By Per Larsson

The Chapin Mine, on the Menominee range, Lake Superior, was first opened in 1880 and has since then produced 1 1/2 million tons of soft blue hematite, containing about 63 per cent. of iron and 0.07 per cent. of phosphorus. Up to the present time, the ore has been mined from three separate lenticular deposits, which conform with the Huronian strata of the district, striking N. 75' W., dipping from 70' to 80' N., and pitching about 30' W. The largest of these ore-bodies has a horizontal length of 2500 feet, and a maximum width of 130 feet in the middle, from which it gradually narrows to the pointed ends. Its dimensions have not changed materially as greater depth has been attained. Figs. 1 and 2 show the geology and the mine-workings on the main deposit.. As this main deposit pitches away from the eastern part of the property, it is replaced by another lens, containing ore of the same quality. When first opened on the 1st level, this lens was 150 feet long and up to 50 feet wide, while now on the 6th level it shows a length of 550 feet, and a maximum width of 100 feet. It is separated from the extreme east end of the main deposit by about 30 feet of clay-slates It pinches out gradually between the slates to the west, and stops abruptly against the jasper to the east. Farther east in this belt of jasper occurs the third ore-lens which has a pretty regular length of 100 feet and averages, from the 1st to the 5th level, 20 feet in width. A cross-section of the ore-formation shows, on the north or hanging side of the ore, about 200 feet of clay-slates, and farther north a heavy belt of magnesian limestone. The slates and the dolomite are generally separated near the surface by a conglomerate of broken dolomite and soft slates. The foot-wall rock is also a clay-slate, containing a higher percentage of iron and less magnesia than the hanging-slate. Farther south occur alternate beds of slates and lean ore or jasper.

Jan 1, 1888

By John Mathews

IT is twenty years since the writer made his first molybdenum steels and others were making them commercially five years earlier but the prevailing opinion seems to be that molybdenum steels are new; from time to time the daily press speaks of important discoveries in Europe and intimates that American steel makers have much to learn in regard to alloy steels. The earlier experiments were largely confined to the use of relatively high percentages of molybdenum in tool steels and permanent magnet steels. Recent developments deal with the types of alloy structural steels used for airplane, automobile, and other engineering requirements; in these, the molybdenum content is usually less than 1 per cent. The earlier types generally have been unsuccessful commercially, but the newer types of steels are becoming of increasing importance. The war showed our dependence on foreign sources for alloying metals; molybdenum alone is widely distributed in the United States and seemingly abundant. Many deposits are not now of commercial interest, owing to location and relatively small amount of ore available, but other deposits are being developed and a stable source of supply seems well assured. In tool and magnet steels, it was early found that 1 part of molybdenum was equivalent to from 2 to 2.5 parts of tungsten. The permanent magnet steels investigated by Madame Curie,1 in 1898, contained from 3.36 to 4.05 per cent. molybdenum; in 1902, Dr. E. L. French and the writer thoroughly tested steels containing from 2:0 to 4.0 per cent. These steels gave satisfactory tests for permanence, but were low in residual density and much more sensitive to hardening than the corresponding tungsten products. We discontinued work with them, therefore, and have no advice that such steels have been used commercially here or abroad.

Jan 2, 1921

By B. J. Scheiner, A. G. Smelley

The Bureau of Mines, US Department of the Interior, is conducting research on a dewatering technique for fine particles generated during the mineral beneficiation process that will recover a portion of the water now being lost using conventional waste disposal methods and significantly reduce the time required for land reclamation. The technique utilizes a flocculant, polyethylene oxide (PEO), that forms strong stable flocs that can be dewatered rapidly on static and/or rotary screens. Infield tests, phosphate clay waste has been dewatered from a nominal 2.5% solids to greater than 20% solids. In other field tests, coal-clay waste has been dewatered from a nominal 3% solids to greater than 55% solids. In addition, small-scale continuous tests have shown that bentonitic clays can be dewatered from 12% solids to 40% solids.

Jan 1, 1985

By T. A. Read, M. S. Wechsler, D. S. Lieberman

A theoretical analysis of the austenite-martensite transformation is presented which predicts the habit plane, orientation relationships, and macroscopic distortions from a knowledge only of the crystal structures of the initial and final phases. THIS paper presents a new theory of the formation of martensite. This theory makes possible the calculation of the austenite planes on which the martensite plates form, the orientation relationship between the austenite and martensite crystal axes, and the macroscopic distortions which are observed. The only input data needed are the crystal structures and lattice parameters of the austenite and martensite. Considerable effort has been devoted over the past thirty years to the development of an understanding of the crystallographic features of martensite reactions. Much of this work has been done on steels and iron-nickel alloys, for which a great deal of data has been accumulated concerning the shape and orientation of the martensite plates, the relative orientations of the austenite and martensite crystal axes, and the observable distortions which result from transformation. These observations are reviewed in refs. 1, 2, and 3. The first major step toward an understanding of these phenomena was made in 1924 by Bain,' who showed that the a body-centered cubic structure can be produced from the 7 face-centered cubic structure by a contraction of about 17 pct in the direction of one of the austenite cube axes and an expansion of 12 pct in all directions perpendicular to it. Since that time, most of the efforts at further interpretation have been made by investigators who have worked from the phenomenological data, incorporating some of the information from the lattice properties, and have sought an analysis into likely deformations which would produce the observed results."- "11 but the three most recent papers on the subject have already been reviewed in some detail." Machlin and Cohenl0 measured the components of the distortion matrix and verified that the habit plane is a plane of zero distortion and rotation for the (259) case. They showed that the measured distortion matrix, when applied to the parent lattice, does not yield the product lattice and hence some inhomogeneous distortion must occur. Frank,u working from the lattice properties and taking some clues from the observations, considered the correspondence of close-packed rows and planes in the austenite and martensite. He predicted substantially the observed lattice relationship and habit plane for certain steels which have a (225) habit. Geisler12 suggested that there is a natural tendency for the habit plane to be a (111) and postulated certain slip processes to account for the fact that the experimentally observed habit plane is irrational and deviates from the assumed one. The present work differs from previous treatments of martensite formation in that it permits calculation of all the major manifestations of the process. Habit plane indices, orientation relationships, and observable distortions are all calculated from a knowledge of the crystal structures of the initial and final phases alone. The calculations contain no adjustable parameters. The agreement found between calculated results and the observations reported in the literature constitutes powerful evidence in favor of the mechanism of martensite formation proposed. The theory is applicable to systems other than steel (as is discussed later in this paper) which exhibit a diffusionless phase change but because of the wide-spread interest in the austenite-martensite transformation, particular attention will be given to the iron-base alloys. For other systems which undergo a similar face-centered cubic to face-centered tetragonal transformation, the mathematical treatment is identical with that presented here. Hence the theory successfully describes the transformation in the indium-thallium alloy.'" Homogeneous Transformation to Martensite The distortion which any homogeneously transforming volume of austenite undergoes in order to become martensite is shown in Fig. 1, as was first suggested by Bain.' (This distortion will hereafter be referred to as the "Bain distortion.") This specification of a contraction along one cube axis ;ombined with an expansion in all directions perpendicular to this axis describes what is properly called the "pure" distortion associated with this transformation. The distinction between a "pure" and an "impure" distortion plays an important part in the discussion which follows. A "pure" distortion is characterized by the existence of at least one set of orthogonal axes fixed in the body which are not rotated by the distortion. (These are called the "principal axes" of the distortion.) No such set of axes exists in the case of an "impure" distortion. On the other hand, an impure distortion can always be represented as the result of a pure distortion combined with the rotation of the specimen as a rigid body. For a given impure distortion the corresponding pure distortion

Jan 1, 1954

By P. Somasundaran, Yee-Ho Wang

Carrier flotation of anatase impurities from clay using oleate is compared in this study with conventional flotation. The role of relevant parameters such as carrier size, carrier amount, dissolved calcium and carbonate, conditioning speed, pH, time and temperature and collector concentration is investigated in order to elucidate the mechanisms involved in carrier flotation. Addition of coarse calcite particles is found to contribute towards the enhanced separation of anatase from clay mainly due to aggregation of anatase fines with calcite and the subsequent flotation of the aggregates.

Jan 1, 1980

By W. A. McCurdy, Joseph W. Leonard, William F. Lawrence

INTRODUCTION Utilization from the Point of View of the Preparation Engineer The primary interest of the coal preparation engineer is in process design, operation, and maintenance to produce an acceptable product that can be sold at the greatest possible profit. Because of emphasis upon these interests, attention to other potential values of coal is sometimes neglected. The intent of this chapter is to alert the preparation engineer to the utilization possibilities of the product as well as the tributary coal flow moving through a modern coal preparation plant. The basis for any unrealized potential derives directly from the coal seam itself. Most coal seams consist of coal bands and benches sandwiched together in layers that differ visually from each other in physical structure and luster. Randomly selected physical and chemical ranges determined from layers of coal in a single seam can easily differ by as much as 30 Hardgrove grindability indices, 0.30 of a specific gravity point, 20 percentage points of ash, 6 percentage points of dry volatile matter, and 10 percentage points of total su1fur.l Similar wide variations exist for calorific value, seam moisture content, and, undoubtedly, for any other conceivable coal test parameter that might be used for comparative purposes. These observations all point to the long-established fact that coal is not homogeneous, as conventional analytical methods might tend to indicate, but is instead a highly heterogeneous substance.

Jan 1, 1979

By H. L. Marcus, C. D. Turk

Titanium was physically vapor-deposited by electron beam high rate evaporation. Rates of 50,000 and 85,000Å per min at deposition temperatures of 480°, 535°, and 595°C were used. Deposited thickness ranged front 0.004 to 0.010 in. The evaporated titanium had a high degree of basal Plane texture. The specimens were tested in tension at temperatures ranging from 78° to 520°K. From the data, the yield stress, thermal component of the yield stress, and work hardening characteristics were found as a function of temperature, deposition rate, and deposition temperature. It was found that Taylor's equation, best fit the work hardening data with m = 1/2. MANY investigations have been made on the tensile deformation characteristics of commercial- and high-purity titanium.1"7 The data obtained from these experiments emphasize the fact that the mechanical properties are generally related to the method of production. The correlation of mechanical properties to production history arises from the dependence of impurity concentration on the extraction and melting technique used. Additional effects are derived from crystallographic texturing which can result from fabrication history. Lee and Backofen8 and other investigators9 have shown that crystallographic texturing in titanium sheet has a significant effect on the deformation characteristics. Bunshah and Juntz10 prepared high-purity titanium by high rate physical evaporation techniques. These authors found the deposited material to have a columnar structure with grain sizes ranging from 12 to 104 µ, depending upon the substrate temperature. The room-temperature strengths of the coarse-grained distillate were similar to arc-melted, rolled. and annealed crystal bar titanium. Commercial-purity titanium was also produced experimentally in our laboratory using high rate physical vapor deposition techniques. The commercially pure material has a finer structure than the high-purity distillate,10 and is highly textured. Since the method of preparation and degree of texturing affect the mechanical properties, a research program was initiated to determine the temperature dependence of the yield stress and work hardening characteristics as a function of high rate deposition parameters. This paper relates the results of the investigation. EXPERIMENTAL A) Material Preparation. The titanium was received in the form of commercial-grade 0.096-in.-diam wire which has a composition of 0.016 pct C, 0.0037 pct N, 0.110 pct 0, 0.011 pct H, 0.05 pct Mn, 0.051 pct Fe. balance Ti. The wire was continuously fed into a vacuum evaporation unit as shown schematically in Fig. 1. The deposition chamber was evacuated, purged with argon, and reevacuated to a pressure of 10-5 Torr which was maintained during deposition. A focused electron beam was used to evaporate the titanium from a water-cooled copper crucible. The titanium vapor was condensed onto a preheated titanium substrate. The temperature of the substrate was controlled within ±5°C for the deposition temperatures of 480°, 535°, and 595°C. Control of the input power enabled the use of two deposition rates. 50,000 and 85,000Å per min. The evaporated titanium had a final analysis similar to that of the input titanium, within experimental limits. B) Testing. The evaporated titanium was physically stripped from the titanium substrate and machined into tensile specimens with 1-in. gage lengths. In addition, tensile specimens of as received annealed 35-A titanium sheet with a 20 µ grain size and 45 pct cold-rolled 35-A were also prepared. All specimens were tested in tension in an Instron at a strain rate of 3.3 x 10"4 in. per in. per sec. Proportional limit has been used as a measure of yield strength. Tests were conducted at 78°, 220°, 300°, and 520°K. Metallography, X-ray diffraction, and electron microscopy were used to correlate structure with the deposition parameters and mechanical properties. Room-temperature X-ray measurements were made to determine the phases present. Pole figures and a scans were made to determine deposition texture. Because the vapor deposition was symmetrical about the normal to the substrate, there was no preferred di-

Jan 1, 1969

By W. T. Lankford, Edward Saibel

During the course of an investigation of the plastic flow of aluminum aircraft sheet under combined loads, several problems arose in which analyses of the conditions leading to unstable plastic flow were needed. In order to provide these analyses, and in the hope of attaining a better understanding of the general problem of unstable plastic flow, the present study was undertaken. It is well known that unstable plastic flow is associated with a form of mechanical instabi!ity frequently observed during the plastic deformation of ductile metals. This instability is characterized by the fact that, at its onset, plastic straining mill proceed at a constant magnitude of the externally applied forces. It is further typical that the resulting unstable flow is generally accompanied by the formation of a neck, a local bulging, or some other form of heterogcneous deformation. Perhaps the most familiar example of unstable plastic flow to the metallurgist is the formation of the neck in the ordinary tension test. It is well known that in this test most metals exhibit a maximum in the externally applied load, followed by the process commonly referred to as "necking down." Instability in the simple tension test has been frequently discussed and numerous investigators1'2'3'12 have derived the criterion for instability in terms of a critical rate of strain hardening. It is the purpose of the present study to extend the criterion for unstable flow to the more general case where the body undergoing flow is subjected to combined loads. It is hoped that the problems considered will provide a more consistent picture of the general features of this important form of mechanical instability. The most practical implications of instability in plastic flow arise in connection with sheet metal forming operations. In the formation of a great many sheet metal parts, the deformations are produced primarily by stretching. If the conditions which lead to unstable flow are fulfilled in such a formation, and if the resultant instability leads to a pronounced localization of flow, then the useful limit of ductility of the material will have been reached. It i; also essential that the effects of instability be taken into consideration in any study of the plastic flow and rupture of metals under combined stresses. In general, when unstable plastic flow is initiated, straining becomes localized, the geometry of the test splecimen changes, and the state of stress in that portion of the specimen undergoing plastic flow is no longer under external control. In many past studies of the effects of combinetl Metals On flow and rupture) account has not been taken of the fact that, although a given test may be started under constant

Jan 1, 1947

By Edward Saibel, W. T. Lankford

During the course of an investigation of the plastic flow of aluminum aircraft sheet under combined loads, several problems arose in which analyses of the conditions leading to unstable plastic flow were needed. In order to provide these analyses, and in the hope of attaining a better understanding of the general problem of unstable plastic flow, the present study was undertaken. It is well known that unstable plastic flow is associated with a form of mechanical instabi!ity frequently observed during the plastic deformation of ductile metals. This instability is characterized by the fact that, at its onset, plastic straining mill proceed at a constant magnitude of the externally applied forces. It is further typical that the resulting unstable flow is generally accompanied by the formation of a neck, a local bulging, or some other form of heterogcneous deformation. Perhaps the most familiar example of unstable plastic flow to the metallurgist is the formation of the neck in the ordinary tension test. It is well known that in this test most metals exhibit a maximum in the externally applied load, followed by the process commonly referred to as "necking down." Instability in the simple tension test has been frequently discussed and numerous investigators1'2'3'12 have derived the criterion for instability in terms of a critical rate of strain hardening. It is the purpose of the present study to extend the criterion for unstable flow to the more general case where the body undergoing flow is subjected to combined loads. It is hoped that the problems considered will provide a more consistent picture of the general features of this important form of mechanical instability. The most practical implications of instability in plastic flow arise in connection with sheet metal forming operations. In the formation of a great many sheet metal parts, the deformations are produced primarily by stretching. If the conditions which lead to unstable flow are fulfilled in such a formation, and if the resultant instability leads to a pronounced localization of flow, then the useful limit of ductility of the material will have been reached. It i; also essential that the effects of instability be taken into consideration in any study of the plastic flow and rupture of metals under combined stresses. In general, when unstable plastic flow is initiated, straining becomes localized, the geometry of the test splecimen changes, and the state of stress in that portion of the specimen undergoing plastic flow is no longer under external control. In many past studies of the effects of combinetl Metals On flow and rupture) account has not been taken of the fact that, although a given test may be started under constant

Jan 1, 1947

By J. K. Stanley, R. F. Meel

The recrystallization of cold-worked metals is studied ordinarily by determining the temperatures required for complete recrystallization to occur within a given arbitrary time period, usually within 15 min. to 2 hr. The results obtained are conventionally assembled in a three-dimensional diagram relating this temperature to the amount of cold-work (percentage deformation) and the resultant grain size, though sometimes other modes of representation are emp1oyed.l Such three-dimensional diagrams are not complete, for the number of variables exceeds the number represented. The process of recrystallization is characterized by a time-rate, a fact that is not portrayed upon ordinary recrystallization diagrams. It is known that recrystallization consists in the formation of new nuclei and the growth of these nuclei, a process that continues until the matrix is completely consumed and the original set of grains entirely replaced by the new. This knowledge is old.2 Truly heterogeneous reactions invariably proceed by nucleation and growth; the decomposition of eutectoid solid solutions provides an example about which much is known,3 and freezing, originally studied by Tammann, provides the classic example. Although recrystal- lization is not a heterogeneous reaction within the orthodox meaning of the term, the mechanism of the process is the same. As in eutectoid inversion and freezing, it should be possible to study the rate of isothermal recrystallization as a function of time, and it should also be possible to analyze the isothermal reaction curve into the component rates of nucleation and growth that determine them.* Other methods, not employing the rates of nucleation and growth, have been used to represent the rates of such reactions, but these in general have been artificial and have not led to progress. 4,5 The theory of recrystallization is not in advanced state; if recrystallization data were obtained in terms of the rate of isothermal recrystallization, and in terms of the rate of nucleation and the rate of growth of recrystallized grains, and in particular if the temperature coefficients of these rates were measured accurately, an adequate theory should be more readily developed.27 Such an effort requires proper experimental technique, but especially requires suitable methods of mathematical analysis to convert mcasurements made upon a surface of polish into values for the rate of nucleation and the rate of growth and to combine these into a rate of isothermal recrystallization. These methods are now available for the case of three-dimensional recrystallization (recrystallization of

Jan 1, 1942

By R. F. Meel, J. K. Stanley

The recrystallization of cold-worked metals is studied ordinarily by determining the temperatures required for complete recrystallization to occur within a given arbitrary time period, usually within 15 min. to 2 hr. The results obtained are conventionally assembled in a three-dimensional diagram relating this temperature to the amount of cold-work (percentage deformation) and the resultant grain size, though sometimes other modes of representation are emp1oyed.l Such three-dimensional diagrams are not complete, for the number of variables exceeds the number represented. The process of recrystallization is characterized by a time-rate, a fact that is not portrayed upon ordinary recrystallization diagrams. It is known that recrystallization consists in the formation of new nuclei and the growth of these nuclei, a process that continues until the matrix is completely consumed and the original set of grains entirely replaced by the new. This knowledge is old.2 Truly heterogeneous reactions invariably proceed by nucleation and growth; the decomposition of eutectoid solid solutions provides an example about which much is known,3 and freezing, originally studied by Tammann, provides the classic example. Although recrystal- lization is not a heterogeneous reaction within the orthodox meaning of the term, the mechanism of the process is the same. As in eutectoid inversion and freezing, it should be possible to study the rate of isothermal recrystallization as a function of time, and it should also be possible to analyze the isothermal reaction curve into the component rates of nucleation and growth that determine them.* Other methods, not employing the rates of nucleation and growth, have been used to represent the rates of such reactions, but these in general have been artificial and have not led to progress. 4,5 The theory of recrystallization is not in advanced state; if recrystallization data were obtained in terms of the rate of isothermal recrystallization, and in terms of the rate of nucleation and the rate of growth of recrystallized grains, and in particular if the temperature coefficients of these rates were measured accurately, an adequate theory should be more readily developed.27 Such an effort requires proper experimental technique, but especially requires suitable methods of mathematical analysis to convert mcasurements made upon a surface of polish into values for the rate of nucleation and the rate of growth and to combine these into a rate of isothermal recrystallization. These methods are now available for the case of three-dimensional recrystallization (recrystallization of

Jan 1, 1942

LUTHER B. EAMES, Pueblo, Colo. (written discussion*).-In reading Mr. North's interesting paper, several points have been noted that appear to warrant discussion. With a feed all through 20 mesh, I feel inclined to question the use of steel balls as large as 2 in. in a tube mill. I have seen balls as small as-3/4 in. used for the dry grinding of cement clinker, and surely many more points of contact would result from smaller balls. This would seem to be desirable in a mill as short as 6 ft. The heavy load in the classifiers would also indicate a high proportion of returned pulp. I hope that some discussion by Mr. North -and others may develop this point. The flow sheet on page 1181 shows the solution returning from the dam valued at 40 c. per ton being added to the last decantation tank. Theoretically, this solution should not be added to that of a lower value. As I calculate it, if this solution were added to tank X the solution finally discharged from tank Z would be reduced in value by nearly 4 c. per ton.

Jan 10, 1919

By Michael Tenenbaum

Selected characteristics of nonmetallic phases were determined in low-carbon sheet steels which had been produced by various refining; deoxidizing, and casting procedures. The results showed little influence of the refining process on the quantity, distribution, size, and character of the nonmetallic phases. The quantity of inclusions was governed by the deoxidation procedures. While the mode of casting influenced the internal structure and the pattern of inclusion distribution, it had little effect on the quantity of nonmetallics. The vast majority of inclusions were under 30 µ in diam, and there was little change in size distribution during hot and cold rolling. The composition and structure of the inclusions were expained an the basis of known equilibrium phase diagrams for the appropriate systems. Additional work is needed to explain some of the observations of this paper. HENRY Marion Howe's contributions to the metallurgical profession include his many writings, the wisdom that he imparted to his students, and the inspiration that he gave to the many scholars, teachers, and industrialists who knew him personally. It was Professor Howe's intimate colleague, Albert Sauveur,1 who, in the first Howe Memorial Lecture, could have been speaking for the metallurgist of our generation as well as his own when he wrote, "...how many of us on the point of going astray were called back to the right path by Howe's guiding torch?" More than a quarter of a century later, Francis Foley,2 one of the last in the Howe Lecture series who worked directly with the great man, delivered the ultimate tribute, "...truth, in its time is so hard to identify." While Professor Howe strove to be right, "he was content if he provoked the reader to take the next step along the path to greater knowledge." Like so many of my predecessors, I sought guidance for this lecture by referring to Professor Howe's two classic texts, Metallurgy of steel,3 and Metallography of Steel and Cast Iron: the former book interpreting the facts as he saw them near the start of his career, and the latter—published 26 years later—pointing to many fertile fields for metallurgical investigation. Those of us who harvest the fruits of Henry Marion Howe's contributions to the metallurgical profession now look with wonder at the tremendous legacy he has provided. It is rewarding to study his writings and to recognize the anticipation of such aspects of modern ferrous metallurgy as: 1) Direct reduction 2) Steelmaking reactions 3) The approaches and benefits of degassing 4) Solidification mechanisms 5) Habits and behavior of nonmetallic inclusions 6) Recrystallization phenomena 7) Slip and slip propagation 8) Dislocations 9) Discontinuous deformation 10) Microscopic and macroscopic segregation

Jan 1, 1970

By S. Yukawa, M. J. Sinnott

A high resolution autoradiographic study of the diffusion of a nickel isotope (NP3) into copper in the temperature range of 650° to 925°C, with particular emphasis on grain boundary diffusion, has been made. The extent of grain boundary diffusion is a function of the grain boundary angle and the diffusion temperature. The ratios of the grain boundary diffusion coefficient to the lattice diffusion coefficient ranges from 104 to 105. The activation energy for grain boundary diffusion decreases with increasing grain boundary angle. STUDIES and reviews&apos;-8 of metallic diffusion have indicated that grain boundary diffusion is a common phenomenon but quantitative studies of the many variables involved are not numerous. The present work was concerned with determining the influence of the crystallographic orientation of the grain boundaries and the temperature on the extent of boundary diffusion of nickel into copper. The study involved essentially three steps: 1—the production of grain boundaries of known crystallographic orientation, 2—the determination of the extent of diffusion into the boundaries, and 3—the analysis of the resulting data in terms of the usual diffusion concepts. The grain boundaries investigated approximated the simple tilt variety having l° of freedom. They were produced by controlling the solidification from a melt of Cuprovac (a high purity vacuum-melted copper obtained from Vacuum Metals Corp.) of a pair of seed crystals so that the bicrystals of copper produced had a common <100> axis. By rotating one seed crystal relative to the other, a simple tilt boundary was produced. The angle of rotation between the two crystals is the grain boundary angle 8, or what is sometimes termed the misfit angle. In all, some 16 boundaries ranging from 2" to 72" in 5" to 10" steps were investigated. The crystallographic orientations were measured with the use of both X-ray and optical goniometric techniques. The <100> axes in the crystals were found to be parallel within 2" to 3" with the exception of one crystal (8 = 12") in which the axes were 6" from being parallel. All bicrystals showed evidences of sub-grain structures. Laue analyses showed that these subgrains differed in orientation up to a maximum of 2". Because of these variations, and some curvature in the boundaries, the grain boundary angles listed are actually average values and deviate from the 1 o of freedom boundaries. The stripping film technique of high resolution autoradiography was used to detect the diffusion of the nickel isotope into the grain boundaries of the bicrystals of copper. Kodak experimental permeable stripping film with an emulsion layer 5 u thick

Jan 1, 1956

By Grover J. Holt

IN order to provide a clear picture of the development of the sink-and-float process of concentration as applied to the iron ores of Minnesota, a few pertinent facts should be brought out concerning the ores and the products of concentration. Iron ore is primarily a cheap commodity handled in immense quantities. The price of iron ore at present, based on a natural iron content of 51.5 per cent, varies from $2.55 to $2.70 per gross ton f.o.b. cars at the mine or washing plant in Minnesota. Last year 92,000,000 gross tons were shipped from the Lake Superior district (Minnesota, Michigan, and Wisconsin) to the furnaces. Concentrated iron ores have no greater value per unit of iron content than ores that can be mined and shipped direct from the shafts or open pits. For years only the higher grades of concentrating ores could be treated and sold in competition with the immense reserves of direct shipping ore available. These higher-grade "straight wash" ores required only the simplest treatment; namely, the washing out of fine sand from coarse ore particles. As the exhaustion of the "straight wash" ore is reached, rock is found replacing part of this sand, and the ore no longer responds to the former sizing treatment. Substantial tonnages of this marginal (jig ore) remained to be treated. Because of the limitations placed on concentrates by the furnaces-namely, low price of product and minimum amount of fines-iron-ore concentration has been and must continue to be a one-pass process. Only an increase in price or a change in structure of concentrates allowed by the ore consumer will encourage departure from this practice. Faced with the necessity of handling large tonnages, with the limitations mentioned, iron-ore research men have found their search for new and more efficient methods of treatment seriously handicapped and removed from the field of fine crushing. Sink-and-float treatment appeared to offer the best field in coarse concentration and has been proved by several plants to be well adapted to our problem. The use of ferrosilicon as a medium solid was decided upon. In our present practice, the ferrosilicon metal, carrying about 83 per cent iron, 15 per cent silicon and 2 per cent carbon and nonmagnetics, is crushed to pass 65 mesh and used without further sizing. When mixed with water the specific gravity of the medium may be controlled to within 0.02 per cent above or below the required gravity. Table I shows examples of a change in solid content of the medium for varying gravities. [ ] Table I is based on clean ferrosilicon, whereas some contamination is always present in the mill circuit, tending to

Jan 1, 1943

By A. J. Lynch, J. A. Holmes, F. C. Bond, D. W. Fuerstenau

This is an outstanding paper on comminution theory and represents a considerable advance in mathematical formulation. It clears the way for a discussion that should ultimately decide whether the work index should be considered as a parameter according to the Third Theory or as a constant. In the empirical differential equation dE = C dx/xn either C or n must be treated as a variable to satisfy known crushing and grinding conditions. The author has chosen the exponent n as the variable, with C as a constant.

Jan 4, 1958

By D. L. Wood

INTERNAL oxidation of alloys has been investigated by Rhinesl,2 and by Meijering and Druy-vesteyn. Rhines showed that dilute Cu-A1 alloys can be internally oxidized without forming an external scale by annealing in an oxygen partial pressure equal to the decomposition pressure of Cu2O. The oxygen is supplied at the outside surface at a rate sufficient to maintain saturation of the surface with respect to oxygen. Oxygen diffuses inward and, at the interface between the subscale and the alloy, oxygen meets the solute and reacts to precipitate its

Jan 1, 1957

By Robert Anderson Cook

The subject of refractory materials occupies such an important position in all metallurgical works, and particularly in those of iron and steel, that any data concerning it must be of interest to the metallurgist. No apology is needed, therefore, for this attempt to describe the mining of fire-clay and the manufacture of fire-brick at one of the largest establishments in this country. Mount Savage is a small village situated in the northwestern part of the Cumberland coal basin, on the Cumberland & Pennsylvania Railroad, and at the foot of Savage Mountain, from which the village takes its name. Fire-brick have been manufactured here almost, if not quite, as long as in any place in America; and as the brick are still shipped to nearly half the States in the Union every month, the manufactory is probably the most generally known. In the year 1837, a company was formed called the Maryland & New York Coal & Iron Company. It built two blast-fiirnaces, the ruins of which still remain. It was in the construction of these filmaces that the first fire-brick made here were used ; and though the iron works ran but spasmodically, the brick works have been in constant operation ever since. From 1837 until 1846, the Maryland Coal & Iron Company, from then until 1548, the Lochiel Iron Co., and from 1848 until 1861, the Mount Savage Iron Co., ran the brick-works, and in

Jan 1, 1886

By D. J. Carney, R. R. Burt, E. J. Whittenberger

Hardenability (multiplying) factors for carbon, mongonese, silicon, chromium, nickel, and molybdenum have been developed for hypereutectoid low-alloy steels in which bainite is the first subcritical transformation product. These factors permit the calculation of 95, 80, and 50 pct martensite hardenability from chemical composition when steels with spheroidized structures are quenched from 1475°, 1525°, and 1575°F. The strong contributions to hardenability of the less expensive elements, silicon and manganese, suggest their use to obtain additional hardenability in hypereutectoid low-alloy steels. DURING the past decade a number of investigators&apos;"11 have carefully developed information which permits calculation of the hardenability of medium -carbon low-alloy steels from chemical composition and grain size. These data have been especially valuable in developing less costly low-alloy steel compositions with equivalent or Improved

Jan 1, 1957

By J. F. Lewis

Believing that one of the essential points in mining, as in all other business, is to know the expense incurred in each particular department, I have carefully kept an account with each department for the past three years; and, as it may be of interest to some of our members, I herewith present it to the Institute, reduced to per centages of the total yearly expense, showing the cost for materials, repairs, expenses, tools, team accounts, powder, oil, and fuel, also for labor under its several heads: 1875—Materials. 1875—Labor, Repairs,...040 Expenses,....016 Team,. .. .. .017 Machinery,. .. .055 Tools,..006 Repairs,. .. .027 Improvements,.....030 Washer,. .. .076 Oil ..008 Pit,.. 178 Powder,..,043 Dirt,.. 130 Fuel,. .325 Superintendence,. ..050 .485 .516 100.1 1876—-Materials. 1876-Labor. Repairs,. . • .. .043 Expenses,......012 Team,.011 Machinery,. .. .090 Tools,..005 Repairs,... 027 Improvements,.....007 Washer,. .. .085 I,. ...,015 Pit,.. 139 Powder,. .. .. .030 Dirt,.. 160 Fuel,...321 Superintendence,. ..078 .444 .559 100.3 1877—Materials. 1877—Labor. Repairs,......102 Expenses,......019 Team,..031 Machinery,. .. .050 Tools,..030 Rrpairs,. .. .046 Improvements,....,031 Washer,. .. .057 I,...009 Pit,.....179 Powder,...035 Dirt,.. 162 Fuel,...200 Superintendence,. ..054 .457 .548 100.5 Average for the three years 1875, &apos;76, and &apos;77. Materials. Labor. Repairs,...062 Expenses,...016 Team,..016 Machinery,. .. .065

Jan 1, 1879