By M. C. Udy, F. W. Boulger

AN incomplete phase diagram for the U-Ti systern was determined earlier 1 and more recently, a tentative diagram was presented for the uranium-rich end of the system.' In the present re-examination of the whole system of U-Ti alloys, high purity materials were used. Melting stock for the alloys was high purity uranium, containing about 0.09 pct C as the only appreciable impurity, and high purity iodide-process titanium purchased from New Jersey Zinc Co. Both metals were cold rolled to about 1/6 in. thickness, sheared to about I/' in. squares, and cleaned by pickling. The alloys were arc melted under a helium atmosphere in a water-cooled copper crucible. A thoriated-tungsten electrode was used. The furnace chamber was evacuated, then flushed with helium, prior to each melting. It was finally filled with stagnant helium at one atmosphere pressure. Each alloy was remelted three times after the original melting, to insure homogeneity. The alloy button was turned bottom side up before each re-melting operation. Some 22 alloys were examined. Their compositions were spaced at appropriate intervals between 100 pct Ti and 100 pct U. Analyses were made on chips taken after fabrication. The major contaminant was carbon, which varied from 0.03 to 0.08 pct. It appeared in the microstructure as titanium carbide. Alloy compositions were calculated to a carbon-free basis for consideration on the diagram. Tungsten and copper, possible contaminants from the melting operation, were generally less than 100 parts per million each. Fabrication All alloys were forged and rolled to bars approximately V8 in. square. They were clad either in SAE 1020 steel or in a 5 pct Cr-3 pct Al-Ti-base alloy, depending on the fabrication temperature. A temperature of 1800°F (980°C) was used for alloys near the compound composition. This necessitated using the titanium-base alloy, since iron reacts with titanium at this temperature, producing a low melting alloy. Other alloys were fabricated at 1450°F (790°C), using steel jackets. No iron-titanium reaction occurred at this temperature. The jackets were welded in place in an argon atmosphere. Those alloys sheathed in steel were declad and then reclad between rolling and forging operations. On the other hand, those clad with the titanium alloy were cut to a roughly rectangular shape prior to clading and were then carried through both the forging and rolling operations without opening. Those alloys near the compound composition were found to be cracked when the clading was removed. The cracked materials had been plastically deformed, however, and at least some of the cracking had OCcurred during cooling. Heat Treatment The rolled bars, after being declad and shaped to remove surface contamination, were all given an homogenizing treatment of 160 hr at 2000°F. (Samples were taken for analysis following the declading and shaping operations.) All were heat treated at the same time in one furnace, but each was sealed in a purified argon atmosphere in an individual Vycor glass tube. Argon pressure was such that it was approximately atmospheric at temperature. One end of each tube contained titanium chips and this end was heated to 1200°F (650°C) for 10 min prior to the heat treatment. This purged the atmosphere of residual reactive gases. The balance of the tube was warmed during the purge to liberate adsorbed moisture and gases, which also reacted with the hot chips. The bars were furnace cooled from the homogenization treatment. Specimens of each alloy were water quenched after 2 hr heating at 1000°, 1200°, 1400°, 1600°, 1800°, and 2000°F (540°, 650°, 760°, 870°, 980°, and 1095°C). In addition, some were treated at intermediate temperatures of 1300°, 1500°, and 1700°F (705", 815", and 925°C) and at 2150°F (1175°C). Specimens, about '/s in. cubes, were cut from the bars, sealed in individual Vycor tubes, and heat treated as described. All specimens heat treated at the same temperature were processed together. Samples were quenched by breaking the Vycor tube rapidly under water. Metallographic Examination Specimens were mounted in bakelite and ground wet on 180 grit paper held on a 1750 rpm disk. They were then ground wet by hand, using 240, 400, and 600 grit papers. The rough grinding was continued long enough to get well below the surface. Specimens were mounted separately because of the variation in the rate of etching between alloys. The specimens were polished with rouge on a 4 in., 1725 rpm wheel covered with Miracloth. Alloys on the titanium side of the compound composition were etched with a solution of 2 pct hydrofluoric acid in water saturated with oxalic acid. A few crystals of ferric nitrate were added as a bright -ener. Specimens were immersed 5 sec, polished to remove the etch, then re-etched. With the higher titanium alloys, it was often necessary to start the etch on the polishing wheel, because of the formation of a passive film. In some instances, a plain 2 pct hydrofluoric etch was satisfactory. For the alloys on the uranium side of the compound, a distinction between the compound and the uranium phase developed after standing a short time in air. This could be hastened by the application of heat, such as obtained by placing the specimen on a radiator. A deep etch was necessary to develop details in the uranium-rich phase, such as the Widmanstaetten pattern sometimes obtained by quenching y uranium. A 2 pct hydrofluoric acid solution was used for this deep etching.

Jan 1, 1955

By R. F. Mehl, R. W. Parcel

THE rate of the decomposition of austenite in eutectoid steels, forming only pearlite, may be expressed fundamentally in terms of the rate of nucleation and the rate of growth of pearlite nodules. This matter has received much attention in recent years. (The basic references are listed in ref. 1; references of particular import to the present work will be given separately.) Systematic data have been developed for plain carbon eutectoid steels.:! Although the physical factors affecting the rate of nucleation, N, in case of plain carbon steels have presumably been identified, they cannot as yet be evaluated quantitatively.' Several somewhat successful attempts, however, have been made to calculate the rate of growth, G. In the latter case the important factors determining the edgewise growth of pearlite have been assumed to be: 1—the interlamellar spacing; 2—the concentration extremes and concentration contours of carbon in austenite in front of the growing pearlite interface; and 3—the rate of diffusion of carbon in austenite.* The only systematic data on N and G for pearlite in alloy eutectoid steels are those for Co-steels;6 there are no data on alloy eutectoid steels in which the alloying element is known to decrease the rate of formation of pearlite, apart from a few scattering data reported earlier' for steels containing manganese. This paper reports a systematic study of N and G for eutectoid alloy steels containing molybdenum and nickel, respectively. In order to provide information of help in understanding the results, new data are presented on the effect of molybdenum on the interlamellar spacing of pearlite, So; data on the effect of nickel on So have already been published.' The alloys used were in five groups: 1—Pure Fe-C-Mo alloys (Table I) were supplied by the Climax Molybdenum Company of Michigan, Detroit. They were made from Armco ingot iron of standard analysis, Acheson graphite, and ferro-molybdenum, melted in silica-lined crucibles in a high frequency induction furnace. The ferromolyb-denum was added to the melted steel, followed in 5 min by 0.08 pct Al. The ingot as-cast measured 23/4x 31/4x10 in.; it was hot-forged at 1150°C to a bar 1 in. sq.

Jan 1, 1953

By Walter Weeks

THE process of cooling air by allowing it to expand and do work in an engine is well known, but the theory of obtaining cold air by free expansion without the aid of an engine operating with cutoff has been little discussed. CASE I If compressed air is allowed to expand to the atmospheric pressure through an orifice in an air line that is supplied by a running compressor, no cooling results except the negligible one due to the Joule-Thompson effect, which will not be considered in this discussion. The effect of moisture will also be neglected.

Jan 1, 1937

By Messervey, J. P.

NOVA SCOTIA is sharing in the rapid advance of the mining industry that is one of the remark- able features of Canada's recent progress. The production of coal and gypsum has increased rapidly, and there has also been a marked development in the mining of gold, salt, zinc, copper and other minerals. Coal, the basis of the principal mining industry in the Province, was discovered by the early explorers on the shore of Cape Breton Island, and used by the garrison at Halifax as early as 1749. The first government record shows total annual sales amounting to 1668 long tons in the year 1785, while last year production was 6,643,000 long tons. The principal mines are discussed in a separate paper by Alexander L. Hay1.

Jan 1, 1928

By R. M. Leibrock, C. W. Ziemer, R. P. Vincent

The Stanolind flowmeter, which employs a hot-wire anemometer connected in a Wheat-stone bridge circuit, has proved useful for determining the relative productive ability of individual sand members of gas wells. The operation of this instrument in measuring gas velocities in the well bore above each producing member has provided both a direct and accurate means of analyzing reservoir performance. Results of tests conducted with the well flowmeter in the Hugoton gas field of western Kansas have indicated some rather unusual production characteristics. In two cases it was found that all or the greater part of the total gas produced was coming from one section in wells where four "pay" sections had been perforated individually. These actual measurements contradict in many instances the indications of data obtained from electric logs and from core analysis; the fact that these latter sources often give incorrect results, demonstrates the necessity of a method, such as is provided by the well flowmeter, for accurately determining the amount of gas coming from each producing member. Introduction In any gas well where a number of pay sections have been perforated individually and are producing to a common outlet, the question arises as to the relative amounts of gas being passed through each set of perforations. In the past it has been the policy to depend on core analysis to estimate relative productivities, or, where the sections were not cored, to obtain some idea of production characteristics from electric-log studies. The weaknesses in these methods are readily apparent and indicate the need for more reliable means of measuring gas flow from each zone. The Stano-lind flowmeter* was developed for this purpose. Preliminary tests were made with the instrument in the Katy gas field near Houston; however, the bulk of the routine work with the well flowmeter has been confined to the Hugoton gas field in western Kansas, where results obtained have been encouraging. A description of the instrument, the field technique employed in testing, and a few of the results obtained in the Hugoton area are discussed in this paper. Description or Instrument The well flowmeter is 1¾ in. od and 7 ft long; it is entirely self-contained, can be run through tubing as small as 2 in. id in wells with high pressure (4500 psi) and temperature (210°F) and is lowered on a wire line commonly used for other instruments of the bottom-hole type at falling rates up to 500 ft per minute. It will detect gas flow as low as 10 ft per minute linear velocity, and yet withstand and record velocities of 1000 ft per minute without damage to the detecting element. Killing the well is not required nor desirable for running a production profile when using the instrument, and it is necessary to stop flow for only a short time. The detecting element of the instrument is a hot-wire anemometer connected in a

Jan 1, 1948

By R. M. Leibrock, R. P. Vincent, C. W. Ziemer

The Stanolind flowmeter, which employs a hot-wire anemometer connected in a Wheat-stone bridge circuit, has proved useful for determining the relative productive ability of individual sand members of gas wells. The operation of this instrument in measuring gas velocities in the well bore above each producing member has provided both a direct and accurate means of analyzing reservoir performance. Results of tests conducted with the well flowmeter in the Hugoton gas field of western Kansas have indicated some rather unusual production characteristics. In two cases it was found that all or the greater part of the total gas produced was coming from one section in wells where four "pay" sections had been perforated individually. These actual measurements contradict in many instances the indications of data obtained from electric logs and from core analysis; the fact that these latter sources often give incorrect results, demonstrates the necessity of a method, such as is provided by the well flowmeter, for accurately determining the amount of gas coming from each producing member. Introduction In any gas well where a number of pay sections have been perforated individually and are producing to a common outlet, the question arises as to the relative amounts of gas being passed through each set of perforations. In the past it has been the policy to depend on core analysis to estimate relative productivities, or, where the sections were not cored, to obtain some idea of production characteristics from electric-log studies. The weaknesses in these methods are readily apparent and indicate the need for more reliable means of measuring gas flow from each zone. The Stano-lind flowmeter* was developed for this purpose. Preliminary tests were made with the instrument in the Katy gas field near Houston; however, the bulk of the routine work with the well flowmeter has been confined to the Hugoton gas field in western Kansas, where results obtained have been encouraging. A description of the instrument, the field technique employed in testing, and a few of the results obtained in the Hugoton area are discussed in this paper. Description or Instrument The well flowmeter is 1¾ in. od and 7 ft long; it is entirely self-contained, can be run through tubing as small as 2 in. id in wells with high pressure (4500 psi) and temperature (210°F) and is lowered on a wire line commonly used for other instruments of the bottom-hole type at falling rates up to 500 ft per minute. It will detect gas flow as low as 10 ft per minute linear velocity, and yet withstand and record velocities of 1000 ft per minute without damage to the detecting element. Killing the well is not required nor desirable for running a production profile when using the instrument, and it is necessary to stop flow for only a short time. The detecting element of the instrument is a hot-wire anemometer connected in a

Jan 1, 1948

By Willard P. Ward

SOME TIME in the year 1874 or 1875, I conceived the idea that spiegeleisen might be made -in a blast furnace from ores that were not carbonates, and which did not contain both manganese and iron in the same ore. Up to this time, such ores had formed the basis of all the spiegel that had been produced; and all the ferromanganese that was on the market before 1875 was made in crucibles, and cost about 00 per ton, for 80 per cent. Mn. I consulted the great steel metallurgist of the day, Alexander Holley, who listened attentively to what I had to say, and told me he did not think my plan was practical, so I abandoned it for the time being. But I was so stubborn that I could not get the notion out of my head. It seemed to me that a good metallurgist should be able to work the thing out in some way. I had already had some experience in smelting refractory lead ores in Utah, and was young and not lacking in self confidence, so after waiting a bit, I got Anton Eilers, the best all-around metallurgist I knew, and J. H. Bramwell, the best iron blast-furnace man I knew, both intimate friends of -mine, to come to my place in Bartow County, Georgia, and look over things. They remained for several days, and made all the examination they thought necessary; and they also advised me to give up the project, and either to keep the furnace running on car-wheel iron or to blow it out. After my talk with Holley, I improved my plant in several ways. I closed the top of the furnace, put in a hot-blast stove, a steam boiler and a Weimer blowing-engine which gave me blast enough, at a pressure high enough for all the requirements of, the furnace, and which I could bring up to a temperature of 600° to 700° F.

Jan 1, 1921

By J. Gordon Parr, A. J. Goldak

OgdEN et al.1 and Bumps et al.2 suggested that the solubility of aluminum in a titanium extended to 30 pct.* Sagcl,3 Clark and Terry,4 Anderko et al.,5 Ence and Margolin6 and Saulnier and croutzelles,7 subsequently proposed the existence of an intermetallic compound in the region of 25 pct Al. Although Anderko et al.5 suggested that the structure of this phase, Ti3Al, was of the DO,, (Ni3Sn) type, their conclusion was based only upon the results of a powder photograph that included reflections from ? = 0 to ?= 27° (CuK),some of which were reported to be indistinct. Ence and Margolin,6 referring to a 25 pct alloy (but without indicating whether the figure referred to weight or atomic pct) stated: "The structure of Ti2Al is isomorphous with Ti3Sn DO19, as pointed out by Pietrokowsky". But the point was not proven, because Ence and Margolin did not report values of calculated intensities of Ti2Al with the DO,, structure. In fact, the observed intensities they reported are in poor agreement with the values we calculate for DO19 (see Table I). Saulnier and croutzelle7 concluded, on the basis of electron micrography and microdiffraction studies, that the structure of the 25 pct A1 alloy was ordered hexagonal. Our purpose has been to unequivocally determine the Ti3Al structure. Alloys containing 25 pct Al were prepared from iodide titanium and spectrographic standard aluminum by levitation melting. The levitation chamber was evacuated to 10-6 mm Hg before filling with 99.999 + pct A. After casting, the alloy was chilled to liquid air temperature and crushed to -200 mesh in a percussion mortar. The powder, wrapped in molybdenum foil, was annealed (by induction heating) at 1000 "C for 2 hr in the argon atmosphere of the levitation chamber. No sublimate was seen on the foil or elsewhere, and therefore the assumption is

Jan 1, 1962

By F. W. Gordon

Since the waste gases of the blast-furnace came to be generally utilized in heating the blast and raising steam, the gradual improvement in the economy of fuel, mainly through the nse of higher temperature in the blast, has impoverished the gases. The increased output per unit of measurement of the furnace, and the increased height of the furnace, have markedly increased the resistance to the blast, thus enormously increasing the duty required from the gases. In other words, a gas reduced in heating power by a further dilution of CO, is required to raise the temperature of the blast to 1800' Fahr., where formerly 600' was a good temperature, and at the same time to raise steam enough to drive the air into the furnace at a pressure of from four to eight pounds in coke practice, and from eight to twelve pounds in anthracite practice, and also pump at least double the water formerly used at furnaces. Hence the necessity for the employment of the best scheme for thoroughly consuming these gases with the least dilution of air, and the use of the best device for absorbing the heat prodnced for the purposes above mentioned. In a former paper before this Society the writer called attention to such improvements as had been made by his firm, by which it was claimed 1400' Fahr. could be maintained in the blast by a less consumption of gas than was required to maintain 900' when using pipe-ovens; and it would not be too much to say that 1600' Fahr. might now be written in place of the 1-400. The object of this paper is to give the practice of our firm in the

Jan 1, 1884

By Pieter W. Greeff, Graeme W. Mitchell

INTRODUCTION This paper describes the underground environmental planning parameters developed for Pancontinental Mining Limited's Jabiluka uranium deposit. The deposit is located 230 km east of Darwin in the Alligator Rivers region of the Northern Territory, Australia. The deposit is situated within land subject to an Aboriginal land claim, adjacent to a National Park and within a proposed extension to that National Park, as well as being close to a long- established Aboriginal reserve. In addition, being the first large underground uranium mine planned in Australia, the environmental considerations, both on surface and underground are considerable. Pancontinental is committed to the highest practicable standard of environmental management in the operation of the mine. In addition, Government regulations and requirements are particularly stringent by world standards. The underground environmental problems are discussed later in the paper with emphasis placed upon radiation aspects, both gamma and radon daughters, and dust. Consideration has also been given to heat and humidity due to the location of the deposit in a sub-tropical region 12° south of the equator. The paper explains how these environmental factors influence the design and selection of stoping methods. GEOLOGY AND ORE RESERVES The Jabiluka Two orebody is completely overlain by flat-bedded Kombolgie Sandstone with a thin layer of surficial colluvial sands. The orebody occurs in an east-west striking folded succession of Lower Proterozoic metasedimentary rocks of the Cahill Formation. Uraninite and pitchblende constitute essentially all the uranium mineralisation and are contained in the four lithological series, as shown in Fig. 1. - ,Upper Graphite Series - Main Mine Series - Lower Mine Series 1 - Lower Mine Series 2 The succession at Jabiluka has been folded and forms an east-south-east striking, asymmetric syncline-anticline which dips south and plunges to the east. A major fault bisects Jabiluka Tw8 having a north-south trend and dipping about 80 to the west. A near vertical tourmaline granitic pegmatite dyke up to 30 m in thickness has intruded the Jabiluka Two orebody at the western end. Current drilled ore reserves for Jabiluka Two are 52.0 million tonnes at 0.39% U308. Included in these reserves are 1.1 million tonnes of gold ore at 10.7 g/tonne. A large proportion of the orebody can be mined in thick sections (over 80% of tonnage) either as single sections or by bulking a number of thin sections which are close together.

Jan 1, 1981

By P. T. Chiang

Chemical etching methods for the simultaneous revealing of the tellurium or selenium Phase and the chalcogenide grain boundaries of the alloy systems are given. A tellurium eutectic was found Present in zone-melted ingots. Similarly, a selenium monotectic was present in ingots. In general, the second phase (tellurium or seleniumn) occubies three different sites; viz., along the chalcogenide grain boundaries, as inclusions within the chalcogenide grain, and on the undersurface of the ingot. The detection limit for the tellurium phase is about 1 u in width. THERMOELECTRIC materials based on Group V (bismuth, antimony) and Group VI (selenium, tellurium) elements have aroused considerable interest in recent years in the practical application of thermoelectric cooling. In many cases, a small amount of excess tellurium (or selenium) was added to the material to optimize its thermoelectric properties. Then the question immediately arises as to the number of phases present in the resultant alloy. In the binary systems of Bi-Te, Sb-Te, and Bi-Se, the congruent melting compositions have been reported to be non-stoichiometric and are represented by Bi~Te respectively. It is to beexpected and known that Bi2Te3 and SbzTe3 crystallize from the melt with an excess of bismuth and antimony in the lattice and that tellurium forms a eutectic.~' The same could be assumed to take place in the pseudo binary systems of (Bi,Sb)zTe3 and Bi2(Se,Te)3 as well as in the system studiedby puotinen5 and other workers. Likewise, BiaSe3 crystallizes from the melt with an excess of bismuth in the lattice and selenium forms a monotectic.~ Therefore, in practice, alloys solidified from the melt often contain a second phase (tellurium or selenium) in one region or another of the solid mass even without the addition of excess tellurium (or selenium). ~u~~recht' studied the thermoelectric properties of (Bi,Sb)2Te3 alloys with excess tellurium and simultaneous additions of selenium. He mentioned that the materials show two phases because of the considerable excess of tellurium or selenium. However, he did not report as to how the tellurium or selenium phase was identified. It is generally believed that the presence of an excessive amount of tellurium or selenium phase in the alloy would adversely affect its thermoelectric properties and its uniformity. Consequently, there is a need for a simple method for the identification of the tellurium and selenium phase. The quantity of the second phase present is usually too small to be detected either by chemical analysis or by normal X-ray techniques. This investigation was therefore carried out, first, to devise a simple metallographic method for the identification of the tellurium or selenium phase coexisting with the chalcogenides and, second, to determine the distribution and specific location of the tellurium or selenium phase in the ingots. EXPERIMENTAL PROCEDURE The starting materials used for the alloy preparations were 99.999 pct pure bismuth, antimony, and tellurium and 99.997 pct pure selenium. The bismuth and antimony were obtained from Consolidated Mining and Smelting Co. of Canada Ltd., while the selenium and tellurium were obtained from Canadian Copper Refiners Ltd. The tellurium was purified further in the laboratory by zone refining. The elements were pulverized in a stainless-steel pestle and mortar. The amounts for the desired composition were weighed out each time on an analytical balance to make up a 100-g sample. Then the sample was introduced into a Vycor ampule (19 by 150 mm), pumped down to a vacuum of 10"5 Torr for 15 min, and sealed off. The ampule was then heated in a horizontal resistance furnace at 800" to 900°C for about 20 hr. During this period the assembly was rocked back and forth several times to ensure good mixing. At the end of the heating period, the ampule was quenched in cold water and then transferred to the zone-melting apparatus described in a previous publications to grow large-size aligned polycrystals. The background and ring-heater temperatures were adjusted to make the freezing solid-liquid interface slightly convex to the liquid. The recorded temperature gradient in the vicinity of the freezing solid-liquid interface was around 15°C per cm. The ampule was moved horizontally at a speed varying from 0.4 to 2 cm per hr so that the ring heater would cover the whole ingot length from end to end. A single zone-melting pass was used for the Bi-Te, Sb-Te, and Bi-Sb-Te ingots. Two passes in the forward and reverse directions were carried out for the Bi-Se and Bi-Se-Te ingots. Six passes in the forward and reverse directions were performed for the Bi-Sb-Se-Te ingot. The zone-melted ingots were found to contain several large crystals, with their basal planes (0001) approximately parallel to the growth axis. Samples of bismuth and antimony tellurides coated with a layer of tellurium, and bismuth selenide coated with a layer of selenium, were prepared for comparison in phase identification. These coatings were made by dropping a piece of the zone-melted ingot into some molten tellurium or selenium under argon atmosphere and allowing them to cool slowly to room temperature. The metallographic specimens were prepared by

Jan 1, 1969

By Rex B. McLellan, W. A. Oates, William W. Dunn

Vapor transport experiments have been carried out in order to determine the saturation solubility of carbon in cobalt and nickel with respect to graphite over a large temperature range. Some of the uncertainty existing in the thermodynamics of these systems has been removed and accurate estimates of the heat and entropy of solution of carbon in nickel and cobalt have been deduced. The relatitle partial entropies of carbon are considered to be predominantly vibrational in origin. ALTHOUGH the thermodynamic properties of solid solutions of carbon in cobalt and in nickel have been investigated previously, the results of these investigations show a marked lack of agreement amongst themselves. In this investigation simple vapor transport experiments have been undertaken in order to measure the temperature variation of the saturation solubility of carbon in nickel and cobalt with the object of removing to some degree the uncertainties in the thermodynamics of these systems. In the case of the C-Co system, early measurements of the saturation solubility of graphite in Co show results at the same temperature differing by almost an order of magnitude.1-5 Recently Schenck, Frohberg, and Jaspert6 measured the equilibrium between CH4-H2 mixtures and C-Co solid solutions at five temperatures ranging from 850° to 1050°C. Their values of the activity of carbon in the solid solution, deduced from a knowledge of the chemical potential of carbon atoms in the gas, varies linearly with composition at each temperature and the authors concluded that the solutions were Henryan. The saturation solubilities deduced from Schenck, Frohberg, and Jaspert's measurements are in good agreement with the solubility determined at 1000°C by Rao and Nicholson7 and the value at 1000°C deduced from the measurements of smith8 on the equilibrium between CO/CO2 mixtures and C-Co solutions. The object of this investigation was to check the results of Schenck, Frohberg, and Jaspert and also to extend the range of solubility data to higher temperatures. In the case of the C-Ni system, there is fairly good agreement between the values given by schaefer9 for the saturation solubility of carbon C, in nickel, the value given at 1000°C by Rao and Nicholson,7 and that deduced from Smith's8 measurements of the equilibrium between C-Ni solutions and CO/CO2 mixtures at 1000°C. The values of C, deduced from Schenck, Frohberg, and Jaspert's6 measurements of the carbon activity in nickel are also in fairly good agreement. However, there is a large discrepancy between the above set of measurements and those of Lander, Kern, and Beach," who measured the carbon solubility of nickel in equilibrium with graphite by depositing an excess of graphite on the surface of Ni-foils from a gaseous mixture and subsequently diffusing in the carbon. These results are considerably higher than those mentioned above. The determinations6 of carbon activity a, in nickel from the CH4-H2 equilibrium showed that at all the temperatures investigated, the ac-values varied linearly with concentration up to about a, = 0.6 and then began to increase with concentration much more rapidly. On the basis of auxiliary experiments in which C-Ni solutions were equilibrated with graphite, Schenck, Frohberg, and Jaspert concluded that their CH4-H2 solid equilibrations at high values of a, were spurious and a, behaved linearly with composition up to the saturation limit (a, = 1). The short linear extrapolations of Schenck, Frohberg, and Jaspert's a, data yield values of C, in good agreement with those of Lander, Kern, and Beach." The solubility data for nickel discussed here is presented in Fig. 1 in the form of plots of ln[Cc/(l - 2cc)] vs 1/T. The discrepancies mentioned are clearly seen. In this investigation a vapor transport method is used to measure C, over as wide a temperature range

Jan 1, 1969

By G. H. Kennedy, H. E. Criner

CYCLONE thickeners are "hydraulic centrifuges" designed either to produce a maximum practical separation between the water and solids of a feed slurry or to classify the slurry solids according to particle settling rate. The possibilities of utilizing the thickener to "close" plant water circuits have been investigated. Since the thickener becomes an integral part of the plant water circuit when installed, the basic means by which the solids content of all circulating water systems must be controlled is reviewed. All coal not separated from the circulating water by means of dewatering screens or settling devices must be bled from the plant at the same rate as they are being fed or created by degradation. If this were not true, the circulated volume would finally be completely filled with solids. If the rate of bleed is low, the solids concentration in the bleed and circulating water generally will be high. To keep a reasonable circulating water concentration, large amounts of fresh water must be supplied and the bleed rate must be high. These conditions are usually undesirable because of the difficulty in securing fresh water, the loss of large quantities of coal, and the pollution of nearby streams. Thickeners are the primary stage in the separation of the water contained in the bleed from the coal. Since a thickener, when operating with reasonable efficiency, usually cannot be expected to deliver an underflow containing less than 50 pct water, secondary dewatering devices such as a slurry screen or vacuum filter must be used to separate additional water from the bleed. The surface area required by the filter or screen will be nearly proportional to the total water which must be handled, and therefore the thickener becomes necessary to hold down the original cost. The water separated from the coal is then returned to the plant circuit to maintain the water balance and thus becomes the source of fresh water. It is not necessary to return clear water to the plant to maintain control of the circulating water concentration. It is only necessary that the bleed dewatering devices remove coal in all sizes at a rate equal to that at which these sizes are entering the circulating water. However, practically speaking, in order to maintain low solids concentration, it is usually necessary that the thickener have good recovery characteristics on bituminous coals in those sizes down to 400-mesh. The thickener can remove the smaller sizes from the closed-circuit system at the "solids in" rate and prevent their "build up" in the circulating water as shown in Fig. 1. With the portion of the feed water going directly to the underflow, comes the very fine solids not concentrated by the cyclone. All the larger solids are removed from the feed and delivered in a concentrated condition at the underflow. To apply thickeners with some reasonable assurance that operating requirements will be met, it is necessary to know the rate at which solids of all sizes must be removed from the circulating water and to know the thickener characteristics. The required removal rate of fine solids not recovered by other dewatering devices may be estimated from the size distribution and tonnage of the plant feed with a reasonable allowance for degradation in the circulating water system. A more reliable estimate may be secured by sampling the plant bleed water during a constant load period.

Jan 1, 1952

By Paul R. Wieber, Atam P. Sikri

This paper describes the U. S. Energy Research and Development Administration's (ERDA) program to develop in situ coal conversion processes, especially gasification. The potential of this technology, the technical directions being explored, and the program strategy to carry the process concepts toward commercialization are emphasized. The geographic location of the U. S. coal resources and a market analysis are described. Commercially successful in situ coal processes could add over a trillion tons of coal to the U. S. coal reserves. The economics of these processes is compared with surface gasification. Independent studies show this process to be 25% cheaper than surface gasification for Western coals. The major projects are briefly described. The Linked Vertical Well process is in the most advanced stage and shows great promise. The last test produced a low-Btu gas averaging 171 Btu per standard cubic foot for average production rates of 8.5 million standard cubic feet per day. The other projects are Packed Bed, Longwall Generator, and Steeply Dipping Beds. Unique factors of the process development are discussed which may lead to commercial processes in the near term. A development strategy is proposed by which this technology could be commercialized before 1985 with potentially lower gas prices and lower environmental impacts, relative to mining plus surface gasification.

Jan 5, 1978

By O. P. Dolph

SPANIARDS were probably the first to mine the rich surface ore in the veins cutting the rhyolite capping that outcrops on the hills of La Mazata, oil the Allyones side of the Magdalena valley in Jalisco, Mexico, although the name comes from a word of Indian origin meaning "deer". The camp is about 12 km. west of Magdalena, a town on the Southern Pacific Railroad, and about 17 km. north of Etzatlán, on the Mexican National Railroad, at an elevation of 4500 ft. The climate is subtropical with no extremes of heat or cold, the rainy season beginning in June and ending in October.

Jan 1, 1938

By Alexandre Mitinsky

The theory of elasticity, the science of the strength of materials, and all our calculations regarding engineering structures are based on Hooke's law, that in loaded bodies the deformations are proportional to the load producing them. Without this law it would be impossible to design intelligently engineering structures such as bridges, frames, axles, etc. This being the case, the proportional limit,l that is, the point at which deformation ceases to be proportional to load, is the most important factor in engineering design. Further, the working fiber stress should be fixed in reference to the proportional limit instead of, as is usual, in reference to the ultimate strength. The incorrect use of the ultimate strength instead of the proportional limit in setting the working fiber stress is probably due to two reasons: (1) it is a more delicate operation to measure the proportional limit; (2) it is usually assumed, though incorrectly, that the proportional limit is determined by the ultimate strength. In Germany the poin't at which permanent set first appears is often taken instead of the proportional limit. The two points will coincide if Gerstner's law, that elastic deformations are proportional to the loads producing them both before and after permanent set, is true; and the limit of proportionality and the elastic limit or point of permanent set will both be represented on a stress-strain diagram, by the point at which the line ceases to be a straight line and becomes curved or changes its inclination. It is to be further noted that the difference in definition between proportional limit and elastic limit introduces a difference in methods of determination in the testing laboratory. The German method of determining the elastic limit by alternately loading and unloading the test specimen is a lengthy process and time has in itself a very considerable influence on the results of physical tests.

Jan 1, 1916

By AIME AIME

NAPOLEON'S dictum that an Army travels on its stomach has not changed in this present war, but the things an Army's stomach calls for would be more than strange to Napoleon. Today one of the main articles of diet for the mechanized army is oil and gasoline, and the chief and most efficient source of 'apply overland is the pipe line. It was a flexible 4-in. pipe line that supplied the voracious appetite of tanks, trucks, jeeps, and planes across the North African desert. and it is the 1800-mile pipe line from Calcutta to Kunming, Yunnan Province in China, the longest in the world, that supplied oil and 100-octane gas for the trucks, tanks, Jeeps, and planes fighting on the Assam-Burma-China front in recent months. Completion of this approximately 1800-mile pipe line to China over rivers that had never been bridged, over hill that towered 9000 ft., and over swamps

Jan 1, 1945

By William E. Bruce

This paper is intended to provide an improved understanding of natural draft (natural ventilating pressure) and the effect of natural draft on underground mine ventilation circuits. Attention is focused on measurement of natural draft pressures during ventilation surveys in mechanically ventilated mines and on different methods for modeling natural draft using the measured data. A number of examples are presented which utilize data collected during absolute air pressure surveys made by personnel of the Ventilation Division of the Mine Safety and Health Administration's Safety and Health Technology Center, Denver, Colorado. Examples are used to illustrate how the data from absolute air pressure surveys may be interpreted to determine whether natural draft pressure is present and what its magnitude is. In addition, two different methods are described for mathematically estimating the magnitude of the natural draft pressure. Comparisons are made of results obtained using the different methods. Different procedures are described for modeling natural draft using the MSHA-modified Penn State computer program. Use of the routines is described and illustrated relative to drafts that aid or oppose the mechanical ventilation system. Tabulations of results facilitate comparison of outcomes obtained using the different modeling procedures.

Jan 1, 1982

By Jacques B. Wertz

Both the San Andreas fault complex and the Murray fracture zone are apparently found to be contemporaneous with the Laramide mineralization period. Their compounding effects certainly have disturbed the Texas lineament belt and its components with serious lateral offsets and most probably have been instrumental in allowing intrusives to be emplaced as well as mineralization to accompany these intrusions at some of the fracture intersections. While the main fracture centers can be almost accepted as being structurally linked together, the Texas lineament trend definitely predominates, exerting a prevailing direction to graben (Silver Bell) and to elongated depressions (Bisbee). That this lineament belt also influenced the concomitant mineralization seems a logical inference. The orebodies are generally found at intersections near the most centrally-located intrusive with a distance varying from contiguity to one or two miles. The Southeast Arizona copper province owes its existence primarily to a particularly favorable structural setting of broad semi-continental scope. Thus, various regional structural elements are to be considered as possibly direct or remote cause for the widespread mineralization, although the one or the ones really responsible may never be singled out. There arc three basic regional elements: (1) The north-northwest-trending anticlinorium that diagonally crosses Arizona is quite obvious because many mountain ranges follow this direction. This anti- clinorium, which merges northward into the Wasatch-Jerome Belt, marks a broad zone of weakness where tension seems to prevail. Mineralized trends such as Jerome-San Manuel-Bisbee may give some weight to the economic value of this structural element. (2) Northeast-trending fractures, parallel to the Colorado Mineral Belt (Landwehr, 1967), appear troincident with mineralization as evidenced by the Questa-Grants-Morenci and the Lordsburg- Tyrone-Santa Rita alignments. This structural direction is accepted as one of the most economically significant in the Southwestern United States. (3) The Texas Lineament.

Jan 1, 1970

By Charles E. Wait

HAVING had some experience in the use of gasoline-gas in a laboratory, I have been induced by frequent inquiry to present a few hints concerning it, which I hope may be of some value to those who are out of the reach of coal-gas, and who contemplate using this gas. While I will not delay to describe the method by which this gas is made, it may not be out of place to note that, unless frequent charges are put into the carburetter, the gas is variable in richness. This may be partially avoided, it is said, by repeatedly pumping from one cell in the carburetter to another. If a machine is in constant use for many months without re charging, the gas becomes rather poor for illuminating purposes ; but in this condition it may be burned in a Bunsen burner with advan tage. Could the gas be used always in this condition, no difficulty would be experienced, and it would be quite satisfactory for general laboratory purposes. Considerable annoyance, however, is experi enced whenever the machine is filled with gasoline. The Bunsen and other burners then produce a flame too smoky to be used with com fort, and, in fact, with most of them, a full supply of air; turned on at the base of the burner, will not suffice to completely burn off all the carbon. Finding it necessary to adopt some method by which I could get a flame free from unconsumed carbon, I adopted a plan which has in every way proved satisfactory. In addition to the pipe conveying the gas to the table, and ar ranged with a stopcock, there is brought to the table, within a fern inches of the gas-pipe, another pipe, conveying air direct from the pump. This pipe is also arranged with a stop-cock. The air- and gas-pipes are now connected with one pipe by a T joint; and to this last pipe is attached, by rubber tubing, the Bunsen or other burner. I have successfully used this simple system in connection with both small and large Bunsen burners, a burner with three tubes, arid a Fletcher burner; and recently I have added a new still to our equipment, and have been tising with it a Fletcher special high power burner No. 6, to which this system has been applied. With

Jan 1, 1886