By E. S. Davenport

WHEN annealed carbon, or low-alloy, steels are suitably heated the ferrite (alpha iron solid solution) and the carbide, of which they are composed, react together to form a single solid solution of carbon (and other elements) in gamma iron (austenite). This reaction may begin only at a certain minimum temperature called the eutectoid temperature. The first ferrite and carbide thus to react together do so in definite proportions known as the eutectoid composition. With further heating the original constituent that is present in excess is dissolved in the austenite until exhausted. Whether the excess constituent be ferrite (hypoeutectoid steels) or carbide (hypereutectoid steels) the procedure is much the same, and upon slow cooling the homogeneous austenite expels the excess of either (proeutectoid ferrite or carbide) until the eutectoid composition is reached. Thus the reaction upon heating is strictly reversed upon cooling and accordingly an equilibrium diagram of this process may be constructed. Such an equilibrium diagram concerns itself only with the tempera¬tures involved and with the proportions and compositions of the phases developed under conditions that suffice to permit equilibrium. Specifically it has no concern for the type or mode of distribution of these constituents nor with any extra-equilibrium conditions such as undercooling, which is almost universally encountered in metals. Actually, however, of great importance is the sluggishness toward equilibration caused by the not inconsiderable time involved in diffusion. Thus instead of the theoretical transformation point AE, we find for a certain rate of heating or cooling the use of the designations Ar and Ac (transformation temperature found on cooling and upon heating). These figures obviously have no particular meaning except as measured and expressed for a definite heating or cooling rate, and represent the apparent temperature displacement caused by an inadequate time allowance. In this paper are presented the results of a study of the time required for' the transformation of austenite to ferrite and carbide at a variety of temperatures and also of the time required for the reaction austenite ?martensite at the temperatures at which this reaction occurs instead of

Jan 1, 1930

By George S. Rice

A problem of possible subsidence of the surface from mining operations, which might have had disastrous results, arose in 1913 at the Brier Hill mine, of the Penn Iron Mining Co., near Norway, Mich., now managed by Pickands, Mather & Co. for the Bethlehem Steel Co. A double track and sidings of the Chicago & North Western Railroad passed over part of the mine, and if subsidence had reached the surface it might have affected the stability of the tracks. The chief purpose of this paper is to record the facts disclosed by investigations of underground movement from 1913 to 1919, when the tracks were moved, and subsequently at intervals, as engineering data of value from mining carried on below the tracks in the steeply pitching lenses. A secondary purpose of this paper is to describe a novel method for determining the rate of speed of upward breaking above the mine excavations. This method was found effective and might be used elsewhere under similar conditions. The mine workings under consideration were developed from the Brier Hill shaft, which was circular, concrete-lined, 14 ft. in diameter and about 900 ft. deep. They extended about 800 ft. westward from the shaft, and nearly parallel to a corresponding length of the railroad tracks. The highest part of these workings was at a depth of 400 ft. below the tracks (Figs. 1 to 12). The mining company had the right to remove the ore, the railroad assuming that the surface would be supported. Finally, without legal controversy, an amicable adjustment was reached as to what should be done to lessen or obviate the hazard of subsidence. Method oF Mining Before the problem became acute, the mining company, to decrease the possibility of subsidence, had been mining the part of the orebody that lay under the tracks by a room-and-pillar system, back-filling with

Jan 1, 1934

By A. I. Blank, S. E. Maddigan

Many experimental and theoretical investigations have been made on the processes involved in annealing and recrystallization of metals. Most of these, however, have treated the time element as constant and heat-treatments used have been for relatively short times. Aside from the early work by Carpenter and Elam,' the few that have investigated the effect of time on the processes have usually done so for fairly short time periods. During recent years the growing interest in long-time creep properties of metals and alloys under stress has made increasingly important a better knowledge of the recrystallization during prolonged heating. The recrystallization temperature of 70-30 brass given by Clark and White" in 1932 was somewhat above 400°F. (204°C.) but under 500" (260°C.), whereas in our laboratory recrystallization has been observed in creep specimens at 204°C., the lowest temperature of Clark and White's range. Since the creep properties are quite different above and below the recrystallization temperature, erroneous conclusions can readily be drawn by the application of short-time recrystallization data to creep problems. It was thus considered of both practical and theoretical value to make long-time annealing studies near the minimum recrystallization temperature. In this way useful additions could be made to data on recrystallization temperatures and, since the reactions in this range are relatively slow, additional insight could be obtained into the factors involved in annealing. Several comprehensive reviews of recrystallization processes have been written,3-6 therefore only a brief review of the generally accepted facts will be given here. Though the effects of heat-treatment usually are expressed as related to observations with varying temperatures, it is logical to assume that the same order of occurrence will exist with time as a variable. Thus, we may postulate that with increasing time we mill observe the following

Jan 1, 1940

By S. E. Maddigan, A. I. Blank

Many experimental and theoretical investigations have been made on the processes involved in annealing and recrystallization of metals. Most of these, however, have treated the time element as constant and heat-treatments used have been for relatively short times. Aside from the early work by Carpenter and Elam,' the few that have investigated the effect of time on the processes have usually done so for fairly short time periods. During recent years the growing interest in long-time creep properties of metals and alloys under stress has made increasingly important a better knowledge of the recrystallization during prolonged heating. The recrystallization temperature of 70-30 brass given by Clark and White" in 1932 was somewhat above 400°F. (204°C.) but under 500" (260°C.), whereas in our laboratory recrystallization has been observed in creep specimens at 204°C., the lowest temperature of Clark and White's range. Since the creep properties are quite different above and below the recrystallization temperature, erroneous conclusions can readily be drawn by the application of short-time recrystallization data to creep problems. It was thus considered of both practical and theoretical value to make long-time annealing studies near the minimum recrystallization temperature. In this way useful additions could be made to data on recrystallization temperatures and, since the reactions in this range are relatively slow, additional insight could be obtained into the factors involved in annealing. Several comprehensive reviews of recrystallization processes have been written,3-6 therefore only a brief review of the generally accepted facts will be given here. Though the effects of heat-treatment usually are expressed as related to observations with varying temperatures, it is logical to assume that the same order of occurrence will exist with time as a variable. Thus, we may postulate that with increasing time we mill observe the following

Jan 1, 1940

By Robert L. Wilson

Computation of reserve tonnages, stripping ratios, and grade of ore has long been a revolting aspect of the young mining engineer's job. Weeks at the desk calculator may turn into months before a single job is completed. Then many additional hours are necessary to check the calculations. During the last decade, computing machines have been widely publicized as instruments which will accomplish fantastic feats. Tales of their magical qualities have overshadowed their most basic characteristics-that of being a labor-saving device. Prior to a discussion of the electronic calculator's use on a mining problem, it may be well to point out that these machines are neither magic nor will they replace the judgment of an experienced engineer. In short, the "mighty morons," as the computors are sometimes called, are excellent labor savers but must be used correctly. They are not a substitute for thinking.

Jan 6, 1961

Discussion of the paper of E. G. Woodruff, presented at the Butte meeting, August, 1913, and printed in Bulletin No. 78, June, 1913, pp. 1001 to 1010. F. A. LINFORTH, Butte, Mont.:-I have not had an opportunity of reading this paper thoroughly, but I would like to call attention to the possible use of the contours on fault planes. It is obvious that if the contours of fault surfaces call be determined, we will be able to determine the axes of the hollows in the fault surface. It seems probable, and there are examples to point to the accuracy of, the assumption, that the axes of these hollows may be the direction of movements on the faults, and if that is true it will aid materially in locating faulted ore bodies or the shoots of ore on the opposite sides of faults. A few such contour maps of faults have been attempted on some of the faults of the Butte district, and those faults which are believed to have the nearly normal movement exhibit for the axes of these hollows a line nearly up and down in the plane of the fault, but in those cases where the throw is believed to bee nearly horizontal we find that the axes of the hollows are almost horizontal lines. In other words, the movements on faults, I believe, would be more nearly indicated by the larger grooves in the fault surfaces than by the small slickensides and minor hollows that are seen, so that contour maps might be valuable in geology in that way. C. W. GOODALE, Butte, Mont.:-I received a letter from Mr. Woodruff asking me to take part in the discussion of his paper, but I have not had time to give the paper any study. I can certainly add my opinion to that of all the engineers here that the topographic maps of the government are of great aid to the engineer. When I visit a new district, the first thing I do is to see if that district has been covered by the U. S. Geological Survey avid if topographic map has been issued. And I find that some of the younger engineers frequently come into my office to see if I have such maps. I know in some cases the reports made out by engineers contain copies of these topographic maps, or clippings from them. I am sure that. the topographic maps furnished by the government are of very great value to our engineers.

Jan 11, 1913

By John D. Price

R. W. Campbell (Jones and Laughlin Steel Carp., Pittsburgh)—As usual John Price has presented an excellent paper. I know of no one who has devoted more time and conscientious thought to this subject than he has, and his efforts have produced scientific data and conclusions of real value. Results of similar studies made by the Jones and Laughlin Steel Corp. on the blending of Pennsylvania coals may be of interest. During 1935 the late F. W. Wagner and the present writer developed an empirical physical fuel value formula for evaluating the combined physical tests of metallurgical coke, see Table IV. In the development of the formula, the tumbler test, shatter test, screen test, and porosity of coke have been taken into consideration. Each of these tests brings out some physical property not expressed by the others, and in estimation of the importance of these tests as a medium for evaluating coke for the blast furnace, their worth has been graded as follows: It was thought that some additional penalty should be applied to cokes that do not show a uniform screen size, assuming that coke larger than 4 in. was not desirable and that this size was an indication of irregular size. Therefore the screen test factor is further corrected by applying a penalty of 1 pct for each 1 pct material greater than 4-in. size as shown by the screen test. The physical fitness of coke for blast furnace use depends upon four fundamental characteristics: l—gen-era1 strength, as indicated by the shatter test; 2— abradability, or the resistance of cell walls to reduction in size by attrition, as indicated by the tumbler test; 3—porosity; and 4—size and uniformity. Each of these characteristics is not of equal importance, but surely, in an attempt to determine an accurate physical value, the individual value of each should be taken into consideration. The formula is used as a yardstick, so to speak, in determining variations in the normal production of metallurgical coke and in making comparisons between normal coke and experimental blends with other coals. Table IV gives results of coking tests on raw and washed high volatile coals and these same coals with blends of coke breeze, anthracite coal, char and low volatile coals, all from Pennsylvania. The table also gives the source of the coals and coke breeze, as well as their proximate analyses. It will be noted that the washing of the raw high volatile coal increased the physical fuel value from 26.17 to 39.16, showing the effect of removing shale and slate which produces a detrimental fracturing and weakening of the coke. It is a well known fact that many Pennsylvania high volatile coals contain an excess of resinous material or binder which has a tendency to weaken the coke, owing to its high evolution of gases during carbonization. Tests were therefore made with coke breeze, an inert material, in an attempt to alleviate this condition. Blends of washed coal with 5 pct and 7.5 pct coke breeze collected from the coke plant quenching sump (82.9 pct through 1/8-in. screen) resulted in cokes with a physical fuel value of 20.75 and 16.73 respectively, lower than results obtained from 100 pct raw high volatile coal. It will be noted that the percentage of + 4-in. coke increased but that the tumbler test was very low. Undoubtedly better results could have been obtained if the coke breeze could have been crushed extremely fine. During World War II the government asked the coking industry to consider the use of anthracite coal as a substitute for high quality low volatile coal, which was extremely scarce at the time. The next series of tests was made with blends of raw and washed high volatile coals and 5, 10, and 15 pct Pennsylvania No. 5 buckwheat anthracite (100 pct through l/8-in. screen). It was necessary to use some raw high volatile coal in these blends because of insufficient washer capacity at the time. It will be noted that the physical fuel values

Jan 1, 1954

By R. C. Davis, R. F. Berry, G. W. White, B. T. O’Connell, L. A. Stacha

The formation density logging tool provides a radioactivity measurement that yields formation densities in situ. The relationship between bulk density and porosity is well understood. With knowledge of grain and fluid densities, porosity may be computed from the indicated formation bulk densities in shale-free formations. The porosities thus determined may be used with a resistivity log for water-saturation determinations. One technique utilizes a density vs resistivity plut. A plot of density vs Sonic-log transit time is used for porosity determinations in shaly sands. This method is particularly suited to wells drilled with oil-base or salt muds. In shale-free formations, comparisons of density values nnd neutron-log readings are used to identify lithologr and, thus, to select appropriate values of grain density for porosity computations. Through the use of Formation Density, Sonic and neutron logs, the interpretation problems caused by complex matrix lithologies are simplified. Other applications of the Formation Density log are found in the identification of minerals in evaporite deposits and in yield determinations of "oil shales". INTRODUCTION Widespread field application has demonstrated that the measurement of formation density is a useful and revealing technique for well logging. Responding to the bulk density variations of the formation, the Formation Density log affords valuable data on the porosity, lithology and fluid content of the formations. Although not without its own limitations, the Formation Density tool may provide effective interpretation under conditions that hamper or preclude the use of other porosity devices. When used in conjunction with other devices, such as the Sonic or neutron, complex matrix conditions may be better understood, defined and evaluated. A previous paper' described the valuable contribution of the Formation Density tool in the logging of empty, or gas-filled, holes. The purpose of the present paper is to describe applications of the device in liquid-filled holes. THE FORMATION DENSITY TOOL The Formation Density tool was devised to measure the bulk densities of formations in situ. Actually, the device responds to electron density, but in the overwhelming majority of cases of interest, the electron density is very closely proportional to the bulk density. In other cases appropriate corrections can be made if necessary. Comparisons of log-derived densities with true densities for the more common matrix minerals are shown in Table 1. The tool consists of a gamma-ray source and detector mounted in a skid which, during the logging operation, is in contact with the borehole wall (see Ref. 1 for schematic). Gamma rays are emitted by the source and diffused through the formation. The number of diffused gamma rays reaching the detector at a fixed spacing from the source are counted. An increase in counting rate by the detector indicates a decrease in bulk density in front of the skid. Conversely, a decreased counting rate signifies an increase in bulk density. A measurement of hole diameter, between the face of the skid and that of the eccentering arm, is recorded simultaneously with the measurement of diffused gamma rays. Since the tool is a wall-contact device, the size of the borehole has little influence, provided good contact is maintained with the wall of the hole. Only in extremely large or small boreholes does the actual diameter become significant. However, for most accurate measurements the borehole size should be taken into account. Fig. 1 presents the departure curves for the conversion of counting rate to bulk density for liquid-filled holes of various sizes. It is of utmost importance that the skid maintain good contact with the wall of the hole. If, due to roughness or caving, there is mud between the skid and the formation, the tool will include in its response the relatively low-density mud, and the apparent density reading will be too low. Normally, permeable beds do not cave appreciably, so that reliable readings are usually available for zones of interest. Nevertheless, the caliper reading over the zone of interest should be examined for any wall roughness. When mud cake exists between the skid and the formation, the Formation Density log sees it as part of the formation. When thick mud cakes exist, a correction is required. For best results in wells having thick mud cakes,

By P. Chiotti, G. R. Kilp

Thermal, metallographic, vapor pressure, and X-ray data were obtained to establish the phase diagram for the zinc-zzrconiz~m system. Five compounds corresponding to the stoi-chiometric formulas ZrZn, ZrZn,, ZrZn,, ZrZn,, and ZrZn14 were observed. All these compounds, with the exception of ZrZn2, which melts congruently at 1180°C under constrained zinc-vapor conditions, undergo pexitectic reactians. The temperature at which the zinc vapor pressure is I atm for a series of alloys was determined from vapor-pressure measurements. The data obtained are summarized in the construction of a I-atm-pressure phase diagram and a phase diagram corresponding to a pressure of less than 10 atm. THE purpose of this investigation was to establish the phase diagram for the zinc-zirconium system. Thermal, metallographic, vapor pressure, and X-ray data were employed in determining the phase regions. Partial investigations of this system have been conducted by Gebhardt1 and Carlson and Borders.' Carlson and Borders studied the high-zirconium region and established the existence of a eutectic at 69 wt pct Zr with a melting point of 1015°C. The terminal phases of the eutectic horizontal were shown to be an intermetallic compound ZrZn and a solid solution of ß zirconium containing 21 wt pct Zn. The ß solid solution decomposes into ZrZn and a zirconium at 750°C. The eutectoid composition is given as 15 wt pct Zn, and the solubility of zinc in a zirconium at temperatures below 750°C is indicated to be negligible. Gebhardt studied the zinc-rich region and observed a lowering of the melting point of zinc from 419.5" to 416°C and temperature horizontals at 545" and970°C. Some preliminary observations by Chiotti, Ratliff, and Kilp were reported by Hayes.2 pietrokowsky3 has reported the compound ZrZn2 to have a cubic MgCu2 structure with ao = 7.396A. MATERIALS AND EXPERIMENTAL PROCEDURES The metals employed in the preparation of alloys were Bunker Hill slab zinc or Baker analyzed reagent granulated zinc, both 99.99 pct pure and hafnium-free iodide-process crystal bar zirconium obtained from the Westinghouse Electric Corp. The zirconium contained 200 ppm Fe, 200 ppm Si, 100 ppm C, and minor amounts of other impurities. The zirconium was milled or machined into thin chips or shavings. These were cleaned with a nitric-hydrofluoric acid solution, rinsed with water, and acetone, and dried just prior to their use in alloy preparation. The granulated zinc was similarly cleaned using dilute nitric or hydrochloric acid. Weighed quantities of these materials, 20 to 30 g total, were mixed and pressed at 20,000 to 70,000 psi to give relatively dense compacts. During the early part of this investigation the pressed compacts were placed in MgO-15 wt pct MgF, crucibles which were then sealed inside of quartz ampules. The compacts were given various prolonged heat treatments prior to their use for thermal analyses, or vapor-pressure measurements. Because of expansion of the compacts and the relatively high zinc vapor pressure it was difficult to heat to the melting temperatures of the alloys without failure of the quartz ampules. Homogenization at temperatures below the melting temperature gave brittle, porous alloys unsuitable for metallographic examination. It was also difficult to prevent condensation and segregation of zinc on the colder parts of the quartz ampules during heating and cooling operations. These problems were eliminated to a great extent by the use of tantalum crucibles. Tantalum proved to be a satisfactory container with little or no reaction between the alloys and the tantalum. Small tantalum thermocouple wells were successfully welded in the bottom of these crucibles. Pressed compacts were sealed inside the tantalum crucibles by welding on preformed caps under an argon atmosphere. Heat treating and differential thermal analysis were combined into a single operation. The experimental sample assembly is shown in Fig. 1. This assembly was enclosed inside a stainless-steel tube heating chamber which could be evacuated and filled with an inert gas. The thermocouple leads were brought out of the heating chamber between two rubber gaskets used to provide a vacuum seal for the water-cooled head. Most of the compounds in this system undergo peritectic decomposition. After heating above the temperature of a particular peritectic horizontal the sample was cooled to just below the peritectic temperature and held at temperature for several hours. The sample was then reheated through the peritectic temperature and the size of the thermal arrest, if still present, compared with the one previously obtained. If the thermal arrest was not characteristic for the alloy composition being investigated its magnitude diminished and repeated cycling and annealing eventually eliminated it. The peritectic thermal arrests characteristic of a particular composition were established in this manner.

Jan 1, 1960

By AIME AIME

THE session on milling methods on Monday afternoon.* with G. H. Clevenger, chairman of the Mining Methods Committee presiding, was well attended. However, none of the authors of the papers presented were present except Messrs. Taggart and Ince. The paper on "Elements of Operations of the Pneu¬matic Table," by Messrs. Taggart and. Lechmere-Oertel, was presented by Professor Taggart as was the paper on "Calculations in Ore Dressing," by Luyken and Bierbrauer, due to the absence of the authors.

Jan 1, 1929

By John E. Miller

The Miller Number System is a well established method of measuring the relative abrasivity-friability of slurries, resulting in data that can be used in the selection of pump type and in forecasting wear-life of pumps and pipelines in slurry service. 1,2 Then after the pump type is selected, a Flow Analysis is determined by computer using pump design and operating parameters. This is used to determine pulsation control, suction requirements and stabilization, etc.

Jan 1, 1977

By Charles G. Maier

It has long been supposed that when crystalline materials are comminuted the energy used in the production of increasingly smaller grain sizes is not entirely dissipated as heat but that a certain portion is "stored" as a part of the internal energy of the material. This portion usually has been called the "surface energy" of the particles. The practical interest of the Bureau of Mines in this subject in connection with the energy requirements of crushing processes has led to the author's attempt to measure the "stored" energy in finely divided calcite by heat-of-solution methods1.t The experiments on calcite showed that "storage" of energy could not be proved for this material, because fine grinding caused a lack of chemical homogeneity evidenced by loss of carbon dioxide and subsequent adsorption of water on the surfaces of the calcite particles. When thermochemical correction was made for composition changes the corrected heat of solution was less for fine material than for coarse. Continuation of the experimental work into the problem of comparing work and heat in the deformation of metallic crystals, where the calorimetric difficulties were less, showed, however, that in the case of copper and aluminum a real discrepancy between work and heat could be shown. Similar results had previously been obtained by Farren and Taylor2 and Hort3 and more or less simultaneously with the author's work by Rosenhain and Stott4 and by Taylor and Quinney9 The results obtained by the different investigators were not satisfactorily consistent, but the experiments of Taylor and Quinney constitute by far the best figures obtained to date. The previous paper1 presented evidence to show that if energy is stored in the surfaces of crystals the densities of fine crystals should differ

Jan 1, 1936

By J. J. Bodmer

The four different modes, more or less practiced for subdividing slag (that is, producing slag sand), are the following: 1. Crushing the slag from the lump in Blake's crusher, by edge runners or other suitable means. 2. Blowing water, steam, cold or hot air, into the stream of viscous slag whilst it runs from the furnace. So treated, the slag takes

By J. J. Bodmer

THE four different modes, more or less practiced for subdividing slag (that is, producing slag sand), are the following : 1. Crushing the slag from the lump in Blake's crusher, by edge runners or other suitable means. 2. Blowing water, steam, cold or hot air, into the stream of viscous slag whilst it runs from the furnace. So treated, the slag takes

Jan 1, 1874

By R. W. Lai, I. Iwasaki

Some physical as well as chemical aspects of the methods of dispersion of various corn starches and their derivatives are investigated and their effects as depressants in anionic silica flotation of iron ores ascertained. The adsorption behavior of starches on hematite and quartz is strongly affected by their molecular sizes as inferred from viscosity measurements. The implication of this behavior on flotation and flocculation is discussed. Mechanical treatment of causticized starch solutions is shown to reduce the starch requirements in flotation appreciably. Starches and starch products have been used as depressants for iron oxides both in amine flotation of siliceous gangue and in soap flotation of activated silica from iron ores. Cooke and his associates1,2,3,4 extensively studied the effects of certain starches and their derivatives in the amine flotation of iron ores at near-neutral pH and found that although most starches were good flocculants for hematite and de- pressed that mineral more or less selectively1,3 they did not flocculate quartz suspensions. Further, that replacement of active groups in corn starch modified its behavior as a flocculant for hematite or quartz suspensions1 and as an iron oxide depressant. Schulz and cooke2 showed that many starches and their derivatives, except aminoethyl starch, were abstracted more effectively by Brazilian hematite than by quartz and that the adsorption of a starch product was strongly dependent on pH and on the presence of calcium ion. In soap flotation of calcium-activated quartz, certain starches and their products have been used to depress iron oxides.5'6 The behavior of these substances in flotation appears at times to be at variance with those previously reported and especially with results obtained in the Mines Experiment Station laboratories. This is attributed, at least in part, to differences in flotation procedure and flowsheets and in the method of preparing the depressant. Most of the investigators referred to above, solubilized the starch products by autoclaving at 120°C. Others have used acid,7 alkali8 or oxidizing agents.9 In view of the limited knowledge of the depressing action of starches and their derivatives in iron ore flotation, particularly in soap flotation of calcium-activated silica at high alkalinity, an extensive study

Jan 1, 1965

By A. C. Losekamp, J. B. Conway

Thermal-expansion data for, tungsten, rhenium, tantalum, .molybdenum, niobium, W-25 pct Re, Ta-10 pct W, ant1 Mo-50 pct Re are presented covering the range from room tempature to 2500°C. In these measureMents, made in a resistively heated tungsten tube furnace operating in a helium atmosphere, data for rod and sheet specimens were found to be identical; in addition, arc-cast and sintered tungsten were found to yield essentially identical results. Optical rneasurenlents of thermal expansion .made in any atmosphere other- than vacuum are subject to a refraction error which can be quite substantial. Specimens tested in helium appear shorter than when tested in racuum and hence a special correction factor must be applied to the helium data in order to obtain accurate results. WHILE it is true that linear thermal-expansion data for many of the refractory metals have been measured to very high temperatures, it is also true that except in a few instances the data from various investigators are not in good agreement. This is particularly evident in the case of tantalum and niobium although some tungsten data have been reported which differ by as much as 40 pct from the data of other investigators. Due to the sensitivity of both tantalum and niobium with respect to impurity absorption during exposure to high temperatures, it is probable that this single factor accounts for the majority of the discrepancies in the thermal-expansion data for these metals. However, this same factor can probably not be employed to explain the existing differences in the tungsten data. In all probability, these are due to errors in the measurement technique, to material composition variations, or to changes which take place in the material during the heating process (e.g., additional densifica-tion resulting from heating a sintered specimen above the original sintering temperature). In view of the discrepancies which exist in the linear expansion data reported for many of the refractory metals, the current study was initiated in an attempt to resolve such differences. Also, no high-temperature linear thermal-expansion data were found to be available for several refractory metals. Providing such data was another objective of the current investigation. MATERIALS In this study test specimens were employed in either rod or sheet form and in several instances both arc-cast and sintered material were employed. Material compositions are presented in Table I. Helium gas was fed to the furnace at a rate of about 0.5 SCFH and no special purification procedures were employed. However, the helium contained less than 50

Jan 1, 1967

By A. W. Furbank

IN reviewing the aerial cameras produced in different countries, it becomes apparent that in nearly all of them an attempt has been made to secure the greatest possible angle of view. This angle, of course, is determined by the objective. The objectives most commonly in use in aerial cameras have a maximum angle of 65º. The objective developed for this new Zeiss camera combines freedom from distortion and brilliant definition, with an angle of 95º. Aerial mapping, it is claimed, has been placed on a different economic basis, and new possibilities presented, particularly in connection with automatic stereoscopic plotting instruments, to which some short references are made. One way of enlarging the angle of view is to couple several instruments with their axes convergent, thereby producing a multilens camera. Typical of cameras of this sort in the United States is the Bagley four-lens camera, which later was developed into the five-lens camera (T3-A) of the U. S. Air Corps. More recently, in order to get away from the unfavorable Maltese cross image field of the five-lens camera, and to obtain a more practical form, two five-lens cameras were combined. By using them in tandem and rotating them by 45º relatively to each other, a ten-lens camera was produced, covering an octagonal ground area, with a total angle of view of 140º. Similar designs have been evolved in other countries. In all of them, however, a number of difficulties have arisen, quite apart from their large weight and high cost. Because of their complex mechanism, numerous shutters and magazines, and the high precision with which these parts must be interadjusted and synchronized, these cameras are far from dependable Moreover, a multilens camera by itself does not yet constitute a complete outfit for producing pictures suitable for photogrammetric survey. Because all the component pictures, except the central one, are obliques, it is always necessary to employ rectifying apparatus which transforms the marginal views to the perspective of the central one. In multilens cameras with many individual magazines, it is not convenient to

Jan 1, 1938

By G. G. Gunther, C. L. Boeke

(Any discussion resulting from presentation at the Los Angeles Extractive Metallurgy Division Meeting will appear in the November 1953 issue.) I. M. Symonds (Cia Minera de Penoles, Monterrey, N. L., Mexico)—This is a most interesting paper describing zinc deleading operations. Mr. Gunther was kind enough to show me his operation last fall. Outside of the excellent results, I was most impressed by the ease of control. I had expected a difficult operation requiring careful control and supervision, but found one requiring little attention. The only disappointing fact of the separation is the poor copper recovery in the concentrate of the deleading float. The final zinc concentrate still has about 3 pct chalcopyrite (assuming the copper is chalcopy-rite) which adversely affects the zinc grade. If the copper mineral is free, the poor recovery is probably due to the high cyanide concentration. Fortunately, about 75 pct of the copper is recovered before the pulp goes to the zinc circuit. Mr. Gunther's remarks about proper cyanide to zinc sulphate ratios cannot be overemphasized. Although our experience has been mostly confined to the conventional Pb-Zn separation, we have found these ratios most important, and more important in the mill than in the laboratory. The laboratory appears to give optimum results over a wider range of reagent control than the mill, especially in regard to the effect of cyanide. In the mill in handling relatively high grade ores, we usually find that ratios of cyanide to zinc sulphate of 1 to 10 or 20 or higher work best. Where there is a substantial amount of chalcopyrite present, it has been noted that cyanide in the range of 0.02 to 0.10 lb per ton of ore is often beneficial in zinc rejection and possibly in copper recovery in the lead concentrate, while larger amounts, say 0.20 to 0.25 lb per ton, will float more zinc and cause a serious rejection of chalcopyrite. On an ore with 15 to 20 pct Zn content, we have had to use 0.8 to 1.2 lb of zinc sulphate per ton of ore with the above cyanide to obtain optimum results. Sometime ago we made a laboratory study following Parral and Santa Barbara practice on an ore which never had a very satisfactory rejection of zinc in the lead concentrate. The results were not encouraging and a mill test was not run. Since then the study has been reopened using fresh zinc concentrate from the mill in the laboratory instead of one made in the laboratory. A reasonably clean lead float from the zinc concentrate was obtained. It has been checked several times and each time the zinc concentrate made in the mill responds and the one made in the laboratory does not. Although undoubtedly some reasonable explanations can be given, it is presented here only

Jan 1, 1953

By A. W. Furbank

In reviewing the aerial cameras produced in different countries, it becomes apparent that in nearly all of them an attempt has been made to secure the greatest possible angle of view. This angle, of course, is determined by the objective. The objectives most commonly in use in aerial cameras have a maximum angle of 65". The objective developed for this new Zeiss camera combines freedom from distortion and brilliant definition, with an angle of 95". Aerial mapping, it is claimed, has been placed on a different economic basis, and new possibilities presented, particularly in connection with automatic stereoscopic plotting instruments, to which some short references are made. One way of enlarging the angle of view is to couple several instruments with their axes convergent, thereby producing a multilens camera. Typical of cameras of this sort in the United States is the Bagley four-lens camera, which later was developed into the five-lens camera (T3-A) of the U. S. Air Corps. More recently, in order to get away from the unfavorable Maltese cross image field of the five-lens camera, and to obtain a more practical form, two five-lens cameras were combined. By using them in tandem and rotating them by 45" relatively to each other, a ten-lens camera was produced, covering an octagonal ground area, with a total angle of view of 140". Similar designs have been evolved in other countries. In all of them, however, a number of difficulties have arisen, quite apart from their large weight and high cost. Because of their complex mechanism, numerous shutters and magazines, and the high precision with which these parts must be interadjusted and synchronized, these cameras are far from dependable. Moreover, a multilens camera by itself does not yet constitute a complete outfit for producing pictures suitable for photogrammetric survey. Because all the component pictures, except the central one, are obliques, it is always necessary to employ rectifying apparatus which transforms the marginal views to the perspective of the central one. In multilens cameras with many individual magazines, it is not convenient to

Jan 1, 1941

By A. W. Furbank

In reviewing the aerial cameras produced in different countries, it becomes apparent that in nearly all of them an attempt has been made to secure the greatest possible angle of view. This angle, of course, is determined by the objective. The objectives most commonly in use in aerial cameras have a maximum angle of 65". The objective developed for this new Zeiss camera combines freedom from distortion and brilliant definition, with an angle of 95". Aerial mapping, it is claimed, has been placed on a different economic basis, and new possibilities presented, particularly in connection with automatic stereoscopic plotting instruments, to which some short references are made. One way of enlarging the angle of view is to couple several instruments with their axes convergent, thereby producing a multilens camera. Typical of cameras of this sort in the United States is the Bagley four-lens camera, which later was developed into the five-lens camera (T3-A) of the U. S. Air Corps. More recently, in order to get away from the unfavorable Maltese cross image field of the five-lens camera, and to obtain a more practical form, two five-lens cameras were combined. By using them in tandem and rotating them by 45" relatively to each other, a ten-lens camera was produced, covering an octagonal ground area, with a total angle of view of 140". Similar designs have been evolved in other countries. In all of them, however, a number of difficulties have arisen, quite apart from their large weight and high cost. Because of their complex mechanism, numerous shutters and magazines, and the high precision with which these parts must be interadjusted and synchronized, these cameras are far from dependable. Moreover, a multilens camera by itself does not yet constitute a complete outfit for producing pictures suitable for photogrammetric survey. Because all the component pictures, except the central one, are obliques, it is always necessary to employ rectifying apparatus which transforms the marginal views to the perspective of the central one. In multilens cameras with many individual magazines, it is not convenient to

Jan 1, 1941