By C. R. Masson, M. L. Pearce

The nitrogen contents of seven specimens of iron and steel were determined by the three methods. Good agreement won generally observed between the results of the isotope -dilution and Kjeldahl determinations, tltzts establishing the reliability of the isotope -dilutzon technique. For some specimens, the vacuum-fusion values at 1650 °C were lower than the corresponding Kjeldahl values by up to 0.0015 pct absolute. These differences were eliminated for a specimen of "pure" iron by performing the vacuum-fusion analyses at 2100 ° to 2240 °C. The reason for this relatively high temperature required m the vaczium-fusion analyses is discussed. ThE determination of nitrogen in iron and steel has been the subject of numerous investigations and a concise review of the extensive literature in this field has recently appeared.' Two methods of analysis are most commonly employed, the vacuum -fusion and the chemical or Kjeldahl method. Except in special cases where the presence of certain alloying elements may present difficulties, both methods are generally regarded as applicable, although the vacuum-fusion method is more sensitive and is often preferred for samples of very low-nitrogen content. The method of isotope dilution, first employed for the determination of gases in metals by Kirshenbaum and Grosse,2 has recently been applied to the determination of nitrogen in iron and steel.3,4 The method is attractive in that it does not require the quantitative extraction of gas from the metal specimen. Staley and Svec3 modified the standard Kjeldahlpro-cedure by introducing, along with the steel sample, a measured amount of ammonium sulfate enriched in the isotope 15N. The nitrogen content was obtained by measuring the isotopic ratio 15N/14N in the resultant solution. The technique involved the distillation of nitrogen as ammonia from alkaline solution and subsequent oxidation of NH4+ in the distillate to gaseous nitrogen. The results for iron and steel samples of commercial origin were often in reasonable agreement with values quoted by the suppliers, although occasional marked discrepancies were observed, particularly with the results of vacuum-fusion analyses. Preliminary work in this laboratory4 on the determination of nitrogen by isotope-dilution in the gas phase yielded results for three samples which were significantly higher than the values obtained by vacuum-fusion. The present paper describes an extension of this work to a wider variety of samples. Analytical results by the Kjeldahl method are also reported. EXPERIMENTAL The technique employed for the isotope-dilution determinations was similar to that described elsewhere.4 Several minor modifications were made to the apparatus. These included the use of molybdenum instead of platinum-rhodium suspending wires when crucibles were degassed at temperatures above 1600°C. The circulatory system used previously for converting CO to CO2 was replaced by a single chamber, the walls of which were cooled directly in liquid nitrogen. Temperatures were measured with an optical pyrometer which had been recently calibrated and, as in the previous study, were minimum values obtained by sighting on the center bottom of the crucible. Temperatures obtained by sighting on the interior walls were always higher by 100' to 130°C with the design of crucible employed. Flat-bottomed crucibles exhibited an even larger temperature difference. To check the efficiency with which crucibles were degassed in the isotope-dilution apparatus, several experiments were done in the vacuum-fusion apparatus, suitably modified4 for isotope-dilution studies. Faster pumping speeds and higher degassing temperatures were possible, the latter due to the use of a generator with a higher power output (10 Kva at 398 kc per sec). In these experiments the combustion of CO was omitted and a correction4 was made for the contribution of CO to the ion current at m/e 28, used in determining the isotopic ratio R = l5NP4N. This correction did not seriously influence the re-

Jan 1, 1962

By Frank Marotta, Louis B. Lesem, Frank Greytok, John J. McKetta

Although one of the primary variables in the calculation of the flowing bottom-hole pressure in gas wells from surface measurements is the temperature at any point and its distribution in the flow-string, only few experimental data are available in the literature and little attention has been given to analysis of the problem. Virtually all of the recently published methods of calculating flowing bottom-hole pressures depend on the assumption that either the temperature is constant at some average value or that the variation is linear with depth. The purposes of this work are to analyze the problem theoretically and to verify the analysis by comparison with experimental data so that practical problems in the analysis of the behavior of gas wells can be solved with greater accuracy, reliability, and ease. MATHEMATICAL OUTLINE OF PROBLEM Assuming that: 1. The mass velocity and chemical composition of the gas stream are constant and in normal gas well operations, the change in linear velocity in the entire flow-string is trivial, 2. The product of the density and heat capacity of the gas is constant, 3. No horizontal temperature gradient exists in the gas stream, 4. Net flow of heat by conduction within the formation and in the gas stream in the vertical direction is trivial in magnitude and can be neglected, 5. The regional vertical geothermal gradient is constant, and 6. The temperature of the gas entering the borehole is constant, and equal to that of the reservoir, a set of two simultaneous, linear partial differential equations with appropriate boundary conditions was derived to describe the temperature distribution in the gas stream and the surrounding formation. These equations were solved by operational techniques for the distribution of temperature in the gas stream. The resulting integrals were evaluated numerically on an IBM 604 at the Machine Accounting Div. of the Railroad Commission of Texas. DERIVATION OF FUNCTIONS FOR THE DISTRIBUTION OF TEMPERATURE The physical system is a circular hole of radius a in an infinite medium with thermal conductivity K, density p8, and heat capacity c,. Under shut-in conditions the well is in thermal equilibrium with the surroundings and the increment in temperature is given by - ?T3/L x. Gas of density pg and heat capacity c.. flows upwardly through this hole in the direction of increasing x with a linear velocity W. Writing a heat balance on an element of gas ?x in thickness, convective heat transfer + conductive heat transfer + energy required to lift a unit mass of fluid = change in energy content. pa2W po Co To - pa2Wpo Co To x+xx - 2apK?x ?T8/?r r=a - Wpa2 po?x/778 = CoPopa2?x?To/?t... Dividing by (copopa2?x) and taking the limit as ?x tends to zero, -W (?To/?x + 1/778Co) + 2 K/a Po Co ?T3/?r r=u = ?To/?t

Jan 1, 1958

By G. R. Rubly, H. J. Steele

LOCATION AND HISTORY THE San Manuel property is in townships 8S and 9S, range 16E, Gila and Salt River Base and Meridan, State of Arizona. This area is in the Old Hat mining district, southern Pinal County, and is about 3;2 miles southwest of the town of Mammoth on the San Pedro River and one mile south of the Mammoth mine at Tiger, Arizona. The property consists of over 150 contiguous lode claims. The Old Hat district was prospected prior to the Civil War, but there was little or no production until 1881.1 The chief producers have been the Mammoth and Mohawk mines, now consolidated and operating as the St. Anthony Mining and Development Co., Ltd. Production to 1936 was $5,200,000, of which 83 pet was gold.2 Since 1940 the production has been chiefly lead and zinc, and some molybdenum and vanadium. There are a few small properties in the vicinity that have produced very minor tonnages of copper ore. In the San Manuel group there are claims which have been held continuously from 1906 to the present time, and at least two churn-drill holes were put down on or near the outcrop in 1917. No logs for these holes are available, but it is assumed that the grade of copper encountered was not sufficient to encourage further exploration. A small amount of ore has been shipped from open cuts on the San Manuel outcrop area, but there is no record of the tonnage or grade. It is estimated that not more than 5o tons were mined. These cuts, plus a few shallow shafts and some short adits indicate limited and unenthusiastic prospecting at San Manuel. In 1942, through the efforts of James M. Douglas, R. B. Giffin, Victor Erickson, and Henry W. Nichols, owners of the San Manuel group, the Reconstruction Finance Corporation and War Production Board authorized the United States Geological Survey to investigate the property, and by their recommendation, the United States Bureau of Mines was authorized to put down a limited number of churn-drill holes. The Bureau of Mines carried on drilling from November 1943 to February 1945. Seventeen holes were drilled, varying from 305 to 1990 ft in depth. The property was brought to the attention of Magma Copper Co. in June I944 and an option agreement was made with the owners. Subsequently, a group of claims lying north of the original group and held by the Apex Lead Vanadium Mining Corp., and a group to the east held by the Quarelli family, were optioned. A drilling program was laid out to conform to the Bureau of Mines pattern, and drilling started in December 1944. San Manuel Copper Corp. was incorporated September 1945, and has carried on the exploration program to the present time. GEOLOGY General The mineralized outcrop, chief copper mineral of which is chrysocolla, is a tri-

Jan 1, 1947

The fundamentals of blasting involve both the properties of explosives and of the rock being blasted. Four of the most important explosive properties appear to be energy density, bulk density, rate of energy release and the pressure- time history of the gases produced. Important rock properties are density and porosity, strength, and energy absorption including the effective moduli of elasticity. Rock structure also has a marked effect on its properties: for example, joints, bedding, and fracture alteration. Several mechanisms enter into rock fragmentation by blasting. These include slabbing, radial fracturing, crushing and bursting by the gas bubble. All of these factors are closely related to properties of both explosives and rock. Slabbing depends upon the first generated stress wave, whose shape and magnitude are a result of the pressure generated by the explosive, its time history and the resultant response of the rock, including its ability to sustain the stress wave. Actual slabbing, in turn, is a function of the magnitude and shape of the pressure pulse and the tensile strength of rock. Further fragmentation depends to a great extent upon the amount of gas in the bubble and its energy and pressure.

Jan 10, 1967

By M. B. Kahle, A. D. Pernichele

Four types of slope failures in waste dumps are recognized debris flow, foundation failure, edge slump, and blowout. The first three types, although at times causing considerable damage to property and interfering with mine operations, are not usually dangerous to personnel because of their slow rate of movement. The fourth type, the blowout, is the most dangerous because of its explosive mode of failure and lack of forewarning. The December 1969 failure at Verona dump is presented as an example of a blowout. Data from piezometer holes indicate that the blowout was due to perched leach solutions near the face of the dump. The level of water in this zone is very closely related to the rate of leach water application on the dump. A detailed analysis of core samples indicates that the impounded water was perched on a zonal accumulation of jarosite which is associated with a buried dump surface. Drain holes proved successful in controlling perched leach solutions in the critical zone near the face of the dump. Monitoring of the water level in the perched zone is considered essential in preventing blowouts. The use of drain and piezometer holes has allowed an increase in the rate of water application on the dump while preventing additional failure.

Jan 1, 1972

By A. L. Barnes

Residual oil in watered-out reservoirs is a tremendous reserve which has been unrecoverable by established production methods. A study of the new recovery methods indicated that the forward combustion urocess might- recover oil from such reservoirs; however, no thermal recovery operating experience in a watered-out system was available. The Delaware-Childers pilot thermal test was undertaken to test the feasibility of thermal recovery in this watered-out reservoir. The pilot test consisted of a 2.22-acre, inverted five-spot in the 600-ft deep Bartlesville sand. The reservoir in the pilot area had a porosity of 20.6 per cent, a permeability of 118 md and an average sand thickness of 45 ft. The reservoir contains a 33' API, 6-cp oil. Combustion was started Nov. 22, 1960. The initial air injection capacity was 750 Mscf/D, but it was eventually increased to 2,000 Mscf/D. The test was surrounded by an active water flood; therefore, water production was initially high, but decreased as the heat wave moved toward the producing wells. Oil-bank arrival at an individual well was indicated by a drop in GOR and WOR, and an increase in oil production. Combustion-front arrival was evident at three of the pilot producers, and they were plugged. Cumulative oil production from pilot area wells war over 12,000 bbl. Operational difficulties were negligible and only conventional equipment was necessary. The combustion efficiency of this test averaged over 80 per cent. Results from coring showed that the leading edge of the combustion front tended to be wedge-shaped but a nearly complete sweep of the reservoir was eventually obtained. An isopach map based on evidence from 10 core holes and the existing wells showed that 126 acre-ft had been swept by the heat wave. Using this swept volume, an air requirement of 15.7 MMscf/acre-ft was calculated. It was calculated that 275 ,STB/acre-ft was consumed bv the heat wave. INTRODUCTION There is a large amount of oil remaining in reservoirs that have been water flooded. A study of ways to recover this oil showed that the forward combustion process might be applicable. Results from a number of forward combustion tests have been reported in the literature, but none of these tests were conducted in a watered-out system. The Delaware-Childers pilot thermal test was initiated in 1960 to define the operating characteristics of underground combustion in this watered-out Bartlesville sand reservoir, The purpose of this paper is to present the pilot test results in detail. FORWARD COMBUSTION PROCESS The forward combustion process consists of initiating combustion in the formation surrounding an injection well and driving this heat wave through the formation toward offset producing wells. As the combustion front progresses through the reservoir, oil and formation water are vaporized, driven forward in the gaseous phase, and recon-densed in the cooler part of the formation. These distilled liquids, water of combustion and gaseous combustion products, form a bank or three-phase region ahead of the burning front. This bank pushes mobile reservoir fluids toward the production wells. The rate of movement of the combustion front is controlled by the rate at which the nondistill able residue which serves as process fuel can be completely burned off the sand. The production performance from a heat wave conducted in a watered-out oil reservoir will differ from one conducted in a dissolved gas-depleted reservoir because of the difference in fluid saturations. The primary depleted reservoir contains connate water saturation, relatively high oil saturation and some gas saturation. The watered-out reservoir contains a highly mobile water saturation, residual oil saturation and little gas saturation. As the combustion front moves forward in either type of depleted reservoir, it drives the distillable oil, the water in place and the water of combustion ahead, and burns the nondistillable portion of the oil. The heat-wave process in a watered-out reservoir differs from the process in a

Jan 1, 1966

By J. E. Crawshaw, Francis B. Foley

In the first report1 disks of steel of known composition and history were exposed, under carefully prescribed conditions, to impacts of explosion products resulting from the explosion of 50-gm. charges of explosives having well-determined rates of detonation, or to impacts of a weight of known mass, falling through measured distances. There were available at the Bureau of Mines Experiment Station five explosives, having rates of detonation of 5716, 4470, 3190, 2296, and 1523 meters per second. It being desired to continue this exposure downward, and no explosives with a lesser rate of detonation being at hand, resort was had to the impact of a falling weight, the differences in the velocity of impact being attained by varying the height from which the weight was allowed to fall. It was expected by this means to demonstrate experimentally that the development of Neumann bands was determined by the suddenness of the deformation of the metal in which they were produced. But while progressive deformations were obtained with the explosive charges, the falling-weight method failed because the tup was progressively deformed, also the disks were so flattened as to be unfit for metallographic examination. A return, therefore, has been made to the use of explosives as the source of energy, an air-gap being interposed between the charge of explosive and the disk, as the effect diminishes as the function of the distance between the charge and the object on which the products of its explosion, or the shock wave from its detonation, impinge. The details of the arrangement of the tests by the air-gap method were the same as those described by Foley and Howell,2 except that after the system had been set up and the desired apparent specific gravity for the explosive attained by tamping it, the small lead block, with the steel disk adhering

Jan 1, 1926

By Cyril Wells, Paul E. Busby, Donald P. Hart

EARLY workers in the field have established that the diffusion of nitrogen follows normal diffusion laws. Concentration-penetration data from layer analyses of reasonably pure iron specimens nitrided in an atmosphere of CO-NH, are given in the literature,' and were utilized to calculate diffusion constants for nitrogen. The diffusion of nitrogen in y-iron may be represented approximately by the equation D - 1.07x10-' e-:".'m'"'r The diflusion coefficients, D, given by this relation represent mean values, since carburization occurred simultaneously with nitriding. The rate of diffusion in a-iron has been determined from calculations based on data obtained by measuring the internal friction of samples at each of several frequencies and temperatures.' The expression for the diffusion of nitrogen in a-iron derived from these experiments is D= 1.4x10-1 e-it tudent Increasing carbon content decreases the diffusion of nitrogen in a-iron.3 Oxygen, either dissolved or combined, has been shown' to exert a marked influence on the diffusion of nitrogen from a nitriding atmosphere. D values increase rapidly with increasing amount of dissolved oxide in the metal, but diffusion is completely inhibited if preliminary oxidation has produced the slightest trace of iron oxide on the surface. Diffusion coefficients have also been calculated from permeability and solubility data,' but these values are of questionable accuracy since the boundary conditions assumed may not actually exist. Experimental Method The method selected for determining the diffusion coefficient of nitrogen in a-iron in the present investigation was the so-called fractional saturation method. This method consists of heating the specimen in an atmosphere of H2-NH8 mixtures of known composition for a predetermined time. Following this treatment, the specimen is analyzed for nitrogen; and the diffusion coefficient is calculated from a known relationship of the fractional saturation, time of diffusion, and dimensions of the specimen. This relation is based on a solution of Fick's second law and assumes that the surface of the specimen immediately reaches a given concentration which remains constant during the diffusion anneal. Tabular solutions are available4-5 and provide the relationship between fractional saturation and the quantity \/Dt /a, where D is the diffusion coefficient in cm2 per sec, t is the time of the diffusion anneal in seconds, and a, in the present experiments, is the half-thickness of the slab specimen in cm. The method is adequately discussed elsewhere.9-10 Material The material for this study consisted of 3/32 in. thick (0.24 cm) carbonyl iron plate. The major impurities in this iron are oxygen and carbon, which are readily removed by long time high temperature treatment in an atmosphere of purified hydrogen. In order to reduce the diffusion anneal time for saturation runs, some of this material was rolled to a thickness of 0.015 in. (0.038 cm) prior to the hydrogen treatment. Hydrogen treatments were carried out in a hydrogen-purified Armco iron tube heated in a global

Jan 1, 1957

By J. R. Spencer

When supplies of high pressure mercury or other liquids are required in analytical work, it is convenient to have the source of supply at a relatively constant pressure and available in sufficient volume to satisfy the requirements of the apparatus in use. It is also desirable that the pressuring device be as simple and as inexpensive as possible and convenient to operate. This pump combined with a small storage reservoir containing gas under pressure has the attributes of (1) positive control of the maximum output pressure through the use of a regulator in the low pressure air supply; (2) an increasing capacity as the rate of withdrawal of mercury from the pressured system is increased; and (3) simplicity, requiring only the use of a lathe, drill press, and welding unit in its construction. DESCRIPTION Essential parts of the pump are shown in Fig. 1. In appearance the unlt is similar to the usual steam pump in common use in industrial applications although considerably smaller in size. The main differences lie in the area ratio of the air and mercury pistons and in the design of the air valve mechanism. Approximate diameters of these pistons are 4.25 in. to 0.375 in. respectively, giving an area ratio of about 130 to 1. The air piston (2) is attached to the end of shaft (4), with the mercury piston being merely a reduced extension of the shaft. Mercury intake and discharge to the pump are controlled by high pressure check valves that screw into the ports indicated at (6). Air supply is controlled by the valve assembly mounted on top of the

Jan 1, 1950

By Charles Austin

IN a recent paper the authors1 discussed the reactions to tempering of hypereutectoid steels quenched from 1000° C., as revealed by studies on changes in hardness, electrical resistivity, coercive force and metallo-graphic characteristics. The data, which related specifically to temper-ing temperatures of 550°, 650° and 710° C., for varying periods up to 125 hr., permitted the following important conclusions: 1. The rate of softening of the steels at the temperatures examined differed markedly although the steels were of "similar" general chemi-cal composition. 2. The temperature of maximum softening spread over a range from about 650° C. to the eutectoid inversion. 3. The divergence in behavior was ascribed, at least in part, to a profound difference in tendency to graphitization on annealing at sub-eutectoid temperatures. 4. The mode of spheroidization of the cementite, as revealed by metallographic studies, also varied considerably in the different steels. The purpose of the present investigation is to pursue further the study of the difference in behavior of the steels on tempering over a wider range of temperature. To this end the following features have received particular attention: 1. Comparison of temperatures of maximum softening of the various steels when the quenched samples were tempered for 5 hr. and for 75 hr. followed by furnace cooling and by quenching in water. 2. Determination of the effect of quenching temperature, prior to tempering, on the rate of softening. Quenching temperatures of 1000° and 850° C. were used in the investigations. 3. Examination of the microstructures obtained with the various heat-treatments employed.

Jan 1, 1938

By W. A. Backofen, D. Lee

Tlze condition of superplasticity or neck-resistanl flow that results front high strain-rate sensitivity has been observed in isothermal tension tests on several titanium alloys and one of zirconium hi general, il was associated with reasonably fine-grain micro-structures being stvained in the transformation range at rates below i - 10 -3 sec-&apos;. The metallographic mean-free path, L, was measured at room temperature after rapid cooling from the temperature of test-ing. The flow stress of Ti-GAL-4V at 950°C was proportional to La at different constanl <; the value of a decreased with increasing. E but at E< 1.5 x 10-4 sec-1 it varied only from 0.9 to 1.25. The findings were interpreted to mean that viscous boundary shear is the rate-controlling process of deformation at high levels of strain rate sensitivity in these materials. Elongation of over 1000 pet could be obtained, but a1 temperatures so high and rates so low that any practical application of the full effect would probably be difficult. As the transformation range was narrowed, by turning from Ti-6AL-4V to Ti-5Al-2.5sn to nomznally pure titanium, the allowable temperature varialion was correspondingly reduced. Superplasticily was not found in Armco iron, presumably because the transformation range was too narrow to allow the developtnenl of a reasonably stable microstructure for isolhermal lesting. THE work represented by this paper grew out of a recent study of texture hardening in a(hcp) titanium and zirconium-alloy sheet,&apos; of which part has now been published.2 It was found that, with heating, the tensile plastic-anisotropy index, R,* was decreased from well above 1 towards 1 as the temperature range for the a(hcp) -ß(bcc) phase change was entered. The clearest example of that trend is illustrated with previously unpublished data in Fig. 1. It might have been thought that such a development resulted simply from introduction of the cubic and therefore plastically less anisotropic phase. However, the accompanying change in the index of tensile strain-rate sensitivity, m = a log a/a log E, was rapidly upwards, to a high of 0.85 in some cases (also illustrated in Fig. 1). At the same time, the total tensile elongation rose to a maximum and the flow strength dropped away as R (and m) approached 1. Taken together, the observations cannot be understood as resulting from the presence of cubic phase, per se. It has been concluded instead that they reflect the largely noncrystallographic deformation which characterizes superplasticity. As demonstrated in other recent work? a necessary condition for super-plasticity is strain-rate sensitivity of flow stress sufficiently high that m is above a lower limit of -0.3. The origin of large m has been traced, in turn, to grain size so small that a substantial amount of viscous deformation is introduced by such processes as Nabarro-Herring diffusional flow4 and/or grain boundary shear.5,6 Because of problems in the processing of titanium and zirconium alloys—problems of high strength, limited ductility, and excessive springback, originating largely in slip resistance-it was natural to wonder if something useful might be done with superplasticity in those materials. Therefore experiments were made for more closely identifying and generally bounding the phenomenon with temperature and strain-rate limits, before attempting to decide about its exploitation. The results are being reported here. EXPERIMENTAL Materials. The two of primary interest were the titanium alloys of nominal composition (in wt pct) 5A1-2.5Sn and 6A1-4V. Others were a 4A1-1/4O2 titanium alloy, titanium of commercial purity (RC-70), Zircaloy-4. and Armco iron. All were received as annealed 3/16 in. thick sheet, except RC-70 which was & in. thick, and tested in that condition. Details of transformation temperature and grain size are given in Table I. The results of dilatometry for the measurement of transformation temperatures were unsatisfactory. Data were finally obtained by metallographic examination of each specimen after test, to determine from the amount of transformed 4 where the specimen had been heated in relation to the critical temperatures. Results were in reasonable agreement with information from the supplier. Strip tensile specimens were of full sheet thickness and taken along the rolling direction, except for those

Jan 1, 1968

By AIME AIME

Further details of the 97th meeting of the Institute, at Spokane, have been sent to members in the Special Circular of May 8, 1909, and for convenience a summary of the additional information is given later in this announcement. In spite of the present small number who have joined the party, final arrangements have been made to complete the itinerary given in the circular. It is greatly to be desired, both in behalf of the Institute and in recognition of the special courtesies to be extended on the trip, that the party be made larger. Exceptional facilities to visit the many mines and smelters have been freely provided; and members are requested to make all reasonable effort to attend the meeting at Spokane and participate in the excursions. . For those who cannot take the entire trip, it may be possible to provide special Pullman accommodations after leaving the Yellowstone Park. In order to make the necessary arrangements, however, the names of members and guests contemplating this partial trip should be sent at once to Mr. Theodore Dwight, .39 West 39th St., New York, N. Y. A special train of Pullman cars will leave Chicago September 16. This train will be side-tracked at all places visited, and the sleepers will be available for lodging and the dining-car for meals (luring the entire trip, except while taking the tour through the Yellowstone Park. The general cost of the trip per member will be $300, which includes transportation, berth, and meals for the entire trip from Chicago back to Chicago, almost 6,000 miles, and the tour through Yellowstone Park, occupying in all about 30 days. Special accommodations on the train will be furnished at the following rates

Aug 1, 1909

By Stefan Boshkov, Malcolm T. Wane

The validity and accuracy of velocity measurements underground have been questioned repeatedly by those in mine ventilation work. The general disagreement on the subject is well illustrated in an AIME publication.&apos; Although the presence of errors is readily admitted, their magnitudes are not known and often are described by practical operators merely as "great," "small," or "of no importance." The belief that errors are of academic interest only prevails because of a justifiable claim that actual volumes of air circulated are well in excess of those required by law and safe mining practices. Poor understanding of the source and nature of errors inherent in velocity measurements, coupled with questionable determination of cross-sectional area, result in faulty techniques for the purpose of expediting ventilation surveys and render doubtful the calculated volume. Often consistency of readings is confused with accuracy. A succession of check readings showing a maximum deviation of 5 pct in the measured value of velocity usually signifies nothing more than diligent application of technique in a stable ventilating current.

Nov 1, 1955

By N. O. Taylor

THE failure, by swelling, of several cast aluminum-zinc, spiral, pump rods, used to circulate water in a constant-temperature bath, brought up the question as to whether the presence of tin in varying quantities would have any appreciable influence in controlling this action. Previous workers had found the same difficulty with aluminum-zinc alloys, due to their swelling in water or solutions of electrolyte^.^ It was known that pure aluminum was practically insoluble in concentrated sulfuric and nitric acids, presumably due to the formation of an oxidized film on the surface. Concentrated sulfuric acid had little or no effect on pure zinc and tin and concentrated hydrochloric acid would attack all three metals. These facts aroused curiosity as to the probable reaction of the ternary alloys of these metals, and tests were made to determine their resistivity to the action of common laboratory reagents. Samples, covering the entire range of the ternary series of aluminum, zinc and tin alloys, were made up from good grades of the commercial metals.2 The materials were melted, at as low temperatures as possible, in graphite crucibles in a gas-fired crucible furnace. Graphite crucibles were used in preference to clay, to prevent the absorption of silicon by the aluminum, as found by previous workers. The melted materials were stirred thoroughly with pine sticks in order to ensure complete mixing and the greatest possible freedom from oxidation, and were cast in sectional, iron molds giving bars % in. in diameter and 5 in. long.

Jan 1, 1927

By M. R. Tek, F. H. Poettmann, M. L. Grove

The general problem of single-phase natural gas flow through porous media has been considered both by mathematical analysis and field experiments. Theoretical studies on the fluid dynamics of natural gas wells resulted in derivations of expressions which permit a ber-ter understanding of the flow mechanism for conditions under which Darcy&apos;s law is no longer valid. In applying these results to natural gas production and testing technology, special emphasis war placed on the study of low permeability, slowly stabilizing formations. These applications resulted in a method of predicting the performance coefficients of tight natural gas wells. The calculation of the performance coefficient requires the determination of the "test-index", pkh/µ, the drain- age radius, R, and the effective wellbore radius, rw. Methods for estimating these parameters from field data were also developed. Field data from 15 wells were collected and analyzed. The measured values of the performance coefficients were compared with the predicted values. This statistical evaluation gave a bias of 7.14 per cent and a standard deviation of 11.6 per cent. INTRODUCTION The performance of a natural gas well is determined by the physical properties of the reservoir rock, the extent and the geometry of the drainage area, the properties of the flowing fluid, and the conditions of pressure distribution within the drainage matrix. The relation between the quantity of gas delivered and the pressure drop within the reservoir is characteristic of the behavior of each well and is often referred to as the back-pressure behavior of the well. It is well established that for normal, single-phase gas wells the relationship between the gas delivery rates and the bottom-hole pressure take, in general, the form, Q = c(P3 8 -P2 1)n. ,.......(1) where C is the performance coefficient, and n is the exponent corresponding to the slope of the straight-line relationship between Q and (P2 s, — P2 l) plotted on logarithmic coordinates. The determination of a well&apos;s performance by the back-pressure behavior not only permits the production engineers to analyze many operating problems, but also provides necessary information useful and essential to predict the future development of the field.&apos; Important engineering and production problems such as calculation of gas deliverability into a pipeline at a predetermined line pressure, design and analysis of gas-gathering lines, determinations of spacing and number of wells to be drilled during field development to meet future market or contract obligations, etc., all depend, at least in part, on the availability and use of reliable back-pressure curves.&apos; In the past the behavior of gas wells was evaluated

Jan 1, 1958

By H. M. Wilten

THIS article presets a view of a problem encountered in petroleum refining in the deterioration of equipment used in condensation of vapors and cooling of liquids. Discussion is limited to the problems of shell- and tube-type exchangers and condensers. In this service shell- and .tube-type equipment is gradually displacing other types and, for this reason, its economic importance ill oil-refining practice is also increasing. Considering oil - refinery practice during the last two decades one can readily see many important improvements in the apparatus used. Briefly, the present equipment is safer, more efficient, and Ignore economical. Improvement in apparatus used for the condensation of distillates has, in my opinion, been less than that in other essential distilling apparatus. So it is hoped that this discussion will stimulate research among the producers as well as among the consumers of this equipment with a view to ameliorating this condition.

Jan 1, 1937

By D. N. Seidman

In the course of a study of the electronic and thermodynamic properties of Pb-Se alloys it was found necessary to have an accurate knowledge of the phase diagram. However, the literature is in disagreement as to whether or not a monotectic reaction occurs in the lead rich portion of the phase diagram. Pelabonl reported only a two-phase region consisting of lead-rich liquid and solid PbSe extending from almost pure lead to the compound PbSe, and gave the melting point of PbSe as 1065°C. The data of Friedrich and Leroux2 are in general agreement with this type of diagram, with the melting point of the compound being 1088°C. However, Nozato and Igaki by inverse rate thermal analysis observed a monotectic reaction isotherm exlacing at 860°C with a monotectic composition of 20.5 at. pct Se. The miscibility gap in the liquid state extends from 7.5 to 20.5 at. pct Se. Hansen and Anderko4 accepted Nozato and Igaki&apos;s phase diagram in the region of the lead-rich monotectic. To reinvestigate this portion of the phase diagram, both thermal analysis and metallographic examination of various compositions were performed. The thermal analysis apparatus was constructed according to the specifications of the National Bureau of Standards. A t/t-l pct Rh thermocouple was calibrated against the melting point of copper (NBS), zinc (NBS), and antimony (A. D. Mackay), the emf being measured with a Rubicon Type B potentiometer sensitive to lpv. The absolute accuracy of the thermal analysis obtainable with this system is ± 0.5oC. Starting materials were semiconductor grade lead and selenium purchased from the American Smelting and Refining Co. Both elements were 99.999 pct pure with only trace impurities detected upon spectroscopic examination. One hundred galloys were sealed in quartz crucibles with a central thermocouple well under a vacuum of less than 1 p. This procedure prevented any composition change due to vaporization during the run. Cooling curves were obtained on the alloys listed in Table I. Data was taken by the direct method at cooling rates ranging between 1/2 to 2°C per min. The alloys were heated well above the liquidus and shaken vigorously to insure homogeneity. No evidence of an arrest indicative of the monotectic reaction was observed, and the two-phase region reported by Pelabonl and Friedrich and Leroux? was confirmed in general, although our data give higher liquidus temperatures than Friedrich and Leroux. The melting point of stoichiomet-ric PbSe determined for two different samples was 1080.7 0.5oC. The results of this investigation are compared with Nozato and Igaki&apos;s data in Fig. 1. To Complement the thermal analysis data, an 86 at. pct Pb specimen was examined microscopically. This composition was in the center of the miscibility gap reported by Nozato and Igaki.3 The alloy was heated to 1000°C, held for 1/2 hr, and water quenched. The specimen was polished using standard metallographic techniques for lead. The alloy was etched with an acetic-nitric acid etchant for 10 min at 45°C. Microscopic examination did not indicate the existence of two separate layers or solidified droplets imbedded in a matrix, as would be expected if a miscibility gap were present. The mi-crostructure shown in Fig. 2 consists of uniformly dispersed, dendritic PbSe in a lead-rich matrix.

Jan 1, 1962

APPLICATIONS for loan contracts for the exploration, development and mining of strategic and critical metals and minerals are now being accepted by the Department of the Interior. The RFC is authorized and directed by Executive Order 10161 to make such loans but the Secretary of the Interior must pass on the necessity for the loan. Applications should be addressed to James Boyd, acting deputy administrator, Defense Minerals Administration, Department of the Interior, Washington, D.C. rather than to the Field Offices of the Bureau of Mines as was first planned. Application forms are not yet available but it has been learned that data accompanying the application should include the known quantity and grade of reserves, the anticipated rate of production, the equipment, supplies, and man power required for the additional production, etc.

Jan 12, 1950

By J. B. Fletcher

The Miami mine first started operations in 1910. For convenience, the history of the orebody can be divided into the following categories (Fig. 1): 1) 1910 to 1925: 24.4 million tons of high grade ore, mined by top slicing, sublevel caving, etc. 2) 1926 to 1954: 102 million tons of low grade ore, mined by block caving.

Jan 1, 1961

THE program for the 126th meeting of the Institute, to be held in San Francisco Sept. 25 to 29, 1922, is being prepared by the General Arrangements Committee of the Local Section and its details are not yet ready for announcement. The program, however, has developed to a sufficient extent to permit members to decide whether they wish to attend or not. Briefly stated, Monday, Sept. 25, will be devoted to technical sessions which will be held at the Engineers Club, and there will be as many sessions as may be required to present the papers available, some of which are listed below. Under the registration fee plan (see July magazine) entertainment expenses during the week in San Fran-cisco will be borne by those in attendance, not by local members alone. Members who expect to attend the San Francisco meeting, but who will not accompany the President&apos;s party, will please notify C. H. Fry, Secretary of the San Francisco Section, 625 Market St., San Francisco, Cal., of their intention.

Jan 8, 1922