By Walter Weeks

LITTLE study has been made of the pressure changes and energy losses that take place when an air current is divided into splits which subse-quently unite. The discussion and the experiments that are described in this paper deal with the division of an air current into square splits of equal size, the area of each of the splits at the downstream junction being one-half the area of the main duct. APPARATUS AND SYMBOLS The duct system shown in Fig. 1 was built of Y4-in. redwood and made as smooth as possible.The section of the top over the splits and the zone of mixing was of plate glass to permit observation of the stream lines. FIG. 1-DUCT SYSTEM. Static pressures were measured by means of pinhole tubes and a precise inclined manometer. Measurements of rates of flow were .made by determining the drop in pressure through concentric square orifices in the splits. The air was supplied by a fan operated by a direct-current motor that received its current from a motor generator set. Delicate rheostats in the armature. of the motor. made possible the perfect control of the fan speed, which was indicated on an electrical tachometer. Vanes to straighten the. flow were placed at the head of the main duct.

Jan 1, 1933

By R. J. Wasilewski

Elastic constants have been determined on single crystals of maximum-melting-temperature NiAl compound (50.6 at. pct Al) at 25°C. Temperature variations of Young&apos;s modulus in the three principal crystal directions between -150°C and +800°C exhibit no anomalies similar to those repovted for the isomor-phous compounds brass and AuCd. It is concluded that the ordered CsCl structure is stable throughout the temperuture range investigated NICKEL aluminide is a congruently melting inter-metallic compound of CsCl (B2) structure, stable over a rather wide composition range (40 to 54 pct Al). It exhibits a lattice-parameter maximum of a. = 2.883A at 50.6 pct 1,&apos; at which composition the excess aluminum atoms are randomly distributed on the vacant nickel sites;&apos; at higher nickel compositions the excess nickel atoms replace substitutionally in aluminum sites, while at higher aluminum compositions vacancies are present in the nickel sublattice.&apos; For compositions close to NiAl no significant variation in order has been observed at temperatures up to 900°C.3 At high nickel (65 pct) compositions the existence of a martensitic structural transformation has been reported.4 NiAl is isomorphous with the ordered B-brass structure and with the high-temperature structures of AuCd and TiNi alloys close to equiatomic composition. All of these exhibit anomalous elastic behavior as the temperature of their diffusionless transformation to lower-symmetry structures is approached.&apos;-&apos; This behavior has been explained as indicative of low stability of the CsCl structure in these compounds.8 The present paper reports the experimental determination of the elastic compliances of single-crystal NiA1. EXPERIMENTAL METHOD 1) Specimens. Polycrystalline NiAl was prepared by induction melting of carbonyl nickel and high-purity aluminum and casting into solid copper molds in gettered helium atmosphere. The castings thus produced were canned in mild steel and impact-extruded at 1100 to 1200°C to 38-in.diam rod. After the steel sheath was pickled off, the rods were converted to single crystals by repeated high-frequency satisfactorily produced the desired orientations in the form of crystals 38 in. diam by 8-12 in. long. These were subsequently center less-ground to 7 to 8 mm diam by 12 cm long, electropolished (in 80 pct methanol, 20 pct HzSO, at 25°C and 15 v), and their axial orientation determined to 1 deg by the Laue back-reflection technique. The rod dimensions were determined to 0.01 mm and the densities determined from geometrical dimensions and the weight of every specimen. The average density was 5.905 0.005 g per cu cm. 2) Elastic Data Measurements. Room-temperature elastic compliances Sii were obtained by determining to 0.1 cps the fundameGtal resonance frequencies in the longitudinal and torsional vibration modes. At these frequencies the following relations hold: E =p(2lfif =pvl= Sn- 2r[Sll- S12- -£„«] g -P(2iftf = pvf = (s<« - fr(sii - sw - ±s»y where vl and vt are the velocities, and f andft the resonance frequencies of the longitudinal and torsional waves, respectively; 1 is the length of the specimen, and r is the direction cosine factor—{cos2 a • cos2 0 + cos2 a . cos2 y + cos2 0 ¦ cos2 Y}. Given three crystals of orientations (loo), (110), and (111)) i.e., F = 0, 14, and 13, we can obtain six equations for the three unknown compliances, thus providing adequate internal check. Mode mixing can readily occur in the relatively long wavelength resonance utilized here. This could cause a significant error in the torsion wave velocities calculated from the apparent resonance frequenies. Therefore, throughout the present work, a method, described previosl,&apos; was used to ensure that no significant mode mixing took place at resonance. The apparatus used was originally designed for the Elastomat, Magnaflux Corp.. Chicago, 111. determination of flexural vibration resonance frequencies. At room temperature torsional vibration mode could be established by suitable positioning of the thin wires from the input and pick-up transducers, and longitudinal mode by cementing thin magnetic foils at the ends of the specimen, and inducing the vibration by means of electromagnetic transducers. Only flex-ural resonance frequencies could, however, be obtained reproducibly over the temperature range of -150 to 800°C. These data are considerably less accurate, the error in the modulus being estimated at -0.6 pct from the specimen dimensions and the room-temperature Poisson&apos;s ratio. The reproducibility of the resonance frequencies in repeat runs was, however, to better than l in 15,000, hence the relative elastic modulus error less than 0.02 pct. Therefore, the temperature variation of the principal Young&apos;s moduli obtained by flexural resonance, relative to room-temperature values, is believed to be satisfactorily accurate.

Jan 1, 1967

By Michael J. Callow

THE PROPERTY of Mount Isa Mines, Ltd., is located at Mount Isa, Northern Queensland, Australia, at roughly 20" south latitude. It is 600 miles from Townsville on the east coast, the port for Mount Isa, 1200 miles from Brisbane and approximately 1600 miles from Sydney in New South Wales. Living conditions in the camp, though wild and crude at the commencement of building, are now excellent and little has been left undone to provide comfort and attractiveness. The climate being warm and dry, many of the buildings are built on posts, 8 to 10 ft. off the ground, with spacious screened-in verandas. Club houses, stores, school, hospital and ice plant have all been provided by the company as well as modern conveniences, such as running water, shower baths, electric lights, septic tank arrangements, tennis courts and amusement grounds.

Jan 1, 1932

By Charles E. Weaver

During the past few years there has been considerable activity in prospecting for oil and gas in several parts of western washington. From time to time seepages of oil or emanations of gas have been reported from various places. Several companies have been organized for the purpose of drilling, but only a part of these have actually begun operations. In certain localities very small seepages of oil occur, but up to the present time no oil or gas in commercial quantities has been obtained. In order to determine the conditions which may be favorable or unfavorable to the occurrence of petroleum it becomes necessary to know the character and extent of the geological formations in which such deposits might occur. In other regions where producing wells have been developed it is possible to know what formations contain the oil and what structural conditions influence its concentration in reservoirs or zones. It is usually possible to determine those strata which contained the materials from which the petroleum may have been derived and also the position and distribution of the more porous sandstone belts into which it may have collected. Detailed stratigraphic surveys may even determine the depth at which a certain known oil-bearing zone may be tapped at any particular place. It is also possible to recognize those formations which are presumably barren of oil, as well as those which are absolutely so. In new regions far distant from any of those which are now producing or have produced in the past, it becomes absolutely impossible to foretell whether oil may exist in commercial quantities or not. Assuming that such deposits do exist, it is extremely difficult to predict at what depth the produciqg zone or zones occur. However, in prospecting in a new and unexplored region, use should be made of such laws as have been found to govern the occurrence of petroleum deposits in other well-developed fields. Such deposits in their world-wide distribution are found almost exclusively associated with sedimentary rocks. Areas composed predominatingly of igneous and metamorphosed rocks are to be rcgarded as extremely unfavorable localities for the occurrence of commercial deposits of oil or gas. Assuming that such oil deposits are

Jan 1, 1916

By M. T. Simnad, R. F. Mehl, L. Yang

Techniques for studying marker movement in K-Rb interdiffusion have been worked out. The results indicate that Rb diffuses faster than K and that the ring mechanism of diffusion cannot be the dominant one operating in this case or probably in cases involving other alkali metals, despite their low ion core repulsive energies. SEVERAL theoretical attempts have been made in the past decade to elucidate the mechanism of diffusion in body-centered-cubic metals. No general agreement, however, has been reached by different authors. Zener,1 and later LeClaire,2 on the basis of a correlation between the entropy of activation for self-diffusion and the temperature dependence of the elastic constants, predicted that a ring mechanism should operate in the diffusion of body-cen-tered-cubic metals. Paneth3 calculated the activation energies of various ring, vacancy, and interstitial mechanisms for the self-diffusion in alkali metals and concluded that the most likely one was based on the linear motion of "crowdions," which is in fact a different form of interstitial diffusion. Fumi,1 however, showed that the experimental values of the activation energies for self-diffusion in the alkali metals could be better accounted for if the diffusion process in these metals was assumed to follow a vacancy mechanism. The same conclusion was reached by Kojima5 for the self-diffusion in lithium. Experimental evidences published during the past few years seem to exclude the ring mechanism as the predominating one in the diffusion of body-centered-cubic metals. For instance, maker movement has been observed in ß-brass, first in this laboratory" and later by Resnick and Baluffi.5 Shewmon and Bechtoldh also found marker movement in the body-centered-cubic system Ti-Mo and showed that the argument which led Zener and LeClair to favor a ring mechanism was not incompatible with a vacancy mechanism. In spite of this, it seemed to the authors that further experimental tests should be made by studying the Kirkendall effect in body-centered-cubic systems that characteristically have small ion core repulsion, such as the alkali-metal systems. Since the ion core repulsion term constitutes the main part of the activation energy needed for the rotation of a ring, such a test should be the most critical of all. The system K-Rb was chosen for experimental study because these metals form a continuous series of solid solutions. Experimental Investigation Owing to the extremely active nature of these two metals, a brass dry box (18 x 11 x 10 in.) was built for making the diffusion couple. It had a big lucite window on top, two side ports through which neo-prene-rubber gloves were inserted, and another side port covered with an optically flat-glass window for microscopic examination of the sample. Inside the box there were a circulating fan driven with a rotating horse-shoe magnet located outside the box, a heater used to generate potassium vapor for getter-ing the box, and a cold trap for keeping the inside of the box cool. Chemically pure grade K and Rb were triple distilled before they were transferred in vacuum into cylindrical steel molds kept in pyrex-glass ampules, Fig. 1. The latter together with the tools needed for making the diffusion couple were put into the dry box. After the box was flushed with purified argon and gettered with potassium vapor, generated from a heated steel crucible inside the box, the glass ampules were broken and the mound on the top of the alkali-metal ingot was cut off with a razor blade to yield a flat surface. To make the diffusion couple, one K ingot and one Rb ingot were pushed out of the molds together with their steel supports by screwing a metal plunger into the bottom of each mold. They were then laid on a brass cradle inside the assembling carriage (shown separately in Fig. 2) with the flat faces opposite to each

Jan 1, 1959

By L. G. Huntley

The occurrence of oil or "tar" in Mexico was mentioned as early as the seventeenth century by Friar Sagahun, who gives the Indian name "chapopote," by which these asphalt seepages are still called. This asphalt was apparently used, as it has been used by primitive people in many parts of the world, in religious ceremonies and for medicinal purposes. Travellers also report that the ruins in Yucatan and the pyramids in southern Mexico show traces of the use of "chapopotel&apos; as a building cement.l DeGolyer says that the first attempt to exploit oil or gas in Mexico in a commercial way is shown by the records of the Memoria de Fomento of 1865, when permission was granted to a Senor Ildefonso Lopez to exploit the deposits of petroliferous substances in the San Jose de las Rusias area in the State of Tamaulipas. Other concessions follow, and probably refer to surface seepages which occur in that district. This was several years after the discovery of oil in Pennsylvania. In 1868, a well 125 it. deep was :drilled by a company organized in Mexico City, in what is now known as the,, Furbero district, and a little oil was refined there. In 1873, residents of Tampico denounced seepages along the Tamesi River, and asphalt was mined near Tempoal in the Canton of Tantoyuca. No drilling was attempted. But between 1880 and 1883 several shallow wells were drilled for oil in Mexico, two of them being near the present Potrero de Llano field west of Tuxpam. The wells were drilled by a Boston company with Canadian rigs, and are said to have reached a depth of about 400 ft., while one is reported to have flowed. Several other abortive attempts were made to drill for oil between 1885 and the beginning of the present century, about which time the Mexican Petroleum & Liquid Fuel Co., Ltd., in which Cecil Rhodes was interested drilled 24 wells unsuccessfully, several of them as deep as 1,500 ft., in the State of Vera Cruz. Also Messrs. Doheny and Canfield of California pur-

Jan 1, 1916

By R. Bainbridge

THE Consolidated Mining and Smelting CO. of Canada Ltd. has operated a lead smelter at Trail, B. C., for many years. In order to take advantage of metallurgical advances, as well as to improve materials handling methods, this company, commonly known as "Cominco," commenced planning a program of smelter revision and modernization some years ago. The first stage of this program involved the design and construction of a new blast furnace gas cleaning system. The selection of equipment, the design of facilities, and preliminary operating details of this system will be dealt with in this paper. The essential problem was to clean and collect 100 tons of dust daily from 153,000 cfm* (12,225 lb per min) of lead blast furnace gas which varied in temperature from 350º to 1100°F. Because it was desired to collect the dust dry, either a Cottrell or a baghouse cleaning plant was to be selected. Comin-co&apos;s many years of experience with both systems provided a background for choosing the most satisfactory installation. All information pertinent to the two methods of dust recovery was carefully investigated, and it was decided to replace the existing equipment with a baghouse. Very briefly, the reasons for this decision were as follows: 1—A baghouse installation would be practical because the SO2 content of the gas was low and corrosion would not be a problem if the baghouse operating temperatures were held sufficiently above the dew point. 2—Variations in the physical characteristics of fume and dust, which are inherent in this blast furnace operation, should not substantially affect the operating efficiency of a baghouse. 3—For the same capital cost, metal losses (stack and water losses) would be appreciably less in a baghouse. 4—A baghouse would be easier to operate, and would not require the use of highly skilled labor. 5—Operating and maintenance costs of a bag-house would be lower. 6—The only available space for reconstruction was relatively small, and not suited to a Cottrell installation. Once the baghouse system was decided upon, detailed design of the installation was begun. Baghouse Design Gas Cooling: Before the required capacity of the baghouse could be determined, the method of cooling the gas to the temperature necessary for bag-house operation had to be chosen. The problem confronting the design engineers was how best to cool 153,000 cfm of gas from a temperature ranging from 350°F to brief peaks of 1100°F, down to 210°F, the maximum safe baghouse inlet temperature. A survey of existing blast furnace gas temperatures in the outlet flue showed that the normal range was as given in Table I. The obvious choices of cooling method were: 1— cool completely by the addition of tempering air; 2—utilize a heat exchanger; 3—cool by radiation; and 4—cool with water spray in conjunction with the admission of tempering air. The advantages and disadvantages of the various cooling methods were: Air Addition: To cool completely by the admission of tempering air involved tremendous volumes, Fig. 1. For example, to cool 1 lb of blast furnace gas at 450°F requires 1.84 lb of air at 80°F or 1.60 lb at 60°F. As it is necessary to design for peak conditions, it can readily be seen that volumes of tempering air in the order of 1,500,000 cfm would have to be handled. Using the normal design figure of 2.5 cu ft per sq ft of bag area, a baghouse installation comprising some 600,000 sq ft of filter cloth would be necessary. Such design requirements would be prohibitive, not only from a standpoint of capital expenditure, but also because of space limitations. Heat Exchanger: The utilization of a heat exchanger was given serious consideration. A horizontal tube unit using air as the medium to cool the required volume of blast furnace gas from 400" to 250°F was investigated. Cooling above 400°F would be done by water spray, and below 250°F by admission of tempering air. The estimated capital cost of such a unit was found to be prohibitive. From an operating standpoint, there was considerable doubt as to whether the soot blowing equipment provided would effectively keep the dust from building up on the tube surface. The performance of heat exchangers operating on dusty gas in other company operations had not been too favorable. Radiation Cooling: Although somewhat cumbersome, gas cooling by radiation from &apos;trombone&apos; tubes or other similar equipment (cyclones) is employed in many metallurgical operations. Such an installation was also considered. However, calculations showed that an installation much larger than the space available would be required to handle the gas volume involved. For example, to cool 153,000 cfm of blast furnace gas from, say, 600&apos; to 250°F (i.e., remove in the order of 58,500,000 Btu per hr with heat transfer rates varying from 1.1 Btu per sq ft per hr per OF for the higher temperature ranges to 0.88 Btu per sq ft per hr per OF for the lower ranges) would need a cooling area of some 175,000 sq ft.

Jan 1, 1953

By Albert Sauveur

IN an important paper on The Critical Ranges of Pure Iron1 presented at the May, 1913, meeting of the Iron and Steel Institute, Professor Carpenter reports and illustrates the results obtained by him in determining the critical points of some very pure electrolytic iron sheet about 0.01 in. thick. The iron strip was rolled into the form of a cylinder 1; in. long and fn in. wide, weighing 42 g., the thermo-couple being inserted in a small hole in the center. The points Ac3 and Ar3 were readily detected, as well as the point Art, but the point Act was absent from every heating curve. The author concluded from this occurrence that the conception of A2 as an independent allotropic change must be abandoned. At the October, 1913, meeting of the American Institute of Mining Engineers, Dr. G. K. Burgess and J. J. Crowe read a paper on The Critical Ranges A2 and A3 of Pure Iron2 in which they described some extremely important experiments conducted by them at the Bureau of Standards, Washington, D. C. They tested Professor Carpenter&apos;s electrolytic iron and detected a sharp and well-defined absorption of heat corresponding to the point Act. Professor Carpenter&apos;s failure to detect this point is explained by them on the ground that unless the iron be in a single piece entirely surrounding and in contact with the thermo-couple junction, the thermo-couple will integrate the irregular progress of the heat through the sample and the curves will lose their sharpness. In discussing Messrs. Burgess and Crowe&apos;s paper, Professor Carpenter accepted this explanation as probably accounting for the absence of Act in his heating curves.

Jan 2, 1914

By W. S. Row

This mine is operated at 4000 to 4500 tons daily through a single shaft, with one rock hoist and one service hoist. Latest shaft construction is concrete with wooden dividers. Economics of drifters and air-leg drills are compared, as well as costs of shrinkage and sub-level stoping. Economy of large haulage equipment and underground crushing is shown.

Jan 3, 1953

By David T. Day

IN 1897 I published a proposed explanation t for the variation in color and specific gravity of Pennsylvania oils. A resume of this subject was also presented at the First International Petroleum Congress, in Paris, in 1900. Since that time much experimental work bearing upon this explanation has been carried on by myself, in the United States Geological Survey, and under my direction, by Dr. J. Elliott Gilpin, Marshall P. Cram, and 0. E. Bransky, at the Johns Hopkins University. The experimental results thus accumulated seem to throw considerable additional light upon the variations in color and specific gravity of petroleum, as found in different parts of the world, and also upon the variations in chemical composition. Therefore, it seems as if a, summary of the evidence thus obtained might be of value to those members of the Institute who are interested in the examination of oil-fields. The summary is here presented for that purpose. The phenomenon has often been observed in many oil-fields that oils of different color, specific gravity, and chemical composition may be found within short distances of each other. A conspicuous example of this is the occurrence at Jennings, Welsh, and Anse la Butte, La., of petroleum chemically somewhat similar to Russian petroleum; that is, characterized by the presence of naphthenes. Another characteristic is the presence of considerable percentages of asphaltic compounds, sufficient in quantity to disguise the presence of solid paraffin wax, and perhaps also to render that paraffin wax more soluble * Published by permission of the Director of the United States Geological Survey. 1 Proceedings of the American Philosophical Society of Philadelphia, vol. xxxvi., No. 154, pp. 112 to 115 (January, 1897).

Jun 1, 1910

By Gerald G. Griswold, James O. Greenslade, Cherie Tilley, Richard Reseigh

INTRODUCTION The Harrison Western Corporation, a leading Denver based mine contracting and engineering concern, is presently engaged in sinking two 1,006 m (3,300 ft) shafts for the Phillips Uranium Corporation at their Nose Rock Project, approximately 13 miles northeast of the small community of Crownpoint in McKinley County, New Mexico. The Nose Rock Project is the first attempt by the Phillips Uranium Corporation to tap the deep uranium reserves in what has become known as the Grants Mineral Belt. (See Figure 1) Project Description Phillips Uranium Corporation&apos;s plan for the large 2700 metric ton per day (2950 tons/day) mining facility calls for a series of deep access and ventilation shafts ranging from 4.27 m (14 ft) to 5.49 m (18 ft) in diameter to approximate depths of 1,006 m (3,300 ft). The initial pair of shafts consists of one production shaft and one ventilation shaft separated by a distance of 91 m (300 ft). The interbedded layers of sedimentary sandstones and shales to be penetrated by the shafts contain several major water producing aquifers, the deepest being the mineralized zone called the Westwater Canyon Member of the Morrison Formation. A series of temporary and permanent water pumping stations is planned. Generally, the temporary stations are located above major aquifers to facilitate water removal while sinking through the aquifer and the permanent stations constitute what, in the final mode, will be the mine dewatering system. In addition, Phillips Uranium Corporation has In- stalled and is maintaining a system of depressurization wells that temporarily pump the major aquifers and considerably reduce the water inflows during shaft construction. The major aquifers are also chemically grouted prior to sinking. Site work for the project was initiated in the fall of 1976. Full scale shaft sinking commenced in November of 1977 on the 4.88 m (16 ft) diameter ventilation shaft and on the 5.49 m (18 ft) production shaft by another contractor. Harrison Western Corporation began work on the project on November 4, 1979 wlth the production shaft at a depth of 633 m (2,076 ft) and the ventilation shaft at a depth of 474 m (1,554 ft). This paper will address only the portion of shaft sinking completed by Harrison Western. Geology and Hydrology The Nose Rock Project is located on the Chaco Slope in the southern extreme of the San Juan Basin in northwest New Mexico. The southern San Juan Basin is generally bound by the Defiance Uplift to the west, the Zuni Uplift to the south and the Nacimiento Uplift to the east. The Grants Mineral Belt occupies most of the southern portion of the San Juan Basin and this project is located on the northern extreme of the Grants Mineral Belt. The San Juan Basin is comprised of sedimentary rock of continental, marginal-marine and marine origin, that dip northward from the Zuni Uplift and Chaco Slope into the interior of the San Juan Basin. (See Figure 2) Major Formations The major geologic formations to be penetrated range from mudstone and shales to siltstones and sandstones. The sandstones are highly productive aquifers which, under static conditions, would flow artesian. Water temperatures in the aquifers are high and therefore are a force to be dealt with. Temperatures range from 18ºC (65OF) in the upper aquifers to 48ºC (118º&apos;F) in the lower. The mudstones are generally bentonitlc. (See Figure 2) GALLUP SANDSTONE: The Gallup Sandstone is the first major regressive wedge in the San Juan Basin of the Cretaceous era and at this project is about 35 m (115 ft) thick. It is medium grained and prior to depressurization carried a hydrostatic water pressure of over 72.5 kg per cm2 (1,031 psi) which 1s artesian. Compressive strength ranges from 334.7 kg per cm2 (4,760 psi) to 421.8 kg per cm2 (6,000 psi). Water temperature is approximately 30°C (86°F).

Jan 1, 1982

By James R. Swaisgood, Ronald E. Versaw

Hundreds of shafts have been sunk in the United States in the past. Most of these have been successful however, in some instances thousands of dollars have been lost due to work stoppage while emergency measures were taken to control unexpected water flows. In cases where it was not possible to control the water, the shafts were completely lost. Many thousands of dollars have also been wasted in overconservative support design for the successful shafts. These "hell for stout" designs were necessary because of the importance of the shaft in the operation of the mine. If there was trouble in the shaft, all underground operations would come to a halt. Over-design was also necessary because no reliable preconstruction investigation methods or rational support design methods were available.

Jan 6, 1974

The income of the Institute is derived from dues, subscriptions to MINING AND METALLURGY and sale of publications. These sources are fortunately supplemented by the interest from invested funds now amounting to over $500,000, a considerable portion constituting endowments for especial purposes. Aside from the medal funds the principal endowments are the James Douglas Fund for support of the Library, the Rocky Mountain Fund and the Seeley W. Mudd Memorial Fund. The income from the two last named is available for the support of research and a variety of other purposes. It is allocated by the Board of Directors upon recommendation of standing committees in each case. An active effort is being made to increase the endowments of the Institute, it being felt that unusual opportunities exist for research and public and professional service through the organization and at a minimum of expense. J. V. W. Reynders is chairman of the Endowment Committee.

Jan 1, 1923

By W. S. Hyler, L. W. Berger, R. I. Jaffee

Hydrogen additions of 390 ppm to A-55 titanium and 368 ppm to Ti-8 pet Mn have no deleterious Hydrogenadditionseffect on the unnotched and notched rotating-beam fatigue properties of these materials. &apos;These amounts of hydrogen, however, are sufficient to cause severe notch-impact thesematerials.embrittlement in A-55 titanium and pronounced loss of tensile ductility in Ti-8 pet Mn. The lack of embrittling effect in fatigue in the latter alloy is consistent with the postulated strain-aging mechanism of hydrogen embrittlement in a-ß alloys. There is a significant strain-agingincrease in the unnotched endurance limit of A-55 titanium with the addition of hydrogen. This increase may be explained as the result of internal heating effects which would dissolve the hydride and cause solid-solution strengthening. TITANIUM and its alloys may be seriously embrittled by relatively small amounts of hydrogen. The form which this embrittlement takes has been shown to vary with alloy type. The a alloys, for example, suffer most strongly from loss of notch-bend impact toughness&apos; when sufficient hydrogen is added, and this effect has generally been associated with the presence of hydride phase in the micro-structure. In a-ß alloys, on the other hand, hydrogen is most detrimental to tensile ductility in slow-speed tests,2-1 and the embrittlement may be detected in a most convincing manner by means of rupture tests at room temperature. This particular kind of embrittlement has not been associated with a change in microstructure, but has been classified rather generally as associated with a strain-aging type of mechanism.&apos; In the present paper, the effect of an embrittling amount of hydrogen on the rotating-beam fatigue properties of both an a and an a-ß titanium alloy is covered. For this study, annealed commercially pure (A-55) titanium was chosen as an a alloy, and equilibrated and stabilized Ti-8 pet Mn as representative of a typical a-ß alloy. Nominal hydrogen levels of 20 and 400 ppm were evaluated, the latter amount having been shown previously to be severely detrimental to the impact toughness of commercially pure titanium and to cause pronounced strain-aging embrittlement in the Ti-8 pet Mn alloy. The only report of the effect of hydrogen on the fatigue properties of titanium is given by Anderson et al.,° in which a push-pull type of fatigue test was conducted on as-received commercial-purity titanium sheet. Much scatter was found in the results, but generally the presence of hydrides slightly decreased the fatigue strength of unnotched specimens in the longitudinal direction. The results of notched tests were masked too greatly by scatter to be significant. Experimental Procedure Preparation of Materials—Analyses of the A-55 titanium and the Ti-8 pet Mn alloy used in this investigation are given in Table I, which indicates the 8 pet Mn alloy to be more nearly a 6 pet Mn alloy. This alloy will be referred to as Ti-8 pet Mn, however, since this is the commercially designated composition. Both alloys were received in the form of5/8-in. diam rod and, after suitable surface preparation, 5-in. lengths were vacuum annealed at 820°C. Half of the rods for each material were then hydrogenated at 820°C to a nominal hydrogen content of 400 ppm. The hydrogenated and vacuum-annealed A-55 rods were hot swaged at 700°C from 5/8-in. diam to 1/4-in. diam, and then annealed 1 hr at 800°C and air cooled prior to preparation into test specimens. Fabrication of the Ti-8 pet Mn alloy was by hot swaging to 3/8-in. diam at 760" and then 1/4-in. diam at 704°C. This material was then annealed 1 hr at 704", followed by furnace cooling to 593"C, and finally air cooling to room temperature. Evaluation—In order to examine more completely the effects of hydrogen on the particular materials studied, slow-speed tensile and notch-bend impact properties were determined in addition to fatigue data. Tensile specimens were of the standard ASTM type with a reduced section of 1/8-in. diam and a gage length of 1/2 in. A subsize cylindrical Izod specimen was used for impact tests. These specimens had a 45" notch with a 0.005-in. radius and a 0.150-in. root diam, and the stress concentration factor of this notch in bending was Kr = 3. Both the ten-

Jan 1, 1959

By W. T. Ober

the hammering effect acts only to a point 3 in. back from the cutting edge, and the hardening heat extends back only 1 in. from the cutting edge. Then, as a steel is taken from the fire, the grain condition is as shown in Fig. I. After the forging operation has been performed the condition shown by Fig. 2 exists. The heating operation to harden the cutting edge produces the effect shown in Fig. 3. The questions that naturally arise are: Will the cost of the extra heat treatment necessary to change this condition (annealing) be more than the saving that may be effected in the drill steel or will the extra heating be an economical as well as a wise thing to do? Is this condition necessarily detrimental to the maximum service of the drill steel? Can this annealing action be obtained in the hardening heat by heating more of the bit, say at least 5 in., to the hardening temperature but quenching only the end of the bit by a shallow immersion? Short Rock-drill Steels Reclaimed by Welding By W. T. Ober, Lynn, Mass. Experimental tests by the Thompson Company have shown that short lengths of rock-drill steels may be reclaimed by electric butt welding. The drills used in the experiments were hollow drills l1/4-in. in diametcr containing 0.95 per cent. to 1.05 per cent. carbon. The ends to be joined must first be ground off fairly square and the greater part of the rust, scale, etc. removed for 3 or 4 in. back in order to insure good electrical contact with the dies of the welder and countersunk, with an 80° countersink, approximately 1/4 in. The steels are then clamped in the copper dies of the welder, so that a length projects from the inside edge of each pair of dies equivalent to from one-half to three-quarters the diameter of the drill. The drills should also be brought into accurate alignment. The first step is to bring the ends into close proximity and then close the primary circuit of the transformer, slowly bringing the steels together until their ends lightly touch, when they will "flash," that is, minute

Jan 1, 1922

By W. T. Ober

the hammering effect acts only to a point 3 in. back from the cutting edge, and the hardening heat extends back only 1 in. from the cutting edge. Then, as a steel is taken from the fire, the grain condition is as shown in Fig. I. After the forging operation has been performed the condition shown by Fig. 2 exists. The heating operation to harden the cutting edge produces the effect shown in Fig. 3. The questions that naturally arise are: Will the cost of the extra heat treatment necessary to change this condition (annealing) be more than the saving that may be effected in the drill steel or will the extra heating be an economical as well as a wise thing to do? Is this condition necessarily detrimental to the maximum service of the drill steel? Can this annealing action be obtained in the hardening heat by heating more of the bit, say at least 5 in., to the hardening temperature but quenching only the end of the bit by a shallow immersion? Short Rock-drill Steels Reclaimed by Welding By W. T. Ober, Lynn, Mass. Experimental tests by the Thompson Company have shown that short lengths of rock-drill steels may be reclaimed by electric butt welding. The drills used in the experiments were hollow drills l1/4-in. in diametcr containing 0.95 per cent. to 1.05 per cent. carbon. The ends to be joined must first be ground off fairly square and the greater part of the rust, scale, etc. removed for 3 or 4 in. back in order to insure good electrical contact with the dies of the welder and countersunk, with an 80° countersink, approximately 1/4 in. The steels are then clamped in the copper dies of the welder, so that a length projects from the inside edge of each pair of dies equivalent to from one-half to three-quarters the diameter of the drill. The drills should also be brought into accurate alignment. The first step is to bring the ends into close proximity and then close the primary circuit of the transformer, slowly bringing the steels together until their ends lightly touch, when they will "flash," that is, minute

Jan 1, 1922

By N. F. Fiore, M. F. McGuire

THIS communication describes a series of experiments in which dislocation etch pitting was used to ascertain the depth of damage in crystals which were mechanically polished or which were cut with either a commercial metallographic cut-off wheel,* a com- All specimens were cut from single crystals of American Smelting and Refining Co. 99.999+ pct pure copper which were grown from the melt by the Bridge-man technique. The test specimens were disks, with faces being (111) planes and the disk axis a (111) direction. The disks were annealed in a vacuum of 10-5 Torr for 24 hr at 950°C prior to cutting or polishing and were given a light electropolishing in an ortho-phosphoric acid bath before etch pitting. Both Youngs1 and Livingston&apos;s2 reagents were used for etch pitting and the reagents gave identical quantitative results; however Livingston&apos;s reagent produced less staining and so all photomicrographs shown are of {111) surfaces etched with this solution. The surface of the annealed crystals showed well-defined subboundaries and a density of dislocations of about 1 X 106 per sq cm excluding those present in subboundaries, Fig. 1. The depth of cold work produced during mechanical polishing was determined after an annealed specimen was mounted in a paraffin holding block to protect it from extraneous damage. The exposed (111) surface was ground on metallographic papers and then polished on billiard cloth through 0.05-p alumina abrasive. It was necessary to remove about 0.3 mm (-0.01 in.) to obtain a structure representative of the annealed sur- face, indicating that the crystal was damaged to this depth during mechanical polishing. The cold work caused by standard cutting methods was measured in another series of tests in which cuts

Jan 1, 1967

By J. J. Stokes

Literature on the electrolysis of aluminum from cryolite melts and on the structure of these melts is surveyed critically. Data on density, freezing point, and other properties are reviewed. Theories of the electrolysis are examined in the light of these data. Two theories are presented which account equally well for the observations. ALTHOUGH the production of aluminum is a large-scale industrial process, consuming approximately 3 pet of all of the electric current generated in this country, the mechanism of the Hall Process remains a 70-year-old mystery. It is a remarkable fact that the aluminum industry, which was established largely through research and owes much of its growth to research, still employs as its basic process the one developed by Charles Martin Hall while he was still a young man working in a woodshed. There are, of course, modifications in detail and a tremendous expansion of the size of the units used, but basically the process employs carbon anodes and a carbon-lined iron vessel as a cathode for the electrolysis of alumina dissolved in molten salt. Of the almost infinite variety of salts available, the relatively minor Greenland mineral, cryolite, 3NaF.A1F3, is still the only one which gives good performance in the electrolysis. In the early days, the process was thought of as a simple one. The dissolved alumina dissociated and, during the electrolysis, the aluminum was carried to the cathode where it was discharged and collected in a pool of metal. The oxygen was carried to the carbon anode where it reacted to form primarily carbon dioxide together with some carbon monoxide. About the only virtue that can be claimed for this hypothesis is that of simplicity. The actual mechanisms must be tremendously more complex. This paper is devoted to a rather narrow part of the whole subject, namely, what ions are present in the bath, and by what mechanism the current is carried. The complexity of the literature on this system is demonstrated in Table I, which shows the ions postulated as being present during the process. This system is not easy to investigate. Cryolite melts at about 1000°C, so that all the investigations are at relatively high temperatures. Molten cryolite fumes in air, particularly if excess aluminum fluoride is present. The cryolite changes composition on heating at 1000°C, principally by reaction with moisture in the air, but apparently also by reaction with oxygen. Cryolite reacts with most of the customary materials of construction, and those that are not attacked by cryolite seem inevitably to react with molten aluminum. Graphite is the only common material that is inert to the electrolytic bath. Pure cryolite can be held in platinum. There is hope that some of the newer refractories will stand up in bath, and their development for this purpose would be a major advance in the field. The techniques to be discussed, then, are not the most advanced ones. Rather, they are examples of old standardized methods applied under difficult conditions. The principal methods that shed real light on the mechanism are density, electrical conductivity, freezing-point lowering, transport number, viscosity measurements, and reactivity of bath with carbon dioxide. The first measurement to be discussed is density. This procedure is relatively straightforward. A hollow platinum bob is suspended by fine platinum wire from an analytical balance into the melt being investigated. Density1-4 of the system sodium fluoride-aluminum fluoride is shown in Fig. 1. There is a maximum in the density near the cryolite composition, but actually the maximum is on the NaF-rich side of cryolite, close to the composition NaF - Na3AlF8. Density measurements are also useful in giving a clue to the nature of cryolite-alumina melts.1, 4 On the first addition of alumina, density decreases, Fig. 2, although the density of alumina, either solid or liquid, is higher than that of cryolite. These density results indicate that the systems are not simple. A great deal of effort has been spent in measuring the electrical conductivity of molten cryolite and of cryolite with various additives. Conductivity measurements are quite easy for fused salts that can be measured in a dip cell, but no successful dip cell has been made available yet for cryolite. Recourse is had

Jan 1, 1959

By B. M. Loring, I. R. Kramer, F. M. Walters

No observations on the mechanical properties of iron-manganese alloys have been published since pure manganese became readily available, either distilled manganese or electrolytic manganese. The purpose of this investigation was to determine whether iron-manganese alloys are essentially brittle, as reported by Hadfield,1 or whether the lack of ductility observed was due to impurities in the alloys that he studied. EXPERIMENTAL METHODS The alloys were melted in a 100-lb. high-frequency induction furnace with a magnesia crucible, using ingot iron and electrolytic manganese. The heats were split, the first giving six 18-lb. ingots and the second three. Each successive heat was higher in manganese and about 0.3 per cent silicon [ ] was added as ferrosilicon. The alloys forged without difficulty-and were given a 90 percent reduction to 3/4-in. rounds. The chemical analysis of the alloys is given in Table I. The forged rods were homogenized for [ ] 24 hr. at 1150°C. (2100°F.) and air-cooled. The alloys were tested in two conditions of heat-treatment: (I) as normalized from 870°C. (1600°F.) and (2) normalized from 870°C. and tempered for z hr. at 540°C. (1000°F.) and air-cooled. The tensile specimens were 0.505 in. in diameter with a 2-in. gauge length, and the impact specimens were V-notch Charpy. The proportional limit and yield strength were taken from the stress-strain diagrams drawn by a Peters recorder. The data obtained from the tensile test and the hardness measurements are given in Table 2. Specimens that were normalized are designated by N; those that were normalized and tempered by T. Alloy G was tempered after forging (D).

Jan 1, 1941

By Ballard H. Clemmons

THE future of the steelmaking industry of the Birmingham, Ala., district is closely related to and, in a large measure, dependent on the development of workable, economic processes of ore concentration. Operations thus far in the area have been possible only because of the fortuitous occurrence of iron ore, fluxing stone, and coking coal-all the primary iron-making materials- within a 25-mile radius of the blast furnaces. Commercial ore of the district consists mainly of a 10 to 20-ft hematite-calcite-silica bed locally known as the "Big Seam," a component of the Clinton formation of Silurian Age. At present mining rates, this ore will be available for a number of years. It is largely mined under 1000 to 2000 ft of cover and transported on 15 to 20" slopes that, in some instances, are as much as 10,000 ft long. Under these conditions, particularly with increasing distances from face to portal, mining costs are gradually becoming disproportionately high. Although not a major factor thus far, it should also be noted that the average annual ore output of the district is gradually be- coming more siliceous.

Jan 1, 1950