Search Documents

By L. K. Jetter, C. J. McHargue

The use of axis charts for representing the texture of cold-rolled thorium sheet was compared with conventional pole figures. Four texture components were deduced from the axis charts and shown to be consistent with the pole figures. It was shown that consideration of the pole figures alone could lead to an apparent component which is the average of two actually present. It was also shown that the spread about the "ideal" textures and the amount of material associated with each could be readily obtained Fom the axis chart method. BECAUSE of the crystallographic nature of the deformation mechanisms in metals, plastic flow results in the alignment of certain crystallographic directions with the primary flow directions. In the study of the "preferred orientation" thus developed, one wishes to discern the distribution of the crystallographic directions with respect to some reference direction, usually a direction related to the fabrication procedure, such as the rolling direction. The pole-figure method, introduced by ever,' involves the plotting of the distribution of the poles of some family of planes on a stereographic projection which places the reference direction(s) at the north pole and/or in the center. By noting the angles between the reference directions and concentrations of poles on several such pole figures, one can deduce the crystallographic directions which are aligned with the reference directions. If the preferred orientation is relatively simple and well-developed, one to three pole figures may be sufficient for obtaining the desired information; if there are several texture components, more pole figures may be needed. A significant improvement in the method of representing the textures in wires and rods resulted from the introduction of the "inverse pole figure" or axis-distribution chart by Harris.2 Such a chart gives directly the distribution of the reference axis relative to the standard stereographic projection. There has been widespread acceptance of this method for the representation of fiber textures, and methods have been proposed for converting observed diffraction intensities into axis densities.2-6 The suggestion by Mitchell and Rowland3 and Jetter, McHargue, and williams5 that sheet textures could be represented as distributions of rolling, normal, and transverse directions have been criticized on the basis that they offer no significant advantage over a combination of two ordinary pole figures and that it has not been proved that sheet textures can be treated as quasi fiber textures.6 If the purpose of a texture determination is to study some property which is related to the orientation of a particular crystallographic plane or direction, then conventional pole figures certainly are sufficient. For example, the distribution of the slip planes in face-centered cubic metals (the (111) pole figure) serves to indicate the variation in mechanical properties of sheet. On the other hand if the study is directed at an understanding of the factors influencing texture formation, it is desirable to know not only the preferred orientation but the kind and degree of spread from it and the relative amounts of material in each component, if there are more than one. Axis charts give this information as well as the orientation distributions. Consider the procedure for deducing a texture component from a pole figure for the (111) planes

Jan 1, 1961

By O. E. Palasvirta

Close examination of most so-called n.eu processes in mineral dressing reveals that they were conceived and developed a long time ago. High-intensity magnetic separation is no exception. Although its application in iron ore beneficiation seems new, in Germany the process has been commercially successful for almost two decades. High-intensity separators have long been standard equipment in the glass sand industry; they have also been used in concentrating some of the more unusual para-magnetic minerals. The basic features of an induced-rotor, high-intensity magnetic separator were described by Desire Korda in Paris in 1905,' and many patents have since been issued for improvements on the original design. Fig. 1 shows the basic design of an induced-rotor separator. Several U. S. manufacturers have been supplying induced-rotor separators for many years, but these are all devices of relatively low capacity, not suitable for treating such low-cost commodities as iron ore. On the other hand, two German manufacturers are offering induced-rotor separators of high capacity, both proven in the field. The present investigation was prompted by the apparent success of the German installations and by the discovery of iron ores on this continent which may be amenable to high-intensity separation. The objective was to gain better insight into the underlying principles of separation in a high-intensity field and to use this knowledge in selecting or designing an optimum separator. THEORETICAL CONSIDERATIONS he well known low-intensity magnetic separators are. without exception, of the the magnet type with more or less similar field shapes. It is therefore permissible to speak of their comparative strengths in terms of field intensity alone. However, proper understanding of the high-intensity magnetic separation process requires somewhat deeper analysis of the relationship between the magnetic field and the attractive force. Contrary to a widely held belief, a magnetic field of parallel lines of flux exerts no attractive force on a magnetically susceptible particle, but merely aligns its poles parallel to the lines of flux. On the other hand, a non-uniform field attracts a magnetically susceptible particle in the direction of the converging lines of flux. Thus the force of magnetic attraction varies as the product of the field intensity and the field gradient: dH ds As the induced-rotor magnetic separator is primarily intended for separating feebly magnetic materials, it is important that maximum attraction be attained. For the designer, then, the relationship between the magnetic field and the attractive force has the following implications: 1) Insofar as possible, the separation gap must be saturated with flux. 2) The rotor surface must be shaped to insure maximum convergence of lines of flux toward the rotor. 3) The primary pole face (opposite the rotor, on the other side of the separation gap) must be shaped so that the lines of flux do not diverge from it at any location in the effective separation zone. The actual attractive force of the rotor, and its critical speed, can be calculated as shown by Runo-linna, provided that the true flux density, the field gradient, and the magnetic susceptibility of the mineral can be measured with sufficient accuracy. The irregular shape of the rotor surface makes flux measurements difficult, but it can be done if a suitable gaussmeter is available (see Fig. 2). Calculations by the author, and comparisons with the centrifugal force exerted by the rotor, indicate that the force pinning a hematite particle to the rotor is of the same order of magnitude as the force holding a

Jan 1, 1960

By Oscar Johnson

The industry has been canvassed for information on methods of handling grinding steel at milling plants, an important subject overlooked in most descriptive articles on milling plant arrangements. The data collected are offered in this paper as a guide to designers and planners who have loading and storage problems to solve. WITH capacities of milling plants expanding from a few hundred tons per day to many thousand, replenishment of grinding media is an important phase of mill operation. Information on this aspect of milling procedure, solicited from several mining companies, is summarized here. At International Nickel's Copper Cliff concentrator the normally strenuous job of changing rods is considerably simplified by the use of the Garrow rod charging machine, Fig. 1. The overhead crane, Fig. 2, brings a bundle of rods, weighing four to a ton, to the loading platform of the machine, positioned in front of the mill. The rods roll one by one down the slight incline of the platform onto a conveyor which sends them into the mill. A modified version of the Garrow machine, Fig. 3, is used at the Federal mill of St. Joseph Lead Co. An overhead crane places the portable steel structure in position in front of the discharge end of any one of the five 9x12-ft rod mills. It then raises a bundle of about twenty 3-in. rods to the discharge platform of the charging machine. The rods are 11 ft 7 in. long and weigh about 278 lb. By tripping a lever the operator allows one rod at a time to roll onto the inclined rollers. A slight push by the operator sends the rod smoothly into the mill. The Union Miniére du Haut Katanga rod charging machine, Fig. 4, is mounted on a pair of wheels at the forward end with swiveling castors at the back for steering it to position for use or storage. Wheels are equipped with locking brakes to maintain the machine in position while it delivers rods to the mill. The device is made in two parts. The first consists of the base, which carries the supporting wheels, grooved rollers, and drive. The other part serves as the rod deck, which can carry up to six 3-in. x 12-ft rods. A short boom built integral with the base reaches through the mill trunnion and delivers the rods into the mill barrel. Three grooved guide rollers ,are provided to receive the rods from the sloping charging deck. One rod at a time is fed to the rollers and thus delivered into the mill. Two of the rollers are driven by 11/2-hp motor through a V-belt drive. The third roller is driven off the first by a single V belt in a groove below the rod groove and on the same center line. Rods are delivered to the charger by an overhead crane in bundles of three to six as needed. The power is supplied by cables plugged into power outlets, suitably located near the rod mill discharge end. The Oliver Iron Mining Co. uses a rod charger, Fig. 5, suspended from a monorail by cables. It is constructed .of structural steel and has two decks, each capable of carrying five rods of 4-in. maximum diameter. The rods ride in grooved free-turning rollers. Legs extending down from the mill end of the mechanism act as supports when the unit is ex-

Jan 1, 1955

By N. K. Chen, R. Maddin

Single crystals of molybdenum were extended at temperatures from 1300° to 2500°C. It was found that with increasing temperatures, the yield becomes more pronounced and the number of slip bands for equal amounts of elongation decreases. Slip at high temperatures fragments the structure. OTHER than the investigations on sodium and potassium by Andrade and Tsien,&apos; the researches of Steijn and Brick&apos; on a iron single crystals at low temperatures are about the only studies of the influence of temperature on glide of body-centered cubic single crystals. The effect of test temperature on glide has been rather widely investigated with hexagonal crystals" and less widely with face-centered cubic crystals. ~~ a result of these studies it can be said that, in general, the onset of plastic flow as measured by the initial rate of strain hardening becomes more abrupt with increasing temperature, and the value of the yield decreases with increasing temperature. Strain hardening, however, is markedly affected by changes in temperature except at very low and very high temperatures where the strain hardening rate becames constant. In the present investigation it is shown that temperature affects the glide of molybdenum single crystals in much the same manner as crystals of other classes, it., for comparable strains the number of slip bands decreases with increasing temperature; shear along the slip bands increases with increasing temperature; the yield becomes more pronounced with increasing temperature of test; and the strain hardening approaches a constant at very high temperatures. In addition, it is shown that, in agreement with the work of Tsien and Chow, Qlip occurs on (110) planes in <Ill> directions. It is further shown that slip at high temperatures fragments the structure into either irregular sized cells or bent atomic planes which are roughly aligned in crystallographic directions. Experimental Procedure Single crystals 3 mm in diameter by about 25 mm long were prepared using the technique previously described.&apos; The furnace in which the crystals were grown served as the extension apparatus for the tension tests. It consisted of a 4 in. water-cooled brass tube 20 in. long which was continuously evacuated at the bottom. Two water-cooled copper electrodes held the specimen by means of spherical collets secured in place in the electrodes by set screws. These electrodes served also to transmit power and stress to the specimen. The lower electrode was clamped to a stand, while the upper electrode was fastened to one side of a lever arm flexibly supported at the top through a slightly offset pinion. A metal bellows operating elastically was attached to the upper electrode to affect a vacuum seal and allow freedom of motion. The level of the arm was adjusted by rotating a graduated nut. Rotation of the electrode was prevented by a key fitted into a groove. After the specimen was mounted and the vacuum secured, the lever arm was adjusted so that the bellows was at its relaxed position. This insured that the total weight of the specimen, the upper electrode, and the downpull of the vacuum were balanced by the horizontal beam. Since the specimen was heated by its own resistance, expansion of the specimen proceeded freely by this arrangement. During the time of heating the specimen, the beam was maintained in a horizontal position by turning the nut at the top. By graduating the lever arm and using a known dead weight on the lever arm to supply a tensile stress, the graduated nut could be read to 0.0001 in. extension. Since

Jan 1, 1955

By E. S. Bumps, W. F. Craig, M. Baeyertz

Metallurgists have looked at fractures macroscopically for many years and have evolved a vocabulary in which such words as "cleavage," "brittle," "shear," "ductile," "granular," "fibrous," and "silky" are used to describe the appearance of the fractured surface; but the meaning of these words in terms of metal structure is not well established. Observations of the structural meaning of "brittle" and "ductile" fractures in plate steels have been made, notably, by Kramer and coworkers1 and by Tipper.2 Grossman3 has studied the fracture of tempered martensite and combinations of ferrite and martensite. Notwithstanding these and other less concerted attacks on the problem, present understanding of fracture rests more on assumptions and logic than on experiment. It is the purpose of this paper to add a little to the growing fund of experimental observations of the nature of fractures in steel. The particular fractures to be described were obtained in conventional impact testing of an ordinary structural steel shape. In impact tests of the Charpy type, the specimens fail in a characteristic manner that depends on the steel and the temperature of testing. With ordinary structural and many other steel products, an appropriate range of testing temperature will cause a considerable change in the energy absorbed before fracture. This change is known as the energy transition and is accompanied, more or less closely, by alteration in the appearance of the fracture. At testing temperatures below the transition, the terms "brittle," "cleavage," or "granular" are used to describe the fracture; above it, "ductile" or "shear" are often used. Within the transition, the fracture changes from "brittle" to "ductile" by a progression in appearance, wherein the "brittle" portion of the fracture becomes restricted to a smaller and smaller central area of the fracture, as the testing temperature is raised and the "ductile" type of fracture is approached. All this is well known to metallurgists. The specimens under consideration are of the conventional V-notch Charpy type. They were taken from a structural steel shape of the following analysis: C Mn P S Si 0.17 0.46 0.009 0.029 0.03 Both longitudinal and transverse specimens were tested and examined. Fig 1 shows the energy values plotted against testing temperatures in the usual way. The curves for both longitudinal and transverse specimens show an energy transition, although the maximum energy absorbed at testing temperatures above the transition is greater in the case of the longitudinal specimens. Fig 2 illustrates the changes in the macroscopic appearance of the fractures that are associated with the energy transitions shown in Fig 1. Macrographs of the fractured surfaces of the specimens have been identified with the fracture ratings at intervals on each fracture curve. The numerical fracture rating on the ordinate of Fig 2 indicates the percentage of the area of each fracture that was considered to be "brittle" on macroscopic observation. Such rating of the fracture type in impact tests is now customary in many laboratories. Hereafter the specimens will be identified by reference to Fig 2 as 90 pct "brittle," 80 pct "brittle," and so on, in accordance with this macroscopic evaluation of the appearance of the fractured surface. The discussion of the fractures is divided into three parts. The first two are concerned with the mode of fracture and its relation to general structural features. As the same metal-lographic features occur in both longi-

Jan 1, 1950

R. W. Raymond, New York, N. Y,:—Since the presentation of my note on this subject at the New York Meeting, Professor Louis has pointed out an error in my statement of his conception of " pitch "—namely, he understands the pitch, in the restricted sense which he proposes, to be the angle of inclination of the axis of an ore-body, measured on the vertical plane drawn through the body; whereas, I represented him as proposing to define " pitch " as the angle of inclination of an oblique body, measured on the plane of the dip, in the direction of the strike. The difference will appear upon consideration of the accompanying isometric projection, Fig. 1, in which ABCD represents the plane of the inclosing ore-deposit (vein or bed), and AC the axis of the oblique ore-shoot. ABE is the angle of the dip, as universally understood; and ACE

Jan 1, 1909

By L. H. Robinson

Triaxial compression tests on Indiana limestone indicate that chemical additives in the pore fluids can increase or decrease the strength in plastic failure but not in brittle failure. Tests using a series of the sodium salts of dicarboxylic acids show that odd-number carbon-atom chains decrease the yield strength as much as 3.0 x 10 3 psi, and even-number carbon-atom chains increase the yield strength as much as 9.0 x 102 psi. ,The most effective chemical (sodium citrate) decreased the yield strength of Indiana limestone from 16.0 x 103 to 12.0 x 103 psi. The chemical additives investigated have no influence on microbit drilling rate when drilling with zero differential pressure. However, when drilling at a 2.0 x 103-psi pressure differeniial and using an odd-number carbon chain compound as the circulating fluid, the roller bit drilling rates were slower than with water whereas the drag bit drilling rates were faster. One even-number carbon chain compound added to the circulating fluid produces the opposite effect: the roller bit drilling rate is slightly faster than with water and the drag bit slower than with water. INTRODUCTION A Russian book by Rehbinderl published in 1944 generated much interest in the possibility of aiding and accelerating the destruction of solids by the action of a liquid in which the solids are deformed. This book describes a process in which microcracks are generated during elastic deformation. To describe this process, the rock is divided into three zones: (1) the zone in which the destruction takes place, (2) the predestruc-tion zone (an affected area immediately below the destroyed zone) and (3) the undisturbed specimen. Consider a load applied normally to a surface of an infinite slab of rock. Immediately below the point of application of the load, the rock is destroyed by compression or shear forces. Below this area of destruction, because of a great number of discontinuities ranging from defects to weak points in crystals of discontinuities in crystal latices, very small cracks are created in or between the crystals (often referred to as microcracks). Upon removing the load, the broken rock in the destroyed zone could be removed. In the lower predestruction zone, however, the microcracks in and between the crystals could disappear by the process of rehealing, i.e., the molecular attraction from one side of the crack to the other side being sufficient to completely eliminate the crack. Thus, a large number of these microcracks possibly exist only for a relatively short period of time. The concept of small cracks being generated within the crystals of a rock is not unreasonable. If the rock matrix is deformed below the yield point, some of the defects present within the crystalline structure could start small cracks through the interior of the grains. Upon removal of the load, these microcracks reheal (or the newly generated surfaces come back together) so that all evidence of cracks completely disappears. Under various types of loading, and in various types of fluids, the rehealing of these cracks would be time dependent. If a liquid adhered to the surface of a rock, it could penetrate into the microcracks and thus delay or prevent the rehealing process. This suggests that the prevention of healing of the microcracks may be dependent upon the wetting characteristics of the solid. Thus, rocks which are water-wet should be more easily destroyed in water than in nonpolar hydrocarbon liquid. Adsorption of a liquid could also reduce the free surface energy which could explain the decrease in strengths of materials under nonrepetitive-type loading. Rehbinder&apos;s work prompted Boozer, Hiller and Serdengecti 2 to examine the effects of pore fluids on the deformation of rocks subjected to triaxial compression over a range of confining pressures, temperatures and strain rates. Fluids which strongly adsorbed on the rock grain surfaces decreased the strength of sandstone and limestone, which deformed plastically. For certain strain

By Brown, R. W., G. H. Neill, R. G. Loper

All facets of ball sealer behavior must be known and understood to design for their optimum use in well treatments. The down-hole factors including the inertial forces, drag forces and holding forces have been discussed. Equations have been developed and presented for these forces. The use of these equations in this process will contribute to the most efficient use of an economical and proven ball sealer process. The urocedure presented has been used to successfully analyze field results indicating problems involving the use of ball sealers. These problems have been isolated and corrected in future treatments by using the procedure presented to revise the perforating program, the injection rate, the design of ball sealer stages and/or the type and size of ball sealers. The procedure presented also indicates that dislodgement of ball sealers occurs primarily in ultra slim-hole completions. INTRODUCTION The perforation sealing process has been proven highly successful and economical since it was introduced to the oil and gas industry in early 1956.&apos; Since it has proved so successful in multistage fracture treatments at a much lower cost than conventional packers, the ball sealer process has become a byword in well completions.&apos; Not only has it changed the design of fracture treatments, it has changed the concepts of selectively perforating and has greatly aided the success of the single-point and limited-entry techniques." Yet with all the advantages, there are still facets of ball sealer behavior that are not widely recognized. These must be known and understood to better design and execute the optimum ball sealer treatment. The down-hole behavior of ball sealers is influenced by a number of factors including an "inertial force", a "drag force" and a "holding force". These are considered in two phases—the initial seating of the ball and the forces tending to unseat the ball after contact has been made (see Fig. 1). This paper presents a theoretical study of these factors and formulas for predicting their influence. The authors acknowledge the fact that the flow equations presented herein describe the behavior of Newtonian fluids and do not cover the so-called power-law fluids. The assumptions made, however, are reasonable and well within practical limitations of the conditions encountered during field application. For example, it is assumed that the perforations are round with a discharge coefficient of 0.82. While this may not be exactly true, it has been verified within practical field limitations.&apos; The discharge coefficient would not vary significantly even if the perforation size or configuration varied pronouncedly. The approach of assuming uniform perforation size is not as strained as it might first appear. Normally, a perforator contains charges equally spaced with the same number in each vertical (or horizontal) plane. If the perforating gun is not centralized, the holes in one plane will be smaller than average, while the holes in opposing planes will tend to be larger than average. The net result is that the two effects tend to balance. FACTORS AFFECTING CONTACT WITH PERFORATlON Ball sealers are injected into well treating fluids for the purpose of contacting and sealing those perforations which are accepting the fluid flow. The efficiency of the sealers is primarily influenced by: (1) the velocity of the balls down the pipe, and (2) the fluid velocity through the perforations. To divert the sealer to the perforation, the inertial force of the ball must be overcome by the drag force created by the fluid velocity through the perforation. BALL VELOCITY The final, or stable, velocity of the ball is the sum of the actual fall velocity and the fluid velocity. This will be

By I. Zaplatynskyj, G. C. Kuczynski

SINCE the excellent studies of metal powder compaction executed by Kamm, Steinberg, and Wulff, no work on the subject has appeared in the technical literature. Kamm et al. were the first to investigate quantitatively the distribution of density in a powder compact, as a function of pressure, height and diameter of the die, powder particle size, etc. For this purpose they devised a very ingenious method. They inserted a thin lead grid into a die and then filled the die with powder. During cold pressing, the lead grid -moved downward. Due to its deformability it followed closely the downward descent of the adjacent powder. The die was then radiographed and, from the deformations of the grid openings measured on the radiographs, the density in the vicinity of each opening was evaluated. Their findings led them to the conclusion that the friction on the side walls of the die is a major controlling factor of the density distribution inside the cold pressed powder compacts. However, it is difficult to conduct tests similar to those of Kamm, Steinberg, and Wulff in a processing plant laboratory, which usually lacks the necessary expensive radiographic equipment. The purpose of this note is to describe a method which makes it possible to determine the density distribution in green powder compacts with the same accuracy as the lead-grid method but which is far simpler and faster and requires only standard laboratory equipment. Instead of using a lead grid, the hardness at selected points of the sectioned compact is determined. If the relationship between hardness and density is known the density distribution is readily obtained. This relationship is easily found from measuring hardness and densities of thin compacts. In such compacts the density, for all practical purposes, is constant throughout. The method was tested on a Plast nickel powder, grade FlA-A20, kindly supplied by Plast Metals Co. Thin compacts (height to diameter ratio 0.2) were pressed in a single action cylindrica1 die at various pressures. The density of the compacts was determined by weighing and by measuring the height and diameter with a micrometer. Subsequently the Rh hardness was determined. Up to ten readings were taken on each specimen. The difference in hardness readings on each compact was never greater than three corresponding to about 0.1 g per cu cm uncertainty in density. By varying the compaction pressure of the samples, a whole scale of densities was obtained allowing construction of a set of density-hardness calibration curves. To test the method several compacts of different height were pressed under varying pressures. Die walls were always well lubricated. After pressing, the compacts were mounted in bakelite and halved by grinding, and hardness readings taken along the diameters of the specimens. The distance between adjacent indentations was about 2.5 mm. After hardness readings were translated into densities, contour maps of densities of the compacts were prepared. One of them is reproduced in Fig. 1. The areas encompassed by the curves are labeled with numbers representing the density in g per cu cm of those regions. In Fig. 2 the same results are re-plotted to emphasize the radial density changes at various depths. The results thus obtained confirm the findings of Kamm, Steinberg, and Wulff kentioned previously. They are recapitulated here briefly. 1—The densest part of a compact pressed from one side is at the outer circumference at the top and the least dense part at the bottom, at the outer circumference. Figs. 1 and 2 show this clearly. 2—The density near the cylindrical surfaces of the compact decreases uniformly with height from top to bottom. 3—The density variation increases with the height to diameter ratio. References R. Kamm, M. A. Steinberg, and J. Wulff: Trans. AIME (1941) 171,&apos;R. p. 439 ;MetaLs Technology (February 1941). R.p. Kamm, M. A. Steinberg, and J. Wulff: Trans. AlME (1949) 180, 2R.P. 694; MetalS Technology (December 1948).

Jan 1, 1957

By E. A. Gulbransen, K. F. Andrew

Thermodynamic information on the solubility of hydrogen in exothermic metals is limited. Thus, the overall solubility decreased as the temperature rose, which suggests the heat of solution of hydrogen in the metal is negative; yet the terminal solubility in the metal phase increased, which suggests an endothermic reaction. A thermodynamic analysis, therefore, was made of the several equilibria involved when hydrogen dissolved in the metal. Equations were derived expressing the solubility, terminal solubility, and decomposition pressures of hydrogen in terms of the heat, entropy, and free energy of solution of hydrogen in the given phase. The relations between the thermodynamic functions for the a-zirconium and 8-hydride phase were developed. The thermodynamic quantities were determined experimentally by the measurement of the decomposition pressures over a broad composition and temperature range. Two new methods of analyzing the experimental data were developed for determination of the terminal solubility. STUDIES&apos;, &apos; of the impact strength of zirconium at room temperature indicated that small quantities of hydrogen, of the order of 10 parts per million, embrittles the metal. Micrographic&apos; and X-ray diffraction&apos; studies showed this embrittlement to result from the precipitation of a second phase upon slow cooling. These studies suggested that the terminal solubility of hydrogen in the metal phase increased with increase of temperature. This behavior appeared to contradict the effect of temperature on exothermic hydrogen occluders such as zirconium. For these metals, the solubility of hydrogen should decrease with increase of temperature. Before these facts could be understood, a thorough analysis of the several equilibria was essential. It was the purpose of this paper to consider the several equilibria involved when hydrogen was reacted with zirconium from both the theoretical and experimental points of view. Since the overall solubility of hydrogen in the metal has been considered by a number of workers, it was proposed to study the composition range 0 to 6 atomic pct H in detail. Literature Schwartz and Mallett&apos; determined the terminal solubilities of hydrogen in the metallic phase from diffusion studies. They extrapolated concentration-penetration curves to the boundary between the solid solution phase and the hydride phase at the surface. Their results showed values of 2.6 atomic pct at 400°C and 5.2 atomic pct at 500°C. Extrapolations of the data to room temperature suggested very low values for the terminal solubilities. This study confirmed the hydrogen embrittlement results and indicated that the terminal solubilities increased as the temperature was raised. The solution of hydrogen in zirconium over the complete concentration range was studied by Hall, Martin, and Rees3 and by others. The results showed that hydrogen was absorbed up to a maximum composition of 66 atomic pct or ZrH This composition represented the t-hydride phase. The maximum amount of hydrogen absorbed increased with pressure and decreased with temperature. Due to this temperature behavior, zirconium was classed as an exothermic occluder." In 1930 Hägg studied the crystal structures of the Zr-H alloys over a broad composition range. Four hydride phases were found. However, the range of homogeneity of the several phases was not studied. Gulbransen and Andrew" recently studied the phase diagram of this system by X-ray diffraction methods and by a thermodynamic method based on decomposition pressure measurements. The results showed that only two hydride phases existed for low temperatures, the 6 and the .-phases of Hagg.&apos; Both phases had broad regions of homogeneity. The lower limit of the two-phase region of a and d-phases suggested a terminal solubility of 4 atomic pct at 500°C. This value was in agreement with the results of Schwartz and Mallett.&apos; To avoid hydrogen embrittlement at low temperatures, it was necessary to heat the metal in high vacuum at elevated temperatures. To choose the conditions of temperature and high vacuum, it was

Jan 1, 1956

By W. E. Bearce

The recent concern for the recovery of even the finest fractions of coal preparation plant feeds has created needs for new equipment. Thermal dryers currently available have difficulty reducing the filter cake moisture on down to the desired point. This difficulty involves 1) the physical problem of handling this wet, sticky material and making each particle accessible to the hot gases, and 2) removing the extremely fine dried particles from the cooled gases. The dryer described in this paper handles the first of these problems, and eliminates the second by the substitution of steel balls for air as the heat transfer medium. As a general statement, the cost of preparing coal for market is inversely proportional to the size of the lumps or particles. In the not too distant past the finer sizes were discarded as being uneconomical to treat and this practice might be still continuing if it were not for the insistence of the public that this material be kept out of our streams. This being the only cost-free outlet, the disposal of fine refuse became a significant item of expense in every preparation plant. When this happened it was only reasonable to look to the recovery of the values in this material, not only to defray this expense, but to reduce the tonnage which had to be wasted. There seemed to be no device available suited to reducing the moisture in this material to what the market requires. All of the fine coal dryers commonly employed make use of air to bring the heat of combustion into contact with the coal particles. Any device employing air as a heat transfer medium, has the following two strikes against it in attempting to handle 28 mesh by 0 filter cake: 1) It is practically impossible to bring the hot air into intimate contact with the enormous number of fine particles stuck together in the cake. 2) Even if this can be effected, it is impossible to remove the dried coal from the air. A wet scrubber must be employed, the discharge of which must go back to the filter and dryer as a circulating load of the most objectionable sort, being the extreme fines. Various compromises have been used to cope with the problem of drying this relatively small tonnage of high moisture coal. Often some of the dried coal is mixed back with the feed to the dryer in an attempt to make the mixture more handleable and more available to contact with the hot air than the filter cake alone would be. This may help to some extent with the first problem but it does nothing about the second and a dryer operated in this way has to be oversized. Sometimes the filter cake is mixed with a coarser fraction for the same reason. Here again, while this may make a mixture (the particles of which are more readily brought into contact with the hot air), the problem of getting the fine coal out of the air remains and a larger percentage of the total coal to be dried is handled by the most expensive means. Mechanical dewatering has accounted for more and more of total coal drying lately and in many cases would satisfactorily handle the whole load, down to 28 mesh, if there were a means available for doing a good job on the —28 mesh by itself. The dryer which is the subject of this paper was designed expressly for doing this job — drying fine material by itself regardless of how wet it may be to start with, how fine it may be, or how gummy and sticky these properties in combination may make it. The essential features are depicted in Fig. 1. A rotating cylinder is supported on a frame in such a way that one end may be raised or lowered by hy-

Jan 1, 1968

By W. Mckewan, W. M. Fassell

The oxidation rates of copper have been determined at temperatures from 600" to 900°C in oxygen from 14.7 to 400 psi total oxygen pressure. The oxidation rate of copper is unchanged by oxygen pressures within the range studied. The observed data extend Feit-knecht&apos;s conclusion concerning the pressure independence of copper from atmospheric pressure to 400 psi. All samples studied in the above-mentioned temperature and pressure range have both Cu2O and CuO present in the oxide film. NUMEROUS papers have been published on the oxidation of copper, some of which have noted the effect of oxygen pressure on the oxidation rate of copper. It must be noted, however, that no data on the oxidation rates of copper at pressure in excess of 1 atm have been reported in the literature. (Le Chatelier¹ reported that a black oxide of silver was formed at 300°C and 15 atm pressure.) This is likewise true for the other metals. This investigation was initiated to obtain experimental oxidation rate constants for pure metals at elevated temperatures and high oxygen pressure. Copper was selected as the first metal since probably more reliable data are available on its oxidation rates and related physical and chemical properties than for any other metal or alloy. As a general summary, the following conclusions appear well established for the oxidation of copper: 1—The oxide coating consists of Cu2O with a superficial coating of CuO providing the ambient oxygen pressure exceeds the equilibrium pressure for the coexistence of Cu2O and CuO.² The following sequence of phases is then Cu/Cu2O/CuO/O2 (gas). The Cu2O consists of large crystals that have no relation to the orientation of the metal crystals, except for a very thin layer adjacent to the metal." The CuO consists of very fine crystals randomly oriented. If the oxygen pressure is below the equilibrium pressure for the coexistence of Cu2O and CuO, the coating consists of Cu,O only. 2—The rate-determining factor in the parabolic oxidation of copper is the diffusion of Cu+ ions through the Cu,O layer.4,6,7 The Cu+ ions are accompanied by electrons to maintain electrical neutrality. The mechanism of the reaction at the Cu2O/CuO interface and the method of growth of the CuO is in some doubt. 3—On copper, there are three reported pressure effects: (a) At pressures below 0.3 mm Hg oxygen pressure, the oxidation rate increases directly with pressure.&apos;, &apos; .Vxygen starvation at the surface may account for this effect. (b) At oxygen pressures from 0.3 to 63 mm, the oxidation rate increases as the 7th root of the oxygen pressure providing the temperature is such that only Cu2O is present in the film. (c) At pressures from above the equilibrium pressure for the coexistence of Cu2O and CuO (varies with temperature) to atmospheric pressure, the oxidation rate is independent of the oxygen pressure.&apos; Equipment In order to determine the oxidation rates of metals in an oxidizing atmosphere at pressures up to 400 psi, the equipment is somewhat different than for low pressure work as is shown in Figs. 1 and 2. A Leeds and Northrup Micromax recording controller (A) is used to control the temperature of the Ni-chrome furnace winding in conjunction with a Micromax electric drive unit. The drive unit adjusts a 20 amp Variac (variable transformer) to control the power input into the Nichrome furnace winding. Due to the "self heating" of the sample by oxidation, frequently encountered in oxidation rate studies, it is essential that the sample temperature be measured independently. This is done by means of a series of six chromel-alumel calibrated thermocouples located spirally around the oxidizing metal sample. Each thermocouple is partially shielded from the direct radiation of the furnace wall by

Jan 1, 1954

By J. H. O’Dette

BLISTER formation on wrought aluminum products has been a matter of concern to aluminum fabricators for many years. The fact that blisters make their appearance during the final stages of fabrication means that much time and effort have been expended before it is evident that the material must be scrapped. This and the loss of production are ample reasons for embarking on a research program to find out more about blistering and possible methods of control. Many excellent papers on this subject have appeared in the technical literature in the last few years. In one of the more recent papers, Kostronl gives a fairly complete review of the problem of gas in aluminum and blistering in general. From the work of the various investigators, a general mechanism for the formation of blisters has evolved and may be summarized briefly as follows: Hydrogen gas is usually present in the cast ingot, in the atomic or ionic state, in excess of the solid solubility. At room temperature the gas atoms are relatively immobile, but at elevated temperatures they become mobile and diffuse to free surfaces where they associate to form molecules. If these free surfaces are discontinuities within the ingot then the associated gas molecules collect and build up considerable pressure until equilibrium is reached with the dissolved gas around the discontinuity. Since the solubility of the gas is proportional to the square root of the partial pressure it is evident that large pressures may be built up at the discontinuities. When the metal is rolled to sheet the pressure of the gas in these, discontinuities is sufficient to deform the surface of the sheet and form a blister, particularly when the strength of the material is reduced during the annealing. Although the mechanism of the formation of blisters was fairly well known, the actual impor- tance of the individual roles played by the gas and the discontinuities was not so well established that positive methods for control of blistering were at hand. It was the object of the investigation to learn more about the nature of the discontinuities giving rise to blistering and to develop methods of control. The investigation was carried out in three stages as follows: a) A study of the more commonly used methods of removing hydrogen from aluminum, such as fluxing and holding, and their effects on blistering. b) Location of the discontinuities giving rise to blistering. c) A study, by indirect methods, of the movement of gas in the metal and its effect on blistering, and the development of methods of blister control during fabrication. Removing Gas and Reducing Blistering by Fluxing or Holding-—The work of removing gas and reducing blistering by fluxing or holding was carried out on metal of Alcan 2s (1100) composition with an artificially high gas content. The high gas content was obtained by introducing water into the melt prior to casting; the water reacted with the aluminum forming A12O3 and hydrogen. The procedure was to raise the gas content by introducing water into an aluminum melt and using half the melt to cast one ingot immediately. The remaining metal was treated again with water to make up for the reduction in gas content during holding, while the first ingot was being cast, and then given a fluxing or holding treatment and cast into an ingot. Samples for gas determination were cast from the molten metal before and after the gassing operation; before, after, and during fluxing, and while casting. Samples were also cut from sections of the ingots. Gas determinations were made on these samples using the well known vacuum fusion technique. All ingots were hot rolled at 500°C to 0.250-in. slab which, in turn, was cold rolled to 0.040 in. sheet. The sheet was coiled and annealed for 2 hr at 500 °C and then cut into 5-in. squares which were inspected for

Jan 1, 1958

By B. F. Decker, J. H. Keeler, W. R. Hibbard

Textures of hot-rolled, of cold-rolled, and of cold-rolled and annealed zirconium sheets were determined by use of an X-ray spectrogoniometer. All textures showed a tilt of the basal planes 240" from the rolling plane about the rolling direction. Deformation textures showed the [1010] direction to be approximately in the rolling direction. After recrystalliza-tion, the 111201 direction was approximately in the rolling direction. This texture was sharpened by annealing above the allotropic transformation. Textures of sheet produced by alternately cold rolling and then annealing were less strongly oriented than sheets that underwent severe deformation without intermediate anneals. THIS study of the deformation and annealing textures of high purity zirconium was carried out to supplement an investigation of zirconium and zirconium-base alloys. The spectrogoniometer method of pole figure determination was used and yielded more detailed and precise information than the photographic techniques used by previous investigators. Earlier investigations of the rolling textures of hexagonal metals titanium,1,2 beryllium," and zirconiumL having a c/a ratio slightly less than 1.6 disclosed a rotation of the basal planes from the rolling plane about the rolling direction so that the basal poles were inclined toward the transverse direction, and with one exception,& the [1010] direction was found parallel to the rolling direction. Similarly, hot rolling produced a spread of the basal poles in the transverse direction,2,3,5 With the [1010] direction parallel to the rolling direction. The textures of these metals after recrystallization differ somewhat from each other although still exhibiting the transverse rotation of the basal poles about the rolling direction. Zirconium" was found to have the [1120] direction in the rolling direction, beryllium" continued to have the [1010] direction in the rolling direction, and titanium&apos; was shown to have the [1010] direction in the rolling direction (the cold-rolling texture) when annealed at 1000°F, changing to the [1120] direction in the rolling direction when annealed at 1500°F. It was suggested2 that the titanium retains the deformation texture after re-crystallization, and preferred grain growth at higher temperatures produces the second texture. Annealing above the allotropic transformation temperature did not appreciably change the high temperature recrystallization texture for titanium.&apos; Coarsegrained zirconium showed more spread" in the transformation texture than in the recrystallization texture. The material used in this investigation was crystal-bar zirconium prepared by the iodide process. The major impurity was hafnium which was less than 0.3 pct. The composition obtained by spectro-graphic analysis is given in Table I. The hot-rolled specimen was prepared from a 50-g button of zirconium arc-melted in a water-cooled crucible under an argon atmosphere. This button was enclosed in a welded sheath of soft iron and the ensemble was rolled at 825°C. After each pass the sheath was put back into the furnace to allow it to return to the desired temperature. The zirconium ingot was reduced in this manner to a thickness of about 0.035 in., a reduction of approximately 90 pct. The sheet after removal from the sheath was alternately polished and etched to a thickness of 0.001 in. Cold-rolled specimens were prepared from crystal bar by a series of reductions of approximately 0.010 in. until the sheet reached a thickness of 0.010 in. after which it was cold-rolled to 0.001 in. thickness between sheets of alloy steel. The total cold reduction amounted to about 99.8 pct. Specimens were annealed in an evacuated Vycor or quartz tube. The transmission pole figures were obtained by the quantitative method of Decker, Asp, and Harker6 modified by Geisler7 using an X-ray spectrogoniometer with Cu Ka radiation. Unless otherwise specified all four quadrants were examined with 5" increments along the radius of the pole figure. Absorption corrections were made for changes in length of the X-ray path through the sample as inclination of the

Jan 1, 1954

By T. M. Geffen, J. L. Sanderlin, F. F. Craig, D. W. Moore

Scaled reservoir models have been used to study the effect of gravity on oil recovery performance in frontal-drive operations; namely, water, gas, or solvent flooding. The difference in density between the reservoir oil and the injected fluid causes their segregation, resulting in a non-uniform advance of the fluid front. In the laboratory flow tests, which simulated both five-spot and linear injection operations in flat reservoirs, the viscous, capillary, and gravity forces present in these operations were scaled. Dyed fluids were used so that the gross movement of the injected fluid could be observed. The studies covered a range of injection rates, formation thicknesses, and rock and fluid properties normally encountered in field operations. The results of the model tests indicate that the volume of the reservoir contacted by the injected fluid at its breakthrough into the producing well is less than that expected based on information which neglects gravity effects. This difference can often be as much as 80 per cent by gas or water injection in uniform sand bodies. Preliminary flow tests on a non-uniform sand body indicate that the uniformity of the flood fronts may in some situations be influenced to a much greater degree by permeability variations within the rock body than by gravity effects. The magnitude of fluid segregation due to gravity is controlled by the average injection rate, rather than day to day or week to week variations. INTRODUCTION One of the important factors controlling the oil recovery from a frontal-drive operation, such as water, gas, or solvent injection, is the volumetric sweep efficiency. This factor is a measure of the gross portion of the reservoir that is contacted by the displacing fluid. The volumetric sweep efficiency is influenced by gravity effects, well arrangements, and variations in rock permeability within the reservoir. The gravity effects are due to the displacing fluid being of different density than the reservoir oil. This causes the displacing fluid to move preferentially toward either the top or bottom of the formation. Non-uniform advance of the flood front can be caused by the relative positions of the injection and production wells. Variations in rock permeability also result in an uneven advance of the displacing fluid. Gas zones, representing paths of low resistance, may result in non-uniform movement of the injected fluid. The more uneven the advance of the displacing fluid, the lower is the volumetric sweep efficiency and thus the lower the oil recovery efficiency. The effects of well arrangement and permeability variations, upon the gross movement of the injected fluid have been the subjects of extensive investiga-ti0ns.1,2,3,4,5,6 Gravity effects have been recognized as being present in frontal-drive operations&apos;.&apos; but there has been little quantitative measure of their magnitude. Very likely the reason gravity effects have not been studied is that this problem does not lend itself to simple experimental or mathematical analysis. The development of reservoir modeling techniques has made possible a quantitative determination of the effect of gravity on fluid segregation and thus upon the oil recovery performance of frontal-drive operations. This paper presents a progress report on a laboratory investigation of gravity effects in fully liquid-saturated, horizontal, uniform as well as non-uniform systems. These results were obtained from scaled experiments on both linear and five-spot systems within the range of conditions normally encountered in secondary recovery operations. This study is concerned with the gross movement of the injected fluid to the time it first reaches the production wellbore. Therefore, it should be emphasized that the results of this paper can not be used to determine the effect of gravity segregation on oil recovery efficiency at abandonment conditions. MODEL SCALING The science of scaling models is relatively new as applied as petroleum production problems, Many of the scaling techniques have been adaptions of those used in basic studies of heat and fluid flow. There are

Jan 1, 1958

By J. S. Browning

The U.S. Bureau of Mines has been experimenting with flotation processes to separate the spodumene-beryl ores mined at Kings Mountain, N.C. The success to date as well as the present status of the process is discussed. Further experimentation is underway and studies will be made on the milling costs involved in the flotation process. The pegmatites of the Kings Mountain-Lincoln ton, N.C., area constitute the largest known domestic reserve of beryl and spodumene. The reserve is estimated to contain 90 million tons of pegmatic material with 1,280,000 tons of recoverable Li,O(lithia) as spodurnene.&apos; The pegmatites also contain 0.4 to 0.5 pct beryl disseminated throughout the orebodies. The pegmatites may contain a potential reserve of 240,-000 tons beryl, equivalent to approximately 34,000 tons of BeO. Different flotation methods for separating beryl from feldspar or quartz, or both, have been developed by various investigators.2-7 On the other hand, published information is limited on concentration of spodumene-beryl ores. As the response of beryl and spodumene to flotation is essentially the same, a successful separation of the two minerals depends upon use of a selective depressant or a selective collector for one of the minerals. Several years ago, the U.S. Bureau of Mines, recognizing the need for developing a large domestic supply of strategic beryl, undertook studies to develop improved methods of recovering this mineral. Because of the low beryl content of the pegmatites, economic production of the beryl entails its recovery as a byproduct of spodumene flotation. Thus, the development of procedures that would provide for maximum recoveries of the spodumene, as well as the beryl, was a primary objective of the studies. Tests were made on run-of-mine ore and spodumene flotation tailing from the Foote Mineral Co.&apos;s spodumene concentrator at Kings Mountain (Fig. 1). Pet-rographic analyses of the ore and flotation tailing are given in Table I. Detailed analyses and examinations of the ore and tailings revealed that the beryllium was present in the form of a low-alkali beryl. The crystals were small, rarely larger than 14-mesh diam, and were clear and colorless. About 10 pct of the Li20 content of the ore was present in the mica and feldspar components of the pegmatite. In some weathered ores the associated clays also contained small amounts of lithia. This is typical of pegmatites in the Kings Mountain area. LABORATORY TESTS In the past, a vigorous chemical treatment of the spodumene surfaces with acid or caustic soda has been considered essential for satisfactory selective flotation of the spodumene from the other minerals in pegmatites. Many tests were made during this investigation to determine if chemical treatment of the spodumene could be eliminated in favor of a reagent combination that would depress the other minerals while selectively floating the spodumene. A simple reagent combination and process was developed that gave better spodumene recovery and grade of concentrate than the more elaborate acid or caustic treatment methods previously used. The finely ground ore pulps were conditioned with either an ammonium, alkali, or alkaline earth lignin sulfonate and sodium fluoride, and the spodumene was floated and cleaned using oleic acid as the collector. The spodumene tailing was deslimed, conditioned with sulfuric acid and coco amine acetate, and floated to reject mica. The mica tailing was thickened and conditioned with hydrofluoric acid, then washed to remove the acid. The washed pulp was conditioned with sodium hydroxide for pH control, and the beryl was floated and cleaned with oleic acid as the collector. Table II summarizes the results of the laboratory test work. About 77 pct of the spodumene and 75 pct of the beryl were recovered from the pegmatitic material. The spodumene concentrate assayed 6.1 pct Li20 and 0.01 pct BeO, and the beryl product assayed 3.0 pct Li20 and 1.57 pct BeO. Similar results were ob-

Jan 1, 1961

By G. R. Speich, D. J. Mack

The transformation of was studied by isothermal methods. At all temperatures, the ß transforms quickly to fine grained ß" which develops silver-rich striations. At higher temperatures the striations disappear, the final structure being Widmanstatten a in ß&apos;. At lower temperatures, the striated ß" is consumed by pearlite nodules of a + ß&apos; which in turn form the Widmanstatten a in ß&apos;. The transformation is unlike any previously reported for a eutectoid. AS part of a general program of study on the eutectoid reaction, the Ag-Cd eutectoid seemed particularly attractive because the ß phase which undergoes the reaction is another of the typical "electron compounds," AgCd, having the disordered body-centered cubic structure. This work deals with the eutectoid which occurs at 50.5 wt pct Ag, and not with the eutectoid which has been reported at 42.9 pct Ag.&apos; There has been no work reported specifically on the Ag-Cd eutectoid which was studied. The only information available on this eutectoid is that work done in the determination of the phase diagram. For the most part, the terminal portions of the diagram, Fig. 1, are well established; however, the region from 40 to 60 pct Cd is still somewhat in doubt. The X-ray evidence&apos;..&apos; in this region is in conflict with the results of thermal analysis. X-ray analysis3 does not show a polymorphic transformation at about 240°C as indicated by thermal analysis.1,5 Even the X-ray evidence, within itself, is confusing in this region of the diagram. One investigator2 reports the ß phase as hexagonal close-packed and has found three phases in the one-phase ß field. Other X-ray investigators"&apos; &apos; report the ß phase as body-centered cubic. The authors believe that much of the confusion resulted from incomplete homogenization of the alloys. It was found that it takes almost a week to produce a completely homogeneous two-phase structure at 370°C. Another possible source of error is the volatilization of cadmium from the surface and cracks of the specimen during annealing with the possible formation of a cadmium-poor phase. The only metallographic data available on this eutectoid alloy are those of Durrant1 and Fraenkel and Wolff.5 his information is very limited. The phase diagram chosen as most nearly correct is that in the Metals Handbook," which is almost identical with the phase diagram suggested by Durrant.1 Materials and Procedure The alloy was prepared from high purity silver (999.5 plus fine) and high purity cadmium (0.02 Pb, 0.005 Cu, trace Fe). The metals were melted in carbon under a nitrogen atmosphere. Some cadmium was lost by volatilization but by remelting several times and adding cadmium a 200 g ingot of approximately eutectoid composition was obtained. Because the CdO fumes are quite toxic, the exit gas from the furnace was led through a water trap to condense the CdO. The ingot was homogenized at 650°C for 24 hr, no attempt was made to prevent decadmiumization. This resulted in a narrow decadmiumized rim on the ingot which was removed. Filings for analysis were obtained from cross sections of the ingot. Silver was determined by the Volhard thiocyanate method,? cadmium by difference. The ingot analyzed 50.8 pct Ag at the top of the ingot and 50.7 pct at the middle and at the bottom of the ingot. This alloy was only slightly hypo-eutectoid compared to the accepted value of 50.5 pct Ag and was used for the isothermal studies. It was felt that further attempts to adjust the composition might be futile because of the volatility of the cadmium. The ingot was sectioned to specimens approximately 3/4 x 3/4 x 1/8 in. These specimens were "austeni-tized" for 3 hr in air at 650°C to yield homogeneous ß and then quenched into a salt bath held at constant subeutectoid temperatures where the transformation

Jan 1, 1954

By J. P. Morgan, J. R. Dawson

A review of Jones & Laughlin&apos;s Vesta coal preparation plant flowsheet in 1959 indicated that, of the three sizes making up the company&apos;s metallurgical product, the -48-mesh fraction offered the greatest potential for improvement. Efforts to improve quality and yield were directed toward the use of froth flotation. After laboratory and plant tests were completed, it was decided that treatment of the entire -@-mesh fraction of the coal mix by flotation was a significant step forward in providing better coal quality and recovery. Reduction of ash in the metallurgical coal from 6.75 to 6.25% provided material savings at the coal washer, coke plant and blast furnace. The Vesta preparation plant of the Jones & Laughlin Steel Corp. is located on the Monongahela River, eight miles south of Brownsville, Pa. This plant is capable of cleaning 2400 tph of a mixture of Pittsburgh seam high volatile coals from the Vesta and Shannopin mines to produce a metallurgical coal of 6.75% ash and a steam coal containing 14% ash. Heavy media vessels are utilized to upgrade the coarse coal while launders and tables handle the -1/4-in. fraction of the raw coal feed. Cleaned -1/4-in. coal goes to boot classifiers where the 48 mesh material settles and is removed by bucket elevators. This 1/4x48 mesh material is then sent to centrifugal dryers for dewatering. As designed, the -48 mesh fraction overflows the boot as a 7 to 8% solids slurry and is recovered by cyclones and a thickener and then dewatered by filtration. The products of the heavy media circuit, the launder-table-boot-dryer circuit and the cyclone-thickener-filter circuit, are combined to constitute the shipped metallurgical coal. The Vesta-Shannopin mix is combined at Jones & Laughlin&apos;s Pittsburgh and Aliquippa Works with purchased low and medium volatile coals for the production of metallurgical coke. A review of the preparation plant flowsheet in 1959 indicated that of the three sizes making up the metallurgical product, the -48-mesh fraction, containing 16.7% ash, offered the greatest potential for improvement of coal quality. This fraction was considered low, averaging 55%, while the rejects averaged only 33% ash. It was evident that while the boot overflow fraction represented only 6% of the product mix, a reduction in ash to 6 or 7% would reduce the ash of the metallurgical coal by 0.5%. The original plant flowsheet handling the boot overflow (Fig. 1) consisted of ten 14-in. cyclones treating 70% of the overflow and producing a 48x150-mesh underflow and a -150-mesh overflow. The cyclone overflow was combined with the remaining 30% of the boot overflow to constitute the feed to a 150-ft thickener. The cyclone underflow and the 48x325-mesh thickener underflow were fed to vacuum disk filters for dewatering prior to combination with the coarse metallurgical coal. The thickener overflow stream containing the -325-mesh material was split, 40% being recycled directly to the plant water system and 60% being flocculated and clarified in an 85-ft thickener. The underflow of this thickener was pumped to waste. Efforts to improve quality and yield on the -48-mesh coal were directed toward the use of froth flotation early in the investigation. A review of the fine coal flowsheet indicated that three streams should be considered for treatment by froth flotation. These were the -325-mesh thickener overflow, the -150-mesh cyclone overflow and the -48-mesh boot overflow. Flotation of the thickener overflow was considered basically to improve recovery by upgrading the reject stream so that it could be fed to the filters along with the thickener and cyclone underflows. The overflow from the thickener contained 3.7% solids and had an ash analysis of 33%. Flotation of the cyclone overflow and boot overflow were considered to upgrade coal quality as well as yield. Treatment of the cyclone overflow, a 5.4% solids slurry averaging 27% ash, would eliminate the coal thickener and provide a feed of flotation concentrate and cyclone underflow to the filters. Treatment of the boot overflow would eliminate both the cyclones and thickener and feed only flotation concentrates to the filters. Flotation feed in this

Jan 1, 1962

By R. G. Ward, A. E. El-Mehairy

A technique was developed to calculate the density of liquid metals from the profile of a weighed levitated drop obtained by emitted light photography and calibration. The density of liquid copper was determined over the temperature range 1370" to 2100°K and expressed with the equation: The molar volumes and thermal coefficients of expansion are calculated. Copper, upon melting, was found to expand 3.34 pct. A knowledge of the density of liquid metals is essential as it is a parameter appearing in most theories of the liquid state. The liquid density is also necessary for the calculation of the commercially important contraction occurring on solidification. Unfortunately good density values are rarely available and the present work was undertaken to establish a new method of density determination free from the limitations of the existing methods. For liquid metals with high melting points, the variation and the limited number of density values reported in the literature have been caused primarily by difficulties in technique, a matter which has been adequately discussed by Urbain.&apos; In all the methods used for measuring the density of the high-melting liquid metals there are sources of error, and corrections have to be made. For example, in the method of balanced columns, the formation of gas bubbles in one or both arms was a great source of error. In the pyknometer3 and immersed-sinker methods, corrections of certain volumes for thermal expansion to the operating temperature exceed 4 pct. In the maximum-bubble method5 a correction for the thermal expansion of the bubble-tube is used (about 1.6 pct); a second correction takes into account the change in the volume of liquid displaced by the bubble-tube (about 3.5 pct). Another method used is based on the shape of a drop of liquid, at rest on an inert refractory plaque, obtained photographically or radiographi-cally. The volume is calculated from the shape, which is sensitive to the surface tension and supporting material, by some intricate empirical relation. The drop contour changes with 90 deg rotation of the support.7 The application of all methods is limited by reaction between liquid metal and the apparatus. The successful stabilization of a mass of liquid metal during levitation melting8 afforded a technique for measuring the density of liquid metals out of contact with solid materials. The technique was developed by using copper as the density of liquid copper has already been studied extensively, thus allowing comparison with the new method. It consists of calculating the volume from the dimensioned profile of the levitated drop obtained by emitted-light photography and careful calibration. The molten egg-shaped drop spins around the magnetic axis of the coil (lined vertically) at a speed which seems to increase with increasing temperature. The method does not involve corrections and the experimental setup allows the use of vacuum or special atmospheres. The maximum operating temperature is limited by excessive evaporation of metal from the droplet. EXPERIMENTAL Levitating System. A stabilizing ring was used in conjunction with a 3-turn levitating coil energized by a 450-kc per sec, 10-kw Toccotron with a high current-low voltage output stabilized to f 1 pet.&apos; APyrex glass tube with a Pyrex Optical flat window inserted through the coil and ring allowed the use of special atmospheres during levitation melting, as shown in Fig. 1. Optical System. Fig. 1 shows the optical arrangement used to photograph the profiles of the drop, parallel and perpendicular to the vertical spinning axis, simultaneously on the same frame of a high-speed 35-mm film. The optical system was adjusted to avoid any distortion of the profiles and to ensure that both profiles are in focus. The length of path from object to objective was about 30 cm, and a magnification factor close to 1 was obtained with the single-lens reflex-camera system. Temperature Measurement and Control. In operation, the specimen temperature was constant to 5 C for a fixed power input to the levitating coil and fixed rate of gas flow through the tube. The temperature was measured by an automatic two-color pyrometer (Coloratio) checked at the melting

Jan 1, 1963

By J. C. Martin

A theoretical analysis of steam stimulation is presented for single sands. The analysis includes the effect of steam production and most of the effects of heat conduction. The results show the effects of a number of important variables on the performance of an idealized well under steam stimulation. Calculated responses are presented which indicate the effects of steam production, amount of steam injected, water production, formation thickness and formation damage. Results indicate that steam production can cause large reductions in the heat contained in the formation. This effect can be eliminated by drawdown control. Water production reduces the amount of oil produced during stimulation. The optimum amount of steam to inject depends on economic factors as well as the well response. In many cases, the increased temperature resulting from stimulation reduces oil viscosity near the well sufficiently to overcome the effects of formation damage even if the damage is not removed during steam injection. Calculated responses for thin sands are more favorable than anticipated. INTRODUCTION Little has been published on the theory of steam stimulation&apos;-&apos; despite the interest it has created and the wide variation in well responses. The results of the present analysis provide an insight into steam stimulation, and the methods employed provide a foundation for future work. Analyses presented in Refs. 1 and 2 are very limited and apply to gravity drainage conditions. Ref. 3 contains an analysis similar to the one presented here. The idealized models used and the assumptions made in Ref. 3 are different from those used in this paper. The analysis assumes that after steam injection has heated a small portion of the volume within the radius of drainage of a single uniform sand, a shut-in soaking period is allowed before returning the well to production. The effects of gravity, capillarity, transient pressure and water-sensitive sands are neglected. The injection and soaking times are assumed short compared to the stimulated production time. The initial temperature is assumed uniform; thus, the results apply primarily to first-cycle stimulation. The effects of gas production other than steam are neglected, and the water-oil ratio during production is assumed constant. Steam stimulation involves the simultaneous variation of the temperature, pressure and saturations. General mathematical equations for these variations are complicated and can be very difficult to solve. Simplified equations based on idealized models are used to reduce the mathematics sufficiently to allow approximate solutions to be obtained. DISCUSSION INJECTION An idealized model for which heat conduction is neglected is used to represent the behavior of a well during steam injection. The mathematics for this model is presented in Appendix A which also contains an approximate solution for the behavior of the no-conduction model. SOAKING During soaking, the well is shut in. Only the temperature, pressure and saturation distributions at the end of soaking are needed in the analysis. During soaking the heat is considered to be conducted in a uniform medium from an initially uniformly-heated circular cylinder confined to the producing interval. At the end of soaking the saturations and pressures are assumed to correspond to the cold zone. Analysis of the heat flow during soaking is included in the next section. The radius of the heated cylinder is calculated from the following heat balance (for constant quality steam injection). At the end of the soaking period it is assumed that little or no free gas is present near the well, and that the soaking period has been sufficiently long that the steam zone has had time to expand and the steam has condensed. The condition where there is no soaking is considered in the next section. PRODUCTION In this section, an approximate method is presented for solving the equations of heat and fluid flow associated with the production of oil and water during steam stimulation. Where initial pressure drawdowns are sufficient to cause steam to flow into the wellbore, steam production is assumed to occur within a short initial adjustment period (Appendix B). The production practices followed soon after the well is returned to production can have a large influence on the amount of oil produced during the stimulation cycle. Under most conditions, there is a period of time in which some or all of the water in the heated zone is converted into steam and produced. This flashing of hot water is caused by the pressure in the heated zone dropping below