By Y. Nakahiro

The removal of heavy metal compounds from a synthesized waste cyanide solution is achievable by a precipitation-flotation method. However, the differential separation of constituting metals by this method was thought to be very difficult. The present author found that addition of ferrous salt to the synthesized waste cyanide solution of cadmium and copper can modify the separation characteristics of these metals. In this paper, the separation of cadmium from copper in the synthesized waste cyanide water by the precipitation-flotation method is discussed. This differential flotation uses ferrous salt as a precipitant and sodium oleate as a collector. Based on a series of fundamental flotation tests, actual differential flotation tests were made. The separation of cadmium from copper in the synthesized waste cyanide water was found to be satisfactory. This method can be effective for the removal of difficult-to- separate colloidal precipitates from liquids by the sedimentation method, provided the applicability of this method to the separation of the other metals is promising. This consists of the intensive studies which have been conducted at author's laboratory.

Jan 1, 1980

By M. Herman, G. J. London

A series of dilute Fe-Co alloy specimens were prepared from zone-melted iron. The iron used was given ten floating-zone passes in purified hydrogen. Alloying was accomplished by plating a gradient of metallic cobalt onto a 1/4-in.-diam bar of material from a pure plating bath. The deposit was radioac-tively tagged by a small addition of co80 to the plating bath. Alloy homogenization was accomplished by passing an additional floating-zone pass through the plated section of the bar. The final concentration gradient achieved was from residual to about 1000 ppm (0.1 pct) added Co. After homogenization, the bar was swaged to 0.057 in. wire and cut to tensile specimen blanks 1-1/16 in. long. Each specimen was counted in a well-type scintillation counter. The concentration of cobalt was computed by combining the normalized specimen counting rate with the known weight (measured to the nearest 0.01 mg) of cobalt added during plating. Fig. 1 shows the cobalt gradient obtained, exclusive of residual cobalt which was estimated by neutron-activation analysis to be approximately 50 ppm. Results of recrystallization for 1 hr at 750°, 700°, 650°, and 600°C with specimens containing 40, 170, 470, and 870 ppm added Co are shown in Figs. 2, 3, 4, and 5. Recrystallization was accomplished in a dynamic vacuum of less than 1 x 10 torr. The specimens were mounted and polished parallel to the swaging direction. The recrystallization re- sults show a radical coarsening of structure with increasing cobalt concentration. The coarsest structure obtained was at the 470-ppm level (at all recrystallization temperatures) with a slight grain refinement at the 870-ppm level shown. A more normal solid-solution effect is seen in Fig. 5 (60OoC, 1 hr) where the only specimen completely recrystallized is the one containing 47 ppm Co. Since the possibility existed that some atmosphere-contamination phenomenon might be responsible for the observed results the recrystallization series was repeated using sealed quartz capsules. These were filled with purified argon which was gettered during heat treatment on metallic titanium included in the capsules. The results obtained were essentially the same as shown. Another identical alloy was made using a 5-mm-diam bar of Westinghouse Puron. Specimen preparation and recrystallization treatment were also as described. The results obtained (see Table I) were somewhat erratic. Some coarsening in structure does appear at the highest cobalt concentrations. There is no apparent relationship between the coarse, columnar, directionally solidified structure of the as-melted bars and any of the recrystallized grain structures observed, all of which are much finer than the former structure. A recrystallization process can be most simply described as one of homogeneous nucleation of recrystallized grains in a cold-worked matrix followed by more or less uniform growth of the strain free grain into the cold-worked material.' An impurity element may influence one or both of these processes. Aust and utter' have shown that impurities strongly influence grain boundary mobility in lead. Moreover, definite recrystallization textures are produced by small concentrations of tin,3 while additions of silver or gold4 produce large boundary in-

Jan 1, 1964

By D. J. Carney, C. W. Boquist, E. C. Rudolphy

Effect of variations in sinter feed composition on sinter strength, bulk density, re-ducibility, chemical composition, and microstructure were determined by sintering experimental samples on a production sintering machine. Increasing amounts of roll scale, ore fines, return fines, and blast furnace slag were most beneficial to feed permeability, sinter bulk density, and strength. Burnt lime additions improved feed permeability but were not beneficial to sinter strength or bulk density. Sinter reducibility was adversely affected by all additives. DEVELOPMENT of methods for evaluating sinter quality, which would in some way predict the behavior of the sinter during charging and smelting in the blast furnace, has been given considerable attention in recent years. In a previous investigation at South Works of the United States Steel Corp., standard sinter sampling and testing procedures were developed.1,2 By modifying the sinter sampling device, a method of sintering experimental mix sinter samples upon a production Dwight-Lloyd sintering machine was also developed. This technique afforded a rapid and controlled method of investigating the effects of the various raw materials and additives on sinter quality and was used in this present investigation. Since the beginning of the present study in 1953, the results of numerous sinter investigations have been published, most of which were concerned with production tests of iron ore sinter, both here and abroad. Three groups of investigators reported results of experimental sinter studies that were related to this investigation. Voice et al.3 studied the effects of controlled variables on sinter quality by producing and testing experimental Northants iron ore sinter using an experimental sintering unit. Mor-rissey and Powers' determined the relationship between iron ore sinter quality and the moisture and coke content using a small laboratory sintering system. Burlingame et al.5 studied the effects of "additives" upon iron ore sinter using a laboratory sintering apparatus and laboratory grade raw materials. At South Works, it was considered desirable to study the effects of sinter mix composition and additives upon the quality of a flue dust-base sinter produced on a production sintering unit. Extrapolation of controlled laboratory test data to sintering plant operation lacking such precise control is not altogether satisfactory. Therefore, the present study was conducted in a manner which approximated production conditions as closely as possible. The raw materials used were those commonly encoun- tered in the production of flue dust and flue dust ore-type sinters and these were varied within extremes encountered in this type of sinter production. Experimental Procedure The experimental sinters were produced from 100 lb mixtures of sinter feed. The principal raw materials and additives used, their particle size, and approximate chemical composition are listed in Table I. The mixing of the raw materials was accomplished by means of a miniature single shaft pug mill shown in Fig, 1. The use of the pug mill as a mixer was decidea upon after encountering difficulty in reproducing the mixing and chopping effect of the sinter plant pug mill with other types of available small mixers. The miniature pug mill was constructed, consisting of 31/2x2x1/4 in, blades spaced 3 in. apart along a 3 ft shaft. Preliminary tests were run with this small mixer to establish the proper rotation speed and the required number of passes through the pug mill to thoroughly mix and distribute all the raw materials in a manner approximating the production Pug mill- Although the effects of varying the mosture content were determined in one particular series of tests, the amount of moisture added was changed as the composition of the experimental mix was varied. The aim in making water additions was to achieve a permeability as high as possible for each particular

Jan 1, 1956

By C. E. Wood, T. L. Joseph

This paper is a brief report of experimental work undertaken determine whether barium oxide in any quantity increases the desulfur ing action of blast-furnace slags. Industrial furnace operation wi slag containing small quantities of barium oxide, referred to later, intc ested S. A. Sanford of the Commercial Chemical Co., Youngstown, Oh to conduct experiments to furnish comparative results on desulfurizati with normal slag and slag containing small quantities of barium oxic The U. S. Bureau of Mines agreed to assist on the problem because the possible saving in fuel if the desulfurizing action of blast-furna slag can be substantially increased, also because the experiments woi yield new information on sulfur elimination in general, a matter economic importance in furnace practice. A more complete and func mental study of desulfurization of iron by slag is in progress. Distribution of Sulfur iN the Blast Furnace More than 90 per cent. of the total sulfur entering the blast furnz is in the coke. Sponge iron formed by reduction of iron oxides absor part of the sulfur as ferrous sulfide. Kinney's examination of sample taken from various levels of a 3004,011 furnace, shows that the me continues to take up sulfur until it reaches a level near the tuyer Desulfurization must therefore take place as the metal falls through t slag and as the slag and metal exist as layers in the crucible. The relative amounts of sulfur removed while the metal falls throu the slag and while the slag and metal exist as layers in t crucible are not definitely known. Preliminary experiments by t

Jan 1, 1929

By D. Harker, M. J. Murphy

The mechanism by which age-hardening takes .place is still not completely understood. The principal theories range from the extreme of "precipitaiion-hardening" to that of "order-hardening," with many intermediate gradations. In the hope of obtaining new data on which to base a choice among the many theories, the authors have made electron micrographs of formvar replicas taken from metallic specimens at various stages of age-hardening. The results so obtained on an alloy of 2 per cent beryllium in copper and one of 20 per cent molybdenum in iron will be described in the following pages, as well as the technique used in preparing the replicas. Preparation of Formvae. Replicas of Metallic Specimens This section is concerned with the techniques that have roved successful in preparing formvar replicas for studying the microstructure of metals with the electron microscope. Because of its simplicity and accuracy, the formvar replica1 method developed in the General Electric Research Laboratory has been used exclusively, since it is much simpler than the silica replica method of Heidenreich and Peck2 and produces as good results. The formvar method to be described requires a technique acquired only by practice, and no foolproof set of rules can be given. it is a rapid method and a replica can be obtained in less than five minutes under favorable conditions. This does not mean that perfect replicas can be produced every five minutes, but rather that one can well afford to take several strippings* in order to produce a replica of high quality. The metallographic technique required for replica work—very fine polishing and etching with very dilute solutions—is described here. It can be said, in general, that almost any surface that has been carefully prepared for a photomicrograph at 1000 or more diameters can be used to obtain a replica for the electron microscope. Preparation of Metallographic Specimens The preparation of the metallographic specimens is somewhat more exacting than that usually given to samples to be used for inspection under the light microscope. After much experimentation, it was concluded that the best method consists in polishing the metal through to the coarse cloth, then etching and repolishing on final cloth until the layer of distorted metal is removed. After this procedure has been completed, a dilute etch—to approximately the depth necessary for a micrograph at 1000 diameters—usually produces a sur-

Jan 1, 1945

By Clyde Williams

IF you would allow me some liberties, I would restate the title of this talk as "Scientific Research, Our Greatest Resource," because that title would represent more clearly a present-day conception of the metals and minerals situation. It is a subject worthy of careful consideration. Canada and the United States are so similar and interdependent in their national economies that, in the following discussion, examples of conditions in the United States may be interpreted to apply to Canada as well. Moreover, it is a striking fact that the per capita value of mineral production in Canada and the United States in 1940 was almost the same. Therefore, in the consideration of this subject, I have made no attempt to differentiate between the two countries. Consumption of the world's mineral resources in the last few decades. and particularly during World War II, has been so enormous as to require some form of magic to ensure the continued progress of civilization in the face of a diminishing supply of these resources which are so critically essential. As C. K. Leith pointed out, in 1941, indus-

Jan 1, 1947

By B. C. Wonsiewicz, G. Y. Chin

THE presence of deformation bands in cold-worked metals is known to influence the development of deformation textures1 but has not been considered in any theoretical treatments. At the present time the most rigorous theory of deformation textures appears to be based on Taylor's concept of homogeneous deformation of a crystal within a polycrystalline aggregate.' For each crystal the Taylor theory allows the operation of several equivalent combinations of five or more slip systems. Hence deformation bands can arise from the operation of a separate combination of slips in each of several portions within a crystal. On the other hand, a second type of band may occur as a consequence of slip on systems other than those selected on the basis on homogeneous deformation. This type appears to be associated with crystals of symmetrical orientations, such as the [loo] and [lll.] axial orientations in drawn wires of fcc single crystals studied by Ahlborn.3 In this note we propose a simple mechanism of deformation banding of the second type, and compare the theoretical results for wire drawing of [loo] and [Ill] with Ahlborn's observations. In outlini the model requires that the work to accomplish a given overall shape change by banding be less than or equal to the work to accomplish the same change by homogeneous deformation. While the work by homogeneous deformation, WH = ?T ;dri, can be calculated exactly by the equivalent methods of Taylor2 or of Bishop and Hill,4 the work by banding, WB, is less certain. The latter consists of 1) Wi, work by slip within a band, 2) Wb, work associated with formation of a boundary between bands, and 3) Wc, work to correct the difference in shape change arising from banding and homogeneous deformation. The Wi term can be evaluated explicitly for a band with an assumed set of slip systems, but a satisfactory analysis of Wb and Wc has not been obtained. Since WB = Wi + Wb + Wc WH, for banding to occur, however, a necessary condition is Wi = WH . Hence it seems reasonable to choose a band with the lowest value of Wi among competing bands consistent with Wi = WH, and then minimize Wb and Wc by arranging the physical configuration of the selected band. Wc is minimized by combining neighboring bands such that their net strain matches the macroscopic strain as closely as possible, and Wb is minimized by enforcing strain compatibility across the boundary between two neighboring bands, similar to the case of a grain boundary.5 It is realized that this procedure is not completely satisfactory, but it does seem to explain Ahlborn's observations reasonably well. The procedure is now outlined for the two corner orientations. a) [l00]. Fig. 1 shows a (100) stereographic projection. The results of the Taylor analysis for axi-symmetric flow by homogeneous deformation6 show that, while [loo] itself is unstable, the rotation of the tensile axis will nevertheless be confined to within about 15 deg from [loo]. Alternatively, less work may be expended by banding with slip on a pair of systems with primary-conjugate relationship, e.g., (ll1)[10l.I + (li1.)[110]. The latter represents minimum Wi for all possible bands.* Since there are four symmetrically

Jan 1, 1970

By J. E. Johnson

The description of the machine which coilstitutes the subject of this paper is best iutroduced by a statement of the conditions which led to its construction, which may be briefly given as follows : The ore handled at the plant to be here described* is of the variety sornetimes called by those familiar with the brown ores of the South, " Mountain," as distinguished from the " Lime-

Jan 1, 1899

By Alan D. Smith

Mine roof fall characteristics of 250 falls in 5 different room-and-pillar coal mines, located in Pike, Martin, and Floyd counties, were investigated to determine the relationship of selected parameters associated with roof failure and the assumed condition of the mine roof before failure. The selected parameters used in the study included: presence of cracks and water before the occurrence of fall, sloughing of coal ribs, floor heave condition, type of roof support (resin or mechanical anchor bolts), distance to coal face, and time of occurrence of fall after initial coal extraction. In addition, research hypotheses, utilizing multiple linear regression techniques, were generated to test the relationship among the selected parameters and mine roof condition. The results indicated that the vast majority of falls portrayed some presence of water before the actual fall, occurred in less than 30 weeks after initial coal excavation, located usually greater than 30 meters from nearest coal face, gave evidence of cracks in mine roof before occurrence of fall, generally portrayed a good roof condition before the fall, showed presence of sloughing of coal ribs, and gave no occurrence of floor heave before occurrence of fall. In terms of the characteristics of the original support systems in the mine roof falls studied, most roofs were either supported by mechanical-anchor bolts or resin or full-column bolts; very rarely did the roof appear to fail if supported by posts or cribs. A detail inspection of the hypothesis and model comparison results gave supporting evidence that the condition of the roof is not dependent on the usual indicators of potential failure, such as presence of cracks and moisture. In fact, in most cases of mine roof failure, the immediate roof condition was rated as good or better, which gives little or no indication of pending failure and collapse. Hence, a combination of factors that are not easily accessible to measurement, are the dominant factors in the determination of roof fall-potential areas.

Jan 1, 1984

By R. L. Rickett, W. C. Leslie

The influence of deoxidation practice, prior thermal history, and aging time and temperature on the strain-aging behavior of low-carbon open-hearth steels was investigated. The criterion of aging employed was the increase in yield strength in the tensile test, after straining and aging. Composition, prior heat treatment, and aging conditions were all found to be important in governing the strain-aging characteristics of these steels. THAT deoxidation changes the strain-aging propensities of low-carbon steels has been known for a long time, but there has been little agreement, and even contradiction, between results obtained by different investigators and between results obtained in the laboratory and in the mill. This investigation was begun in the hope that some of the uncertainties connected with the strain aging of commercial steels could be eliminated. In considering this problem, it was necessary to define strain aging and to examine the methods used to measure this property. Strain aging can be defined as the changes in properties of a metal or alloy with time, after cold working. The rate at which these changes occur increases as the temperature is raised above atmospheric. The requisite plastic strain is the principal distinction between strain aging and quench aging, the latter being due to precipitation from supersaturated solid solution. Strain aging is also characterized by rapid attainment of maximum hardness at high aging temperatures and lack of softening (overaging) at low aging temperatures. Several possible criteria of strain aging have been listed by Sachsl and by Davenport and Bain.' Because changes in mechanical properties are the most easily measured and the most commonly used, consideration of methods to be used in this investigation was confined to three tests: tensile, notch-impact, and hardness. Hardness tests are the most economical and easiest to perform, but produce only one measure of strain aging. Also, as pointed out by Felmly, Hartbower, and Pellini,³ hardness changes due to aging are not pronounced for steels containing more than 0.15 pct C. Notch-impact tests require careful preparation of large numbers of specimens. Above and below the transition temperature the test lacks sensitivity; furthermore, it is extremely difficult to impart a uniform strain to the specimens, followed quickly by aging and final testing; machining must generally take place after straining. For these reasons, the tensile test was selected for use. Although this test requires a considerable expenditure of time, labor, and money in preparation of the specimens and performance of the test, more information can be gained than from any other single mechanical test, information which includes upper and lower yield points, yield-point elongation, tensile strength, strain-hardening exponent, reduction of area, and elongation. Low and Gensamer' and Schwartzbart and Low5 lso used the tensile test, taking the increase in flow stress after straining in tension and aging as a measure of strain aging. In our work, as in theirs, each specimen was strained an arbitrary amount, sufficient to pass through the

Jan 1, 1954

By H. E. Gross

A plausrsle method of drilling beyond the continental shelves is set forth with limitations of the method. The continental shelves comprise the water-covered portions of land masses out to 600 ft. of water, or roo fathoms. The problems and possibilities of drilling beyond this depth are discussed in this paper. Introduction Much attention is being given the problem of developing petroleum beneath the open sea. Geophysical surveys have been made 26 miles offshore1 from the continental United States, and onco offshore ownership is established it is likely that there will be drilling for oil on the continental shelves. More than two years ago the author presented the means for drilling in deep water.2 at the fall meeting of the Petroleum Division of the AIME at Los Angeles. His concepts then were based on the use of rigid foundations suitable for drilling in water up to 600 ft. deep. The present paper suggests a method for drilling in deeper water. Possibilities and Problems of Drilling beyond the continental shelves It being conceded that because restricted deep-water portions of the hydrosphere might contain oil in commercial quantities, and that at any rate it is pertinent to know more of the nature of the lithosphere beneath the hydrosphere, the possibilities and problems of drilling beyond the continental shelves should be set forth. Drilling in open water would offer few if any advantages over drilling on land. These are: 1. The ocean transportation is available to deep-water drilling sites, and extensive pipe lines and roads are unnecessary. 2. Refinery facilities and markets perhaps are established on the near-by shore where adjacent fields on land are nearing depletion. 3. There is freedom from jungle pests and tropical diseases. 4. Competitive drilling is less likely. 5. Extensive areas attractive for development arc not yet under lease or concession. Disadvantages are great and numerous: 1. Storm hazards from wind and wave. 2. Expensive foundations, either rigid or floating. 3. Shutdown times because of weather. 4. Marine Regulations of Federal Bureaus in addition to customary regulations on land. 5. Frequent difficulty in moving men and materials to and from drilling platforms. 6. Extra precautions required in open sea. For drilling in water more than 500 or 600 ft. deep, rigid foundations2 become too costly, and floating foundations must be used, and they must meet the following requirements:

Jan 1, 1947

By H. E. Gross

A plausrsle method of drilling beyond the continental shelves is set forth with limitations of the method. The continental shelves comprise the water-covered portions of land masses out to 600 ft. of water, or roo fathoms. The problems and possibilities of drilling beyond this depth are discussed in this paper. Introduction Much attention is being given the problem of developing petroleum beneath the open sea. Geophysical surveys have been made 26 miles offshore1 from the continental United States, and onco offshore ownership is established it is likely that there will be drilling for oil on the continental shelves. More than two years ago the author presented the means for drilling in deep water.2 at the fall meeting of the Petroleum Division of the AIME at Los Angeles. His concepts then were based on the use of rigid foundations suitable for drilling in water up to 600 ft. deep. The present paper suggests a method for drilling in deeper water. Possibilities and Problems of Drilling beyond the continental shelves It being conceded that because restricted deep-water portions of the hydrosphere might contain oil in commercial quantities, and that at any rate it is pertinent to know more of the nature of the lithosphere beneath the hydrosphere, the possibilities and problems of drilling beyond the continental shelves should be set forth. Drilling in open water would offer few if any advantages over drilling on land. These are: 1. The ocean transportation is available to deep-water drilling sites, and extensive pipe lines and roads are unnecessary. 2. Refinery facilities and markets perhaps are established on the near-by shore where adjacent fields on land are nearing depletion. 3. There is freedom from jungle pests and tropical diseases. 4. Competitive drilling is less likely. 5. Extensive areas attractive for development arc not yet under lease or concession. Disadvantages are great and numerous: 1. Storm hazards from wind and wave. 2. Expensive foundations, either rigid or floating. 3. Shutdown times because of weather. 4. Marine Regulations of Federal Bureaus in addition to customary regulations on land. 5. Frequent difficulty in moving men and materials to and from drilling platforms. 6. Extra precautions required in open sea. For drilling in water more than 500 or 600 ft. deep, rigid foundations2 become too costly, and floating foundations must be used, and they must meet the following requirements:

Jan 1, 1947

By A. Taylor

IN a previous communication,l the quaternary system Ni-Cr-Ti-A1 was described in detail and it was shown how certain alloys used for high-temperature applications could be construed as consisting of Ni,Cr suitably modified by the addition of aluminum and titanium in relatively small amounts. With the correct aging treatment, the ordered face-centered-cubic Berthollide phase, y'-Ni,Al, could be precipitated from the face-centered-cubic primary y-solid solution. By increasing the proportion of titanium with respect to aluminum, it was also possible to precipitate the very brittle hexagonal-close-packed Daltonide phase, ?-Ni,Ti. From the nature of the system it seems reasonable to expect the y and y'-phases to take appreciable amounts of cobalt and iron into solid solution. In the case of the present investigation it was decided to confine the work to iron additions only. This element may be introduced in two quite distinct ways: 1) as a simple replacement for nickel; and 2) as a replacement for chromium, titanium, and aluminum. The second method of iron addition forms the basis of the present investigation, which is, in effect, a study of the pseudo-quaternary system Ni,Cr-NiPe-Ni,Ti-NLAl. For purposes of reference, Figs. 1, 2, and 3 have been included and illustrate the quaternary system Ni-Cr-Ti-A1 described in the previous paper along with sections through N&Cr-Ni,Ti-Ni,Al at 750" and 1000 "C respectively. As will be shown below, the pseudo-quaternary system with components Ni,Cr, NiPe, Ni,Ti, Nihl is remarkably similar in many ways to the face defined by Ni,Cr-Ni,Ti-Ni,Al because of iron re-

Jan 1, 1958

By Charles H. White

+1HARVARD UNIVERSITY, CAMBRIDGE, MASS. The equipment of a laboratory in which students are to be trained for practical work in metallurgical chemistry presents many difficulties not encountered in the fitting up of a commercial or works laboratory. At an industrial plant the chemical work required usually demands the frequent repetition of a comparatively limited number of methods. In a steel-works laboratory, for instance, by far the larger part of the work consists in making determinations of the usual impurities found in iron and steel; at a smelter the great bulk of the work is confined to the analysis of ores, slags, mattes, and fuels, which involve the frequent application of perhaps not more than a dozen different methods. In a laboratory of this character, therefore, those operations most frequently applied may each have a certain section set apart and fitted permanently with such apparatus as best facilitates the carrying out of this one operation. The work of a commercial or custom laboratory is perhaps more varied than that of a works laboratory, but the couditions are similar in these respects, that there is usually no great need for economy of space, and that a few skilled workmen are employed to carry the determinations through from beginning to end without interruption. On the other hand, the laboratory of a technical school should be planned on such a scale that a comparatively large number of students may work at the same time, and each desk should be equipped for general metallurgical analysis. In most institutions for technical education the student's program is so arranged that his day is divided among several subjects in the course of study; only a few consecutive hours being devoted to one subject, or spent in one laboratory. Therefore, those appliances should be provided that render possible the safe continuation of such processes as

Jan 1, 1905

By Edwin H. McKee

Eruption of rhyolitic ash-flow tuffs in the area of the McDermitt (Cordero) caldera began about 17.4 million yr (m.y.) ago and continued for about 1.5 m.y. During this period of silicic eruptions, a circular area about 30 km in diameter collapsed to form a caldera that subsequently filled with sedimentary and volcanic rocks. A total of more than 200 km30f silicic rocks was erupted from the volcano. The final phase of igneous activity, about 15.0 m.y. ago, included resurgent doming and intrusion in the south-central part of the caldera. Three to 4 m.y. later (-1 2 m.y. ago), hydrothermal solutions using the northern part of the caldera ring fractures as conduits deposited silica, cinnabar, pyrite, alunite, and other minerals in tuffaceous lake beds and volcanic rocks accumulated within the caldera. The ore-forming solutions may have been a residuum from the silicic magma, or connate water, or ground water heated by the still-hot resurgent magma in the central part of the caldera. The source of the mercury and other elements has not been identified.

Jan 1, 1977

By T. Busch, R. A. Dodd

The solubility of hydrogen in pure iron and pure nickel, and of nitrogen in pure iron, has been determined and agrees well with earlier data. Nitrogen is insoluble in pure nickel and cobalt. The solubility of nitrogen in Fe-Ni alloys also confirms earlier- work. The solubility of hydrogen in Fe-Ni alloys increases non-linearly with increase in nickel content, but the solubility of hydrogen in Ni-Co and Fe-Co alloys reaches a minimum at 75 and 50 at. pet, respectively. The solubility of nitrogen in Fe-Co alloys decreases approximately linearly with increase in. cobalt content. Nitrogen is insoluble in Ni-Co alloys. Determined interaction parameters are in good agreement with predictions of Gokcen and Ohlani. THE solubility of hydrogen and nitrogen in liquid iron and iron alloys has been studied by various investigators.'-l' The method of solubility measuremerit due to Sievertsl is usually preferred when the vapor pressures of the liquid components are sufficiently small, but other techniques such as sampling the equilibrated melt and then analyzing by vacuum fusion have been used quite often. Previously reported data on the solubility of hydrogen and nitrogen in ostensibly pure liquid iron are summarized in Table I; certain of the quoted results were obtained by interpolation of the published data. Agreement between the various investigators is only fair, indicative of the experimental difficulties involved in obtaining gas solubility data. The only report found on the solubility of hydrogen in pure nickel is that of Sieverts.2 The solubility of nitrogen in iron-nickel alloys has received some attention, 10, 11 the results indicating that the solubility decreases with increase in nickel content, becoming zero for pure nickel. There is no published information on the solubility of these gases in either pure cobalt or alloys containing cobalt EXPERIMENTAL PROCEDURE Sieverts' method of solubility measurement was used throughout the investigation. The construction of the melting chamber is somewhat different from A. Optical pyrometer F. Alundum cover B. Vycor chamber G. Alumina crucible C. Furnace coils H. Alundum sand D. Glass water jacket I . Alundum thimble E. Chamber support J . Detachable vycor base sealed with de Khotinsky cement

Jan 1, 1961

By Carl E. Swartz

ALTHOUGH a number of articles appeared during the war advocating the use of cadmium in lead-tin solders, very little information of value can be found in the literature regarding the properties of solders containing cadmium. In most of the published articles the cadmium seems to have been considered merely as a partial substitute for tin in a tin-lead alloy rather than as an essential constituent of a ternary alloy. The primary object of the substitution of cadmium for tin was to lessen the amount of tin required, at a time when the latter was scarce and high-priced, and thus to produce a cheaper solder. While this object was accomplished, the new properties resulting from a change from a binary lead-tin alloy to a ternary lead-tin-cadmium alloy were not given proper consideration in many cases. For the past few years, the American Smelting & Refining Co. has been marketing a very considerable amount of cadmium in the form of lead-tin-cadmium alloys for use as solders for certain special purposes, and the successful use of these solders suggested that if more extensive knowledge were available concerning the properties of lead-tin-cadmium alloys of various compositions their field of usefulness might be materially extended. The investigation described in the present paper was undertaken to obtain this information and, by means of tests under conditions approaching those of practical use, to determine the suitability of cadmium solders for various purposes. CHARACTERISTICS AND REQUIREMENTS OF SOLDERS IN GENERAL General Physical Properties.-When cast into bars, solder should present a smooth and bright appearance free from oxide inclusions and bubbles. Ductility should be as great as possible without sacrificing tensile strength, and vice versa. Hardness and specific gravity are not of any great importance. Melting Characteristics.-The melting or solidification range is important. This statement applies both to the extent of the range and to the actual temperature at which complete solidification occurs. A rather narrow solidification range is desirable in soft solders in order that solidification may take place quickly. The solder should have high fluidity at temperatures only slightly above its melting range. For a

Jan 1, 1928

By J. Chipman, J. C. Fulton

Reduction of silicon from blast-furnace-type slags by carbon-saturated iron is a very slow reaction even under conditions of rapid stirring. Equilibrium under atmospheric pressure of carbon monoxide was approached from both sides, and the silica-silicon relation was established at temperatures of 1425º to 1700°C for slags containing up to 20 pct Al2O3. Silicon carbide is formed by reaction of graphite with high silica slags and the conditions for its formation were determined. Activities of SiO2 and of CaO in their binary solutions at 1600°C were determined. The effects on the activity of SiO2 were established for additions of 10 to 20 pct AI2O3 and of 10 pct MgO. STUDIES of chemical reactions between blast-*>-5 furnace slags and metal have been focussed on the transfer of sulphur from metal to slag. The important role which silica reduction plays in this process' has led to a study of the transfer of silicon from slag to metal and the equilibrium represented by the equation SiO2 (in slag) + 2C (graphite) = Si + 2CO (g). [I.] The authors2 have published an account of the experimental method employed in attacking this problem and of three series of experimental results at 1600°C. This paper contains data on some additional compositions and extends the observations to cover the temperature range 1425° to 1700°C. The data are used to determine the activity of silica in the slags. As in the earlier experiments, the atmosphere was carbon monoxide which flowed through the furnace at 150 ml per min. In certain heats designated in the tables and figures, the gas was bubbled through the melt using a graphite tube. The latter increased in porosity during a run and in some cases bubbling ceased as indicated by cessation of surging. Some results were discarded for this reason. Experimental Results The new data are shown in Tables I through V and both old and new data are plotted in Figs. 1

Jan 1, 1955

By F. O. Garrabrant

Power is furnished to the Climax Molybdenum Co. by the Public Service Co. of Colorado over two 100,000-volt lines to a bank of three 3333-kva. transformers 100/13.8 kv. These transformers are so designed that with the addition of forced cooling their capacity may be increased 33? per cent at 12,000-ft. altitude. Under present conditions, these transformers are operated at 140 Per cent of their rating with forced air cooling. On the secondary side of this bank there is a 15-kv., 1200-amp. Westinghouse oil circuit breaker provided with automatic reclosing relays allowing three successive short circuits before lockout. From this breaker 13.8-kv. power is transmitted to a central switching station (Fig. I) where all circuits radiate to the different operations of the property. Each circuit is protected by a 23-kv., 600-amp. oil circuit breaker with by-pass and isolating disconnecting switches. Mine Power at 13.8 kv. enters the mine through a ventilation raise over a three-conductor, size 1-0 varnished cambric insulated, leaded, steel-wire armored cable, insulated from 17 kv. This power is received and distributed through one switching station and four underground substations, shown in Fig. 2. No. 370 substation (Fig. 3) contains three a 13,800/440-volt, single- phase Pyranol transformers protected on the high-voltage side by a 600-amp. manually operated oil circuit breaker. This station serves 20 slusher-hoist motors, a 45-kw., three-phase, 220-volt electric furnace, a Massco hot miller for tempering and milling Timken detachable bits and a hoist with 175-hp motor on the No, 3 development shaft. Also at this shaft are three pumps. One two-stage pump, 1200 gal, per min., 500-ft. head, 3600 r.p.m., driven by a 150-hp. motor, is at the bottom of the shaft, Two deep-well pumps, 500 gal. per min., 500-ft. head, are at the collar of the shaft. under normal operation the one pumping 1200 gal. per min, is controlled by a float switch to take care of the water. If this pump fails, or if its capacity is insufficient, the first 500-gal. pump is automatically started1 and if still more capacity is needed the second 500-gal. pump automatically starts. Time delay relays are provided on the deep-well pumps, so that if power fails the column will have time to drain before the Pumps restart. On failure of any Of these, an alarm is sounded in the train dispatcher's office, so that mechanics can be sent to ascertain the cause of failure and make repairs. The cable from No. 37' substation is run to the switching station, in which are four 15-kv., 600-amp. direct-current sole-noid-operated oil circuit breakers. The current for Operating and tripping is furnished by a 125-volt storage battery. All breakers are operated from the switchboard in the compressor room. One circuit from this switching station goes to the

Jan 1, 1946

By J. H. Swisher

The solubility of graphite in CaO-S2O2-Al,O3 slags was measured by equilibrating slag samples with graphite crucibles and CO gas. Carbon contents as high as 2 ut pct were obtained in CaO-saturated, CaO-A1,O3 slags, and 1.3 wt pct in slags of the composition CaO.Si0,. Although the observed conditions for Sic formation were in agreement with those predicted from thermodynamic data, CaC, was found to form at a lower temperature than predicted frotn thermodynamic data. From measurements of the equilibrium carbon content as a function of CO Partial pressure, it was found that carbide ions dissolve in CaO-A12O3 melts with a valence of minus two. The carbon content increased with CaO concentration in Ca0-Al,O3 melts and increased with SiO, content along the CaO'AlO3-CaOSi0 join in the ternary system. When solid CaC2 was added to CaO-A12O3 and CaO-SiO2-A12O3 slags, it was found that one of the oxides in the slag was reduced by the carbide (Al2O3 in the forrner and SiOz in the latter). In electric furnace steelmaking, a double-slag practice is frequently used to meet alloy specifications. Initially a flush slag, which is oxidizing in nature, is used to remove phosphorus and carbon from the steel bath. Later in the refining period, the flush slag is replaced by a highly reducing carbidic slag. When calcium carbide is formed in or added to a finishing slag, the slag is effective as a desulfurizing agent and also permits alloying elements such as chromium, vanadium, and tungsten to be added to the slag in the form of oxides. The oxides are readily reduced by calcium carbide, thereby minimizing the use of expensive ferroalloys. More work has been done on the thermodynamics of silicon carbide in slags than on calcium carbide. Baird and alor' and Kay and alor' determined the free energy of formation of Sic by measuring the partial pressure of CO in equilibrium with solid silica, silicon carbide, and graphite. Using a similar technique, they determined SiOz activities in CaO-SiOz and Ca0-Si0,-A1203 slags. Rein and chipman3 also determined the free energy of formation of Sic using slag-metal equilibrium measurements. A literature survey has uncovered only one experimental study of the behavior of CaC, in slag systems. Shanahan and cooke4 report the results of some preliminary experiments on the solubility and stability of CaC, in a CaO-A1,03 and a Ca0-Si0-A1,03 slag at a temperature of about 1500". The carbon solubility as CaC, in a slag containing 50 pct CaO and 50 pct A1203 was reported to be 0.6 pct. They also review earlier work on the binary CaO-CaC, system. A eutectic exists in this system, but various investigators disagree on the eutectic temperature and composition. eal has given an explanation for carbide furnace erruptions in terms of the thermodynamic properties of CaC,; his analysis is not based on experimental data, but on compiled data for the free energies of formation of CaC, and CO.' , These data for steel-making temperatures are all extrapolated from the results of low-temperature measurements. In the experiments described in this paper, slag samples were equilibrated with graphite crucibles and with mixtures of CO and argon or with CO gas at 1 atm total pressure for measurement of the carbon solubility. Most of the work was done on Ca0-A1203 binary slags, although in some experiments CaO-SiO, and Ca0-Si0,-A1,03 slags were used. EXPERIMENTAL Slag samples of the desired composition for the solubility measurements were obtained by blending pre-fused master slags. The master slags were prepared by fusing mixtures of reagent-grade CaC03 with either A1,03 or Si0, in a graphite crucible. The master slags were crushed, then decarburized in air in a muffle furnace at 1200O C. A schematic diagram of the apparatus is shown in Fig. 1. The source of carbon for the solubility meas-

Jan 1, 1969