By T. Egleston

The materials containing copper which are refined in the United Statrs, are, for the most part, the natiye noppers of Lake Superior. IJntil quite recently but little pig copper Was made for sale, and that came principally from the pure sulphorous ores of New England and the Sonth, and was generally sdd to reSneries not far from the ore filrnaceu. A stnall aiuoiint found its way into the'niarket which was produced either as the by-product of the treatment of gold and silver ores, or as the result of the treatment of impure copper ores; but both these grades, on account of the impurities they contained, were loolced on with stlspicion, and were not sought for. A11 the grtlGis of pig coppcr are sold by the unit of oopper contents, a great redtiction being made in the price when impurities are present. There are at the present time only three works which treat native copper, the two of the Detroit and Lake Superior copper Company, and the works of C:G. Hussey & Co., in Pittsburgh. There are a few works ivhich smelt sulphuroris ores and refine their pig; bo sides these t1le1-e arc a few siuall works where gig copper is refined uuly. Some of these purcIlase blscir copper, refine scrap, or simply refine such grades of ingot copper as are found in the market, but nlostly that from Lake Superior, for the purpose of getting it into swh shapes that can be handled cpmtriercially to advantage, such as in making large plates or high grades of wire fir electrical purposes. A nomher of such works are situated in the Xaugaturk Vatley aud elsewhcre in New England. The recent discoveryof vnlt~sblc ores in Ariarona makm it probable that within a few year8 the refining of capper In the United States will make great develupments. Up to the time of the discovery of the mines on Lake Superior, only a very small quantity of native copper had ever been foond, not sufficient to justify the erection of worlrs fbr its special treatment. It had, besides, never been found in very large maweq so that the discovery of greabblocks of it presented serious difficulties, not oolp in mining it,-I- but in bringing it into a merchantable condit'ion. It seemed a very simple process to melt these large maws,

Jan 1, 1881

By S. Skowronski

OvErpolEd copper, as commonly defined,- is copper which has been excessively reduced during the poling period of the refining process. Owing to its porosity, such coppcr is unfit for commercial purposes. The cause of this phenomenon is undoubtedly the lack of oxides in the copper, yet this does not completely explain it. Refined copper of the same "pitch" and "set" varies considerably in oxygen contents, and analyses of overpoled bars also show similar wide differences; moreover, it is possible to melt copper in 'crucibles so as to obtain bars that are practically free from oxygen although they show a "tough pitch" and "level set" surface. Frederick Johnson advances the following theory: The regulation of the quantity of oxygen in copper is the keynote of all copper refining. It is the presence of a well defined proportion of oxygen in the form of cuprous oxide, forming a copper-cuprous oxide eutectic, which enablcs copper to be cast free from blowholes. It seems that when oxygen is present, other gases are less soluble in molten copper; when oxygen is absent, or is present in insufficient quantity, the copper dissolves other gases, such as hydrogen and carbon monoxide, which are insoluble in the copper when solid, and, being rejected during the process of solidification, causes internal porosity and external ridges and excrescences.1 The "level set" of wire bars, etc., is entirely the result of a compromise between the occluded gases and cuprous oxide. With excess of the former the metal would be "overpitch" and spongy, while an excess of the latter would result in the metal being "underpitch" and brittle.2 The result of the absorption and subsequent expulsion of reducing gases, carbon monoxide and hydrogen,' and the effect of this action on the overpoling of copper are in dispute; the literature on the subject is full of contradictory statements and will continue to be so until better analytical methods have been developed. Sulfur, however, is tangible. The refiner can see it in his button sample and consequently attributes to it any trouble that may happen during the melting of the copper.

Jan 1, 1919

By J. S. Bryner

INTRODUCTION IN the study of metallographic specimens in the electron microscope, there is need for a method of locating the same field in both the light microscope and the electron microscope. This need arises chiefly from the fact that in the electron microscope the magnification and degree of resolution are so much higher, and the field so much smaller than in the light microscope that it is often difficult, if not impossible, to identify positively what is being observed. The difficulty is increased by the fact that, because a transparent film replica of the metal surface must be used in the electron microscope, micro-constituents can be identified not by their color but only by their texture and contours. For these reasons it is desirable to obtain a series of photographs showing the same field in both microscopes in order that the appearance of common microstructures and micro-constituents in the electron microscope may be identified and catalogued for future reference. The need for a method of locating the same field in both microscopes arises also when it becomes desirable to enlarge in the electron microscope for more detailed study a particular interesting structure observed in the light microscope. Using the standard polystyrene-silica1,2 replica technique, in which the silica film replica is fished from the ethyl bromide on a 1/3 in. diam 200-mesh specimen screen, the possibilities of locating a particular area on the film in the electron microscope are rather remote. The desired structure may be obscured by the wires of the specimen screen or unrecognizable at the high magnification. A solution to the problem would be provided if a specially designed specimen screen, containing an opening which could be absolutely identified and quickly located in the electron microscope, could be fastened to the silica film replica in such a position that the desired field on the specimen would be located at the identifiable opening in the specimen screen. The design for such a specimen screen, a method for producing it, and a technique for fastening it to the silica film replica are described below. DESCRIPTION OF METHOD The Specimen Screen A simple design for a specimen screen containing an opening easy to identify and locate in the electron microscope is one with two lines of openings at right angles in the form of a cross. Such a screen is shown in Fig I. The opening at the center of the cross is identified easily and can be located quickly in the light microscope and in the objective image of the electron microscope. The specially designed specimen screens for this work were produced in quantity by electroforming. On both sides of a polished strip of copper 1 X 3 X 1/8 in., twenty patterns of the cross of openings were punched with a diamond point micro-hardness tester, using a load of magnitude

Jan 1, 1948

By Richard A. Arnold

The evolution of planning processes in the United States from the early 1900's is briefly examined. From one year operating budgets, planning processes have evolved into sophisticated analyses of alternative long-term future strategies and the management issues and practices which relate to their implementation. Increasing complexity within the business environment has led to numerous planning methodologies and extensive use of computers to analyze operating and financial information. All of these developments, however, have not supplanted the real need for decision-makers to continue to give important weight to the intuitive or soft data inputs into the planning process.

Jan 1, 1985

By M. Allingham

This paper examines the contribution which econometric methods may be expected to make to the specification of commodity agreements, and how in turn computer methods may help in this. Starting from the specification of a model, the paper examines four activities: estimation of the unknown parameters; analysis of the properties of the model; simulation experiments with the model; and control of the model. In each of these activities the basic methodology is outlined, and the contribution of computer methods assessed.

Jan 1, 1977

By Laurence Delisle, Aaron Finger

THE alloys formed by the addition of nickel to iron by convelltional metallurgical procedures show physical properties that differ widely from those of the individual metals. The effect of alloying on the mechanical properties is most pronounced in alloys containing between 15 and 25 per cent nickel. The tensile strength of an alloy containing, for example, 20 per cent nickel and 80 per cent iron (with 0.06 per cent carbon), in an annealed condition, is above 150,000 lb. per sq. in.? owing to a martensitic type of transformation, as compared with about 50,000 lb. per sq. in. for pure iron in the same condition. The object of this work was to determine whether the same beneficial alloying effect could be obtained in alloys of iron and nickel prepared by powder metallurgy technique. PROCEDURE Bars and pellets for tension and compression tests, respectively, were made. Two groups of specimens were prepared: (I) by cold-pressing the powders and sintering; (2) by cold-pressing the powders, sintering, repressing and resintering. Raw Materials Nickel powder supplied by Metals Disintegrating co., marked MD-151, was used. A typical analysis of this powder was as follows: sulphur, 0.040 per cent; copper, 0.18; iron, 0.23; manganese, 0.002; magnesium, 0.001 5 ; lead, 0.035; tin, 0.025 ; silicon, 0.08; chromium, 0.008. Electrolytic iron powder supplied by Plastic Metals Inc. was used. A representative chemical analysis for impurities other than gases, supplied by the vendor, gave the following results: carbon, 0.005 per cent; manganese, 0.002; silicon, 0.003; phosphorus, 0.001; sulphur, 0.004; nickel, 0.008. The fractions from these powders passing a 3 2 5-mesh sieve were reduced in hydrogen at 600°C. for one hour, to clean the surfaces of the particles. The reduced powders, slightly caked, were ground in a mortar and screened again through a 325- mesh sieve. Mixing The proper proportions of the powders were mixed overnight on rolls, in glass jars fitted with iron-wire baffles to break aggregates of particles that might form. Pressing All specimens were compacted on hydraulic presses. The pellets were compacted in a cylindrical die, ½ in. diameter. The ratio of thickness to the diameter of the pellets was maintained as nearly as possible at 0.9, as specifed for standard short compression pieces. The tensile bars were made by compacting 30 grams of powder. Their shape is shown in Fig. I. The compacting pressures for the pellets and the tensile bars were:

Jan 1, 1946

By A. Sutulov

The segregation process, an alternative to benefi-ciation of oxidized and mixed sulfide-oxide copper ores, is studied here with particular emphasis placed on time, temperature, and coke and salt percentage factors. The results show that in a segregated charge, the copper assay of the coarsest fractions normally is of the same order as the copper assay of the tails obtained from grinding and flotation of the same charge. This observation suggests the possibility of limiting or even eliminating the grinding step from the flowsheet of a segregation plant. The segregation process, which offers an alternative to beneficiation of oxidized and mixed sulfide-oxide copper ores, was discovered in 1923 by Moulden and Taplin1,2 who were attempting to apply the Perkins process3'4 to a Chilean ore from the Sagasca mine. After a number of investigations and pilot plant tests,'-' the segregation process became a successful industrial operation.'r9 The process aroused considerable interest in Chile because of the existance of large reserves of oxidized copper minerals which could not be treated by conventional hydrometallurgical methods because of the high consumption and prohibitive cost of sulfuric acid. During the last two years, the Mineral Dressing Dept. of the Institute de Investigaciones Tecnology cas of University of concepci6n (Chile) has carried out a test program on 23 different ore samples representative of the national territory. These tests were carried out on a semi-continuous and batch scale with a rotary, automatically controlled and gas-fired furnace (supplied by Bartlett and Snow, Fig. 1). The results of these tests indicate that out of the 23 samples 20 can be successfully treated by this process with recoveries of copper ranging from 85 to 95%.10,11 The purpose of this paper is to treat some specific problems related to the segregation process. TIME AND TEMPERATURE FACTORS Time and temperature of calcination play an important role in the segregation process. When moderate salt and coke conditions were maintained (each of reagents was added in the quantity of 1 — % wt), systematic testing easily demonstrated the influence of these two factors on segregation and flotation recovery. The pertinent results are summarized in Fig. 2. To determine what specific changes the segregation process made on the ore, the samples, segregated at 700°C for different periods of time and under standard conditions, were granulometrically analysed and

Jan 1, 1963

By R. E. Shinkosk

This paper outlines the development of a program for increasing the life of woolen bags used for filtering Dwight-Lloyd gases by treating the bags and gases with hydrated lime. Methods and apparatus are described for determining alkalinity of dusts, acidity and breaking strength of bag cloth. Procedure and results, based on several years of operation, are presented. DURING 1939, additional facilities were constructed in the Dwight-Lloyd Blast Furnace and Baghouse departments at the Selby, California, Plant of the American Smelting and Refining Co. In order to handle adequately the increased volume of gases from the resultant increase in production, it was necessary to increase gradually the amount of water used for cooling gases ahead of the sinter machine baghouse. As a result of this increased water cooling, the average bag life dropped from 27 months in 1939 to 14 months in 1941. (Table I). This drop in life meant an increased. bag cost, as well as lower recovery of dust and some curtailment of operation. During 1941, it was found new bags showed as high as 0.3 pct acidity* after two weeks of opera- tion and as much as 2.0 pct acidity after some months of operation. This high acidity was present in spite of the fact that free oxide or relative alkalinity of the unburned dust ran from 5 to 6 pct. In view of these circumstances, a twofold program was started in Nov. 1941.t Part one of this program consisted of vigorously dipping all new bags in a weak lime solution, containing 50 lb of hydrated lime per 50 gal of water. Part two consisted of feeding fine, dry, hydrated lime into the gas stream intake of the sinter baghouse fan. Apparatus for feeding this lime is shown in fig. 1. All baghouse chambers are shaken in rotation about once each hour. On alternate hours, the baghouse operator places 50 lb of hydrated lime (one sack) into the lime feeder, starts feeder and immediately starts the bag shaking machinery. The rate at which lime is fed is set to coincide with the approximate time necessary to shake all sinter bag-house chambers, or about 15 min. It is felt this method of lime addition is most effective for getting lime into the woolen bag fabric. The amount of lime so fed averages about 600 lb per day. The amount of lime fed per day is varied to keep a minimum relative alkalinity of 9 pct in the unburned sinter dust. A daily dust sample is taken for alkalinity by allowing dust to accumulate in a sample pipe over a 24-hr period. This sample pipe, placed in any chamber cellar, is 2 in. in diam, 4 ft long, is sealed on the inner end, and capped on the outer end. It has a 1/2 in. slot cut for 18 in. along the tip end. This slot faces upward and allows the pipe to fill gradually with dust as bags are shaken. Breaking strength of bags has, in most cases, been the deciding factor in bag replacement. Bags that normally test 100 psi breaking strength when new are replaced when they test under 35 lb. The method for determining breaking strength is shown in the description accompanying fig. 2. Since the start of the liming program in 1941, bag life has increased from 14 months to an average of over 23 months, with a consequent material decrease in bag cost per year. Acidity, as per cent sulphuric acid, may be determined by means of a Beckman pH meter as follows: From a piece of bag cloth. which has been thoroughly cleaned of dust, a 5 g sample is weighed on a balance. Cut the sample into fine pieces and place in a 400 cc beaker. Add 100 cc (measured) of distilled water and stir vigorously. Filter on suction funnel, holding cloth pulp in beaker with a stirring rod. Wash cloth sample and filter wash water four additional times, each time with 20 cc distilled water, the last time squeezing cloth pulp over funnel. Discard pulp and rinse funnel and filter paper. Pour wash solution jnto measuring graduate and make up to exactly 300 cc with distilled water. Place into clean 600 cc beaker and measure the pH on meter. The per cent acid in bag cloth is read from the following table:—

Jan 1, 1951

By R. V. Norris

The anthracite coal trade, with a shipment averaging about 70,000,000 tons per year, differs essentially from other coal business, iii the fact that the larger sizes, comprising about 65 per cent. of the total, are used almost exclusively for domestic purposes, principally during the winter months; and that for proper combustion close-sizing is imperative, so that eight sizes are made; broken, egg, stove, and nut, known as prepared sizes, and pea, buckwheat, rice, and barley, known as steam sizes. These sizes are made in the regular course of preparation, and but little variation in the natural percentage of each is practicable. Thus it is necessary either to work the collieries intermittently, or to dispose of all the varying sizes in their fixed proportions. Unfortunately, the market does not at all times absorb the coal in proper proportions, and rather than interfere with the regular operation of the mines it has been found economical to provide storage for the excess. While the cellars of' the consumers are the great storage-plants of the country, this capacity is not under the control of the trade, except so far as reduced prices during the spring and summer months may tempt the use of this reserve. The same remark applies but with less force to the retail yards, which, though usually small, store in the aggregate a large amount of anthracite. While every effort is made to utilize to the utmost the individual storage-capacity of the country, there still remains the necessity for taking care of the irregularities of the market by the construction of storage-plants under the direct control of the producers. Such plants are usually the property of the railroads, and are situated at points most convenient from a traffic stand-point.

Jan 1, 1912

By L. C. Brown, J. S. Kirkaldy

AS part of a program to investigate the diffusive properties of dilute ternary austenites, we have made a determination of the effects of cobalt on the activity of carbon in y iron. Samples of pure iron and Fe-Co alloys were equilibrated at 1000°C in controlled CO-C02 atmospheres, following the procedure of R. P. smith.' The 0.010-in.-thick samples were analyzed for carbon by microcombustion analysis2 to give a set of isoactivity curves. The latter were converted to activity-coefficient (standard state at infinite dilution) plots by combination with Smith's data' for the activity of carbon in pure iron measured in a CO-C02 mixture. Table I shows the composition of the base alloys used, while Fig. 1 shows the experimental results superimposed on a set of curves generated by the relation In the notation of Wagner,' the interaction parameter is the second coefficient on the right, Eq. [I] adequately correlates the experimental points for those alloys which were prepared from electrolytic iron by arc-melting (2,4, and 7 pct Co). The results for the 10 pct Co alloy (supplied by Crucible Steel Co.) do not correlate with the others. In fact, the experimental points for this alloy correspond to an interaction parameter of It is possible that the interaction parameter is a function of concentration for large cobalt additions, but we are inclined to attribute the discrepancy to the presence of a significant amount of aluminum added to this alloy for deoxidation purposes (Table I). Preliminary measurements for the system Fe-C-A1 have indicated an interaction parameter of Which implies that the effect of aluminum in solution on the carbon activity is sixty times greater than the effect of an equal weight percentage of cobalt. These observations cast some doubt on the precision of the results of Chandhok, Hirth, and Dulis who used this same 10 pct alloy for their experiments, obtaining an interaction parameter of E = 2.2. There is considerable doubt as to the activity of a plane Fe-C system. Using a CH4-Ha mixture, Smith obtains cg = 6.1 for the effect of carbon on the activity of carbon in austenite, rather than the value of 8.9 given in Eq. [I]. The use of CHa-Ha mixtures has recently been questioned by Kaufman, Radcliff, and cohens who state that there is some possibility that other hydrocarbons are formed. Fortunately, the determination of the interaction parameter is not sensitive to the coefficient of Nc. For example, using the CHI-H2 results we obtain a value which is almost the same as that obtained using the CO-CO, results. The authors wish to thank Mr. E. J. Dulis of the Crucible Steel Co. of America for supplying us with samples of the 10 pct Co alloy used in their original work. Financial assistance from the American Iron and Steel Institute is gratefully acknowledged.

Jan 1, 1963

By F. H. McDowell

The electro-magnetic separator of Mr. G. Conkling, Glens Falls, N. Y., described by Mr. Birkinbine* in a paper at the New York meeting of the Institute, in February, 1889, has been in successful operation at the Tilly Foster 'mine for a considerable period, under the disadvantages which seem to be the inevitable attendants of pioneer enterprises in new technical fields. The results of a run of several months, which the Superintendent, Mr. S. P. Tomkins, has taken pains to collate, are here presented by his courteous permission, and that of Mr. E. S. Moffat, the energetic and skilful General Manager of the Lackawanna Iron and Coal Company, to whom our profession is already indebted for examples of bold and ingenious practice in mine-engineering. It is believed that these figures will assist those who are planning similar operations to decide intelligently what they may, and, more important still, what they may not, expect to accomplish. The local difficulties in the way of this experiment at the Tilly Foster mine were many and great. Only about two-thirds of the waste-dump, resulting from the assorting of previous years, is ore; and this varies in content of iron from 20 to 28 per cent. The remainder is rock, some (from horses in the vein) showing particles of adhering mineral, some (from the foot- and hanging-walls) entirely barren. The expense of overhauling the dump and removing this rock is by no means the least of the numerous items which must be charged against the concentration. Associated with the lean ore are hornblende and other minerals, carrying iron in the non-magnetic state, which must necessarily be washed away with the tailings. The waste-dump was originally located without reference to future treatment, and now can only be handled by means of a locomotive,

Jan 1, 1891

By J. H. Frye, C. P. Sun

A Frimary substitutional solid solution is a solution that has the same crystalline structure as the solvent metal, and in which solute atoms have replaced, solvent atoms at random on the host lattice. This replacement usually results in an increase in hardness as measured by conventional penetration tests. The factors controlling this hardness increase have been investigated in some detail for copper and silver alloys.1-5 It has been shown that at least four factors are involved: (1) concentration of solute, (2) row of the periodic table from which the solute is taken, (3) increase in lattice parameter of the solvent produced by the solute, and (4) work-hardening produced by penetration of the hardness indenter.2,4 The last factor is of the utmost importance. An investigation of the available data2,4 leads to the conclusion that the solutes that produce large hardness increases in copper or silver do so principally because they increase the rate of work-hardening. Furthermore, it is doubtful whether any solute produces appreciable hardening in the absence of plastic deformation and hence work-hardening. Thus it is clear that an understanding of the effect of solutes on rate of work-hardening is essential to an understanding of the hardness of solid solutions. This effect of solutes is also important in forming operations such as rolling or deep drawing. The presence of elements that confer rapid rates of work-hardening will increase power consumption and may well decrease the amount of deformation possible between anneals. This paper is the report of an investigation of the factors that control rates of work-hardening in copper and silver solid solutions. The silver and copper alloys considered are those in which all solutes are from the B subgroups or second short period of the periodic table. Experience with hardness, with structure of alloys, and with electrical conductivity has proved that results of a fundamental nature are most likely to be obtained if alloys are made up on the basis of the positions of the constituent elements in the periodic table. In previous work, Meyer analysis data on high-purity copper and silver solid solutions were obtained through careful measurements with fully calibrated equipment and these data were corrected to correspond to a standard grain size. From these corrected Meyer analysis data rates of work-hardening have now been calculated. Calculation of Rates as Work- HARDENING The Meyer analyses, on which this study of rates of work-hardening is based, consisted in determining impression

Jan 1, 1944

By J. H. Frye, C. P. Sun

A Frimary substitutional solid solution is a solution that has the same crystalline structure as the solvent metal, and in which solute atoms have replaced, solvent atoms at random on the host lattice. This replacement usually results in an increase in hardness as measured by conventional penetration tests. The factors controlling this hardness increase have been investigated in some detail for copper and silver alloys.1-5 It has been shown that at least four factors are involved: (1) concentration of solute, (2) row of the periodic table from which the solute is taken, (3) increase in lattice parameter of the solvent produced by the solute, and (4) work-hardening produced by penetration of the hardness indenter.2,4 The last factor is of the utmost importance. An investigation of the available data2,4 leads to the conclusion that the solutes that produce large hardness increases in copper or silver do so principally because they increase the rate of work-hardening. Furthermore, it is doubtful whether any solute produces appreciable hardening in the absence of plastic deformation and hence work-hardening. Thus it is clear that an understanding of the effect of solutes on rate of work-hardening is essential to an understanding of the hardness of solid solutions. This effect of solutes is also important in forming operations such as rolling or deep drawing. The presence of elements that confer rapid rates of work-hardening will increase power consumption and may well decrease the amount of deformation possible between anneals. This paper is the report of an investigation of the factors that control rates of work-hardening in copper and silver solid solutions. The silver and copper alloys considered are those in which all solutes are from the B subgroups or second short period of the periodic table. Experience with hardness, with structure of alloys, and with electrical conductivity has proved that results of a fundamental nature are most likely to be obtained if alloys are made up on the basis of the positions of the constituent elements in the periodic table. In previous work, Meyer analysis data on high-purity copper and silver solid solutions were obtained through careful measurements with fully calibrated equipment and these data were corrected to correspond to a standard grain size. From these corrected Meyer analysis data rates of work-hardening have now been calculated. Calculation of Rates as Work- HARDENING The Meyer analyses, on which this study of rates of work-hardening is based, consisted in determining impression

Jan 1, 1944

By C. DeWitt Smith

"It just looks like everything is doing fine but humans," wrote Will Rogers fifty years ago. "Animals are having a great year, grass was never higher, flowers were never more in bloom, trees are throwing out an abundance of shade for us to loaf under. Everything the Lord has a hand in is going great, but the minute you notice anything that is in any way under the supervision of man, why, it's cockeyed." Do these words from two generations ago apply to oil shale? The United States has been blessed with deposits that can yield synthetic crude oil at a cost competitive with natural crude oil-under present economic conditions and with existing technology. Yet, the oil shale program is cockeyed because of the artificial obstacles that have been placed in its path "under the supervision of man." But more about this later. For the moment, let's focus on...

Jan 10, 1974

By Alvin W. Schillinger

During the past ten years, the Calumet Div. of Calumet & Hecla, Inc. has conducted extensive exploration and mining in the footwall of the Osceola amygdaloid lode in the native copper district in Michigan's Upper Peninsula. In an attempt to delineate more clearly the extent and nature of high-grade footwall copper mineralization, 876 diamond drill and long steel holes aggregating slightly more than 47,000 ft have thus far been drilled from the accessible hanging-wall workings. Early in this program it became obvious, through inspection of footwall workings in progress, that due to the erratic and bunchy occurrence of the native copper in the footwall zone, the exploration drilling was failing to outline completely the extent of the oreshoots. Early drilling results indicated isolated pockets of ore whereas in actual practice the footwall was found to be fairly thoroughly mineralized in shoots within the ore zone. Based on drill results only, the "success factor" (discovery ratio) was only 34%.

Jan 11, 1964

By J. M. Gaines, C. H. Herty

It is a matter of frequent record in the literature that manganese will desulfurize molten iron under proper conditions. Particularly has much been written with regard to this action in the mixer, and numerous reports have been published describing experiments in which advantage was taken of this phenomenon in order to obtain a purer iron for the open hearth. The question of sulfur elimination in the ladle has, however, received comparatively little attention. The reaction by which sulfur is removed is considered to be: FeS + Mn = MnS + Fe. The manganese sulfide, being but sparingly soluble in the iron, and of a lower density, will rise from the body of the metal and collect as a slag on the surface. It is therefore an action taking place solely in the metal, and independent of interaction between slag and metal. As will be shown later the presence of slag on the metal tends to offset the effect of manganese elimination. It is this fact which distinguishes desulfuriza-tion in the ladle from desulfurization in the mixer, for it has been shown1 that the amount of sulfur eliminated in the mixer is closely tied up with the composition of the slag. Experimental Procedure In order to ascertain the extent of and the factors controlling this elimination in the ladle, several casts were sampled carefully at the blast furnace and again when the ladles were being emptied, either at the mixer, open hearth, or foundry. If the sulfur content varied from ladle to ladle at the blast furnace the average sulfur content of each ladle was obtained by integrating the curve "sulfur vs. time " for the cast under

Jan 1, 1927

By R. L. Smith, I. G. Greenfield

The binary system Ga-Sb has been investigated by thermal, X-ray, and metallo-graphic methods. 'The intermetallic compound GaSb melts at 705.9OC and forms a eutectic with antimony at 11.8 atomic pct Ga. This eutectic melts at 589.8OC. A eutectic appears to be formed at 29.8°C but is too close to the composition of pure gallium to be detected. IN the course of an investigation of the semiconducting properties of the intermetallic compound, GaSb, the phase equilibrium between gallium and antimony has been investigated. Recently, the phase diagram of similar systems, such as In-Sb,' In-AS,' and Bi-As3 have been determined. These diagrams have the same general appearance in that an intermetallic compound is formed at 50 atomic pct and a eutectic is formed on both sides of the intermetallic compound. Jenny,& who has been investigating the semiconducting properties of intermetallic compounds, has concluded from thermal data of several alloys that the phase diagram of the Ga-Sb system resembles those mentioned previously. This paper represents a more detailed study of the Ga-Sb equilibrium. Experimental Procedure The gallium that was used to prepare the alloys was obtained from A. D. Mackay Inc. and the Aluminum Co. of America; the latter reported the purity as 99.95 pct. The antimony was obtained from Bradley Mining Corp. who specified a purity of 99.997 pct. Since the intermetallic compound of GaSb was prepared primarily to be used for further studies of the semiconducting properties, additional purification by a standard zone-melting technique under an atmosphere of hydrogen was performed. Hall-effect measurements on this material indicated an impurity content of less than 3 ppm.5 The antimony also was purified by zone melting and used in conjunction with the compound GaSb to make the necessary alloys for the determinations of the antimony-rich side of the phase diagram. The antimony-rich alloys were chill cast in Vycor tubes which were evacuated to a pressure of less than one micron. Since these alloys expand on freezing, precautions were taken to prevent oxidation of the ingot in the event the tube fractured. To insure homogeneity, the brittle alloys were ground and then placed in the furnace for the thermal-arrest determinations. Since the cost of gallium is high, the experimental procedure was complicated somewhat because of the necessarily limited sizes of the melts. In order to economize, the gallium-rich side of the diagram was determined by using a 35 g ingot of pure gallium initially and adding increasing amounts of antimony in order to obtain additional alloys. The furnace used in the determination of the cooling curves is illustrated in Fig. 1. A 2¼ in. quartz tube, sealed at one end, was fitted with a brass flange which was attached with DeKhotinsky cement. The brass collar was water cooled to prevent the cement from softening. An "0" ring was used to provide a seal between the brass collar and the furnace cover. Nichrome ribbon was wound around a 2 ½ in. asbestos-covered copper core which was used to reduce the thermal gradient in the furnace. The insulation consisted of alternate layers of asbestos and aluminum foil surrounded by sil-o-cel refractory and

Jan 1, 1956

By H. D. Merchant

NUMEROUS publications have examined hot hardness of metals and alloys. Some have studied creep in long-time hardness tests, few of which, however, were tested under a spherical indentor. 1-3 The results of Mulhearn and Tabor' indicate a parabolic-type creep for indium and lead, whereas Moore and Tabor2 how a logarithmic-type creep for indium. Similar semilog relationships between hardness and time have been found by Goffard and wheeler3 for magnesium, aluminum, and their alloys. In this note, the elevated-temperature hardness of some complex alloys, shown in Table I, was examined to discover whether any basic information about the deformation behavior of the alloys could be obtained. One of the alloys, H-13 alloy steel, was tested for short-time creep tests to examine the hardness-time relationship at various temperatures. A standard Brinell Hardness Tester, mounted with an appropriate furnace and 99 pct A12O3 poly-crystalline indentor, was employed for the purpose. The alloys were tested at temperatures from room to 1400°F for 30 sec under 1500-kg load. The creep studies were conducted for about 8500 sec at 7l°, 500°, 1000°, and 1200°F. For constants A and B, a relationship of the type H = Aexp(-BT) [ll was obtained for all alloys between hardness, H, and temperature, T. In the semilogarithmic plot, the data points for each alloy were arranged into two groups, each group on a straight line with a specific set of A and B values. These results are in agreement with many such observations on hot hardness, notably those of Westbrook for pure metals,4 The thermal softening coefficient, B, and transition temperature, Tt, for various alloys are shown in Table I. The change in slope around the transition temperature suggests an apparent change in the mechanism of deformation, probably from the shear (below Tt) to the diffusion type of mechanism. At the temperatures above Tt, for constants A' and B, a relationship of the type was obtained between H and T, Fig. 1. The nature of the equation, where R is gas constant, suggests the possibility of a thermally activated mechanism of deformation above Tt. The constant B' may hence be defined as the apparent activation energy of indentation. The B' values of various alloys are shown in Table I. A plot of B vs B' gives a curvilinear relation shown in Fig. 2. The indentation-creep data for H-13 alloy steel is shown in Fig. 3. At 71" and 500°F, the creep initially follows the logarithmic time law. However, the indentation size stabilizes after 7 sec at 71°F, and after 10 sec at 500°F. Further increase in loading time has no effect on indentation size. The creep of 1000° and 1200°F follows the logarithmic time law for the first 1000 sec, after which the

Jan 1, 1964

By G. P. Boomslitter

In previous discussions on stresses in hoisting ropes, little has been said concerning the effect of the elasticity of the rope itself on the stresses due to acceleration. Laschinger1 has calculated acceleration stresses for several cases but he has ignored the elasticity of the rope as a factor, except as it compresses the drum and stretches itself as it winds thereon. He also deals with steam plants and he shows the effect of the "jerky" start of the engine. This effect would actually be reduced by the elasticity of the cable. With the advent of the motor-driven hoist, new conditions have arisen. The jerk mentioned by Laschinger has been eliminated and smoother starting made possible. But the elastic properties of the rope seem to introduce considerable periodic acceleration stresses in the rope. The following discussion of acceleration stresses is based on the assumption of a constant acceleration at the drum. To be exact, the mathematical work is based upon the assumption that the top is moving upward with a constant acceleration, and ignores the fact that the cable is shortening as it winds. However, the effect of the shortening would be inconsiderable during the first part of the acceleration period. Most hoisting engineers make the assumption of constant acceleration at the drum. Under the older method of calculating acceleration stresses, this would be true with a constant torque motor. But if stresses vary, as this paper attempts to show that they do, constant torque would not give constant acceleration, although the velocity-time curves obtained in the full size test herein described showed that they approach rather closely to this condition, at least as nearly as could be measured. Theoretical Discussion According to elementary physics, the force required to accelerate a Wf body of weight W at the rate of f ft. per sec.2 is wf . To raise the body Wf with acceleration of f ft. per see.2 the total force required is I + Wf, in if

Jan 1, 1927

By W. J. Feuerstein

Plastic deformation of the germanium adjacent to the re-growth material has been observed after alloying single crystal germanium with tin. Of several solder alloys investigated, plastic deformution was observed only in the germanium samples in contact with a tin-doped regrowth material. Dislocations were observed to move on a viewed (111) plane following thermal cycling of tin-doped regrowth material on germanium. OBSERVATION of germanium samples to which solder had been fused indicated that plastic deformation, as evidenced by slip arrays of dislocation etch pits, occurred during the fusion of the solder alloy, Figs. 1, 2. The samples had been prepared by placing the solder in contact with the germanium and heating the assembly to approximately 575"C, followed by cooling to room temperature. During this process, the solder first melts, and then as the temperature is further increased, dissolves a portion of the germanium with which it is in contact. During the cooling portion of the thermal cycle, the dissolved germanium is precipitated, and provided

Jan 1, 1961