Search Documents

By Philip D. Shelton

INTRODUCTION Traditional design of support for permanent underground mine excavations place great emphasis on the magnitude of the maximum radial load which a specific support or lining must sustain. However, this depends upon so many factors that reliable prediction in advance of excavation is very difficult except in strong-self supporting ground. Some of the factors affecting the loads acting on a support are illustrated in Table 1. [ ]

Jan 1, 1984

By Alfred L. Beebe

to. A strip of thin platinum foil, about one inch square, is perforated with pin-holes over its entire surface. It is then bent into the shape of a letter U, and its opposite corners are connected by short pieces of platinum wire, so as to form a sort of basket. In this is placed a piece of amalgamated zinc of convenient size, and the whole is suspended by a stout platinum or silver wire in the bottle containing the solution to be reduced. Another strip of platinum foil,

Jan 1, 1886

By D. S. Jacobus

The boiler here referred to was of the water-tube type, having 2535 square feet of heating-surface, which the makers held to be capable of generating 325 horse-power of steam; this being understood to mean that 325 times 30 pounds of water would be evap-

Jan 1, 1889

By Persifor Frazer

IN his “Final Report," Vol. II, part second, p. 763, Prof. Rogers sums up the metalliferous veins of the mesozoic sandstone by remarking that these are not associated with dykes or trap-rock, but are independent metalliferous injections. But singularly enough, in enumerating the different kinds of ores, no mention is made of

Jan 1, 1877

By Kwong Yung Kwang

This mine, which is sometimes called Tong colliery, from its director, Tong King Sing, is about 80 miles northeast of Tientsin (see map, Fig. 1). Fig. 2 shows a vertical transverse section through the coal-beds. These beds have a dip to the south of about 45' and are interstratified with sandstone, shale, indurated clay and fire-clay. Of the

Jan 1, 1888

By Robert H. Richards

VERY little has been published recently on this subject in the mining journals or proceedings of societies. The attention of experts has been diverted perhaps by the demands for pan amalgamation of refractory ores. Yet free milling ores occur in many localities, and it may be interesting to have on record some data as to details of running a small test-mill, especially as details of results do not seem to be accessible to students and investigators. Küstel, in 1863, under battery amalgamation, dismisses the subject by stating that "amalgamation on copper-plated platforms, troughs, and other copper fixings" is " very imperfect, and mostly abandoned." J. Arthur Phillips says, in 1867, under placer mining : A well-amalgamated copper plate is considered as effective for

Jan 1, 1880

By Max Roesler

Page I. Introduction........................... 78 Location.......................... 78 Scope of Work and Acknowledgments.............. 79 History and Mining...................... 80 I1. Topography and its Interpretation................. 80 III. Petrology............................ 82 Sedimentary Rocks...................... 82 Description....................... 82 Age.......................... 84 Igneous Rocks........................ 85 Diabasic Rocks..................... 86 Dioritic Rocks...................... 87 Granitic Rocks...................... 88 Later Dike Rocks.................... 88 IV. Areal Geology.......................... 88 Rock Types Found in the District............... 88 Distribution of the Various Rock Types............. 89 Surface Distribution................... 89 Vertical Distribution................... 90 Causes of Present Areal and Vertical Distribution of the Various Rock Types..................... 91 Faulting...................... 91 Magmatic Differenti~tion............... 91 Tilting........................ 95 Erosion....................... 96 V. General Description of Ore Deposits................ 96 Nature of Ore ........................ 96 Shap~ and Size of Orebodies.................. 96 Geologic Position....................... 97 Mineralogy......................... 98 Distribution....................... 98 Interpretation...................... 99 Superficial Alteration................... 102 VI. Genesis of the Ore Deposits.................... 104 Previous Theories...................... 104 J. P. Kimball...................... 104

Jan 1, 1917

By Jacques Friedel

Jan 1, 1964

By B. E. Warren

Jan 1, 1965

By T. F. Kassner

The dissolution kinetics of type 304 stainless steel in the Bi-Sn eutectic alloy have been investigated under the well-defined hydrodynamic conditions produced by the rotating-disc sample geometry. In addition, the mutual solubilities of iron, chromium, nickel, and manganese from 304 stainless steel in the eutectic alloy were determined over the temperature range 450" to 985°C. The convective -diffusion model for mass transport from a rotating disc was used to interpret the experinlental dissolution data. The dissolution process was found to be liquid-diffusion-controlled under specific conditions of temperature and Reynolds number. Liquid penetration into the 304 stainless steel resulted in a reduction of the di,ffusion-controlled mass flux and thus precluded the calculation of the diffusion coeficients of the four components from 304 stainless steel in the Bi-Sn eutectic alloy. The convective-diffusion model for diffusional limitations of electrode reactions and mass transport at the tationssurface of a rotating disc set forth by Levich 1,2 has found wide applicability in the investigation of electrochemical and dissolution phenomena in aqueous systems. Riddiford 3 and Rosner have reviewed the model and also include numerous references on work of this nature. More recently the rotating-disc system has been applied to the investigation of hetereogeneous reactions in liquid-metal systems. Shurygin and Kryuk 5 have measured the dissolution rates of carbon discs in molten Fe-C, Fe-Si, Fe-P, and Fe-Ni alloys. Shurygin and shantarin6 also studied the dissolution kinetics of iron, molybdenum, chromium, and tungsten, and the carbides of chromium and tungsten in Fe-C solutions with a rotating-disc sample geometry. In these systems it was possible to distinguish between diffusion and reaction control mainly through experimental confirmation of the velocity dependence of the dissolution rate predicted by the model. However in the absence of dependable solubility data and the virtual lack of diffusion data in these systems, a quantitative check of the magnitude and the temperature dependence of the rate was not possible. In many instances, estimates of the activation energy for solute diffusion and the diffusion coefficient based upon the experimental dissolution data are not credible. A recent study by this author7 has resulted in a critical test of the model in a liquid-metal system. The solution rates of tantalum discs in liquid tin were measured over a wide range of temperature and velocity conditions. In addition, the solubility and diffusion coefficient of tantalum in liquid tin were determined as a function of temperature. The latter data were used with the model to predict both the magnitude and the temperature dependence of the dissolution flux. In that work it was also deemed necessary to reevaluate the solution to the convective diffusion equation to incorporate the effect of the lower range of Schmidt numbers encountered in liquid-metal systems. Good agreement between the model and the experimental dissolution data in the region of diffusion control was obtained in the Ta-Sn system. The Bi-Sn eutectic alloy is used as a seal between the reactor head and the reactor vessel in the Experimental Breeder Reactor-11. The alloy is fused periodically prior to fuel-handling operations. In that connection, it was necessary to investigate the compatibility of the liquid alloy with the type 304 stainless-steel containment material. The results of a rotating-disc study in this multicomponent system are presented. EXPERIMENTAL METHOD The 5.08-cm-diam discs were machined from 0.317-cm-thick plate. Chemical analysis information for the type 304 SS material is given in Table I. The discs were ground flat on metallographic paper and given a final polish on Linde B abrasive. A thin support rod was threaded into the disc and the region around the threads was fused under an inert gas. The support rod was fitted with a quartz protection tube and then was attached to a supporting shaft which passed through a rotary push-pull vacuum seal. The disc and supporting shafts were dynamically balanced prior to insertion into the furnace tube. The apparatus is shown schematically in Fig. 1. The 58 pct Bi-42 pct Sn eutectic alloy melts were prepared from 99.995 pct pure Bi and Sn by fusing the components in a 7-cm-ID Pyrex crucible. The system in which the melts were made was evacuated to a pressure of 1 x 10-6 Torr and back-filled with purified argon several times before melting the charge. The ingot was reweighed and placed in a slightly larger-diameter Vycor crucible used in the dissolution runs. A run was started by lowering the disc into the liquid

Jan 1, 1968

By Eckley B. Coxe

The subject of this paper will be treated as briefly as possible under the following heads : I. The latest designs of some of the machinery used at these collieries in the preparation of coal. 11. The means employed for elevating, conveying and transporting the coal and slate in and about the breaker. 111. The means employed for raising the coal from the mines to the top of the breaker. IV. The iron breaker as a structure. V. The preparation of the coal as effected in the iron breaker. A key to the plates and the letters and numbers designating different parts, will be found at the end of the paper. I. Preparing Coal. Anthracite coal as it comes from the mines is not marketable. The "run of mine" cannot, as in the case of bituminous coal, be sold. Anthracite, being very compact and practically free from volatile combustible matter, burns only at the surface, and it is, therefore, deemed important to have the lumps as nearly of a uniform size as possible, so that between them a large amount of surface will remain exposed to the action of the air without checking the draught too much, or allowing enough air to pass to cool the coal below the ignition-point, In other words, if the pieces of coal of the size of a chestnut and smaller are mixed with lumps of the size of an egg they fill the air-passages and prevent a free draught. It has long been recognized, therefore, that one of the most important points in preparation is to have a uniform sizing, and also to make as large a number of different sizes as can be produced without too

Jan 1, 1891

By M. F. Hawkes, R. F. Mehl

The rate of isothermal transformation of austenite to pearlite depends upon the rate of nucleation, N, and the rate of growth, G, of pearlite in austenite. Values of N are given in terms of the number of nuclei forming in unit time per unit grain boundary area of unreacted austenite; values of C are given in terms of the linear rate of radial growth. Variations in the isothermal rate with temperature result from variation of N and G with temperature. Depth of hardening of a steel depends fundamentally upon values of N and G; changes in carbon and alloy content effect changes in N and G and thus affect depth of hardening. Quantitative studies are available on N and G for the formation of pearlite in plain carbon eutectoid steels.3 Systematic studies in this field are necessary if the phenomena are to be well enough known to furnish a proper basis for full rationalization and for theory. Accordingly, the studies are continuing, both with respect to the effect of alloying elements upon the values of N and G in the formation of pearlite and to the values of N and G for the formation of ferrite in hypoeutectoid steels. The present paper is the first relating to the effect of alloying elements upon the values of N and G for pearlite. It offers special interest since cobalt is known to have an anomalous effect upon the rate of formation of pearlite, accelerating it, whereas all other elements retard it.4 It will be shown that cobalt increases both N and G for pearlite and that this effect is inherent in the Fe-Co-C system and not dependent upon factors relating to austenite heterogeneity nor upon any recognizable adventitious factor. Inasmuch as the rate of diffusion of carbon in austenite and the interlamellar spacing of pearlite are variables related to G and possibly to N (in a manner not yet certain), measurements of the effect of cobalt upon them are also reported here. In the course of the work, measurements were made on the effect of cobalt upon the marten-site temperature and these are given. COBALT AS AN ALLOYING ELEMENT IN STEEL Properties of Cobalt Cobalt resembles iron more closely than does any other chemical element. Its atomic number is 27, hence it is the element immediately following iron in the periodic system. The two differ in atomic structure only in the fact that cobalt contains seven electrons instead of six in the third, or transition, level of .the third shell. The next shell, which is the

Jan 1, 1948

By M. F. Hawkes, R. F. Mehl

The rate of isothermal transformation of austenite to pearlite depends upon the rate of nucleation, N, and the rate of growth, G, of pearlite in austenite. Values of N are given in terms of the number of nuclei forming in unit time per unit grain boundary area of unreacted austenite; values of C are given in terms of the linear rate of radial growth. Variations in the isothermal rate with temperature result from variation of N and G with temperature. Depth of hardening of a steel depends fundamentally upon values of N and G; changes in carbon and alloy content effect changes in N and G and thus affect depth of hardening. Quantitative studies are available on N and G for the formation of pearlite in plain carbon eutectoid steels.3 Systematic studies in this field are necessary if the phenomena are to be well enough known to furnish a proper basis for full rationalization and for theory. Accordingly, the studies are continuing, both with respect to the effect of alloying elements upon the values of N and G in the formation of pearlite and to the values of N and G for the formation of ferrite in hypoeutectoid steels. The present paper is the first relating to the effect of alloying elements upon the values of N and G for pearlite. It offers special interest since cobalt is known to have an anomalous effect upon the rate of formation of pearlite, accelerating it, whereas all other elements retard it.4 It will be shown that cobalt increases both N and G for pearlite and that this effect is inherent in the Fe-Co-C system and not dependent upon factors relating to austenite heterogeneity nor upon any recognizable adventitious factor. Inasmuch as the rate of diffusion of carbon in austenite and the interlamellar spacing of pearlite are variables related to G and possibly to N (in a manner not yet certain), measurements of the effect of cobalt upon them are also reported here. In the course of the work, measurements were made on the effect of cobalt upon the marten-site temperature and these are given. COBALT AS AN ALLOYING ELEMENT IN STEEL Properties of Cobalt Cobalt resembles iron more closely than does any other chemical element. Its atomic number is 27, hence it is the element immediately following iron in the periodic system. The two differ in atomic structure only in the fact that cobalt contains seven electrons instead of six in the third, or transition, level of .the third shell. The next shell, which is the

Jan 1, 1948

By Lyall, Zickrick

As a result of the studies on recrystallization and crystal growth made in this laboratory, certain theories have been developed. These are expressed briefly in a paper by Dean and Hudson.' One of the principal points brought out in that paper is that in the deformation of a crystal, the energy supplied is distributed to the atoms of the lattice, probably by the forced formation of molecules. It is found that a Maxwellian distribution of the energy among these atoms will account for the grain growth at various temperatures. According to such a distribution the number of atoms with energy above a certain critical value, E, necessary for recrystallization at the absolute temperature T is given by n = Ne-E/kT where N is the total number of atoms. It is apparent that if this line of reasoning is correct, a metal which has been cold-worked and reheated to a temperature below that of complete annealing will have the atoms with the higher energy recrystallized, that is, reduced to normal energy and there will remain only atoms below a certain energy. If this metal is again cold-worked the peak in the number-energy distribution curve will, as compaied with its position after the first cold-working, be displaced toward the regions of lower energies, that is, the temperature of recrystallization will be higher. By a repetition of this process the position of this maximum and hence the recrystallization temperature of the metal could be raised considerably. In order to check this theory, experiments have been made on copper wire. The wire was drawn from 1/4-in. rod to 22 B & S gage and then sample lots were annealed at 400 and 220° C., respectively. The wire annealed at 400° C. gave an elongation of 34 per cent., whereas that annealed at 220° C. gave only 23 per cent. These wires were then drawn by identical practice to 34 B & S gage and the elongation determined after an anneal of 3 min. in an oil bath held at various temperatures. The figures obtained have been plotted in Fig. 1. It will be seen that the

Jan 1, 1927

By Pat McCarran

WHEN this Government was founded, the framers of the Constitution wrote into that instrument a provision that Congress should "coin money and fix the value thereof;" and the Constitution prohibits making anything but "gold and silver" lawful money. So silver is written into our basic law. Shortly after President Washington took office in 1789 the Congress passed the first Mint Act, setting up the U. S. Mint. In that Act, signed by President Washington on April 2, 1792, the weight of the American dollar was fixed, and it was provided how much silver should be contained in a silver dollar and how much gold should be contained in a gold dollar. It was decided that 371 1/4 grains of pure silver was to be the standard dollar of America. That standard with respect to the pure silver content of the dollar has never changed.

Jan 1, 1947

I HAVE now traversed for you in the small and fragile bark of my writing all the shores of the deep and spacious sea embracing the uses of material fires, drawn on by my own desire to enrich you with more learning and with the procedures of these things, as much as to satisfy your demands. Having through the grace of God arrived at the appointed end of my voyage and neither knowing nor perceiving a way of going farther, I had decided to furl the [167] sails and cast die heavy anchors into the water in order to enjoy in tranquillity respite from my sailing, when I was warned by my pilot that before I could disembark I should turn my glance backward and reexamine my work in detail to see if there were any part that had by chance remained undescribed in the obscurity of silence. When I did this there immediately appeared in my mind's eye the many sublimates and smoky tinctures that had been made by the burning and most powerful fire of love. I need not say that I knew of it in far-off countries or from the knowledge of others, but I knew it in my own breast and as my very own and can therefore surely esteem it as hotter than all the other fires that the world calls by that name. Although today its sparks and living flames are spent because of my cold and hoary season, nevertheless it is true that the memory of acts of love of long ago still remains with some smoke and warmth. Therefore, since in this work of mine I wish to describe for you the effects and powers of fires, I should logically have spoken of this before any of the others, because of its actual nearness and the great acquaintance I had with it. But since I have had the glance of my intentions directed at distant things, I have behaved as one does who does not see where he places his feet because he is looking at the sky, or as one who thinks about the affairs of others and forgets his own. But now I do not wish to pass over this thing and I wish to correct my error, particularly in order to provide a happier ending to my written work than by remaining among the horrible uproar of guns, powder, and saltpeter, which would be a harsher ending than speaking of love. Never-

Jan 1, 1942

By Robert E. Green, T. Hinton

The velocities of the three possible modes of elastic-wave Propagation have been calculated for single-crystal aluminum at 1-deg intervals throughout the standard steveographic triangle. The results are presented as isospeed contours. The deviations between the direction of maximum energy propagation and specirzen axes are presented as arrows drawn within the standard triangle. The orientation factors associated with dislocation nzotion on the primary slip system only and also on all twelve slip systenzs have been calculated for all three elastic waves. The orientation factors associated with a longitudinal standing--7aue resonant specivnen hazle also been calculated. The relevance of these results to ultrasonic attenuation measurements is discussed. DUE to the widespread use of ultrasonics in the investigation of the properties of solids a number of authors15 have discussed in detail the theory of elastic-wave propagation in solids. In this paper the modes of wave propagation are evaluated according to the procedure suggested by reeen' for the case of single-crystal aluminum at 1-deg intervals throughout the standard stereographic triangle. The wave speeds are presented in the form of contour diagrams within the standard triangle. The deviations between the direction of maximum energy propagation and the normals to the wave fronts are presented as arrows drawn within the standard triangle. The orientation-de pendent factors (orientation factors) associated with dislocation damping as derived in the preceding paper6 have been calculated for the case of aluminum at 1-deg intervals throughout the standard triangle. The orientation factors for dislocation motion on the primary slip system only and on all twelve slip systems are presented in the form of contour diagrams, for both the traveling- and the standing-wave conditions. The relevance of these results to ultrasonic attenuation measurements is discussed. ELASTIC-WAVE PROPAGATION Three waves can be propagated in a linear elastic homogeneous anisotropic medium. The velocity of propagation v of each of these waves in a medium of density p can be obtained from the determination of the eigenvalues and eigenvectors of the matrix equa- The A's are a series of moduli which are functions of the elastic constants cij and the direction cosines 1, m, and n of the specimen axis. In the case of cubic single crystals where there are only three nonzero elastic constants cll, c12, and C, the A's are, The solution of Eq. [I] will give the wave speeds (eigenvalues) and the direction cosines a, 0, and y of the particle displacements (eigenvectors). To obtain the direction of maximum energy flux requires the calculation of the energy-flux vector ET with com- w is the angular frequency, A, the amplitude, and v the velocity of the wave. The direction cosines a, b, and c of the energy flux vector are then given by

Jan 1, 1967

By E. H. Mohr

At the McGill concentrator of the Nevada Consolidated Copper Co., all flotation operations have been carried out in Forrester cells since November, 1926. In respect to cost of operation, the new cell has proved to be superior to the Callow, which it supplanted, and its incorporation in the flow sheet has resulted in a marked improvement in the metallurgy. Before citing the advantages of the new machine over the old, it should be explained that the Forrester has not only replaced the Callow, but it has made possible the elimination of a number of tables as well. When Callow cells were in use, table concentration preceded flotation. The ball mill pulp was elevated, by means of air lifts, to roughing Wilfley tables situated two floors directly above the flotation floor. On an intermediate floor were additional tables which cleaned the concentrate from those above. The finished table concentrate constituted approximately 60 per cent. of the total mill production, and contained about 40 per cent, of the recovered copper. The table tailings were returned to the classifiers, the overflow from which went to the flotation cells and the oversize to the ball mills. As soon as the Forrester cells were installed, this tabling operation was discontinued. The ball mill pulp now discharges into the classifiers direct, without the intermediate tabling. It was impracticable to ernploy the present flow sheet when Callow cells were in use, for the reason that unless the great,er part of the heavy mineral was first removed, it accumulated on the mats and adversely affected the flotation operation. By tabling ahead of flotation, it was practicable to maintain the concentrator at 10 to 20 per cent. greater capacity (depending up on the pyrite contnt of the ore) than was possible by flotation alone. This was due to the necessity for finer grinding in the latter case. Even though the table conecntrates contained only 6 to 8 per cent'. copper content, the low smelting costs made it advantageous to operate at high mill capacity, at the cost of low grade of product. Standard Section equipment With the old flow sheet, a standard section consisted of four ball mills and classifiers, one air. lift, 20 roughing tables, 10 cleaner tables, 12 primary

Jan 1, 1928

By T. H. Weldon, L. V. Whiton, R. R. McNaughton, J. H. Hargrave

Oxygen enriched air is being used quite extensively in the metallurgical plants of The Consolidated Mining and Smelting Co. of Canada, Limited, at Trail, B.C. The oxygen used for this purpose is a by-product from the Company's chemical plants located in the area. Most of the ore treated in the Trail metallurgical plants comes from Com-inco's Sullivan Mine at Kimberley, B.C. At Kimberley the ore is milled to produce lead and zinc concentrates which are shipped to Trail for further treatment to metal. One section of this paper deals with the use of oxygen enriched air in the suspension roasting of the zinc concentrates. In this process the concentrate is calcined for leaching preparatory to electrolytic recovery of the zinc. A second section of the paper describes the use of oxygen enriched air in operations at the lead smelter. There oxygen enriched air is used in the blast to the lead blast furnaces and in the slag fuming furnace which recovers the lead and zinc contained in lead blast furnace slag. The final section of the paper outlines the precautions necessary for the safe use of oxygen enriched air in any plant operation. The Use of Oxygen Enriched Air in the Suspension Zinc Roasters The suspension roasting of zinc concentrate developed at Trail, B.C., has been described in AIME Vol. 121, "The Electrolytic Zinc Plant of The Consolidated Mining and Smelting Company of Canada, Limited" by B. A. Stimmel, W. 11. Hannay and K. D. McBean. Since the publication of that paper, the use of oxygen enriched air in suspension roasting has been introduced as regular practice with marked advantage. The relative importance of a specific advantage may vary with changing conditions, but, in general, it may be stated that improved operation has been achieved at increased capacities. Suspension roasting is carried out at Trail in converted standard 25 ft diam Wedge roasters. The 2nd, 3rd, 4th and 5th roasting hearths have been removed and the drying hearth covered over. Drying of the concentrate is done on the drying hearth and the 1st roasting hearth. The dried concentrate, after any lump's have been broken up in a ball mill, is fed to a single burner located in the upper part of the combustion chamber. Oxygen is introduced at the burner fan along with the gases from drying, returned combustion gases from the waste heat boiler outlet and the required amount of new air. Up to 60 pct of the concentrate settles out on the 6th roasting hearth, the rest passilig out of the roaster. The product collected in the waste heat boiler is finished calcine, but the dust collected in the cyclones after the boilers is returned to the base of the combustion chamber where the sulphate is decomposed. Gases from the c'yclones go to a Cottrell precipitator. The discharges from the 7th roasting hearth and the waste heat boiler are combined with the Cottrell dust to give the finished calcine. Following small scale tests started in 1933, oxygen enriched air has been used continuously in the suspension roasting of zinc concentrate in Trail, beginning in 1937. A significant factor in promoting its use in this operation was the availability of by-product oxygen from the Company's near-by Chemical and Fertilizer Division. To-day it is standard practice at Trail to use oxygen enriched air for zinc concentrate roasting. The most important requirement in roasting a zinc concentrate for an electrolytic plant is that the zinc in the calcine should have maximum solubility. It is also desirable at Trail that the gas produced for the manufacture of suhhuric acid should have a ~naximum concentration of SO2 and that a substantial recovery of waste heat from the gas be achieved. High solubility of zinc requires that the sulphide sulphur and zinc ferrite in the calcine be kept low. These are both functions of temperature and time, with formation of zinc ferrite also dependent on contact between the iron and zinc particles. One of the inherent advantages of suspension roasting is that minimum time and contact are achieved. The limit on temperature is imposed by the fusion point of the concentrate and not by the need to control zinc ferrite formation. Operating temperatures are normally maintained within the limits of 1725" and 1850°F. A relatively low zinc sulphate in the calcine is required at Trail, and this results from discharging the calcine from the high sulphur dioxide atmosphere at a temperature above 1600°F.

Jan 1, 1950

By George C. Fryburg

The oxidation of platinum at high temperatures (above 800°C) is controlled by boundary-layer diffusion, except at the lowest pressures. The rate of oxidation is determined by the rate of diffusion of oxide through the boundary layer away from the platinum. This is in contrast to the situation in tungsten and molybdenum oxidation, where the rate is controlled largely by the diffusion of oxygen through the boundary layer towards the metal. The difference in mechanism is a consequence of the much lower rate of oxidation of platinum. Evidence is presented that supports this mechanism for the oxidation of platinum. SOME years ago we reported1 a study of the oxidation of platinum in ordinary oxygen in the temperature region above 800°C, where the oxide is volatile. All the data available up to that time had been obtained with platinum crucibles or plates heated in tube furnaces. The results were widely variant and highly dependent on the flow rate of gas through the furnace: the faster the gas flow rate, the higher the measured oxidation rate. These results indicated to us2 that reaction equilibrium was being approached in the furnace and that the rate was diffusion limited. To minimize these effects, we employed1 electrically heated ribbons placed in a cooled bulb. We were primarily interested in the low-pressure region, but some experiments were performed at pressures up to 1 atm. We found a peculiar pressure dependency which was explained on the basis that the rate of oxidation was proportional to the pressure at all pressures, but that with increasing pressure an increasing fraction of the volatilizing oxide was back-reflected to the ribbon by the surrounding gas molecules. The oxide molecules are not stable at the temperature of the platinum and are decomposed on impact, the platinum being re-deposited on the specimen. Because of the limitations of space, this explanation was offered summarily without detailed support. Recently, Jaffee and associates3, 4 have suggested that the pressure dependency of our data up to 0.5 torr could be explained on the basis of a Langmuir-type adsorption of molecular oxygen followed by dissociation. Since the correct explanation of the effect of pressure on the oxidation rate is a necessary requirement to the development of the basic mechanism of the oxidation reaction, we felt that the back-reflection theory should be presented in more detail. This is the object of the present paper. RESULTS AND DISCUSSION A typical set of results showing the pressure dependency of the oxidation reaction is presented in Fig. 1, where we have plotted, on logarithmic scales, the rate of oxidation, R, vs the pressure, p. For comparison some results of Krier and Jaffee4 and of Raub and plate5 are also shown. These data were taken at atmospheric pressure using furnaces. The effect of reaction equilibrium within the furnace is apparent from the much smaller values that these observers obtained: Raub and Plate In O2 found a rate of 3.1 µg cm-2 hr-1 compared to our value of

Jan 1, 1965