By R. W. Diamond

Low-grade ores can be designated by two main classifications: (1) simple low-grade ores, and (2) complex low-grade ores. As a rule the first type has a relatively small metal content, although low- grade iron ores contain a rather high percentage of metal. As the simple type is the one that is ordinarily in mind when the term "low-grade ore" is used, the paper will be devoted mainly to ores in this general category. Cheap treatment is the prime requirement in utilizing low-grade ores of the simple type, although in some cases the value of nonmetallic by-products, such as limestone for fer- tilizer and silica for flux, allows a little more lati- tude than in the usual situation. When the costs are divided under the three headings-mining, milling, and smelting-it is apparent that the last group will not constitute an important factor as a rule because the high concentrating ratio makes the smelting cost per ton of ore fairly low.

Jan 1, 1949

By R. G. Gifkins

Mean boundary migration depended linearly upon creep extension under various conditions. Prolonged annealing or air-casting increased the proportion of immobile boundaries at a given stage of tests. Grain growth during annealing followed a power law. The linking of migration and sliding in creep and models for migration are examined; activation energies are calculated from these models. Segregation of oxygen to boundaries appears to be a controlling factor. THE idea that boundary migration and boundary sliding during creep are linked has often been suggested,'-5 especially when evidence has been obtained for an alternation between the two processes. In simple bicrystals sliding can occur without any migration6 but in more complex bicrystals7 it is observed. McLean' and Couling and Roberts 5 made measurements of both sliding and migration; McLean concluded that there was no linking of the two processes whereas Couling and Roberts supported the idea. McLean' also developed a model for migration during creep and annealing. The present work was initiated as part of a study of the recrystallization of lead during creep9 but has been extended to examine some aspects of the mechanism of migration. MATERIALS AND METHODS Specially refined high-purity lead* was used; the total of impurities, excluding oxygen, was 0.0008 wt pct. Oxygen was removed as far as possible by melting in vacuo, treating at 550" to 600°C with hydrogen and then casting at 450°C under a vacuum of 10-2 mm Hg; the oxygen was then believed to be 0.00005 wt pct. Specimens were made from extruded strip and then annealed at the required temperature in an air oven, controlled to 5 lac. They were then polished in a mixture of acetic acid and hydrogen peroxide. At this stage some specimens were etched to give grain contrast and their grain sizes determined by the intercept method. Migration of boundaries during creep was measured on the surface of polished (not etched) specimens, directly loaded at room temperature (22°C) or 50°C (52"C) to initial stresses of 300 to 700 1b per sq in. Twenty six vacuum-cast hydrogen-reduced specimens were used and, in addition, two specimens were from material air cast after hydrogen reduction ("partial" air cast) and two from air-cast material not treated with hydrogen ("full" air cast). Duplicates were made in the majority of tests. At intervals through the creep tests, specimens were unloaded and the migration measured, normal to the direction of migration at the point of measurement, for each boundary along standard traverses. Usually between 110 to 180 boundaries were measured at each of some twelve stages of the tests. Migration was measured on the projected image (X100) using prism illumination. Fig. 1 illustrates the method of measurement and shows the kind of variation of migration found from boundary to boundary and along particular boundaries. Fig. 2 gives an example of more extensive migration. The mean value of distance migrated was generally reproducible to *10 pct but occasional points gave a scatter of *20 pct. The correctibn applied by McLean8 to allow for the contribution sliding makes to the apparent distance of migration could not be used, for the sliding at most boundaries was too small to measure with the equipment available. There were two reasons for supposing the correction unnecessary in the present work;

Jan 1, 1960

By Elmer Weber, W. M. Baldwin

Solid lead obeys a single parabolic weight increase vs. time law. In contrast, liquid lead undergoes three successive parabolic weight increases vs. time laws, the first of which has a low constant relative to the latter two. The conversion times for the change from one parabola to the next decrease with increasing temperature. IN recent reports on the subject,1,2 it was noted that zirconium and titanium scale in air by a complex mechanism. The scale first forming on the metal is protective to the extent that it gives a low constant, K, for Tammann's, and Pilling and Bedworth's parabolic equation: w² = Kt [1] relating weight increase, w, due to chemical reaction of the metal with the air, and time, t. After hundreds of hours of apparent stability in some cases the first scale yields to another that offers little protection to the metal. This transition from one scale to another, from a slow parabolic oxidation reaction to a fast one, was not due to impurities in the atmosphere or incidental effects (changing environment, etc.) but was a specific behavior of the metal itself, the transition occurring at definite times (dependent on temperature) and showing other reproducible traits. In view of this behavior how can long-time service behavior be predicted from short-time laboratory tests, not only in the case of these metals, but in any case? Certainly a systematic study of the type of scaling behavior described above—wherever it is found—would help to answer this question. The present paper is a report on the behavior as it is found in lead—the only metal to the authors' knowledge for which the behavior has been described at all, if inadequately, for our present purpose.* At least four oxides of lead are known, of which one occurs in two allotropic forms. They are ß (red) tetragonal PbO stable up to 486°C;8 a (yellow) orthorhombic PbO stable from 486°C up to its dissociation temperature in air at about 2300°C;9 minium or Pb3O4 which from the dissociation pressure data given in Fig. 1 decomposes to PbO at 540°C in air; lead sesquioxide or Pb2O3,; and lead dioxide or PbO2 which, according to Fig. 1, decomposes in air at 400°C to minium. In view of the high dissociation temperature of PbO, lead will scale up to at least its boiling point. Further, it is known that oxygen is almost insoluble in liquid lead.'V his implies a fair probability that an oxide scale would not dissolve in the molten metal and would afford the same protection to lead in the liquid state as in the solid. All of the oxides of lead for which specific gravity data are available are more voluminous than an equivalent weight of metal or a lower oxide from which they might form, hence the scales will be in compression. Lead oxides are known to be ductile, so it would be anticipated that they would form coherent nonporous scales. It is not surprising to learn, then, that both solid and liquid lead scale according to the Tammann, and Pilling and Bed-worth law.14,15 (Gruhl states that at 600°C and above lead oxidizes linearly with time because of "spitting" of the scale.) The parabolic constants K reported by various investigators3,14-16 are badly scattered, however, as shown in Fig. 2. The oxides formed on solid lead were described as being reddish-brown but were not chemically identified by Pilling and Bedworth.15 Gruhl's descripdin³ of the appearance of the scales On his liquid samples indicates that a (yellow orthorhombic) PbO is formed initially on the specimens but gives Way eventually—at least at temperatures below 486 °C— to .ß (red tetraunal) PbO, and that below 540°C minium—Pb3O4 :is firmed at an even later time as an overlay on either the red or yellow PbO. Fig. 3 is a graphical interpretation of Gruhl's description. Gruhl does not indicate any change in the parabolic scaling rate as yellow PbO converts to red. He does indicate that minium reduces the scaling rate, al-

Jan 1, 1953

By T. P. Chen, F. W. Bowdish

Studies made with a captive bubble apparatus on the sulfidization and collection by amyl xanthate of true chrysocolla specimens have defined the ranges of pH value and sulfide concentration which permit contact between the bubble and the mineral surface. Titanium compounds were the most effective of the materials found to activate the sulfidization of chrysocolla. With titanium activation, the contact angles and the ranges of pH value and sulfide wncentration giving bubble contact were all increased. Chrysocolla ores were concentrated by flotation. Chrysocolla ores occur at many localities in grade and quantity sufficient to make mining and millin feasible, but no satisfactory method of concentratio has been found. Although chrysocolla may be leached with acid, only those ores without acid-consuming gangue may be leached economically. Because of its potential importance, a study of the conditions nece sary for flotation of chrysocolla has been carried ou The literature contains a few references to flotation of chrysocolla. Two methods were developed by the U. S. Bureau of Mines.1,2 The first consisted of a fatty acid soap and a high xanthate as collectors of chrysocolla from a synthetic ore, while the second involved the use of hydrogen sulfide and xanthate. Ludt and DeWitt3 demonstrated the difference in adsorptive powers of chrysocolla and quartz for bas triphenyl methane dyes and suggested the use of butyl, hexyl or octyl-substituted malachite green as collector. Jackel4 emphasized the effects of combin tions of reagents such as Aerofloat 31, pine oil, and Reagents 404 and 425 with sodium sulfide and zinc hydrosulfite as conditioning agents. Although he reported recoveries of 89% from a synthetic ore and 98% from a natural ore containing azurite, malachite, chalcopyrite and chrysocolla, careful application of Jackel's method to chrysocolla from Tyrone, N.M., failed to give a high recovery. MATERIALS AND TECHNIQUE Samples from Inspiration, Ariz., and Tyrone and Magdalena, N. M., were used for experimentation and verified as true chrysocolla by leaching tests, specific gravity tests and X-ray diffraction. Chrysocolla does not dissolve at pH 4, although malachite and azurite do. Chrysocolla is about half as dense as the copper carbonates. X-ray diffraction analyses by the powder camera method confirmed the samples as true chrysocolla. A captive bubble apparatus, which cast an enlarged image of the air bubble and the mineral surface upon a screen, was used to check on the character of the surfaces. The specimens were prepared by grinding a flat surface on a glass plate using fine abrasive; then they were washed and kept in distilled water until they were to be treated with reagents. Before each reagent treatment, the specimen was carefully checked for cleanliness in the captive bubble apparatus. It was assumed that the surface was clean if, after fine grinding and washing of the specimen, the bubble would not stick. Specimens were handled with glass forceps, and precautions were taken to avoid contamination of the mineral surfaces. Contact angle measurements were carefully made several times on each treated specimen to obtain reliable average values. EFFECT OF pH VALUE AND SODIUM SULFIDE CONCENTRATION In each experiment, a specimen with a freshly ground surface was immersed for 10 min in a solution of sodium sulfide, washed and immersed for 15 min in a solution containing 30 mg per 1 of potassium amyl xanthate. The specimen was then washed again in distilled water and tested for contact angle in the captive bubble apparatus while submerged in distilled water. In this series of experiments, the pH of the sulfidizing solution was varied from 3 to 7, and the concentration of sodium sulfide, containing 60% Na2S, was varied from 50 to 650 mg per 1. Many combinations of pH value and sulfide concentration resulted in no contact between the bubble and the surface, but over a limited range of conditions, contact angles varying from 24ºto 52ºwere obtained. The data in Fig. 1 show sulfidization conditions that lead to bubble contact and those that do not. The region of contact is surprisingly small, which may indicate why flotation of chrysocolla involving sulfidization has proven so difficult in practice. Several features of the system are illustrated in Fig. 1. In the region between pH values of 4 and 6 with sodium sulfide concentrations below about 350

Jan 1, 1963

By J. M. Boutwell

I. Introduction. THE object of this paper is to present a concise statement on the genesis of the copper- and lead-deposits of the Bingham Mining District, Utah. It is essentially a condensation of a chapter in a detailed report on this district, together with so much on geologic features, and on the character and occurrence of the ores as bears on the problems of ore-deposition. The studies upon which the paper is based were undertaken in 1900 under the direction of S. F. Emmons, Geologist-in-Charge of the Section of Metalliferous Deposits, U. S. Geological Survey; and a little additional data was secured in subsequent years. The evidence then obtained as to the genesis of the replacement copper-ores has led, to conclusions which differ somewhat from explanations hitherto current. Accordingly, it seems desirable briefly to present the facts together with the resulting conclusions in a separate paper.

Nov 1, 1905

By G. W. P. Rengstorff

In an effort to find an oxidation-resistant alloy of molybdenum, binary and ternary alloys containing aluminum, chromium, cobalt, iron, nickel, silicon, titanium, tungsten, vanadium, and zirconium were screened. Fourteen other alloying additions were also tested. Many of the alloys were more oxidation-resistant than molybdenum, but none were entirely satisfactory. MOLYBDENUM oxidizes extremely rapidly above 1450°F in air. At 1800°F, a loss of metal at the rate of 0.1 in. in 4 hr is typical. The high speed of this oxidation may be judged by comparison with the oxidation rate of 0.1 in. per year (0.00005 in. in 4 hr), sometimes taken as the maximum permissible oxidation rate at 1800°F for a satisfactory Fe-Cr-Ni alloy. Great strides have been made in the development of coatings and cladding to protect molybdenum from oxidizing atmospheres. These developments in surface protection will undoubtedly make it possible to take advantage of the excellent hot strength of molybdellum and its alloys in many new applications. Still, even the best coating can protect molybdenum only as long as the surface layer is unbroken. Research was undertaken to determine whether an alloy of molybdenum could be found which would resist oxidation. Such an alloy would not deteriorate suddenly when the protective surface layer was destroyed in a small area. In seeking an alloy of molybdenum to resist oxidation, the physical properties of molybdenum could not be sacrificed entirely. The development of an alloy with the desired resistance to oxidation was not achieved. The information obtained on the effect of a large number of elements on the oxidation of molybdenum is, however, of value in the development of coatings. Indeed, many of the alloys tested for oxidation resistance were already known to have poor mechanical properties but were tested to aid in the development of coatings. Oxidation of Molybdenum The rapid oxidation of molybdenum is usually attributed to the volatility of Moo,,. Gulbransen and Wysong have shown that molybdenum oxidizes very slowly up to 850°F, the temperature at which the oxide film begins to evaporate. Melting as well as evaporation of molybdenum oxides promotes the oxidation of molybdenum. MoO melts at 1465°F. MOO, the oxide which is believed to form at the metal-oxide interface, combines with MoO, to form a eutectic having a melting point of 1432°F.' The liquid oxide, even if nonvolatile, could cause poor resistance to oxidation by allowing easy transport of molybdenum and oxygen ions through the oxide. Actually, a sudden increase in the rate of oxidation of molybdenum at 1460°F has been observed to coincide with the appearance of a liquid phase. The formation of a volatile oxide is not unique with molybdenum. The problem is also encountered with vanadium, tungsten, and some of the Pt-Pd group of metals. Vanadium not only forms the volatile V2O3 but, like molybdenum, forms a liquid oxide coating. Few attempts have been made, however, to prevent the rapid oxidation of these metals by alloying. Oxidation of Molybdenum Alloys At the beginning of this work, very little was known of the oxidation resistance of molybdenum alloys. It was known that molybdenum disilicide (with 37 pct Si) has extremely good oxidation resistance,' but this compound is so brittle that it has few uses. It is an effective protective coating for molybdenum when allowance can be made for its brittleness. Chromium was known to retard the oxidation of molybdenum,' but at least 50 pct Cr was necessary to have an appreciable effect. Other, unpublished, reports show that a few other alloys have been given preliminary tests, but the results have not been promising." Choice of Alloys to be Investigated An alloying element might be expected to protect molybdenum in either of two ways: Its oxide might combine with molybdenum oxide to form a stable, nonvolatile complex oxide (a molybdate); or the oxide of the alloying element might form in preference to molybdenum oxide, developing an impervious layer which would prevent the formation of a volatile molybdenum oxide. The knowledge available about the formation of molybdates was meager. Therefore, the initial study was made on alloys of molybdenum with elements having especially stable oxides. On this basis, binary and ternary alloys containing the following six elements were investigated: aluminum, chromium, titanium, zirconium, silicon, and vanadium. Nickel was also added as an alloying element. Although it does not form a more stable oxide than molybdenum, it does impart some oxidation resistance to copper and iron. Its inclusion in the study was fortunate because its alloys proved to be the most promising of those first tested. Apparently nickel formed a stable molybdate. Because nickel was effective in reducing the oxidation rate of molybdenum, the elements iron, cobalt, and tungsten were added to the list. The ten alloying elements mentioned form ten binary and 45 ternary alloying systems with molybdenum. A series of alloys was tested in each of these systems. In addition, at least one test was made on the effect of each of the following alloying elements:

Jan 1, 1957

By Walter Lee Brown

One of the characteristic steps in the march of modern scientific progress is the substitution of improved time-saving and labor-saving appliances for the antiquated and, in most cases, inconvenient forms of chemical and physical apparatus used by the earlier experimenters. This fact is strongly impressed upon us when we consider the question of the employment of illuminating-gas as a source of light, heat and power. Concerning its value as a light-producer, let the record of the past three-quarters of a century speak for itself. As a factor for power, we have evidence of its efficiency in the shape of the gas-engine. But its adaptability as a medium of heat, is the feature to which I wish to call attention, and in a special direction, viz., the assaying of ores. Gas assay-furnaces have been known and used for some years, but not to any very great extent, in this country at least. Therefore no apology on my part is required for the description I now give of a complete gas assaying-plant. The illustration accompanying this paper is a faithful representation of the group, as it was designed by, and arranged for myself, and appears in actual running order in my laboratory to-day. Its duty is to do roasting, crucible-fusion, scorification and cupellation. The furnace at the left is for roasting sulphurets or other ores for experimentation or actual work. It is what is known as a Fletcher No. 163, and consists of a fire-clay body strapped with sheet-iron bands, and a burner (No. 16, Fletcher). The opening at the top

Jan 1, 1885

By W. M. Myers

Certain minerals possess inherent color and other properties that make them suitable for the pigmentation of paints, mortar, plaster, concrete, face brick, and other materials. Their production is one of the most ancient of mineral industries and their use by primitive man is well known. These natural pigments have some economic factors in their favor, particularly wide geographic distribution, low cost of production, ease of preparation, chemical stability, and permanence in use so that they continue to form the basis of a small but useful industry. When used in paints such pigments act as a filler and supply body and opacity in addition to color. Natural mineral pigments are prepared for the market by the comparatively simple operations of washing, grinding, blending, and calcining. Any one, or all of these processes may be applied to a single pigment. The development of synthetic pigments and the use of by- product materials have introduced competition with the products of nature and are having a growing influence on the economic position of the mined minerals.

Jan 1, 1949

By K. W. Smith, E. A. Thomas

Various grades of synthetic mullite have been developed in recent years to replace or supplement natural sources of mullite deriued from the mullite group of minerals consisting of sillimanite, kyanite, and andalusite. Raw materials and heat treating processes used in making synthetic mullite are described. Chemical and physical data are given for typical grades and crystalline structure is illustrated with micrographs. Use of synthetic mullite as a refractory material in the glass and metallurgical industries is discussed. Mullite (3A12O3.2siO2), the only stable compound formed in the alumina-silica system, is usually present to some degree in all aluminum silicate ceramic products. The formation of mullite is considered beneficial to give rigidity to the structure and is dependent upon the ratio of Al2O3 to SiO2 in the original composition, particle size, degree of mixing, firing temperature, cooling rate, and the presence of auxiliary glass-forming fluxes. Mullite may also be formed at the reaction interface of fire clay or alumina-type refractories in contact with glass or slag melts. The term synthetic mullite is commonly used today to identify a class of sintered and fused aggregates or grains in the alumina-silica system having a highly developed mullite structure but derived mainly from raw materials other than the sillimanite group of minerals. Within the past 15 years extensive research has been done to develop economical processes to form sintered synthetic mullite aggregate to replace calcined Indian kyanite in super-refractories. Severa1 brands of such mullite are now being produced in commerical quantity and finding extensive use in refractories. Based on the service results of such refractories in many applications throughout the metallurgical, ceramic, and glass industry these developments have been considered successful and suitable substitutes for Indian kyanite now appear assured. EARLY DEVELOPMENT The conversion of kyanite, sillimanite and anda-lusite minerals of the sillimanite group to mullite and their use in refractories and porcelain have been discussed quite extensively in the literature by peck,' Grieg,' Riddle and Foster,3 Bowen and Grieg,4 and others and will only be mentioned here for reference to compare properties with synthetic mullite. In 1928, curtis5 reported on the development of a high temperature gas-converter process for forming synthetic mullite. The raw materials were derived mainly from lumps of high alumina clay of the correct natural composition or blends of clays and alumina that was interground and briquetted to form a suitable charge to maintain a surface combustion firing within the converter. Curtis was, no doubt, the first to illustrate by micrographs in natural color the crystalline structure of mullite derived from kyanite and mullite derived by sintering clay and alumina mixtures at temperatures above cone 32 (3123°F) and by electric fusion. In 1937, sei16 was issued a patent covering the use of a mixture of alumina-silica minerals and alumina in the proportion to form a mullite-yielding material at temperatures in excess of 3100' F. During the period from 1930 to 1940, economic conditions were not favorable for the production of synthetic mullite mainly due to an adequate supply of good grades of Indian kyanite ore suitable for conversion to mullite. Uncertain conditions on availability of the Indian kyanite during the early stages of World War II fostered further study on the development of synthetic substitutes. In 1943, McVay and wilson7 reported on an extensive investigation of domestic substitute materials. Their work covered essentially the use of mixtures of electric furnace mullite, calcined topaz, and calcined domestic kyanite. Compositions were found that gave equivalent or better hot load strength than Indian kyanite in mullite-type brick compositions; however, the calcining of the topaz presented certain physical and chemical problems on the disposition of silicofluoride and hydrofluoric acid while the high cost of electric furnace mullite was a limiting factor. In this work it was pointed out that water-quenched fused mullite was found to be unstable on reheat and gave poor hot load strength due to excessive glass present whereas the slow cooled or annealed mullite contained large crystals of mullite and corundum with little glass and gave superior results.

Jan 1, 1961

Discussion of the paper of John H. Hall, presented at the New York. Meeting, October, 1913, and printed in Bulletin No. 79, July, 1913, pp. 1247 to 1256. WILLIAM 'R. WEBSTER, Philadelphia, Pa.:-I would like to call ,attention to the fact that the results of the ordinary tension and bend tests do not always give us the information we want even if we figure out the amount of work done. You want a bending test of sufficient width and full thickness. In the case of eyebars, for instance, I have had experience with a 10- by 1-in. eyebar which gave perfectly good results in a full-size test of the finished bar. The 10- by 1.5-in. and 10- by 1.75-in. eyebars from the same heats-of steel were absolutely worthless in full-size tests. The narrow bending tests from all these bars gave good results. Bat after going into the matter fully, we found that if pieces about 3 in. wide and full thickness were used for the. cold bending tests, the heavier material would not stand this test, but failed. That is, in order to check the quality of the rolled bar you should have a wide piece of full thickness for cold bending, as the narrow pieces give misleading results. J. E. JOHNSON, JR., New York, N. Y. :-I would like to ask if there have been any tests made to compare the results of Charpy tests with the true dynamic test similar .to the Wohler test, except that the piece is subjected to a tensile or compressive stress and to alternating stresses in addition, at the same time. This seems to me to approach more nearly than any other test to the conditions of actual service. where the piece is under a fixed initial stress plus a highly variable and often alternating stress. Some tests were made on this plan in England within a year or two. The test piece was Subjected to either a tensile or compressive stress of known amount and simultaneously to alternating stresses in addition. Such a. test as this gives information which we cannot get by a tensile test or even from the tensile strength multiplied by an. elongation. Such tests, however, are exceedingly tedious and require long periods of time in order to obtain valuable results. If material could be subjected to these dynamic tests and the same material to the. Charpy shock test, and if some reasonable qualitative relation could be established between the results of the two tests, then we could assume that the shock test, which is so simple and easy to make, was a measurably accurate test of the dynamic qualities of the material. At present it does not seem

Jan 12, 1913

By John A. Graves

Anaconda's Jackpile-Paguate mine, located between Albuquerque and Grants, N.M., is situated at an elevation of 6000 ft in a semi-arid desert region. The original Jackpile deposit was discovered by Anaconda air and ground exploration parties in Nov. 1951. A large percentage of the uranium mined in New Mexico comes from the Jackpile-Paguate, which is one of, if not the largest, open pit uranium mines in the world. From 1953 to the present, 120 million tons of overburden, mining waste, and low-grade material have been removed to produce approximately 10 million tons of merchantable uranium ore, having an average grade of about 0.25% uranium oxide. Identifying the Orebody Surface drill holes delineate the ore bodies on a predetermined grid which varies in dimension but usually affords 100-ft control. These holes are probed immediately after drilling by geophysical logging trucks, resulting in a gamma log and digital readout from each hole. From this information it is possible to arrive at an almost immediate conversion to percentage of U3O8 on 6-in. intervals. Initially a hole is probed at a reconnaissance speed of 10 fpm with a time constant of 8 sec. Wherever the gamma recording goes off scale on an initial run, that particular zone is rerun at 2 fpm and at a time constant of 2 sec. This time constant is the interval that emissions are counted and accumulated for recording purposes. The search radius of the Geiger probe is approximately 18 in.

Jan 8, 1974

By Cheri Eby, William R. Eby

INTRODUCTION Pneumatic conveyance systems provide for material placement at high compaction rates in confined spaces. This method of conveyance provides proper roof support and ground stabilization important to underground mining activities. Today underground mining activities are conducted far differently than those of our ancestors, in that the reclamation process is the final step in any mining activity. Responsible mine owners are constantly seeking innovative methods to assist them in their reclamation procedures. During the last few years, particular attention has been paid to previously mined areas, as many of these abandoned areas lay open, imposing a constant threat to humans and animals. Considerable attention is being directed to applying proper methods for the filling and sealing of underground slopes, drifts, tunnels, and adits, because today we are experiencing the effects of past mining activities such as subsidence, acid mine water run-off, buring refuse piles, and underground mine fires. Furthermore humans and animals who have ventured into abandoned mine openings have died from exposure, suffocating gases, and mine collapse. This paper explains the method of pneumatically filling and sealing these openings and underground works by means of employing pneumatic equipment and proper backfill material together, thus achieving high material compaction and thereby providing the complete filling of the voids and alleviation of the mentioned dangers. NEUMATIC SYSTEMS The use of air to transport material is widely used; however, conveying abrasive material (e., rock, earth, and cement) requires certain pneumatic transport systems designed to handle the abrasiveness as well as the size of these materials. The Eby pneumatic transport sys tem, known as a Mobile Stower, in mounted on a 42-foot trailer pulled by a Kenwor th tractor. This arrangement allows for quick mobilization and project set-up. The pneumatic system, composed of several components assembled together, produces the volume and pressure of air required to transport the material. Knowledge of elevation, ambient temperature, and material composition at the locations to be backfilled play a big part in the design and useage of the pneumatic system. In this particular system design, material is placed by a front-end loader into an eight (8)-yard hopper which is located over a belt conveyor. The conveyor transports the material up to an air lock feeder, which is the metering devise used to feed the material into the Tee Injector located directly below. Air is supplied by a positive displacement blower which, in this instance, delivers up to 4400 CFM's of air at 8 to 12 PSI. Horse power requirements to drive the blower are met with the useage of either a diesel engine or an electric motor. A diesel engine enables the Mobile Stower to operate in remote areas. As the air flows through the upstream air piping, it passes through the Tee Injector and picks up the material and conveys it through the material conveyance pipe, (referred to as down-stream pipe), and out the placement nozzle. Depending upon material composition and the amount of tonnage to be moved, either mild carbon steel pipe or specially heat- treated hardened pipe is used for the material conveyance line. The entire pneumatic system is controlled from the operator's console. With the aid of instrumentation, only one person is required to operate the system. Tonnage rates vary in accordance with horse power and air supply, as well as

Jan 1, 1982

Jan 1, 1922

Jan 1, 1922

By J. S. Aronofsky

The first step in a quantitative analysis ot the mechanism of oil displacement by water in a fractured reservoir is usually conceded to be the solution of the differential equation describing the saturation distribution of two immiscible fluids flowing in a porous medium, where the capillary pressure is taken into account. In such a system the production mechanism may consist of displacement of oil both by the flow of water due to natural or artificially imposed pressure gradients and by imbibition, which implies a flow of water not due to external pressure gradients. Owing to the presence of the two oil displacement mechanisms, the mathematical model given by the differential equation intended to describe the system may not properly represent the behavior of the physical system. In fact, in the reservoir the rate of water advance may be very slow, and in the case of a fractured reservoir with a great number of large fractures, the pressure difference determining the flow of water through the matrix may be much less than 1 lb/'psi over lengths of a few feet. In such a case, imbi-bition (the exchange between oil in the matrix and water in the fractures resulting from capillary forces) may become, with time. a significant element of the production mechanism. It occurred Lo the authors, however, that without going into a physical analysis of the process of production, it might be possible by means of simple abstract reasoning to throw some light on the variation of recovery with time under conditions occurring in a highly fractured oil reservoir with rising water table. The object of this paper is to present both the reasoning and its application to a reservoir of the highly fractured type. Specifically, the analysis given here was undertaken to try to explain the increase of recovery (as defined later) with time as observed in this reservoir, without having to assume unlikely variations in the reservoir parameters with depth. This attempt has been successful as will become clear upon comparison of the computed recoveries with the actual field data. ABSTRACT MODEL Let us consider a small volume. of porous matrix saturated with oil at time, t = 0. Let the process of oil displacement by water start at time, t = t,,. At some time, t, the process will have terminated. Then a volume of oil equal to or smaller than the original oil contained in the matrix will have been produced. The first basic assumption that describes the model and guides the forthcoming reasoning is that the oil production from the small volume. dv, is a continuous monotonic function of time and that it converges to a finite limit. Such an assumption is not inconsistent with the results of laboratory waterflood tests as well as with results of imbibition tests where this is, in fact, observed. The second basic assumption is that none of the properties which determine the rate of convergence change sufficiently during the process to affect this rate or the limit. Let it be assumed that the form of the function of time relative to production from the matrix volume. dv, is given by where V,(t) is the volume of oil produced up to that time t. R is the limit toward which the recovery converges, A is a constant giving the rate of convergence, and V,(t) is the volume of oil originally in place in the volume, dv. It should be noted that recovery at time I will be understood here to he It follows that r. tends to R as t tends to infinity. CONSTRUCTION OF RESERVOIR FROM ABSTRACT MODEL Let the reservoir consist of a series of identical blocks of porous matrix stacked vertically and separated by fractures. Let each of these blocks satisfy the conditions of our abstract model. These conditions are: (1) that recovery is a continuous mono-tonic function of time converging to finite limit, and (2) none of the properties that determine the rate of convergence change sufficiently to affect the rate or the limit. Let water be rising in fractures so that oil production from any part of the block starts when the water comes in conLact with it. TOTAL RECOVERY FROM THE RESERVOIR COMPARED TO RECOVERY FROM A SINGLE MODEL ELEMENT As stipulated in Eq. 1, in the case of the abstract model,

By Harlowe Hardinge, R. C. Ferguson

Laboratory and plant data covering 12 different operations show that lower than "standard" ball mill speeds increase grinding efficiency. In the case of high pulp-level mills, the gain is so great that the increase in capital cost of the larger lower speed mill will pay for itself in less than a year's time.

Jan 1, 1950

By Jeff Steinhoff

INTRODUCTION The Henderson mine utilizes a highly mechanized, continuous, panel-caving, mining system to extract ore from a deep, massive, molybdenite deposit. The mine is located 80.5 km (50 miles) west of Denver, Colorado. The mine surface facilities are located 3,170 m (10,400 feet) above sea level in a steep valley on the eastern side of the Continental Divide. Milling facilities are 24 km (15 miles) west on the western side of the divide at an elevation of 2,804 m (9,200 feet) above sea level. The ore- body is located approximately 3,000 feet south of the valley under Red Mountain. Access to the ore for men and materials is through a 915 m (3,000-foot) deep, 8.5 m (28-foot) diameter, vertical, concrete-lined, service shaft. Access from the mill is through a 15.5 km (9.6-mile) rail haulage tunnel. The mine is ventilated through an additional intake shaft and two exhaust shafts. Mine production at this time is 27,255 mtpd (30,000 stpd). The mine ventilation system supplies 1,038 cubic meters per second (2.2 million cfm) through approximately 60 miles of drifting or 2.7 tons of air per ton of ore mined. There are 130 fans in the mine in fixed locations and in vent lines with 6,900 connected horsepower in the mine. MINING METHOD AND LAYOUT The orebody is divided vertically into two major zones. The upper zone is the 8100-level production area. The bottom zone is the 7700- level production area which is in the early development stage. The rail haulage level at 7500 feet is common to both production zones. Each mine production zone consists of five associated sublevels. The cave undercut level is 16.8 m (55 feet) above the production level. Two boundary cutoff levels are located 44.2 m (145 feet) and 62.5 m (205 feet) respectively above the production level. The fresh-air level is positioned 15.2 m (50 feet) below the production level, and the exhaust vent level is 19.8 m (65 feet) below the production level. Horizontally, each production zone is divided into three panels each, 224 m (800 feet) wide. These panels are caved from south to north. As the caving in one panel nears completion, caving in the adjacent panel is initiated. Development for the caving panels is continuous so that the sublevels above the production level and the production level itself have a combination of development drifting and production-related activities. UNDERGROUND VENTILATION NETWORK The ventilation system is zoned in the same manner as the orebody itself. One major split of 600 cubic meters per second (1,270,000 cfm) ventilates the 8100-level production zone; one split of 100 cubic meters per second (210,000 cfm) ventilates the development of the 7700- level production zone; and one split of 165 cubic meters per second (350,000 cfm) ventilates the 7500 rail haulage level. The haulage tunnel requires an additional 188 cubic meters per second (400,000 cfm) of air. Development-drift ventilation is accomplished by hanging 1.0 m (3.5-foot) diameter steel ducting in the drifts with 40-horsepower, 0.96 m (38-inch) diameter fans supplying 9.4 cubic meters per second (20.000 cfm). The normal maximum length for these systems is 300 m (1,000 feet). The 8100-level production-area ventilation system is especially suited to a high level of mucking activity confined in a small area. Approximately 93 per cent of the mine's total production is transferred from the drawpoints to ore passes in 10 production drifts. The active area in each drift is 300 m (1,000 feet). Twelve 5-cubic-yard LHD units with Cat turbo- charged 170-horsepower engines are assigned to the area. Under these conditions, more than one LHD is assigned to a particular production drift. Adequate ventilation is maintained by making an air change every 97 m (320 feet) along the production drifts. Fresh air is brought into the production drifts from the fresh-air level through 1.37 m (4.5-foot) diameter raises. Air travels south along the production drift to the ore pass where it is exhausted down the ore pass to the exhaust level. The ore pass is followed by another intake which is followed by an ore-pass exhaust. At the south end of the production area, a series of exhaust fans maintain a southerly air- flow through the production level.

Jan 1, 1981

By W. H. Bassett, C. H. Davis

The late J. P. Sparrow, chief operating engineer of the New York Edison CO., carried out a series of practical tests on condenser tubes of several copper alloys and reported on the results to the Association of Edison Illuminating Companies at its meeting in September, 1913. In the preparation of these tubes the senior author had the pleasure of cooperating. Copper-zinc alloys in the proportions of 60-40,70-30,80-20, 90-10, and Admiralty metal, which is in effect 70-30 with 1 per cent. of tin, were tried. Monel metal and several copper-nickel alloys, and 8, 5, and 3 per cent. aluminum bronze were also tried. At the time of this report, the aluminum bronze had been in service for 4 1/2 years and seemed to be giving especially good results but later it began to fail and showed no substantial improvement over Admiralty metal. Monel metal was unsatisfactory and the nickel alloys apparently did not give better service than the Admiralty alloy. Previous to the publication of the report, and after considerable discussion, it was agreed that a test where tubes of different kinds could be under laboratory observation would be advisable, so the apparatus described here was set up in The American Brass Co.'s Waterbury Laboratory. This was fitted with tubes of copper, brass, bronze, nickel silver, cupro-nickel and other alloys, and the test started on Oct. 11, 1912. Salt water from East River, New York harbor, was barrelled and transported to the laboratory for the test. A fresh supply, completely replacing the water in service, was obtained at the end of each six months period. Plan of Procedure In general, the procedure was to inspect the tubes at short intervals and to remove those that had begun to leak. The tubes removed were carefully examined and a photographic and microscopic record of the

Jan 1, 1925

By Glen R. Neighbors, Sylvan Cromer

HIGH subsurface temperatures and pressures are making cementing operations more difficult as deeper producing horizons are being sought. Recorded bottom-hole temperatures above 200°F. and pressures in excess of 12,000 Ib. per sq. in., obtained by combining hydrostatic and pump pressures, are not uncommon. Insufficient time is available for proper placement of standard Portland cement, because of the shortened setting time produced by these excessive temperatures and pressures, therefore special types of cements have been developed to overcome these difficulties. From the standpoint of placement, the ideal slurry would be one that would remain fluid long enough to be placed, then harden rapidly, so that there would be a limited amount of contamination and the well could be placed on production in a minimum of time. It is highly desirable, therefore, that some method be devised to measure accurately the time that any slurry will remain in a fluid state while being pumped into the well. To study the effect of elevated temperature and pressure on fluidity, the authors have developed the pressure-type consistometer (Figs. I and 2) described below, and are presenting data obtained with it, using slurries of both quick-setting and slow-setting cements. Studies were made over a temperature range from 110° to 270°F., and a pressure range from atmospheric to 3000 lb. per sq. inch. APPARATUS The fluidity of cement slurries at atmospheric pressure is usually determined with the Halliburton consistometer1 or the Thickening Time Tester.2 These instruments are similar, in many respects, to an ordinary ice-cream freezer. The slurry to be tested is placed in a container that is rotated at a constant speed with an electric motor. Constant temperature is maintained by surrounding the container with a thermostatically controlled bath. The torque on the paddles, which is proportional to the force needed to shear the slurry, is indicated on a scale. The Halliburton instrument is calibrated from 0 to 100 poises against fluids of known viscosity. To permit direct correlation of observed elevated pressure data with those published at atmospheric pressure, the authors' designs of the slurry container, paddle, and torque indicator closely resemble those used on the Halliburton instrument. Duplicate results may be obtained at atmospheric pressure in either instrument. Instead of the atmospheric constant-temperature bath, one was built from a high-pressure steel bull plug. A Uni-Bolt union equipped with a blanking plug serves as the top, permiting the instrument to be opened or closed in less than one minute. The slurry container is built from Shelby steel tubing. A wrench socket welded to the bottom of the container engages a hexagonal nut on the top of the steel shaft that rotates it. This acts as a universal

Jan 1, 1941

By G. Willard Quick

FAILURES in railroad rails have been of vital concern to engineers; railroad executives, rail manufacturers and the general public for years. Failures from transverse fissures originating from internal nuclei have received particular attention in the past 20 years. Dr. J. E. Howard first reported this type of failure in 1911, as being responsible for a wreck-on the Lehigh Valley R. R. in which several lives were lost. Since then many transverse fissures have been found. In 1919, Waring and Hofammann1 etched longitudinal sections of rails in hot acid and found cracks extending both longitudinally and transversely in certain used rails as well as in some new rails.. Since then it has been thought by many that these "shatter" cracks are the nuclei from which transverse fissures subsequently develop in service. Methods for reducing the rate of cooling rails on the hot. bed have been devised to decrease the temperature gradient and consequently the stress gradient in the rails. A study of the tensile properties of rails at elevated temperatures was made by Freeman and Quick,2 who investigated the properties at temperatures through which rails pass on the cooling bed after leaving the hot saw. In their investigation a special study was made of the ductility of the steels in the temperature range 400° to 700° C. In this temperature range it was found that certain rail and other steels showed a marked decrease in elongation and reduction of area. The phenomenon was called "secondary brittleness" and the temperature range the "secondary brittle range." A tentative explanation was presented that internal failure such as "shatter cracks" and "hair cracks" in rails are the result of thermal stresses developed in the steel structure while cooling through the secondary brittle range. The investigation showed that the magnitude of the phenomenon varies for different heats, but that it did not differ for specimens from different ingots or for different rails in a particular ingot. It was also shown that annealing rail steel at a temperature either above or below the critical

Jan 1, 1932