By Jaakko Kajamaa

Neutron diffraction was applied to determine sheet textures by the transmission method. Cold-rolled and recrystallized copper sheets were investigated. The amount of cube texture was determined for three compositions, in which the phosphorus content was, respectively, 0, 0.005, and 0.03 wt pct. The heat treatment was in every case 8 sec at 650°C. In the two latter cases the cube texture was prevented. In addition a comparison with the X-ray diffraction transmission method was made with the 96 pct cold-rolled copper sheet. Outer parts of both (111) pole figures can be considered to be rather identical. This is seen from the fact that the intensity ratio ITD/120" was 0.45 for neutron diffraction and 0.40 for X-ray diffraction. Differences between the methods were discussed in detail. Features peculiar to neutron and X-ray diffraction in texture studies were listed and compared. In this work neutron diffraction was applied to determine sheet textures. Specifically, it was desired to ascertain whether this method can be used to reveal differences when compared to other methods. In addition, the amount of the cube texture in copper sheets was determined as a function of phosphorus content. Previous applications of neutron diffraction to texture problems include the following: nickel wires,' wire of some bcc metals,' and uranium bars.3 In the neutron diffraction technique the greatest difference is in the sample—its method of production and its volume. A sample needs no treatment and its volume is roughly 105 times larger than the volume of an X-ray diffraction sample. The cold-rolled sheet was investigated both by neutron diffraction and by X-ray diffraction, because it is expected that, due to large number of defects, possible differences in the results of the two methods would be revealed. It is a well-known fact that X-ray lines show broadening when cold-worked. Analysis has shown that this is based chiefly on small crystalline size, micro-stresses, and/or faults.4'5 Neutrons are sensitive to the above-mentioned disturbing factors as well, but circumstances in diffraction are different from the X-ray case. Because the sample represents a larger volume, the result is an average over that volume. In addition, it can be assumed that the sample has preserved its original structure, because it needs no special preparation. The particular limitation of neutrons is the relatively low neutron intensity available from nuclear reactors. This decreases the resolution as compared to the X-ray diffraction methods. Furthermore, absorption mainly reduces diffracted X-ray intensity, while multiple scattering effects, i.e., secondary extinction, disturb neutron diffraction. SO neutrons and X-rays behave in a different way when interacting with matter. As in other structural investigations, one can utilize this difference in texture studies as well. One cold-rolled and three recrystallization textures in copper sheets were investigated by neutron diffraction. The samples were produced at the Outokumpu copper factory to the specifications shown in Table I. The paper is divided into five parts. The first deals with the theory of the measurement. In the second, experimental procedures are described. Results are presented in the third part. Both cold-rolled and re-crystallized samples are studied. Discussion is in the fourth part, and finally in the fifth part some conclusions are drawn. 1) THEORETICAL CONSIDERATIONS Properties peculiar to neutron diffraction are the following: a) the scattering length varies greatly between one element and another; b) many of the elements do not absorb neutrons appreciably. In this connection it is of primary interest to know the interaction of neutrons with lattice imperfections. As with X-rays this problem leads to diffraction analysis of deformed and recrystallized metals. From the physical point of view the main difference is that neutrons are scattered by nuclei (magnetic scattering is not considered here), whereas X-rays are scattered by electrons. The features peculiar to neutron and X-ray diffraction methods in texture studies are listed in Table 11. Pole figures are an important tool in performing structural analysis of deformed or recrystallized metal. Present texture research technology requires pole figures which are as precise as possible. The choice between these two methods depends on the technical information which is required. The X-ray diffraction transmission technique may give results which are not necessarily representative of the average physical state of the sample. Although foil samples normally contain enough crystallites for diffraction, they may not necessarily represent the whole structure. An example of this problem is the frequently observed difference between the "surface" and the "inside" texture of a sample. The production of foil samples may disturb the original structure of the parent material. The selection and orientation of the foil from the sample is quite arbitrary. Normally, a highly deformed piece of metal has several texture components. Different components are deformed in a slightly different manner. This is a re-

Jan 1, 1969

By A. Ojanen, T-L. Huggare, A. Kuivala

An electrolytic zinc plant with a capacity of 90,000 tons/year went on stream in Kokkola, Finland, in late 1969. It is a standard electrolytic zinc process plant; however, it has been subjected to several process improvements and enlargements during its time of operation. A fluidized bed roaster treats 500 tons/day of zinc concentrates which also contain mercury. Since the mercury evaporates completely in the roasting process, a mercury removal unit has been added to prevent, contamination of sulphuric acid produced in the neighbouring acid plant. The same unit also removes selenium from the roaster gases. In a separate unit, about 6 tons a year of metallic 99.999% mercury is recovered. The neutral leaching, originally a batch process, has been converted to a continuous operation, and a residue treatment system comprising hot acid leaching and jarosite precipitation has been added. Purification comprises a "hot arsenic-zinc dust" step and a cadmium removal step with zinc dust, both operated batchwise. Purification residues are used to make about 200 tons/ year of 99.99570 cadmium in a process developed by Outokumpu Oy. The electrolytic precipitation of zinc carried out at medium current density gives zinc of 99. 995% purity.

Jan 1, 1973

By M. D. Hassialis, C. G. Myer

THE nature of a collector-coated mineral surface has been the subject of some experimentation and much speculation. Various aspects of the problem have been isolated and studied; it is probable, however, that there exist aspects as yet unrecognized, which are needed for a complete description of the system. The recognized elements of the problem are: 1—The nature of the chemical units comprising the film and the nature of the forces holding these chemical units to the mineral surface; 2—The orientation of the chemical units at the surface; and 3—The disposition of the collector units at the mineral surface. This report touches upon all three aspects of the broad problem; it deals, however, with a new and heretofore unrecognized element—the mobility of the collector units in the two dimensions of the solid-liquid interface. Regardless of the viewpoint adopted as to whether the chemical units comprising the collector film are collector ions or molecules, held either by chemical or physical forces, the writers on flotation theory are in apparent agreement as to the orientation of the chemical units at the mineral surface. Wark and Cox' showed that the contact angle at a stable collector-coated surface in a constant chemical environment is independent of the nature of the mineral and of any resurfacing agent; it depends solely upon the collector used. They showed further that the value of the contact angle increases with the number of carbon atoms in a homologous series of compounds. Taggart, Taylor, and Knoll2 postulated that the collector ion is oriented with the chemically reactive, polar end toward the mineral surface and the non-polar, hydrocarbon-like end toward the liquid phase. In support thereof they cited the abstraction of p-p1 dihydroxydiphenylthiourea and of glycol xanthate8 by galena without a concomitant increase in the contact angle above that of clean galena. It was argued that in these cases the water-repellent layer which normally would be presented to the liquid phase owing to the orientation of the collector ions is overlain by a layer of water-avid groups, the hydroxyl groups. Implicit is the analogous orientation exhibited by a monomolecular layer of an insoluble substance at an air-water interface. It should be pointed out that these facts also are consistent with the concept that the collector units be flat on the surface of the mineral and that the response of the surface to an air bubble is determined by the ratio of the area covered by water-avid groups to the area covered by water-repellent groups; the areas being weighted according to the relative watef-avidity or water-repellency of the groups involved. The disposition of the chemical units of the collector film at the mineral surface has not received the attention it merits. Taggart4 concluded from the observed stoichiometry of the ions entering and leaving a surface that the stoichiometry is obeyed in detail at the surface of the mineral. Thus, in the case of xanthate-coated galena, pairs of xanthate ions are attached to surface lead ions. In the case of chemisorption, Gaudin and Preller postulated an agreement between the atoms or ions of the substratum (the mineral surface) with those of the superstratum (collector film); in the case of the physical adsorption their position is not clear. In one place they state "the first type (physical adsorption) does not require any agreement between the atoms or ions of the substratum with that of the superstratum" and in another place that "It seems, in fact, as though some slight influence of the substratum is formed even in physical adsorption." The present work shows that in some cases of chemisorption the chemical units of the collector film are in constant surface-bound motion and may not be assigned to any site of the surface, hence there is no permanent association between the chemical units of the film and the atoms or ions of the solid. The physical property of the collector film that is of paramount importance is its surface energy. Although this property is not susceptible to direct experimental determination, the related contact angle is. Much of the knowledge of the properties of a collector film derives (by deductive and inductive reasoning) from the behavior of an air bubble thereat

Jan 1, 1952

By N. J. Grant, B. C. Giessen, M. Morris

The slvuclures of alloys in the system In-Bi have been investigated after (levy vapid queuching from the mell (splat cooling) to -190°C. Tuo-phase fields could be suppressed over most of the tota1 concentvalion range; five melastable phases a1, a2, ?, ?1. and ß exisl, of which four have simple elementtike structures. For example, ß has the A5 struclure of white till. Crystal-tographic data and coordination numbers for these phases aye given, as well as addilional information on the equilibrium diagram, where a new phase In5Bi3 teas found. THE phase diagrams of binary combinations of B elements from the groups B2, B3, B4, and B5 are usually of a simple type and show considerably fewer intermediate phases than combinations of these elements with A metals, transition metals, or the B1 noble metals. Aside from phases such as the typical B3-B5 compounds with the ZnS-B3 structure type, few stoichiometric phases are known; among them are In2Bi and 1nBi.l Nonstoichiometric phases include ß (In-Sn), a1, (In-Pb), and the tin-rich ? phases in the In-Sn, Cd-Sn, and Hg-Sn systems.' The first two phases have a close relationship to indium, while the latter group are known to be structurally related to a Sn. Thus, there are generally no immediate experimental data for the correlation of the crystal structures of B metals and B metal combinations with certain monotonously varying parameters, such as the valence electron concentration (VEC), or the average atomic size. Such parameters have been recognized as structure determining, e.g., for the transition 4 Sn — y phase,2,3 where nonintegral valence electron concentrations are encountered. It should be possible to extend such correlations to other binary systems, if nonequilibrium single-phase alloys could be produced over broad valence electron concentration ranges, and if their crystal structures could be regarded as being imposed by their electronic states. It has been shown in the case of the tin-rich 7 phases3 that alloy phases with typical crystal structures can be produced in B metal alloys rapidly quenched from the liquid to -190°C by the splat cooling technique due to Duwez,3-8 and reviewed in Refs. 5 and 6. The In-Bi system was selected because it extends over a valence electron concentration range in which several metastable, nonstoichiometrir phases could be expected to occur. Further, the low melting points of the known intermediate phases, In2Bi and InBi, Fig. 1(a), indicated low binding energies and thus possibly low driving forces for the formation Of the equilibrium structures. EXPERIMENTAL TECHNIQUES AND RESULTS The preparation of the quenched foils followed the practice described in Ref. 3. Master alloys were produced by melting of indium (99.97+) and bismuth (99.99+) in evacuated Vycor capsules or in an inert gas arc furnace; quantities of 20 mg were splat-cooled onto copper and silver substrates held at - 190°C; and crystal structures and lattice parameters were determined on a GE XRD-5 diffractometer using Cu Ka, radiation at -190°C and at room temperature. The duplication of each run with both substrates permitted the elimination of overlap of the substrate diffraction pattern and that of the investigated substance. The XRD patterns were usually taken from sin2 " = 0.03 to 0.35; the substrate was used as a means of internal calibration. The fractional accuracy of the lattice parameters of metastable phases is approximately 10-3 In the following, all percentages are in atomic percent. The stable and metastable phases found after rapid quenching to -190°C are listed in Table I, together with estimated concentration ranges and crystallographic data. The investigated alloys and phases present in them are given in Table 11. Except for the region between indium with 33 and 50 pct Bi, where a revision of the equilibrium phase diagram became necessary to include a new stoichiometric phase In5Bi3, the diffraction patterns taken after heating to room temperature agreed with those expected from the phase diagram, Fig. l(a). This suggests that the new nonstoichiometric phases are not stable at room temperature, thus following the observations made for the y phases based on tin.3 Results concerning the equilibrium phases In2Bi and In5Bi3 and the revision of the equilibrium phase diagram which is made necessary by the inclusion of In5Bi3 will be treated first. The Crystal Structure of In2Bi. Makarov7 had identified In2Bi as belonging to the AlB2-C32 type ; however, in a later paper the structure was revised.8 In2Bio was found to be of the Ni21n-B8ß type,21 with a = 5.496A, c = 6.57.9A, and N = 6 atoms per unit cell.9 This crystal structure was confirmed in the present work; definite evidence for the doubling of the c axis, as compared to the A1B2-C32 type, and for the proposed order structure, was found in the powder pattern. The observed lattice parameters agree well with those of Ref. 8; those measured at -190°C are given- in Table I. The Crystal Structure of In5Bi3. A new, equilibrium, intermediate phase was identified in slow-cooled, as-cast alloys; it was identified as In5Bi3. The structure has been worked out by Giessen and Grant;" lattice parameters at -190°C are given in Table I. This phase is probably identical with "In3Bi2", produced by vapor deposition techniques, but not recognized as an equilibrium phase by Palatnik et a1.11 After completion of the present work, the existence of In5Bi3 has also been demonstrated by superconductivity measurements on In-Bi alloys.20

Jan 1, 1968

By G. Baralis, P. Gondi, I. Tangerini, G. Scandola

The precipitation behavior of Zn-0.5 pct A1 alloy single crystals was studied by means of electrical resistivity measurements and by optical and electron microscopy. The single crystals for the resistivity measurements were prepared by an original method in - 100-p -thick sheets. The order of the precipitation kinetics ranged between 1 and 1.5. The dislocations play a relevant role in the first-order kinetics. Precipitation always occurs both on dispersed particles and on dislocations. Statistical examinations have shown that the first-order kinetics can have two different activation energies; i.e., the precipitation can have dz;fferent mechanisnrs which could not be identified, however, in the course of the research. During the tnetallographic exanzination of the precipitation structures a specific process of dislocation decoration was obsereed. The main purpose of this work was to study the contribution of dislocations to the precipitation. A number of authors have observed precipitation on dislocations and reference might be made to several monographs on the ubject.'' The possibility that dislocations also accelerate precipitation has been considered by Turn-bull3 and Fischer et al.4 The studies described in the present paper were carried out on zinc, chosen as a base metal owing to the ease with which dislocations can be introduced into it and because of the absence of excess vacancies after quenching in conditions where phenomena of accelerated precipitation still occur. Aluminum was preferred as alloying element because of the accelerated precipitation phenomena that resulted in a preliminary reearch. EXPERIMENTAL METHODS The observations refer to a Zn-0.5 pct A1 alloy. The zinc was 99.995 pct pure; a typical spectroscopical analysis is given in Table I. As a rule the alloy was subjected to homogenization, quenching, or slow cooling and annealing. Homogenization was carried out by heating at 390" to 410°C for 24 hr. From the homogenization temperature, some specimens were quenched and some slowly cooled at a rate of 2°C per sec. At this rate no precipitate was detectable under the optical microscope just after cooling. Quenching was carried out simply by dropping the specimens into water, aqueous ethylene glycol solution at -30" c, or liquid-nitrogen baths placed close to the homogenization oven. Vaseline oil baths were used with a thermal stabilization of 10-20 for both the aging treatments and the measurements; aging was generally carried out at 90" or 130°C. To avoid oxidation phenomena during heating, the vaseline oil baths had to be frequently renewed. The precipitation kinetics were studied by means of electrical resistivity measurements, using ans potentiometric method (reproducibility ± 5 x 10 5 v, that is 0.5 pct of the total voltage decreases on the specimens during precipitation). First, various types of specimens were tested, i.e., polycrystals, single crystals grown in capillary quartz tubes, and thin single-crystal sheets prepared by means of an original method requiring no container except for the natural oxide. Even if fully annealed, the polycrystals and the capillary grown single crystals showed resistivity in -creases, most probably due to dislocations introduced in the course of the measurements. Similar resistivity increases in pure zinc were noticed by another author. Only the single-crystal sheets showed no resistivity change; thus they were chosen for the subsequent tests. As already mentioned, these single crystals were obtained by using, as a container, the natural oxide on the zinc surface; the oxide strength is sufficient to maintain the original shape during melting with sheets up to 500 p thick. An initial zone melting and subsequent zone leveling, which led also to formation of the single crystals, were thus carried out on rolled sheets of the required thicknesses (- 100 p) and shape, lying on a flat silica surface. The resistivities were first evaluated by measurements at the liquid-nitrogen temperature. This method gave poor reproducibility, however, and this was attributed to the thermal cycles which had to be operated. To avoid cycles and handling, it was therefore decided to make measurements directly in the annealing oil baths; this required thermal stabilization at ilo-' "C. In this way only the resistance changes were measured. Specimens of pure zinc and of completely annealed alloy were always examined as controls together with those under consideration; only those measurement runs were taken into account where the reference samples showed no resistance increases. Again, the main inconvenience was due to oxidation and this was avoided by renewing the oil baths; even so data reproducibility was poor and the observations were therefore carried out on a large number (many hundreds) of specimens so as to provide indications of statistical value. For the transmission observations under the elec-

Jan 1, 1969

By Charles H. Fulton

Experimental work on the process was begun on a laboratory scale at Cleveland, Ohio, in 1914, and transferred to East St. Louis, Ill. in 1916, where a commercial sized furnace was in technical operation until January, 1918. The essential steps of the process are as follows: Oxidized zinc ore or roasted zinc concentrate is mixed with crushed coke and coal-tar pitch and formed into briquets 9.25 in. (23.5 cm.) in diameter and 21 in. (53 cm.) long in a manner similar to that used in the manufacture of graphite or carbon electrodes, except that much less care and time are required. The composition varies with the nature of the ore; in one case, the composition was 100 parts ore, 70 parts coke, and 18 to 20 parts pitch. These briquets maintain their form and volume during and after the distillation of the zinc. This object is gained by using coke as the matrix and coal-tar pitch as the binder; this pitch becomes coke on heating and unites the ore particle and the original coke particle into a continuous mass. The briquet is an electrical conductor but only to such a degree that it can be used as a resistor. The size of the ore, as in the present practice of zinc metallurgy, ranges from fine material, such as flotation concentrate, to coarse table and fine jig concentrate. The process is not restricted to any particular kind of ore, but is applicable to pure high-grade ores, ores high in iron, and complex zinc-lead ores, since the residue from the distillation IS held immovably in place within the briquet. In the case of complex zinc-lead ores, the distillation is conducted with a carefully regulated temperature so that a high percentage of lead is retained in the distilled briquet, which may then be smelted for its lead content. In present zinc smelting practice, the reduction fuel is from 40 to 50 per cent. of the weight of the ore. In the briquet, it is from 60 to 85 per cent. of the ore; but unless the ore is exceptionally high in residue, the distilled briquet may be used over again as coke, or as a high ash coke for fuel purposes in power production. Baked briquets are hard and tough and may be handled roughly

Jan 1, 1921

By L. F. Mondolfo

R301 is a clad aluminum alloy, composed of a core of a duralumin-type alloy clad with a magnesium silicide alloy. It differs from other well-known clad alloys in that the cladding and the core respond to the same heat-treatments, and therefore the cladding contributes appreciably to the mechanical properties of the material. In Table 1 are reported the compositions of the core and cladding alloy for the material used for the experiments. [ ] In clad aluminum alloys where the core contains copper and the cladding does not, at elevated temperatures the copper tends to diffuse from the core through the cladding. This fact is well known and many investigations have been conducted to determine the features of this diffusion.1-7 Most of those investigations cover materials clad with pure aluminum; the present investigation covers a material clad with an alloy. Since the cladding thickness on R301 varies with the gauge, as shown in Table 2, several gauges were investigated. [ ] MATERIAL AND PROCEDURE The material used was sheet of the following gauges: 0.025, 0.040, 0.064, 0.102, 0.170. Cut in pieces approximately 3 by 5 in., it was in the cold-rolled state and was soaked for increasing times at the following temperatures: 910°F., 940°F., 970°F. A Lindberg cyclone furnace was used for the experiments. The procedure was as follows: The furnace was started empty with controlling pyrometer set at the determined temperature. After the furnace had reached that temperature, it was run for some 20 to 30 min. empty, in order to allow the temperature inside to become stabilized. Then the first samples were introduced. A load thermocouple, with recording pyrometer, was connected with the sample of the heaviest gauge. About 10 min. was required for the material to reach temperature and the soaking time was counted from that point. After 200 min. soaking, the second group of samples was introduced without stopping the furnace. After 200 min. more, the third group of samples was introduced, and so on, until the last sample had been introduced. Every time the furnace was opened and new samples were added, a drop of temperature was registered by the thermocouple connected with the material

Jan 1, 1945

By Henry T. Mudd

FLUORSPAR is a nonmetallic mineral aggregate or mass containing a sufficient quantity of fluorite (CaF2) to be of commercial interest. It has only moderate value per unit of weight and its cost as a percentage of the cost of finished consumer products is nearly negligible. Nevertheless, it has wide and great industrial importance. In periods of national emergency it is a mineral without which many very necessary manufacturing processes would be greatly handicapped; a few could not exist. Fluorite contains 51.1 pct calcium and 48.9 pct fluorine. Industrial grades of fluorspar prepared for the consumer normally contain from 85 to 98 pct fluorite, depending on the use. The ores may contain as little as 30 pct fluorite, depending on many factors such as accessibility to transportation and markets, character of ore, and prices. Fluorite is a lustrous, glasslike mineral, generally translucent to transparent; it may be clear and colorless or range in color from slightly bluish through various shades of violet, amethyst, purple, green, and yellow. It crystallizes in the isometric system and possesses perfect octahedral cleavage. Commonly it occurs in masses of very pure crystal- line material with aggregates of cubical crystals in open spaces, but - it is also found in fine to coarse granular form. Banded veins and masses with fibrous, radiating structure occur locally. It is usually found associated more or less intimately with other minerals and rocks, from which it must be separated for commercial use. The specific gravity of fluorite is 3.18 and the hardness is 4 in the Mohs scale, compared with 7 for quartz and 3 for calcite. It is distinguished from calcite by its failure to effervesce with dilute hydrochloric acid. Heated with sulphuric acid, it gives off fumes of hydro- fluoric acid, which etch glass.22,25,33.34,35.41

Jan 1, 1949

By C. H. Li, R. J. Stokes, T. L. Johnston

A portion of the Ni3Cr-Ni3Al phase dzagram has been investigated, including the precipitation of 1 (Ni3Al) as well as the existence of ordered Y (Ni matrix), Extensive metallographic studies by electron microscopy have been carried out and X-ray diffraction diagrams have been taken at both elevated and ambient temperatures, No long-range ordering of the phase was found above 893°C (1639°F) in the compositional range investigated. The high rate of formation of the ordered ?1 phase upon quenching has been confirmed, a phenomenon which up to the present Lime has retarded the understanding of this phase diagram, Specimens with controlled amounts of ?1 exhibited up to a six-fold improvement in yield and creep strength compared with single-phase Ni-Cv-A1 alloys. MOST of the important high nickel heat-resistant alloys are related to the nickel-chromium-aluminum system. One of the important functions of the aluminum, often accompanied by titanium, is to produce a precipitate of the very fine ?1 phase (Ni3A1, X) where X may be Ti, Cr, or other elements. A number of investigators1-" have demonstrate the presence of y' in these alloys but most of their materials contained large amounts of other elements resulting in appreciable amounts of con- fusing phases such as carbides. Further clouding of the precise role of y' has been the suspected existence of an ordering reaction in the y matrix itself, ro-3,12-17 It appeared from these investigations that aluminum in Ni-Cr alloys would raise the ordering temperature of the matrix from 540°C at NisCr to 1300°C at Ni,Al. In support of this possibility, the matrix phase in the parallel Ni-Fe-A1 system is ordered to very high temperatures.1 OBJECTIVES OF THIS RESEARCH From this survey of the literature it appeared desirable to conduct an investigation of the simple Ni-Cr-A1 system using the alloys of the highest available purity to avoid the complication of foreign phases and thereby isolate the structures in the Ni-Cr-A1 system. Procedures were developed to study ? - ?o and ? - ?1 equilibria. Preliminary mechanical tests at elevated temperatures were also conducted.

Jan 1, 1962

By V. B. Kurfman

Grain refinement of Mg-Al melts by carbonaceous additions has been attributed to nucleation by aluminum carbide. The effects of process and alloy variables are interpreted and predicted in terms of the dispersion and chemistry of this phase. The grain coarsening action of Be, Zr, Ti, R.E., chlorination, temperature extremes, and prolonged holding times is described. Measures necessary to insure an adequate dispersion of the catalyst are discussed. CARBON inoculation treatments have become fairly well known and used for grain refinement of magnesium alloys containing Al. Although there is general agreement that a nucleation process occurs, the process is not understood and the inoculants are used in a rather empirical fashion. The treatment is applied to the class of alloys containing 3 to 10 pct Al, i.e., AZ31A to AM100A. Typical methods involve melting, alloying, and adjusting the temperature to 1400° to 1450°F. Then 0.01 to 0.5 pct C as CaC2, C6C16, or lampblack is added by any convenient means, and the melt poured within 10 to 30 min. Investigators generally have been impressed by an assumed similarity of this refinement process to superheat grain refinement, which depends on heating approximately the same alloys to a temperature in the range of 1550" to 1650°F, then pouring promptly after the melt is cooled to the pouring temperature. Various predictions have been made that carbon refinement would replace superheating in commercial practice due to reduced process costs, but this replacement has not fully taken place because of production difficulties and conflicting observations. Davis, Eastwood, and DeHaven1 agree with Nelson2 and wood3 in suggesting that an excess of inoculant may be harmful. Wood however says that overtreat-ment is not a problem in production use of hexa-chlorobenzene inoculation, and Hultgren and Mitchell4 claim no evidence of harm from excess additions. Various grain coarsening reactions are known to occur, including the possibility of overtreatment mentioned above. Trace amounts of Be,2 Zr, and Ti may prevent refinement by either a carbon treatment or a superheat. Occasionally treatment with cl25 may cause coarsening, although the Battelle refinement process' uses a CC14-C12 blend. Grain coarsening also tends to occur on holding at temperatures below 1350°to 1400°F, especially after a superheat treatment, and for this reason Nelson2 stresses the desirability of a refinement method useful at lower temperatures for open pot melting practice. Since a carbon treatment can be made to work at temperatures below 1400°F, it seems desirable to investigate the mechanism of the refinement and the mechanisms of the coarsening reactions in order to establish control conditions for use in commercial production. The identity of the nucleating phase must first be established and then the factors affecting its chemistry and physical dispersion must be determined. THE IDENTITY OF THE NUCLEATING PHASE Davis, Eastwood, and DeHaven suggested that the nucleating phase in this system is Al4c3,1 but Mahoney, Tarr, and LeGrand8 disagree, largely because they found no evidence of the compound in alloys after carbon treatment and because there is no indication that aluminum carbide should be unstable over the temperature range used in the superheat treatment. This latter objection is based on the assumption that both the carbon treatment and the superheat treatment introduce the same nuclei. Electron diffraction studies have been made to identify the nucleating phase. Samples of grain refined A292 have been selectively etched SO that clean surfaces are obtained and so that secondary phases are in relief. Electron diffraction patterns from these surfaces have established that the carbon treatment of A292 introduces into the metal a large number of small, plate-like particles with a structure very similar to Al4C3. In most cases, the plate-like nature of the particles prevented positive identification but in the cases where the identification could be made the particles proved to be AIN A14C3. However, enough variation in lattice constants was observed so that all compositions from pure A14C3 to the 50:50 solid solution A1N.Al4C3 were probably present.14 In A14C3 and especially AlN.Al4C3 the A1 atoms occur in layers within which they have the same hexagonal symmetry and spacing as the Mg atoms in a single basal plane of a magnesium crystal. The solid solution spacing lies between the 3.16 of AIN and the 3.3? for Al4C3, in satisfactory agree-

Jan 1, 1962

By J. J. Kramer, W. A. Tiller, G. F. Bolling

The solidification of poly crystalline zone-refined lead has been examined. A novel casting technique was used, with several advantages such as unidirectional heat flow, atmosphere control, and decanting of the liquid during any stage of growth. The experimental results show the separate existence of two textures, a (111) surface texture at the chill surface and a texture in the columnar zone, in the absence of conditions which would produce dendritic growth. WALTON and chalmers have most recently shown that the dendrite direction is the preferred axial orientation for the solidification of many metals in casting. Experimentally, for aluminum and lead, they showed that in the columnar zone the dendrite direction, <l00>, predominated, developing from an equiaxed chill cast layer that exhibited no preferred orientation. A reasonable description of the way in which grains closer to the dendrite orientation were able to encompass other grains was then set forth. For their materials, it was also shown that high superheats could inhibit a preferred axial orientation from developing, presumably by inhibiting dendrite growth. The observations of Rosenberg and iller, on the other hand, showed that zone-refined lead, cast under conditions similar to those of Walton and halmers,&apos; had a definite <111> texture in the columnar zone. However, no examination was made of the chill surface to find out if the columnar zone texture was independent of the orientations at the surface. Since the existence of preferred growth in Upure" lead is thus in doubt, a reexamination of the casting of zone-refined lead is presented here, using a novel casting technique. EXPERIMENTAL PROCEDURES AND RESULTS Zone-refined lead was prepared from two starting materials;99.999+pct supplied by ASARCO, and 99.999pct supplied by COMINCO. The manner of zone-refining and the phenomenological tests for purity after refining, have been describedelsewhere.&apos; The casting apparatus is shown schematically in Fig. 1. The following general procedure was used: The metal was cut directly from the best parts of

Jan 1, 1963

By Edward W. Parker

This plant was built in 1907 at the Bankhead mines to manufacture briquettes by the Zwoyer process under license from the Zwoyer Fuel Co., of New York, N. Y. The building was constructed to contain two units, each of a capacity of 10 tons per hr.; one unit was installed at the time the building was constructed, and the second unit is now being built. The coal used is an anthracite, which is more friable than that of Pennsylvania, and, as a consequence, a larger percentage of dust or waste is produced, which was formerly thrown upon the slack-pile as waste, but is now passed to the ? dust-bin " in the breaker, from which it is conveyed to the briquette-plant.

Jan 5, 1908

By J. Chipman, N. J. Grant, H. L. Bishop

In a recent review1 of the iron-oxide activity of simple open-hearth type slags containing lime, magnesia, silica, and iron oxide, it was established that activity values were lacking in the range of slag composition most interesting to open-hearth operators. That is, laboratory experimental results were not available for simple slag compositions having basicity ratios ranging from about 1.5 to 4.0 and iron-oxide concentrations ranging from about 10 to 30 pct. However, in order to estimate iron-oxide activities for the range of slag compositions of interest to open-hearth operators, activity values were calculated using ionic concepts of slags by following the treatment of Flood and Grjotheim.2 A study of these data indicated that the desired slag compositions were probably not obtained due to the limited solubility of the basic constituents lime and magnesia. Thus, it was decided to make additional heats equilibrating molten carbon-free iron with slags containing MnO, P2O5, and A12O3 in percentages commonly found in open-hearth refining slags, and to examine the liquid slag field over a greater composition range than that of the simple slags studied previously. The ranges of the constituents used in the present study are summarized as follows: Metal Pct 0 0.070-0.201 PctMn 0.005-0.142 Slag Pet CaO 24.45-41.90 Pct MgO 3.23- 9.21 Pct MnO 1.13- 9.62 Pct FeO 20.08-48.7 Pet Fe2o3 2.23-10.14 Pct SiO, 3.51-28.50 Pct P2O5 0.23- 3.65 Pct A12O3 0.43- 3.38 The experimental procedure consisted of equilibrating the slag and metal in an induction furnace provided with a carbon-arc slag heater as described previously by Winkler and chipman.3 The data obtained were used to establish both the iron-oxide activity values and the activity coefficients for FeO and MnO in the open-hearth type slags. RESULTS AND DISCUSSION I) Iron-Oxide Activity of Open-Hearth Type Slags—The iron-oxide activities of various iron-oxide contents of the open-hearth type slags, as calculated from the oxygen content of the metal by the method of Taylor and Chipman, 4 are plotted against the molar ratio of bases to acids in Fig. 1. The data represent slag-metal studies carried out in the temperature range 1530" to 1700°C. For the purpose of this study, the constituents CaO, MgO, and MnO are assumed equal on a molar basis in their effect on the iron-oxide activity; and, PO2,5 is calculated as an equivalent to SiO2 and A12O3 on a molar basis. The total iron content of the slag is calculated to FeO and is represented by the symbol (FeO) The points presented in Fig. 1 represent the results of this investigation for iron-oxide slags containing between 1 and 8 mol pct MnO and less than about 2 mol pct each of A12o3 and PO2,5 The curved lines shown in Fig. 1 represent the results of the summary1 of the iron-oxide activities of simple slags of the system (CaO + MgO) - SiOz - (FeO),. The solid portions of the curved lines represent experimental data, and the broken portions represent iron-oxide activities calculated from ionic concepts of slags. The iron-oxide values of the open-hearth type slags of this study are in good agreement with the values of the simple iron-oxide slag system. Only a slight modification is indicated. The results of this study suggest that the line for 20 mol pct (FeO), should be lowered slightly in the basicity range 1.5 to about 3.

Jan 1, 1959

By T. C. Craig

For the year 1934, there were 382 oi1 wells completed for a total initial of 146,965 bbl. Fifty-three wells were deepened for a total increase of 8363 bbl., bringing the total volume of new oil to 155,328 bbl. As of Jan. 1, 1934, the daily potential of the field as determined by the Texas Railroad Commission was 159,740 bbl. Of this amount 26,429 bbl. is "marginal oil," and 2682 bbl. is exempt on account of water. In December, 1934, the daily potential was established by the Railroad Commission as being 297,501 bbl. with a daily allowable of 56,800 bbl. Of this amount 31,993 bbl. is "marginal oil," and 2183 bbl. is exempt on account of water. There has been no field-wide test made during the year, and as a result the rated potential of the field is in all probability much higher than the actual potential. As each new well comes in, a five-day test is made under the supervision of the Railroad Commission. The potential thus established is added to the field potential and shares its pro rata part of the market outlet, which is the allowable production, no allowance

Jan 1, 1935

By A. H. Geisler, F. Keller

Some of the important changes that take lace in the structure of aluminum alloys are largely submicroscopic in character. This is especially true of the changes that accompany age-hardening and recrys-tallization. Although improved metal-lographic practices have been helpful in indicating some of these changes indirectly, results are limited by the resolving power of optical microscope lenses. The electron microscope, however, provides a new and important means for investigating the fine structure of metals in a range not possible heretofore. It is anticipated that this microscope will yield new and useful information to metallurgists when suitable techniques are developed to utilize its very high resolving power. Several unique methods have been devised to permit the examination of the structure of opaque samples by the electron microscope. These are all based 011 the principle of producing a very thin film that represents the prepared surface of the opaque metal sample, which can be examined in the transmission microscope; however, the available methods fall into three categories, depending on the manner in which the film is obtained. With the oxide-film method developed by Mah13-l7 a very thin surface layer of the metallographic sample is converted into oxide by a thermal, chcmical or anodic treatment. .After removal from the metal sample by one of the special techniques described by Evans,l9 this oxide film is examined in the electron microscope, and is found to portray the structure of the original metal surface. Films formed on aluminum,8,l7 nicke1,7 iron3,8,9 and a nickel-beryllium alloyl1 by heating; films formed on iron8,9 by chemical action; and films formed on aluminum3-&apos;" by anodic oxidation, have been examined. The other two are more recent methods developed principally in this country; they consist in making the thin film in the form of a mold or replica of the surface contour of an etched sample. With the negative replica method the thin film is made directly on the sample; with the positive replica method it is made on a negative reproduction of the sample. With both methods, variations in the contour of the metal sample, caused mainly by etching, produce variations in the thickness of the surface replica. Because of the direct dependence of the amount of scattering of the illuminating electrons upon the thickness of the film penetrated, only the variations in thickness of the replica are responsible for tones in the electron image. Negative replicas are made by forming a thin film of some suitable material directly on the polished and etched metal sample, and derive their name from the fact that after removal from the sample they have the high and low points in the sample reversed, as shown in Fig. I. Nega-

Jan 1, 1944

By F. Keller, A. H. Geisler

Some of the important changes that take lace in the structure of aluminum alloys are largely submicroscopic in character. This is especially true of the changes that accompany age-hardening and recrys-tallization. Although improved metal-lographic practices have been helpful in indicating some of these changes indirectly, results are limited by the resolving power of optical microscope lenses. The electron microscope, however, provides a new and important means for investigating the fine structure of metals in a range not possible heretofore. It is anticipated that this microscope will yield new and useful information to metallurgists when suitable techniques are developed to utilize its very high resolving power. Several unique methods have been devised to permit the examination of the structure of opaque samples by the electron microscope. These are all based 011 the principle of producing a very thin film that represents the prepared surface of the opaque metal sample, which can be examined in the transmission microscope; however, the available methods fall into three categories, depending on the manner in which the film is obtained. With the oxide-film method developed by Mah13-l7 a very thin surface layer of the metallographic sample is converted into oxide by a thermal, chcmical or anodic treatment. .After removal from the metal sample by one of the special techniques described by Evans,l9 this oxide film is examined in the electron microscope, and is found to portray the structure of the original metal surface. Films formed on aluminum,8,l7 nicke1,7 iron3,8,9 and a nickel-beryllium alloyl1 by heating; films formed on iron8,9 by chemical action; and films formed on aluminum3-&apos;" by anodic oxidation, have been examined. The other two are more recent methods developed principally in this country; they consist in making the thin film in the form of a mold or replica of the surface contour of an etched sample. With the negative replica method the thin film is made directly on the sample; with the positive replica method it is made on a negative reproduction of the sample. With both methods, variations in the contour of the metal sample, caused mainly by etching, produce variations in the thickness of the surface replica. Because of the direct dependence of the amount of scattering of the illuminating electrons upon the thickness of the film penetrated, only the variations in thickness of the replica are responsible for tones in the electron image. Negative replicas are made by forming a thin film of some suitable material directly on the polished and etched metal sample, and derive their name from the fact that after removal from the sample they have the high and low points in the sample reversed, as shown in Fig. I. Nega-

Jan 1, 1944

By M. J. Marcinkowski, A. Szirmae, R. M. Fisher

Room -temperature hardness measurements obtained from single and polycrystalline samples of a 47.8 at, pet Cr-Fe alloy which were aged for various times al 500°C show a two-fold increase over that of the unaged alloy after annealing for 1000 hr. A detailed examination of the deformation markings in the neighborhood of the hardness imbressions reveals that twinning becomes an increasingly more important mode of deformation as aging proceeds. this observation is shown to be inconsistent with the Proposals that the transformation is eve of order-disorder On the other hand, the results are in agreement with previous observations of Fisher et al. of a coherent chromium-rich precipitate which forms in an iron-rich matrix as a result of a miscibility gap in this alloy system as proposed by Williams . Using the coherent precipitate hypotlzesis as a model, a detailed analysis of the various possible strengthening contributions to both the slip mid twinning stresses is made. In the case of&apos; slip, lattice friction within the chromium-rich phase and the chemical energy associated with the interface between the two phases contribute about 60pet to the total strength. The contributions from coherency strains and modulus differences are thought to contribute the remaining 40 pet of the strength but are difficult to evaluate because of uncertainties regarding the flexibility of the dislocation line. All of the factors have nearly the same or else a smaller effect on the twinning stress in the aged alloy. Twinning is never observed in the unaged alloy because the twinning stress is much higher- than that for slip. With increased aging times, the various contributions to the total stress for both twinning and slip increase, but most of those for slip increase much more rapidly, so that, in the fully aged alloy, it surpasses the stress for twin propagation. When a twin is nucleated by the chance occurrence of an internal stress concentration during a test, the subsequent twin burst results in a low hardness reading. FeRNTIC Fe-Cr alloys from about 15 to 80 at. pet Cr content show considerable change in properties such as hardness, electrical resistivity, saturation magnetization, and so forth, after aging in the vicinity of 500°C.* The most marked change is a large increase in hardness accompanied by a sharp decrease in ductility, so the phenomenon has often been referred to as the 475°C (885°F) em-brittlement problem. Changes in microstructure are rather subtle and most investigators have not been able to observe any X-ray diffraction or metal-lographic changes during aging. There is little doubt that the phenomenon is inherent to the Fe-Cr binary system and is not directly related to the formation of a phase. Two distinct schools of thought have developed during the past decade concerning this problem. Masumoto, Saito, and sugiharal have concluded, from their own specific-heat measurements, that atomic ordering occurs in this temperature range. Pomey and Bastien2 have also attributed the changes in physical properties with aging in the neighborhood of 500°C to atomic ordering. In addition, Takeda and Nagai3 claimed to have found X-ray verification for superlattices corresponding to the compositions FesCr, FeCr, and FeCr3. However, all known attempts to observe superlattices in Fe-Cr alloys using neutron diffraction, which should be much more sensitive, have been unsuccessful. These have been reported by Shull et al.4 for 25 at. pet Cr, williams5 for 75 at. pet Cr, and Tisinai and samans6 for a 28.5 at. pet Cr. steel. The second and more prevalent opinion ascribes the 475°C embrittlement phenomenon to the formation of a coherent precipitate due to the occurrence of a miscibility gap in the Fe-Cr system below about 550°C. This latter concept was first indicated by the results of Fisher, Dulis, and Carroll,7 who were able to extract fine particles about 200Å in diameter from samples of 28.5 at. pet Cr steels aged from 1 to 3 years at 475°C. The extracted material was found to be nonmagnetic, to have a bee structure with a lattice parameter between that of iron and chromium, and to contain about 80 at. pet Cr. Williams and paxton8 and williams5 confirmed these results and first explicitly proposed the existence of a miscibility gap below the a region in the equilibrium diagram. Alloys aged within this gap

Jan 1, 1964

By P. Shahinian, R. L. Stegman, M. R. Achter

Creep strength has been determined as a function of oxygen pressure for nickel at 510" and 600°C. Creep-rupture life drops from its highest value at the ultimate vacuum of 10-7 torr to a high pressure plateau of nearly constant life which, at 600°C, commences at torr. This behavior is described in terms of a model that relates surface gas adsorption and the generation of fresh crack surfaces. In a calculation based a this model the predicted pressure beyond which the creep strength should not decrease further has been found to agree well with the observed value. The introduction of oxygen during creep in vacuum was found to cause a prompt rise of the creep rate. The magnitude of the environmental effect was much less than generally observed in fatigue and this is attributed to the diffarent crack morphologies in creep and fatigue. GASEOUS environments are known to affect creep resistance adversely1-5 but the effects have received less attention than the much larger ones in fatigue. At low temperatures it has been shown for nickel that the creep rates are faster and the rupture lives are shorter in air than in vacuum and that these environmental effects can be correlated with faster crack growth rates in the reactive environment.&apos; In support of a mechanism of gas adsorption at the crack tip to explain the above effects, a calculation based on kinetic gas theory showed that surface coverage by gas was not as rapid as the exposure of fresh metal at the crack tip in the ultimate vacuum but was in air.7 In fatigue a number of investigations have demonstrated that the reduction of life with gas pressure usually follows a step curve with most of the reduction occurring in a transition range at intermediate pressures and little or no change at high and low pressure.8 There have been no studies, however, in which creep strength has been determined as a function of reactive gas pressure to see whether similar effects would be found. This investigation was undertaken to study the kinetics of the environmental effect in the creep of nickel. EXPERIMENTAL PROCEDURES The environmental creep apparatus was constructed to minimize many of the experimental conditions which can cause scatter in data. Dead weight loading is employed and weights are contained within the environmental chamber to eliminate bellows and the necessity for compensation for gas pressure changes. Elongation over the specimen gage length is recorded from a Riehle Model DV Controlled Environment Extensometer which provides readout to 2.5 x 10- in. Temperature is monitored and controlled from a thermocouple at- tached to the specimen gage length to +0.5oC or better. The freon trapped oil diffusion pump vacuum system included an auxiliary liquid nitrogen trap and, with a wide range variable conductance leak valve, pressures from the ultimate vacuum of 10"7 to l03 torr of any desired gas are obtainable. Pressure is measured by means of a hot filament ionization gage below 10"3 torr and a NRC Model 530 Alphatron Vacuum Gauge above 10-3 torr. The oxygen, which was leaked into the environmental chamber, was an Aviator&apos;s Grade of 99.5 pct purity with a dew point of -80°F. Analysis of the nominal 99.8 pct Ni showed the following percentages of major impurities: 0.02 C, 4.01 Mn, 0.005 Si, 0.01 Cu, 0.02 Fe, and 0.034 Mg. Cylindrical specimens were machined with a 0.180

Jan 1, 1970

By Robert Roberts

(Butte Meeting, August, 1913.) In order to obtain data on the thermal effect of the blast-furnace jacket and on the water consumption in these jackets a series of tests were run on the 56 by 180 in. blast furnaces at the Great Falls Reduction Department of the Anaconda Copper Mining Co., at Great Falls, Mont. The arrangement of the jacket is shown in the transverse section of one of the furnaces (Fig. 1) on which the tests were made. The nose, spout, and breast jackets have independent water supplies and discharges. The end and side jackets are connected in pairs, as regards water supply, the feed water entering at the bottom of the lower jacket and overflowing into the bottom of the jacket immediately above it, and discharging into an independent overflow pipe for each pair of jackets. Tests were run on the main side and end jackets, the breast jacket, the spout, and the nose. Measurements were taken of the quantity of water discharged, per minute and the rise in temperature of the water in its passage through the jacket. The product of these two results, expressed in the proper units, evidently gives the number of units of heat removed per minute by the water. Sufficient work was done on each type of jacket to determine its behavior under different conditions, and the results from each set of conditions were checked by repeating the work from three to six times. The method used was as follows : The overflow from the jacket to be tested was arranged to discharge at will into a barrel, mounted upon platform scales. The discharge temperature was read just before turning the water into the barrel, and just before turning it back to the sluice; if the test lasted more than a minute, additional temperature readings were taken at 1-min. intervals from start to finish. The elapsed time of running the water into the barrel was, determined with a stop-watch, and this figure, combined with the in-

Jan 7, 1913

By G. T. Hahn, C. N. Reid, A. Gilbert

An evaluation is made of the possible cautsal relationship between twinning and fracture in molybdenum. For both single and poly crystalline material no instance of twin-induced fracture was observed. Instead brittle fracture was found to be slip-induced at heterogeneities. For single-crystal material, the yield stvess in compression and the fracture stvess in tensiow obey a similar angular- relationship which follows approximately a 1/cos2 ? law. where 0 is the angle between the specimen axis and the nearest (100) plane. This sittlilarity between yield and fracture behavior casts doubt on the interpretations made previoltsly that a 1/cos2? relationship supports a critical normal fracture stress criterion. SINCE fracture in brittle materials takes place at stresses an order of magnitude lower than the theoretical strength of the lattice, it must be postulated that some stress-concentrating effect is operative during the fracture-initiation process. Several mechanisms have been proposed whereby the necessary stress concentrations could be produced. The well-known Cottrell mechanism1 describes a dislocation interaction which can lead to the formation of an incipient cleavage crack on a cleavage plane, and both zener2 and stroh3 have discussed models which predict the stress concentration at the intersection of a slip band with a grain boundary. When twinning occurs twin/twin intersections and twin/grain boundary intersections represent another possible means of fracture initiation. Although still controversial, the concept of twin-induced fracture is supported by a weighty mass of evidence, which has been reviewed in a recent paper.4 This investigation was conducted in order to assess the extent to which the brittleness of molybdenum can be ascribed to this cause. Emphasis was placed on seeking direct metallographic evidence for twin-induced fracture such as arrangements of twins located at the fracture origin. EXPERIMENTAL PROGRAM Materials. The experimental materials are described inTable I. From the chemical analyses and estimates of the amounts of interstitials likely to be retained in solution,5 it is concluded that all were mul-tiphased systems. X-ray diffraction experiments6 showed no evidence of preferred orientation in the polycrystalline materials. Single crystals were grown from Molybdenum X and Y using the floating-zone technique,&apos; in a vacuum of better than 3 x 10-5 Torr. However difficulties were experienced with Molybdenum X due to violent gas evolution from the molten zone, and additional crystals (Crystals 3 to 6) were produced by annealing for 5 1/2 hr at 2300°C under a vacuum of 10-4 Torr. Techniques. A series of tension, compression, and bend tests was conducted. Tension tests were used to demonstrate brittle behavior, to measure brittle-fracture stresses, and to provide fractured specimens for metallographic inspection. Compression tests were employed in order to obtain some ductility and a measure of the yield stress. Furthermore, it was considered that compression loading would permit the study of crack nucleation in the absence of propagation. The bend tests were conducted to facilitate identification of the fracture origin, which would be expected to be at, or near, the tensile surface of the sample. Tests were carried out at temperatures between 78" and 298°K attained by means of a liquid-nitrogen evaporator of modified Wessel design.&apos; Specimens were fashioned by mechanical grinding, and, prior to heat treatment, were electropolished at 10 v in a 3:l mixture of ethyl alcohol and sulfuric acid, using a stainless-steel cathode. Except where noted, a strain rate of 4 pct per min was used. All specimens had a gage section 0.75 in. long; diameters of 0.10 and 0.20 in. were adopted for the tension and compression specimens, respectively, the former of single shoulder design, the ends being gripped in split collets with a conical bearing surface. In the bend test, electropolished specimens measuring 0.080 by 0.25 by 1.25 in. were deformed at 78°K by four-point loading. The bending device had spans of 1 in. between the outer and 4 in between the inner fulcra; it was stressed between the compression anvils of the Instron machine at a constant deflection rate. EXPERIMENTAL RESULTS Polycrystals. Tension and Compression Tcsls. It is apparent from Fig. 1(a) that above 170°K fracture of Molybdenum X takes place at stresses equal to or greater than the compressive yield stress whereas

Jan 1, 1967