Search Documents

By Gerhard Derge

The rapidity of oxygen steelmaking has created renewed interesl in the mechanisms and kinetics of the various processes involved. These studies can now be approached with increased confidence because of the more adequate thermodynamics, physical chernislry, and relevant engineering infornzation available. These combine to offer promise of useful control and automation if the details of each specific problem can be sufficiently well-defined. The hot filament microscope provides new insig-hi into many of these problems by direct observation at temperature, allowing the appraisal of the relative importance of thermal gradients, convection, and intermediate phases. All of these have a direct bearing on the overall rates and control of most pyrometallurgical processes. It is one of the special privileges of the Howe Lecturer to become better acquainted with this distinguished man. All of us interested in the metallurgy of iron and steel have developed some sense of his widespread influence by the annual reference to his work in these Memorial Lectures. Each lecturer since 1923 has been able to identify his personal specialty with the broad interests of Professor Howe. This has become even more rewarding with the background information from Professor Gensamer's monograph, "Henry Marion Howe's Contributions to Metallurgy, which brings out his happy combination of intellectual and professional activities. Beyond this, I found my personal bond with Professor Howe in his book on The Metallurgy of Sleel first published in 1891.' After a detailed discussion of the dephosphorizing action of slags, he relates the mineral species identified in the frozen sample to the chemistry of the fused slag with the question, "Is it not most philosophic to hold that these independent entities were wholly integrated in the initial magma; that their presence in it was wholly

Jan 1, 1968

William Metcalf, Pittsburg, Pa. (communication to the Secretary*): I am greatly pleased that some one has at last reached what I have long regarded as the only rational explanation yet given of the reasons why steel hardens. Mr. Field claims originality; and doubtless he is entitled to it, but not to priority, mhich must be granted to Prof. John W. Langley.' The difference between them is that Langley says " Tension, probably molecular," and Field says " Tension, probably atomic "; in either case the vital thing after solution is tension. Mr. Field's argument carries with it the idea of increase of density with hardness; if he mill study the facts farther he will observe that the case is just the reverse; that is, the greater the hardness the less the specific gravity; it was just this fact that led Langley to his conclusion, in mhich I have always concurred. Field agrees with Langley that the first requisite for perfect hardening is complete solution of the carbon, not combination; and all of the facts agree with this conclusion. The fact that increase of hardness causes reduction of density was first brought to my notice some 40 years ago, when Major William Wade was testing Jones & Laughlin's cold-rolled iron, and I mas his assistant. We found the well-known increase of tenacity, compressive strength, torsional resistance, and hardness. Specific-gravity tests showed that the cold-rolled iron was less dense than the hot-rolled bars. Major Wade was so surprised at this result that he gave me a lot of samples to weigh, saying that he was not satisfied with

Jan 1, 1904

By H. T. Clark, H. K. Work

The instrument for the rapid determination of carbon in steel, described in this paper, was developed originally to facilitate the operation of the pilot-sized open-hearth furnace in the Jones & Laughlin Research and Eevelopment Laboratory. In this small furnace, with its shallow bath, the drop in carbon is accelerated, and a rapid, reliable test for carbon content is indispensable. This problem becomes rather acute when it is desired to finish heats at a carbon content higher than can be estimated with any degree of accuracy by the fracture test. Several independent methods for determining carbon were investigated, therefore, and it was found that a relatively simple magnetic device could be made to give reproducible results. A laboratory instrument was designed and set up for the use of the furnace operators. It was tested exhaustively in the laboratory and was used with considerable success for following the carbon content in the furnace bath. As soon as sufficient data had been compiled to indicate that the instrument might have a wider application, a more rugged model was constructed and placed in the mill to be tested on commercial heats. Finally, about a year ago, instruments were furnished to the plant open-hearth shops, and these have been in use since that time. As a matter of convenience, the instrument has been named the "Carbanalyzer," and will be referred to by this designation in the following pages. $ Eaklier Investigations While by far the greatest number of magnetic investigations in which the carbon content of ferromagnetic materials was considered have had to do with the evaluation of the magnetic properties of steels of known

Jan 1, 1940

By H. K. Work, H. T. Clark

The instrument for the rapid determination of carbon in steel, described in this paper, was developed originally to facilitate the operation of the pilot-sized open-hearth furnace in the Jones & Laughlin Research and Eevelopment Laboratory. In this small furnace, with its shallow bath, the drop in carbon is accelerated, and a rapid, reliable test for carbon content is indispensable. This problem becomes rather acute when it is desired to finish heats at a carbon content higher than can be estimated with any degree of accuracy by the fracture test. Several independent methods for determining carbon were investigated, therefore, and it was found that a relatively simple magnetic device could be made to give reproducible results. A laboratory instrument was designed and set up for the use of the furnace operators. It was tested exhaustively in the laboratory and was used with considerable success for following the carbon content in the furnace bath. As soon as sufficient data had been compiled to indicate that the instrument might have a wider application, a more rugged model was constructed and placed in the mill to be tested on commercial heats. Finally, about a year ago, instruments were furnished to the plant open-hearth shops, and these have been in use since that time. As a matter of convenience, the instrument has been named the "Carbanalyzer," and will be referred to by this designation in the following pages. $ Eaklier Investigations While by far the greatest number of magnetic investigations in which the carbon content of ferromagnetic materials was considered have had to do with the evaluation of the magnetic properties of steels of known

Jan 1, 1940

By Noel Jarrett, Allen S. Russell, Bernard M. Starner, Stanley C. Jacobs

A process has been developed to refine high-grade commercial aluminum to 99.99 pct purity. This enzploys precipitating titanium, vanadium, and zirconiu~ as borides. The upgraded liquid is partially crystallized under conditions that prevent massive freezing. The resulting crystals are compacted and washed free of adhernig impure liquid aluminum by melting the top crystals while draining off the liquid. Finally, the bottorn portion of the crystal bed is melted and removed as the pure product. Leakage from the crystallizat~on vessel is prevented by a layer of alumina granules that are not wetted by the aluminum. ALUMINUM of 99.99 pct purity is desired in a variety of applications. These include electrolytic capacitors, catalyst carriers, decorative trim for automobiles, aluminum powder, and high-strength alloys. This market was for many years filled by refining commercial-purity aluminum in a three-liquid-layer electrolytic cell of the type originally proposed by Hoopes. To meet the expanding need for lower-cost high-purity aluminum, a refining process based on chemical precipitation and fractional crystallization was developed. The availability of this super-purity metal was announced in November 1961, and three patents1-3 relating to the process were issued in 1965. An alternate process, comprising continuous fractional crystallization of a portion of a liquid-aluminum feed stream under conditions of strong agitation at the surface of the growing crystals, was published by Dewey4 in 1965. Earlier proposals by Larsen 5 and by Regner6 also emphasized the advantage of rapid agitation of the melt in the region of the crystallization zone. johnson 7 more recently proposed extracting purified aluminum from an alloy by mixing crystals of pure aluminum into the molten alloy, allowing them to grow, and removing the pure aluminum as by casting. Aamot's 8 recent patent describes a freeze refining process that involves controlled partial freezing against cooled moving retort walls. The Alcoa process to produce high-purity aluminum is schematically described in Fig. 1. Relatively pure aluminum is treated with boron in a furnace (a) to precipitate high melting point impurities, the supernatant liquid is transferred to a crystallization vessel (b), the liquid is partially crystallized with mechanized "tamping" (c), the remaining impure liquid is tapped out and the crystal bed partially and directionally re-melted to wash the underlying crystals (d), and the balance of the crystals is melted and withdrawn as high-purity aluminum (e). PRINCIPLES OF FRACTIONAL CRYSTALLIZATION Commonly encountered impurity elements form two types of systems with aluminum. Titanium, vanadium, and some other transition elements in periodic groups IV, V, and VI are the high melting point impurities. Initial solidification of aluminum containing small percentages of these elements will produce solid markedly enriched in them at temperatures slightly above the freezing point of high-purity aluminum. Most other elements, such as silicon and iron, produce eutectic type reactions with aluminum. In this case the first solid formed on initial solidification at temperatures slightly below the freezing point for high-purity aluminum is markedly depleted while the remaining liquid is enriched in these elements. The equilibrium change in composition during solidification of aluminum contaminated with silicon, iron, or titanium is illustrated in Fig. 2. Here, for clarity, the temperature scale is expanded beyond the

Jan 1, 1968

By Dale A. Vaughan, Oliver M. Stewart, Charles M. Schwartz

A. U. Seybolt (General Electric Research Laboratory)—The authors should be commended for adding some important information to our knowledge of the solubility of interstitial elements in metals. It is becoming increasingly evident that the effect of even traces of such elements have very far-reaching effects upon the mechanical properties of the body centered cubic metals. Those who have worked in this area know that the accurate determination of the small solid solubility limits in systems of the type reported by the authors is a quite difficult task, and it is therefore not surprising that frequently the results of different workers are not in agreement. It is instructive, and usually helpful, to plot the solubility results on log weight or atomic percent -1/T coordinates to find out if a straight line is obtained. A straight line is expected because in systems displaying solubilities of the order of 1 to 3 at. pet or less, Henry's law is usually obeyed—or at least well enough obeyed so that the deviation from linearity is not very appreciable. If Henry's law is obeyed, one canthen use the Van't Hoff Equation in the form In N = ?H/RT + C, where N is mole fraction, at. pet, or wt pet for small values, and AH is the partial molal heat of solution of the solute. R and T have the usual significance, and C is an integration constant. If one plots the reported nitrogen solubility values as indicated above, the three points fall reasonably well on a straight line. The oxygen values for the two upper temperatures fall very closely to the nitrogen values as shown in the authors' Fig. 15. However, the value at 500°C departs widely from the straight line established by the data at 1500" and 1000°C. It is, of course, true that one cannot place too much emphasis on the significance of a line established by only three points, but in the absence of reasons for anticipating deviations, data exhibiting wide departures from linearity should at least be examined closely. Fig. 16 shows the log at. pct -1/T plots for the authors Ta-O and Ta-Ndata including a solid circle point at 500°C and 1.8 at. pet for Ta-O, which is simply extrapolated from the two higher temperature points. In addition, the data of R. P. Elliott9 for Nb-O are shown. These points were picked off his curve and are not very exact, but as can be seen they line up well on a straight line. It is interesting, and probably significant, that the slope of Elliott's results is not far from those of Vaughn, et al. This is probably to be expected because one would anticipate that the partial molal heats of solution of oxyten in these two very similar metals should be not too far apart. AH for Ta-O is about -1900 cal per mol, while for Nb-O it is near -2300 cal per mol. Hence, this lends some support to the thesis that the point at 500°C for Ta-O is much too high. The data of Gebhardt and Preisedanz10 are also plotted, and it is seen that their data while lying on a linear plot, have an appreciably steeper slope. The possible reasons for this will not be discussed here except to point out that their pressure-composition data show anomalies which suggest that they may have been dealing with a different equilibrium from that being discussed. There is another consideration which would also suggest that the solubility at 500°C is lower than shown. The solubility values were obtained by the classic method of first establishing a lattice parameter-composition curve. This the authors did, and there is probably little doubt that it is quite accurate. Such a plot is generally almost error-free because it has a self-correcting feature in that any deviation from linearity makes a data point immediately suspect, and subject to confirmation. Unfortunately, this is not true with respect to the actual solubility values. These are obtained ordinarily by taking an alloy containing more solute than is soluble at some temperature and then thermally

Jan 1, 1962

By R. J. Wagner, G. H. Gronhovd, A. J. Wittmier

The paper describes the results of a series of full-scale boiler tests run to determine the ash fouling characteristics of a North Dakota lignite as a function of sodium content of the coal. Four levels of sodium were investigated and rate of fouling was determined both by boiler performance and by specially constructed probe equipment. Discussed is information on chemical and physical properties of the ash deposits. The vast lignite deposits in North Dakota are becoming increasingly important as a source of low-cost fuel for power generation. A new 200-megawatt lignite-burning plant located near Stanton, N.D., was placed in operation early in 1966. Another 172-mega-watt unit in the same area is scheduled for operation late in 1966, and plans have recently been announced for a 212-megawatt unit to be in operation by 1970. If these plants show good performance, western North Dakota could become a major power production center for a large geographic area in the upper midwest. One of the problems associated with the use of lignite in power boilers is its tendency to form troublesome ash deposits on boiler tube surfaces. This problem varies considerably from one lignite-fired boiler to another and is dependent upon such factors as source of lignite, boiler design, load factor, tube metal temperatures, and soot-blowing practices. This report presents data on sodium content* variation in a North Dakota mine, describes the results of a series of tests performed to determine the relationship between ash fouling tendencies and the sodium content, and tells how the mining company and electric utility have coordinated their operations to reduce the ash fouling problem. GENERAL BACKGROUND Until recent years it was generally assumed that North Dakota lignite from a given mine had qualities peculiar to that mine, but that within the mine, the lignite was quite uniform. In 1959, the Otter Tail Power Co. installed a 53.5-megawatt lignite-burning unit at its Hoot Lake plant, Fergus Falls, Minn. Shortly after the unit was put into operation, it was noted that at certain times under high load conditions, ash fouling problems were quite severe, but not consistent or predictable. Each time fouling occurred in the unit the position of the loading shovel at the mine was noted. Within two years it became apparent that there were certain areas in the Knife River Coal Mining Co. mine at Beulah, N.D., where the lignite apparently had a high fouling tendency for the Hoot Lake unit. Results from analyses of the coal did not show large differences in moisture percentage, ash percentage, heating value, or ash fusion temperature between the highly troublesome and less troublesome coals. After three years of operation, the troublesome areas had been quite well defined and the mining company started a procedure of bypassing these areas when load conditions at the plant were high and then returning to the troublesome areas to load the lignite during the summer months when peak loads were lower. It was noted that the lignite from the areas which caused severe fouling under high load conditions produced much less fouling at the lower summer loads. However, bypassing certain areas in the strip pit caused the mining company to disrupt their continuous loading schedule, which in turn upset their continuous stripping schedule and made for less efficient mining operation. Meanwhile, at the Hoot Lake plant, the number of soot blowers on No. 2 boiler had been increased from 30 to 55, and a very rigorous blowing schedule had been adopted resulting in soot blowers operating at least some part of 21 hrs per day. Fouling problems continued, with a resulting reduction in plant economy and reliability. During this period the Federal Bureau of Mines Coal Research Laboratory at Grand Forks, N.D., had initiated various research programs relating to the study of lignite ash and ash fouling problems. One project was a survey in which full seam samples were obtained from various locations in all the major

Jan 1, 1968

By Allan J. Clark

It may be said that the history of gold in the Black Hills begins with one of South Dakota's most. interesting relics, the so-called Thoen Stone, now in the Adams Memorial Hall at Deadwood. This slab of reddish sandstone, about 14 in. square, was found in by Louis and Ivan Thoen, at the base of Lookout Mountain, near Spearfish, a town in the northern foothills of the Black Hills uplift. Both sides of the stone bear clearly legible inscriptions. One side reads: Came to these hills in 1833. Seven of us, De Lacompt, Ezra Kind, G. W. Wood, T. Brown, R. Kent, Wm. King, Indian Crow. All ded but me, Ezra Kind. Killed by Indians beyond the high hills. Got our gold June 1834. On the reverse side: Got all the gold we could carry. Our ponys all got by the Indians. I hav lost iny gun and nothing to eat, and Indians hunting me. Attempts were made to trace these men. Relatives of Brown were found in Missouri, and it was learned that he had left for the West in 1832, with one Kent. Kind's relatives were also found, and stated that he had started West the same year. None of them had been heard from since their departure. So Kind failed to get out with "all the gold we could carry"; 15 years later California became the center of the first great gold rush, and the Hills waited 40 years for their gold to be rediscovered. It is interesting to speculate on what might have been "the course of Empire" had this little group won through. The history of Dakota, of Montana, indeed, of all the Northwest, might have been very different. When, late in 1875, the goldseekers arrived, they passed quickly northward from the first discovery near Custer, and soon were established on Deadwood Creek, along which, as well as for short distances above the mouths of its tributary streams, Blacktail and Bobtail, placer operations went forward vigorously. These placers were near the northern outcrop of the Homestake ore-body. Their gold was partly derived from this, perhaps in greater quantity from the erosion of the conglomerate or cement deposits, of Potsdam time, themselves a "fossil placer" or beach deposit formed by

Jan 1, 1935

By Charles M. Packer, Oleg D. Sherby, Roy H. Johnson

Originally round tensile specimens of a eutectic Zn-A1 alloy develop elliptical cross sections during superplastic deformation. This observation, coupled with a detailed study of the microstructure and preferred orieniation, suggests that crystallographic slip and continuous grain boundary migration or re-crystallization are important processes during super-plastic deformation. In spite of the extensive activity in superplasticity1-15 and the numerous explanations proposed, no single model has had universal acceptance. It has been established, however, that the general requirements for superplastic extension of two-phase alloys include an extremely fine, stabilized grain size of the order of a few microns, a temperature about equal to or greater than one-half the melting point, a critical range of strain rate, and a similarity in the mechanical strength of the major phases. The proposed models can perhaps best be characterized in terms of the important phenomena associated with them. These phenomena include: phase instability,1 diffusional creep by volume diffusion3 or grain boundary diffusion4,5 slip and continuous grain boundary migration or recrystalliza-tion,= grain boundary Sliding,7-9,13,14 and dislocation glide.'5 In this paper, experimental observations will be reported which support a model involving slip and continuous grain boundary migration or recrystalliza-tion. Specifically, a correlation will be made between this model and the development of elliptical cross sections as originally round specimens are superplas-tically deformed. For the most part, superplasticity studies have been conducted with eutectic or eutectoid alloys. Probably the most thoroughly studied material has been the monotectoid Zn-A1 alloy.1,2,6,12,13,15 No attention to the eutectic Zn-A1 alloy has previously been reported, and the results discussed in this paper represent part of a general study of the superplastic properties of this alloy. MATERIALS The alloys used in this investigation were prepared by melting appropriate quantities of 99.99+ pct A1 and 99.999 pct Zn in air, mixing, and pouring into a water- cooled stainless-steel mold. Wet-chemical analysis was conducted with each heat of alloy prepared, using the procedure of Fish and smith.16 The composition of the eutectic alloy was 95.1 wt pct Zn. Ingots about 2 in. thick were rolled to 0.4-in. plate at about 300°C with a reduction of 5 to 10 pct per pass. Specimens were machined from the plate with the tensile axis parallel to the rolling direction. The specimens were round, with 0.150-in.-diam, 1.25-in.-long gage length, and 0.25-in.-diam threaded grip sections. EXPERIMENTAL PROCEDURE Specimens were mounted inside a uniform-temperature quartz tube which was surrounded by a double elliptical radiant furnace with a 12-in.-long uniform-temperature hot zone and a low thermal capacity. The tube extended through the top and bottom of the furnace and permitted rapid quenching of the loaded specimens when quickly filled with cold water at the conclusion of the test. The quench precluded any effects on specimen microstructure from a normal, slow cool. Constant stress was applied to test specimens by suspending a load on a constant stress cam of the type described by Hopkin.17 The design of this cam permitted application of a constant stress for elongations up to 200 pct. For greater elongation, approximately constant stress conditions were maintained by systematically reducing the load manually. RESULTS As part of an investigation of the superplastic properties of the eutectic Zn-A1 alloy, evidence was obtained for the development of elliptically shaped cross sections as originally round specimens were extended. For example, after an elongation of about 100 pct, a round specimen with an initial diameter of 0.150 in. became elliptical with major and minor axis of 0.128 and 0.88 in., respectively. Photographs are presented to illustrate the ellipticity developed during superplastic deformation, Fig. 1. The specimen shown was deformed at a stress of 500 psi, at a temperature of 285°C, and a strain rate of 2.28 x 10-2 min-1. The strain-rate sensitivity exponent* was measured at *The strain-rate sensitivity exponent, m, is defined as d In o/d In c where o is the steady-state flow stress and E is the strain rate. this temperature and in the strain rate range 10"3 to 10-1 min-1 was found to be about 0.5. This value is typical of those observed with superplastic materials. The material studied exhibited negligible strain hardening during superplastic deformation, the creep rate remaining constant under constant stress and temper-

Jan 1, 1969

By J. Suiter, H. F. Ryan

H. F. Ryan and J. Suiter (CSIRO)—In this paper the authors have presented "a physical model which has as its central hypothesis the solution strengthening of regions along grain boundaries in the order of tens of angstroms thick", and their calculations have used 40Å as the zhalf-width of this boundary region. Selection of this value by the authors suggests that they were unaware of a number of recent field-ion microscope observations of grain boundary structures (e.g., Refs. 29 and 30). The accompanying figure, Fig. 9, shows a portion of an ion micrograph of a tungsten specimen containing a grain boundary, and the regular arrangement of atoms in various crystal planes in each grain can be seen, except in the boundary zone which is not more than two atom diameters in width. Since it is expected that solute atoms will segregate only to the region where the lattice is disturbed, it would seem that a value of 4Å for the half-width of the boundary region would be more appropriate than the value of 40Å assumed by the authors. If the former value is used in Eq. [8] of their paper to obtain curves showing solute concentration in the grain boundary as a function of temperature, the resulting curves differ significantly from those obtained by the authors. Although there are only relatively slight changes in the regions corresponding to higher temperatures (i.e., grain boundary concentrations of approximately 1 at. pet), at lower temperatures the curves are no longer realistic. For example, the curve corresponding to u = 7000 cal per mole gives a solute grain boundary concentration in excess of 100 pet at a temperature of approximately 360°K, and "flattens out" at a grain boundary concentration of about 300 pet! Similar results are obtained with each of the other curves. Ion microscopy of dilute solid-solution alloys has shown that solute atoms give rise to image points which in most cases are of higher intensity than those of the solvent atoms.31 If the same behavior occurs when the solute atoms are present in much lower concentrations then ion microscopy should provide a sensitive tool for studying the segregation of impurities to the grain boundary regions. Although many grain boundaries in tungsten have been examined after different thermal and mechanical treatments, there has not been, as yet, any systematic study of such segregation. In general the micrographs show no clear indications of marked grain boundary segregation, but occasionally areas are found where the grain boundary contains an appreciable number of image points of high intensity in a very narrow zone, see Fig. 9. If it is assumed that these correspond to impurity atoms then it is possible to estimate the impurity concentration both in the grain boundary and within the body of the grains. Application of this method (to a larger area

Jan 1, 1965

By R. M. Goldhoff, H. J. Beattie

The high-temperature properties of a 1 Cr-Mo-V forging steel are described. A series of controlled heat treatments was designed to delineate the effects of austenitizing and tempering treatments, temile strength, and grain size on such properties. Studies indicate that the mechanical properties and their varlations under creep can be described by the initial metallurgical structures and their changes droPirzg exposure, particulavly the carbide reactions. Such structures are described and correlated with the mechanical properties. FOR many years the large steam turbine industry has relied on the 1 Cr-Mo-V type forging steel for critical applications. Because of its adequate heat resistance and relative economy, it is currently in use in the temperature range up to about 1050" to 1075°F. Attempts to understand the large property variations attainable in this steel involve the structural modifications due to the wide latitude in its heat treatment. The heat treatment essentially involves a two-step process which includes solution-ing of carbides in the austenite range followed by a suitable tempering treatment below the critical to adjust the level of properties. The latter step is referred to as "secondary hardening" and is basically an ordinary aging reaction involving carbides. In the commercial heat treatment of large components of such steel, homogenizing and stress-relief anneals may be included and have some importance in determining subsequent properties. Several studies of the engineering properties of this steel as a function of transformation micro-structure have been reported.1 3 However, in this steel the carbide reactions, which are a function of composition and heat treatment, appear to be the property-controlling factor rather than the micro-structure defined as a transformation product. Thus, the tempering resistance of this type of alloy steel is mainly a function of the size and distribution of alloy carbides.4 However, it is also necessary to consider the stability of the microstructure and the effect of dynamic carbide reactions on subsequent properties. It is the purpose of this paper to show the interdependence of properties and corresponding structures, particularly carbide reactions, developed for a limited set of controlled heat-treatment conditions applied to 1 Cr-Mo-V steel. MATERIALS AND PROCEDURE The material for this work came from a large production forging whose chemical composition is shown in Table I. The property data accumulated on this steel as a function of heat treatment were room-temperature tensile and smooth- and notch-bar creep rupture at 1050°F (notch geometry: shank diameter = 0.357 in., depth = 50 pct, radius = 0.005 in.). To achieve controlled structural variations the temperature and time of both austenitizing and tempering were varied in a manner to produce a series of eight steels each at one of two grain sizes and one of two hardness levels in proper combination for valid comparisons. This will be clear upon examination of Table I. Structural studies involved the use of optical and electron microscopy as well as X-ray and selected-area electron diffraction. To reveal the nature of carbide precipitations, electrolytic extraction techniques were used with subsequent analysis of the residue by X-ray diffraction. Weight losses of the steel specimens during electrolysis were measured and successive chemical fractionations of the residues were applied and checked by X-ray examination. The details of fine structural distributions, morphologies, and crystallography of the precipitates as well as dislocation distributions were investigated by examining in the electron microscope three common types of preparation. a) Relief Replicas. Mechanically polished sections were etched in 2 pct nital, replicated with a nitrocellulose film, which was shadowed by chromium vapor deposited at a glancing angle of 20 deg. b) Extraction Replicas. A thin film of carbon was vapor-deposited on the polished and etched surface. The carbon films were then etched off and gathered on electron-microscope supporting grids. The carbides left imbedded in the carbon replica in their original distribution were then examined crystallo-graphically by selected-area electron diffraction. c) Thin Films. Specimens were mechanically ground and polished down to a thickness of 0.001 to 0.003 in. Final thinning was done electrolytically in a "chrome-acetic" electrolyte. When holes began to appear in the foil, the voltage was interrupted and applied in several 1-sec bursts. Sections of the foil between holes were thin enough to pass a 100-kv electron beam that carries an image.

Jan 1, 1965

By C. Feng, P. Levesque

HE addition of rhenium to molybdenum is known to produce alloys with good workability.&apos; Lawley and Maddin found that the critical stress for twinning in this system was lowered by the addition of 35 pct Re, which suggests that twinning may re- place the usual slip operation as the major element of deformation. The twinning elements in bcc Mo-Re alloys have been reported as the (112) planes and the <111> directions.3 This note represents the continuation of this investigation, in which the authors found that the occurrence of twinning promotes the formation of a bcc tetragonal phase, previously identified as u by Greenfield and Beck.4 Specimens of Mo-35 pct Re alloy, prepared as described previusly, were solution annealed at 2400o, cooled to room temperature, and plastically deformed by compression to induce twinning. After subsequent aging for 8 hr at 1300°C, traces of a were observed along the grain boundaries and at the interfaces between the twins and the matrix, Fig. 1. With increased aging time the cr phase grew into larger clusters and finally occupied the entire twinned area, Fig. 2. Experiments also indicated that if twinning did not precede aging, there was no visible evidence of a in the microstructure.

Jan 1, 1962

By James G. Crawford

Correlation Of water with its reservoir zone or formation has been one of the applications of oil-field water analysis of greatest direct value to the petroleum engineer. The water in each producing zone tends to have diagnostic characteristics by which it can be distinguished from every other water above or below that zone in that immediate vicinity. Representative analyses of oil-field waters from producing oil and gas fields in the Rocky Mountain region are included, and the diagnostic characteristics are discussed briefly. It is concluded that the generally dilute nature of Rocky Mountain oilfield waters is a result of dilution by meteoric waters, and that there is no relationship between presence or absence of commercial oil and the character of water in a structure. Introduction The study of waters associated With oil and gas began more than 50 years ago and has been well recognized by operators, engineers, and geologists for about 30 years. It appears unnecessary at this time to recite the history of oil-field water analysis; suffice to say that it has proved its worth many times to the production engineer suddenly confronted with water problems in producing oil and gas wells. Chemists and geologists have studied the possible origin of these waters and as Yet the subject is unsolved in many important phases. There are both local and regional problems connected with the explanation of concentrations and character- istics peculiar to each field, each subsurface zone and each province. Criteria useful in postulating the Occurrence of oil Or gas in One province completely fail when applied to another, and data carefully prepared and analyzed from one field may be actually misleading when applied to another. Correlation of water with its reservoir zone or formation has been one of the applications of oil-field water analysis of greatest direct value to the engineer. The concentrations and characteristics of the waters are essential to the engineers and geologists making interpretations of electric logs in this region. The behavior of water under conditions of reservoir temperature and pressure is dependent to a great degree upon its concentration and characteristics, and thus important to the reservoir engineer. With the advent of secondary recovery methods in the Rocky Mountain region the characteristics and treatment of water will become increasingly important. Premises upon which Correlation Is Based A brief review of the geochemical history of oil-field waters will suffice to present the premises upon which correlations of the waters are based. Sedimentary rocks which are now stratified were first sediments in seas, lakes and streams. These sediments were filled interstitially with connate water. With burial the sediments were compressed arid consolidated, integrated and indurated into bed rock and much of the connate water was dispelled. Following the formation of bed rock the strata were sub-

Jan 1, 1949

By P. S. Rudman

Crystal-structure occurrences in binary phase diagrams of fifth- and sixth-period elements, zirconium through palladium and hafniun through platinum, are surveyed with the conclusion that average .group number GN is the dominant correlative. This is interpreted in terms of curves of enthalpy differences between competitiue structures that are continuous func -tions of GN. It is further reasoned that the absolute formation energies may also be continuous functions of GN and if so can be simply obtained from the regatives of the heats of sublimation of the elements. It is shown that from such a heat of formation-GN plot the heats of mixing of alloy systems can be quantitatively predicted. For example, for sixth-period alloys very large exothermic heats of mixing are predicted for systems that span GN = 6 (i.e., Hf-Pt, Ta-Os, ...). Thermodynamic data with which to test these predictions do not appear to be available. If in the latter transition (A subgroup) elements we eliminate from consideration the fourth period where magnetic terms contribute to crystal-structure stability, as shown in Table I, there is a very regular sequence of structures. Using the group number (GN) assignments of Table I, which differ from the usual assignments of 8 to the elements listed as 8 through 10, it is perhaps trivial to say that the phase occurrence is a unique function of GN. However, the interesting aspect of alloys from among these elements is that the alloy structures also appear to correlate with GN. The GN for an alloy is given as GN = SixiGNi, where xi and GNi = atomic fraction and GN of component i, respectively. It is difficult to credit anyone in particular with having discovered this correlation, so many people have implicitly or explicitly employed it in the last 10 years. However, Bloom and Grant&apos; in their correlation of s-phase occurrence with total number of d + s electrons were certainly one of the first to appreciate the correlation and Hume -Rothery2 appears to be responsible for the use of average GN as defined above. Only in the last few years have the phase diagrams of enough alloy systems been determined for this correlation to be surveyed with any degree of completeness. We shall here, in an abbreviated format, summarize the available phase-diagram literature and discuss some consequences of the GN correlation. BINARY DIAGRAM SURVEY In Figs. 1 to 3 the phase occurrences are summarized. In Fig. 4 the occurrence limits for the more common structures are summarized. That the GN of an alloy falls within the occurrence limits of a particular structure is a necessary but not a sufficient condition for the appearance of that structure. The preceding figures certainly illustrate that GN is a dominant correlative for structures of these elements. Many of the diagrams have complications, with ordering and other phase changes occurring in intermediate phases, that cannot be clearly accommodated in such a schematic survey and have hence been left out. Such omissions cannot, however, negate the GN correlations discussed here. Relative atomic size is also an important crystal-structure determinant and since atomic size varies quite regularly with GN for these elements it is possible that the apparent GN correlation is basically a size correlation. In Fig. 5 relative size occurrence limits are given for intermediate phases and extended terminal solutions. The relative volume, ?v/(v) - 2(vA - vB)/(vA + uB), has been taken as the measure

Jan 1, 1968

By J. J. Lander, L. H. Germer

MOLYBDENUM and tungsten have desirable corrosion and temperature resistant properties, but the metals in bulk are expensive and their fabrication is difficult. Such considerations led to a search for a method of plating them upon base metals. This search was successful and led furthermore to a number of developments which could not have been foreseen. Neither pure tungsten nor pure molybdenum has been electroplated successfully, although the literature of electroplating is liberally sprinkled with the description of unsuccessful attempts. The process of plating these metals by thermal reduction of their halides has achieved only limited usefulness because of technical limitations and because of limited range of product quality. Plating by thermal decomposition of the carbonyls does not suffer from limitations of the same sort and the properties of the plate are readily controllable. This paper describes the plating of molybdenum and tungsten, and of compounds and alloys of these metals, by pyrolysis of their carbonyl vapors. Chromium also has been plated in this manner, but the experiments upon chromium have been less extensive and the results much less satisfactory. Probably the most important of the products which we have obtained are the alloys with carbon, and the carbides of the metals. Either molybdenum or tungsten can be deposited upon a base metal as a coherent and adherent coating. By adjusting the plating condition the carbon content of the coating can be made to have any value from substantially zero to about 35 atomic pct. The hardness is dependent primarily upon the amount of carbon in the plate and can be regulated over a very wide range, some coatings containing considerable carbon being harder than sapphire. In addition to products already known this method of plating has yielded new carbides of molybdenum and tungsten and alloys supersaturated with carbon. These new products are possible because, in the process of plating, carbonyl can be decomposed at temperatures as low as about 150&apos;C, and thus in the presence of other substances reactions occur which could perhaps not be produced in any other way. In addition to carbides and alloys with carbon, sulphides and oxides of molybdenum and tungsten have been produced and studied. There are certain other advantages of the carbonyl method of plating. It is not required that the base have good electrical conductivity as in electrochemical processes, and the base need not have the temperature stability required in plating from a halide. Thus low melting glasses, as well as other ceramics, can be plated almost as readily as metals. In particular, the plating of glass with

Jan 1, 1947

By H. R. Peiffer

Recently artin has indicated that the recovery of resistivity at 145°C following elongation of molybdenum at room temperature was the result of the annihilation of vacancies. The activation energy for this process was, according to Martin, 1.26 ev. This energy seems to be a reasonable one for the activation energy for the diffusion of vacancies in molybdenum. However, impurity atoms such as carbon, nitrogen, and oxygen4 have an activation energy for diffusion in molybdenum of the same order of magnitude (i.e., 1.45, 1.15, and 2.09 ev, respectively). Cottrell and Churchman have already correlated the return of impurity atoms to dislocations in cold-worked iron with the return of the upper and lower yield point. According to cottrel16 the diffusion of carbon atoms to dislocations results in the return of the yield point. As the carbon atoms become trapped by dislocations, Bhatia has shown that a decrease in the electrical resistivity is to be expected. Cottrell and Churchman were able to correlate experimentally the decrease in electrical resistivity with the return of the yield point. Since one would expect strain aging to occur in molybdenum, an experiment was performed to determine whether the resistivity recovery at 150°C for molybdenum cold-worked at room temperature can be correlated with the return of an upper and lower yield point. For this experiment 3/16-in. tensile bars of Climax molybdenum, 99.961 pct pure, were used. The specimens were annealed at 1000° C for 1 hr in an argon atmosphere and then were elongated up to 10 pct on a Baldwin-Lima-Hamilton FGT

Jan 1, 1959

By Klaus Detert

Fifteen and 18 pct Ni maraging steel and several binavy and ternary alloys of the iron-rich corner of the Fe-Co-Ni system have been studied. After annealing in the austenite range, these alloys were deformed slightly by cold rolling and subsequently aged. Compavison of experimental measurements at various processing stages indicates that small degrees of deforn~ation (5 to 10 pct reduction in thickness) do not influence hardness and strength or the aging kinetics. Electrical resistivity and ductility are somewhat redu]ced and the coercive force is substantially lower when compared to identical samples which were not deformed. The results are explained in terms of retained austenite which transforms into martensite with the small amount of deformation. RECENTLY there has been increasing interest in maraging steel for applications in electric power generators requiring a high ratio of power to weight.&apos; Fifteen pct Ni maraging steel has been investigated to evaluate its properties and performance for application as high-strength magnetic rotor steel,&apos; and a thorough investigation of the precipitation and transformation processes in this alloy has been conducted in this laboratory.3 The influence of deformation, which preceded the aging treatment, was also studied. It was found that a small deformation in the order of 5 pct has a rather striking effect in reducing the coercive force. Other interesting effects on the properties caused by such deformation have led to the more detailed studies reported herein. EXPERIMENTAL METHOD The methods used to produce the samples from 15 pct Ni maraging steel have been described elsewhere.3 The general procedure of hot forging and cold rolling to sheet has been followed. The composition is included in Table I which also contains the composition of the 18 pct Ni maraging steel grade 250 studied. More data about the material and the processing of the 18 pct Ni maraging steel have been recently reported.4 The experimental alloys of binary and ternary Fe-Ni-Co alloys were made by levitation melting in an argon atmosphere and casting into rod-shaped ingots 7 mm thick weighing 20 g. From these ingots 25-mm-long rods were machined to study the phase transformation by a dilatometer. These rods were then cold-rolled to strips, 2.4 mm thick. Annealing for austenitizing was done in tube furnaces in an argon or helium atmosphere followed by cooling in the water-cooled portion of the tube. Aging was done in a salt bath containing a neutral blend of Alkali nitrates and nitrites. Vickers hardness was measured using a load of 50 kg for 15 sec. Tensile tests were carried out on a hard beam tensile tester at a strain rate of 5 X lo-&apos; per sec using flat samples with a gage length of 37.5 mm and a cross section of 1.25 by 6.25 mm. Estimated sensitivity was 5 K x strain and 0.35 kg per sq mm stress. Magnetic saturation was determined on small cylindrical samples, 2.5 mm in length and diameter, by measuring the force exerted by the gradient of a magnetic field of 1000 oe per cm in a mean field of 11,500 oe. The measured values could be reproduced within *1 pct. Coercive force was measured by a precision-type magnetic field probe in a magnetic coil as described by Foerster.5 The magnetizing field was 1300 oe. The samples were 5 cm long, 1 cm wide, and 2.4 mm thick. he coercive force was measured to within +0.1 oe. Electrical resistivity was measured by using a potentiometer on flat strips with a gage length of 100 mm and a cross section of 2.5 by 0.5 mm. The accuracy of the measurement was 0.1 pct but the reproducibility of the measured specific resistivity among different samples was in the order of 1 pct. The method used to prepare the samples for electron transmission has been reported elsewhere.3 RESULTS Fig. 1 shows the influence of deformation after annealing on the resistivity, hardness, and coercivity. The samples were annealed for 30 min at 1000"C,

Jan 1, 1968

By J. S. Kirkaldy, R. J. Brigham

AS part of a program to investigate the diffusive properties of dilute ternary austenites we have made a determination of the effect of chromium on the activity of carbon in ? iron. Samples of pure iron and Fe-Cr alloys were simultaneously equilibrated at 1000°C with atmospheres of controlled CO/CO2 ratio following the procedures of Darken and Gurry 1 and smith.&apos; The 0.020 in. thick samples were analysed for carbon by microcombustion analyses3 to yield a set of isoacti-vity curves. The latter were converted to activity coefficient (standard state at infinite dilution) plots by combination with Smith&apos;s data2 for the activity of carbon in pure iron. Table I shows the compositions of the base alloys used while Fig. 1 shows the experimental results superimposed on a set of curves generated by the relation In?C=6.9NC- 10.7 Ne In the notation of wagner4 the interaction parameter is the second coefficient on the right, Sgr = - 10.7 This can be compared with a rather inaccurate value deduced from the transient equilibrium diffusion data of Kirkaldy et al.&apos; as The authors are indebted to the American Iron and Steel Institute for financial support. This material is condensed from a B.Sc. Thesis submitted to Mc-Master University by R.J.B.

Jan 1, 1963

By P. R. Kalischer

In the production of alloys by powder metallurgical processes it is often necessary or desirable to include one or more cornponents that tend to form very stable oxides. Included in this group of metals are aluminum, manganese, magnesium, silicon, and a few others. In many cases it is not necessary for the sintered compact to have full density and the other physical characteristics of a cast alloy and in that event no undue precautions need be taken. If, however, it is required that the sintered part be entirely homogeneous, and have maximum density and physical properties, some method must be found to reduce the surface films of oxide, which are always present on the metals, and for the metals mentioned above this is always extremely difficult, if not impossible. since the production of high-density alloys is of particular interest to powder metallurgists, some experiments were undertaken to devise methods of reducing the refractory oxides. For this work, alloys of iron, nickel, and aluminum were chosen because aluminum oxide is one of the most stable oxides and because these alloys in the right compositions form excellent permanent magnets. All of the pertinent properties of the magnets could be accurately and delicately measured by density measuremerits and magnetic tests of sufficient scope to give a complete demagnetization curve. From such a curve the maximum coercive force, residual magnetism, and energy products could be obtained and compared with the same properties for a cast material. Any lack of homogeneity, density, or solid diffusion would be immediately apparent as a decrease in the magnetic properties. Nature and Removal of Surface Barriers The early work of the present investigation was based upon published processes.* In the published information it was claimed that by intimately mixing iron, nickel, and iron-aluminum alloy (50 Per cent Fe, So Per cent Al) powders, compressing such a mixture into the desired shape and size, and then sintering (heating to a temperature below the melting point of the component metals) in hydrogen at 1200°C. or higher, a sound, homogeneous article could be made having the desired physical size, shape, and strength, and good magnetic characteristics. However. this early work showed clearly that something in the powder compress was inhibiting diffusion and the process was almost entirely unworkable. In the initial phase of the investigation samples of iron powder, nickel powder, and iron-aluminum alloy powder were pressed into separate bars and sintered in hydrogen. Both the iron and nickel powders sintered

Jan 1, 1941

By R. B. Adamson

The fatigue behauior of irradiated copper single crystals is compared to that of unirradiated crystals. Proton or electron irradiation did not substantially change the fatigue-lzj.e, fatigue-hardening-, or slip-line characteristics, while neutron irradiation did appear to alter these parameters. Postfatigue transrrzission electron microscopy did not reveal any marked structural differazces between irradiated and unirradiated specimens. Possible dislocatio~a mechanisnzs to explain the observed behavior are discussed. A LTHOUGH considerable work has been done to ascertain the effects of radiation on the tensile properties of metals (e.g., Refs. 1 and 2), little work of a basic nature has been reported on the effect of radiation on fatigue properties. Since it is known that fatigue properties are sensitive to conditions at the surface of the metal, it was felt that charged particle irradiation, whose penetration into metals is very small, might influence the fatigue behavior. To investigate this surface effect, irradiations with 10 mev protons and 1.5 mev electrons were conducted. The range of 10 mev protons in copper is about 0.236 mm; which is very small compared with the thickness of the specimens used (1.53 mm). The range of 1.5 mev electrons is somewhat larger, on the order of 0.665 mm.4 On the other hand, irradiation with reactor neutrons produces damage throughout the entire specimen, so neutron irradiation can be used to study the effects of bulk damage. The damage introduced by proton and neutron irradiation is expected to con!ist of large interstitial dislocation loops,5 tiny (<25A) vacancy loops," and/or various vacancy-rich regions called depleted zones.&apos; In the case of electron irradiation at about -173°C the damage is expected to consist of isolated Frenkel pairs.&apos; The effect of radiation damage on the fatigue properties of some engineering materials has been reported,g,10 but the results are not clear-cut or consistent. SPECIMEN PREPARATION Zone-refined copper was used to grow single crystals by a modified Bridgeman technique in an inert helium atmosphere. Using a seeding method, single crystals were obtained as bars about 6 in. long with a cross section of 3 by $ in. Immediately upon removal from the split-mold graphite boat in which they were grown, the very soft bars were embedded in a room-temperature setting plastic. They could then be cut into specimen lengths without introducing any long-range damage. Generally, four or five specimens plus one seed were obtained from each bar. The plastic material was dissolved away in acetone and the orientation of each sample was checked by the standard Laue X-ray

Jan 1, 1968