By ERNEST A. HERSAY

ACCURATE ore-sizing with screens is drawing attention to certain details that now, more than ever before, require attention. There are many tests that must be preceded by careful sizing. The assayer often could profit by a more careful selection of screens. In milling, more attention is given the slimes produced. Cement-manufacturers are pulverizing and screening finer than they formerly did, and others are reducing materials to fine sizes at high cost, with screens used to govern the fine¬ness of the pulverized product. Fine screens are expensive, easily injured by mis-use, are carried in stock sparingly by most dealers, and are handled often by those who know little about them except their designated number. More attention, on the whole, needs be given the actual size of the mesh-openings, and less emphasis placed upon any custom or conventionality in numbering. An effort to classify wire screens, in this respect, leads at once into computations, where one is confronted with details of sizes and standards, of different wires, different gauges, and different customs. There is always uncertainty about the exact working-size of a screen until one gives the matter special attention, and devotes more time to it than its simplicity seems to demand. To know only the number is not sufficient for all uses. Often, in sets, superfluous sizes are used; and sizes are omitted that are of critical importance. In wire screens, the use of different standard sizes of wire makes important differences in dimensions that must be taken into account. The dealer usually grades screens by the number of openings per linear dimensions, regardless of the size of the openings or of the wire. Certain 100-mesh screens in use are found, by measurement, to he actually coarser than others of 90-mesh, a result which is due, of course, to the use of larger

May 1, 1906

By Charles L. Guettel

The temperature coefficients of electrical resistance of 31 alloys in the nickel-rich corner of the Ni-Cr-Fe system were determined. The results indicate that a range of binary Ni-Cr alloys has lower temperature coefficients than a specific region of Ni-Cr-Fe alloys which has been reported and quoted by others as providing the lowest coefficients in the ternary system. DESIRABLE properties of resistivity and temperature coefficients of resistance have been the basis for the successful commercial application of various Ni-Cr and Ni-Cr-Fe alloys. In particular, low or negligible temperature coefficients of resistance are necessary for wire used in precision wire wound resistors and potentiometers involved in closely controlled electrical and electronic circuitry. Alloys most successfully applied to this purpose basically have not been ternary Ni-Cr-Fe alloys but rather heat-treated Ni-Cr alloys in the region of approximately 73 to 79 pct Ni and 20 pct Cr with significant additions of other elements such as aluminum, silicon, iron, copper, manganese, and cobalt. While the addition elements play a vital role in the nature and control of the temperature-resistance curve of any one of these alloys, the inherent relatively low temperature coefficient of the binary Ni-Cr base composition itself in the approximate region of 80 pct Ni and 20 pct Cr contributes fundamentally to the eventual negligible temperature coefficient obtained with the applied alloys. W. A. Dean 1 has reported mean temperature coefficients (20' to 100oC) of as-cast samples for the Ni-Cr-Fe system, the nickel corner of which is given in Fig. 1. Dean had to use as-cast samples because alloys from a considerable region of the system were unworkable. Dean refers to the work of Hunter and sebast2 who used annealed wire samples to show that, for chromium contents of 10 to 25 pct, the temperature coefficient increases as the iron content is increased at the expense of nickel. Although the data of Hunter and Sebast were limited in the nickel-rich areas to eight samples of 60 to 91 pct Ni with only four samples containing iron, the possibility that no Ni-Cr-Fe alloy has a lower temperature coefficient than certain binary Ni-Cr alloys should have been given serious consideration. However, Dean's work has been referred to by J. S. Marsh,3 who, quoting Dean, states that for the temperature coefficients "the smallest values-about 0.0001 per oC (100 ppm)—were found for alloys containing about 55 pct Ni and 20 pct Cr" (balance iron). A region such as that reported by Dean would be significant to those trying to develop alloys for the applications described. Therefore, a series of three-pound laboratory open-air induction melts of Ni-Cr and Ni-Cr-Fe alloys were melted, conventionally processed to 0.005 in. diam wire, and continuously strand annealed at 1900° F. The basic Ni-Cr compositions, with balances essentially iron other than usual minor impurities, and the corresponding temperature coefficients of resistance and resistivities are given in Table I. The resistivities are approximate and are not to be considered as a basis for relating them to their position of composition in the ternary system. The wire diameters were determined with a micrometer, and not by weight and density measurements which would be required for accurate resistivity values. However,

Jan 1, 1963

By R. W. Smith, K. H. Lee Discussion by Fred C. Bond

Fred C. Bond (Tucson, Ariz.) — This is a valuable paper presenting much well directed research testing. It describes a practical method by which the long and relatively accurate Bond closed-circuit grindability can be adapted to a known ore so that results of comparable accuracy can be obtained on the same ore from much shorter batch grinding tests. This can be very useful in control work. In large mills a routine batch grinding test on the head sample can be made each day, or even each shift, to check grinding performance by comparison of the work index from each mill grinding section with that obtained from testing. However, it would be well to re-standardize the batch test against a Bond test, perhaps once a week at

Jan 1, 1969

By M. L. Requa

EVERY forward step in civilization brings with it an increase in population and increasing demand for raw materials. Modern civilization, because of its industrial development, depends more and more for its well-being on ample supplies of raw materials; the higher the type of that civilization, the greater its dependence. No fact is more obvious than that the raw materials should be put to use with greatest prudence and efficiency. National life is not a matter of a decade or a century. Conservation is no longer a matter for political discussion; it is a vital element in the future welfare of all nations. Unfortunately, to the minds of many, conservation means the locking up of natural resources, their arbitrary withdrawal, bringing about, in short, a condition of industrial stagnation. This has occurred in past centuries through misdirected governmental effort. Two eminent engineers have variously defined conservation as follows:

Jan 1, 1925

By AIME AIME

THE following compilation of State bureaus and officials that deal with mineral resources is compiled in part from a new "Check List of State Agencies and Officials Concerned with the Management of Natural Re- sources," compiled for the National Resources Committee, Washington, D. C., by Clifford J. Hynning. Alabama-Geological Survey of Alabama, University. Walter B. Jones, State Geologist. Chief Mine Inspector: W. B. Hill- house, 614 Lincoln Life Bldg., Birmingham.

Jan 1, 1939

By A. R. Calawa, T. C. Harman, M. Finn, P. Youtz

A study has been made of the growing, annealing, and diffusion parameters in PbSe, Pb1-ySnySe, and Pb1-xSnxTe. Single crystals of these materials have been grown using the Bridgman technique. For all of the above materials the as-grown crystals are p type with high carrier densities. To reduce the carrier concentration and increase the carrier mobility, the samples are annealed either isothermally or by a two-zone method. From isothermal anneals, the liquidus-solidus boundary on the metal-rich side of the stoichiometric composition has been obtained for some alloys of Pb1-xSnxTe and on both the metal- and seleniunz-rich sides for PbSe and alloys of Pbl-ySnySe. In Pbo.935 Sno.065 Se carrier concentrations as low as 5 x1016 Cm-3 and mobilities as high as 44,000 sq cm v-1 sec-1 at 77°K have been obtained. Inter diffusion parameters mere also studied. The ddiffusion experiments mere identical to the isothermal or two-zone annealing experiments except that the samples were removed prior to complete equilibration. The resulting p-n junction depths were determined by sectioning and thermal probing. Inter diffusion coefficients for various temperatures were calculated for both PbSe and Pb0.93Sn0.0,Se. RECENTLY, there has been considerable interest in the PbTe-SnTe and PbSe-SnSe alloys with the rock salt crystal structure. The unusual feature of these systems is the variation of energy gap EG with composition. Several investigations1-3 have shown that EG for the lead chalcogenides decreases as the tin content increases, goes through zero, and then increases again with further increase in tin content. The possibility of obtaining an arbitrary energy gap by selecting the composition is an especially attractive feature of these alloys for applications involving long-wavelength infrared detectors and lasers. In addition, some unusual magneto-optical, galvanomagnetic, and thermomag-netic effects should occur for alloys with low band gaps. If uncompensated low carrier density crystals can be obtained, then a small carrier effective mass, a large dielectric constant, and the resultant high carrier mobility should yield enormous effects at low temperature in a magnetic field. The relative variation of the energy gap with pressure should also be very large for these low gap materials. The primary purpose of this paper is to provide some information concerning the preparation of low carrier concentra- tion, high carrier mobility, and homogeneous single crystals with a predetermined alloy composition. I) DETERMINATION OF ALLOY COMPOSITIONS In all of the work described in this paper, the composition of lead and tin chalcogenides in the alloys was determined by electron microprobe analysis. Separate X-ray spectrometers are used to make simultaneous intensity measurements of the Pb La1 and Sn La1 lines emitted by the sample under excitation by a beam of 25 kev electrons focused to a spot about 2 µm in diam. These intensities are compared to the intensities of the same lines emitted by standards under the same conditions. The standards used are the terminal compounds of each pseudobinary system, i.e., PbTe and SnTe for Pbl-xSnxTe alloys, PbSe and SnSe for Pbl-ySnySe alloys. The composition of the sample is then obtained from theoretical calibration curves which relate the weight fractions of lead and tin in the alloy to the measured ratios of X-ray intensities for the sample and the standards. The lead and tin calibration curves for each alloy system were calculated by using corrections for backscattered electrons,4 ionization,5 and absorption,6 and assuming that the atom fraction of tellurium or selenium in the sample and standards is exactly +. Results obtained by using the microprobe are in good agreement with those obtained by wet chemical analysis. II) CRYSTAL GROWTH FROM THE VAPOR Early work on the vapor growth of PbSe was carried out by Prior.7 He used small chips of Bridgman-grown single crystals as the source material and frequently converted the whole charge of a few grams into one crystal. In the present work, vapor growth occurred using a metal-rich or chalcogenide-rich two-phased alloy powder as the source material. Small, nearly stoichiometric crystals are formed on the walls of the quartz tube. The procedure will now be described in detail. Initially, a 100-g charge containing (metal)o.51(chalco-genide)o 49 proportions or (metal)o.49(chalcogenide)o. 51 proportions of the as-received elements in chunk form are placed in a fused silica ampoule. After the ampoule is loaded, it is evacuated with a diffusion pump and sealed. The sealed ampoule is placed in the center of a vertical resistance furnace. The region containing the ampoule is heated to about 50°C above the liquidus temper-ature for the particular composition used. After about one-half hour at temperature, the elements are reacted and the molten material homogenized. The ampoule is quenched in water. The quenched ingot is crushed to a coarse powder for vapor growth experiments and to a fine powder for the isothermal annealing experiments which are discussed in a later section. Vapor growth experiments were carried out using the powdered, metal-rich or chalcogenide-rich alloys

Jan 1, 1969

By D. S. Cahn, D. W. Fuerstenau

Specimens of glass, plexiglass, and naturally occurring minerals were irradiated by a 15-joule ruby laser pulse to determine criteria for the fracture of nonmetallic solids by internal thermal stresses. Fracture did not occur in those specimens with either a very high or very low internal absorptance or with a high spectral reflectance. If significant amounts of melting and vaporization do not occur at the surface of irradiation, the specimen will fracture if a derived 11fracture stress" exceeds the ultimate tensile strength of the specimen. The purpose of this investigation was to determine criteria for the fracture of nonmetallic solids by internal thermal stresses which are caused by absorption of laser irradiation. A laser produces a very short pulse of light which has a high energy density distributed over a very narrow part of the visible spectrum. The laser system used in this investigation had an energy output of 15 0 joules at a wavelength of 6940 A. Fracture in a non-metallic solid, then, would be caused by the absorption of light energy by that solid, and subsequent conversion of this energy to heat or mechanical energy. Fracture is caused by internal stresses that result from rapidly imposed nonequilibrium thermal gradients. ANALYSIS OF CONDITIONS FOR FRACTURE BY LASER IRRADIATION For this analysis, the laser beam is assumed to be circular and centered on the junction of the major and minor axes of a rectangular specimen. The laser beam forms a cylinder of radius rb extending through the specimen width. The beam cylinder may be then thought of as a heated mass constrained by a surrounding unheated mass. The instantaneously heated cylinder will at-

Jan 1, 1968

By V.K. Zworykin

Throughout its development the science of electronics, like so many other branches of science and industry, has been indebted to the metallurgist. Metallurgy has provided the electronic engineer with conductors to furnish passage for electrons outside of his evacuated tubes: it has developed tungsten and tantalum wires for emitting electrons and various refractory metals and alloys suitable for electrodes, which receive them and guide them within the tube; finally it has supplied ferromagnetic materials both for shielding electronic apparatus from magnetic fields and for forming highly concentrated fields for deflecting electron . Today I hope to show you that electronics has not been altogether ungrateful for this assistance. More specifically, I wish to indicate the role that the electron microscope, a relatively recent product of electronic engineering, is playing even now in the study of metals. Every metallographer is aware that his standard metallographic microscope will not reveal structural detail involving separations smaller than a certain fraction —at the very best a tenth—of a micron. This limitation, he knows, is a consequence of the fact that the wave length of the light employed for forming the image has this order of magnitude. It is, thus, a property of all light microscopes. TO overcome it, a different imaging medium must be employed, The existence of such a medium became evident when it was demonstrated1 that electrons were affected by magnetic and electric fields with axial symmetry just as light is affected by glass lenses; these fields, or "electron lenses," curve the paths of electrons reaching them from an object located on the axis of symmetry in such a manner that, at some distance from the lens, a true image of the object is formed. Furthermore, although a wave length may . be ascribed to electron beams just as to light, this wave length is much shorter; for electrons accelerated through a difference of potential of 50 kilovolts, the wave length is only about one hundred-thousandth of that of visible light. Actually, the elcctron microscopes of today resolve detail one hundred times as fine as light microscopes; if the maximum useful magnification of the latter is taken to be a thousand, that of electron microscopes is one hundred thousand. The Electron Microscope Since electrons are readily scattered and absorbed by matter, specimens to be observed in the electron microscope must be prepared to be less than one micron in thickness; furthermore, the interior of the microscope must be carefully evacuated to prevent collisions between the clectrons and the molecules of the air. Finally, as already mentioned, the lenses are formed by axially symmetric magnetic or electric fields, and not by any material medium such as glass. Apart from these basic differences, the electron microscope closely

Jan 1, 1943

By V. K. Zworykin

Throughout its development the science of electronics, like so many other branches of science and industry, has been indebted to the metallurgist. Metallurgy has provided the electronic engineer with conductors to furnish passage for electrons outside of his evacuated tubes: it has developed tungsten and tantalum wires for emitting electrons and various refractory metals and alloys suitable for electrodes, which receive them and guide them within the tube; finally it has supplied ferromagnetic materials both for shielding electronic apparatus from magnetic fields and for forming highly concentrated fields for deflecting electron . Today I hope to show you that electronics has not been altogether ungrateful for this assistance. More specifically, I wish to indicate the role that the electron microscope, a relatively recent product of electronic engineering, is playing even now in the study of metals. Every metallographer is aware that his standard metallographic microscope will not reveal structural detail involving separations smaller than a certain fraction —at the very best a tenth—of a micron. This limitation, he knows, is a consequence of the fact that the wave length of the light employed for forming the image has this order of magnitude. It is, thus, a property of all light microscopes. TO overcome it, a different imaging medium must be employed, The existence of such a medium became evident when it was demonstrated1 that electrons were affected by magnetic and electric fields with axial symmetry just as light is affected by glass lenses; these fields, or "electron lenses," curve the paths of electrons reaching them from an object located on the axis of symmetry in such a manner that, at some distance from the lens, a true image of the object is formed. Furthermore, although a wave length may . be ascribed to electron beams just as to light, this wave length is much shorter; for electrons accelerated through a difference of potential of 50 kilovolts, the wave length is only about one hundred-thousandth of that of visible light. Actually, the elcctron microscopes of today resolve detail one hundred times as fine as light microscopes; if the maximum useful magnification of the latter is taken to be a thousand, that of electron microscopes is one hundred thousand. The Electron Microscope Since electrons are readily scattered and absorbed by matter, specimens to be observed in the electron microscope must be prepared to be less than one micron in thickness; furthermore, the interior of the microscope must be carefully evacuated to prevent collisions between the clectrons and the molecules of the air. Finally, as already mentioned, the lenses are formed by axially symmetric magnetic or electric fields, and not by any material medium such as glass. Apart from these basic differences, the electron microscope closely

Jan 1, 1943

By K. G. Davis, P. Fryzuk

WEINBERG,' in an investigation of solute distributions along unidirectionally solidified rods of dilute silver in tin alloys, concluded that, for rods of 2 mm diameter or larger, a very high degree of convective mixing takes place in the melt ahead of the advancing interface. Suggested causes for this mixing were (1) thermal convection, (2) convective currents set up by changes in fluid density associated with concentration gradients, and (3) currents set up by changes in volume during freezing. Evidence was presented that causes (2) and (3) were not primarily responsible for solute mixing. Further, convective mixing took place in horizontal rods with temperature gradients as low as 6°C per cm, putting doubt on the importance of thermal convection. In the present work, convective mixing is examined in melts with known initial solute distributions. The absence of a moving solid-liquid interface eliminates convection caused by volume changes on solidification. In the first experiment, three silica tubes 2 mm in diameter and approximately 20 cm long were filled with an alloy of 100 ppm Ag in tin (99.999 pct purity), placed adjacent to one another in a horizontal furnace, and solidified from one end at 1 cm per hr. A110, a Y emitter, was used as tracer. A few centimeters at the start of the rod were left un-melted, to determine the initial concentration Go. After solidification was complete, one sample was removed. The hot furnace was then brought back to

Jan 1, 1965

By J. H. Swisher

The rate of internal sulfidation of austenitic Fe-Ti alloys in H2S-H2 gas mixtures is controlled primarily by sulfur diffusion, with counterdiffusion of titanium playing a minor role. At temperatures below 1100°C, enhanced diffusion along grain boundaries becomes important. The rate of internal sulfidation at 1300°C is approximately equal to the rate computed from the sulfur diffusion coefficient. The diffusion coefficient of titanium in y iron has been determined from electron microprobe traces in the base alloy near the subscale interface. The solubility of sulfur in Fe-Ti alloys has been measured in the temperature range from 1150° to 1300°C. The equilibrium sulfur content is found to increase with titanium content, due to the large effect of titanium on the activity coefficient of sulfur. The Ti-S interaction becomes stronger as the temperature decreases. TITANIUM as an alloying element in stainless steels is an effective scavenger for interstitial impurities, carbon in particular. Titanium is known to form stable sulfides; however extensive thermodynamic data on the Ti-S system are not available. Schindlerova and Buzek1 have shown that the Ti-S interaction in liquid iron is moderately strong. There have been no previous studies of the Ti-S interaction in solid iron. Internal sulfidation of Fe-Mn alloys was the subject of a recent investigation by Herrnstein.2 He found the rate of internal sulfidation to be an order of magnitude greater than predicted from available solubility and diffusivity data. A satisfactory explanation for the discrepancy could not be given. In the present study, the solubility of sulfur in austenitic Fe-Ti alloys was measured using a standard gas equilibration technique. Fe-Ti alloy specimens were also internally sulfidized. The rate of internal sulfidation was measured as a function of temperature and alloy composition. Supplementary electron micro-probe measurements were made to provide additional information on the nature of the internal sulfidation process. EXPERIMENTAL The starting materials were alloys containing 0.12, 0.24, 0.38, and 0.54 wt pct Ti. The alloys were made in an induction furnace by adding titanium to electrolytic iron that previously had been vacuum-carbon-deoxidized. The major impurity in the alloys as determined by chemical analysis was carbon. The carbon content of the alloys averaged about 100 ppm; metallic impurities were presented in concentrations of 50 ppm or less. Specimens were made in the form of flat plates, 0.03 by 2 by 4 cm for the equilibrium measurements and 0.5 by 1.5 by 3 cm for the rate measurements. The experiments were performed in a vertical resistance furnace wound with molybdenum wire and containing a recrystallized alumina reaction tube. In the gas train, flow rates of the reacting gases were measured using capillary flow meters. The source of H2S was a mixture of approximately 2 pct H2S in H2, which was obtained in cylinders from the Matheson Co. A chemical analysis was provided with each cylinder. The H2-H2S mixture was diluted with additional hydrogen to obtain the desired ratio of H2S to H2, and the resulting mixture was diluted with 30 pct Ar to minimize thermal segregation of H2S in the furnace. Argon was purified by passage over copper chips at 350°C and subsequently over anhydrone. Hydrogen was purified by passage over platinized asbestos at 450°C and then over anhydrone. The H2-H2S mixture was purified by passage over platinized asbestos and then over Pas. The samples used in the solubility measurements were analyzed for sulfur by combustion and iodometric titration. The subscale thickness in the internally sulfidized samples was measured on a polished cross section, using a microscope with a micrometer stage. Electron microprobe traces for titanium in solution were made on several samples that had been internally sulfidized. A Cambridge microanalyzer was used, and the known titanium content at the center of the specimen was used as a calibration standard. The procedure for the microprobe measurements will be described further when the results are presented. RESULTS AND DISCUSSION Equilibrium Data. Fig. 1 shows the sulfur concentration as a function of gas composition for three alloys equilibrated at 1300°C. The dashed line is based on data published by Turkdogan, Ignatowicz, and pearson3 for pure iron. The breaks in the curves are the saturation points for the alloys. The fact that the initial slope decreases with increasing titanium content indicates that titanium interacts strongly with sulfur in solution. To obtain information on the composition of the precipitating sulfide phase, the measurements described in Fig. 1 were extended to higher sulfur partial pressures. These results are shown in Fig. 2. (The initial portions of the curves are reproduced from Fig. 1.) The highest PH2s /pH2 ratio used is believed to be below the ratio required for the formation of a liquid sulfide phase. Time series experiments were used to study the approach to equilibrium in the samples. It was found that equilibrium with the gas phase was reached in less than 4 hr at 1300°C.

Jan 1, 1969

By F. K. Pence

THE reduction of the firing of clay wares to a science has been one of the most difficult problems of modern ceramic engineering. The number of factors involved in the treatment of these wares has been such a complicated composite of the chemical and the physical properties that, according to the old practice, results depended rather on the art of the operator than on any scientific data available. The combined influence of the chemical and physical properties of clay minerals renders it difficult to apply the data obtained in one operation to the forecasting of details to be applied in another. In maturing clay-ware bodies by the application of heat, the chemical reactions involved are, in general, incomplete. The object frequently is to secure a certain physical quality, as density, color, or strength, rather than any particular chemical composition or development: This is more generally true of the so-called crude clay products. In the case of certain more high-grade wares, as the porcelains, it is necessary to reach the temperature required to bring about a certain molecular development or crystalline structure; but even here, time and temperature are at work and must be considered jointly. The conditions attending the firing of clay wares has led to the use of certain devices in the measurement of the progress of the firing process whereby the influence of the various burning factors on the clay composition under fire is indicated. In the simplest application of this practice, samples of the ware itself are so placed as to be drawn for observation at various intervals during the burn. Although the appearance is affected by the quick cooling treatment, by experience, this practice is successfully used, particularly in the brick industry. The settle of the setting of brick, as measured from the top of the kiln may also serve as a guide in the firing operation. Another example is found in the stoneware industry, where the practice of arranging test pieces made of the same composition

Jan 9, 1919

By D. R. Parrish, T. M. Geffen, R. A. Morse, G. W. Haynes

Flow tests on small core plugs have indicated that a large amount of gas is trapped and not recovered by water flooding a gas sand. Instead of I to 15 per cent pore space, as is usually assumed, the residual gas saturation is 15 to 50 per cent pore space, and is thus of the same magnitude as residual oil after water flooding oil sands. A thorough investigation was made to ascertain that large amounts of residual gas actually remain in reservoirs after a water flood and that this condition is not merely a laboratory phenomenon. In field experiments, the amount of gas left in a watered-out gas sand was measured by use of a pressure core barrel and the residual gas saturation of two watered-out gas sands was determined by electric log evaluation. In the laboratory, an investigation was made of factors that could possibly cause the value of residual gas saturation as measured on small core plugs to differ from that in the reservoir, and the effect of these factors on the amount of residual gas saturation was studied. The factors studied include flooding rate, static pressure, temperature, sample size and saturation conditions before flooding All evidence established that a relatively high gas saturation is trapped in water flooded gas sands and that this residual gas saturation can be measured in the laboratory by tests on small core plugs. INTRODUCTION There. has been general agreement among engineers that very high recovery of gas could be obtained from natural reservoirs By water displacement. Gas recoveries of 80 to 95 per cent of the original gas in place have become the normal expectation in water drive fields. The assumption of high recovery has been based on: 1. low density and viscosity of gas compared with water; 2. the erroneous assumption that the flow relationship in a gas-liquid system where gas is the displaced phase will be the same as when it is the displacing phase. It has long been recognized that gas can flow at very low gas saturations (in the range of 1 to 15 per cent pore space) in systems where liquid is being displaced by gas. By assuming the reversibility of this process, the conclusion was reached that the residual gas saturation following water flooding of a gas reservoir would be the qame (1 to 15 per cent) as that at which gas first flowed continuously as a displacing phase. Recent laboratory relative permeability Studies have demonstrated that the flow characteristics are very different in gas-liquid systems, depending on whether gas is displacing or being displaced by, a liquid. Also, it has been shown that there is no difference between the flow characteristics of oil and water or gas and water in water wet porous rocks. The residual gas saturation that can be expected following water flooding of a gas reservoir then would be in the same range as the residual oil saturation normally expected after water flooding an oil reservoir! i.e., in the range of 15 to 50 per cent pore space, depending on the rock characteristics. Obviously, such a difference in residual gas saturation means very important differences in recoverable gas reserves from water drive reservoirs. For example, if the original gas saturation in a field were 70 per cent, and the residual gas following flooding were 35 per cent, only half of the gas in place could be recovered by complete water drive, compared to the previously expected 80 to 95 per cent. This is a situation in which complete pressure maintenance could result in very greatly reduced recovery, since straight pressure depletion recoveries from gas reservoirs can approach 80 to 90 per cent. Such a change in thinking must be based on more complete information than a series of small core tests. Hence the work reported herein was undertaken with the objective of determining whether or not residual gas saturations indicated from small core relative permeability tests at atmospheric pressure and room temperature are representative of the residual gas saturations which could be expected after water flood of natural reservoirs. A study was made both through laboratory and fields tests to determine any differences in residual saturation which might be occasioned by differences in pressure, temperature, rate of flooding, and original saturation conditions. Four separate types of laboratory experiments and two field mesurements were made in this investigation. The apparatus and testing methods of each will he discussed individually. LABORATORY EXPERIMENTS, APPARATUS AND PROCEDURE Relative Permeability Tests Steady state flow experiments Here conducted using the Penn State type apparatus. The equipment used has beer (described in a previous publication? "Irreducible" water satu-ration was established in the core' by imposing ,a capillary pressure of 45 psi before simultaneous flow of air and water

Jan 1, 1952

By Theodore R. Butkovich, Jesse L. Yow

Geological storage of spent-fuel assemblies from an operating nuclear reactor has been underway since the Spring of 1980 at the U.S. Department of Energy's Nevada Test Site. The primary objective of this generic test is to evaluate granite as a medium for deep geological storage of high level reactor waste and to provide data on thermal and thermomechanical behavior of granite from imposed heat loads.(l) The underground installation in the Climax stock granite was sited at about 420 m below the surface and 145 m above the existing water table. As shown in Figure 1, three parallel drifts were excavated spaced on approximately 10 m centers. Seventeen storage holes were drilled at the central drift on 3 m centers in which eleven spent fuel canisters and six thermally identical electrical simulators were emplaced. Electrical resistance heaters were emplaced in vertical holes in the floor of the side drifts on 6 m centers. The thermal output of these heaters is being periodically adjusted to simulate the thermal response of a large storage array. Rock and ventilation air temperatures are being measured continuously in the drifts and throughout the rock surrounding the excavations. Measurements of drift deformation have been made routinely since the emplacement of the spent fuel. Both vertical and horizontal measurements are being taken at five locations along the heater drifts and at six locations along the central canister drift (Fig. 1). Two types of instrumentaton are being used: convergence wire extensometers which are monitored automatically, and a manually operated tape extensometer with which measurements are taken periodically. The tape extensometer measurements were initiated about 6 weeks following fuel emplacement. The lack of a temperature correcting capability for the convergence wire extensometers make that data unavailable for analysis at this time.

Jan 1, 1982

By W. E. Bearce

The recent concern for the recovery of even the finest fractions of coal preparation plant feeds has created needs for new equipment. Thermal dryers currently available have difficulty reducing the filter cake moisture on down to the desired point. This difficulty involves 1) the physical problem of handling this wet, sticky material and making each particle accessible to the hot gases, and 2) removing the extremely fine dried particles from the cooled gases. The dryer described in this paper handles the first of these problems, and eliminates the second by the substitution of steel balls for air as the heat transfer medium. As a general statement, the cost of preparing coal for market is inversely proportional to the size of the lumps or particles. In the not too distant past the finer sizes were discarded as being uneconomical to treat and this practice might be still continuing if it were not for the insistence of the public that this material be kept out of our streams. This being the only cost-free outlet, the disposal of fine refuse became a significant item of expense in every preparation plant. When this happened it was only reasonable to look to the recovery of the values in this material, not only to defray this expense, but to reduce the tonnage which had to be wasted. There seemed to be no device available suited to reducing the moisture in this material to what the market requires. All of the fine coal dryers commonly employed make use of air to bring the heat of combustion into contact with the coal particles. Any device employing air as a heat transfer medium, has the following two strikes against it in attempting to handle 28 mesh by 0 filter cake: 1) It is practically impossible to bring the hot air into intimate contact with the enormous number of fine particles stuck together in the cake. 2) Even if this can be effected, it is impossible to remove the dried coal from the air. A wet scrubber must be employed, the discharge of which must go back to the filter and dryer as a circulating load of the most objectionable sort, being the extreme fines. Various compromises have been used to cope with the problem of drying this relatively small tonnage of high moisture coal. Often some of the dried coal is mixed back with the feed to the dryer in an attempt to make the mixture more handleable and more available to contact with the hot air than the filter cake alone would be. This may help to some extent with the first problem but it does nothing about the second and a dryer operated in this way has to be oversized. Sometimes the filter cake is mixed with a coarser fraction for the same reason. Here again, while this may make a mixture (the particles of which are more readily brought into contact with the hot air), the problem of getting the fine coal out of the air remains and a larger percentage of the total coal to be dried is handled by the most expensive means. Mechanical dewatering has accounted for more and more of total coal drying lately and in many cases would satisfactorily handle the whole load, down to 28 mesh, if there were a means available for doing a good job on the —28 mesh by itself. The dryer which is the subject of this paper was designed expressly for doing this job — drying fine material by itself regardless of how wet it may be to start with, how fine it may be, or how gummy and sticky these properties in combination may make it. The essential features are depicted in Fig. 1. A rotating cylinder is supported on a frame in such a way that one end may be raised or lowered by hy-

Jan 1, 1968

By W. H. Bassett, C. H. Davis

In the commercial annealing of cartridge brass there are four points regarding which definite data are essential. They have to do with the correct interpretation of grain count in its relation to annealing temperature and, incidentally, to Brinell hardness. These points are: 1. The comparison of the grain sizes of two cartridge-brass mixtures: 69 copper, 31 zinc, 0.376-in. (9.5-mm.) gage; and 68 copper, 32 zinc, 0.130-in. (3.3-mm.) gage 2. The comparison of the grain sizes of annealed metal that had previously been reduced by rolling varying amounts; for instance, 20.0, 36.6, 50.9, and 59.1 per cent. 3. The determination of standards for grain sizes on annealed brass of the composition 68 per cent. copper, 32 per cent. zinc and 69 copper, 31 zinc. 4. The comparison of grain size with Brinell hardness on identical samples of annealed metal. In their comprehensive and thorough investigation of the recrystal-lization of cold-worked alpha brass on annealing,l Mathewson and Phillips have discussed the relations between temperature of anneal, degree of deformation, and structural alteration in alpha brass. They have also shown certain comparisons between the ordinary physical properties and the grain size of annealed brass. The purpose of the present investigation is mainly concerned with the grain size of cartridge brass, its relation to Brinell hardness, and the publication of sufficient data to enable those engaged in the inspection of such material to have a correct foundation upon which to work. The first alloy was taken from regular mill stock that had been rolled from 0.580 in. to 0.376 in. (14.7 mm. to 9.5 mm.) gage, a reduction of 35.1 per cent. This bar (No. 1) had the following composition: Copper, 69.20 per cent.; zinc, 30.76 per cent.; lead, 0.02 per cent.; iron, 0.02 per cent. The second alloy was also taken from mill stock of 0.325 in. (8.25 mm.) gage and was rolled as shown in Table 1, in order to get four bars reduced two, four, six, and eight B. & 5. numbers respectively. This second alloy

Jan 1, 1919

THE following employment items ore made available to AIME members on a nonprofit basis by the Engineering Societies Personnel Service, Inc., operating in cooperation with the Four Founder Societies. Local offices of the Personnel Service ore at 8 W. 40th St., New York 18; 100 Farnsworth Ave., Detroit; 57 Post St., Son Francisco; 84 E. Randolph St., Chicago 1. Applicants should address all mail to the proper key numbers in care of the New York office and include 6c in stamps for forwarding and returning application. The applicant agrees, if. placed in a position by means of the Service, to pay the placement fee listed by the Service. AIME members may secure a weekly bulletin of positions available for $3.50 a quarter, $12 a year. MEN AVAILABLE Graduate Mining Engineer, 31, married. Six years' engineering experience, mining and construction, U. S. A. and Alaska. Underground metal mining, production, development, geology, mine engineering. Engineering on airfield construction, earthwork, location work, mapping, topography, road location; office work. Commercial pilot license. Desires position mining or construction. Available 45 days. Prefer Latin America. M-676-477-E-8-San Francisco. Mining Engineer, 42, married, one child. Fourteen years' mining with much supervisory experience in developing and operating metal mines; also mine safety engineering. Familiar with many large and small mines in the western U. S. and Mexico. Excellent references. M-677.345-E-1¬San Francisco.

Jan 1, 1952

By Carls Benedicks

It is well known by every one who has had to deal with boiler tubes that these are often seriously affected by a sort of corrosion, occurring as a local pitting, that frequently causes a perforation of the tube in a rather short time. The characteristic appearance of this corrosion is shown in Fig. 1. A very similar corrosion occurs in condenser tubes (Fig. 2).l A study of the microstructure or local chemical composition of the metal (iron 70:30 brass) fails to reveal any cause for this pitting. Of course one might possibly assume the starting point to be some oxide particle, causing an electrolytic local action, but this in no way explains the continued corrosion, progressing even when the assumed oxide particle must have disappeared. By the excellent work done by the Corrosion Research Committee of the Institute of Metals, and communicated, in October, 1923, to the Institution of Engineers and Shipbuilders in Newcastle-on-tyne, stress was laid on the faot that a content of entangled air has a very obnoxious effect. In the following correspondence, Sir George Goodwin stated that "engineers have, for a long time past, regarded air as the big enemy to be fought against in all questions of corrosion'72 and Kenneth Fraser pointed out that the most vital point is "the avoidance or removal of possibly the chief cause of present day corrosion, i. e. entrapped air and gases brought out of solution."3 In their reply, however, the authors state that they had "never for a moment believed that entangled air was responsible for the beginnings of corrosion, and express the opinion that the gradual liberation of air could not account for localized corro~ion."~ On consulting the many textbooks on corrosion, as that

Jan 1, 1925

By P. van Meurs, C. van der Poel

From observations of the linear displacement of oil by water from a porous medium as visualized in transparent models, new insight into the mechanism of vircous fingering, as occurring in the case of unfavorable oil-water viscosity ratios, has been obtained. A mathematical description of the observed phenomena leads to formulas. expressing both oil production and pressure drop across the formation as a func-tion of cumulative water injection with the oil-water viscosity ratio as a parameter. Theoretical results are compared with those obtained from scaled laboratory experiments in sand-filled rubes in which water was injected at the one end and production was obtained from the other end. In the second part of the paper the same principles are used to calculate a more realistic production scheme in which production of oil and water is obtained from wells regularly distributed over the field. Results show satisfactory agreement with production data of an actual oil field. Application of the theory is extremely simple as only a limited number of readily available parameters have to be known and results are presented in an analytical form. INTRODUCTION When oil is displaced from a porous medium by water having a viscosity lower than the oil. the oil-water interface is essentially unstable and has the tendency to break up into what are called "fingers" or "streamers". This Viscous fingering has been noted before by Engelberts and Klinkenberg' and has recently been demonstrated in transparent models by van Meurs-. It is highly questionable whether it is at all possible to perform relative permeability measurements In the laboratory reproducing the same distribution of water and oil in the cores as Present in practice. Therefore, we based our descriptive theory on an idealized model which was "tailored" to the fingering mechanism as observed in transparent models under scaled conditions. This approach was the more attractive, as a highly simplified model had already yielded an adequate description of the process. Though we are aware our theoretical approach can be extended in several ways, it is given here in its simplest form to explain the fundamental principles and to avoid complicated formulas. SIMPLEST CASE OF A LINEAR DRIVE Observations and Theoretical Model In Fig. 1 a series of photographs shows how water penetrates into a formation saturated with an oil which is considerably more viscous than the water. The technique for obtaining these photographs, using transparent models, has already been described?. The fingers can be clearly observed and are seen to be mainly parallel to the flow direction. Note that the contours of these fingers are not smooth but show protrusions of water enclosing oil pockets.

By C. A. Siebert, D. J. Girardi

PRACTICALLY every metallurgical process in-volves, at some stage or another, the contact of a metal with a gas. Because of this, gas-metal re-actions are of great practical importance and have been subjected to numerous investigations. It has long been recognized that the presence of cuprous oxide in liquid copper has an important effect on its casting characteristics and .physical properties. This has led to the desirability of determining the quantitative relationships between cuprous oxide in the liquid copper and the usual gases present during processing. Such data are not only of practical importance but also of a theoretical interest in that they provide a means of applying the principles of physical chemistry to problems in applied metallurgy. The object of this investigation was to determine the quantitative relationship at equilibrium between the gases carbon monoxide and carbon dioxide and the cuprous oxide content of liquid copper. The reaction and its equilibrium constant may be expressed as follows: 2 Cu (liq) + CO2 (g) = Cu2O + CO (g) acu2o X aco/a2 cu X aco2 Here the underlined symbol Cu2O designates cuprous oxide dissolved in liquid copper and (a), the activity of the various constituents. The activities of carbon monoxide and carbon dioxide are assumed to be directly proportional to their re- spective partial pressures and the activities of cuprous oxide and copper are taken to be proportional to their respective mol fractions. The equilibrium constant may then be expressed as follows: K2 = Ncu2o X Pco [Ncu]2 X Pco2 where N = mol fraction The solubility of carbon monoxide and carbon dioxide in liquid copper is a rather controversial subject.'-' A review of the literature is given by 0. W. Ellis.' It appears that carbon monoxide and carbon dioxide are both only very slightly, if at all, soluble in liquid copper. Volskii and Slobodskoi5 determined the equilibrium between carbon monoxide, carbon dioxide, and liquid copper at 1100°C. Their results show a higher cuprous oxide content for a given CO/CO2 ratio than found in the present work. The system hydrogen, water vapor, and liquid copper was investigated by Allen and Hewitt8 over the temperature range of 1090" to 1350°C. Equilibrium values for the system carbon monoxide, carbon dioxide, and liquid copper calculated from these data agree reasonably well with the present work. Materials and Procedure The copper used was oxygen free, designated as OF and analyzed as 99.98 pct copper with no appreciable amount of any one impurity based upon spectrographic determinations. The carbon dioxide was cylinder gas averaging about 99.95 pct CO2 with air as the major impurity. The carbon monoxide was produced by passing carbon dioxide over heated charcoal. Alundum combustion boats were used as containers for the liquid copper. No appreciable reaction took place between the copper and the alumina. This was evident from the fact that the copper sample after a run did not ordinarily adhere to the bottom of the boat and that the

Jan 1, 1951