By E. N. Skinner, Arthur Philliops

During the course of an experimental program concerned with the hydrogen embrittlement of copper containing oxygen in concentrations within the solubility limits it became necessary to make a critical appraisal of the literature dealing with the solubility relationships of oxygen and solid copper. The latest determinations, and perhaps the only data obtained on "spectroscopically" pure copper, are those of Rhines and Mathewson' who reported that the solid solubility increases from 0.007 per cent oxygen at 600°C. to about 0.01; per cent at 1500ºC. Hanson, Marryat and Ford2 had previously placed the solubility limit at less than 0.009 per cent oxygen at 1000ºC. and Allen and Street3 had suggested, on the basis of an unpublished research by T. Hemitt, not over 0.005 per cent oxygen at 500°C. In the introductory stages of the investigation indirect evidence accumulated to suggest that the solubility limits were significantly lower than those previously reported. For this reason it was deemed essential to clarify this point before proceeding with a program intended to establish a quantitative relationship between hydrogen embrittlement and oxygen concentrations positively known to be within the solid solution range. Furthermore, the increasing production and the highly selective applications of the commercial "oxygen-free" coppers inevitably direct attention to the practical necessity for exact knowledge regarding the effects of mini-tie concentrations of the elements ordinarily found in the high-purity coppers now available. Of these elements oxygen occupies a unique position, not only by virtue of its specific effects on copper but more particularly in view of its important reactive tendencies toward the other impurities with which it is associated. Rhines and Mathewson considered several methods for measuring the solubility of oxygen and finally adopted the simple plan of saturating the specimens, obtained from redeposited cathode copper, by heating at the desired temperature in air. After the removal of surface oxide by mechanical and chemical means, the oxygen content was determined in the underlying metal. In general, this process of saturation, with a few modifications, was followed by the present writers. Although the procedure is direct and has obvious advantages, its effectiveness, unfortunately, is reduced by an excessive scaling of the copper, particularly at the higher temperatures. After saturation treatments above 900°C. the writers found that the specimens, necessarily rather thin in the original condition, consisted largely of scale and yielded too little metal for a satisfactory analytical sample. Furthermore, great difficulty was experienced in effecting complete removal of the scale. Needless to say, it is necessary to exercise extraordinary care in the preparation of the surface of the analytical sample in order to eliminate submicro-scopic fragments of cuprous oxide which ordinarily are lodged in the crevasses and

Jan 1, 1941

By E. N. Skinner, Arthur Philliops

During the course of an experimental program concerned with the hydrogen embrittlement of copper containing oxygen in concentrations within the solubility limits it became necessary to make a critical appraisal of the literature dealing with the solubility relationships of oxygen and solid copper. The latest determinations, and perhaps the only data obtained on "spectroscopically" pure copper, are those of Rhines and Mathewson' who reported that the solid solubility increases from 0.007 per cent oxygen at 600°C. to about 0.01; per cent at 1500ºC. Hanson, Marryat and Ford2 had previously placed the solubility limit at less than 0.009 per cent oxygen at 1000ºC. and Allen and Street3 had suggested, on the basis of an unpublished research by T. Hemitt, not over 0.005 per cent oxygen at 500°C. In the introductory stages of the investigation indirect evidence accumulated to suggest that the solubility limits were significantly lower than those previously reported. For this reason it was deemed essential to clarify this point before proceeding with a program intended to establish a quantitative relationship between hydrogen embrittlement and oxygen concentrations positively known to be within the solid solution range. Furthermore, the increasing production and the highly selective applications of the commercial "oxygen-free" coppers inevitably direct attention to the practical necessity for exact knowledge regarding the effects of mini-tie concentrations of the elements ordinarily found in the high-purity coppers now available. Of these elements oxygen occupies a unique position, not only by virtue of its specific effects on copper but more particularly in view of its important reactive tendencies toward the other impurities with which it is associated. Rhines and Mathewson considered several methods for measuring the solubility of oxygen and finally adopted the simple plan of saturating the specimens, obtained from redeposited cathode copper, by heating at the desired temperature in air. After the removal of surface oxide by mechanical and chemical means, the oxygen content was determined in the underlying metal. In general, this process of saturation, with a few modifications, was followed by the present writers. Although the procedure is direct and has obvious advantages, its effectiveness, unfortunately, is reduced by an excessive scaling of the copper, particularly at the higher temperatures. After saturation treatments above 900°C. the writers found that the specimens, necessarily rather thin in the original condition, consisted largely of scale and yielded too little metal for a satisfactory analytical sample. Furthermore, great difficulty was experienced in effecting complete removal of the scale. Needless to say, it is necessary to exercise extraordinary care in the preparation of the surface of the analytical sample in order to eliminate submicro-scopic fragments of cuprous oxide which ordinarily are lodged in the crevasses and

Jan 1, 1941

By L. W. McKeehan

The occurrence of twins in large ferrite crystals, made by a new process, was reported in a recent note.' This paper describes a typical case of such twinning and suggests, on the basis of the observed facts, why smooth slip-planes are rarely observed in this metal. Method of Preparation The material in which the crystals here dealt with were grown was made from 1/8in. Armco iron welding rod containing C, 0.04; S, 0.037; P, 0.003; Si, 0.008, and Mn, 0.02 per cent. This rod was cold drawn into wire about 1 mm. dia. A piece of this wire was supported vertically and was locally heated in hydrogen at atmospheric pressure to about 1400" C. by an alternating current (60 cycles per sec.) of about 35 amp., passed through it between a pair of traveling contacts about 8 cm. apart. The rate of travel for the case in hand was 12 cm. per hr. After some 30 cm. of the length of the wire had been heated and cooled in this manner the whole wire was immersed for a few seconds in dilute nitric acid, not restrained by alcohol. Etching was continued until, as nearly as could be judged by eye, the original smooth cylindrical surface of the wire was no longer capable of specular reflection. Measurements The wire in the etched state was next mounted in a goniometer of special form which allowed the measurement of the spherical coordinates of the normals to any plane surfaces left by the etching. These coordinates were most conveniently a polar distance, 8, from one direction of the wire axis, and an azimuth or longitude, ?, from an arbitrary prime meridian. The region to be described more particularly is shown at a low magnification in Fig. 1, which gives two different views, differently illuminated to show the spatial relationship of a crystal occupying most of the part shown and of an inclusion, or rather a series of three inclusions suspected of being twins based on the principal crystal.

By J. Donovan Jacobs

An underground excavation project usually is a highly organized complex of different but interrelated construction activities. It is the whole effort, including the necessary tools, which will be referred to as the System. Tunnel-driving and shaft-sinking operations are among the most systematic of construction efforts. Systems are not new in the performance of construction. It is the Systems Concept which seems only recently to have been discovered and made the subject of much study and discussion. HISTORICAL From the seventeenth century, when explosives were first utilized for rock excavation, until the successful application of the rotary-head continuous tunneler in this decade, the cyclical drill-blast-muck-support method has been standard tunnel-driving procedure throughout the world. Whatever improvements occurred were the result of development of better tools for performing the various operations of the cycle. The electric locomotive replaced the mule and permitted the use of larger muck cars. The steam drill, which ended the day of the double jack, was itself quickly made obsolete when compressed air replaced steam as the source of drilling energy. Power shovels were introduced to save the time and money involved in the hand-loading of excavated materials. A cubic yard of rock tunnel muck can be excavated today for just half the man-hours of labor required in 1948. Developments over 20 years which cumulatively have resulted in this economy include: drifter drills mounted on hydraulically controlled booms and positioners; tungsten-car- bide-tipped bits; long feed shells on the drifters, making it possible to drill the full depth of a round without changing steel; better designed,

Jan 1, 1970

By William G. Christy

EFFORTS at smoke abatement date back to the year 1273 in England when a law was passed prohibiting the use of "sea cole." The law was not enforced, so King Edward I, 33 years later, appointed a commission "to enquire of all such who burnt sea cole in the city or parts adjoining, and to punish them for first offense with great fines and ransomes, and for the second offense to demolish their furnaces." Many other commissions have since been named to investigate the smoke problem in England, but it still persists in many British cities. In the United States the movement to abate the smoke nuisance started in certain Middle Western cities, and has made considerable progress. Until recently, the coal-producing industry co-operated little in smoke¬abatement programs, taking the attitude that smoke elimination is the dealer's or user's responsibility; and the dealers, in turn placed the responsibility entirely on the user.

Jan 1, 1942

By J. S. Ll. Leach, M. B. Bever

THE system copper-nickel exhibits complete solid and liquid miscibility1 The thermodynamic properties of such a system would not be expected to deviate greatly from ideality. Although the evidence is conflicting, anomalies in the composition dependence of various physical properties of solid copper-nickel alloys suggest that mixing may not be ideal.' From measurements of the Hall coefficient it has been concluded that clustering occurs in these alloys. ' Considerations involving the phase diagram of the ternary system copper-nickel-chromium have led Mei-jering3 to predict a positive heat of formation for solid copper-nickel alloys. An electrochemical investigation of the activity of nickel in copper-nickel alloys showed unexpectedly large positive deviations from ideality.4 wagner5 has proposed that if the entropy can be considered ideal, these measurements would yield the following equation for the heat of mixing at 700°C H" = 3380 x,vl (l-xVi) cal per g atom [I1 The heat of formation at 722°C of solid copper-nickel alloys of the equiatomic composition has been measured in a reaction calorimeter as 540 cal per g atom. This note reports calorimetric measurements of the heat effects on dissolution of some copper-nickel ndon: in tin. These measurements were preliminary to a larger investigation, which was later discontinued. From them the heats of formation of the alloys can be calculated, if certain assumptions are

Jan 1, 1960

By H. F. Winham

The history, development, subsurface geology, production, economics and estimated reserves are discussed in this paper. The Magnolia structure is an anticline with a known maximum structural relief at 372 ft., and the areal extent of the producing acreage is 4494 acres. Production is obtained from the Smack-over oölitic lime and 116 successful wells have been drilled. The field, which was developed on 40-acre spacing, has been under strict control. It is believed to be producing with a strong water drive, To date it has produced more than eighteen million barrels and the estimate of ultimate recovery is 220 million barrels. Early History The Magnolia field is in colurnbia County, Arkansas, T. 17 s., R. 19 and 20 W. Various geologists had long been interested in this general area, and as early as 1921, John F. Magale was able to define a surface structure. The first wildcat, one of the first in Columbia County, was drilled in 1923 by Mid-States Oil Co., in sec. 10, T. 17 S., R. 20 W. This well was about 11/2 miles northwest of the Kerlyn oil Company's discovery well and was based on surface geological work done by Jewel and Dobie. Subsequently, several shallow wells that were not carried below the Upper Cretaceous beds were drilled in the immediate area of the discovery well, but none of them contained any commercial showings of oil Or gas. In the latter part of 1935, Elam and Magale (or Southwood) Garrett NO. I was located in sec. 13, T. 17 S., R. 20 W., 3/4 mile east of the discovery well. It was drilled to a total depth of 4018 ft. in the lowermost Glen Rose beds but failed to obtain any showings of oil or gas. Interest had been stimulated in this general area, however, by the discovery of several oil fields, mainly Glen Rose oil production in the Rodessa field in Louisiana in 1935, Smackover lime productioil in Snow Hill in May 1936, production from the Cotton Valley formation in Schuler in 1937, and Smackover lime production from the Buckner field in November 1937. With this background and subsequent seismic work, which was carried on partly because the old shallow wells drilled in the township had shown evidence of closure in the Upper Cretaceous beds, the discovery well, Kerlyn Oil Company's Barnett No. I, Sec. 14, T. 17 S., R. 20 W., was originally projected to a total depth of 6300 ft., to test the equivalents of the Morgan sands of the Cotton Valley series, then producing at Schuler. The well was carried to a depth of 6325 It. and tested the objective beds without finding commercial production. In the meantime, however, one well had found production in the Jones sand and another in the Smaclrover lime at Schuler. Kerlyn immediately made arrangements to deepen the Barnett well to the Smackover lime. The top of the Smackover lime was encountered at 7618 ft. and the well

Jan 1, 1943

By H. F. Winham

The history, development, subsurface geology, production, economics and estimated reserves are discussed in this paper. The Magnolia structure is an anticline with a known maximum structural relief at 372 ft., and the areal extent of the producing acreage is 4494 acres. Production is obtained from the Smack-over oölitic lime and 116 successful wells have been drilled. The field, which was developed on 40-acre spacing, has been under strict control. It is believed to be producing with a strong water drive, To date it has produced more than eighteen million barrels and the estimate of ultimate recovery is 220 million barrels. Early History The Magnolia field is in colurnbia County, Arkansas, T. 17 s., R. 19 and 20 W. Various geologists had long been interested in this general area, and as early as 1921, John F. Magale was able to define a surface structure. The first wildcat, one of the first in Columbia County, was drilled in 1923 by Mid-States Oil Co., in sec. 10, T. 17 S., R. 20 W. This well was about 11/2 miles northwest of the Kerlyn oil Company's discovery well and was based on surface geological work done by Jewel and Dobie. Subsequently, several shallow wells that were not carried below the Upper Cretaceous beds were drilled in the immediate area of the discovery well, but none of them contained any commercial showings of oil Or gas. In the latter part of 1935, Elam and Magale (or Southwood) Garrett NO. I was located in sec. 13, T. 17 S., R. 20 W., 3/4 mile east of the discovery well. It was drilled to a total depth of 4018 ft. in the lowermost Glen Rose beds but failed to obtain any showings of oil or gas. Interest had been stimulated in this general area, however, by the discovery of several oil fields, mainly Glen Rose oil production in the Rodessa field in Louisiana in 1935, Smackover lime productioil in Snow Hill in May 1936, production from the Cotton Valley formation in Schuler in 1937, and Smackover lime production from the Buckner field in November 1937. With this background and subsequent seismic work, which was carried on partly because the old shallow wells drilled in the township had shown evidence of closure in the Upper Cretaceous beds, the discovery well, Kerlyn Oil Company's Barnett No. I, Sec. 14, T. 17 S., R. 20 W., was originally projected to a total depth of 6300 ft., to test the equivalents of the Morgan sands of the Cotton Valley series, then producing at Schuler. The well was carried to a depth of 6325 It. and tested the objective beds without finding commercial production. In the meantime, however, one well had found production in the Jones sand and another in the Smaclrover lime at Schuler. Kerlyn immediately made arrangements to deepen the Barnett well to the Smackover lime. The top of the Smackover lime was encountered at 7618 ft. and the well

Jan 1, 1943

By Harold Rose

THE peak of production from the Appalachian natural gas field was apparently reached about 10 years ago, and the annual production from Pennsylvania, West. Virginia and Ohio has now dropped to about two-thirds of the amounts obtained in 1916-and 1917. This falling off in production has occurred in spite of vigorous efforts and large expenditures by producing companies to maintain or increase their output. The greatly increased costs of development and handling are reflected in the present average value of natural gas at the point of consumption, which value in the three states referred to, has more than doubled in the past 10 years. While it is true that the natural gas production of the United States has increased during recent years, this increase has come from southwestern states, particularly from Oklahoma, California, Louisiana and Texas, which states are now leaders in the production of this valuable but fleeting resource. Pennsylvania, originally the leading state in natural gas production, occupies sixth place in the latest (1924) U. S. Bureau of Mines statistics. West Virginia, which held first place for 15 years, has dropped to third rank, and Ohio is the seventh state in the order of natural gas production. Domestic and industrial demands for gas are constantly increasing everywhere in the United States. These growing demands have accentuated the difficulties in the localities with depleted natural gas supplies, and serious shortages have already occurred during winter months in the Pittsburgh district. Some relief has been obtained by placing restrictions on the industrial use of natural gas, and by, increasing the price (which tends to reduce consumption). Yet these are but temporary expedients for checking gas consumption, which fail to solve the problem of adequate future supplies of gas.

Jan 10, 1926

By Max Y. Seaton

THE scope of this paper will be limited to finished materials that contain a large preponderance (around 80 per cent or more) of magnesium oxide. The large and commercially important production of refractory dolomite and modified dolomites is not discussed here, and the production of magnesium basic carbonate for use as a heat insulator is barely mentioned. The discussion is confined mainly to magnesias produced in comparatively great quantity by direct processing of naturally occurring raw materials and hence excludes secondary or highly purified products such as pharmaceutical products or U.S.P. light and heavy calcined magnesias of commerce. NOMENCLATURE The nomenclature of the magnesia products that will be discussed is somewhat confusing, in that it is customary in the trade to designate as "calcined magnesite" the materials that result from the calcining of magnesite to temperatures that remove the contained carbon dioxide. The finished product, therefore, is not magnesite at all but simply a more or less pure magnesium oxide or magnesia. Furthermore, partly for statistical and partly for commercial reasons, it has been customary, during recent years, to classify as "calcined magnesite" products that result from the heat-treatment of magnesium hydroxide precipitated from magnesium-containing brines; products that, obviously, have no relationship whatever to magnesite. In the listing of magnesia-containing materials, tonnages of which are regularly reported by the Bureau of Mines, reports ordinarily are made under two headings: "caustic calcined" magnesite, in which all of the varieties of products treated at relatively low temperatures are lumped; and "dead-burned" magnesite, in which are included both high-purity and low-purity, and particularly both high-iron and low-iron, materials that have been so heat-treated that the magnesium oxide occurs predominantly as crystalline periclase-materials used almost entirely for refractory purposes. In 1940 the apparent domestic consumption of "caustic calcined" magnesite was approximately 17,000 tons, about 95 per cent of which was produced in this country. The apparent consumption of "dead-burned" magnesite was approximately 172,000 tons, some 82 per cent of which was domestically produced. In both total quantity and percentage of material produced within the United States, these figures are record highs for many years past. UTILIZATION As indicated by these figures, the major tonnage outlet for magnesia is the refractories industry, in which magnesia is employed principally in three ways: (I) as dead-burned grain magnesite for the construction and maintenance of the hearths or bottoms of basic open-hearth furnaces; (2) in the form of refractory magnesite bricks and shapes; and (3) as a chemical

Jan 1, 1942

By Max Y. Seaton

THE scope of this paper will be limited to finished materials that contain a large preponderance (around 80 per cent or more) of magnesium oxide. The large and commercially important production of refractory dolomite and modified dolomites is not discussed here, and the production of magnesium basic carbonate for use as a heat insulator is barely mentioned. The discussion is confined mainly to magnesias produced in comparatively great quantity by direct processing of naturally occurring raw materials and hence excludes secondary or highly purified products such as pharmaceutical products or U.S.P. light and heavy calcined magnesias of commerce. NOMENCLATURE The nomenclature of the magnesia products that will be discussed is somewhat confusing, in that it is customary in the trade to designate as "calcined magnesite" the materials that result from the calcining of magnesite to temperatures that remove the contained carbon dioxide. The finished product, therefore, is not magnesite at all but simply a more or less pure magnesium oxide or magnesia. Furthermore, partly for statistical and partly for commercial reasons, it has been customary, during recent years, to classify as "calcined magnesite" products that result from the heat-treatment of magnesium hydroxide precipitated from magnesium-containing brines; products that, obviously, have no relationship whatever to magnesite. In the listing of magnesia-containing materials, tonnages of which are regularly reported by the Bureau of Mines, reports ordinarily are made under two headings: "caustic calcined" magnesite, in which all of the varieties of products treated at relatively low temperatures are lumped; and "dead-burned" magnesite, in which are included both high-purity and low-purity, and particularly both high-iron and low-iron, materials that have been so heat-treated that the magnesium oxide occurs predominantly as crystalline periclase-materials used almost entirely for refractory purposes. In 1940 the apparent domestic consumption of "caustic calcined" magnesite was approximately 17,000 tons, about 95 per cent of which was produced in this country. The apparent consumption of "dead-burned" magnesite was approximately 172,000 tons, some 82 per cent of which was domestically produced. In both total quantity and percentage of material produced within the United States, these figures are record highs for many years past. UTILIZATION As indicated by these figures, the major tonnage outlet for magnesia is the refractories industry, in which magnesia is employed principally in three ways: (I) as dead-burned grain magnesite for the construction and maintenance of the hearths or bottoms of basic open-hearth furnaces; (2) in the form of refractory magnesite bricks and shapes; and (3) as a chemical

Jan 1, 1942

By Julian Szekely

Through the simultaneous statement of Maxwell's equations. the turbulent Navier-Stokes equations and the differential thermal energy balance equation, a mathematical representation has been developed for heat transfer and fluid flow in electric arc furnaces. In broad outline the theoretical predictions appear to be consistent with experimental measurements. A discussion is presented of the general arc furnace control and optimization problem, together with the potential for the incorporation of the mathematical model given in the paper, into future control and optimization schemes. ELECTRIC ARC FURNACE STEELMAKING accounts for about 24% of the total steel produced in the U.S., consuming about 550kw-hr/ton of steel which amounts to about 1.4x1010 kw-hr annually. The percentage of steel produced by the electric arc furnace route has doubled since 1960 and is expected to increase further in the foreseeable future, particularly with the more extensive use of direct reduction technology. Table I shows, in terms of percentages, the principal items that contribute to the cost of running an electric arc furnace. It is seen that in addition to the fixed costs (labor, depreciation, taxes etc.) electrode costs and power consumption are the dominant inputs, and it follows that process changes that would ultimately reduce any of these cost components would have a significant impact on the efficiency of the operation. There are three main areas where progress in arc furnace design and operation must be directed in the next decade (Committee on Technology, 1981). 1. Increased furnace productivity 2. Reduction in processing cost 3. Improvement in the thermal efficiency of the furnace An estimate of the current operating efficiency of the electric arc furnaces may be obtained by comparing the theoretical minimum energy consumption per ton of steel with those achieved in operational practice. Theoretically 330-360 kw-hrs of electricity are required to melt one ton of cold scrap. For superheating, 8-12 kWh per 100°F are required. The actual energy requirements are given in Table II. It is seen that furnaces currently operate at 70-80% efficiency, with the major heat loss from the furnace resulting from the waste gases (Committee on Technology, 1981). While it is apparent that operational experience has produced a technology that is reasonably energy efficient this has been achieved in the almost complete absence of any detailed knowledge concerning the fundamental heat transfer mechanisms occuring in the furnace. The purpose of the present paper is to present a case for the usefulness of mathematical models in increasing the thermal efficiency of furnaces by investigating these heat transfer mechanisms and then combining this knowledge with existing electrode regulator mechanisms to produce truly efficient power cycles for melting and refining. In particular, existing mathematical models describing convection, radiation, and electro-magnetism in the furnace should be employed, and the development of optimization models which balance the cost of electrodes and energy against the thermal efficience of the furnace should be undertaken. Recent work in this laboratory (Szekely, McKelliget, 1981, 1982, 1983; Szekely, McKelliget, Choudhary, 1983) has made a useful start towards solving the problem of heat transfer within the electric arc furnace but the work still needs to be directly related to existing furnace power cycles and tested against plant scale measurements.

Jan 1, 1984

By M. R. J. Wyllie, Walter D. Rose

The use of electrical well logs for the quantitative determination of such reservoir parameters as connate water saturation, formation permeability and connate water salinity has recently been attracting the attention of a number of workers1,2,3,4,5. While the theory of the determination of connate water salinity from the self potential S.P. log has received rather detailed treatment, relatively little attention has been paid to the theoretical aspects involved in the quantitative interpretation of resistivity data. It is clear that if electrical well logs can be used for the quantitative evaluation of physical characteristics of reservoir rock, they will provide a valuable tool to supplement cheaply information obtained by more laborious core analysis. In certain cases it is conceivable that the coring program could be considerably curtailed if the electric log could be relied upon to give reasonably accurate quantitative information. It is our object in this paper to examine the theoretical basis of quantitative log interpretation as expressed in such well-established logging concepts as formation factor and cementation factor. It is also our object to investigate the physical aspects of the rela- tionship which is presumed to exist between resistivity index and brine saturation in reservoir rock. In particular, we will endeavor to draw attention to the fact that it is possible to express these logging concepts in terms of capillary pressure-saturation relationships, permeability and tortuosity, parameters which we will consider in this paper to be fundamentally indicative of rock texture. The probability of being able to obtain from log recordings alone the data theoretically essential to permit quantitative log interpretatiou will be examined, and consideration will also be given to the problem of formulating simple semi-empirical relationships for use in the field. THEORETICAL CONSIDERATIONS The concept of formation resistivity factor, or as it is now commonly called, formation factor, appears to have been introduced by G. E. Archie",". Formation resistivity factor as defined by Archie is the resistivity of a rock 100 per cent brine-saturated divided by the resistivity of the brine. This relationship had previously been used by physical chemists and the concept is, for example, implicit in an early treatment by Fricke7 of the conductivity of aqueous slurries. Archie was able to establish the fact that although the relationship between formation factor and porosity did not change too greatly for different rock textures, the relationship between formation factor and permeability was markedly dependent on rock texture. The relationship found by Archie between formation factor and porosity was expanded by H. Guyod8. Archie had suggested that the formation factor, F, could be expressed in terms of the porosity, F, as follows: F =F-m .... (11 where, F = effective porosity fraction of the sand, and, m = an exponent greater than about 1.3. Guyod introduced the term cementation factor for the exponent, m, since it may be qualitatively shown that formation factor for any given porosity tends to increase as the sand becomes more cemented. It would appear that the concept of m as an exponent representing the cementation in a sand is strictly only of qualitative value, since the quantitative estimation of m by means other than the determination of F and F has not been possible. Guyod suggests that m can be estimated from a visual examination of a sample of rock, but this method appears to be both arbitrary and unreliable. It can be said, however, that in intergranular reservoirs of practical interest, the range of m is from about 1.4 to 3.0. A possible explanation for the fact that m is found to lie between these limits will be offered below. The determination of formation factor is an essential preliminary to the

Jan 1, 1950

By A. G. H. Andersen, A. W. Kingsbury

SILICON bronzes containing iron are used to a considerable extent in industry, under the trade name of P.M.G. alloys. Various classes of wrought alloys fall in the composition range 1.5 to 3.5 per cent silicon, and 0.5 to 2.5 per cent iron. Castings may contain as much as 6 per cent silicon and 3 per cent iron at present. The constitutional diagrams of these alloys are thus of considerable practical importance. Copper-silicon-binary alloys have been thoroughly investigated by a number of workers, the latest reports being those of C. S. Smith1 and of A. G. H. Andersen.2 Although much work has been done on iron-copper alloys,3 recorded investigations on the copper-rich copper-iron binary constitutional diagram are not numerous. Tammann and Oelsen4 determined the solubility limits of iron in copper by means of magnetic measurements, and found that the solubility of iron in copper amounts to a fraction of one per cent at 400°C., increasing slowly to one per cent at 800°C. From 800°C., the solubility increases rapidly and attains 4 per cent at 1100°C. Hanson and Ford,5 using electrical resistivity measurements and the microscope, determined a somewhat different solubility limit. Of earlier X-ray works on the copper-iron system, very little has been published. The work by Bradley and Goldschmidt6 on copper-iron-aluminum alloys includes some information on the copper-iron binary. These investigators conclude that substitution of iron in the copper lattice decreases the spacings, which is contrary to the evidence of the present work. Hanson and West7 have investigated the ternary alloys of copper with iron and silicon. Although their diagrams are valuable contributions to the understanding of these alloys, they did not recognize the kappa phase,12, 7,8 and their diagrams do not everywhere conform to the phase rule. The present work contains a check by means of X-rays of the solid solubility limit of iron in copper, and an X-ray investigation of the ternary-phase diagram, which, owing to present conditions, it became necessary to curtail considerably. PREPARATION OF SAMPLES Castings weighing about 75 grams were melted under vacuum. The charges were made up of ingot iron, copper cathodes from Laurel Hill, and refined silicon supplied by the Electrometallurgical Co. Alundum crucibles were generally used. The exceptions were alloys 77 and 78, which were melted in graphite crucibles. The ingots were annealed at 800°C. for one week, then samples were cut for chemical analysis. Longitudinal sections of the binary alloy ingots were hammered into plates 3 in. thick. Wherever possible, these plates were homogenized at temperatures ensuring

Jan 1, 1942

By John D. Weibmer

A strong step towards acknowledgement of mining as a skilled trade has been taken by the Tintic Division of Kennecott Copper Corp. In May 2 ceremonies, a pilot program was signed into force which, possibly for the first time in US history, recognizes mining as an apprentice trade and grants journeyman status to those who complete the prescribed training sequence. The apprenticeship standards, hammered out after months of consultation between management, labor, and government, are presently limited only to underground hard-rock mining and only within Kennecott's Tintic Division, but the architects of the program are confident that the concept will spread-first to other underground operations where miners desire documented evidence of their special skills, then to open-pit and soft-rock operations.

Jan 6, 1977

By Eric S. Cheney

Sulfur isotopes are best used in conjunction with other geological studies to determine the origin of known deposits; concept-oriented exploration programs can then be developed to find similar deposits. Geochemical processes are capable of causing different S '41S" ratios in the minerals and fluids participating in natural reactions. Because the magnitude of the resultant isotopic difference is inversely proportional to temperature, sulfur isotopic studies can be used to determine the source of the sulfur in high temperature deposits. The narrow spread of sulfur isotopic values from ores related to cupolas of felsic intrusions suggests that the sulfur in the ore-forming fluids was derived from a fairly uniform source (such as the intrusions) rather than by heated ground water from the adjacent country rocks. However, geologic and isotopic evidence suggest that the sulfur of many nickel sulfide ores may have been derived from the country rocks rather than the associated mafic igneous rocks. This sulfurization hypothesis implies that mafic intrusions in sulfur-rich country rocks should be prime exploration targets. Sulfur isotopic analyses of sulfides in the mafic rocks may indicate whether sulfurization has occurred. In equilibrium geochemical reactions S" is concentrated in the minerals with the greater bonding strengths. Thus the isotopic compositions of coprecipitated sulfides that have not undergone exsolution may be used as geothermometers and to distinguish multiple periods of mineralization, post-ore metamorphism, etc. The sulfur isotopic compositions of coexisting sulfides at Butte, Mont., indicate that the copper minerals did not originate by simple replacement of pyrite. Geologic and isotopic evidence suggest that the mineralogical and isotopic zoning at Butte formed almost isothermally during the geochemical evolution of the ore-forming fluids upward and outward from the Central zone. Unidirectional reactions cause enrichment of S" in the products. At low temperatures the isotopic effects of bacterial and inorganic reactions are difficult to distinguish. Anaerobic sulfate-reducing bacteria apparently were responsible for the sulfur of Gulf Coast salt domes and for diagenetic pyrite in sandstone-type uranium deposits. Sulfur (and carbon) isotopic data suggest that the roll ore bodies of sandstone-type uranium deposits originated by limited inorganic oxidation of diagenetic pyrite rather than by bacterial activity. Accordingly roll ore bodies should be most numerous and thickest against those portions of the sandstone aquifer that contain pre-ore pyrite.

Jan 1, 1975

By Harold Rose

THE peak of production from the Appalachian natural gas field was apparently reached about 10 years ago, and the annual production from Pennsylvania, West Virginia and Ohio has now dropped to about two-thirds of the amounts obtained in 1916 and 1917. This .falling off in production has occurred in spite of vigorous efforts and large expenditures by producing companies to maintain or increase their output. The greatly increased costs of development and handling are reflected in the present average value of natural gas at the point of consumption, which value in the three states referred to, has more than doubled in the past 10 years. While it is true that the natural gas production of the United States has increased during recent years, this increase has come from southwestern states, particularly from Oklahoma, California, Louisiana and Texas, which states are now leaders in the production of this valuable but fleeting resource. Pennsylvania, originally the leading state in natural gas production, occupies sixth place in the latest (1924) U. S. Bureau of Mines statistics. West Virginia, which held first place for 15 years, has dropped to third rank, and Ohio is the seventh state in the order of natural gas production. Domestic and industrial demands for gas are constantly increasing everywhere in the United States. These growing demands have accentuated the difficulties in the localities with depleted natural gas supplies, and serious shortages have already occurred during winter months in the Pittsburgh district. Some relief has been obtained by placing restrictions on the industrial use of natural gas, and by increasing the price (which tends to reduce consumption). Yet these are but temporary expedients for checking gas consumption, which fail to solve the problem of adequate future supplies of gas.

Jan 10, 1926

By Ming-Kao Yen

A considerable amount of work has been reported in the literature in regard to the texture and earing behavior of copper strip. The rolling texture of copper has been confirmed as (110) [112] and (112) [111], which yields ears of a drawn cup at the position 45" from the rolling direction.1-3 The recrystallization texture has been established as the cubic or (100) [001] texture, where the earing positions are at 0" and 90" to the rolling direction.4-8 It has also been reported that in the development of cubically aligned grains of copper strips, the percentage of this cubic texture increased with an increase of final reduction and final annealing temperature.8,9 A comprehensive study on H.C. copper (British commercial copper of high-conductivity quality = Cu 99.95 pct, O2 0.03 pct, Ag 0.003 pct, Fe 0.005 pct and Pb < 0.001 pct) was made by Cook and Richards.6 They concluded that the recrystallization textures could be described as one or more of the following textures: (1) a single texture (100) 10011, (2) a twin texture (110) [112] and (3) a random orientation, depending upon the previous history of the specimen concerned. The effect of various alloying additions in copper was reported by Dahl and Pawlek.10 They found that certain alloying additions, such as 5 pct Zn, 1 pct Sn, 4 pct Al, 0.5 pct Be, 0.5 pct Cd, or 0.05 pct P suppressed the formation of cubic texture. Brick, Martin and Angierll reported that the cold rolled textures due to various additions fitted a rather simple pattern. However, the recrystallization textures were subject to very considerable variations. In the discussion of this paper, Baldwin stated that deoxidized copper containing 0.02 pct P gave a complicated recrystallization texture at lower temperature. When this copper was annealed at high temperature, a single texture appeared which was described as (110) [ill] but. according to a pri- vate communication from Baldwin, this orientation reported was in error and should have been reported as (110)[112]. He also reported that the earing positions of drawn cups were at 60" to the rolling direction.12 Recently, Howald, in his discussion on the paper by Hibbard and Yen,13 reported that the rolling texture of phosphorus deoxidized copper, containing from 0.006 to 0.020 pct phosphorus, was of the pure copper type. When these coppers were annealed at lower temperatures, they exhibited a random orientation, and when they were annealed at higher temperatures they had a mixed (111)[110] and (100)[001] texture, depending on the severity of the final reduction and annealing temperature. However, the specific influence of phosphorus and other impurities on the recrystallization textures and the deep drawing properties of copper strip has not been thoroughly reported. Therefore, an attempt has been made in the present work to determine the rolling and recrystallization textures and also the earing behavior of five types of commercial copper and thereby to evaluate the effect of phosphorus and some other significant impurities on the development of texture for cold reductions of about 87 to 89 pct. Materials Used The five types of copper employed in the present investigation were two phosphorus deoxidized coppers of different phosphorus content (0.007 and 0.013 pct P), an oxygen-free copper (OFHC), an electrolytic tough-pitch copper, and a fire-refined tough-pitch copper. These materials were subjected to a thorough spectroscopic and chemical analysis. The designations and the chemical compositions were as shown in Table 1. The coppers, FA1, FA2 and FA3. were hot-forged from 3-in. billets into a ½ X 6-in. plate and cold rolled to the ready-to-finish gauge indicated below. FA4 and FA5 were hot rolled and scalped to ready-to-finish gauge. The grain size of all the materials in the ready-to-finish condition was about 0.030 to 0.045 mm. Table 2 shows the last stage of the production schedule for each copper strip used. Experimental Procedure ANNEALING, GRAIN SIZE AND HARDNESS DETERMINATIONS Specimens of each type of copper were finally annealed in air for periods of one hour at temperatures ranging from 300 to 1600°F and were subsequently cooled in air. The average grain diameter of the annealed specimen was estimated by comparing with a standard grain size chart. Hardness was determined on the Rockwell 15 T scale. CUPPING TESTS Cups were made in a blanking and drawing set, in which blanks of 2-in. diam were drawn to a cup of 1.25-in. diam with an average depth of about 0.75 in. The clearance between the punch and die was about 0.032 in. The ears of the cup were measured with a special fixture which read the height of ears to one-thousandth of an inch on every ten-degree interval along the circumference of the cup. POLE FIGURES The usual transmission diffraction method with unfiltered copper radiation was employed to determine the pole-figures of the specimens cold-rolled or annealed at 900°F. All the pole-figures were derived from the positions of intensity maxima on 111 diffraction rings of the X ray photo-grams taken at 10 rotation of a

Jan 1, 1950

By G. W. Traer

The distillation of bituminous coals at what is commonly termed low temperature, and the quantities, nature and adaptabilities of the products have been the subject of considerable experimentation, during recent years. Fortunately, the earlier work in this country was done by men whose scientific training qualified them properly to record and interpret the results of their experiments. The work of Prof. Parr, of the University of Illinois, is especially notable in this respect. Prof. Parr&apos;s work, added to that of English experimenters, demon-strated-certain things to a degree which is generally regarded as convincing. They have proved that a caking bituminous coal, when subjected to a temperature of not more than 1000" F. (preferably somewhat less) will yield light tar having low specific gravity (about 1.06) and high value; also, that this yield, with a given coal, will depend upon the percentage of hydrocarbons in the coal, the maximum temperature used, and the promptness with which the distillate gases are removed. It is assumed that air is excluded from the retort, and that the coal is subjected to heat for a sufficient time to drive off all of the tarry hydrocarbons. The results attained in the first, or low-temperature stage of the car-bocoal process, recently described by C. T. Malcolmson,1 corroborate these general principles. It is the purpose of the writer to describe other work of a practical nature, directed toward the commercial adaptation of these principles, which was begun nearly two years ago; this investigation was assisted by A. J. Sayers, of the Link-Belt Co., and Carl Scholz. The first step was to draft tentative designs for the handling of the coal and coke so as to produce a coke having a suitable structure for sizing, storage, shipment, and handling, without the necessity of briquetting. Prof. Parr&apos;s results had indicated that the rather open-pored volatile coke produced by him had a low ignition point, which would contribute toward easy control of the fire in stoves, house furnaces, fire-boxes, and boilers. It is recognized by those experienced in the marketing of fuels that the hard non-volatile coke from the high-temperature process,

Jan 1, 1920

By F. E. Rizzo, L. R. Bidwell, D. F. Frank

THE poor high-temperature oxidation resistance of the refractory metals becomes an important problem as higher operating temperatures are sought. A meaningful analysis of their oxidation behavior requires a knowledge of the phases that can appear during oxidation as well as their relative stability. Although several extensive investigations have been carried out to obtain this information for the W-0 system,1-10 serious inconsistencies still remain. First, the standard free energies of formation (AG°) determined in recent studies which used the solid electrolyte galvanic cell technique6,7,9 differ significantly from those obtained primarily from gas equilibration measurements.1,3,4,10 The disagreement is especially large for the highest oxides. These data have been used to predict the decomposition temperatures of WO2. 72 and WO2.90.1 A considerable extrapolation is required, resulting in a large uncertainty in the decomposition temperatures. Second, Bousquet and perachon3 have presented convincing evidence, ob- tained by gas equilibration measurements, in support of the long-contested existence of W30. Phillips and chang,ll on the other hand, were not able to observe this phase under similar experimental conditions. The purposes of this work, which is part of a continuing investigation of the W-Mo system, were to resolve the discrepancies between the AGO measured by gas equilibration and solid electrolyte galvanic cell techniques, to extend the latter measurements to lower temperatures, to redetermine the WO2.72 and WO2.90 decomposition temperatures, and to apply the more sensitive electromotive-force method to the question of the existence of W3O. I) EXPERIMENTAL PROCEDURE The measurement of ?G° of reaction by the use of calcia-stabilized zirconia solid electrolyte galvanic cells has been described previously.12 The method is based on the measurement of the difference in chemical potential of oxygen between an electrode containing the two oxides of interest and a reference electrode of known oxygen activity. Two different types of cell holders were used in this study. The first type of apparatus has been described earlier." It consisted of two solid electrodes separated by a disc of electrolyte. Both electrodes were exposed to the same stream of purified helium. With this design a gaseous transport of oxygen between the two electrodes is possible. The second type of apparatus, which has also been described earlier,14 effectively separated the two electrode atmospheres. It utilized a closed-end impervious, calcia-stabilized zirconia tube that was open to the atmosphere. The tube served as an electrolyte for the cell and provided a means for separating the anode compartment, which was held under a static vacuum, from an air reference cathode. The cells and reactions of interest are described in Table I. High-purity tungsten metal was obtained from the Fansteel Metallurgical Corp. and the Allied Chemical Corp. Table II contains an analysis of each material. WO3 was prepared by oxidizing the metal in air at approximately 600°C in high-purity recrystallized alumina boats and by the dehydration of reagent-grade tungstic acid in alundum boats. The two methods of preparing WO3 resulted in slightly different purities.

Jan 1, 1968