table also contains the average values calculated from Seeger and Trauble's results at the corresponding temperatures: z.e., four results at -183oC and two at-70°, -71°C. These authors calculated 9 in a slightly different way, but this is unimportant. The agreement between the a-values shows that both sets of experiments are comparable despite the differences in experimental techniques. The rates of strain hardening also agree and it may therefore be concluded that the anomaly is not

Jan 1, 1962

By F. N. Koepel, L. A. Callaway

The property of the Andes Copper Mining Co. is in the central part of the Republic of Chile, Province of Atacama, about 75 miles to the eastward from the port of Chafñaral. At this point the Andean system is made up of two principal ranges, and the mine and metallurgical plant are both on the westerly slope of the outer or western range. Mean elevation of the mine is 10,500 ft., while at the plant the elevation ranges from 9445 to 9700 ft. A meter gage railroad extends from the company's port at Barquito, near Chañaral, to the reduction plant at Potrerillos. This road has a total length of 94 miles, of which 57.79 miles are owned by the Andes Copper Mining Co. and the remainder of the road is controlled by the State. Development of the Potrerillos mine and installation of the metallurgical equipment presented unusual difficulties due to the arid nature of the country, high altitude and remoteness of the location from any considerable center of population. As a primary step it was necessary that railroad transportation be provided in order that mine development and plant construction could go forward on an economical basis. Provision of an adequate supply of water for domestic and metallurgical uses involved the construction of approximately 178 miles of pipe lines, all of which have their sources at altitudes ranging from 12,000 to 14,000 ft. above sea level and traverse rough and difficult terrane. Water for metallurgical use is brought to Potrerillos from the Ola River, a stream originating in the high cordillera to the eastward from the property. It is delivered by means of a steel pipe line, 32 miles long, having diameters ranging from 22 to 36 in. Domestic water is supplied to the various camps through a system of pipe lines aggregating 146 miles in length, the Ola water being unfit for this purpose. These conductors gather water from numerous springs in the high mountains to the eastward from Potrerillos and deliver it to the mine, the reduction works and the port at Barquito. Extensive permanent housing facilities had to be provided as it was necessary to care for more than 3000 workmen and employees at the

Jan 1, 1934

By J. A. Holmes

It is a fact that is coming to be more widely recognized by the general public, as well as by members of the medical fraternity, that the health of persons living in our hill-country depends in no small degree upon the drinking water obtained, just as it has been found that the* use of pure water in the lowlands and swamp-areas of the Southern States results in practical immunity from malarial diseases. Hence the problem, how to obtain supplies of wholesome water for the towns and manufacturing establishments in the hill-country or Piedmont plateau-region of the Southeastern States, becomes one of considerable interest, the importance of which will continue to increase, as the favorable conditions for manufactures and agriculture in this region will make it, in the near future, the most thickly populated portion of the South Atlantic States. Water-supplies from Surface-streams are unquestionably of the first importance; and in the mountain counties, where the region is still largely forest-covered and the streams are swift and continually aerated by rapids and cascades, the water is of superior purity and clearness. This statement is also applicable to the more elevated and sparsely settled portions of the Piedmont plateau; but in the less hilly and more thickly settled portions of this region the streams are more sluggish, and the waters more muddy and less pure, owing to the fact that a much larger proportion of the surface is under cultivation.

Jan 1, 1896

By A.S. Richardson

AIR conditioning, or air cooling, for the improvement of ventilation in the Butte mines has come into increasing use during the past 10 years. In part, the methods practiced have been described in previous publications of the Institute, but some improvements on earlier methods have been made and a number of new features have been developed. This paper is presented as a record of progress made, and for the sake of completeness describes all general features of the work. The need for air conditioning in the ventilation of mines in the district arises from the fact that the temperature of the ground and mine water has shown a very great increase with increase in mining depth, and has now reached a maximum of slightly over 130°F. The most difficult part of the ventilation problem is the maintenance of temperature and humidity of a satisfactory standard in the working places, especially on the lower levels. Although ordinary ventilation is adequate to maintain good conditions in most of the working places it is subject to a number of limitations at great depth. Most important among these limitations is that with increase in depth the air becomes heated before it reaches the working places, both by compression from increase in atmospheric Pressure and by heat transferred to it from rock at high temPerature, so that its capacity for lowering temperatures is greatly reduced before it reaches the operating zone. Increasing depth of mining also increases the distance traveled by the air in its passage through the mine, and this causes a corresponding increase in resistance to air flow, so that there is greater difficulty in maintaining even the same volume in circulation. Thus, in the face of a demand that the ventilating system have a very much greater capacity to remove heat from the mine, the tendency is for that capacity to diminish. The only evident alternatives were (I) the opening of additional air shafts to increase the volume of air in circulation, (2) an extension of the existing system that would be subject to the same limitations, or (3) the adoption of an entirely different method such as air cooling. Fortunately for an economic solution of the problem, the mean annual temperature of the surface atmosphere at Butte is about 40°F., with very low relative humidity in summer, so that there is unlimited natural cooling power at a temperature range adaptable to air-conditioning methods. Methods Two similar methods of air conditioning are used, as necessitated by service requirements and dependent upon the equipment available. In one, which is the more important and has the greater cooling capacity, water is circulated in a closed circuit, and, alternately, first absorbs heat from warm mine air and then dissipates it in the surface atmosphere by cooling at a cooling tower. The second

Jan 1, 1943

By A. S. Richardson

AIR conditioning, or air cooling, for the improvement of ventilation in the Butte mines has come into increasing use during the past 10 years. In part, the methods practiced have been described in previous publications of the Institute, but some improvements on earlier methods have been made and a number of new features have been developed. This paper is presented as a record of progress made, and for the sake of completeness describes all general features of the work. The need for air conditioning in the ventilation of mines in the district arises from the fact that the temperature of the ground and mine water has shown a very great increase with increase in mining depth, and has now reached a maximum of slightly over 130°F. The most difficult part of the ventilation problem is the maintenance of temperature and humidity of a satisfactory standard in the working places, especially on the lower levels. Although ordinary ventilation is adequate to maintain good conditions in most of the working places it is subject to a number of limitations at great depth. Most important among these limitations is that with increase in depth the air becomes heated before it reaches the working places, both by compression from increase in atmospheric Pressure and by heat transferred to it from rock at high temPerature, so that its capacity for lowering temperatures is greatly reduced before it reaches the operating zone. Increasing depth of mining also increases the distance traveled by the air in its passage through the mine, and this causes a corresponding increase in resistance to air flow, so that there is greater difficulty in maintaining even the same volume in circulation. Thus, in the face of a demand that the ventilating system have a very much greater capacity to remove heat from the mine, the tendency is for that capacity to diminish. The only evident alternatives were (I) the opening of additional air shafts to increase the volume of air in circulation, (2) an extension of the existing system that would be subject to the same limitations, or (3) the adoption of an entirely different method such as air cooling. Fortunately for an economic solution of the problem, the mean annual temperature of the surface atmosphere at Butte is about 40°F., with very low relative humidity in summer, so that there is unlimited natural cooling power at a temperature range adaptable to air-conditioning methods. Methods Two similar methods of air conditioning are used, as necessitated by service requirements and dependent upon the equipment available. In one, which is the more important and has the greater cooling capacity, water is circulated in a closed circuit, and, alternately, first absorbs heat from warm mine air and then dissipates it in the surface atmosphere by cooling at a cooling tower. The second

Jan 1, 1943

By E. S. Machlin, S. Weing

GRAIN boundary stress relaxation has been the subject of several investigations in recent years, but as yet the phenomenon is not well understood. One of the major difficulties has been the lack of a sufficient amount of data with which to evaluate any proposed mechanism. Little information is available on the effect of small amounts of substitutional solutes on grain boundary stress relaxation. It is with this important phase of the problem that this investigation is concerned. The influence of substitutional solutes on grain boundary stress relaxation has been recently investigated in copper by Pearson: and in aluminum by Dorn et al.' Pearson studied the effect of zinc, gallium, germanium, and arsenic on the relaxation peak of OFHC copper.* The pure OFHC copper decreased the peak intensity and a second peak appeared at a higher temperature. This latter peak was termed the alloy grain boundary peak. At the lowest binary concentration studied, approximately 1 atomic pct, the primary peak was almost completely obliterated. Pearson found that the activation energy calculated from the alloy grain boundary peak for all solutes, irrespective of the concentration, was 44,000 cal per mol. Pearson concluded that the increase in activation energy from 33 to 44 kcal per mol is not continuous but abruptly changes from the lower to the higher value. As no attempt was made to investigate the intermediate range of concentration and hence calculate the possible variation of the activation energy for the initial grain boundary peak, this conclusion is hardly valid. In contrast to these results, Dorn et al. studied the effect of zinc, silver, copper, germanium, and magnesium on the grain boundary stress relaxation of aluminum. No change in the energy of activation was observed for binary alloys of the flrst four solutes, but a linear increase was found for increasing concentration of magnesium. Saturation was not found up to the maximum of 1.6 atomic pct. The energies of activation were obtained by plotting the horizontal displacement of the dynamic modulus curve vs temperature for two vibrational frequencies. As the modulus is proportional to the square of the frequency, this requires the measurement of the torsional frequency over a range of temperature. However, the technique does not lead to an unambiguous interpretation of the grain boundary

Jan 1, 1958

By Gram Curtis

The apparatus described below for the handling of plates upon their delivery from the rolls, embodies features believed to be of interest to those contemplating the building of new plate-mills, and also to such owners of existing mills as may be considering the improvement of their works. The points to which attention is called are the small space required for the finishing-end of the mill, and consequently the very moderate size of the building for the amount of plates handled; the directness and ease of manipulation, and therefore the mall amount of labor required; the distribution of plates; the facilities and time allowed for their cooling. These, together with other features of detail and general arrangement scarcely less important, will become apparent when the descriptions and illustrations herewith given are understood. As these devices deal with the finishing of the plates only, they may be added to any plate-train when the floor-space and the building are large enough to permit their introduction; and it will be obvious that the features of this method, more or less modified, are applicable to any existing mill. Figs. 1 and 2 show a three-high 32-and 19- by 120-inch Lauth mill, with hydraulic lifting-tables, served by four heating-furnaces, with hydraulic cranes for charging and drawing. Upon leaving the rolls, the plate is allowed to rest with its forward edge projecting somewhat beyond the end of the catcher's table. Here it is seized by the automatic tongs, A, suspended from a buggy travelling in the overhead trough, B, and actuated by the hydraulic cylinder, C. These tongs are operated by a boy, who stands several feet from the heated plate, and controls the long light handle, D, shown in the plan, Fig. I. His duty is merely to advance the tongs by means of .the hydrulic cylinder, C, to raise or

Jan 1, 1892

By H. M. Otte

Certain choices for the shear elements of the inhomogeneous distortion in the phenomenological theory of martensite formation are examined for their agreement with crystallographic and X-ray data of iron alloys. The assumption that the shear elements must represent slip or twinning systems characteristic of bcc metals is found to covey all observations, even when a small uniform dilatation is taken into consideration. In bct martensite, (011) becomes a possible twinning or faulting plane, in addition to {112), and qualitatively similar X-ray line broadening is to be expected from both. The basic concept inherent in the current theoriesl-4 of the formation of martensite is that the interface between the parent (austenitic) and product (martensitic) phase is an invariant strain plane (i.e., one that is undistorted and unrotated). Experimental evidence that the interface is of such a nature is available in certain transformations2'5'6 but for the transformation in iron alloys direct observation has not proved enlightening. Internal strains resulting from the formation of the small martensite platelets within the parent austenite matrix7 make it difficult to produce the desired evidence. Indirect evidence, however, such as the continuity of scratches in passing from untrans-formed to a transformed region, strongly indicates that the habit plane in iron alloys is an invariant strain interface. The scatter in habit planes in a given specimen8 would suggest that internal stresses have a slight but definite influence. On the other hand, composition changes which affect the lattice parameter can alter the habit plane appreciably, and by an amount greater than the scatter.' The success of the theories depends on the choice made for the "inhomogeneous distortion" or "complementary shear'' in the analysis and also on the choice for the parameter 6 representing a small uniform dilatation. In the approach developed by Wechsler, Lieberman, and Read'," it is implicitly assumed that 6 is unity. In the case of iron alloys, all observations cannot be explained without varying either the inhomogeneous distortion or 6 . Bowles and Mackenzie3 considered only the effect of varying d. They found it difficult to reconcile the wide scatter of habit planes with the theory and were forced to the conclusion that it may also be necessary to consider variations or different choices of the inhomogeneous distortion. Wechsler and Read" considered a limited number of possible choices for the inhomogeneous distortion, but no variation in 6, though this could easily have been introduced if so desired. It is the purpose of the

Jan 1, 1961

By A. C. Stoddard

Early in the present century, prospect-ing was active in the area of the present Miami district. There were plenty of blue and green copper outcroppings, but very little ore of a grade that would stand shipping costs had been uncovered. Late in the first decade of the century, tunnels were driven into the north and south slopes of the Inspiration ridge, and two of them exposed disseminated copper sulphide ore. This was the original discovery of such ore on the ground of what eventually became the Inspiration Division of the consolidated company. By 1910 exploration of the ground area was well along and by 1911 underground development had been started. In the next few years a large tonnage of disseminated copper ore had been proven— sufficient to justify the expenditure of several million dollars in mine development and for mine equipment plus large sums for treatment plants. The mine and treatment plants were placed in production July 1, 1915. To Jan. I, 1945, there had been produced from the mines of the Inspiration Consoli-dated Copper Co., more than 106,000,000 tons of ore. Nearly all of this tonnage had been recovered by block caving. GeologIcal and EconomIc FActors Block caving is a mining system based on the fact that if a mass of rock has a sufficient number of fractures and planes of weakness the mass will disintegrate if the support of an area of sufficient size is taken away—that is, "undercut." If the material that caves away from the bottom of a block is drawn off the spalling is progressive. There is a limit to the speed of this spalling or caving action, which varies with the structure of the rock being caved. If the rock is drawn at a rate faster than the caving rate, and if this drawing is continued too long, a void may be created that could make a very dangerous condition if the area should drop as a block and force the air below the uncaved rock out through the raises and drifts. This can be a very destructive force. On the other hand, if the broken material is not drawn fast enough the swell of the material in place to broken material would pack the mass until it was almost solid again and could not be drawn without much blasting, or perhaps even partially undercutting again. Geologically therefore it would seem that any rock with seams and fractures would cave; but for block caving there should be enough seams and fractures in a limited area so that such an area will cave and produce a product that can be drawn safely, rapidly enough and at a cost justified by the value of the product being drawn. At the Inspiration the disseminated ores occur in two formations, the Pinal schist and the Schultze granite. There is no material difference in the grade of the ore formed in the schist and in the granite. The chief copper minerals are chalcocite, malachite, azurite and chrysocolla. Other copper minerals occur in limited quantity.

Jan 1, 1946

By W. A. Tiller, S. O’Hara

Grain refinement in stirred melts has previously been shown to arise from dendrite segmentation. The present work discusses experiments capable of distinguishing between remelting and mechanical effects which result from fluid motion. Nucleation of still un-dercooled Sn-1 pct Pb melts with a single-crystal seed shows that the grain size of the resulting ingots decreases as the undercooling at nucleation increases up to about 1Z0C, then increases again for larger undercoolings. Pure melts exhibit little refinement as a result of nucleation at any undercooling up to 12°C. The presence of fluid motion gives rise to grain multiplication in pure melts, but the magnitude of this effect is partly obscured by solid-state pain growth. The results indicate that two grain-multiplication pvocesses can operate, one which involves dendrite remelt ing, and another associated with fluid motion. Small ingot experiments indicated that an equiaxed transition can be caused by fluid motion. THE presence of forced convection during recales-cence of undercooled Sn-1.3 pct Pb melts has been shown to give rise to extensive grain refinement during solidification of small ingots of this alloy.''2 In Ref. 2, this refining was shown to result entirely from dendrite fragmentation and not from any nucleation mechanism. The purpose of the present work is to establish what processes lead to dendrite segmentation. Experiments were therefore carried out to determine the resulting structure of both pure tin and Sn-1 pct Pb melts, nucleated at various undercoolings by single-crystal seeds in the absence of forced or natural convection. By comparing the information obtained from these experiments with the results of Refs. 1 and 2, the effects of fluid motion on the ingot structure, and the details of the segmentation mechanisms, should become clear. The results of these experiments should also be helpful in understanding the solidification structures of larger ingots since natural convection, which is known to play an important role in determining ingot structure13 differs only in degree from the fluid-motion effects studied here. I) EXPERIMENTAL PROCEDURE The apparatus shown in Fig. 1 was constructed to permit controlled nucleation of stirred or unstirred supercooled melts using a seed oriented in the tin dendrite growth direction. Because the melts, in all cases, were capable of larger supercoolings than the one used in each experiment, the structure observed always resulted from a single nucleation event at the surface. The sequential procedure was as follows: Tin was melted under purified hydrogen and the oxide removed at a temperature of 450°C . Electromagnetic stirring was then used to clear the surface completely and during this time the guide tube was lowered underneath the melt surface. A pointed Czochralski-like crystal was then propagated from a specially prepared tin dendrite seed4 inside the guide tube while the temperature of the bulk melt was held just above the melting point, ensuring a perfectly clean seed which was epitaxial with the original dendrite. The dendrite and epitaxial seed, still in the guide tube, were withdrawn from the melt which, in turn, was undercooled to 2C° below the temperature at which the nucleation experiment was to be performed. The melt was held there for several minutes, both in stirred and in still-melt experiments. The temperature was next raised to the required value and the melt nucleated by the carrot seed inside the guide tube, the heater power being shut off just after nucleation. In experiments where quenching after nucleation was required, a high-density graphite crucible was used, but otherwise the procedure was as described above. The temperature gradient in the melt before nucleation was kept below 1C° per cm by carrying the experiment out just below the center of the heater shown in Fig. 1.

Jan 1, 1968

By Erskine Ramsay

The following description of the Alabama coal-,fields is taken (with slight omissions) from the report " On the Warrior CoalField, by Henry McCalley, A.M., C. and M. E., Assistant State Geologist:" The coal lands of Alabama are of the great coal basin of the Ohio, or of the great Appalachian coal-field, and are estimated at 8660 square miles. They formed one connected field prior to the great Appalachian revolution, when there was pushed up through them long, narrow, anticlinal ridges which have been denuded into the present well-known anticlinal valleys, and thus this great field has been divided up into three more or less distinct parts. These parts were named by Prof. Tuomey, in 1849, the Warrior, the Cahaba and the Coosa coal-fields, respectively, from the names of the rivers which drain them. They are of very unequal size, the Warrior, with an area of 7810 square miles, being nearly ten times as large as the other two combined, and about two-thirds as large as the coal-area of Great Britain. This Warrior field is the most northwestern of the three coal-fields of Alabama, and comprises all of the coal-measnres in Alabama, northwest of the Alabama Great Southern railroad, or all of those drained by the Warrior and Tennessee rivers. The greater part of this field, almost all of it away from the present railroad lines, has never received more than a surface-examination. Still, we have in the Warrior coal-field one of the richest coal-basins of this or any other country. As a whole, the Warrior coal-field is a broad, shallow, tray-shaped depression, sloping towards the southwest, and with its southwest end covered by a newer formation and its southeast side, especially, complicated by folds and fractures. As is the case with all of our Coal Measures. it is composed of a series of sandstones. conglomerates, shales, slates and coal-seams, with some little limestone at several horizontal positions, but contains no thick bed of this last rock like the Measures of Pennsylvania and other States. The thickest conglomerates are near the bottom and top of the series, and hence these coals might be said to belong mainly to the

Jan 1, 1891

By R. H. Lee

So far as I am aware the references to the " kerosene blow-pipe" in the Transactions comprise only a skeptical opinion from Mr. Witherow (ix., 70), and accounts of the use of the blow-pipe by Mr. Witherbee (xiii., 675) and Mr. Gayley (xiv., 779), together with brief remarks by Mr. Weeks and Mr. Kennedy on Mr. Witherbee's paper. The subject can scarcely be considered novel, in view of these references, yet it is not so far exhausted that an additional account of the successful application of the blow-pipe would be out of place, especially if accompanied with some new details and a drawing of the apparatus itself, showing its simplicity and safety. Some time ago, owing to a variety of causes, my furnace was working very badly, the troubles culminating suddenly one morning in a chilled hearth, solid from the bottom to the tuyeres, with the exception of a narrow passage-way from above to the cindernotch, which remained open. Through this we continued to flush and cast, with the prospect of a long and troublesome siege, in working down to the iron-notch. At the end of two days matters had not greatly improved, and we seemed no nearer the desired result than on the morning of the chill, when, at the suggestion of Mr. Farrell, of Glamorgan, I decided to use the coal-oil blow-pipe; the intention being to cut a hole from the iron-notch up to the tuyeres, and then let the furnace melt out the chilled mass. In four hours from the time of starting, the hole was made and

Jan 1, 1887

By John T. Eash, Clair Upthegrove

During recent years nickel has had an increasingly important role as an alloying element in the copper-tin bronzes. Nickel additions not only produce better casting alloys but also make alloys whose properties can be varied by precipitation hardening; thus leading to increased commercial application of copper-nickel-tin alloys. Recent investigations have indicated a decrease in the solubility of tin in the alpha phase as the annealing temperature is lowered and as the nickel content is increased within certain limits. A further change caused by the nickel additions is produced in the excess phase of the copper-tin bronzes. The alpha plus delta eutectoid is replaced by a clear precipitated constituent in the alloys containing up to 15 per cent tin and not less than 1 per cent nickel. This paper has a dual purpose. The first is to present a new determination of the alpha-phase boundary in alloys containing from 0 to 20 per cent nickel, together with the liquidus and solidus temperatures above that field. The second purpose is to give the equilibrium conditions existing in alloys exceeding the alpha phase containing up to 31 per cent tin and 5 per cent nickel, so that the disappearance of the alpha plus delta eutectoid constituent may be explained. After considering the earlier investigations of the related alloy systems and the experimental procedure used in this investigation, the alloys will be discussed in groups as separate quasibinary systems containing constant amounts of nickel. The systems considered contain 0, 1, 2, 3, 5, 10 and 20 per cent nickel. The straight copper-tin system was reinvesti-gated in order to establish a foundation on which to build the remaining material. The 1 per cent nickel alloys studied give the relations existing in the region of the eutectoid transformation between the copper-tin system and the 2 per cent nickel copper-tin system which has been investigated in detail. The thorough examination of the latter system was made since 2 per cent of nickel is representative of the commercial additions to the cast bronzes and also because it is sufficient to produce

Jan 1, 1933

By H. Van F. Furman

As the cyanide-method for the extraction of gold from ores is extensively used in the United States and elsewhere, and appears destined to prove a factor of increasing importance in the metallurgy of gold, a description of the latest laboratorymethods may prove of interest. The history of the development of the process in the United States has been analogous to that of all new processes. Many failures are to be recorded and a few successes. It is the opinion of the writer that, had the following simple tests been better understood, many of the failures would not have occurred, and we should probably have a larger number of successful plants in operation. While the process is not simple, but requires a high degree of chemical and engineering skill, the determination of the adaptability of an ore to the method is generally not difficult. While the laboratory-results will not always coincide with the actual results obtained in the mill, they will serve as a guide and control on the working of the mill, and mill generally suffice to determine if the ore can be

Jan 1, 1897

By A. S. Appleton, M. B. Bever

The stored and expended energies of an Au-Ag alloy deformed in torsion were investigated as functions of strain, strain rate, and temperature. At room temperature, the stored energy, measured by tin solution calorimetry, increased linearly up to an intermediate strain, above which it was nearly constant; at 78 °K the relation was linear up to fracture. Approximate values of the energy stored at 4 OK indicate a rapid increase below 78 OK. The energy stored by specimens deformed successively at 4o and 78oK changed slowly with increasing second strain from the curve for energy stored at 4 OK (measured after annealing at 78oK) to that for deformation at 78°K. The ratios of the stored to the expended energy at room temperature and 78 oK were unusually large. The additional amount of energy stored at the lower temperature is attributed mainly to an increase in the number and energy of dislocations. The stored energy as a function of strain rate at 4oK (measured after annealing at 78oK) increased to a sharp maximum over a narrow range of strain rates, whereas the expended energy changed only slightly. These effects are explained by the generation of point defects resulting from the enforced nonconservative movement of jogs in fast moving screw dislocations. The effect of straining successively at two strain rates at 4oK was also investigated. Stress-strain curves for 4o, 78oK, and room temperature and the results of micro examination of specimens deformed at these temperatures are also reported. THIS investigation is a continuation of a research program primarily concerned with the effects of variables on the energy relations involved in the deformation of metals. The variables investigated in earlier work have included strain, strain rate, temperature of deformation (room temperature and 78oK), and the type of deformation process. Most of this work has been carried out with Au-Ag alloys. In the investigation reported here, the deformation process was torsion, which had not been used previously in the program. The stored and expended energies involved in the deformation process were measured as functions of strain, strain rate and the temperature of deformation in the range 4" to 373" K. The microhardness and microstructure of deformed specimens were also investigated. The relation between stored energy and strain differs for different deformation processes.1,2 In general, the stored energy increases with strain and may attain a nearly constant value at large strains. This value and the rate at which it is reached, however, depend on the process of deformation. This dependence has been attributed, at least in part, to differences in the effective strain rate and rise in temperature of the specimen during deformation. The effects of the temperature of deformation on both the stored energy and the energy expended in the working process have been the subject of only a few investigations.3-6 Values of these quantities at low temperatures are of special interest as they yield information on point defects which, for many metals, is not obtainable at higher temperatures. The effect of the strain rate on the stored and expended energies has received little attention The strain rate has usually been measured only in relative terms, and hence the interpretation of its effect on the stored energy has been mainly comparative.

Jan 1, 1963