By A. H. Daane, B. J. Beaudry

The Sc-Y and Sc-Zr systems were studied by thermal and X-ray methods. Both systems are characterized by complete solid solubility in the low temperature hexagonal form and in the high temperature bcc form. In the Sc-Y system, there is a minimum in the solidus at 50 at. pct and 1365°C, while the solidus in the Sc-Zr system follows a nearly straight line relationship between the melting point of scandium and zirconium. There is a minimum in the temperature of transition from hexagonal to bcc in the Sc-Y system at 43 at. pct Y and 1175°C; while the temperature of transition is raised in the Sc-Zr system to a maximum of 1415 °C at 30 at. pct Zr. INTEREST in the metals of the first transition series has usually stemmed from their useful properties; however, there is now a great deal of interest in determining the fundamental nature of these metals. Since scandium is the first of these transition metals, a study of the preparation and Properties1 and the alloying behavior of scandium2 was initiated. In a continuing study of the alloying behavior of scandium, the systems of scandium with zirconium and yttrium have been established. Extensive solid solubility in both the Sc-Zr and Sc-Y systems was expected from application of the classical rules of Hume-Rothery. Also, the modified Darken and Gurry plot as suggested by Gschneid-ner3 showed ideal conditions for solubility in the Sc-Zr system with less favorable conditions in the Sc-Y system. The effect of scandium on the transformation temperature of zirconium and yttrium was of interest, since a recent empirical observation by Uly and Burr4 predicted that the solute scandium would raise the transformation temperature of zirconium and lower the yttrium transformation. In addition to noting the validity of the above predictions, the SC-Y and Sc-Zr systems were established. EXPERIMENTAL METHODS Materials. The metals employed in this investigation were crystal bar zirconium, distilled scandium prepared by the method described by Spedding, et al.1 and yttrium prepared by the method described by Carlson, et a1.5 The major impurities present in these metals are listed in Table I in ppm. Alloy Preparation. All the alloys examined were initially formed by comelting the two metals in a nonconsumable electrode arc-melting furnace under an atmosphere of purified helium or argon. The buttons were inverted at least five times and re-melted each time to ensure homogeneity. During preparation of Sc-Zr alloys, approximately 1 wt pct was lost which was attributed entirely to the loss of scandium by distillation. When preparing Sc-Y alloys, approximately 1.5 wt pct was lost, but it was assumed that the intended composition was maintained, since the relative weight lost when arc melting the component metals was nearly the same. Samples weighing 15 to 20 g were prepared for time-temperature thermal analysis, while only 1- to 2-g samples were prepared for the optical pyrometer and X-ray diffraction studies. Thermal Methods. The solidus and the melting points of the metals were determined by an optical pyrometer method described previously.2 The temperatures at which the transformation from hexagonal to bcc occurs were determined by differential thermal analysis. Several points on the solidus and liquidus in the Sc-Y system were also determined by this method and are in good agreement with those obtained by the optical pyrometer method. The procedure followed in the preparation of samples for thermal analysis and the furnace used have been described elsewhere.2'6 Since a limited quantity of scandium was available, most of the alloys were not melted during thermal analysis, thus avoiding contamination by the crucible. The alloy could then be reused and the composition changed by adding the desired quantity of solute to obtain the next alloy. Heat Treatment and X-Ray Methods. In order to ensure homogeneity, the "as arc-melted" alloys Were wrapped in tantalum foil, sealed in quartz capsules and heated at 1100°C for 15 hr and then cooled at a rate of 8 deg per min. Samples for X-ray diffraction were filed from these heat-treated alloys, sealed in 1/8 in. by 1/2 in. tantalum capsules under

Jan 1, 1963

By R. Stickler, A. Vinckier

An optical and electron microscope study was made on a commercial 302 stainless steel heat treated for massive carbide precipitation. Convincirg evidence was obtained that the grain boundary precipitate does not grow away from the grain boundary into the matrix, but grows as a network of large thin dendrites in between the grains. IN austenitic stainless steels the carbon in supersaturated solution precipitates when the steel is heated in the temperature range 450" to 1000°C. During such heat treatments the chromium-rich carbide occurs primarily at the grain boundaries and has adverse effects on the corrosion resistance and low-temperature ductility of the material. It has been shown that the morphology of the precipitated particles differs widely depending on the time and temperature of the heat treatment, the nature of the boundary, the misfit between the grains, and so forth.1"5 It was assumed by Mahla et al.,' Streicher,' and Mc Nutt' that the carbide particles which nucleate in the grain boundary grow in various geometric or dendritic forms away from the boundary into the matrix. However, Kinzel,' Hatwell et a, and Plateau et aL4 found that the particles nucleate in the grain boundary and grow as a network of thin dendrites in the grain boundary interface. We have made a comprehensive studyg of the precipitation occurring in a commercial 302 austenitic stainless steel heat treated for times ranging from 0.15 to 1500 hr at various temperatures from 480" to 1065"~. This study was made to elucidate the influence of heat treatments on both the mechanical and the corrosion properties of this steel. Part of this investigation which is pertinent to the morphology of the grain boundary carbides referred to above is separately reported here. We found that the particles which nucleated in the boundaries grew in the interface of these boundaries, thus supporting the viewpoints of Kinzel,' Hatwell et al.,3 and Plateau et al.4 Furthermore, when carbide particles nucleated in the matrix very close to the boundaries, they possessed a morphology distinctively different from the particles growing in the grain boundaries. MATERIAL A study of metallographic samples and of fracture surfaces of a 302 stainless steel is reported in this paper. The composition and heat treatments are listed in Table I. Polished and etched samples were examined und813r the optical microscope, and carbon extraction replicas of etched micrographic samples and various fracture surfaces3'8'9 were examined under the electron microscope. RESULTS AND DISCUSSION A representative optical micrograph of the 302 steel, condition A, is shown in Fig. l(a). Particles can be seen on the grain boundaries but no traces can be found of particles which grow from the grain boundaries into the matrix. A carbon extraction replica of this sample shows numerous large thin dendrites, Fig. l(b). The lateral dimension of such carbide particles vary up to 100 p, and their thickness estimated from the amoun! of electron penetration i:; between 500 and 1000A. Such large dendrites are extracted from almost all grain boundaries and, if they had grown into the grains, they would definitely be revealed by etching traces in the matrix, Fig. l(a). The reason why these large dendrites on the extraction replica appear to be grown into the grain is due to the mechanism of the extraction replica process. Thus, these dendrites are supported by the carbon replica film only at the edges originally along the grain boundary trace A-A, Fig. l(b), in the polished metal section and have subsequently fallen over onto the carbon replica film during handling. Although such dendrites generally fall only to one particular side of the grain boundary trace, one finds occasionally that parts of a dendrite have fallen to both sides, as shown in Fig. l(b). Further evidence for the growth of carbide in the grain boundary can be obtained from the appearance of fracture surfaces. A small impact specimen of the 302 steel, condition A, was broken at liquid nitrogen temperature. The fracture path follows the

Jan 1, 1962

By F. O. Jones

The capabilities of small proportions of divalent cations, such as calcium or magnesium, for controlling clay blocking are reported. Potentially sensitive formations can be exposed to fresh water if at least one-tenth of the salts dissolved in both the native water and invading fresh water are calcium and magnesium salts. Often, even less suffices. The behavior evidently depends upon the cation exchange properties of the clays, which favor adsorption of calcium and magnesium over sodium. Clays having sufficient adsorbed calcium and magnesium resist dispersion by water and consequent blocking of permeability. An allied phenomenon, the dependency of clay blocking on salinity contrast, is also reported. Abrupt change from highly saline to fresh water can cause blocking which may not occur if salinity is lowered slowly. A process related to osmosis is thought responsible for this behavior. Applications of findings to drilling, fracturing and water flooding are discussed. INTRODUCTION Many formations, when exposed to fresh water, can lose permeability through clay effects.',' For example, drilling-mud filtrate can cause oil permeability decreases, which persist long enough to interfere with drill-stem testing and well completion.3 Ultimate productivity may suffer when clay damage is severe, especially if drawdown pressures are low.' The injection pressures and the time required for water flooding can increase if clay blocking occurs. Earlier work indicates that clay blocking is caused by obstruction of flow channels by clays or other mineral fines dispersed by fresh water.'!" It is well known that increasing salt concentrations in water tends to prevent clay blocking. Also it is well established, although perhaps not as widely known, that the nature of the dissolved solids is also important. If, for instance, formation clays are exposed to calcium chloride solution and then exposed to weaker solutions of calcium chloride or distilled water, considerably less permeability damage results than if the clays had been exposed instead to sodium chloride solutions. The reasons for this behavior are: (1) clays are cation-exchange, or base-exchange, materials similar in this respect to zeolites or exchange resins, and (2) clays in the calcium form do not disperse easily in fresh water, whereas clays in the sodium form do. The base-exchange form of a clay is easily altered by flowing a solution through it. For example, a sodium clay can be changed to a calcium clay simply by passing a calcium chloride solution through the clay bed. There is general agreement that the reason calcium and magnesium clays do not disperse easily in fresh water is because the calcium ions do not ionize easily from the clay surfaces.' Sodium clays, however, are believed to allow the sodium ions to ionize from the clay particle surfaces. In fresh water, this allows the particle to accumulate a net negative electrical charge great enough for the particles to repel one another and, therefore, disperse more easily. The foregoing suggests that, even in the presence of a large excess of sodium, a relatively small ratio of divalent cation, such as calcium or magnesium, might serve to prevent clay dispersion. The divalent ion probably adsorbs to a disproportionately large extent, because of being adsorbed more tightly, with the result that the proportion of divalent cation on the exchange positions of the clay might then be great enough for the clays to resist dispersion. Consequently, an investigation was conducted to find how mixtures of salts in solution influence clay blocking. APPARATUS AND PROCEDURE Water permeability tests were conducted using conventional techniques. The equipment is illustrated schematically in Fig. 1. Flow rates of solutions driven through small core samples at known temperatures and pressures were measured. Regulated compressed air, usually at 10 to 15 psig, was used to drive the solutions. Core samples 0.75 in. in diameter and 1 in. long were used for the most part. Cores were saturated by evacuating and then admitting a de-aerated solution. Tight core samples were first saturated with carbon dioxide gas and then evacuated and saturated with the test solution. After saturation, 140 psig pressure was imposed for several hours. Cores were tested to insure absence of gas saturation by a Boyle's

Jan 1, 1965

By T. Seldenrath

In the development of a fluid -operated hammer drill' for accelerated penetration of hard rock formations in oil wells, a research investigation was conducted to evaluate the percussion effects obtained with different design characteristics and to determine the possibilities of percussion in the low frequency range. Tests were conducted on granite blocks and comparable impact forces were measured with a load cell under selected test conditions. These full-scale laboratory tests provided an evaluation of the effectiveness of percussion which was further supported by actual downhole field performance. While much pertinent data have been presented by other investigators the method of evaluation described in this article resulted in good correlation between laboratory and field performance and may be applicable in other low frequency percussion developments. EXPERIMENTAL METHOD For these tests the bit was held stationary and the test block was rotated and forced upward against the bit by a hydraulically-lifted rotary table. "Weight on bit" was calculated from pressure readings on the fluid system of the lifting cylinders—corrected for tare and friction. Percussion was obtained with several tubular hammers of different weights up to 320 lb. These were lifted mechanically and allowed to drop by gravity from various heights onto a slidably-mounted bit sub or "floating anvil" for calibration of the load cell response with known kinetic energy of the hammers. During evaluation of percussion effects, the hammers were hydraulically operated to provide a range of percussion frequencies up to 1,020 blows per minute delivered to the anvil. To obtain comparable test readings, the load cell of the strain gauge type, was attached to the bottom of the anvil or bit sub in place of the bit. The load cell rested on a typical granite test block mounted on the drilling table. The latter was hydraulically supported as in the actual drilling operation. The effect of support resistance was the same for all tools when calibrating. Impact forces so determined werethusdirectly comparable with one another for the purposes of this investigation. When a roller bit was substituted for the load cell for actual drilling, the impact force would probably be reduced due to the resiliency of the bit body, legs. cones and teeth and the penetration of the teeth into the rock. However, since the bits and rock specimens were uniform in these tests, an evaluation of actual tool performance, in terms of parameters previously determined with the load cell at the selected standard conditions of calibration, proved satisfactory. Throughout these tests, 8¾-in. standard tricone, hard rock toothed roller bits and carbide-insert roller bits were used. Rotary speeds were 50 and 100 rpm; static weight on bit was applied up to 40,000 Ib, and percussion frequencies up to 1,020 blows per minute were available. During this investigation it was found that toothed bits on which the teeth had developed flat ends about 3/16 in. wide did not change appreciably for the duration of a test. Hence, all toothed bits used in this study were in this condition. Conventional reference curves obtained in these tests show that increasing weight on hit by 2:1 yielded an increased penetration rate of approximately 2.7:1, while an increase in rotary speed of 2:1 netted an increased penetration rate of roughly 1.7:l. Results are thus of the same order as those reported for hard rock drilling by other investigators." CALIBRATION Under the selected standard test conditions previously described, with the lifting table hydraulically supported, and the anvil interposed between hammer and load cell, the hammers were dropped from known heights. Thus, with the kinetic energy of the hammer known, the corresponding maximum impact force shown by the cell was determined. (It may be of passing interest to note here that special drop tests with the hammers showed that no appreciable reduction in impact force resulted from introduction of the anvil or hit sub.) From these calibrations, it was possible to determine the theoretical kinetic energy available in the hammer from the maximum impact force shown by the load cell while operat-

By Henry R. Piehler

Continuous seven- and nine teen -filament close-packed silver-steel filamentary composites mere tested in tension. For purposes of comparison, the tensile behavior of the composite was predicted from the measured properties of the individual com-ponents. It was assumed that the axial strain is the same in both components and that the contribution of each component to the composite flow stress is proportional to its volume fraction. Good agreetnent was obtained between the observed and predicted tensile behavior. However, the composite elongation at fracture was about twice that observed when the individual steel wires were tested alone. Composites in which the filaments were widely spaced failed by the consecutive fracture of the filaments. In composites with closely spaced filaments, a composite instability preceded frachcre. These effects are explained in terms of a lateral restraint to the necking of the filaments which develops in the deforming composite. TWO-COMPONENT or composite materials are increasingly being developed and used as structural materials. Of all the composite geometries used, the filamentary configuration has proved to be the most successful. Polymer-bonded fiber-glas, the most common of the filamentary composites, has been investigated most extensively to date. One explanation of the behavior of fiberglas1 suggests that the load transfer between the glass fibers and the polymer matrix occurs primarily through friction. Bond separation between the fibers and the matrix is presumed to occur at very low stresses. Subsequently, only frictional bonding can provide for the transfer of load from the matrix to the fibers. The force normal to the fiber-matrix interface which gives rise to this friction is assumed to arise from the matrix shrinkage which occurs during solidification. The behavior of metallic filamentary-composite materials would be expected to differ from that of fiberglas in several significant aspects. Residual stresses resulting from differences in thermal contraction can be kept to a minimum by proper heat treatment. A strong wetted bond is formed between the two phases. In brazed joints,2 for example, the interphase bond is sufficiently strong that the weaker material will fail before separation occurs at the interface. Most metal filaments can undergo appreciable amounts of plastic deformation before failure. Failure by plastic instability or necking frequently occurs in metallic filaments, but not in glass fibers tested at room temperature. Differences between the behavior of fiberglas-polymer and metallic filamentary composites have indeed been observed in composites containing various types of metallic filaments in a silver matrix.3,4 At strains of the order of 10-2 pct, all the deformation was accommodated by the silver matrix. Hence, the strength of the composite depended only on the fiber concentration and not on the nature of the fiber. At higher strains, the strength of the composite increased when filaments with higher work-hardening rates were used. Surface slip line observations on a silver-mild steel composite that had been stretched 4 pct showed that an appreciable amount of deformation occurred in the filaments. Work on tungsten-copper filamentary composites5 has shown that the ultimate tensile strength for varying filament fractions followed a linear mixture rule. Assuming that the axial strains in both filaments and the matrix are equal, this linear mixture rule can be expressed as: The subscripts c, f, and m refer to the composite, filaments, and matrix, respectively. A and V are the area and volume fractions of each component. sc and of are the ultimate tensile strengths of the composite and the filaments. sm is the flow stress of matrix at a strain equal to the elongation at failure of the filaments. However, the tungsten filaments can undergo only a limited elongation before they fracture without an appreciable reduction in area. A composite containing more ductile filaments might indeed deviate from this linear mixture rule for the ultimate tensile strength, since filament failure by necking might be arrested by the matrix. SPECIMEN PREPARATION Specimens were prepared from 0.8 pct carbon steel piano wires of 0.015 in. initial diameter. The wires were given a thin nickel flash and a silver plate varying in thickness from 0.015 to 0.007 in., depending on the filament fraction desired. In order

Jan 1, 1965

By E. D. Gardner

FIFTY years ago the Utah Copper enterprise at Bingham was just getting under way. An epic in metal mining was in the making. Throughout the West the bonanza deposits were approaching exhaustion and most ore still went direct to smelter. But concentrators were shortly to be constructed for treating milling grade ores, and most important, the pilot plant for the Utah Copper enterprise was being built that year at the mouth of Bingham Canyon. The same decade was to see development at the Inspiration mine in Arizona of the most important new mining method for 50 years to come—undercut block caving. Although the average grade of ore being mined has been declining for 50 years, and wage rates and prices of supplies have been greatly increased, the mining industry has continued to grow and to prosper. Technology has advanced to a point where minerals can be mined under the most severe conditions. The hardest rock can be drilled and broken and the heaviest ground handled. Large or small, an ore-body can be mined successfully, at any desired rate of production. It is possible to pump great volumes of water and to ventilate the most extensive workings; air conditioning has made practicable the mining of ore where the rock temperatures are beyond those that can be borne by man. Mining today in the U. S. is a huge earth-moving operation. In 1953 nearly 2 billion tons of material were mined for direct use or for processing. Stripping at open-cut mines totaled about 1.7 billion cu yd. Table I gives relative tonnages of the branches of the mineral industry in 1953. In addition to the solid materials moved, 350 million tons of petroleum and 340,000 tons of gas were produced in 1953. Fifteen million tons of salt and 5 million tons of liquid sulphur were pumped from wells. An appreciable amount of copper was recovered by leaching old mine workings and dumps. Total value of minerals produced in 1953 was $14.4 billion: oil and gas $7.6 billion, coal $2.6 billion, nonmetallics $2.4 billion, and metals $1.8 billion. Formidable problems face some branches of the industry today, especially pertaining to increased output tons per manshift. The time has come when these problems should be reappraised. With current wage rates, the industry no longer can afford to pay men to do manual labor. It should be recognized, also, that the miner is a skilled worker; efforts to promote the dignity of his calling and his pride of accomplishment have yielded beneficial results. Mineral deposits occur under widely varying conditions. In most instances the degree of support needed by the roof and walls is the deciding factor in selection of an underground mining method. The degree of support needed, in turn, is governed by natural physical characteristics of the ore and its enclosing rocks. Mine operators, of course, learn to judge ground by observation, and an experienced mine boss generally can anticipate what will happen following any given mining operation. A more scientific approach, however, would be advantageous in most cases. More should be known about the strength of the ore and the enclosing rocks, more about stresses set up in the ground when ore is removed, and more about the mechanics of moving ground. Better understanding would work both ways: first, favorable rock conditions could be fully utilized for more efficient mining, and second, hazards of rock falls could be minimized, loss of ore in mining reduced, and expenses caused by ground pressures and subsidence lowered. In general, mining comprises breaking the ore or rock in place, supporting the mine workings, and transporting the ore to the surface. This latter is a materials handling problem. Ventilation, of course, must be provided, and the mines must be kept free of water. Development work at some places is the most important cost item in extracting ore. Drilling and blasting remain the usual practice for breaking ore or rock from place except, of course, at block-caving mines. The drilling and blasting practice at a mine must fit the mining method. In laying out mining procedures attention is being given to

Jan 1, 1956

By K. E. Manchester, A. H. Clark

Hall measurements have been made on three groups of silicon samples, which were implanted with boron, aluininunz, and phosphorus ions. Boron and phosphorus implants show essentially bulk properties when annealed under previously determined conditions, i.e., 15 min at 80O°C for boron and 10 mirz at 600°C for phosphorus. Bulk properties were also observed in alu?rrilzum-implanted samples when ion concentrations were below 1015 cm-'; however, strange low- terrzperalure behavior and a falloff in cavrier concenlralion was observed for sarnples with ion concenlration abozle loL5 ern-'. This can be attributed to solid-solubility effects since the average bulk concentration f0.r the sample exhibiting bulk properties was below the reported solubility limit for aluminum, while the other samples were above the limit. A detailed study of the annealirzg process indicates that mobilities reach bulk c~alues in phosphorus implants at 250DC, in alutninurn ivnplanls a1 500°C, and in boron implants at 700°C. A simple rnodel has been proposed to fit the annealing data. THE technique of semiconductor doping by direct injection of energetic ions is being actively investigated at this Center. Previously published results from this laboratory have been concerned with the investigation of implanted profiles in silicon and the electrical properties of the resultant p-n structures.1'2 Diode properties have been reported for junctions produced by implantation of boron ions and aluminum ions in n-type silicon and phosphorus ions in p-type silicon. Reverse current characteristics, as well as electron diffraction data, have indicated that the damage to the structure produced by the energetic ions during the stopping process can be minimized by a gentle anneal. The time-temperature conditions for this process have been determined by sheet resistivity studies.3 Electrical profiles of implanted phosphorus ions which have been determined by a differential sheet conductivity technique are based on the assumption that the carrier mobilities and activation energies for ionization are the same as in bulk silicon. These assumptions have been substantiated experimentally by measurement of Hall constants and resistivities of these implanted structures and the results are presented herein. After establishing the bulk property equivalence of the annealed layers, a more detailed examination of the annealing process was undertaken. The sheet resistivity technique initially used to determine anneal conditions has been broadened to include Hall constants and mobility behavior with anneal conditions. PROCEDURE The three groups of samples prepared for Hall measurements were implanted with mass-separated beams of boron, aluminum, and phosphorus ions. Ion concentrations are equivalent surface concentration and they have been determined from beam current measurements during implantation. Implant conditions for the samples are shown in Table I. In all cases, the samples had previously been angle-lapped on one edge and the junction delineated with an HF-copper sulfate solution. The surfaces of the implanted regions of the samples were exposed to the delineating solution and in the case of the "n"-type phosphorus-implanted areas it was later discovered that a finite amount of surface could be etched by this solution. This is discussed in the section on results. The implanted samples were ultrasonically cut into the conventional six-probe configuration shown in Fig. l.* In the annealing studies, for which the meas- urements were taken at room temperature, the sample holder was a Bakelite jig incorporating tungsten mechanical probes. The other measurements were taken using a conventional liquid-nitrogen cryostat, in which the temperature could be varied from 77" to about 400°K. For these measurements, 10-mil aluminum dots were evaporated onto the samples and alloyed with the silicon at 530°C for 15 min. The samples were then mounted in flat-packs, and gold wires were bonded to the aluminum dots. The electrical measurements were made with either a Leeds & Northrup K-5 Potentiometer, a Keithley 147 Nanovolt Null Detector, or a Keithley 601 Electrometer. No external bias was applied to the substrate. There is an inherent self-biasing arrangement at one or the other of the current contacts (depending upon the polarity), and this suffices to limit the current flow to the implanted layer. The magnetic field was generated by an A. D. Little electromagnet. Except for occasional checks of linearity of the Hall voltage with

Jan 1, 1969

By T. P. Floridis, J. H. Young

The need for close control of the phosphorus content of steels has led to numerous investigations on the equilibria of the dephosphorization reactions. Winkler and chipman1 have established the general conditions for effective dephosphorization of steel. They are high slag basicity, high oxygen potential, and low temperature. Other investigators have made additional contributions to the understanding of the dephosphorization process. The current status of the understanding of the dephosphorization of steel is concisely presented by Bodsworth2 and by Ward. The investigation reported in this communication was undertaken with the purpose of establishing the effect of additions of barium oxide and calcium fluoride on the dephosphorizing capacity of slags. Esin and Gel'd4 proposed that barium oxide, being more basic than calcium oxide, should cause an increase in dephosphorizing capacity when added to steelmaking slags, or when used as a substitute for calcium oxide. Derge5 has also proposed that in the future conventional slags might be replaced by BaO-Al2O3 slags. There is, however, no experimental evidence confirming the effect of barium oxide on the dephosphorizing capacity of slags. The effect of calcium fluoride on the dephosphorization of steel is not clearly understood. It is generally recognized that additions of calcium fluoride are beneficial. It is not clear, however, whether calcium fluoride affects the equilibrium of the dephosphorization reaction, or whether it simply causes an increase in the fluidity of the slag and, consequently, faster approach to equilibrium. The experimental procedure consisted in equilibrating synthetic molten slags with liquid copper at 1550°C under a gas stream containing argon, hydrogen, and water vapor. In all experiments the argon to hydrogen ratio was approximately 4:1, and the hydrogen to water ratio was 5.42:l. Molybdenum crucibles were used as containers for the slag and metal. Under the above-described conditions of temperature and composition of atmosphere, there was no observable attack of the crucibles by the metal, slag, or atmosphere. Copper was used instead of iron, because iron attacks molybdenum. The equilibration was made in a tubular furnace consisting of a recrystallized alumina tube. The alumina tube was heated by electrical resistance. A Pt-40 pct Rh wire winding was used for most runs. A silicon carbide tubular resistor was also used for some runs. Temperatures were measured with a Pt-Pt-Rh (10 pct Rh) thermocouple and kept constant within ±5°C. Equilibrium was approached from both sides, i.e., by adding the phosphorus either as oxide in the slag or as a phosphorus-rich alloy of phosphorus and copper. The holding time at the equilibrium temperature was 6 hr. At the end of each run the crucibles were rapidly cooled and removed from the furnace. The slag and metal were separated and analyzed. The experimental results are shown in Table I. The phosphorus content of the slag is expressed both as percent phosphorus pentoxide and as percent phosphorus. The basicity ratio is computed by dividing the number of moles of basic oxides-oxides of barium, calcium, magnesium, and sodium—by the number of moles of acidic oxides- oxides of aluminum, phosphorus, and silicon. Calcium fluoride is not included in the computation of the basicity ratio; i.e., calcium fluoride is assumed to be neither basic nor acidic. The distribution ratio of phosphorus—percentage of phosphorus in the slag divided by the percentage of phosphorus in the metal- is plotted in Fig. 1 against the basicity ratio. The results indicate that slags containing barium oxide have greater dephosphorizing capacity than slags containing calcium oxide. The high dephosphorizing capacity of slags containing sodium oxide and the low dephosphorizing capacity of magnesia-containing slags which already have been reported in the literature2 are confirmed by the results of this investigation. It appears that calcium fluoride has a beneficial effect on the distribution of phosphorus between slag and metal in acid slags only. Although the obtained distribution ratios between the phosphorus contents of slag and copper are not directly applicable to the dephosphorization of steel, they are sufficient for evaluating the effect of slag additions on the dephosphorizing capacity of slags in general. An increase in the ratio of distribution of phosphorus between slag and metal indicates lowering

Jan 1, 1968

By A. E. Dwight, Paul A. Beck

Known CsCl-type phases in transition metal alloys are shown to be formed preferentially at an electron concentration of approximately 6; a tetragonally distorted version of the CsCl structure is stable at -e/a = 6.5. The relationship of the distortion to electron concentration is verified by experimental data for the quasibinary systems Time ,Os) , Ti(Re,Ir), and Ti(Re,Pt) and the ternary system Ti-Ru-Rh. It was noted some years ago1j2 that the occurrence of CsC1-type ordered structures in equiatomic binary alloys, AB, of transition metals correlates with the location of the component elements in the periodic table. One of the components, A, must be to the left and the other component. B, must be to the right of the chromium group. It was pointed out2 that the CsCl structure does not occur in CrFe. is metastable in VFe,3 and is stable in TiFe up to high temperatures, and that this progressively increasing stability may correspond to an increase in electron transfer between the two components and to a correlated decrease of the magnetic moment associated with the iron atoms. Such a decrease was in fact later demonstrated by Nevitt. 4 The binary CsC1-type phases that are formed by a transition metal with either another transition metal or a lanthanide are listed in Table I. Thirty-three of these phases occur at an average electron concentration (average number of electrons outside of closed shells) of e/a = 6. The five phases that are formed at an electron concentration of e/a = 5.5 appear to be borderline cases. This is suggested for instance by the fact that TiRe is bcc. without any long-range order, while TiTc (at the same electron concentration) has a CsCl ordered structure. Six of the undistorted CsCl phases formed by transition metals with one another have an average electron concentration of e/a = 6. 5. Table I. With the exception of Zr4,Rhs4 and Hf48Rh52. the B component in these phases is a first long-period transition metal, i.e.. iron or cobalt. TiNi. with an electron concentration of e/n = 7, appears to undergo transformation at around room temperature to a more complex ordered struct~re.~ The five other CsCl structures known to occur at e/a = 6.5 have either scandium or a lanthanide metal as the A component; the difference in the elec-tronegativity and in the e/a ratio between the component elements is in these phases very large, A(e/a) - 7, and they may be expected to have a rather strong ionic bond component. Presumably the ionic bond stabilizes the CsCl-type structure at the equiatomic composition and it overrides the electron concentration requirement. When the B element is not from the first long period and the A component is not a rare earth metal. equiatomic (AB) alloys of transition metals with an average electron concentration of e/a = 6.5 in most cases have a crystal structure closely related to the CsC1-type, but slightly distorted tetragonally, Table I. This was first found6 for VRu, NbRu. and TaRu. It was noted6 that the undistorted CsCl structure is also stable in the three systems. but at a lower electron concentration, near e/a = 6. In these systems this requires a deviation from equiatomic stoichiometry. which is otherwise ideally suited for the CsC1-type structure. A similar situation was later found in the Ti-Rh7 and the Ti-Ir systems. 8 The Ti-Rh alloys undergo a second distortion and become orthorhombic when the rhodium content becomes somewhat larger than 50 pct. As mentioned previously. TiRe does not have the CsC1-type ordered structure. In order to investigate how close TiRe is to the borderline of stability of the

Jan 1, 1970

By R. E. Shinkosk

This paper outlines the development of a program for increasing the life of woolen bags used for filtering Dwight-Lloyd gases by treating the bags and gases with hydrated lime. Methods and apparatus are described for determining alkalinity of dusts, acidity and breaking strength of bag cloth. Procedure and results, based on several years of operation, are presented. DURING 1939, additional facilities were constructed in the Dwight-Lloyd Blast Furnace and Baghouse departments at the Selby, California, Plant of the American Smelting and Refining Co. In order to handle adequately the increased volume of gases from the resultant increase in production, it was necessary to increase gradually the amount of water used for cooling gases ahead of the sinter machine baghouse. As a result of this increased water cooling, the average bag life dropped from 27 months in 1939 to 14 months in 1941. (Table I). This drop in life meant an increased. bag cost, as well as lower recovery of dust and some curtailment of operation. During 1941, it was found new bags showed as high as 0.3 pct acidity* after two weeks of opera- tion and as much as 2.0 pct acidity after some months of operation. This high acidity was present in spite of the fact that free oxide or relative alkalinity of the unburned dust ran from 5 to 6 pct. In view of these circumstances, a twofold program was started in Nov. 1941.t Part one of this program consisted of vigorously dipping all new bags in a weak lime solution, containing 50 lb of hydrated lime per 50 gal of water. Part two consisted of feeding fine, dry, hydrated lime into the gas stream intake of the sinter baghouse fan. Apparatus for feeding this lime is shown in fig. 1. All baghouse chambers are shaken in rotation about once each hour. On alternate hours, the baghouse operator places 50 lb of hydrated lime (one sack) into the lime feeder, starts feeder and immediately starts the bag shaking machinery. The rate at which lime is fed is set to coincide with the approximate time necessary to shake all sinter bag-house chambers, or about 15 min. It is felt this method of lime addition is most effective for getting lime into the woolen bag fabric. The amount of lime so fed averages about 600 lb per day. The amount of lime fed per day is varied to keep a minimum relative alkalinity of 9 pct in the unburned sinter dust. A daily dust sample is taken for alkalinity by allowing dust to accumulate in a sample pipe over a 24-hr period. This sample pipe, placed in any chamber cellar, is 2 in. in diam, 4 ft long, is sealed on the inner end, and capped on the outer end. It has a 1/2 in. slot cut for 18 in. along the tip end. This slot faces upward and allows the pipe to fill gradually with dust as bags are shaken. Breaking strength of bags has, in most cases, been the deciding factor in bag replacement. Bags that normally test 100 psi breaking strength when new are replaced when they test under 35 lb. The method for determining breaking strength is shown in the description accompanying fig. 2. Since the start of the liming program in 1941, bag life has increased from 14 months to an average of over 23 months, with a consequent material decrease in bag cost per year. Acidity, as per cent sulphuric acid, may be determined by means of a Beckman pH meter as follows: From a piece of bag cloth. which has been thoroughly cleaned of dust, a 5 g sample is weighed on a balance. Cut the sample into fine pieces and place in a 400 cc beaker. Add 100 cc (measured) of distilled water and stir vigorously. Filter on suction funnel, holding cloth pulp in beaker with a stirring rod. Wash cloth sample and filter wash water four additional times, each time with 20 cc distilled water, the last time squeezing cloth pulp over funnel. Discard pulp and rinse funnel and filter paper. Pour wash solution jnto measuring graduate and make up to exactly 300 cc with distilled water. Place into clean 600 cc beaker and measure the pH on meter. The per cent acid in bag cloth is read from the following table:—

Jan 1, 1951

By O. W. Simmons, L. W. Eastwood, C. M. Craighead

H. Schwartzbart and W. F. Brown, Jr.—The authors have divided the effects of recovery on the true stress-true strain curve into two types; metarecovery, which effects only the first part of the curve or the yield strength, and orthorecovery, which effects the flow stress at any strain. Both of these are said to be true recovery effects, involve no recrystallization, and are explained by the removal of two different types of imperfections caused by work hardening. However, there seems to be some question as to whether the data are sufficiently conclusive to exclude, as an explanation of the authors' results, a mechanism based on the relief of residual stresses between the grains or slip bands and recrystallization. It appears that metarecovery could be interpreted in the same fashion as a customary interpretation of the Bausch-inger effect. The balanced system of internal stresses which exists between grains in a strained specimen due to varying orientation and, hence, yield strengths, of the different grains is responsible for a reduced yield strength in compression following pre-tension, and, similarly, for an elevated yield strength in tension following pre-tension. If the specimen is now heated so that the internal stresses are relieved by creep, then the yield strength in tension following tension will have been reduced and in compression following tension will have been raised. There seems to be a very strong case for the lack of recrystallization in the aluminum investigated by the authors, if one defines recrystallization as the presence of visually detectable new grains or accepts the X-ray evidence as conclusive. One must remember, however, that the appearance of spots on the back-reflection X-ray patterns cannot be taken as the time when recrystallization first started. The areas of recrystallized strain-free material must first have grown to a size large enough to give distinct spots on the patterns and this may take some time. Averbachl7 in an investigation of brass has shown that recrystallization can be detected by extinction measurements at temperatures lower than those based on hardness or X-ray line width determinations. It can be seen from fig. 10 that the rate of recrystallization is extremely low over a considerable time period at the onset of the process. Observations on the rate at which small amounts of recrystallization effect the flow stress would have given further insight as to whether undetectably small amounts of recrystallization might have been responsible for orthorecovery. Also, the question arises as to whether the effects observed in fig. 6 for various times and temperatures could not have been obtained if the time at 212°F were sufficiently long. In addition, the argument that the curve in fig. 10 is not sigmoidal seems weak in view of the scattering of the points. It is conceivable that an accurate determination of the curve for the first 100 hr would exhibit a relationship other than the one drawn. There is one point we would like to raise about the condition of the starting material. The authors annealed their material at 750°F for 15 min to remove the effects of any previous work hardening or machining strains. Reference to the work by Anderson and Mehl shows that this treatment may not have completely recrystallized the aluminum, so that the starting material may have had some strained areas. Higher temperatures or longer times may have been required to remove the effects of any small strains. We would like to mention some results of tests being conducted at the Lewis laboratory of the National Advisory Committee for Aeronautics in an investigation of the Bauschinger effect in relation to fatigue. Tests were performed on annealed electrolytic copper and several annealed brasses. Specimens were pre-strained 1 pct in tension and then tested in compression or tension with and without intermediate stress-relieving annealing treatments at 500°F for various times. Specimens heated at 500°F for 10 1/2 hr showed an elevation of the flow curve in compression and an approximately equal lowering of the flow curve in tension when compared with the curves for the un-heat treated specimens. After approximately 0.8 pct strain, all flow stresses coincided and were equal to the flow stress of the virgin material at this strain. This behavior is consistent with the metarecovery observed for aluminum by the authors and for which a residual stress model can be used. On the other hand, increas-

Jan 1, 1951

By J. Downie, H. A. Kendall, G. H. F. Gardner

Some cases of the motion of two miscible fluids in uniform linear models are discussed. There is no bulk flow through the models, and the convection currents are caused solely by density gradients. Horizontal, vertical and inclined positions of the models are treated separately. Analytical formulas for the motion of a narrow transition zone between the fluids are obtained and compared with measurements, and the limitations are discussed. Observations of the ultimate stabilizing effect of diffusion on the motion me compared with the theory. It is shown that fluid motion in an inclined model with a constant rate of bulk flow can be directly deduced from the cases discussed, provided the viscosity ratio is small. INTRODUCTION In some reservoirs, convection currents caused by variations in the fluid densities may be significant. For practical purposes it may be desirable either to minimize the effect, particularly in miscible displacement, or to maximize the effect as in some schemes for the production of heavy crude oils by combustion. Experiments by Craig, et al,l have shown the effectiveness of gravity in reducing the efficiency of a miscible displacement when the mixed zone between the displacing and displaced fluids is narrow compared with the height of the system. The presence of a board transition zone from one fluid to the other has been shown by Perkins, et al,2 to nullify considerably the influence of a difference in density. Indeed, the theoretical discussion given by Perrine3 has shown that when the transition zone exceeds a certain critical length the efficiency approaches 100 per cent. Many additional results 495 have been published on miscible and immiscible displacements which show the importance of density difference and also mobility ratio. The aim of the present paper is to discuss some cases of gravity segregation of miscible fluids in linear models such as are often used in the laboratory to evaluate recovery processes, and to supply additional experimental evidence in support of the conclusions. An attempt is made to calculate simply the magnitude of the fluid motion caused by density pdients and mobility ratios, and to quantify the modifications in the fluid motion produced by the combined effect of molecular and convective dispersion. However, it should be pointed out that the uniform permeability of the models and the use of only a single pair of fluids (whereas several pairs of fluids may be employed in a recovery scheme) severely restricts direct conclusions about natural reservoirs. For conciseness, the motion generated by density gradients is emphasized for the case of no bulk flow through the models. This is not a drastic limitation because, as shown in Appendix A, a fluid motion with a constant bulk flow through any linear model is equivalent to a fluid motion with no bulk flow in the same model inclined at a different angle to the horizontal, provided only that the density is a linear function of the viscosity of the fluid mixture. HORIZONTAL MODEL In this case the model is assumed to have a rectangular cross-section with a horizontal breadth b, vertical height and a great length L. Throughout.the paper it will be assumed that x-axis points along the length, the y-axis along the width and the z-axis along the height. Thus, in the present case the x, y plane is horizontal. Initially, the transition zone between the fluids is assumed to be thin and parallel to the y, z plane. An example of this situation in a practical problem arises in a scheme for using air for cushion gas in the storage of fuel gas in aquifers. 6 With the passage of time the denser fluid sinks and spreads along the bottom of the model while the lighter fluid rises. The interface extends from the top plane of the model to the bottom. Experiments have shown that for practical purposes this interface may be treated as a plane surface at all times. The surface is significantly curved, however, for viscosity ratios greater than about 10. Other complications arise with large viscosity ratios because of the nonlinear dependence of the viscosity on the composition of the mixture, so that the simple results given here are restricted to fairly low viscosity ratios.

By Laurance S. Reid, Joe A. Porter

Gas dehydration plays an important part in the production of natural gas. Effective dehydration prevents formation of gas hydrates and the accumulation of water in transmission Systems,2,6,7 insuring uninterrupted gas deliveries at maximum efficiency under the most adverse weather conditions. At the present time, most gas companies require a maximum water vapor content of seven lb per million standard cu ft of gas. so that virtually all gas tendered for sale must he dehydrated to meet this specification. For a number of years it has been common practice to produce gas and gather it at a common point for dehydration prior to discharge into the transmission system.1,3,11,16,17 However, higher transmission line pressures, long gathering lines and relatively low ground temperatures have made it necessary to dehydrate gas at. or near. individual. wells in order to gather gas from a number of newly developed fields without unusual difficulty. Where gas has been dehydrated at pressures ranging from 300 to 800 psi in the past. future trends indicate that these processes may be operated at pressures as high as 2,000 psi. Economics of gas dehydration are of great importance, partitularly where facilities must he provided to process relatively small quantities of gas, such as the production from an individual well. Although the adsorption of water vapor from gas on a granular sorbent material such as activated bauxite, activated alumina, or one of the alumina-silica gels is highly effective and produces virtually "bone dry" gas, the cost of a small unit of this type is substantially greater than that of an absorption process which, through proper selection of the absorbing liquid, will dehydrate the gas sufficiently to meet pipe line specifications. For this reason, a great deal of emphacis has been placed on the development of small, inexpensive dehydration units8,24 and the search for more effective absorb. ent liquids has been intensified. A wide variety of methods for dehydrating gas are known' and many of these have been used in industry. Earlier applications of the absorption process employed concentrated solutions of calcium and lithium chlorides as the absorbent. The severe corrosion problems inherent in handling these solutions and the relatively small dew point depressions obtained caused early abandonment in favor of, or conversion to. diethylene glycol when it was found that aqueous solutions of this organic liquid were more hygroscopic than the brines and were non-corrosive. Processes employing diethylene glycol-water solutions are widely used for gas dehydration at pressures ranging as high as 1,200 psi.13,14,15 At nominal pressures a dew point depression of 45° to 50°F may be be and the data of Russell et al." indicate that a minimum dew point is obtained from the effluent gas at a pressure of approximately 1,200 psi when the gas is in equilibrium contact with a 95 per cent by weight diethylene glycol solution. In a number of instances the dew point depression obtained with diethylene glycol-water solutions is not sufficient to produce a specification product without cooling the inlet gas. In a recent search for a better absorhent, triethylene glycol was used in a small commercial dehydration unit and subjected to rather exhaustive field tests.' The data obtained were encouraging and indicated that, at pressures ranging from 300 to 500 psi, triethylene glycol porduced a substantially greater dew point depression than diethylene glycol. These results led to an investigation of the system natural gas-water-triethylene glycol in an effort to obtain vapor-liquid equilibrium data, to determine pressure limitations, and to develop other data pertinent to the design of gas dehydration processes. A review of the literature has failed to reveal any data which permit reasonably accurate calculation of the vapor-liquid equilibrium conditions for a solution of water and triethylene glycol in contact with natural gas at high pressure. Since these constituents form a non-ideal system, the Poynting equation18,21 or the usual combination of Raoult's and Dalton's laws19,20,22 would not be valid. Correction of Raoult's and Dalton's laws by the use of activity coefficients2' is not feasible for available data are insufficient for the prediction of the actual increase in the ratio of the activity of one component in the vapor phase to its activity in the liquid. Therefore. experi-

Jan 1, 1950

By H. C. Chang, N. J. Grant, A. R. Chaudhuri

During the creep of coarse-grained polycrystalline magnesium at elevated temperatures, a nonbasal type of slip was found to play an important role in the deformation processes. The nonbasal slip traces were examined metallographically in eight specimens (13 grains) and the observed glide plane located stereographically for each grain. The tests were run at 500&apos; and 700°F at stresses of 148 to 786 psi. Based on these measurements and theoretical calculations, the crystallographic elements for nonbasal slip were determined. WHEN a metal deforms by slip, the conventional appearance of the slip bands on the surface of a specimen is that of straight lines. Such is the behavior of the face-centered-cubic metals, as for example, aluminum. The particular slip system on which slip occurs in these metals is governed by the criterion of resolved shear stress. Work on the body-centered-cubic metals a-iron,&apos;. &apos; molybdenum, and columbium4 has shown that the process of slip is somewhat more complicated than the simple gliding of one close-packed plane of atoms over another in a close-packed direction and that it results in the formation of wavy and irregular slip traces on the surface. The recent reviews and experiments of Vogel and Brick and Chen and Mad-din3 show that, for the body-centered-cubic metals, the resolved shear stresses along the planes and the degree of close-packing do not necessarily determine the slip system. Theirs and other investigations indicate that a complete understanding of the slip process in the body-centered-cubic metals is not yet possible. However, one behavior displayed by all these metals is that the slip direction is invariably one of the close-packed directions <11l>. The wavy nature of the slip-band traces has been explained on the basis of cooperative slip by planes sharing this same slip direction.1&apos;3l&apos; It is generally acknowledged that, when the hexagonal-close-packed metal magnesium (axial ratio c/a = 1.624) deforms by slip at room temperature, it does so by basal slip in the close-packed direction <1I%>. This type of slip has the conventional appearance of straight lines and is governed by the critical shear-stress law. Schmid and coworkers" showed that basal slip was operative in the temperature range of —185" to 300°C (—300" to 572°F). Work by Servi, Norton, and Grant6 has shown that, during the creep of coarse-grained aluminum at high temperatures, new slip systems come into operation. The existence of a new high temperature slip system at temperatures greater than 225 °C (437°F) for magnesium was suggested also by Schmid. This was later indicated by Bakarian and Mathewson&apos; to be slip along the pyramidal planes (10i1) in the close-packed direction <11%>.* They * Mention will be made in the text of pyramidal planes and prismatic planes. The pyramidal planes referred to are the type I. order 1 of the form {10il); and the prismatic planes of the type 1 of the form (10i0). For the sake of brevity, they are termed in the teat as pyramidal (10il: and prismatic (10i0) planes, respectively. Where reference is made to the pyramidal plane type 1, order 2 of the form {10i2), they are referred to as the pyramidal planes of the type (10i2:. observed that this kind of slip resulted in irregular markings on the specimen surface. According to them, a possible cause for the appearance of the markings was due to "limited accessory slip on the pyramidal {10i2) planes." Burke and Hibbard," on deforming a single crystal of magnesium at room temperature, found evidence of slip on a pyramidal plane {1011). They explained it as being due to the effect of grip restraints. It is pertinent to note at this point that, although basal slip has received a fair amount of attention, only two specimens have been investigated, that of Bakarian and Mathewson and of Burke and Hibbard, to establish the elements of nonbasal slip in magnesium. During the study of the deformation mechanisms

Jan 1, 1956

By R. J. Wagner, G. H. Gronhovd, A. J. Wittmier

The paper describes the results of a series of full-scale boiler tests run to determine the ash fouling characteristics of a North Dakota lignite as a function of sodium content of the coal. Four levels of sodium were investigated and rate of fouling was determined both by boiler performance and by specially constructed probe equipment. Discussed is information on chemical and physical properties of the ash deposits. The vast lignite deposits in North Dakota are becoming increasingly important as a source of low-cost fuel for power generation. A new 200-megawatt lignite-burning plant located near Stanton, N.D., was placed in operation early in 1966. Another 172-mega-watt unit in the same area is scheduled for operation late in 1966, and plans have recently been announced for a 212-megawatt unit to be in operation by 1970. If these plants show good performance, western North Dakota could become a major power production center for a large geographic area in the upper midwest. One of the problems associated with the use of lignite in power boilers is its tendency to form troublesome ash deposits on boiler tube surfaces. This problem varies considerably from one lignite-fired boiler to another and is dependent upon such factors as source of lignite, boiler design, load factor, tube metal temperatures, and soot-blowing practices. This report presents data on sodium content* variation in a North Dakota mine, describes the results of a series of tests performed to determine the relationship between ash fouling tendencies and the sodium content, and tells how the mining company and electric utility have coordinated their operations to reduce the ash fouling problem. GENERAL BACKGROUND Until recent years it was generally assumed that North Dakota lignite from a given mine had qualities peculiar to that mine, but that within the mine, the lignite was quite uniform. In 1959, the Otter Tail Power Co. installed a 53.5-megawatt lignite-burning unit at its Hoot Lake plant, Fergus Falls, Minn. Shortly after the unit was put into operation, it was noted that at certain times under high load conditions, ash fouling problems were quite severe, but not consistent or predictable. Each time fouling occurred in the unit the position of the loading shovel at the mine was noted. Within two years it became apparent that there were certain areas in the Knife River Coal Mining Co. mine at Beulah, N.D., where the lignite apparently had a high fouling tendency for the Hoot Lake unit. Results from analyses of the coal did not show large differences in moisture percentage, ash percentage, heating value, or ash fusion temperature between the highly troublesome and less troublesome coals. After three years of operation, the troublesome areas had been quite well defined and the mining company started a procedure of bypassing these areas when load conditions at the plant were high and then returning to the troublesome areas to load the lignite during the summer months when peak loads were lower. It was noted that the lignite from the areas which caused severe fouling under high load conditions produced much less fouling at the lower summer loads. However, bypassing certain areas in the strip pit caused the mining company to disrupt their continuous loading schedule, which in turn upset their continuous stripping schedule and made for less efficient mining operation. Meanwhile, at the Hoot Lake plant, the number of soot blowers on No. 2 boiler had been increased from 30 to 55, and a very rigorous blowing schedule had been adopted resulting in soot blowers operating at least some part of 21 hrs per day. Fouling problems continued, with a resulting reduction in plant economy and reliability. During this period the Federal Bureau of Mines Coal Research Laboratory at Grand Forks, N.D., had initiated various research programs relating to the study of lignite ash and ash fouling problems. One project was a survey in which full seam samples were obtained from various locations in all the major

Jan 1, 1968

By John E. O’Rourke, Kevin M. O’Connor, Pamela H. Rey

INTRODUCTION The resurgence of coal mining activity in the United States, brought on by the spiraling costs of fossil fw1 energy in the Seventies, has come at a time of intense public concern for the quality of the environment. Notwithstanding pressure on our economy to develop alternate sources of fue1 energy to the import of oil, the legislatures of several states have reacted to public concern over the environment by passing strict regulations aimed at con- trolling the subsidence effect s of underground mining. Agencies of the federal government charged with assistance to the mining industry, including the Department of Energy and the Bureau of Mines, have sponsored a number of instrumentation and field measurement projects aimed at the development of subsidence prediction models that can aid the mine operator&apos;s task of subsidence control. There are good empirical models developed in Europe for subsidence prediction, but they were made possible by a large body of mining-induced subsidence data collected there over a long period of time. No com- parable subsidence data base exists in the United States, and consequently empirical modeling of subsidence is not a realistic approach for our near term needs. Moreover, the geologic and topographic diversity of the several coal regions in the United States is expected to necessitate the development of several empirical models, each one expected to be relevant to its own region. Because of the time and costs that are likely to be involved in an empirical modeling approach, it is considered more expedient and cost effective to develop a general, mechanistic model for subsidence prediction purposes. In order to develop such a model, it is necessary to investigate and quantify the mechanics of the subsidence process from the mine level up to the ground surface. The series of projects discussed in this paper are designed to achieve this objective and include the following work: (1) the identification of geotechnical instrumentation that will pro- vide mine level overburden and surface subsidence data. (2) a field demonstration of selected instruments, and (3) documentation of case histories for complete subsidence mechanics, using the demonstrated and preferred instruments. An identification of feasible instrumentation and monitoring techniques was completed by Woodward-Clyde Consultants (WCC) in 1977 (O&apos;Rourke and others). This paper discusses a demonstration of those instruments at a mine in Utah, and at two subsequent projects, currently underway at longwall mines in Colorado and West Virginia. &apos;he latter two projects when complete will provide documented case histories of subsidence mechanics. The process of optimizing subsidence instrumentation and monitoring techniques to the conditions encountered during installation and monitoring for these underground mines is shown to be an evolving one, and one which has had some notable successes to date. INITIAL DEMONSTRATION The initial design and demonstration of selected monitoring systems was carried out at the SUFCO No. 1 mine, near Salina, Utah. The instrumented panel was approximately 152 m wide. 640 m long. and was 290 m to 320 m deep. The mined height of coal. seam averaged 2.4 m. The mining method was room and pillar using continuous mining machines. This method allowed some monitoring of the supported condition during development, and eventually allowed monitoring of a caved system when both chain pillars and room pillars were extracted on retreat. The two instrument systems shown on Table 1 were selected from the earlier feasibility report for demonstration at SUFCO No. 1. Collectively, the two systems, one for a fully-supported mining method and the other for a fully-caved method, incorporate most of the instrumentation to be found within all five systems listed in the earlier feasibility report. The instrumentation includes surface, subsurface and mine monitoring installations. All of the SUFCO instruments selected to meet the specifications of the general instrument types listed on Table 1 were manually operated. That is, data from the installed system could only be obtained while a person was there to physically observe or operate the system readout. Automatic data recording equipment was available for some installations, but the objectives were to keep the systems as simple as possible for the demonstration project. A complete description of the surface, sub- surface and mine level instruments, and the demonstration project results are given in WCC (1982), and selected features are discussed in this paper.

Jan 1, 1982

By R. D. MacDonald, John Dasher, A. M. Gaudin

ION exchange is a widely used unit operation in water treatment and elsewhere in chemical industries. It has occasionally been used in hydro-metallurgy for treating plating, pickling, and rayon wastes Concerning ion exchange in extractive hydrometallurgy—for treating ore leach solutions— the literature prior to the Geneva Conference has given only hints."-" Yet most of the ore leach plants now being built or completed in the last three years use ion exchange for this purpose. Most of these plants are used for extracting uranium. The overall process for leaching low grade uranium ores and the history of its development have been given in the authors&apos; previous papers.&apos;,&apos; The object of this paper is to discuss certain engineering aspects of the new application of ion exchange to recover dissolved values from ore leach solutions. Necessarily the illustrations will be taken from the first application—to uranium metallurgy. Although ion exchange processes have been devised in which separation of spent residue from pregnant liquor is not required, as in the RIP process,"-&apos;I only ion exchange operation, in which the resin is contacted with a clear solution, will be discussed in this paper. Uranium exists in acid leach liquors mainly as the cation UO," and can be adsorbed completely by cation exchange resins, but the adsorption is not selective as other cations such as Fe++, Fe+++, Al+++, Mg++, Mn", and Ca++ are also adsorbed. Uranium, however, forms complex anions with sulfate, phosphate," Carbonate"~"~ and even with chloride if the solution is strong enough.15 These anions can be adsorbed by anion exchange resins. The strong base anion exchangers have a very strong preference for these complexes and hence this adsorption is very selective. In this paper, the examples concern acid sulfate leach liquors from which uranium is adsorbed as UO,(SO,),-% and UO,(SO,),". Materials and Equipment Ion Exchange Material—Ion exchange materials include natural and synthetic; organic and inorganic; cationic and anionic; and weak, intermediate, and strong varieties. They consist of fragments or beads normally in the size range —16 to $50 mesh. The newer varieties have been developed to have greater stability, chemical strength, and/or capacity than earlier varieties. The resin used for uranium recovery is a strong base anion exchanger.* To make * Such as Rohm and Haas Amberlite IRA-400 series, British Permutit DeAcidite FF. Permutit lonac SE. and Dow Nalcite SAR. this resin, styrene plus a few percent divinyl benzene are polymerized into long chains with occasional cross links. This resin in bead form is then reacted to introduce quaternary amine groups onto most of the aromatic rings.&apos; These resins are water-avid gels of specific gravity of about 1.1, which shrink and swell by osmosis when the ionic content of the surrounding solution is changed. The beads which are shown in Fig. 1 can be broken like an onion by rapidly replacing 15 pct H,SO, with water. This organic gel can also be broken by mechanical handling as by a centrifugal pump. Otherwise it is remarkably stable. It is unharmed by fairly strong acid or alkali, oxidizing or reducing agents, and heat up to 70°C. The strong base resin when completely in the chloride form (with a chloride anion on each quaternary amine group) holds over 107 g of C1- per dry kg. As all these chloride ions can be displaced by other anions, the resin has an exchange capacity of over 3 g equivalents per dry kg. However, the resin is sold and used by moist volume. The moist resin contains about 50 pct water, weighs about 43 lb per cu ft, has 40 pct voids, and an exchange capacity of over 1 g equivalent per liter of bed volume. Ion Exchange Equipment—Ion exchange equipment used for recovery of uranium from leach solutions is substantially identical to that developed for water treatment and other applications.&apos;" The resin beds are held in closed tanks or columns which, in the uranium plants, have been standardized at 7 ft diam and 12 ft high. The resin bed

Jan 1, 1958

By A. R. Troiano, A. B. Greninger

There is need for an adequate working hypothesis that would describe at least qualitatively the crystallographic mechanism for the transformation from austenite to martensite in steel. A general theory would not only be of great assistance in the correlation of existing data and in planning future experimentation, but would also form the basis for an eventual explanation of the property changes that accompany lattice transformations. The mechanism of martensite formation described in the following pages is the outcome of two new experimental determinations: (1) the accurate evaluation of the lattice relationship between austenite and individual crystals of martensite, and (2) the measurement and analysis of the change in position that a volume of austenite undergoes when it transforms into a crystal of martensite. For this latter study, the stereographic analysis of shear was employed; this method greatly simplifies the solution of lattice-shear problems, and some space is devoted to its description. Lattiice Relationships and Habits PREVIOUS WORK The lattice relationships between austenite and martensite in carbon steels have been studied by Kurdjurnow-and Sachs,&apos; and by Wassermann;2 and in iron-nickel alloys by Nishiyama.3 Wassermann,2 and Mehl and Derge.4 The studies by Kurdjumow and Sachs and by Wassermann were made on single (austenite) crystals of quenched 1.4 pct carbon steel, and the results of these two independent studies agree closely with the postulated lattice relationships: (III)r||(0ll)a [101]r [111]a [1] Both Nishiyama and Wassermann worked with an alloy of iron plus 30 pct nickel (all austenite at room temperature), and "martensitic alpha" was formed by cooling in liquid air. They agree that the lattice relationships for these conditions are: (lll)r||(011)a [112]r[011]a [2] Mehl and Derge worked with a range of iron-nickel alloy compositions centered about 30 pct nickel. They concluded that when the transformation takes place near room temperature or above, relationship [l] holds, but if the same specimen is made to transform at -195°C, relationship [2] obtains;intermediate temperatures evidently produced a combination of these two relationships. Sachs and co-worker~,1,7 as well as Nishiyama,3 have proposed transformation mechanisms for martensite formation.* Both of the mechanisms picture the transformation as initiated by shearing movements along the octahedral [Ill] plane of austenite, followed by suitable expansion and contraction to complete the transformation. These mechanisms have been described and commented upon by Mehl, Barrett, and Smith,8 Mehl and Derge,4 Wassermann,2 and others, and generally accepted by investigators in this field. Greninger and Troiano9 have recently published the results of a detailed study of the shapes and orientation habits of martensite crystals in plain-carbon and nickel steels. They found that, contrary to previous assumptions, martensite plates form not along the octahedral planes but along austenite planes of very high indices; these results were in line with those of previous studies of martensite reactions in nonferrous alloy systems by Greninger and coworkers.6,10 Greninger and Troiano concluded that the transformation theories of Kurdjumow and Sachsl and of Nishiyama3 are untenable. Phragmén11 reached a similar conclusion. EXPERlMENTAL METHODS The object of this particular study was the evaluation of (1) lattice relationship between austenite and martensite, and (2) relationship between the martensite lattice and the martensite plate. The technique used for solving these problems was similar to that used by Greninger6 on martensitic structures in 8 copper-aluminum alloys. Briefly, the method consists of grinding and polishing a specimen on a surface parallel to an individual martensite plate and thus exposing a single martensite crystal for an area of l to 3 mm. The orientation of this exposed martensite crystal is then determined by means of a back-reflection Laue X ray pattern.12 Another pattern is obtained from the matrix crystal, and a stereo-graphic plot of data from these two patterns then provides the solution to the problem. It is necessary to repeat this process on several crystals in order to determine whether or not the solution is unique.

Jan 1, 1950

By J. O. Edstrom, G. Bitsianes

Parabolic rate constants were determined for the formation of wiistite by the solid state reaction between magnetite and iron. The reaction was diffusion controlled and inert marker studies indicated that the mass transport through the wiistite layer was accomplished by means of iron migration. Relationships between rate constants and self-diffusivities are discussed. The transport capacity for iron through dense wustite layers was found to be sufficient to carry on reduction, even in gaseous reduction processes. REDUCTION of iron oxides has been the subject of many investigations. Most of the work, however, has been done on rather crude material and there have been difficulties in correlating the data on a quantitative basis. The reverse process of the oxidation of iron has been studied more thoroughly and usually by starting from the pure metal. As a result, the mechanisms of oxidation are now fairly well known.It has generally been found that the oxidation of metals follows the so-called parabolic 1aw;Q hat is, when the oxides are formed as dense layers, their thicknesses are proportional to the square root of the reaction time. This parabolic law follows directly from Fick&apos;s first law of diffusion The flux, J, is defined as the quantity of diffusing substance passing per unit time through unit area of a plane at right angles to the direction of diffusion. This flux is proportional to the concentration gradient of the diffusing substance, and the factor D, known as the diffusion coefficient, is introduced as the proportionality factor with dimensions of (length)&apos;/time. If the flux is measured as the increase of thickness of the oxide layer (Ax) per unit time (t) and the assumption is made that the concentrations of the reactants at the phase boundaries of the layer are independent of time, Eq. 1 reduces to Integration of this expression yields the parabolic function ax = k . t. [31 The product of the diffusion coefficient and the concentration difference across the oxide layer is included in the constant k. When iron is exposed to a highly oxidizing atmosphere, the oxide phases are formed normally in a topochemical fashion, i.e., the interfaces between the phases maintain parallel positions to the original surface of the specimen. Above 570°C, the phases are orientated usually in the order of iron, wiistite, magnetite, and hematite, a condition in conformance with the requirements of the Fe-0 system. Below 570°C, the wiistite phase is unstable and has not been found as a normal constituent in the oxidation products of iron. There is a strong probability that continuous layers of the solid oxides are formed as the specific volumes of the phases increase in direct order from iron to hematite.&apos; , &apos; Regarding mass transport through dense solid oxide layers, Wagner&apos; has postulated that diffusion in oxides generally may be interpreted as migration processes of ions and electrons. There must be normally a concentration gradient across the growing oxide layer for diffusion to occur. This condition requires that there be deviations from the ideal stoi-chiometric composition of the oxide and accordingly deviations from the strict order of an ideal lattice. Such "lattice defects" include interstitial ions, cation and anion vacancies, quasi-free electrons, and electron holes and are decisive for all migration processes.&apos; Cations, anions, and electrons all may have some mobility in the oxides but the movement of one of the particles generally far exceeds that of the others. Previous work&apos;, 1,2,7 has shown that during the oxidation of iron the migration through the wiistite layer, and probably also the magnetite layer, is confined to the movement of iron ions. Migration through hematite, however, has been found to take place by oxide ion movement. These behaviors are in direct agreement with the type of vacancies present in the respective oxides. Reduction of Iron Oxides The gaseous reduction of iron oxides, like the oxidation of iron, takes place in a topochemical fashion at distinct interfaces between the appearing phases."-&apos;" Porosities might be expected in these reaction products, since their specific volumes are less than that of the starting material. Frank and van Der Merwe" have shown, however, that it is theoretically possible for nonporous layers to form if the degree of misfit in specific volume is less than about 15 pct. These aspects on porosity formation

Jan 1, 1956

By D. R. Wieland, A. N. Barron, A. R. Hendrickson

A definite relationship has been found between the reactivity of flowing hydrochloric acid and its shear rate in a carbonate fracture. Both flow velocity and fracture width affect the acid reaction rate. Laboratory studies were conducted on acid reactivity at different flow velocities through horizontal-linear fractures, using 15 per cent hydrochloric acid at 80&apos; F and approximately 1,100 psi. Fracture width varied from 0.02 to 0.20 in. These data provide a new basis from which the spending time and penetration of the acid can be estimated. Equations were derived expressing the relationship between injection rate, fracture width, acid concentration, time and fracture height, for linear and radial fracture systems. Because the penetration of the acid before spending is closely related to the extent of productivity increase resulting from an acidizing treatment, these data provide a valuable insight into some of the controlling factors that must be taken into consideration during treatment preplanning. INTRODUCTION Acidizing of carbonate reservoirs to improve production characteristics has been widely practiced since 1932. Originally, it was assumed that the acid uniformly penetrated natural formation pores and flow channels, enlarging them and thereby increasing their flow capacity. Little consideration was given to the reaction rate of the acid, or how far it would penetrate away from the wellbore into the formation, before spending. It has been shown recently&apos; that, unless fractures are present in the rock, very little penetration is attained before spending, and the benefits of the acidizing treatment are largely confined to the immediate vicinity of the well-bore. Therefore, acid treatments may be classified into two categories: (1) matrix acidizing, in which the acid flows through multiple: formation pores; and (2) fracture acidizing, in which the bulk of the acid travels through fractures in the rock, whether natural or induced. When acidizing treatments are conducted at pressures of sufficient magnitude to open and extend such fractures, it is often desirable to inject a propping agent to hold the fracture open after the treating pressure has been released, thus providing a highly conductive flow channel through the rock. In some cases where acid attack produces surface irregularities, the resulting flow passages can be sufficient to provide high conductivity without use of a propping agent. During injection, the acid dissolves the carbonate rock with which it comes in contact until it is spent. Deeper penetration of the spent acid into the formation produces no appreciable benefit (if no propping agent is used) because the unetched fracture faces will rejoin when treating pressures are released and the fracture will "heal", with negligible resultant conductivity. The spending time of the acid thus becomes important in determining how far from the wellbore the improved-conductivity zone extends. The spending time of acid after injection into carbonate rock depends on the rate at which the acid reacts with the rock. This in turn is controlled by a number of factors, as previously reported. 2-4 These include temperature, pressure, acid concentration, rock composition, injection rate and the area-volume relationship between the acid solution volume and the surface area of the formation flow channels through which it penetrates. Thus, in matrix acidizing, where an extremely large area is exposed to the acid, spending is rapid. In contrast, spending time is prolonged in open fractures, where the area-volume ratio is much lower. Thus, greatest penetration of the acid before spending will be achieved in acid-fracturing treatments where fractures are held open by hydraulic pressure. Perkins and Kern5 have presented equations for fracture-width determinations which, for hard formations such as limestone or dolomite, indicate that high injection rates and viscous fluids are required to create wide fractures. Increasing the injection rate will, in itself, produce faster reaction rates. Because this type of reaction can be considered to be first-order diffusion-controlled, &apos;-&apos; the rate of movement of fluid past the rock surface affects the thickness of the diffusion layer, in turn affecting the reaction rate. Staudt, et al,10 report the results of tests in which a rotating marble cylinder was immersed in acid, and the weight loss at different speeds determined. Such test conditions, however, are not truly indicative of the situation in a formation during an acid-fracturing treatment. This paper reports reaction-rate data obtained under