By R. P. Abendroth

This study is concerned with the kinetics of selective oxidation of chromium in a commercial Fe-Cr-Ni alloy. Selective oxidation of chromium in this alloy, by use of a low oxygen-potential atmosphere, leads to the formation of a compact, protective layer of Cr2O3. This layer serves to protect this alloy from gross scaling when it is subsequently exposed to severe oxidizing conditions at high temperature. The interaction of low oxygen-potential atmospheres close to equilibrium with Fe-Cr and Ni-Cr alloys has been studied by others."' These studies werk concerned with the surface-structure variations under slightly oxidizing conditions. NO detailed study was made of the oxide scale formation kinetics, however. The alloy samples were cut from 0.012-in.-thick sheet, with an apparent surface area of 7.1 sq cm. These sheet samples were abraded through 4/0 metallographic paper, and washed in alcohol and acetone. The analysis of the sheet alloy is (in weight percent): 42 pct Ni, 5.5 pct Cr, 0.09 pct C, 0.18 pct Al, 0.36 pct Si, 0.26 pct Mn, balance Fe. The weight gain vs time data were obtained with a 2-g capacity fused-silica spring—cathetometer system. The spring deflection was optically magnified ten times before being read by the cathetometer. A sensitivity of about 0.01 mg was attainable. The spring was enclosed in a water jacket maintained at 60°C to minimize the effect of temperature changes. The sample was suspended from the spring with a fused-silica hangdown and was positioned in the thermal center of a mullite furnace tube. Sample temperature was read with the aid of a thermocouple placed outside the mullite tube and an inside vs outside temperature calibration. Temperature change during the course of a run was ±0.25°C, with a temperature gradient of less than l.O°C over the length of the sample. Total temperature uncertainty was no more than ±3.0°C. Alignment difficulties between the hangdown and radiation shields in the furnace tube required that the sample be positioned in the furnace when cold, and heated with the furnace until the temperature stabilized at the desired point. This required 5 to 6 hr, and was carried out in Matheson ultrahigh-purity hydrogen. Oxidation was started, after evacuation, by introducing a hydrogen-water vapor mixture, obtained by saturating hydrogen with water vapor at 31.00o ± 0.02oC. Oxidation was continued for 90 min. Gas flow was 300 ml per min during heat up and oxidation. Since only several milligrams of oxide are formed on each sample, chemical analysis of the oxide is difficult. A representative analysis is: 80 pct Cr2O3, 5 pct Fe2O3, 3 pct Al2O3, 4 pct MnO, 7 pct SiO2, 1 pct or less NiO. X-ray diffraction analysis of the oxide as formed on the alloy gives rhombohedra1 Cr2O3, and barely distinguishable amounts of a cubic spinel phase, and possibly AlZOs and SO2. The identification of these latter two compounds is by no means certain. The spinel phase could be based on iron or manganese as these elements are present in significant amounts in the oxide. The results of the kinetic studies using 31°C dew-point hydrogen-water vapor mixtures were found to conform to a parabolic rate law. In many cases the parabolic plot consisted of two intersecting straight lines, defining an early and a late rate for a particular run, and in the other cases the parabolic plot consisted of one straight line for the entire run. The slopes of the various straight lines were determined by the method of least squares. Reproducibility of the data was good enough for multiple runs at the same temperature such that the value given for the rate constant is the average for two or more closely similar values, rather than widely varying values of the rate, where more than one determination is indicated in Table I. The exhibition of only one or of two rate constants during a run can happen at the same temperature. Thus, Table I shows that at 11'74°C a single rate constant was obtained from one sample, while other samples oxidized at the same temperature gave an early and a late rate constant. It should be noted that the single rate constant corresponds very closely with the early rate constant. This is also true at 1153°C. The time at which the late rate started to appear was variable, usually occurring 20 to 40 min after oxidation had started.

Jan 1, 1964

By B. C. Allen

Surface free energy and surface self-diffusion of solid molybdenum were studied in the temperature range 1600" to 2400°C using pressure-sintered bi-crystals. Comparison of groove angles formed in various surfaces perpendicular to the grain boundary indicate a maximum of 1 pct variation in surface free energy with crystallographic mientation. This anisotropy tends to decrease with increasing temperature. The surface diffusion of the bicrystals is equivalent to that of sheet with a mild (100) Preferred orientation. Anomalously low values found for bi-crystals with surface orientations of (OOl), (012), and (011) are rationalized in terms of anisotropy in surface free energy. THE effect of crystallographic orientation on surface free energy1,' and surface self-diffusion3,4 has been primarily studied in fcc metals. The object of this work was to study the effect of orientation on surface diffusion and surface free energy of bcc molybdenum using pressure-sintered bicrystals. EXPERIMENTAL WORK Materials and Crystal Preparation. Arc-melted molybdenum rod was obtained commercially and electron beam zone refined at 50 cm per hr at 10- 5 torr to form single crystals about 8 cm long and 0.65 cm diam. Three crystals were prepared with axial orientations about 1 deg from [001.], [011], and. [111]. To reduce the carbon content, the crystals were annealed 2 hr in 1.4 atm flowing wet hydrogen at 2050°C. Then the oxygen content was reduced by annealing for 2 hr in -30°C dewpoint hydrogen at 2020°C. The resulting impurity analysis is given in Table I. Bicrystal Preparation. The single crystal rods were cut into transverse slices with a thin silicon carbide abrasive wheel to produce specimens about 0.6 cm long. They were mounted in epoxy and surrounded by stainless steel washers. Cutting in half was done longitudinally at various angles to known crystallographic planes containing the cylinder axis according to Fig. 1. To reduce surface deformation resulting from the cutoff wheel and thus reduce parasitic grain boundary formation on subsequent annealing, about 0.003 cm was manually ground off each cut surface with 600 grit paper. Care was taken to keep the surface flat. After removal from the mounts, one half was generally ro-tated 180 deg with respect to the other to give a po- tential symmetrical tilt grain boundary between the two halves. In the other cases when low misorienta-tion angles were desired, the crystals were not rotated. On the basis of symmetry, sufficient bicrystals were prepared to cover the entire range of misorientations for symmetrical tilt boundaries. The misorientations, +, ranged from 0 to 45, 0 to 90, and 0 to 60 deg for [001], [011], and [111] bicrystals, respectively. One [Ill] twist bicrystal was prepared from 2 single crystal discs rotated 17 deg relative to each other. Each specimen consisted of two pieces which were placed in a cylindrical tantalum can. Sharp edges were rounded and the fit was made as snug as possible to reduce subsequent deformation during bonding. The assembly and crystals generally were vicuum outgassed at 900" or 1700°C and then electron beam welded in the can at l x 10-4 torr. After being leak checked, the samples were placed in an autoclave and hydrostatically gas-pressure bonded5 in four batches under helium at 10,000 to 18,000 psi at 1650°C for 3 hr. Satisfactory bonds were obtained in many cases, and most of the crystals bonded after two exposures. The results did not appear to be affected by the various pressures used, preannealing conditions, crystal orientation, or time-pressure-temperature route taken to the final bonding condition. After bonding, the tantalum cans were selectively removed in cold concentrated HF. Measurements indicated overall deformation was under 1 pct. The bicrystals were metallographically ground and polished flat and perpendicular to the axis. Examination showed the boundaries were straight and almost free of parasitic grains caused by extraneous local deformation. Annealing. In preparation for thermal grooving, the bicrystals were cleaned and annealed by outgassing at 10-5 torr at 1900°C and heating at 2300°C under 1 atm 99.996 Ar for 0.5 hr. The crystals were held in a closed 4-deck box made of molybdenum sheet, and were heated in a Ta-1OW resistance furnace. The ar-

Jan 1, 1970

By R. E. Holmes, T. W. Leland

The solution to the unsteady-state mass- and heat-transfer equations describing the adsorption of a dilute component from a gas stream flowing through a packed bed is readily applicable to the design of hydrocarbon recovery units. The solution to these equations depends on the assumption of a linear equilibrium equation to relate concentrations on the surface to concentrations in the gas. This assumption is shown to be justifiable for components which are very dilute in the gas stream. This approach permits the prediction of the effects of bed shape and size, cycle time, and gas mass velocity on the recovery of each component. It also allows the time and gas flow rate needed for regeneration to be determined. The equations involve a constant for each component and another constant characterized by the type of adsorbent. These constants must be evaluated from operating data. Values of these constants determined for silica gel are presented. This paper points out the type of experitrrental data needed for a thorough design of hydrocarbon adsorption units. INTRODUCTION The growing importance of adsorption processes to recover hydrocarbons from natural-gas streams has created an urgent need for better methods to design and predict the performance of these processes. Since the original use of solid adsorbents in natural-gas processing was for dehydration, most of the current design methods for hydrocarbon recovery re extensions of those developed earlier for dehydration. These methods are based on an adsorptivity or bed loading factor defined as the amount of a particular component adsorbed per unit weight or per unit volume of the packed bed. The recovery of a given component is then expressed as an empirical function of its adsorptivity on a given adsorbent. In spite of the simplicity and initial utility of these methods, they are not completely satisfactory in that they do not predict the effect of the dimensions of the bed in relation to flow rate and cycle time, and do not predict the distribution of various components along the length of the bed. It is possible, however, to make a considerable improvement in the design of these processes by applying the basic equations of mass and heat transfer applicable to gases containing small concentrations of adsorbing components flowing through granular beds. These equations have been developed and solved by Anzelius,' Furnas,% nd Hougen and Marshall." where G = mass velocity of the inert constituents (assumed to be methane), lb/hr-sq ft, y = weight of an adsorbing component in the gas per unit weight of inert, lb of a given constituent per lb of methane, x = bed length, ft, p, = packed bed density, lb/cu ft, P, = gas density, Ib/cu ft, f = void fraction in the bed, t = time, hours, and w = weight of a given component adsorbed per unit weight of adsorbate free solid, Ib/lb pure adsorbent. The term on the left side of Eq. 1 represents the flow rate per unit bed volume of a component entering less the flow rate per unit bed volume of that component leaving the differential bed length. The terms on the right side represent, respectively, the accumulation rates per unit bed volume on the solid and in the gas phase within the differential bed section. The last term is negligible for this application since pgfv is quite small in comparison with p, and G. The partial differential is determined by the mass-transfer rate between gas and solid in the differential section.

By P. Linehan, J. F. Wiss

Vibration and air blast noise from blasting were evaluated during a research program sponsored by the US Bureau of Mines. Blast variables were studied wing small scale model (SCM) tests to evaluate specific variables as well as interactive effects, followed by experiments with production blasts at the surface coal mines. Experimental data showed that the primary variables affecting the ground vibration amplitude are the charge weight per delay and the length of delay interval. Blast variables having a significant effect on the overpressure amplitude include the charge weight per delay, the length of delay, burden and spacing, stemming amount and type, direction of initiation, charge depth, and amount of detonating cord and cover.

Jan 1, 1983

By F. Lynwood Garrison

As the specific gravity of low-carbon steel seems to be attracting considerable attention as a means of détermining the quality and value of the metal, I give here a few of the results of a long series of experiments recently made by me. The object of the experiments not requiring more than approximate correctness in the third place of decimals, the extreme precautions to obtain accuracy which are sometimes used in determining specific gravity were not observed. But each piece of metal was carefully cleaned to remove scale, rust, dirt, etc., thoroughly dried, and then weighed in air, all weighings being carefully repeated. The balance used was one of Troemner's finest, and sensitive to one-tenth of a milligram. Before weighing in distilled water, care was taken to remove, as far as possible, the air enclosed in the pores of the metal. The pieces of metal were suspended by means of fine silk thread, a correction of course being made for the weight of the silk. Care was taken that the water in which they were weighed should he always at the same level, and, as far as possible, at the same temperature.

Jan 1, 1887

By L. S. Darken

IT has been known for sometime that in an ionic lattice, such as that of Ag2S or FeO, the migration velocity of the anion may differ markedly from that of the cation, the cation being usually the more mobile. It has been shown, for example, that during the formation of silver sulfide tarnish on silver, the tarnish layer grows principally by the motion of silver cations through an essentially stationary silver sulfide lattice. Similarly, the growth of wüstite scale on iron proceeds principally by motion of iron ions, this being accomplished with the aid of vacant iron lattice sites into which the iron may readily move. Likewise investigations of solid solutions of various salts show that there is usually considerable difference in the mobility of the different cations. Measurements of the mobility of various metals in liquid mercury indicate that the various metals move at different rates relative to the mercury. In view of the foregoing it seems reasonable to suppose that when any single phase solution is acted upon by a field, the atoms of different elements respond in different ways; in particular, that the force arising from a particular concentration gradient in a binary alloy would cause the atoms of one component to move with a drift velocity which is in general different from that of the atoms of the other component. The recent experiments of Smigelskas and Kirkendall1 support this viewpoint, since they found, in essence, that during diffusion in alpha brass zinc moves appreciably faster than copper. This was evidenced by the relative motion of inert molybdenum wires. Such a phenomenon is incompatible with the place interchange theory of diffusion proposed by several authors, most recently by Birchenall and Mehl.2 This theory has, however, also been questioned3.4 for other reasons, principally because of the high energy required for direct atomic interchange. The rather large difference between self-diffusivity, as determined by tracer technique, and mutual diffusivity, as determined with the aid of another element at low concentration, might also be interpreted as favoring the above idea; however, Birchenall and Mehl have pointed out that there is another possible interpretation of this difference; this is discussed later. A rather interesting and pertinent observation was made by Schwartz,5 who noticed that tungsten lamp filaments, heated by direct current, commonly fail by necking down in the region at the temperature gradient near the positive end, with a concomitant swelling at the corresponding position near the negative end. He introduces considerable auxiliary evidence to show that this phenomenon is occasioned by the motion of tungsten cations which migrate in the high temperature region from the positive end toward the negative end. The mechanism of this migration is not clearly understood. If, however, this experimental evidence be accepted, we are forced to conclude that alloying elements in the tungsten may migrate by the same or a similar mechanism, whatever it may be, at a greater or lesser rate, thus giving rise

Jan 1, 1948

By George W. Sargent

For the experiments here described a rod was used, 0.75 in. in diameter, and rolled from one ingot. Analyses of the ingot and rod showed them to have the following composition respectively: C. Mu. Si. P. 8. Percent. Percent. Percent. Percent. Percent. Ingot,. .. 1.150 0.328 0.223 0.020 0.016 Rod,. .. 1.033 0.327 0.223 0.020 0.016 Pieces 4 in. long were heated to various temperatures in a closed porcelain tube, within a gas furnace, and allowed to cool with the same; they were then turned, threaded, and subjected to physical tests in a Riehlé testing-machine. The elastic limit was determined by the drop of the beam. The elongation was measured in two inches. From the threaded ends of the testrpieces, disks were cut, and prepared by combined polishing and etching, using parchment stretched over a wooden block and moistened with a 2-per cent. solution of ammonium nitrate. The structure, as thus developed, and the fractures, were magnified and photographed. A cooling-curve was constructed, and the critical point was located at 675º-680º C. A thermo-electric pyrometer was used to make the measurements of temperature. The micro-constituents of steel have been so frequently and thoroughly described by others that I need only say here that the theoretical micro-structural constituents of this steel were : pearlite, 95 ; ferrite, 0 ; cementite, 5 per cent. The quenched metal would be expected to consist almost entirely of martensite—provided, however, the quenching be done at or near the proper temperature. Rapid quenching from a high temperature would give rise to austenite.

Jan 1, 1902

By David Baker

IN a paper presented to the American Institute of Mining Engineers, September, 1904, entitled ? Improvements in the Mechanical Charging of the Modern Blast-Furnace,"' I showed the great fault of mechanical charging-devices to be that the materials charged by the dumping of the skip were separated, the coarse materials having high velocity, and the fine, low-thus giving paths of low resistance through the stock in the furnace, which resulted in unequal distribution of the furnace gases, unequal reduction, slips, scaffolds, irregular cutting of the. inwall, " off " iron, and increased fuel-consumption. I showed how this could be prevented by rotary distribution, through which the irregular distribution in one layer charged is compensated by charging the subsequent layers from successively varied positions of the charger, and becomes practically eliminated when the angle between two successive positions is a little more or less than an even fraction of a full circle. Of all the devices then on the market, the nearest approach to the ideal arrangement was found in the Brown distributor, a full description of which was given. The one defect pointed out, however, was the difficulty of maintaining so much mechanism on the top of a blast-furnace. Since the presentation of that paper, I have designed a very simple form of rotary distributor, which may be applied to any form of double-bell charger, retaining the perfect gas-seal, which is so admirably obtained by that construction. In seeking protection for this invention, I found no similar distributor on record in the patent offices of the various countries where application was made; but an application show-

Jul 1, 1906

A mine in the mountains of southeastern British Columbia is fast earning a reputation as the safest metal mining operation of all time. Already officially proclaimed as the safest mine in Canada, the H.B. mine of The Consolidated Mining and Smelting Co. of Canada (Cominco) continues to advance its safety performance far in the lead of average accident frequencies in mines across the country. Official recognition came its way again this spring when the Cominco mine was awarded the John T. Ryan trophy for the fourth time in the last five years. This award is emblematic of top national safety performance of a metal mining operation. The H.B. mine is its only four-time winner. The Ryan award is based on a frequency of accidents involving lost time of more than six days. In each of the years that the H.B. has won the award-1958, 1959, 1961 and 1962-its frequency was zero, with no accidents involving a time loss of more. than six days

Jan 12, 1963

By Dale A. Vaughan, Oliver M. Stewart, Charles M. Schwartz

A. U. Seybolt (General Electric Research Laboratory)—The authors should be commended for adding some important information to our knowledge of the solubility of interstitial elements in metals. It is becoming increasingly evident that the effect of even traces of such elements have very far-reaching effects upon the mechanical properties of the body centered cubic metals. Those who have worked in this area know that the accurate determination of the small solid solubility limits in systems of the type reported by the authors is a quite difficult task, and it is therefore not surprising that frequently the results of different workers are not in agreement. It is instructive, and usually helpful, to plot the solubility results on log weight or atomic percent -1/T coordinates to find out if a straight line is obtained. A straight line is expected because in systems displaying solubilities of the order of 1 to 3 at. pet or less, Henry's law is usually obeyed—or at least well enough obeyed so that the deviation from linearity is not very appreciable. If Henry's law is obeyed, one canthen use the Van't Hoff Equation in the form In N = ?H/RT + C, where N is mole fraction, at. pet, or wt pet for small values, and AH is the partial molal heat of solution of the solute. R and T have the usual significance, and C is an integration constant. If one plots the reported nitrogen solubility values as indicated above, the three points fall reasonably well on a straight line. The oxygen values for the two upper temperatures fall very closely to the nitrogen values as shown in the authors' Fig. 15. However, the value at 500°C departs widely from the straight line established by the data at 1500" and 1000°C. It is, of course, true that one cannot place too much emphasis on the significance of a line established by only three points, but in the absence of reasons for anticipating deviations, data exhibiting wide departures from linearity should at least be examined closely. Fig. 16 shows the log at. pct -1/T plots for the authors Ta-O and Ta-Ndata including a solid circle point at 500°C and 1.8 at. pet for Ta-O, which is simply extrapolated from the two higher temperature points. In addition, the data of R. P. Elliott9 for Nb-O are shown. These points were picked off his curve and are not very exact, but as can be seen they line up well on a straight line. It is interesting, and probably significant, that the slope of Elliott's results is not far from those of Vaughn, et al. This is probably to be expected because one would anticipate that the partial molal heats of solution of oxyten in these two very similar metals should be not too far apart. AH for Ta-O is about -1900 cal per mol, while for Nb-O it is near -2300 cal per mol. Hence, this lends some support to the thesis that the point at 500°C for Ta-O is much too high. The data of Gebhardt and Preisedanz10 are also plotted, and it is seen that their data while lying on a linear plot, have an appreciably steeper slope. The possible reasons for this will not be discussed here except to point out that their pressure-composition data show anomalies which suggest that they may have been dealing with a different equilibrium from that being discussed. There is another consideration which would also suggest that the solubility at 500°C is lower than shown. The solubility values were obtained by the classic method of first establishing a lattice parameter-composition curve. This the authors did, and there is probably little doubt that it is quite accurate. Such a plot is generally almost error-free because it has a self-correcting feature in that any deviation from linearity makes a data point immediately suspect, and subject to confirmation. Unfortunately, this is not true with respect to the actual solubility values. These are obtained ordinarily by taking an alloy containing more solute than is soluble at some temperature and then thermally

Jan 1, 1962

By C. A. Stickels, C. M. Yen

Secondary recrystallization was investigated in vacuum-melted electrolytic iron to which 70 pm N was vacuum-meltedadded. The secondary texture is "near {554}<225>" for material cold-rolled 75 to 90 pct, the sharpness of the texture increasing with increased rolling reduction and with decreased annealing temperature. At reductions of 95 and 97.5 pct the secondary texture is &apos;"near {322)(296)". Both secondary orientations also exist as major components of the primary re-crystallization texture. Development of a strong "near {554) (225)" secondary texture appears to depend on the evolution of the Primary texture to a transition texture depleted in orientations near the secondary orientation before the onset of secondary growth. A variety of qualitative experinzents have been used to show that nitrogen is important in limiling primary grain growth. The presence of nitrogen does not seem essential for the establishment of a transition texture, but a loss of nitrogen during annealing may facilitate growth of grains in the secondary orientation. Secondary grains we shown to form initially at the specimen surface. This is not thought to indicate that surface energies are important in the growth process. It is proposed that the quasi-two-dimensional character of surface grains permits discontinuous growth parallel to the surface before secondary growth of interior grains is possible. An earlier study of recrystallization textures in 90 pct cold-rolled electrolytic iron showed that secondary recrystallization occurred after annealing for several days at 700C1 This type of secondary recrystallization, which had not been reported previously, results in the formation of a strong texture, best described by the indices "near {554}(225)". The purpose of the present work was to investigate the effect of various processing variables on secondary recrystallization in this material and determine the mechanism of secondary grain growth. LITERATURE REVIEW An understanding of the mechanism of a secondary recrystallization process depends on knowing: 1) how grains in the secondary orientation come to be in the primary recrystallization texture; 2) why normal grain growth does not occur; and 3) what factors determine the strength of the secondary texture. For secondary growth of grains of a particular orientation, a certain minimum fraction of the grains must be in that orientation after primary recrystallization. This requirement is apparently satisfied "naturally" in certain systems, i.e., when the primary texture obtained by rolling and recrystallizing material initially randomly oriented contains a sufficient fraction of primaries in the secondary orientation. However, in other cases, e.g., {110}<001> and {100}<001> secondary growth in silicon iron,2 it is necessary to enhance the fraction of primary grains in the secondary orientation by rolling and recrystallizing textured material. In the present case, the "near {554}<225>" orientation is contained within the spread of orientations found in the primary recrystallization texture of iron or bbc iron-base alloys. In systems where the main driving force for secondary growth is the reduction in total grain boundary energy, secondary growth is observed only when normal grain growth is minimized. Four ways in which normal grain growth can be limited are: 1) Limitation by a strong primary texture. When a very strong primary texture consisting of a single component or twin-related components develop, most primary grains are separated from one another by relatively immobile small-angle grain boundaries. The classic instance of this is secondary growth into the primary cube texture in some fcc metals. 2) Limitation by precipitates. Precipitates present in the proper volume fraction with a suitable dispersion will limit primary grain growth. The role of MnS inclusions in impeding normal grain growth in Si-Fe is well-documented.5 3) Limitation by sheet thickness. Normal grain growth slows drastically when the mean grain diameter is of the same order as the sheet thickness. This effect has been used to obtain secondary recrystallization in thin sheets of high-purity silicon iron.&apos; 4) Limitation by solute impurities. It is well-established that certain impurity elements in solution can have a large effect on grain boundary mobility.&apos; However, there does not seem to be any secondary recrystallization process in which primary grain size stabilization has been shown to be due to the drag exerted on grain boundaries by dissolved impurities. In certain systems, e.g., secondary recrystallization in silver,&apos; the means by which normal grain growth is limited has not been identified, and solute-impurity limitation might be suspected. In order to understand the factors which determine secondary texture strength in three-dimensional growth, it is necessary to examine in more detail the current picture of general secondary recrystallization processes. Following Cahn,9 it is assumed that the primary grains have a range of sizes and that secondary growth of one of the large grains in this distribution is possible when it exceeds a critical size with respect to its neighboring grains. The critical size depends on the ratio ?S/?p, where ?s is some sort of average grain boundary energy between the potential secondary and the primary grains and ?p is some sort of average grain boundary energy between primary grains. For a constant primary grain size, the critical size for secondary growth increases as ?$/?p increases. May and Turnbull5 have incorporated the

Jan 1, 1969

By A. W. Bethune, L. M. Pidgeon

The equilibrium vapor pressure of zinc has been determined over the systems: ZnS(s) + Fe(s) = FeS(s) + Zn (vapor) and ZnS(s) + 2Cu(s) = Cu2S(s) + Zn (vapor) by reacting the components in an evacuated tube containing a thin copper fiber, and allowing equilibrium to be established with respect to the brass formed and the zinc in the vapor phase. The composition of the brass formed was determined and equilibrium vapor pressure values obtained from existing data. Between 850&apos; and 1000°C, values for the first reaction ranged from 8 to 58 mm Hg; for the second reaction from 1.8 to 22 mm Hg. THE direct reduction of metallic sulphides may be indicated by an equation of the form MS + X = XS + M [1] where X is some suitable reducing agent. In the case where M is a metal of relatively high volatility, the use of vacuum will displace the equilibrium to the right at comparatively low temperatures in the face of the usually unfavorable thermochemistry. For this technique to be feasible, MS, X, and XS, must of course be nonvolatile compared to M. In this regard, zinc becomes an obvious metal both from the point of view of its volatility and the fact that most commercial ore deposits of this metal occur as the sulphide, and its direct reduction would avoid the expensive roasting process necessary prior to present day reduction methods. Two reducing agents are of interest, namely copper and iron, with the former having the added attraction of being relatively easily regenerated by oxidation in the copper converter. The possibility of these reactions has been considered before. Imbert1 patented a process whereby zinc sulphide was reduced by either copper or iron. The process as described took place at atmospheric pressure and, at the high temperatures required, the system was molten, resulting in the formation of a matte with the consequent reduction in the activities of the reactants. Peterson2 did further experimental work on these reactions and, although promising results were obtained on a small scale, attempts to increase the size of the furnace led to excessive "blue powder" formation. The early workers failed to realize the large reduction in temperature afforded by the use of vacuum and its desirable results. More recently, the direct reduction of zinc sulphide by iron has been the subject of a thermody-namic investigation by Kelley,3 and Gross and War-rington&apos; have studied the kinetics of the reaction in the temperature range 900" to 1000°C, their experiments being conducted using vacuum and indicating that the reaction would proceed practically to completion in 1 to 3 hr, depending on the temperature. A qualitative examination of the system ZnS-Cu carried out at this University indicated that 98 pct of the theoretical zinc in the charge could be recovered in 1 hr at 1000°C when operating under reduced pressure. The purpose of this research program was to study the equilibrium of the two reactions. During the investigation, reference to the experimental work of Schenk5 was found but, due to lack of detail in the report, it was felt that it would be desirable to continue the equilibrium measurements. Selection of Method The measurement of vapor pressure of metals presents obvious problems resulting from the high temperatures which must be employed. In the present case, the production of the "reaction pressure" introduces a further difficulty since a chemical reaction must proceed before any metal vapor pressure is produced, resulting in depletion of the re-

Jan 1, 1954

THE CHAIRMAN (G. H. CLEVENGER, Stanford University, Cal.).¬I would like to ask Mr. Pyne if he has had any experience inn the use of chromite as refractory under conditions that are highly reducing? I am reminded of an experience I once had with an electric furnace. I imagined that chromite would form a splendid lining, but it soon disappeared; hence it seems probable that, under highly reducing conditions at a high temperature, chromite is a very poor refractory. F. R. PYNE.-In copper smelting the atmosphere is generally neutral, or slightly oxidizing; we do not use highly reducing atmospheres at all, not even in the matting furnace. You can take the chromite brick and treat it as you would an iron ore, obtaining ferro-chrome very readily, from which the copper will separate. We have done this; in fact, at one time we considered installing a small electric furnace for the production of ferro-chrome. FOREST RUTHERFORD, New York, N. Y.-During the time I was general superintendent at the smelter of the Copper Queen Consolidated Mining Co., at Douglas, Ariz., a great many experiments were made on the furnaces and settlers with different kinds of brick, and I agree with Mr. Pyne&apos;s statements about chrome brick. Their power to absorb metals is very great, and as they cannot be smelted at any temperatures obtainable in a copper furnace, to get rid of the bats and extract the metal from them is quite a problem. We finally got down to using chrome brick only for lining the settlers, out of which we often got a life of upwards of 2 years, and for lining the blast-furnace bottoms, for the reason that chrome brick can be heated and wet, or wet after being heated, without going to pieces, whereas under these conditions magnesite brick will break down very rapidly. We also used a layer of chrome brick above and below an 18-in. band of magnesite brick put on the slag line of the reverberatories, in order to separate the magnesite from the silica brick, fearing that they would slag each other and let the wall drop. The idea worked, but became unnecessary on account of a change made in the method of feeding the furnaces. Chronic brick will not stand up under pressure so well as a good Grecian or Austrian magnesite brick, on account of the poorer bonding properties of the materials from which the chrome brick is made.

Jan 4, 1918

By K. Tangri, M. Chaturvedi

The addition of 0.5 wt pct Cu to Zr-2.5 Cb alloy increases the as -quenched hardness of the hexagonal martensitic a&apos; phase, produced by water-quenching bccß-Zr phase, by about 35 pct. This strengthening has been attributed to the solid -solution hardening of the matrix. On aging ternary martensite, a&apos; phase reverts to equilibrium a and Zr2Cu and ß-Cb precipitate out, mainly at the twin and grain boundaries, causing a secondary hardening of the matrix. COLD-worked Zircaloy-2 pressure tubes have been in use in power reactors for a considerable period of time. The search for a better material led to the development of Zr-2.5 wt pct Cb alloy which in the quench-aged condition develops 50 pct more strength than that of cold-worked Zircaloy-2, however, its corrosion resistance in water and steam in the temperature range of 316" to 400°C, in absence of neutron flux, is inferior to that of zircaloy-2.&apos; Work carried out by Ells et al.1 and Dalgaard2 has shown that the corrosion properties of Zr-2.5 wt pct Cb alloy can be considerably improved by the ternary addition of 0.5 wt pct Cu. This paper is concerned with the effect of 0.5 wt pct Cu on the formation of martensitic a and its aging characteristics in a Zr-2.5 wt pct Cb alloy. MATERIALS AND EXPERIMENTAL TECHNIQUES Zr-2.5 Cb-0.5 Cu (referred to as the ternary alloy) and Zr-2.5 Cb (referred to as the binary alloy) alloys, supplied by the Chalk River Nuclear Laboratories of the AECL were used. The detailed chemical analysis is given in Table I. Cold rolling and swagging with frequent intermediate anneal of 1000°C were used for the initial fabrication of the alloys. All the heat treatments were carried out after the specimens were wrapped in zirconium foils and encapsulated in silica tubes under a vacuum of 5 x 10-6 mm of Hg. For optical metallography and hardness measurements specimens were mechanically and then chemically polished in a 45 pct HNOj, 45 pct HzO, and 10 pct HF solution. Hardness was measured on a Vickers hardness tester using a 10-kg load. For each specimen at least fifteen indentations were made in order to obtain a representative value. The phase identification and structural analysis were carried out using X-rays and electron diffraction techniques. Wires of 1.5 mm diam reduced to 0.12 mm diam by chemical etching were used for making Debye-Scherrer powder patterns using Cu Ka radiation in a 114.6 mm diam camera. Carbon extraction replicas were prepared by etching the specimens, after depositing a layer of carbon on the metallographic specimen, in one part HF and thirty parts ethyl alcohol. Thin films were prepared by electropolishing heat-treated 3/4 by 1/2 by 0.005 in. thick strips using a modified Bollman-Window technique. The 10 pct perchloric acid-90 pct methyl alcohol bath was kept at -50°C and polishing was done at 5 to 10 V. The thinned specimens were washed in ethyl alcohol at -30º to -40°C and dried between filter papers. Replicas and thin films were examined in a Phillips 300 G electron microscope. For resistivity measurements thin strip specimens 0.02 by 0.3 by 10.0 cm long were used. The potential leads were spot welded to the specimens in order to maintain a fixed length for the initial and the final resistivity measurements. The resistivity was measured by a Kelvin bridge in a temperature controlled room. The temperature was maintained at 72º ±1°F and the accuracy of the resistivity measurements was 0.03 µa-cm. RESULTS As-Quenched Structures. In order to produce a homogeneous matrix to study the precipitation reaction the solution-treatments of both the alloys were carried out in the -field region. From the Zr-Cb phase diagram due to Lundin and cox3 ß/a + ß phase boundary for Zr-2.5 wt pct Cb alloy is 820°C. Ells et al.1 have reported this boundary for Zr-2.5 Cb alloy containing 1100 ppm 0 to be at 920°C. Also, the addition of 0.5 wt pct Cu reduces this temperature by 50°C. Therefore, the solution-treatments were carried out at 1000°C to ensure that the alloys were in ß-phase region. The soaking time was 1 hr and the specimens were water-quenched. The as-quenched hardness of the binary alloy was 245 Vpn whereas, that of the ternary alloy was 330 Vpn. The X-ray diffraction studies indicated that the as-quenched structure of both the alloys consists of martensitic hexagonal phase a&apos;, with a c/a ratio of 1.591, and some retained ß-Zr. The presence of a&apos; phase was further confirmed by thin film electron microscopy. Electron micrographs of typical ß-quenched structures of the ternary and the binary alloys are shown in Figs. 1 and 2, respectively. Fig. 3 shows the diffraction pattern from an area similar to that shown in Fig. 1. Although, the as-quenched hardness of the ternary alloy is about 35 pct greater than that of the binary alloy, the structure of both the alloys seems to be the same. The matrix of both alloys is heavily twinned and shows very few dislocations. Furthermore, there is no evidence of any precipitation taking place in either of the two specimens during quenching from the solution-treatment temperature. Aging Behavior of Martensitic a&apos;. The aging kinetics of the ternary alloy were followed by resistivity and hardness measurements. The as-quenched values

Jan 1, 1970

By E. W. Davis

IF the tonnage of merchantable iron ore remaining in the Lake Superior district is divided by the average of the annual shipments for the past 20 years, it will be found that this ore supply will be exhausted in approximately 35 years. This computed exhaustion period would be an indication of the future activities of the iron-mining industry if it were not for the fact that merchantable ore is being manufactured from low-grade ore, of which there is an almost inexhaustible supply in the Lake Superior district. It is true that at present only the simplest of these low-grade ores are being concentrated to any considerable extent, but progress is being made with the treatment of the more complex ores, and now, in addition to 20 washing plants on the Mesabi Range, three plants are equipped with jigs for the treatment of ore that cannot be concentrated simply by washing. The latest addition to the ore-treating plants of the Mesabi Range is a magnetic roasting and concentration plant at Cooley, Minn., in which ore that cannot be concentrated either by washing or by jigging is roasted to the magnetic state and concentrated on magnetic separators. This plant is beginning its third season of operation, and while it is too soon to make definite predictions, there are strong indica-tions that this new process may make commercially possible the manu-facture of high-grade, merchantable iron ore from large quantities of low-grade ore now considered worthless. After the iron oxide contained in an ore has been converted to mag-netite, almost any desired grade of concentrate can be produced, using magnetic-concentration equipment of the types now in general use for the concentration of the natural magnetites of New York, New Jersey and Pennsylvania. The conversion of hematite (Fe203) to magnetite (Fe304) is easily accomplished by heating the ore to a dull red tempera-ture in a reducing atmosphere. The reaction is slightly endothermic, and while it requires 200 B.t.u. to heat to 900° F. one pound of hematite ore containing 45 per cent Fe, it requires only 100 B.t.u. to convert the oxide into magnetite. In the laboratory, using small quantities of ore, this conversion is very simple, but large furnaces suitable for commercial

Jan 1, 1936

By Edward Sampson

Despite the many industrial uses, the world market for silver as a commodity is far from free, being dominated by the U.S. Government both through acts of Congress and by policy of the Treasury Department. This discussion will consider aspects of supply, demand, and price with a view to the future. Changes in Sources of Supply: The world&apos;s peak production of silver, 278 million oz, was in 1937. In the 1850&apos;s world production was about 30 million oz, having risen from a yearly average of 11 million oz for the first half of the century. From 1860 to 1940 there was a steady rise, broken only by World War I and the depression of the early 1930&apos;s.

Jan 7, 1960

By V. Annamalai, J. B. Hiskey, L. E. Murr

The kinetics of copper cementation on rotating disks of body and tear-top beverage can aluminum alloys were studied as a function of temperature and copper ion concentration. Both alloys followed the two-step kinetic regions, an initially slow rate followed by an enhanced rate. Experimental activation energy determinations (9.04 to 19.62 kJ/mol) indicated that ionic diffusion controlled the reaction mechanism between 20° and 60°C. At low temperatures (< 20°C), the system appeared to be controlled by the presence of an aluminum oxide surface film. The results of this study showed that cementation kinetics for the beverage can aluminum alloys are similar to those for pure aluminum. It was also found that the chemical removal of the oxide layer is less important for the alloys than /or the pure aluminum system. The characteristics of the resultant copper deposits were studied under a scanning electron microscope, and the reaction kinetics seemed to depend strongly on the nature and morphology of the deposits. In addition, maximum rates occurred when the deposit structures were fine feathery dendrites.

Jan 1, 1980

By H. H. Stout

IN the early fall of 1025, the writer was conducting, in the Ledoux and Co. labora-tory, New York, experiments directed to-ward ascertaining the effect on its impurity content when cathode copper was subjected to a current of various gases at an elevated temperature below the melting point. The apparatus consisted of a vertical I-in. dia. silica tube about 12 in. long, heated on the outside. The cathodes were broken to pass 3/8-in. mesh, and a current of various differ-ent gases was passed up through a 4-in. long column of these loose cathode particles in the vertical tube furnace. Temperature was maintained to 1500° to 1600°F. and the gas treatments lasted from 3 to 6 hr. The writer observed that whenever reducing gas (H2 or CO) was used, these cathode par-ticles stuck together at points of contact with each other. The cohesion was so marked and tenacious that an examination was made of the fractured surfaces, when cathode particles were broken from the cluster. Crystal growth was always found to have taken place across the surfaces where separate particles were in contact, but only after all oxides, sulphates, etc., had been completely removed. The idea of a possible new process was then conceived and was disclosed to A. M. Smoot (V. P. Ledoux and Co.) with intent to obtain his views. The first conception as given Smoot was "to gas-clean broken cathodes, put them in an extrusion press, solidify and extrude them at around 1500°F." Smoot&apos;s reaction, after a few moments considera-tion, was, "It looks perfectly all right to me." The writer and his assistants, W. H. Osborn and H. H. Stout, Jr., after confer-ring as to ways and means, decided to go ahead with preliminary laboratory experi-ments, which, it was thought, would move the new process from the possible to the probable. This program followed a course indicated by three basic considerations: I. Since brittle cathodes were often unin-tentionally produced, it seemed probable that the laws controlling this type of deposi-tion could be ascertained. 2. We had already proved the gas-clean-ing feature. 3. There remained to prove: whether a sound, homogeneous metal billet could be produced with crystal growth established over the entire surface of each individual particle in the billet; and, if so, what would be the physical properties? Osborn arranged with Columbia Uni-versity for conducting experiments in its research laboratory to prove or disprove the third item; Columbia assigned C. A. Phillipi, Jr. to assist in the project. A press with a cylinder 2 in. high and of I-in. dia. was used. It was surrounded and heated by a resistance coil of Nichrome wire. Broken tough cathodes were used.

Jan 1, 1940

By Charles E. Reed

With the increasing importance of clay in drilling operations which demand more precise and exacting control over its behavior, there has come the realization that most of our present methods of control over many of its important properties still represent more of an art than a science. Such a situation with respect to a material of such industrial significance is unfortunate, and naturally many investigations have been conducted to improve our knowledge. In general, these investigations have revealed the complex nature of clay behavior and while sometimes they may not have seemed to contribute directly to a solution of the field operator&apos;s problems they have been of inestimable importance in bringing to light the broad fundamental scientific principles upon which must be based any effective working theory correlating the known facts of clay behavior and predicting profitable new lines of attack for its improvement. Major Facts Concerning Behavior of Clays In the study of clays, as in that of most other colloidal materials, it has been impossible to make progress by the study of isolated facts. On the other hand, analysis of large groups of facts, many of which seem at first completely unrelated, can lead to a deeper insight into the structure of clays and the mechanism of their behavior. It will be well to list the major facts on which the analysis here presented is based, starting with those that have emerged repeatedly from past investigations and which thereby constitute an impregnable foundation upon which must rest any comprehensive theory of clay behavior: 1. Clays consist of hydrated aluminosilicates of extremely fine and variable particle size. 2. Suspended in water, clays exhibit variable degrees of swelling, depending upon their origin and upon the chemical and colloidal nature of any other substances present. The magnitude of the swelling is a direct indication of the extent to which the clay has become dispersed.

Jan 1, 1938

By H. Morgolin, M. A. Greenfield, P. A. Farrar

In attempts to correlate mechanical properties with microstructure, it is desirable to determine the effect of ß grain size. Determination of 6 grain size is not a problem where a has precipitated at ß grain boundaries. However, in alloys which have been processed to produce an equiaxed a +ß structure the ß grain size is difficult to determine because ß grain boundaries do not etch. The ß grain size can sometimes be laboriously determined by searching for grains which have some a! outlining the 6 grains. This difficulty of ß grain size determination in equiaxed a + ß alloys can be overcome by heating below the ß transus temperature for a short time and water quenching. Fig. 1 shows the starting equiaxed a + ß structure of the Ti-5.25A1-5.5V-0.9Fe-0.5Cu alloy used in this investigation, and Fig. 2 shows the microstructure of the same sample water-quenched after heating 1 min at 1675"F, which is 25°F below the 0 transus. The heavily etched microstructure consists of some equiaxed a! in a structure showing considerable amounts of transformed ß. The ß grain

Jan 1, 1969