By C. H. Li, R. J. Stokes, S. H. Bendel, J. A. Sartell, T. L. Johnston

The mechanism of the oxidation of high-purity copper has been studied at temperatures from 500° to 981°C employing gravimetric, high-temperature microscopic and inert marker techniques. An investigation of the adhesion of copper oxides was also made. The oxidation of copper is found to be parabolic at all temperatures. It is concluded that the controlling mechanism is the outward diffusion of CU+ ions through the Cu2O layer, but the mechanism of diffusion is modified by the state of compressive stress in the oxide layer at the oxidation temperature. At temperatures below the transition from elastic to plastic behavior of Cu2O the growth stresses reach a value sufficiently high to cause CuO whiskers to be extruded. The extrusion of whiskers results in the injection of a large number of vacancies into the CuO. The Cu20 layer grows by the advance of the CuzO/CuO interface into vacancy-rich CuO. Since there is an adequate supply of non -thermally created vacancies, the activation energy for oxidation is that required to move the Cu+ ion through the appropriate saddle point to a neighboring vacancy, which has been determined to be 20,000 cal per mole. At temperatures at which the Cu20 can deform plastically the stresses are never high enough to cause whiskers to form. thus vacancies must be supplied by themal activation and as a result the activation energy increases to 40.000 cal per mole. ALTHOUGH extensive studies of the oxidation kinetics of pure copper have been made in the past. the mechanism has received relatively little attention. As a result, certain features of the kinetic data have not been satisfactorily explained' For example, several workers1,2 have reported that the activation energy for oxidation in the range from 500° to 700° C was about 20,000 cal per mole whereas that above

Jan 1, 1960

By J. L. Walter

Tungsten ingots with and without small amounts of aluminum, silicon, and potassium were prepared by conventional powder-metallurgy techniques and hot-rolled to 0.001-in.-thick sheet. The ingots were rolled three different ways: I) initially cross-rolled, then straight-rolled; 2) straight-rolled, and 3) straig-ht-rolled, then cross-rolled. Total reductions were 99.8 pct. Samples of the sheet were annealed, in vacuo, at temperatures from 1200" to 2200°C. Substructures and textures were determined by transmission electron microscopy and X-ray diffraction. The doping agents were found to form particles of mullite (Al,Si,O,,) which, on rolling., appear to form strings of particles aligned parallel to the rolling direction. These strings of purticles are associated with an increase in the recrystal-lizution temperature from 1400°C for undoped sheet ThE addition of small amounts of aluminum, silicon, and potassium to tungsten has a profound effect on the grain structure of drawn and recrystallized wire.'" The grains generally do not occupy the entire cross section of the wire and have lengths many times the wire diameter. The grain boundaries are, in general, nearly parallel to the wire axis and have long ''fingers" projecting one into the other as may be seen in Fig. 1, a longitudinal section of recrystallized doped wire. When unsuitable additions or no additions are made or the wire is not sufficiently reduced during draw- to 2000°C for doped sheet. The particles also limit lateral grain growth while allowing growth parallel to the rolling direction. This results in the formation by primary re crystallization of large highly elongated grains of specific preferred orientation. The undoped sheet recrystallized to small equiaxed gains. The preferred orientations of the large grains were determined from axis density plots to be (113) (691). (0i3) (362), (116) (304) types for the initially cross-rolled then straight rolled material. These orientations are similar to the orientations of the large elongated grains in doped and heavily drawn tungsten wire. The nucleation of the large grains appears to occur by recovery of certain of the polygonized regions of specific orientation, followed by strain-induced boundary migration.

Jan 1, 1968

By C. S. Yust, J. W. Smith, J. R. Walsh, R. E. Simpson

This paper presents the results of a complete reservoir studv designed to determine a sound economic program for the conservation of oil and gas in the Pickton field, Hopkins County, Texas. The Pickton field produces from the Bacon Lime with all indications of the study being that production is predominately by dissolved-gas drive. Calculations of the total ultimate recovery to be expected under primary operations indicated only 16.7 per cent of the oil originally in place would be recovered. This unusually low recovery is due to the type of drive operating and the extremely high dissolved gas-oil ratio and shrinkage. Results are presented for six plans of returning gas to the reservoir, evaluated to determine (1) comparative recoveries and economics of (a) returning gas at a constant rate by supplementing Pickton gas with extraneous gas during the early portion of the operation, and (b) conventional gas-return operations without using extraneous gas, and (2) the optimum size of compressor plant for each type of pressure maintenance. The over-all economic program considers, for either type pressure maintenance operation. a gasoline plant to process the unusually rich casinghead gas. Since pressure maintenance will disturb equities, pooling of royalties is in the case of Pickton a prerequisite to conservation of oil by this type of operation, both from an economic and legal standpoint. In the event pooling of royalties cannot be achieved, the study considers a gasoline plant to operate under a modified primary production operation which will make the conservation of gas possible. INTRODUCTION The Pickton field, located in Hopkins County, Texas. was discovered in November, 1944. by the completion of Humble's C. D. Nichols 1, in the Bacon lime of the Lower Glen Rose formation, through perforations from 7,888 to 7.896 feet. The well initially produced 50.2 API gravity oil with a gas-oil ratio of 1,350 cubic feet per barrel. Subsurface samples of the reservoir fluid obtained soon after completion of the discovery well showed that the Pickton crude is unique in that it has an extremely high dissolved gas-oil ratio and is subject to very severe shrinkage. Calculations of the future behavior of the Pickton reservoir indicated that ultimate oil recovery by primary operations would be 3,269,000 barrels, representing only 16.7 per cent of the oil in place (19,577,000 stock-tank barrels), and that recovery could be substantially increased by returning the produced gas. The cumulative production of 1,382,694 barrels on November 1: 1947, amounted to 42.3 per cent of the estimated ultimate oil recovery from primary operations. The purpose of this study is to determine and evaluate the optimum program for conservation of oil and gas in the Pick-ton field, including the desirability of conducting gas-return operations and of installing a gasoline plant. LOCATION AND DESCRIPTION Pickton Field, The Pickton field, as shown in Fig. 1, is located in southwest Hopkins County, Texas, 12.5 miles southwest of the New Hope field, 2.7 miles northeast of the Coke field, 16 miles southwest of Sulphur Springs, and 8 miles northwest of Winnsboro, Texas.

Jan 1, 1949

By C. S. Yust, J. W. Smith, J. R. Walsh, R. E. Simpson

This paper presents the results of a complete reservoir studv designed to determine a sound economic program for the conservation of oil and gas in the Pickton field, Hopkins County, Texas. The Pickton field produces from the Bacon Lime with all indications of the study being that production is predominately by dissolved-gas drive. Calculations of the total ultimate recovery to be expected under primary operations indicated only 16.7 per cent of the oil originally in place would be recovered. This unusually low recovery is due to the type of drive operating and the extremely high dissolved gas-oil ratio and shrinkage. Results are presented for six plans of returning gas to the reservoir, evaluated to determine (1) comparative recoveries and economics of (a) returning gas at a constant rate by supplementing Pickton gas with extraneous gas during the early portion of the operation, and (b) conventional gas-return operations without using extraneous gas, and (2) the optimum size of compressor plant for each type of pressure maintenance. The over-all economic program considers, for either type pressure maintenance operation. a gasoline plant to process the unusually rich casinghead gas. Since pressure maintenance will disturb equities, pooling of royalties is in the case of Pickton a prerequisite to conservation of oil by this type of operation, both from an economic and legal standpoint. In the event pooling of royalties cannot be achieved, the study considers a gasoline plant to operate under a modified primary production operation which will make the conservation of gas possible. INTRODUCTION The Pickton field, located in Hopkins County, Texas. was discovered in November, 1944. by the completion of Humble's C. D. Nichols 1, in the Bacon lime of the Lower Glen Rose formation, through perforations from 7,888 to 7.896 feet. The well initially produced 50.2 API gravity oil with a gas-oil ratio of 1,350 cubic feet per barrel. Subsurface samples of the reservoir fluid obtained soon after completion of the discovery well showed that the Pickton crude is unique in that it has an extremely high dissolved gas-oil ratio and is subject to very severe shrinkage. Calculations of the future behavior of the Pickton reservoir indicated that ultimate oil recovery by primary operations would be 3,269,000 barrels, representing only 16.7 per cent of the oil in place (19,577,000 stock-tank barrels), and that recovery could be substantially increased by returning the produced gas. The cumulative production of 1,382,694 barrels on November 1: 1947, amounted to 42.3 per cent of the estimated ultimate oil recovery from primary operations. The purpose of this study is to determine and evaluate the optimum program for conservation of oil and gas in the Pick-ton field, including the desirability of conducting gas-return operations and of installing a gasoline plant. LOCATION AND DESCRIPTION Pickton Field, The Pickton field, as shown in Fig. 1, is located in southwest Hopkins County, Texas, 12.5 miles southwest of the New Hope field, 2.7 miles northeast of the Coke field, 16 miles southwest of Sulphur Springs, and 8 miles northwest of Winnsboro, Texas.

Jan 1, 1949

By E. G. Banks

This paper is presented in the belief that metallurgists and chemists will be interested in the practice of grinding in tube-mills in connection with stamps, especially since the records of working here given extend over a lengthy period of time (since May, 1905). The ore from the Waihi mine—more especially that produced in the upper levels—contains a large proportion of hard, chalce-donic quartz, and the gold exists in an exceedingly fine state, conditions which necessitate very fine crushing in order to obtain a high extraction of the precious metal. Before the introduction of tube-mills at the 90-stamp Waihi mill, it was found necessary to stamp through 40-mesh (1,600 holes per sq. in.) woven wire-screens, having a fairly high discharge. The pulp then graded : Per Cent. Per Cent. On 50-mes11, .- 0.1 On l20-mesh ..8.77 On 60-mesh, . 8-74 On 150-mesh,.... 7.48 On 80-mesh,... 16.06 Passed 150-mesh,... 55.19 On 100-mesh,.... 3.66 The stamp-dnty was 2.89 short tons per stamp per day, or a total of 260 tons daily. Although the extraction on this pulp was: gold, from 88 to 90 per cent., and silver, from 74 to 78 per cent., it was recognized that finer grinding of the sands would prove beneficial, provided a machine could be found to do this work economically. Various grinding-mills and pans were tried, but without satisfactory results, the particles of sand being so hard that the capacity of any of the machines was too small to be economical. The results of grinding in tube-mills in other countries were so satisfactory that three tube-mills mere erected at the Waihi

Jan 1, 1908

By N. A. Gjostein

From their study of the anisotropy of grain boundary mobility in aluminum, the authors conclude that tilt boundaries have a higher mobility than twist boundaries because the atomic misfit at the pure-twist boundary is relatively small compared to the misfit at a tilt boundary for a given amount of misorientation. If this is true, then one would expect a twist boundary to have a lower grain boundary energy than the corresponding tilt boundary. Fig. 6, taken from the work of Gjostein and Rhines,10 shows that this is indeed the case for [001]-cu tilt and twist boundaries in the high-angle region, thus lending support to the authors' conclusion.

Jan 1, 1968

By J. H. Brophy, A. I. Prill

The authors have previously investigated the solid-state activated sintering of tungsten powder with various Ni-Cu additions.' Log shrinkage vs log time plots showed changes in slope from 4 to x at intermediate times during the sintering process. This was attributed to a change in the rate-controlling mass-transport process from solution of tungsten into the tungsten-alloy interface to diffusion of tungsten in this interface. It was postulated that the melting of the activating layer should not affect this transport process. However, the superposition of rearrangement due to the presence of a liquid phase complicates the data analysis. It is the purpose of this note to apply the analysis of Prill, Hayden, and rohy' to account for "rearrangement shrinkage'? in liquid-phase sintering of the W-Ni-Cu system. This results in "solution-precipitation stage" shrinkage plots which were comparable to those obtained in solid-phase activated sintering of the same system. If one assumes total shrinkage to be the sum of rearrangement and solution precipitation, the effects can be isolated easily.2 This results in the general equation:

Jan 1, 1967

By F. W. Jessen, John C. Miller

In many areas where carbonate rocks form important parts of the stratigraphic sequence, stratigraphers have experienced varying degrees of difficulty in differentiating and correlating limestone and dolomite units in both surface and subsurface work. With early Paleozoic rocks of the Mid-Continent, insoluble residues yield a remarkable amount of strati-graphic data and relatively good correlations may be carried over broad distances.' Unfortunately, neither such information nor electric logs and radioactive logs have been particularly helpful in interpreting the limestone sections of the Permian Basin of West Texas. This is because: (1) the variations in the sections may be very slight; (2) no completely satisfactory method of interpretation has been developed; and (3) the measurements themselves are not sensitive enough for small variations. Also, such logs are influenced by the fluid content. Paleontology and micro-paleontology remain the ultimate arbiters. As a routine tool, however, paleontol-ogical examination is slow and tedious. Chemical analysis may be used, but this, too, is extremely slow. Although rocks are not classified according to chemical composition, there is considerable variation with rock types. Correlation by chemical composition has two advantages, first, the characteristics determined are subject to minimum human error and interpretation, and secondly, the lithologic changes are not masked by fluid content as in the case of electric and radioactive logs. Some fossils concentrate certain elements which tentatively might be used to date rock units.' Rapid chemical analysis by spec-trographic means could be used as an adjunct to other means employed in correlation work, or might, in itself, present a suitable method. PURPOSE OF THIS INVESTIGATION Sloss and Cooke' have published data concerning spectrographic analysis of limestone rocks specifically for purposes of direct correlation of a single formation. These authors found satisfactory evidence that differences in percentage of four elements (Mg, Fe, Al, and Sr) in the Mississippian limestones of northern Montana were useful in carrying out correlation of this formation over a distance of approximately 50 miles. It was concluded from the preliminary work that the spectrochemical method offered possibilities of solution of some problems of correlation heretofore not possible. Since the work of Sloss and Cooke' was confined to one particular limestone zone, extension of the use of the method to examine two or more geologic formations would aid materially in the over-all problem of correlation of such rocks. Equipment is now available commercially with which very rapid spectrographic analyses may be made, and hence the problem was to determine whether the variations existing in the minor constituents of limestones were sufficient for use in possible correlation. Qualitative and semi-quantitative investigations were made to determine whether significant changes in the chemical condition occurred. It was a further purpose to investigate the geologic time-boundaries to see whether significant chemical variation could be found corresponding to the paleontological breaks. It was desirable to attempt correlation of a thick section of limestone or dolomite rock and to have as much information as possible on the section. Furthermore, it was felt that examination of formations more difficult to correlate by other means would enhance the value of the method should definite points of correlation be found. Samples were chosen from the Chapman-McFarlin Cogdell No. 25 well in the Cogdell field, Kent County, Tex., and from the General Crude Oil Co., Coleman No. 193-2 well in the Salt Creek field, Kent County, Tex. These fields belong to the famous series of "Canyon" reef fields of West Texas. Cores from the above wells were available from the United States Geological Survey, Austin, Tex. THE SPECTROGRAPHIC METHOD The choice of procedure to be followed in this investigation was based on the anticipated requirements peculiar to the problem. Since the problem was primarily to investigate the possibilities of applying the spec-trograph to problems of correlation in thick carbonate sections, a precise quantitative analysis did not appear necessary. A qualitative analysis to show the possible absence of presence of any element, or a semi-quantitative analysis of the elements present to show the relative changes in magnitude of selected elements was required. Both types of analysis were employed. The two most widely applied methods of semi-quantitative estimates are those of Harvey and of Slavin4,5 though various other procedures have been described.6 while the Harvey method has been modified by Addink,7 this refinement did not seem necessary to the present problem. Essentially, the procedure employed is a variation of the total energy method of Slavin with two exceptions: (1) stressing matrix effect, and (2) using densitometer measurements. As measured by a densito-

Jan 1, 1956

By Robert Maes, Robert de Strycker

The Cu-Sn-As systeM was studied in the region near the Cu-42 and (214-As binary diagrams, where reactions in the solid state appear, resulting from the decomposition of the y(Cu-Sn) phase and from the formation of the 7 phase (Cu,As). The techniques used were microscopic observation, thermal analysis by dilatometry, and X-vay diffraction. The formation of the 7 phase gives rise to a ternavy pevitectoid veaction; the decomposition of the y phase gives rise to five transitional reactions. The temperatures of almost all these reactions could be determined; in the most favorable cases , the accuracy of this determination was of 11.5-C. The 7 phase is stabilized by tin additions, the arsenic atoms being replaced by tin atoms up to 35 pct; this has allowed the preparation of pure j) phase and the confirmation, by extrapolation, of the conrposition of this compound in the Cu-As diagram. In the first part of this work, the solidification reactions in the Cu-Sn-As phase diagram were studied. In the copper corner, the structure of the alloys presented the evidence of reactions in the solid state: on the one hand, all the alloys containing the y phase of the Cu-Sn diagram showed, under the microscope, that this phase had formed different decomposition products after complete solidification; on the other hand, the appearance of the 7 phase of the Cu-As diagram necessitated the introduction of a peritectoid formation reaction. The study of the decomposition of the y phase has been done by preparing about forty alloys that were homogeneous y at high temperature. The formation of the 7 phase has been studied by means of a few alloys with a composition near the homogeneity field of this phase at room temperature. The part of the Cu-Sn phase diagram of interest for this study is represented by Fig. 1, with the phase designation which will be used in the remainder of this paper; it is drawn after Hansen and Anderko.' The Cu-As diagram has already been presented in Part I of this work; the significant features of this study are the existence of the arsenides CusAs and Cu5Asz, and the formation of a compound CUEAS, designated as the 7 phase, by a peritectoid reaction at about 325°C. EXPERIMENTAL METHODS The fundamental technique for the investigation of this part of the Cu-Sn-As constitution diagram was microscopic observation; the greatest part of the observed alloys has also been subjected to thermal analysis by dilatometry; a few selected alloys have then undergone an X-ray analysis by powder diffraction. Alloy Preparation. The alloys were prepared from the same products as in Part I of this study: cathode copper, arsenic with a purity better than 99.5, and tin with a purity of 99.98. The fusion of the ternary alloys was realized from

Jan 1, 1967

By D. M. Blacknall, N. N. Winogradoff, E. W. Williams

Low-temperature measurements of photolumines-cence were used to evaluate the progvess in materials development. Variation of the impurity type, impurity concentration, and method of growth were used to clarify the chemical origin of defects in GaAs. Melt-g~ozun, epitaxial vapor-, and solution-grown samples were studied. A comparison of measurements at 77" and 20°K shows that more defects can be observed at the lower temperature. Th'vee residual defects were identified in relatively pure GaAs. These were: silicon, copper, and a gallium vacancy-donor complex. Solution growth from a gallium solution inhibits the formation of the latter two. Eleven defects were studied and the "optical" activation energy of some of these, namely, silicon, cobalt, and chromium, has not been reported in the literature before. THE discovery of the injection laser in 1962 prompted extensive measurements of the photoluminescence of GaAs. The measurements were made at 77°K on GaAs doped with shallow impurities at various doping levels and compared with electroluminescence1'2 and absorp- tion data.374 In addition, lower-temperature studies were made on relatively pure GaAS' and on GaAs doped with oxygen,5'" manganese,' and copper.' The observation of defects* in GaAs with photolu- *The word "defects" ~efers to both chemical impurities and native defects. minescence at low temperatures makes photolu mines-cence an invaluable tool in evaluating the progress in materials development. The only previous evaluation was done at 77°K when solution-grown and melt-grown GaAs were compared.O No identification of defects was made but it was shown that some of the deep-level luminescence seen in melt-grown GaAs was absent in solution-grown GaAs. The present work extends the comparison of preparation techniques to lower temperatures and to a study of epitaxial vapor-grown GaAs. It is particularly valuable for thin epitaxial layers since they cannot be analyzed by conventional analytical techniques. In addition, by varying the impurity type and impurity concentration the chemical origin and nature of defects in GaAs was demonstrated. Eleven defects were studied in all. Three of the defects were identified as residual defects which often contaminate GaAs prepared from the melt and the vapor. Only one such defect was observed in GaAs grown from a gallium solution and this was identified as silicon.

Jan 1, 1968

By R. G. Aspden

The cold rolling and annealing textures were studied for 3 pct Si-Fe grains initially (001) [hkl]. A concentration of (001) [loo] primaries were observed only in the annealing textures of crystals initially having [loo] within 8 deg of the rolling direction. Eke annealing textures of the (001) [I101 cold rolling textures were sensitive to the initial orientation of the grains. Single crystal data were used to explain the formation of (001) [loo] in poly-crystalline malerial. CUBE texture formation in 3 pet Si-Fe sheet occurs during the final high temperature anneal. Its formation is dependent on the proper distribution of (001) plane primaries with reference to the rolling direction&apos; and on the growth of these primaries by secondary recrystallization. The selective driving force for these primaries with (001) within 7 deg of rolling plane is derived from the difference in surface energy between the annealing atmosphere and the crystallographic planes exposed at the surface of the sheet.&apos;-= The alignment of [loo] directions of (001) secondaries with the rolling direction is required for optimum magnetic characteristics7 and is dependent on processing.&apos; A high degree of alignment has been observed when the final cold rolled texture has a strong (111) [ll2] type component3 and the normal grain growth texture prior to secondary recrystallization has components with a [loo] parallel to the rolling direction and planes from (001) to (110) parallel to the rolling plane.1,3,8,9 Generally, this (001) component is much weaker than the (110) component. The growth rate of (001) plane primaries to secondaries has been found to be independent of the orientation of the primaries with reference to the rolling direction, i.e., the secondaries have the same degree of alignment of [loo] directions with the rolling direction as the (001) primaries.&apos; Hence, the rolling and annealing textures of individual grains or single crystals are of interest in understanding the development of the (001) [loo] secondary recrystallization texture. (001) components have been observed in the annealing textures of cold rolled grains initially having a [loo] parallel to the rolling direction and an (001) rotated up to 30 deg from the rolling plane. Crystals initially near the (001) [loo] orientation when rolled under the influence of constraints imposed by neighboring grains form deformation bands and ro- tate in both directions toward (001) <110>.10,11 Deformation bands have been reported also for crystals initially with an (001) within 1 deg of the rolling plane and a [loo] within 1 deg of the rolling direction when rolled as a free single crystal.12 These crystals have weak recrystallization textures and contain near an (001) [loo] component.10-12 When near (001) [loo] crystals are rolled as free single crystals no deformation bands form and the crystals rotate by a single rotation toward (001) [110]. Recrystallization after a 70 pct cold reduction yielded near an (001) [loo] component13 and after a 90 pct cold reduction an (001) [I201 component." Crystals initially near (210) [001] had a texture after a reduction of 70 and 84 pct which was similar to the (111) [li2] but rotated 10 to 15 deg in the transverse direction. These crystals recrystallize to (210) [OOl] or (410) [001] and contain an (001) [loo] component.10,13 An (001) component has not been detected in the normal grain growth textures of other single crystals. Crystals initially having orientations between (110) [001] and (111) [ll2] have a cold rolled texture of principally (111) [ll2] .10>16 Other crystals with a [I101 parallel to the cross direction rotate to (111) [112] and/or (001) [110] stable end orientations. Crystals initially having from (001) [110] to (111) [lie] retain this orientation after cold rolling.15 The cold rolled textures having [I101 directions parallel to the rolling direction had components in the annealing textures related to the deformation textures by 25 to 30 deg rotations about common (1 10) poles. Cold rolled textures of the (111) (112) type recrys-tallized to (120) [001] or (110) [00l]. The purpose of the present work was to further the understanding of the alignment of [loo] directions of (001) secondaries with the rolling direction. The cold rolling and annealing textures of grains initially (001) [hkl] were studied. These data were applied to the formation of (001) [loo] by secondary recrystallization. PROCEDURES AND EXPERIMENTAL TECHNIQUES The (001) poles near the sheet normal and rolling direction are given in Fig. 1 for the 10 grains studied. Each of these grains was located in the center of a polycrystalline specimen approximately 25 mm wide and 50 mm long. The lower case lettered grains, a through dl were about 1.2 mm in diam and near the (001) [loo] orientation. Specimens containing these grains were from a commercial 3 pct Si-Fe alloy with the principle orientation of (110) [001] as obtained by impurity inhibition of growth with manganese sulfide inclusions.17,18 Upper case lettered grains, A through F, were about 6 mm in diam and had (001) planes near the rolling plane and [hkl] di-

Jan 1, 1963

By B. Alexander, G. Derge W. Peifer

This is part of a research project in the Metals Research Laboratory of Carnegie Institute of Technology, sponsored by the Carnegie-Illinois Steel Corporation. In organizing our program it became apparent that the problem of analyzing molten steel for hydrogen must be divided into two parts: (I) the correct analysis of a given sample, and (2) the correct sampling of the bath. Emphasis has been placed upon these divisions in the order named because methods of sampling cannot be evaluated until a satisfactory method of analysis is available. Vacuum fusion was selected from the list of possible analytical methods because it seemed to us to offer the best possibilities for giving rapid, accurate results on solid steel samples. A number of objections have been raised against this method as usually practiced. We have sought to meet some of these by proper design of the apparatus. Experiments will be described which show that others are not valid. In the conventional apparatus the sample is held under high vacuum for a period of several hours before it is actually analyzed and one might expect considerable hydrogen to escape during this period. We have provided a means of introducing the sample to the vacuum just before analysis. Another difficulty has been that the entire apparatus has been designed primarily for the purpose of analyzing for oxygen, which constitutes upward of go per cent of the total gases evolved from the sample The volume and pressure measurements have therefore been insensitive to the relatively small amounts of hydrogen present. This difficulty obviously can be taken into account in any apparatus designed especially for the amounts of hydrogen expected. Analysis in Vacuum-fusion Apparatus A number of experiments were carried out to determine the importance of several factors that have been stated as possible sources of error or uncertainty in vacuum-fusion analysis for hydrogen; namely, that hot graphite will absorb some of the gases, that metal vapor will cause discrepancies, and that low results may be obtained as a result of the water vapor (produced by the oxidation of the hydrogen) dissolving in the butyl phthalate of the manometer, or that the blanks obtained from the apparatus are so great as to make the method inaccurate. The experiments also checked on the accuracy and feasibility of using differential freezing as a method of gas analysis in a vacuum-fusion apparatus.

Jan 1, 1945

By R. M. Hudson

A study has been made of the decarburization of low-carbon sheet steels at temperatures from 1100" to 1475°F in mixtures containing hydrogen, nitrogen, water vapor, and in some instances carbon monoxide. Decarburization occurs principally by the reaction C (in steel) + H20 = CO + H2 and follows a first-order rate law. The decarburization rate appreciably increases with an increase in temperature up to about 1325°F, but the increase in rate is small with fur- Use of a dry hydrogen atmosphere results in a relatively slow decarburization of steel and use of a wet hydrogen atmosphere results in relatively rapid decarburization. It is now generally recognized&apos; that the reaction C (in steel) + H2O = H2 + CO [l] accounts for most of the decarburization that occurs in wet hydrogen-containing atmospheres. The present article is concerned with the decarburization of low-carbon sheet steel in H2-N2 atmospheres ther increase in temperature. The limiting rate of decarburization can be predicted from a knowledge of the solid solubility and diffusivity of carbon and this rate is approached as the water-vapor content of an atmosphere is increased. Hydrogen contents above about 8 pct are beneficial only in that they permit higher levels of water vapor to be used without oxidation of the steel. A buildup of CO in the atmosphere lowers the rate of decarburization. containing various amounts of water vapor and carbon monoxide. The effectiveness of these atmospheres and the influence of temperature on decarburization rate will be considered. EXPERIMENTAL WORK The chemical compositions of the three steels used in decarburization-rate studies are listed in Table I. Steel A was a commercially hot-rolled rimmed steel that was cold-reduced at the Laboratory to furnish specimens 0.025, 0.041, and 0.059 in. thick. Most of the experiments in which this steel was used were made on the 0.041-in.-thick material. Steel B and Steel C were cut from 0.010-in.-thick commercially cold-reduced coils that were

Jan 1, 1963

By R. Kerby, T. R. lngraham

The rates of cadmiuln cementation from buffered solutions were studied on both the cylindrical and circular faces of a rotating zinc disk. The activation energies are equivalent on both surfaces, but the rate is more rapid on the cylindrical face. At higher temperatures and at pH values above 6.4, the rate of deposition increases because of an increase in the cathodic area of the deposit. The rate may also be increased by decreasing the thickness of the diffusion layer by rapid stirring. The presence of small amounts of copper, cadmium, lead, iron, or aluminum in the zinc does not affect the cementation rate, but when srnall amounts of copper, cobalt, and arsenic were present in the solution cadmium deposition ceased shortly after it started. Small amounts of copper in solution become cemented with the cadmium to form a coarse deposit of Cd3Cu. When zinc ores containing cadmium are processed for electrolysis, the cadmium appears with the zinc in the leach liquors. Because of the discharge potential of the cadmium ion and the hydrogen overvoltage on metallic cadmium, the cadmium ion must be removed prior to zinc electrolysis to prevent its codeposition. Cadmium is usually removed from acidic zinc sulfate solutions by cementation on zinc. When zinc sheets are used with the appropriate conditions of pH and temperature, a finely divided, high-purity cadmium powder is obtained; it floats to the surface with attached hydrogen bubbles and, after careful washing, may be processed directly to a marketable product.&apos; The reaction on zinc sheets is relatively slow because of the limited amount of exposed cathodic area on the sheets. A much more rapid reaction is obtained when zinc powders are stirred into the solution, but this procedure does have a potential disadvantage: some unreacted zinc may be trapped in the cemented cadmium and thus lower its grade.1 The equilibrium constant at 25°C for the displacement of cadmium by zinc is of the order of lo", which indicates that at equilibrium the displacement would be essentially quantitative and no back reaction need be considered. This indication is not entirely true, however, because in the presence of oxygen any loose cadmium which is out of contact with metallic zinc tends to redissolve after cementation.&apos; The overall effect is much the same as that to be expected if the equilibrium constant were much smaller. Previous experimental work on cementation reac- tions3 is in general agreement that the rates of cementation usually follow first-order kinetics. The metal on which cementation occurs is considered to consist of anodic areas from which metal dissolves and cathodic areas onto which the reactive metal is cemented. For the reaction to continue, the cemented deposit must remain open and porous for the removal of ions. Usually, the deposited metal influences the rate of cementation; when it blocks the pores in the deposit, the rate of cementation will be decreased. Alternatively, when the cemented metal grows as den-drites or as coarse powder the cathodic area is correspondingly increased and the rate of cementation increases,3 Thus, it is only during the initial stages of cementation, prior to the development of deposit effects, that the kinetic behavior of the reaction may be studied without ambiguity. In this paper, experiments will be described for cementation of cadmium from dilute solutions onto the surface of a rapidly spinning zinc cylinder. The effects of ionic concentration, disk rotation speed, temperature, and impurities will be described. APPARATUS AND PROCEDURE The apparatus used for the experiments was described in a previous paper.4 It consisted of a 2-liter vessel in which the contents were protected, against oxidation, by a stream of prepurified nitrogen. The vessel was immersed in a water bath which controlled

Jan 1, 1970

By C. D. Stahl, R. Sandrea

This investigation was made to evaluate the comparative effects of the viscosity and the phase behavior of the buffer fluid in the composite solvent displacement of Bradford crude from waterflooded sandstone cores. Buffer slugs of propane, naphtha and other refined hydrocarbons exbihiting increasingly favorable viscosity ratios and decreasing solubility relationships, respectively, with Bradford crude, were used in long Berea sandstone cores. The secondary slug was isopropyl alcohol. The results indicate that higher oil recoveries are obtained for increasingly favorable phase relationships even when these are accompanied by unfavorable viscosity ratios within the range studied. Moreover, when propane is used as a buffer slug with an adverse viscosity ratio of 36, it gives higher oil recoveries than at a similar size slug of an any1 alcohol having a viscosity ratio of 1.09. The investigation was extended to the study of the effect of flooding rate on oil recovery. Residual Bradford crude was displaced from a 6-ft Berea sandstone core at rates varying from 0.3 to 30 ft/ day. The results show that as flooding rates were increased above or decreased below a minimum range of 1 to 2 ft /day, displacement efficiency increased considerably. INTRODUCTION In recent years, the alcohol slug process as a means of tertiary recovery has been the subject of many investigations. Gatlin and Slobod showed the advantages of the combination solvent slugs over the previous single-slug process.1 The combination slugs require less total slug material to obtain similar oil recoveries. The basic combination process involves injecting a primary or buffer solvent which is preferentially oleophilic, followed in turn by a water-driven slug of isopropyl alcohol. This procedure ensures that the buffer slug, which is miscible only with the reservoir oil, displaces and replaces the oil and is in turn displaced, together with the water, by the isopropyl alcohol slug miscible with both fluids. Likewise, for those reservoir oils that show some degree of phase incompatibility with isopropyl alcohol, as does Bradford crude, a proper buffer solvent can artificially make the alcohol process technically feasible. From an economic standpoint, propane or LPG would be the most appropriate primary solvent to be used in the field; however, Taber, et a12 have indicated that the alcohol process becomes highly inefficient in the displacement of light hydrocarbons because of the entrapment of these hydrocarbons during the stabilized bank formation. Moreover, since materials such as propane have such low viscosities, adverse viscosity ratios with most reservoir oils would be penerated, thereby possibly further reducing the efficiency of the buffer solvent. This paper presents the results of an experimental study of the comparative effects of viscosity ratio and phase relationships on the displacement efficiency of Bradford crude by means of dual solvents. The work was extended to include the effect of flooding rate on oil recovery. Rates within the range of field and laboratory values were used. EXPERIMENTAL PROCEDURE APPARATUS The porous media used in this study consisted of two 10-ft and one 6-ft Berea sandstone cores, 3-in. in diameter. These were cast in galvanized steel pipe of 31/2-in. ID and the annulus was filled with Armstrong cement. The 10-ft cores were assembled by connecting two 5-ft units, which were joined together by 8-in. steel flanges fitted to the pipe. Intimate contact between the two sections was obtained by inserting a thin disk of the same sandstone between the core faces. The outlet and inlet ends of the cores were covered with threaded pipe caps. The injected fluid was gravity fed to two variable-rate positive-displacement pumps. The fluids were filtered before entering the core and the effluent was collected in an automatic fraction collector and

Jan 1, 1966

By L. A. Dale, D. A. Dahlstrom

Closed-water circuits are justified today from two standpoints: economical operation and prevention of stream pollution. In today&apos;s modern preparation plant, it has been found very desirable to have the plant circulating water maintained at a relatively low solids concentration of around 3%. In so doing, bene-ficiation equipment can operate at a much higher efficiency. However, makeup water requirements would become excessive if the fines were to be removed from the preparation plant by bleeding a 3% solids concentration to a tailings pond. With the ever increasing percentage of —200 mesh coal, clay and slimes in the raw coal, coupled with the creation of these fines within the preparation plant, the need for water conservation for economy reasons becomes even more important. Because of stream pollution laws, tailings ponds have become very costly to operate and maintain, resulting in the necessity of employing an in-plant method of water recovery. Accordingly, the primary system employed in water recovery in the coal preparation plant today consists of a solids concentration device to thicken refuse solids while at the same time producing a sufficiently clarified effluent that can go back to the preparation plant for water reuse. The thickened product is then normally passed to a dewatering device that will produce a handleable solid that can be disposed of

Jan 1, 1965

By S. Shapiro, R. G. Ames

Background Research on the respiratory health of coal miners has focused predominately on the relationship between coal mine dust exposure and ventilatory function impairment (Lapp et al., 1972; Jacobsen, 1976), on the prevalence of coal workers&apos; pneumoconiosis (Lainhart et al., 1969; Morgan et al., 1973), and on coal miner mortality (Ortmeyer et al., 1974; Rockette, 1977). Lesser attention has been paid to the effects of other mining exposures. For example, underground exposure to diesel exhaust emissions (Reger et al., 1980; Ames et al., 1982,1984). An omission in US coal mining research, however, has been identified by the US Office of Technology Assessment (OTA) as the failure to study the effects of inhaled polyvinyl chloride (PVC) thermal decomposition and combustion products (Seltzer, 1979). These products may be released in the mine environment by cable fires, cable explosions, smoldering cables, and conveyor belt fires. In addition to the OTA concern, recent findings of chronic respiratory conditions and other health complications resulting from exposure to PVC decomposition and combustion products in firefighters (Peters et al., 1974; NBS, 1980; NIOSH, 1982; Wallace, 1982), and in survivors of several large scale PVC-fueled fires (Dyer and Esch, 1976; Wallace, 1981, 1982), add immediacy to the concerns. PVC decomposition and combustion PVC decomposition is initiated at temperatures far below ignition (Hartstein and Forshey, 1974; Wallace, 1981). Hence, exposures to decomposition products from smoldering cables may be important health hazards in addition to cable insulation combustion products. Hydrochloric acid (HCL) appears to be the principle toxic substance from the thermal decomposition of PVC since up to 60% by weight is released as HCL (Barrow et al., 1979). HCL is released both as a gas and as an adsorbant on soot particles (Stone et al., 1973), thus allowing penetration of respiratory defenses. In addition, laboratory results indicate that phosgene (carbonyl chloride), a potentially lethal gas, may be produced in significant quantities from electrical arcing of wires covered with PVC insulation (Woolley, 1971; Brown and Birky, 1980). Health concerns related to PVC Toxic effects resulting from high level exposures to PVC pyrolysis and combustion products in animals (Cornish and Abar, 1969) and in humans (Wallace, 1981) is beyond question. Analyses have reported acute, or short-term, health effects resulting from exposure to PVC decomposition and combustion products (Peters et al., 1974; Polakoff et al., 1975). Recently, however, several studies have found that acute effects are often followed first by apparent healing, and then by delayed chronic effects. This pattern of consequential respiratory involvement among persons involved in major PVC-fueled fires has been noted in firefighters, specifically the 1975 New York Telephone Exchange fire (Dyer and Esch, 1976; Wallace, 1982), and the survivors of the 1977 Beverly Hills Supper Club fire (Wallace, 1981). An obstructive syndrome (low FVC and FEV1) was seen in 15% of workers three months following fighting a PVC-fueled fire (Colardyn et al., 1976). Long-term respiratory symptoms seen in studies of survivors of PVC-fueled fires include the bronchitis symptoms of cough and phlegm, and lung dysfunction (Wallace, 1981). Additional support for the thesis of longer-term respiratory effects resulting from PVC-fueled fires is derived from the finding that four persons who initially survived the Beverly Hills Supper Club fire died within nine months of the fire of severe respiratory impairment (Wallace, 1981).

Jan 1, 1986

By K. Tangri, B. Swaroop

Simultaneous measurements of lattice (elastic) strain by X-ray line shift method and total strain with an electrical strain gage have been carried out on polycrystalli,ne nickel with the help of a specially designed tensometer attachment for the X-ray dif-fractometer. During the initial stages of deformation, the rate of increase in lattice strain closely follows the total strain until the plastic strain sets in. From then onwards, the two strains deviate from each other and with further increase in afiplied stress the rate of increase of lattice strain eventually decreases. Depending upon the mode of unloading, both compressive and tensile strains have been observed in nickel deformed up to 0.29 pct strain. These results have been explained on the basis of the effects of clustering of dislocations and also the production and behavior of point defects during loading and unloading, respectively. POLYCRYSTALS deformed plastically in a uniaxial tension test show residual lattice strains (hereafter referred to as RLS), which broaden the X-ray line profiles and shift their peak positions.&apos;&apos;4 It is known that uniform straining of a crystal lattice (macrostrain) produced movement of ddfraction line peaks, whereas nonuniform straining (microstrain) causes line broadening.= Though the nature and origin of RLS in deformed metals is not yet clearly understood, these are believed to be due to the presence of some form of a locked-up stress system. Several possible detailed interpretations6&apos;" of the stress system have been proposed by various workers and common to all these interpretations is the assumption that different parts of the aggregate have different tensile yield stresses; e.g., that a part A yields under a lower applied stress than a part B. Therefore, during the deformation process, the elastic strain in A will be less than that in B, and, after completion of deformation, B will tend to contract further than A but will be prevented from doing so by the restraining influence of A. Thus, when equilibrium is reached, A will be in compression while B is in tension. Although there is general agreement on the correctness of this argument, controversy still exists as to the exact nature of the parts A and B in a deformed metal. In an alternative approach to the creation of parts A and B, many other investigators have assumed that the RLS observed in unloaded specimens are in some way connected with the lack of proportionality between lattice strain and applied stress in the region above the yield stress." cullity13 has prepared a schematic summary of the results of previous workers, mainly Smith and Wood,2&apos;11 which suggests that, above the elastic limit, the lattice strain may increase less rapidly with respect to strain, or may even decrease with increase in applied stress. If the applied stress is then decreased, the lattice strain would decrease along a line parallel to the loading line in the elastic region and thus produce a compressive residual lattice strain after unloading. At equilibrium, to balance these compressive stresses? there would have to be regions under tensile stress which may well be the grain boundaries or the substructure walls formed during deformation. The present investigation was undertaken to gain a better understanding of the nature and origin of RLS and also to experimentally verify the salient features of this hypothesis. EXPERIMENTAL Stress and strain determinations were made with a specially constructed tensometer attachment for the X-ray diffractometer, Fig. 1: which permits the following measurements simultaneously on a sheet specimen under uniaxial tension at various stress levels during loading and unloading: a) lattice strains, E=. in a direction perpendicular to the direction of pulling (x direction) from shifts in X-ray line peak positions; b) the total strain, ex, in the direction of pulling. with the help of an electrical strain gage affixed to the back of the specimen directly below the area irradiated by X-rays: and c) the applied stress, with the help of a load cell which consisted of a calibrated stainless-steel sample of dimensions identical to those of the specimen under investigation, and to which it was coupled. Because of its high stacking fault energy.I4 nickel

Jan 1, 1970

By R. W. Kraft

A comprehensive analysis of the crystallographic and metallographic structure of several Al-CuAl, lamellar eutectic grains solidified under equilibrium conditions has been performed. A consistent pattern was discovered which was interpreted in terms of a detailed atomistic model of an interface describable as: Interface II {111} AL 11 {211} <101>Al <120> ? Several arguments are presented to substantiate the theory. It is compared in detail with another interface model characteristic of the Wid-manstatten precipitate of CuAl2 in A1 at low Cu levels. In addition, a concept is proposed to help explain the structure of the compound CuAl2. It has been shown that the eutectic alloy between A1 and CuA1, can be forced to solidify as substantially parallel lamellae throughout a relatively large volume&apos; by appropriately controlling the solidification parameters of growth rate, thermal gradients, and impurity level and by causing solidification to proceed in a unidirectional fashion from one end of an ingot to the other. A typical ingot solidified in this manner shows three distinct zones along the length of the ingot, Fig. 1. At the head end is a region consisting of many different grains, some of which are elongated slightly in the direction of solidification. After a few centimeters of growth, this polygrained region gradually merges into the second zone which consists of a very few elongated coarse grains. The third zone at the tail end is a region of eutectic colonies caused by segregation of impurities. Microscopic examination of transverse and longitudinal sections of the ingots reveals that during the initial stages of growth (zone I) the lamellar structure is frequently highly distorted and twisted but that it straightens out in zone 11. This characteristic pattern suggests that nucleation of a eutectic grain begins randomly at the head end of the ingot, and that some particular orientation relationship between the phases is more favorable from an energy consideration than others for one reason or another, so that some grains grow and others which are less favorably oriented do not. The favorably oriented or "low energy" grains continue to grow until excess solute rejected at the advancing liquid-solid interface destroys the parallel lamellar structure by forming a cellular rather than a substantially planar interface. When this occurs, the parallel lamellae fan out and eutectic colonies are formed because the lamellae grow perpendicular to the local interface. Questions naturally arise as to the crystallographic nature of the "low energy" grains. What do the grains which persist into zone II have in common? Can this explain the stability of such grains during growth? To answer the first question it is necessary to determine the crystallographic orientation of the lamellae of each phase relative to one another. This has been done for Al-CuAl2 eutectic alloys by two different techniques on specimens prepared in different ways.2&apos;3 The results were different from each other and from a third orientation relationship between A1 and CuA1, reported for overaged A1-Cu alloys.4 The three orientation relationships are summarized below to illustrate their similarities and their differences. (001) ? 11 (001) A1; [l00] ? 11 [l00] Al Eutectic, Ref. 2 (001) 8 1) (001) A1; [1001 ?11 [1101 A1 Eutectic, Ref. 3 (001) ? 11 (001) A1; [l00] ? 11 [310] Al; Widmanstfitten, Ref. 4 It is not surprising that different orientation relationships were found by Ellwood and Bagley,&apos; and Takahashi3 since the solidification conditions were quite different. Nor is it surprising that Mehl, Barrett, and Rhines 4 found still another value since they were studying another type of alloy. Nevertheless, it would be expected that some logical and systematic pattern could be found if all the alloys were at equilibrium since the same two phases are

Jan 1, 1962

By P. G. Sprang, S. Rosen

The Y-Al- C ternary phase diagram for the com -position range from 55 to 100 at. pct Y and for a temperature of 950°C has been constructed from metallographic and X-ray diffraction data. The significant features of the isothermal section which is presented are the small solubility of aluminum in the binary Y3C phase and the presence of a ternary carbide phase with a small homogeneity range around the composition Y3AlC. The similarity in structure and composition between these two carbide phases is discussed in the light of the misci-bility gap which exists between room temperature and 1300°C, which was the temperature range studied. THE occurrence and stability criteria of ternary T3BC, carbide phases having the L&apos;12 structure and the general formula T3BCx have been discussed in detail by stadelmaier1 and more recently by the present authors., Stadelmaier found many representatives of these phases formed between the T metals Mn, Fe, Co, and Ni and the B metals Mg, Al, Zn, Ca, Ge, Cd, In, Sn, Hg, T1, and Pb. The present authors reported on a new series of iso-structural carbide phases formed between the T metals of the Sc group and the B metal, aluminum. These new phases are unique in that many of the Sc group elements form stable binary carbide phases which occur about the composition T3C and which crystallize with a structure similar to that of the T9BCx ternary carbide phases. Furthermore, these binary and ternary phases are found to coexist in equilibrium with each other. The similarity in structure and composition between, for example, Y3C and Y3AlC in the light of the mis-cibility gap which had been found to exist between these two phases indicated a need for a more thorough knowledge of the phase relations which occur in alloys based upon these compositions. Consequently, an investigation of the phase equilibria in the yttrium-rich portion of the Y-A1-C phase diagram was undertaken. The limiting Y-A1 binary diagram determined by Lundin and Klodt3 and the results of Spedding et al.4 governing the Y3C phase were used as guides in , constructing the diagram. EXPERIMENTAL Alloys weighing about 10 g were prepared by arc-melting powder compacts made from the various components on a water-cooled copper hearth using a tungsten electrode in a gettered argon atmosphere. Good homogeneity was obtained by melting the alloys three times. The purity of the yttrium used was 99.9 pct (0.07 pct rare earths). The purity of the aluminum and the carbon was 99.99 pct. The results of chemical analysis on five representative alloys showed that losses during the alloying process were predominantly carbon losses and that in no instance did the measured concentration of this component differ by more than 3 at. pct from the intended composition. For this reason the alloy compositions which are reported are those of the charges prepared for melting. Three alloys which were analyzed for copper, tungsten, nitrogen, and oxygen compositions showed that no contamination had occurred either during casting or during the subsequent annealing treatments. For the major part annealing treatments were carried out on specimens which were placed in

Jan 1, 1965