By B. L. Dunic, Terkel Rosenqvist

rr has long been suspected that sulphur has a small but finite solid solubility in iron, but up to the present more accurate data have been lacking. The survey given by Hansen' illustrates the divergence of data and opinions. Solubilities between 0.01 and 1.5 pct have been suggested, and opinions vary regarding the effects of temperature and phase transformations in iron on the sulphur solubility. The extent of solid solution and its variation with temperature might be expected to be an important factor in the occurrence of hot shortness in steel. Therefore, the object of the present investigation was to study this problem more systematically. It was furthermore hoped that solubility data for sulphur might contribute to an understanding of the factors which determine solid solubilities in general. Experimental Procedure The present work was based on the measurement of the chemical activity of sulphur in the solid solution by means of equilibrium with a mixture of hydrogen and hydrogen sulphide. When the solid solubility limit is reached, the sulphur activity in the iron becomes equal to that in the coexisting sulphide phase. A gas mixture of a controlled H,S/H, ratio was passed over pure metallic iron heated to a temperature in the range 900" to 1500". The amount of sulphur absorbed by the iron was determined by analysis, and from a plot of percentage of sulphur vs. gas composition the sulphur activity and the solubility limit were determined. As the rate of diffusion of sulphur in solid iron is very small, often several days were needed to be sure that equilibrium conditions had been established. To produce a gas flow with less than 1 pct H,S of constant composition for several days, was in itself a problem. The most satisfactory arrangement was obtained by a continuous synthesis of hydrogen sulphide from the elements. This was done in the part of the apparatus shown to the left in Fig. 1. The hydrogen used was first purified in tank batches by passage through activated charcoal cooled in liquid nitrogen under a pressure of 150

Jan 1, 1953

By Horace Mann

A FEW years ago, it was generally thought that from 15 to 18 per, cent. of zinc oxide was the upper limit of a workable lead blast-furnace slag. With slags above this zinc-oxide content, the furnaces gave so much trouble because of hearth, wall, and crucible accretions that the campaign was very short. The time lost in cleaning out the frozen furnaces, for it was seldom possible to blow them out, and blowing in was so great that it was considered uneconomical to attempt the running of high-zinc slags, even if this were metallurgically possible. It is true that there are, references to one or two slags much higher in zinc than the foregoing,1 but the average smelterman regarded these, as freaks and not to be considered for regular furnace work. One or two plants, notably the plant of the United States Smelting Co, at Canyon City, Colo., ran charges, higher in zinc. At this plant, the zinc-oxide content of the charge was frequently 20 per cent. and higher but the slags from these furnace's seldom ran over 10 to 12 per. cent. zinc oxide. The furnaces were run with a large volume of air under a relatively low pressure, a low smelting column, and a very hot top; as a result, a large amount of zinc was volatilized. Even with the low smelting column and hot top, accretions caused much trouble and barring, down was a daily occurrence. At the time most of the theories on lead blast-furnace work were promulgated or worked out, it was necessary to run a furnace with a cold top in order to avoid an excessive loss due to fines and fume. At the same time, the smelting conditions had to be such that the lead and silver would be reduced and would enter the bullion. The slag had to be liquid but the charge must not give excessive accretions either in the hearth or on the walls of the furnace. This forced the operators to run the furnaces with a comparatively low blast, which, in turn, caused a small fuel consumption per unit of time with the accompanying result of a low working temperature.

Jan 8, 1925

By T. F. Bower, M. C. Flemings

The classical explanation for formation of the fine equiaxed "chill zone " in ingot solidification is that local supercooling near the chill wall causes copious nucleation in this region. This work indicates, however, that convection is an essential element in formation of the chill zone. In the absence of convection, no chill zone forms even though rate of. heat extraction is extremely vapid. Alloy studied was Al-l.5 pct Cu alloy solidified against a copper chill wall. When solidification was initiated at the chill wall in absence of. cor-vection, surface grain size was large (>I cm diam). When it was initiated in the presence of convection, it was fine (<0.05 cm diam). It is concluded that some form of "crystal multiplication" plays an important role in formation of the chill zone. INGOT macrostructures are generally classed as containing one or more of the three zones: "chill zone", "columnar zone", and central "equiaxed zone". These three zones are sketched in Fig. 1; their origin has been discussed in some detail.&apos;-&apos; The classical explanation for formation of the chill zone is that supercooling occurs in the region of liquid metal adjacent the mold wall, and copious nu-cleation then takes place in this region forming numerous small crystals. The columnar region then results by growth of favorably oriented grains (den-drites) which crowd out their less favorably oriented neighbors."5 The mechanism of the columnar-equiaxed transition has been the subject of considerable interest. The generally accepted mechanism, until recently, was that constitutional supercooling developed in front of the growing columnar grains with eventual nucleation of new, equiaxed, grains ahead of the growing solid front.&apos; Recently, it became evident this explanation was not completely satisfactory and it is now evident that "crystal multiplication" plays an important role. This crystal multiplication occurs by separation of dendrite arms from growing dendrites,8?"&apos; and has been shown to be strongly influenced by convection.6, 10-13 Reduced convection results, for a given alloy, in longer columnar zone, larger columnar grains, and larger equiaxed grains.7, 12

Jan 1, 1968

By Didyk M. Marko, Vásquez Ñ. Gregorio

INTRODUCTION The Salvador Division of Codelco Chile is an important copper molybdenum production center, located 1,200 km north of Santiago and 124 km east of the Pacific Ocean, in the foothills of the Andes Range. El Salvador Mine produces by block caving 8,600,000 t of ore with a content of 1 .l0% Cu and 0.02% Mo, from a copper porphyry ore body. The geology of the ore body shows a great heterogeneity as to rocks, grade distribution, ore height and undercutting levels. This has resulted in a variety of designs for the productive units (blocks) and in the mineral handling systems. Up to now, 4 systems have been employed: grizzly and intermediate haulage; slusher drifts with intermediate ore pass and haulage; slusher drifts with scraper loading directly into trains; and, LHD. On the other hand there is a marked dispersion in the final results from each block mined out. We report here the conclusions reached after analyzing the data gathered on the mining of 163 depleted blocks, representing a total production of 102,000,000 t, with an undercut area of 340,000 sq m. The final results of each block, characterized in terms of tonnage and fine cop- per recovery, were studied as a function of a number of design, geological, and operational parameters. BASIC CONCEPTS Indices of Efficiency In order to evaluate the final result of each block, or group of blocks, the following indices of efficiency were defined : Tonnage Recovery (TR) . It is the ratio between the ore tonnage extracted and the in situ tonnage estimate for each block or group of blocks. Grade efficiency (E) . It is the ratio between the Cu mill feed grade and the in situ Cu grade estimate for each block or group of blocks. Grade efficiency is numerically equal to the ratio between fine copper recovery (FR) and tonnage recovery (TR) . Figure 1 shows the final results for 163 mined out blocks, in terms of tonnage and fine copper recovery. Different grade efficiencies are also indicated. The marked dispersion in the final results of mined out blocks must be stressed since it greatly incides in mine planning. It must be kept in mind that an eventual concentration of low overall efficiency in the blocks during a given period (e.g., one year) will make it necessary to bring into production new blocks over the standard development schedule. It is worth noting that the final results in the 163 mined out blocks corresponding to a production of 102,000,000 t of ore with a mill feed grade of 1.445% were obtained from an ore estimate of 93,000,000 t and a grade of 1.671% Cu, which represents 110% tonnage recovery and 86% grade efficiency. Parameters Studied The following parameters are considered in this study: Geological Parameters. These parameters depend exclusively on the geological and geotechnical features of the ore body. IN SITU GRADE: The initial estimate of the block grade. Four copper grade categories were considered : (a) lower than 1.3% ; (b) 1.3 to 1.6%; (c) 1.6 to 2.0%; (d) higher than 2.0%. The overall initial in situ estimate of the ore body was 1.6% Cu. IN SITU TONNAGE: Initial tonnage estimate of the block. Four categories are considered: (a) below 500,000 t; (b) 500,000 to 1,000,000 t (c) 1,000,000 to 1,500,000 t; (d) over 1,500,000 t. CONTACTS SLOPE: Since up to 4 rock types can be found in a block, resulting in a corresponding number of contacts, a horizontal con- tact was defined as that which forms an angle of less than 45" with the horizontal and a vertical contact that which forms an angle of more than 45" with the horizontal. GRADE DISTRIBUTION: As in rock types, horizontal and vertical grades were defined. ORE HEIGHT: The distance measured between the undercut level and the top of ore. Four categories are considered: (a) less than 60 m; (b) 60 to 100 m; (c) 100 to 150 m; (d)over 150 m

Jan 1, 1981

By M. J. Marcinkowski, A. S. Sastri

A detailed compressive stress-strain analysis and transmission electron microscopy investigation has been made of the deformation behavior occurring in a 50 at. pct Ni-Ti (hypoeutectoid) alloy and a 54.5 at. pct Ni-Ti (hypereutectoid) alloy. In the case of the hypoeutectoid alloy, three stages of work hardening are observed. Stage I occurs at a very low stress and is associated with plastic deformation via martensite formation. Stage 11 is characterized by very rapid work hardening and is due to difficulties in causing further deformation in the fine martensite aggregate produced in Stage I. Stage III which occurs at very high stress levels is characterized by smaller work hardening rates and is due to the plastic deformation arising from alternate reconversions of the original martensites to martensites of varying orientation. Rapid quenching of the hypereutectoid alloy leads to very high yield strengths and is related to a fine precipitate dispersion that such treatment brings about. The present investigation represents the final phase of a three-part study directed toward an understanding of the solid-state transformations in near equi-atomic Ni-Ti alloys as well as the deformation mechanisms associated with these alloys. In the first part,"2 to be henceforth referred to as I, it was found that alternate simple shears on {112} planes and in (111) directions convert the parent B2 structure in the equiatomic NiTi alloy into two distinct close-packed monoclinic martensites. All of the marten-sites were of this type, whether they were formed by cooling or by plastic deformation, whether induced to form in bulk samples or in thin foils, or whether examined in the electron microscope at room temperature or below. On the other hand, in the second part of this investigation,3 to be reffered to as 11, it was shown that upon slow cooling to about 640°C. alloys in the neighborhood of NiTi which possess the B2 structure transform eutectoidally into their equilibrium phases Ti2Ni and TiNi3. However, preceding the formation of these equilibrium phases a series of metastable intermediate phases are formed. This paper will set as its goal the elucidation of the remarkable deformation behavior exhibited by NiTi. In particular, Buehler and Wiley4 have found equiatomic NiTi to be surprisingly soft, while Buehler et al.5 have shown this alloy to possess a memory effect: i.e., upon bending at room temperature it will revert to its original shape when heated to above about 50°C. In I it was shown that NiTi was soft in the sense that the yield stress was low; nevertheless, the alloy work-hardened at an extremely rapid rate to very high stress levels. On the other hand, the hypereutectoid alloys with somewhat higher nickel, say 54.5 at. pct (60 wt pct) have enormously increased yield strengths compared to those of the equiatomic alloys. In order to determine the atomistic processes giving rise to the above behavior, it was decided to examine samples that were wafered from bulk specimens deformed in compression to various strains using the techniques of transmission electron microscopy. EXPERIMENTAL TECHNIQUE All of the alloys used in the present investigation contained either 50 at. pct Ni (55.06 wt pct) or 54.5 at. pct Ni (60 wt pct) and were arc-melted in the form of a finger using the same techniques described in I and II. The finger was capsulated in a stainless-steel jacket and swaged at 850°C into rods. Compression specimens 0.300 in, long and 0.200 in. in diam were machined from these rods. In order to completely re-crystallize the samples and remove residual stresses, all of them were capsulated in evacuated quartz, annealed for 1/2 at 1050°C. and then furnace-cooled. Compression tests were carried out in an Instron tensile testing machine covering a range of temperatures from —196° to 200°C using procedures described previously.6&apos;7 In all cases crosshead speed was 0.02 in. per min. Wafers 0.015 in. thick were spark-cut from the cylindrical samples at 45 deg to the compression axes after they had been deformed to the desired strain. These specimens were then spark-planed to about 0.005 in. and then electrochemically thinned for examination by transmission electron microscopy as described in I.

Jan 1, 1969

By Charles Wert

THE diffusion and precipitation of carbon and nitrogen in a iron have previously been investigated using the internal friction as a measuring tool.&apos; Most of this work has been done on rather pure iron; no effect was observed which would indicate that either of these phenomena is affected by the rather small amounts of impurity found in these samples of iron. Fastz observed, however, that both the diffusion rate and the aging properties of nitrogen in iron were sensibly changed by the addition of Vz pet Mn. The diffusion rate at a given temperature is reduced and the nucleation of nitrides is apparently changed somewhat. He observed no such changes for carbon in this alloy. Later Dijkstra and Sladek" extended these observations on nitrogen to other alloys of iron. They found that metals other than manganese also influence the behavior of nitrogen in iron; chromium, molybdenum and especially vanadium affect the diffusion and precipitation of nitrogen even more than manganese does. Their results have been verified in all essential details by this author, who finds in addition that small additions of nickel have about the same effect on the diffusion of nitrogen as the same amount of manganese. The present work was undertaken to study the effect on carbon in iron of these alloying elements. The alloys used had two sources. The material used as a "standard" (designated Fe in this paper) in the measurements was some iron supplied by J. K. Stanley, of Westinghouse Electric Corp., who reported 0.01 pct 0, as the only major impurity. He also made up an alloy of 0.26 pct Ni and one of 0.9 pct Mo using this same iron as a base. They were supplied by him in 2 lb billets, which were sawed into rods and cold formed into 0.030 in. wires for measurement. The alloys of chromium, manganese, and vanadium were prepared by the metallurgy section of the Institute for the Study of Metals, University of Chicago, by adding these metals in turn to vacuum melts of National Research Corp. iron. The small castings prepared in this way were also cold formed into 0.030 in. wires. After these wires had been prepared they were decarburized for 30 min at 730°C in wet Hz. After this treatment, no trace of carbon (as measured by internal friction) could be found. All specimens were then carburized for about 15 min at 710°C and water quenched. By this treatment the internal friction at 40°C was raised to a Q-&apos; ~ 0.015. The diffusion of carbon in these alloys was studied by observing the shape and position of the internal friction peak at 0.9 cycles per sec. These measurements were made using a torsional pendulum in a manner described earlier.&apos; The data are plotted in Fig. 1. It is seen that there is no apparent difference in internal friction between the various alloys. This is in marked distinction to the broadening and shift-

Jan 1, 1953

By George M. Rigg, Samuel M. Cassidy

During 1937 a program was begun to mechanize and modernize the then 28-year old Isabella mine of the Weirton Coal Co., which is on the Monongahela River, in Fayette County, Pennsylvania, at one edge of what is generally known as the Coke Region. Weirton Coal Co. is a subsidiary of the National Steel Corporation, and produces metallurgical grade coking coal for the Weirton Steel Co., Weirton, W. Va. Improvements subsequently made included a cleaning plant for washing the entire mine output, shovel-action track-mounted machines for mechanically loading all the coal, universal-type track-mounted cutting and shearing machines, post drills, 8-wheel mine cars of 10 tons capacity, cable-reel gathering locomotives and other auxiliary equipment. This paper presents the factors, reasons and results of decided changes from the mining system generally prevailing in the region, as well as abandonment of selective mining practices in favor of complete seam extraction. Coal-seam Conditions Fig. 1 illustrates the Pittsburgh coal seam on the property. Cover over the seam averages 450 ft., and 675 ft. is the maxi- mum. Main roof varies from very weak to medium strong; usually it disintegrates rapidly on exposure to air. The "wild" coal makes a fairly strong immediate roof if supported by crossbars and if unbroken affords a seal to the main roof. The draw slate is very weak and treacherous. The floor is characterized by numerous irregular bottom rolls, or "horsebacks," protruding from a few inches up to 3 ft. into the coal. Some are soft, but many are hard and flintlike. Although the bottom slate usually is hard, the underlying fire clay causes it to buckle and heave readily with any moderate increase in roof pressure or where damp. As a whole, the bottom is weaker than the main roof. The coal is characterized by numerous closely jointed face and butt cleats and a woody, springy nature when shot, both having a decided influence on face practices. As shown in Fig. I, at both the top and bottom of the main coal seam is a layer of coal of higher ash and sulphur content than the body of coal in the middle. Factors That Influence the Mining System Equipment was bought and organization for mechanical loading was made on the basis of working each mechanical unit as near its full capacity as possible, to lessen investment cost and obtain best operating efficiency. This led to combination double and triple-shift operation at the start, and, very shortly, to all sections being triple shifted.

Jan 1, 1947

By Samuel M. Cassidy, George M. Rigg

During 1937 a program was begun to mechanize and modernize the then 28-year old Isabella mine of the Weirton Coal Co., which is on the Monongahela River, in Fayette County, Pennsylvania, at one edge of what is generally known as the Coke Region. Weirton Coal Co. is a subsidiary of the National Steel Corporation, and produces metallurgical grade coking coal for the Weirton Steel Co., Weirton, W. Va. Improvements subsequently made included a cleaning plant for washing the entire mine output, shovel-action track-mounted machines for mechanically loading all the coal, universal-type track-mounted cutting and shearing machines, post drills, 8-wheel mine cars of 10 tons capacity, cable-reel gathering locomotives and other auxiliary equipment. This paper presents the factors, reasons and results of decided changes from the mining system generally prevailing in the region, as well as abandonment of selective mining practices in favor of complete seam extraction. Coal-seam Conditions Fig. 1 illustrates the Pittsburgh coal seam on the property. Cover over the seam averages 450 ft., and 675 ft. is the maxi- mum. Main roof varies from very weak to medium strong; usually it disintegrates rapidly on exposure to air. The "wild" coal makes a fairly strong immediate roof if supported by crossbars and if unbroken affords a seal to the main roof. The draw slate is very weak and treacherous. The floor is characterized by numerous irregular bottom rolls, or "horsebacks," protruding from a few inches up to 3 ft. into the coal. Some are soft, but many are hard and flintlike. Although the bottom slate usually is hard, the underlying fire clay causes it to buckle and heave readily with any moderate increase in roof pressure or where damp. As a whole, the bottom is weaker than the main roof. The coal is characterized by numerous closely jointed face and butt cleats and a woody, springy nature when shot, both having a decided influence on face practices. As shown in Fig. I, at both the top and bottom of the main coal seam is a layer of coal of higher ash and sulphur content than the body of coal in the middle. Factors That Influence the Mining System Equipment was bought and organization for mechanical loading was made on the basis of working each mechanical unit as near its full capacity as possible, to lessen investment cost and obtain best operating efficiency. This led to combination double and triple-shift operation at the start, and, very shortly, to all sections being triple shifted.

Jan 1, 1947

By J. Stuart Warner

The reaction COSO4(c)?CoO(c) + So3(g)was investigated from 950° to 1170OK by two different methods. The sulfate was decomposed in a previously evacuated space and Pso3 calculated from the measured total pressure on the assumption that Pso2 = 2P02. The sulfate was also decomposed under conditions of controlled oxygen pressure. The difference in the results obtained by these experimental techniques is attributed to the effects of thermal diffusion. The standard free energy change for the reaction is given by ?F° = 66,292 + 17.273T log T — 102.57 T (±300 cal/mole). It was found by DTA and X-ray diffraction studies that CoS04 undergoes a transformation at 617°± 4°C. THE metal sulfates may decompose directly to the oxide or pass through one or more intermediate basic sulfates. Provided the oxidation state of the cation does not change in the course of the reaction, the decompositions may be described in general as follows: One of the major objectives of this work was to determine the validity of Eq. [3] as much of the existing sulfate data has been calculated from decomposition pressures by Eq. [5]. The type of apparatus generally used for these measurements consists of a reaction vessel at high temperature which communicates with a manometer at room temperature. A temperature gradient is thus imposed on the gas phase causing thermal diffusion which brings about a partial separation of the different gaseous species present in an initially uniform mixture. The basic theory and experimental facts associated with this phenomenon are summarized elsewhere1 and it will suffice to state here that the heavier gaseous species diffuses down the temperature gradient. Since thermal diffusion destroys the homogeneity of the gas phase, it is not necessarily true that Pso2 = 2Po2 in any particular volume element of the gas phase even though there are twice as many molecules of SO, as of 0, in the gas phase considered as a whole. Under these conditions, the decomposing sulfate gives off SO, which dissociates to SO, and 0, and all three species are distributed throughout the system by thermal diffusion. However, the sulfate will continue to dissociate until the equilibrium value of PSo3 is established on the hot zone. Thermal diffusion may distribute SO2 and O2 throughout the gas phase in any way so long as Eq. [2b] is satisfied in the hot zone; i.e. Pso2(Po2)1/2=K3pso3. When a steady state is reached, we can characterize Pso2 in that

Jan 1, 1962

By Luiz C. Correa da Silva, Robert F. Mehl

A. D. Le Claire and R. S. Barnes (Atomic Energy Research Establishment, Harwell, Didcot, Berks., England)-—This much awaited paper admirably confirms that the Kirkendall effect is a true diffusion phenomenon and likely to be found in all diffusing systems. The most likely explanation put forward so far to account for the shift of interface is that the two components of the system, diffusing in opposite directions, do so with unequal rates so that there is a net loss of material from that half of the diffusion zone rich in the more rapidly diffusing component. This loss is accompanied, and at least partly compensated for, by a closing up or decrease in volume of this latter half of the diffusion zone and an expansion of the other half so as to tend to keep constant the overall volume per atom. This is manifest as a movement of the original interface. If this is a true picture of what is taking place then there are at least two important matters requiring further study."1—The quantitative relating of the observed shift with the independently measured separate diffusion coefficients of the two diffusing species."2—A detailed study of the mechanism and characteristics of the closing up process."We would like first to make a few remarks pertinent to these topics. In connection with the first of these, it is a pity that more and detailed measurements were not made on the Au-Ag system, the only one for which the separate diffusion coefficients of the two species have been measured.&apos;" One of us (A. D. Le C.) has calculated from Johnson&apos;s results the shift to have been expected in samples D.2 and D.3. Darken4 showed that the velocity v with which the markers move is related to the separate diffusion coefficients Dau, Dag, by the eauation:"dN"v = (Dag — Dau "dx"dN"where .is the concentration gradient at the mark-ax"ers. Under certain conditions,4, 20 it can also be shown that:"Xm"v = "2t"where x, is the total marker shift after time, t:"dN". . xm = 2t (Dag — Dau) [9]"dX"Johnson measured Dag and DAu in a chemically homogeneous alloy and so his reported figures represent the true or ideal diffusion coefficients"; the same quantities in eq 9 represent the actual diffusion coefficients as would be measured in the presence of a chemical concentration gradient, so we need to multiply Johnson&apos;s reported values of Dag and Dau by the"1 before insert-dlogN "ing them in eq 9. 7 is the activity coefficient of Ag at the concentration prevailing near the markers which we shall assume to be - 50 pct. The values of the thermodynamic factor for N = 0.5 and the temperatures at which D.2 and D.3 were annealed were obtained from thermodynamic data quoted by Darken.&apos; aN/ax was computed from the coefficient of inter-diffusion of Au and Ag given by Johnson on the assumption that in the samples D.2 and D.3, the concentration distance curve could be represented by the standard equation:""No is the original difference in concentration between the two halves of the couple, and + is the error or probability function."aN/ax at x = 0 is then given by:"adN/dx "2/nDt"and we assume that this represents the concentration gradient at the markers, although it is probable that the figure is slightly high."When all the appropriate quantities are inserted in eq 9, we find that the expected shifts are: for D.2, 0.0134 cm and for D.3, 0.0119 cm."The agreement between these results and those

Jan 1, 1952

By J. Chipman, H. R. Larson

The data previously reported for the quantity as a function of oxygen pressure at 1550°C have been used to compute the activities of Fe, FeO, Fe2O3, and COO in slags of the ternary system. Activities of the first three have been obtained also for two quasi-ternaries involving fixed CaO:SiO2 ratios. IN a previous paper1&apos; the authors reported the results of an investigation into the effects of oxygen pressure on the composition of various simple slags analogous to some of those which are found in steel-making practice. The ratio of ferric iron to total iron was studied at 1550°C in iron oxide melts to which lime, magnesia, lime-plus-silica, and other oxides were added. The oxygen pressures involved those of air, carbon dioxide, and carbon dioxide plus carbon monoxide in several proportions. Although very low oxygen pressures could not be used, the slag-metal equilibrium studies of Fetters and Chip-man&apos; permitted extending the results to slags in equilibrium with iron. For the ternary system CaO-FeO-Fe,O, the oxygen pressure-composition relationship has been determined from zero percent lime to lime saturation over an oxygen pressure range from air to that represented by equilibrium with liquid iron. Lime and silica were added to iron oxide in the ratios 0.54, 1.306, and 2.235 to form three quasi-ternary systems which were also studied over the entire region of liquid melts at 1550°C. Ternary Gibbs-Duhem Equation Wagner" has developed a method by which the activities of two components of a ternary system can be calculated if&apos; the activity of the third component is known throughout the composition range being considered. The fundamental form of the Gibbs-Duhem equation for ternary systems is N, d In a, + N2 d In a, + N3 d In a3 — 0. Wagner has developed a usable form of this equation by introducing the term y = N3/(N3 + N1) and rearranging the equation to give (? In a1/?N2)x = -y/(1-N2)2 (? In a2/?y) x2 N2/1-N2 (? In a2/?N2) y To apply this equation to the slag system CaO-FeO-Fe,O,, the activity of one of these components must be known. However, the only activity which is known from the experimental data is the activity or pressure of oxygen in the gas phase with which the slag is in equilibrium. The activity of oxygen in the slag can be defined as the square root of the oxygen pressure. In order to use oxygen as one component, the composition of the slags must be converted to the basis Fe-O-CaO. Oxygen, exclu-sive of that contained in CaO, then becomes com-ponent 2 in Eq. 1, Fe is selected as 1 and CaO as 3. Then y = Ncao/(Ncao + NFe). Eq. 1 then becomes (? In a fe/? Nx) y = -y/(1-No)2 (? In ao/?y) xp - No/ 1- No (? In ao/ O No) y. In order to evaluate Eq. 2, the boundary conditions must be known. The obvious choice of a standard state for iron is to assign slags in equilibrium with iron an activity of one. Then In a,., or log aFe, which is substituted for convenience, is determined by integrating along a line of constant y from the slag in equilibrium with iron to the composition at which log a,, is to be determined. Mathematically this can be expressed as log aFe (Nlog y) = log a&apos;Fe + (? log a Fe/? No) dNo where the primes indicate equilibrium with liquid iron and a&apos;Fe = 1. When Eq. 3 is integrated along a line of constant y, the following is obtained: log a Fe (No, y) = - y No ?/ No ? y ( log ao/(1- No)2) No d No - No/1-No d log ao. Lime-Iron Oxide Slags Iron Activity: The oxygen pressure of lime-iron oxide slags is shown in Fig. 1 as a function of j, de-fined as j = Fe+++/(Fe++ + Fe +++) for various constant mol percentages of lime. The j values at 0 to 60 pct lime were then determined for oxygen pressures of 1, 10-1, etc. to 10-" atm. For purposes of calculation, the line for zero percent lime was extrapolated to

Jan 1, 1955

By Lyman Taylor, Alexander R. Troiano

STUDIES of the transformation of austenite at constant subcritical temperatures have been numerous since the work of Davenport and Bain.1 Considerable information has been obtained on low-alloy steels and on high-carbon alloys containing undissolved carbide or graphite at the austenitizing temperature. Little is known of the isothermal transformation of austenite containing in solution large amounts of both carbon and a single alloying element. In this investigation four steels containing one per cent carbon and with chromium in the range 3 to 9 per cent have been examined with the view to establishing the fundamental character of the isothermal reactions when all carbon and chromium are initially in solution in austenite. EXPERIMENTAL PROCEDURE Alloys The chemical compositions of the steels investigated are given in Table I. The 4 per cent Cr alloy is a commercial steel. The other steels were made by the Carpenter Steel Co. as 50-lb., induction-furnace heats and rolled to 5/8-in. round bars. Bars were softened at 650° to 700°C. before the specimens were cut. [ ] Metallographic Method Most of the lines on the transformation diagrams presented here have been placed on the basis of the microscopic examination of partially reacted specimens. Thees specimens were approximately ½ by ¼ by 1/8 in. in size. Specimens of the 9 per cent Cr steel were held 10 to 12 hr. at 1200° to I225°C. before quenching to the various subcritical temperatures. The other steels were held for 2 to 2 ½ hr. at 1200°C. before quenching. These treatments, carried out in an atmosphere of purified nitrogen, produced an austenite grain size larger than A.S.T.M. No. I, some grains being 1 to 2 mm. in diameter. There were a few undissolved carbide particles in some specimens of the 9 per cent Cr steel. It is believed, however, that any errors in the results due to incomplete solution of carbon and chromium in austenite are negligible; that is, austenite compositions may be considered as being those listed in Table I. X-ray Methods Constituents were identified and martensite axial ratios determined from Debye

Jan 1, 1945

By Joseph Bernhardt

Use of concrete underground at No. 4 mine, Cornwall, Pa., has become increasingly important. Starting with small amounts at finger openings, occasional raises, piers, its use has expanded to entire slushing drifts and haulages. Besides eliminating costly timber repairs, concreting costs of slushing drifts have proved cheaper than timbering. Higher haulage-concreting costs are offset by no maintenance charges during the life of the haulage.

Jan 3, 1950

By Gearge C. Wallick

This paper describes experimental procedures for the calibration of capillary tubes to be employed as comparison standards in gas flow-rate measurements and considers several types of flow which were observed in the calibration of seven capillaries of varying diameter. It is shown that under certain experimental conditions deviations from Poiseuille flow are observed which may not be attributed to turbulence, and that this flow behavior may be described empirically by introducing the classical kinetic energy correction into the Poiseuille equation. INTRODUCTION Techniques have been developed for the measurement of the volume rate of flow of nitrogen through glass capillary tubes as a function both of the differential pressure applied and of the absolute gas pressure. Capillary tubes thus calibrated are frequently used to determine the rate of gas flow through a porous sample in the measurement of slip-corrected permeability. The purpose of this note is to describe the calibration procedure and to discuss some observed deviations from the ideal flow behavior predicted by the Poiseuille equation. EXPERIMENTAL PROCEDURE The volume flow rate of nitrogen as a function of the differential pressure was determined experimentally for a series of seven glass capillary tubes of varying diameter. As is shown in Table 1, the capillary radii in the series ranged from 0.004 cm for K1 to 0.07 cm for K7. The capillary tubes were cut from capillary tubing purchased on special order from several manufacturers and the bore radii were determined by microscopic measurement. The gas volume flow rate was measured for each capillary tube at a series of differential pressures in the range from 0 to 3 cm of mercury and at average absolute pressures of 1.0, 2.5, 4.0, and 6.0 atm. Experimental Procedure for Small Capillaries A schematic diagram of the apparatus used to calibrate the three smallest capillaries, Kl, K2, and K3, is shown in Fig. 1. By means of a standard Ruska Instrument Corp. volumetric pump (equipped with a synchronous motor drive, two stages of gear reduction, and a quick-change lathe gear box), nitrogen was displaced by mercury from a metal cell immersed in a constant-temperature bath. The pump, the line to the cell, and a part of the cell were filled with mercury. As mercury was forced into the cell, it displaced nitrogen which passed through the capillary tube being calibrated and into a large container with a volume of approximately 30 liters. Since the volume of this container was very large compared to the total volume change of the gas resulting from the action of the displacement pump, the absolute pressure of the system was essentially constant throughout any one run. Prior to any determination this pressure could be set at any desired level by means of an auxiliary nitrogen cylinder. The differential pressure across the capillary was measured with a Meriam Red Oil manometer and recorded together with the corresponding pump displacement rate which was equal to the gas flow rate. By repeating this process for a series of different displacement rates at each of the absolute pressures of interest, the data necessary for plotting the calibration curves for capillaries K1, K2, and K3 were obtained. All calibration measurements were made in a constant temperature room to minimize errors due to temperature fluctuations. In each run. the flow was maintained until equilibrium was established. Experimental Procedures for Large Capillaries The flow rates through Capillaries K4, K5, K6, and K7 required to obtain the pressure drops desired were larger than could be obtained from available constant displacement pumps, and it was thus necessary to employ an alternative calibration procedure. The arrangement of apparatus used in calibrating these capillaries at an average pressure of one atmosphere is shown in Fig. 2. Each capillary was calibrated by flowing nitrogen through the capillary and recording the differential pressure as a function of the flow rate. &apos;The differential pressure was measured with a Meriam Red Oil manometer and the flow rate was determined by collecting the effluent gas over water at constant pressure and recording the increase in volume per unit time after an equilibrium had been established. Appropriate corrections were made for the

Jan 1, 1953

By Robert G. Nisle

The classic theory of pressure build-up in shut-in oil wells as developed by Horner and van Everdingen is based on two-dimensional radial symmetry in the well-reservoir system. Such symmetry does not exist in the case of a well which parfiially penetrates the producing formation. As a result of this lack of symmetry the use of the classic theory in such cases become questionable. In this paper the mathematical theory has been extended to include the case of partially penetrating wells. Numerical solutions illustrating the up-dication of the equations are presented. The effect of partial penetration on pressure build-up is shown by a comparison of synthetic pressure build-up curves derived from the numerical solution of the equation for partially penetrating wells for various degrees of penetration. It is shown that partial penetration is detectable from the characteristic shape of the pressure build-up curve and that formation productivity may be calculated from the pressure buildup data in a manner identical to that described by the classic theory. INTRO DUCTION The use of pressure build-up data on shut-in oil wells is a well-established technique for the measurement of reservoir productivity. The work of Homer&apos; and van Everdingen&apos; is well known. Since the publication of their pioneering work, others"&apos; have elaborated and extended the technique. These authors have dealt exclusively with the case of wells that completely penetrate he producing formation. Two-dimensional radial symmetry is achieved, thereby, and the problem is greatly simplified. This ideal situation is seldom encountered in practice. But, in spite of this, the technique is often employed anyway. The question, therefore, arises: how much confidence can be placed in the results of such calculations when the data are taken on wells that only partially penetrate the producing formation? It is the purpose of this work to answer this question. Only the single-phase fluid case will be considered. van Everdigen&apos; has presented a rigorous solution of the two-dimensional case, but because of mathematical complexity, this solution has not proved to be particularly useful. Horner&apos; utilized Kelvin&apos;s point source solution in two dimensions and showed that it is a sufficiently good approximation for oil reservoir studies. The geometry of the well and the producing formation is illustrated in Fig. l. Geometrically the formation may be described as an infinite slab. The infinite slab is defined as the solid (the porous medium in this case) bounded by two parallel planes. Thus, the slab extends to very great distances in both the positive and negative directions of two of the coordinate axes, but is finite in

By Y. M. Chang, C. H. Pitt

A jet slurry apparatus has been constructed to test corrosive/erosive wear properties of grinding ball metal. Plain high carbon steel heat treated to a hardness of about 60 Rc was used. Slurries of quartz and chalcopyrite ore concentrate were used as the jetting media. Weight loss due to pure corrosion was determined by the linear polarization technique. Weight loss due to pure erosion was determined by jetting while cathodically protecting the sample. By comparing the total weight loss with the sum of the weight losses from pure corrosion and pure erosion, it was found that there was a synergistic effect between corrosion and erosive wear. Corrosion rate, erosion rate, and total erosion/corrosion rate are given as a function of pH and mineral type.

Jan 1, 1986

By Y. C. Liu

Both the habit plane of martensite and the orientation relationship between the matrix and martensite platelets of different habit planes have been investigated in binary titanium alloys with molybdenum, chromium, and iron. The effect of the mode of deformation on the martensite habit plane was studied. A micrograph of an exposed mar-tensite platelet is presented. IN the study of martensitic transformation in Ti-Mn alloys,&apos; two martensite habit planes—{334), and {344)8—were reported. The {334), habit was also observed in unalloyed titanium upon transformation,&apos; although there is disagreement with respect to the exact indices. The other habit plane, {344),, has not been reported in martensitic transformation in any other alloys. The present investigation was made to determine whether other binary titanium alloys with P-stabil-izing elements would exhibit a crystallography of transformation similar to that of Ti-Mn alloys. Furthermore, since martensite platelets can be induced by deformation under certain conditions, it was of interest to investigate whether the mode of deformation, compressive or tensile, would influence the formation of martensite platelets on a specific plane in an alloy system which possesses two martensite habit planes. Experimental Procedure The material used for the preparation of the binary alloys of iodide titanium with molybdenum, chromium, and iron had the following purities: 99.99 pct iodide titanium, 99.9 pct molybdenum, 99.423 pct chromium, and 99.9 pct iron. The compositions of alloys listed in this paper are in nominal weight percentage. All specimens used were prepared and treated according to the procedure described in reference 1, unless stated. For the subzero temperature treat,ment the following experimental schedule was followed. After specimens had undergone the grain-growth treatment, they were quenched into an ice-water bath and were then metallographically examined. In specimens of higher alloy content, no martensitic transformation was observed. In those in which mar-tensitic transformation did occur, only specimens in which the martensite platelets existed as fine needles in localized regions were used. All specimens were reannealed 17 hr at 1200°C, quenched into ice water. and the capsule was broken. They were held in the ice water for from 5 to 10 sec, then transferred to a liquid-argon bath. This stepped quenching procedure was found to be more efficient than direct quenching into liquid argon. In the latter case, as soon as the hot specimen was immersed in the liquid argon, a protective, insulating layer of argon gas formed, and the specimen continued to glow vividly in the bath for some time. In the study of the habit behavior of martensite produced by deformation, specimens were deformed at room temperature either by compression, tension, or rolling. Martensite habit planes were determined by the two-surface analysis procedure described in reference 1. A stereographic net of 153/4 in. diam was used throughout the investigation. The method for determining the orlentation relationship between martensite and the matrix follows that used by Greninger and Troiano.&apos; A diamond-polishing table with its auxiliaries was used in order

Jan 1, 1957

By Vasily P. Muravjev, Gennady I. Razgildeev

The theory of reliability is a powerful mathematical tool for determining optimum selection of components and application of electrical power to coal mines. In order to make this tool useful, statistical material on equipment life must be gathered and all failures carefully recorded. Statistical data can be applied to new apparatus design and can be used to determine optimum configuration of network and maintenance to reduce costs. Reference is made to underground power systems in the USSR. Technical progress in the last few years has occurred in the design and application of highly productive coal mining and transporting machinery. One of the most important problems facing mining engineers is to increase the availability of the machine to obtain higher productivity. However, machine failures and breakdowns of electrical power supply components cause serious delays in the coal-winning processes. In spite of the fact that electrical equipment and the power supply contribute only a small percentage of direct mine costs, electrical failures as well as power supply delays can result in severe indirect losses. It is necessary, therefore, to consider reliability and safety in the application of electrical equipment underground. To obtain the best results, it is necessary to investigate and evaluate the reliability of the electrical mining components (starters, breakers, motors, cables, etc.) and optimal methods for minimizing maintenance, the desired result being equipment which is efficient and safe. Electrical equipment reliability directly influences economics: the lower the reliability the more frequently failures occur, causing serious working delays and possibly huge economic losses. By the same token, while increasing the number of preventive maintenance calls per unit time might result in fewer failures, thus reducing delays, the cost of making more frequent maintenance inspections will increase; this is one aspect to be discussed in detail. Obviously, failures of identical types of electrical equipment (starters with the same current and voltage, etc.) are influenced variably by different working conditions, environments, quality of the apparatus, maintenance procedures (personnel, frequency, quality), load, and other factors. Hence, the lifetime of identical types of equipment will vary depending upon usage in terms of the foregoing factors. Thus for a given type of electrical component, these factors must be considered quantitatively; the interaction of all these factors are evaluated quantitatively by a statistical method using probability theory. Equipment reliability must be quantitatively determined from a study of equipment life, since no one laboratory test can reproduce all working conditions and environmental effects. Nevertheless, reliability theory applied to electrical mining equipment is a very powerful mathematical tool for selecting as well as evaluating certain parameters. It is necessary to select several reliability parameters so that one can obtain an expression for the total overall economic situation in terms of cost, taking into consideration damage caused by electrical equipment failure and cost of maintenance. To accomplish this result, such characteristics as apparatus lifetime, breakdown idle time, and losses (damages) can be determined quantitatively on a statistical basis. For identical electrical equipment working under similar conditions, the previously mentioned reliability factors are random variables and therefore can be characterized readily by a probability density function. Investigations carried out by the authors in the Kuznetsk Basin (Kuzbas) in West Siberia, USSR, show that the reliability factors of electrical mining equipment are well described by the exponential, normal, or Erlang&apos;s distribution in most cases. Mining electrical equipment life is well-described by the exponential law. The distribution of lifetime density is

Jan 1, 1971

By R. W. Balluffi, R. Resnick

NUMEROUS investigations of chemical diffusion in a brass have been made and the results are collected in several places.1-3 This work has been mainly concerned with the determination of the chemical diffusivity as a function of composition and temperature. In 1947 Smigelskas and Kirken-dall&apos; showed that zinc and copper diffuse at different rates in face-centered-cubic brass, and since then, a number of efforts have been made to determine the intrinsic diffusivities of zinc and copper in this alloy.1, 5-9 Horne and Mehl8 in particular have recently determined the intrinsic diffusivities as functions of temperature and composition using sandwich-type couples and inert markers. Inman et al." also have determined the intrinsic diffusivities in homogeneous alloys using tracer techniques. When the present work was started, no information of this type was available. Consequently, measurements of the intrinsic diffusivities were made as a function of temperature at a constant composition of 28 atomic pct Zn with vapor-solid diffusion couples where the zinc was diffused into the diffusion couple from the vapor phase. The application of these couples to the study of diffusion in a: brass has been described previously.0,7 The temperature dependence of the intrinsic diffusivities was found to follow the relation D, = A, exp(-Hi/RT) and the values of Hzn, and Hcu, were found to be closely the same. It is emphasized, however, that the chemical dif-fusivity (D = N1D2 + N2D1) is a composite diffusivity and does not necessarily follow this exponential form. It is usually found to do so within experimental error for substitutional alloys because the heats of activation of the intrinsic diffusivities generally are not greatly different.&apos;" Also, at the onset of this work, there was no information available concerning possible unequal diffusion rates of individual components and the existence of a Kirkendall effect in alloys with other than face-centered-cubic structures. Since then, two reports indicating a Kirkendall effect in body-centered-cubic ß brass have appeared. Landergren and Mehl" have published a note describing Kirkendall diffusion experiments with sandwich-type couples. Inman et a1.9 also find a Kirkendall effect in this alloy using the tracer technique. In the present work, several aspects of the Kirkendall effect in ß brass were further investigated using vapor-solid couples. Two different couples were used, one in which the zinc was diffused into the specimen from the vapor phase and the other in which the zinc was diffused out of the specimen into the vapor phase. Briefly, the existence of a Kirkendall effect is confirmed and it is found that Dzn/Dcu = 3 at about the 46 atomic pct composition in this alloy at 600°, 700°, and 800°C. As a result of the unequal diffusion rates of zinc and copper, volume changes occur and subgrain formation is observed in the diffusion zone. In addition, significant porosity is produced by the precipitation of supersaturated vacancies. Diffusion in this alloy is therefore outwardly similar to diffusion in a brass where these effects are also observed, a Brass Experimental Methods—The use of vapor-solid couples in studying diffusion in a brass has been described in previous articles.6,7 The method briefly consists of sealing a copper specimen with Kirkendall markers initially placed on its surface in an evacuated quartz capsule along with a large zinc source of fine a brass chips and then diffusing the zinc into the specimen through the vapor phase. The zinc concentration at the specimen surface rises rapidly enough to a value near that of the a brass source so that the surface concentration may be regarded as constant during diffusion. Under these boundary conditions, values of the chemical diffu-sivity may be obtained by applying the Boltzmann-Matano analysis to the concentration penetration curve, and the intrinsic diffusivities may be obtained from Darken&apos;s5 equations when the velocity of marker movement is known. The diffusion specimens were made from OFHC copper in the form of disks 3.2 cm diam and 0.5 cm thick with faces surface-ground parallel to within +0.001 cm. Markers in the form of fine alumina particles <0.0002 cm diam were placed on the specimen surface. These specimens were then sealed in quartz capsules along with enough a brass chips of a 30.0 atomic pct Zn composition to keep the source concentration from decreasing by more than 0.3 atomic pct Zn as a result of the loss of zinc to the specimen during diffusion. The quartz capsules which were initially evacuated to a pressure of

Jan 1, 1956

By A. Spilners, M. Simnad

The rates of formation of the different oxides on molybdenum in pure oxygen at 1 atm pressure have been determined in the temperature range 500° to 770°C. The rate of vaporization of MOO, is linear with time, and the energy of activation for its vaporization is 53,000 cal per mol below 650°C and 89,600 cal per mol at temperatures above 650°C. The ratio Mo03(vapor.lzing)/MoOS3(suriace) increases in a complicated manner with time and temperature. There is a maximum in the total rate of oxidation at 6W°C. At temperatures below 600°C, an activation energy of 48,900 cal per mol for the formation of total MOO, on molybdenum has been evaluated. The suboxide Moo2 does not increase beyond a very small critical thickness. At temperatures above 725°C, catastrophic oxidation of an autocatalytic nature was encountered. Pronounced pitting of the metal was found to occur in the temperature range 550° to 650°C. Marker movement experiments indicate that the oxides on molybdenum grow almost entirely by diffusion of oxygen anions. USEFUL life of molybdenum in air at elevated temperatures is limited by the unprotective nature of its oxide which begins to volatilize at moderate temperatures. Although the oxide/metal volume ratio is greater than one, the protective nature of the oxide film is very limited. Gulbransen and Hickman&apos; have shown, by means of electron diffraction studies, that the oxides formed during the oxidation of molybdenum are MOO, and MOO,. The dioxide is the one present next to the metal surface and the trioxide is formed by the oxidation of the dioxide. Molybdenum dioxide is a brownish-black oxide which can be reduced by hydrogen at about 500°C. Molybdenum trioxide has a colorless transparent rhombic crystal structure when sublimed, but on the metal surface it has a yellowish-white fibrous structure. It is reported to be volatile at temperatures above 500" and melts at 795°C. It is soluble in ammonia, which does not affect the dioxide or the metal. In his extensive and classic investigations of the oxidation of metals, Gulbransen2 has studied the formation of thin oxide films on molybdenum in the temperature range 250" to 523°C. These experiments were carried out in a vacuum microbalance, and the effect of pressure (in the range 10-6 yo 76 mm Hg), surface preparation, concentration of inert gas in the lattice, cycling procedures in temperature, and vacuum effect were studied. The oxidation was found to follow the parabolic law from 250" to 450°C and deviations started to occur at 450 °C. The rates of evaporation of a thick oxide film were also studied at temperatures of 474" to 523°C. In vacua of the order of 10- km Hg and at elevated temperatures, an oxidation process was observed, since the oxide that formed at these low pressures consisted of MOO, which has a protective action to further reaction in vacua at temperatures up to 1000°C. Electron diffraction studies showed that, as the film thickened in the low temperature range, MOO8 became predominant on the surface. Above 400°C MOO, was no longer observed, MOO, being the only oxide detected. The failure to detect MOO, on the surface of the film formed at the higher temperatures does not militate against the formation of this oxide, since according to free energy data MOO3, is stable up to much higher temperatures. At the low pressures employed, this oxide would volatilize off as soon as it was formed. Its vapor pressure is relatively high and is given by the equations" log p(mm iig) = -16,140 T-1 -5.53 log T + 30.69 (25°C—melting point) log p(mm He) = -14,560 T-1 -7.04 log T+1 + 34.07 (melting-boiling point). Lustman4 has reported some results on the scaling of molybdenum in air which indicate a discontinuity at the melting point of MOO, (795°C). Above the melting point of MOO,, oxidation is accompanied by loss of weight, since the oxide formed flows off the surface as soon as it is formed.5,6 Qathenau and Meijering7 point out that the eutectic MOO2-MOO3 melts at 778C, and they ascribe the catastrophic oxidation of alloys of high molybdenum content to the formation of low melting point eutectics of MOO3 with the oxides of the melts present. Fontana and Leslie -explain the same phenomenon in terms of the volatility of MOO,, which leads to the formation of a porous scale. Recent unpublished work by Speiser9 n the oxidation of molybdenum in air at temperatures between 480" and 960°C shows that the rate of weight change of molybdenum is controlled by the relationship between the rates of formation and evaporation of MOO,. They have measured the rates of evaporation of Moo3 in air at different temperatures and estimated an activation energy of 46,900 cal. This compares with the value of 50,800 cal per mol obtained by Gulbransen for the rate of sublimation of MOO, into a vacuum.

Jan 1, 1956