Search Documents

By H. Margolin, E. Ence

Two versions of the Ti-Mn binary diagram have been published recently.' , -0th diagrams show two compounds in the region between 40 and 70 wt pct Mn, but disagree as to the reaction in which these compounds are involved. The investigation of the manganese-rich portion of the Ti-Mn binary diagram was undertaken at New York University as part of an investigation of ternary systems with titanium and manganese in order to determine which of the proposed diagrams is correct. A number of alloys between 31 and 70 pct Mn were prepared in a manner similar to that described by Cadoff and Nielsen; except that low currents (110 amp in argon atmosphere) and long melting times (up to 20 min) were used to prepare the alloys. Compositions were determined from weight-loss data, assuming all loss as due to manganese. Heat treatments were carried out with relatively large pieces, since there was a tendency for manganese to be lost during heat treatment. When X-ray diffraction data was to be obtained, the central parts of heat-treated specimens were used to make filings or powders which were not heat treated. Specimens were heat treated from the as-cast state. Heat-treatment times were as follows: 1150°C, 1 day; ll00°C, 2 days; 1000°C, 5 days; and 900°C, 15 days. It should be noted that equilibrium was not attained at 900°, 1000°, and in one case, at 1150°C. Metallographic specimens were electrolytically polished and strain etched by a technique described elsewhere.' At least four, and possibly six, phases were found in the region investigated. On the basis of information available at this time, a completely self-consistent diagram cannot be constructed, and therefore data are presented only for those phases which have been identified by both X-ray and microstruc-ture. Of the compounds detected, the one highest in manganese is the Laves phase, TiMn,, which is hexagonal with a MgZn, type of structure.V he diffraction data for TiMn2 from a 70 pct Mn alloy annealed at 1150°C are shown in Table I. The c/a ratio and parameters of TiMn2 agree well with those of Wall-baum hnd Rostoker et al. The values obtained here are c/a = 1.641, a = 4.825A. Another compound is the y-phase which is estimated to contain about 60 pct Mn. The y-phase has a structure which is identical to that of TiMn, with c/a = 1.639, a = 4.906Å. The fact that y has a Laves-type lattice would suggest that TiMn, has a range of solubility which extends from the composition of TiMn2 (69.6 Mn) to that of y (60 pct Mn). However, this could not account for microstructures which, in the 60 to 70 pct Mn region, show several phases in both the as-cast state and after annealing at 1150°C. Fig. 1 shows a two-phase structure of a 60 pct Mn alloy annealed at 1150°C. The phases present are y (white) and e (dark). If y were TiMn, then, according to Rostoker et al.,' the second phase of Fig. 1 should be P-Ti. The diffraction data for the 60 pct Mn alloy of Fig. 1 are shown in Table I. The starred d-values are from the e-phase and these lines do not correspond to those of &Ti. Comparison of as-cast and 1150°C microstructures of the 60 pct Mn alloy indicates that e precipitated from y. Since y has a

Jan 1, 1955

By Philip D. Anderson, Ralph Hultgren

Heat contents of extremely pure iron were measured over the range 300"to 1433"K, using a diphenyl ether calorimeter. Results from three samples containing widely differing impurities agreed with one another and with Previously reported results at higher temperatures (1184 ° to 1809°K) by Olette and Ferrier. From these data a table of heat contents of iron has been Prepared which is believed to be more accurate than those previously available. CP values have been derived which are consistent with these heat contents, with the best experimental Cp data, and with the thermodynamic conditions of equilibrium between bcc and fcc iron. The opinion is expressed that low-temperature extrapolations of presently known Cp values for y-Fe are not reliable. It would seem that the thermodynamic properties of iron, which is by far our most important metal, should have been well established long ago. This is not the case, however. As discussed by Olette and Ferrier,' there is objection to every earlier heat content measurement. While the best true Cp determinations agree well at temperatures below the Curie point, there is wide divergence at higher temperatures. Several investigators have examined available data and attempted to calculate thermodynamic functions for iron that are consistent with the two equilibrium temperatures of bcc and fcc iron. The two primary efforts were those of Austin' in 1930 and Darken and smith3 in 1948. The recommended values differ considerably; integration of Austin's Cp values leads to a heat content at 1100°K which is 300 cal per g-atom higher than the value recommended by Darken and Smith. The compilation of Fisher4 in 1949 was based on the selection of Austin. In 1956, Weiss and Tauer obtained yet another set of values by resolving Cp values into components due to dilation, lattice vibration, electronic excitation, and magnetism. The magnitude of contribution by each component and its dependence on temperature was estimated by semiempirical means. Their values are not self-consistent in that they do not form smooth curves when plotted vs temperature; moreover, their calculations cannot easily be repeated since they do not give the values of some of the parameters used. Clearly, experimental values for iron were in a most unsatisfactory state. The presently described measurements of the heat content of iron were therefore undertaken, covering temperatures as high as 1433°K. While the work was in progress, the high-temperature (1193" to 1789"K) heat content measurements of Olette and Ferrier' were published; in the region of temperature overlap the present results agree with Olette and Ferrier well within experimental accuracy. It is believed that the present results, combined with those of Olette and Ferrier, provide for the first time a reliable set of heat contents of iron from room temperature to the melting point. From these data, guided by available Cp measurements, it proved possible to derive Cp, entropy, and free energy function values for @-iron from room temperature to the melting point, and for y- iron in the temperature region of its stability. Exhaustive study led to the conclusion that extrapolations of y-iron functions to room temperature were not reliable enough to be useful; hence these have been omitted from the tables. EXPERIMENTAL Materials. Three samples of extremely high purity iron from different sources, containing widely different impurities, were measured. The first of these, designated "Chipman", was kindly supplied by Dr. K. K. Kelley of the U. S. Bureau of Mines from a lot which was made many years ago by Dr. John Chipman of the Massachusetts Institute of Technology. The second, designated6'Teddington", was supplied by the National Physical Laboratory, Teddington, England, from a lot zone-refined by them. The third sample, designated "Irsid", was supplied by the Institute de Recherches de la

Jan 1, 1962

By L. S. Reid, Irwin Politziner F. M. Townsend

Recently published data indicate that the water vapor content of a gas, as determined by dew point measurement, is inaccurate when the gas has been dehydrated with diethylene glycol. Water vapor contents and dew point measurements of gases dehydrated with triethylene glycol have been obtained in this investigation in order to determine the magnitude of a similar error, if one exists. Experimental data show a very low concentration of triethylene glycol vapor in gases dehydrated at atmospheric ternperatures and pressures ranging from 500 to 2,500 psia and that the accuracy of dew point measurements is not impaired by the presence of triethylene glycol vapor. INTRODUCTION Nearly all natural gas transported by pipe line to northern and eastern markets must be dehydrated to a low residual moisture content in order to assure maximum transmission efficiency and continuous delivery under peak load conditions. Without dehydration, water vapor often condenses in pipe lines in quantities sufficient to restrict the flow3 and. under low atmospheric temperature conditions, gas hydrates may form and plug gathering. transmission and distribution facilities. Gas may be dehydrated to pipe line specifications by a number of methods. The most widely used methods are (1) adsorption of water vapor on a solid dessicant such as activated bauxite, alumina or silica gel,' (2) by absorption of water vapor by either diethylene or triethylene glycol-water solutions of high glycol concentration,11,13 and (3) by simultaneous expansion-refrigeration of very high pressure gas in which gas hydrates are purposely formed and then quickly decomposed.'"" Of these three fundamental methods, the adsorption and absorption processes provide the bulk of the dehydrated gas moving to market at the present time. The expansion-refrigeration process. a relatively new development, is gaining in favor because of its simplicity but is sharply limited in its application by available differentials between source and gathering system pressures. Where gas sale or purchase contracts contain a maximum water vapor content specification, the water vapor content is usually determined by measuring the dew point of the gas at system pressure. Knowing he dew point temperature and the system pressure, the water vapor content of the gas is determined from a graphical correlation of saturation, or dew point, temperature us the water vapor content of the gas which is customarily expressed as pounds of water vapor per million cubic feet of gas measured at 14.7 psia and 60°F. Dew points are usually measured with the U. S. Bureau of Mines Dew Point Tester. shown in Fig. 1, which is well suited for use at temperatures lower than 120°F and at pressurei; ranging from atmospheric to 3,000 psi. A number of correlations of dew point temperatures vs water vapor content are available,3,5,15 the most recent of which is that by McCarthy et al.4 Where natural gas is dehydrated by absorhing contact with concentrated diethylene glycol-water solutions. considerable difficulty is experienced in observing water dew points due to condensation of liquid hydrocarbon and glycol films on the mirrored surface of the dew point tester. Riesenfeld and Frazierl2 report that the dew point method for determining the water vapor content of a dietllylene glycol-treated natural gas is in error due to the glycol content of the condensate formed on the tester mirror, and that the water vapor content of the gas tested is actually lower than that indicated by the standard' dew point-water vapor content correlation. Extensive experience in testing gases dehydrated by concentrated triethylene glycol-water solutions lias not revesled difficulties of the nature cited above for diethylene glycol. Water dew points are clear and sharp and condensation of

Jan 1, 1951

By Peter A. Allen

INTRODUCTION Lac Minerals Ltd., a significant North American producer of gold and other metals for over three decades, recently completed the financing for its third discovery in an eight year period. From 1975 to 1982, three important gold deposits in Quebec and Ontario: namely Bousquet, Doyon and Hemlo, were located and tested by company geologists. When current development plans are complete, Lac will have injected $400 million into these deposits. A discussion of these projects and their financing reveals some extraordinary challenges faced by top mining management. Responses to these challenges developed by Lac management may interest executives planning to proceed with new North American gold or base metal mines. MINE DE BOUSQUET In 1976, we explored a property containing a large low grade surface gold deposit. The geologial setting was exciting and we tested recent rethinking about the volcanigenic genesis of gold and base metal occurrences. These ideas helped pus to persist in drilling a nearby conductor and 600,000 ton, 0.22 ounce/ton orebody was outlined. With gold at $Cdn.150 per ounce the feasibility was approved and work started February 1978. Availability of a company custom mill 35 miles away reduced our immediate capital needs to $8.5 million. First of all, understanding the geological significance of results at Bousquet was critical. Mine and surface exploration geologists at Lac are continually and closely working together to better understand the nature of gold deposits in the Shield. This management emphasis on both pure and mine geology meant that a much larger ore reserve could confidently be predicted. (A proposal to quickly develop and ship the ore to a nearby company mine was discarded.) Instead of designing just for the initial plan of 500 tons per day we therefore included headframe, shaft and hoisting capacity for 1,700 tons and provided a compartment for future shaft deepening. These prebuilt additions were welcomed within two years. The type of collaboration whereby surface and mine geologists make study and field projects of each other's problems sets the foundation for this predictive ability. At Lac, the traditional responsibility for and supervision of the mine geologist by the mine manager is modified by this collaboration. This adds interest and scope to the geologist's work and lets him think beyond production requirements. Besides such management considerations, dedicated, professional geologists with integrity and lots of practical experience are needed to plan successful developments like Bousquet. Second, projecting future bullion revenue was critical and our experience selling production for future delivery gave us a way to ensure that loan repayment at term would not be jeopardized by falling metal prices. Output from a single mine is often reduced or curtailed for numerous reasons, so "selling forward" is done best and with least risk by companies like Lac with more than one or two producing locations for that metal. At first, a forward marketing program was considered unwise, speculative and unorthodox by analysts and other producers. Declining markets in the early 1980s prolonged gold project capital recoveries however, and critics were better able to appreciate the usefulness of such a tool. The notion that gold miners shouldn't sell forward is rooted in the belief that long-run gold prices will rise as modern social theory implementation in democracies inevitably erodes currency values. Selling against this trend goes against this industry belief or "ethic" and is at odds with the company shareholder who expects the gold price to rise not fall. Nonetheless, an efficient tool is available to the gold producer (not to most other metal producers) to quickly disengage from adverse price trends or to lock in spot prices instantaneously for two years or more of profits. Gold had recently retreated from U.S.$200 to $104 and now had reversed to $150. Lac had been forced to close several of its producers during the late 1960s because central bank-controlled

Jan 1, 1985

By Gordon W. Hodgson, Edward Tipman

INT'RODUCTION An appreciable number of the oil fields in Western Canada are accumulations of heavy black oils in more or less unconsolidated sandstones. When the crude oils are produced by conventional means, they are frequently contaminated with both sand and oilfield water. The water is usually present as emulsified water, and the sand and other solid materials are suspended in the emulsions. The presence of the solid material in the crude oils is troublesome and, in general, little is known about the behavior of suspended solid particles in emulsions. The Stokes equation describes the behavior of suspended particles in homogeneous fluids in terms of particle size, density differential, and fluid viscosity. In the case of an emulsion, particle size and density differential introduce no difficulties, but considerable doubt centers around the viscosity term. It has been reported1 that the viscosity of an emulsion is related to the viscosity of the continuous phase by an expression of the type: n = a, (1 + a C) where n is the viscosity of the emulsion, n,, is the viscosity of the continuous phase, a is a constant, C' is the volume concentration of the disperse phase. The value of 17, the coefficient of the concentration term, has been determined for various systems, and has been found to vary from a value of 1 to 4.75. The value of 2.5 has been found to be applicable to a large number of systems, and this is the value that is widely used in the equation which then becomes the Einstein equation for the viscosity of emuls~ons. It is of considerable significance that neither the particle size nor the viscosity of the disperse phase enters the expression; the expression for the viscosity of the enlulsion is based solely upon the viscosity of the continuous phase and the concentration of the disperse phase. For crude oil emulsions the Simha equation and the data presented by Fukushima and lchimurai show a non-linear dependence of the viscosity ratio on the water concentration. While it is undoubtedly reasonable to use these data for predicting the viscosity of a specific emulsion, and while it is equally reasonable to expect the calculated viscosity to predict the settling rate of a solid spherical particle in the emulsion by means of Stokes equation, there seems to be no direct evidence that this calculation is indeed sound for describing the settling rates of solid particles in emulsions of water in crude oils. PROCEDURE A direct approach to the problem was thus indicated. Laboratory equipment was designed and built for the direct determination of the rate-of-fall characteristics of solid particles in emulsions of water in oil. Although the apparatus incorporated the basic design of conventional falling-ball viscometers, the study was concerned directly with the rate-of-fall characteristics of particles in emulsions, rather than with the viscosity of the emulsions as such. The crude oil used in this study was a very heavy black crude oil—the McMurray oil obtained from oil-soaked sands outcropping on the Athabasca River in northeastern Alberta. It was produced from the sands by strip mining followed by hot-water separation of the oil in the separation plant of the Alberta Government at Bitumount'. The primary plant product was a wet crude oil containing about 5 per cent solids and 35 per cent water. The final plant product was only slightly different from the native oil, having lost only about 4 per cent of its bulk as light ends during dehydration distillations. In the present investigation two kerosene dilutions of the McMurray oil were used in addition to the dry plant product. The McMurray oil contained 1.92 per cent solids. Analysis of the solids by X-ray diffraction showed the presence of kaolinite, pyrite, and illite as major constituents. with lesser amounts of quartz. Particle size of the pyrite and quartz was less than 10

Jan 1, 1957

By R. F. Mitchell, G. F. Dillon, A. F. Armington

In this paper the present methods of boron preparation are discussed with emphasis on the iodide intermediate. Several methods of boron triiodide preparation were investigated, the most satisfactory method being the preparation from the elements. A yield of 60 pct based on iodine is found for this method. Zone-refining, sublinzation, distillation, and fractional-recrystallization results are given for the boron triiodide, with distillation producing the best results. Several methods of decomposition are also discussed. The purity of the resulting iodide boron approximates the puritjl of the best available bromide boron, ELEMENTAL boron has been suggested as a possible high-temperature semiconductor by several workers,' but has never been exploited as a device material. The principal difficulty with boron is the unavailability of pure crystalline material from which accurate information on electrical properties could be obtained. Most boron crystals presently produced are very imperfect in structure and of questionable purity, particularly in relation to carbon content. Several methods of boron purification have been reported in the past few years, all of which produce material with a purity better than 99.0 pct. Most of these methods have been the subject of a recent review by Starks' and will not be elaborated upon in this report. However, of all the purification methods reported, only those using halide intermediates produce a purity approaching that usually required for electronic applications. The bromide intermediate has been most used for the preparation of high-purity boron.'y3 This material is easily prepared from the elements and can be effectively purified by distillation and decomposed by hydrogen reduction. The resulting product contains a trace of silicon, and an uncertain amount of carbon, believed to be approximately 100 ppm. It has been recently reported by Russian workers that high-purity boron can be produced using an iodide intermediate.' In the work cited, boron is reported free of spectro-scopically determined impurities, but the reported detection limits are quite high (- 100 ppm). In addition, no data is given on the carbon content of the product. In the present paper, boron triiodide was chosen as the intermediate for several reasons. First, carbon tetraiodide, which could be a major impurity, is reported to be unstable above 200" and hence could be easily separated from the boron triiodide by its decomposition, since temperatures greater than this are attained during the purification process. The low melting point (45°C) and boiling point (20B°C) and the relatively high vapor pressure of boron triiodide should allow the application of any physical purification technique to the material. The possibility of a lower decomposition temperature than that used for the bromide process is another advantage which might cut down extraneous contamination. The iodide, however, does have certain disadvantages when compared with the bromide, the production cost being the most significant. This is the result of a higher halide-to-boron weight ratio, which means more intermediate must be employed. The cost of the starting material is also greater for the iodide. This cost could be considerably reduced however, by recycling the iodine byproduct. Epitaxial growth of boron, which is probably the best method of producing junctions, should be possible with either the bromide or the iodide as the intermediate. However, this has been attempted only on a limited scale up to the present time because of the unavailability of good crystals. The authors have been relatively successful in laying down a heterotaxy of boron on silicon, however. This will be reported at a later date. Several crystalline modifications have been reported for boron, four of which are now believed to be real.' These are the a! and 0 rhombohedral and the a, and 0 tetragonal. In general, the a! rhombohedral is the low-temperature form and the B rhombohedral is the high-temperature form. The tetragonal structures are detected between 1000"

Jan 1, 1964

By U. N. Bhrany, N. Arbiter

F. C. Bond (Consulting Engineer, Processing Machin-Dept., AllisChalmers Manufacturing Co., Milwaukee) This is a very comprehensive paper. It deals with 1) size distribution functions, 2) energy-particle size relationships, and 3) criteria for grinding efficiency. The method of analysis used consists of tracing the increase and decrease of successive Tyler scale screen fractions as grinding progresses. The treatment is based upon the assumption that the work done in grinding is concentrated entirely upon the coarse size fractions in the mill. It is postulated that when a feed consisting entirely of particles of one size fraction is batch ground that finer fractions increase at a constant rate as grinding progresses, until finally each in turn begins to be ground and to decrease in amount. It is shown that under these conditions the empirical Gates-Gaudin-Schuhmann log-log size distribution plot can be logically explained. It is difficult to imagine any condition of ball mill operation, or any probability analysis, which would result in no grinding contacts on the finer particles present. However, the authors' postulate must be accepted if their conclusions are to be sustained. They conclude that the equation expressing the for mation rate of each size fraction can be resolved into the G.-G.-S. size distribution equation, and that the curvilinear portion of the log-logsize distribution line represents the only particle sizes which are being ground as well as produced. The author's statement that the G.-G.-S. Eq. 4 applies only to the finer portion of the size distribution while the Rosin-Rammler Eq. 6 applies over the whole size distribution range certainly supports the view that an exponential equation of the Rosin-Rammler type corresponds more closely to actual size distribution than does the power law G.-G.-S. equation. However, the G.-G.-S. equation is used to derive Eq. 8 and Eq. 9, which state that the energy required to grind a ton through a particular mesh varies inversely as the particle size to the exponent -a , whic h is the slope of the extended G.-G.-S straight line. This is stated to apply to both batch and continuous grinding. The G.-G.-S. slope exponent thus becomes very important in all crushing and grinding analyses by this method. The authors include some data which can be used to test their conclusions, as described below: We will consider grinding a feed composed of 14 mesh (1190u) to -200 mesh (74u). The average of 17 Allis-Chalmers grindability tests on quartz gives a work index (Wi) of 12.77. The -200 mesh product should have 80 pct passing 41.6u or P = 41.6. The equivalent 80 pct passing size of the 14 mesh feed particles is considered to be the particle diameter, as is true for spherical particles. Thus F is 1190u. In the work index equation 10 wi 10 wi 127.7 127.7 P f 41.6 1190 = 16.1 kw-hrperton. In Table I the ball mill exponent for quartz is 1.0 and from Eqs. 9 and 10: w=kw-hr/ton =Constan/(do/di) = 16.1 ton so that (1190) Constant/ Constant and the Constant equals 259. The tons per horsepower-hour value is 0.0464, in agreement with Table IV. The exponents for other minerals are listed in Tabl e 11. In Table IIA, the kilowatt hours per ton required to grind these minerals between the same sizes as the quartz, both by the authors' method and the work index equation, are listed. According to the authors kw-hrperton = 259/(16.1)".

Jan 1, 1961

By W. R. Hibbard

It has been proposed1 on the basis of slip and flow that the ideal deformation texture of drawn wire for face-centered cubic metals is a (111) direction parallel to the wire axis. Under these considerations, an intermediate [loo] texture is permissible but should eventually change to the stable [Ill] orientation. This theory does not explain why copper and its alloys containing up to about 30 pct nickel, 5 pct zinc and 1 pct aluminum were found to have a double [Ill], [100] texture, while alloys with at least 8 pct zinc and 2 pct aluminum developed essentially a single [Ill] texture.1,2 It does suggest, however, that the [loo] component of the former alloys should disappear with additional deformation.3 Some evidence exists to support this suggestion. Howald4 reported that annealed copper wire previously drawn 93.8 pct and 98.5 pct developed a single [Ill] texture. Since, in wire, the drawn and annealed textures are similar, these wires probably had a single [Ill] deformation texture before annealing. In addition, although cold rolled polycrystalline copper and 80-20 brass were found to form different types of pole figures,5,6 single crystals of these metals when rolled from the stable (110) [112] orientation were found to produce essentially the same polo figure.7.8 It may be, therefore, that while the addition of solute elements changes the path by which the final texture is obtained, the final texture is not changed. Experimental Results The wires remaining from the previous investigation1 already drawn about 50 pct reduction in diameter were further drawn to 86 pct and then to 96.4 pct total reduction in diameter. The textures were determined after these stages by transmission X ray photograms taken with a copper K-alpha beam rotated 0 degrees toward the wire axis. It was found that the ratio of the [111].] and [100] intensities of the double texture in copper and its alloys containing 0.94 pct aluminum, 30.70 pct nickel, 2.61 pct zinc and 4.99 pct zinc increased from about 3:l for the 50 pct reduction to about 9:l for the 86 pct reduction. After 96.4 pct reduction, these wires exhibited essentially a single [lll] texture. Summary Thus, the drawn wire deformation texture of copper and its alpha solid solution alloys containing aluminum, nickel or zinc is essentially a single [Ill] texture as predicted by theoretical considerations of slip and flow.' For copper and its alloys containing up to about 1 pct aluminum, 5 pct zinc and at least 30 pct nickel, an intermediate [loo] component is found after about 50 pct reduction in diameter, but disappears after about 95 pct reduction in diameter. For alpha solid solution alloys containing at least about 2 pct aluminum and 8 pct zinc the single [Ill] texture is developed considerably more easily and is found after about 50 pct reduction in diameter. No explanation of this compositional effect is apparent. Similar work is contemplated for cold rolled and cold compressed alloys. References 1. w. R. Hibbard, Jr. and M. K. Yen: Trans. AIME 175, 126. Metals Tech., Feb. 1948, TP 2334. 2. W. R. Hibbard, Jr. and D. E. Trout, 11: Trans. AIME 185, 620. Jnl. of Melals, Sept. 1949, TN 18. 3. W. R. Hibbard. Jr.: Disc. of R. M. Brick's paper on Deformation Textures, ASM Symp. on Cold Working of Metals, Oct. 1948. 4. T. S. Howald: Disc. of Ref. 1. Trans. AIME, 175, 126. Melals Tech. Aug. 1948, TP 2449. 5. R. M. Brick, D. L. Martin and R. P. Angier: Trans. ASM (1943) 31, 675. 6. 0. Dahl and F. Pawlek: Zlsch. Melall. (1936) 28, 266. 7. C. S. Barrett and F. W. Steadman: Trans. AIME (1942) 147, 57. 8. J. E. Burke and C. S. Barrett: Trans. AIME 175, 106. Melals Tech., Feb. 1948. TP 2327.

Jan 1, 1950

By Adam L. Wesner, A. C. Richardson

This paper describes the development of a continuous float-and-sink process to produce coal low enough in ash content to be suitable for production of electrodes. The cleaned coal had a combined iron and silicon content of 0.239 pct. The efficiency of recovery was 84 pct. DURING World War I1 the demand for electrode carbon was greater than could be met by the supply of petroleum coke available for this use. It was believed that coke made from an extremely low-ash coal might be a suitable substitute for petroleum coke. Requirements for electrode carbon to be used for the production of aluminum are that the silicon plus iron content shall be not more than 0.14 pct of the coke. However, during the period when petroleum coke was in short supply, it appeared that relaxations of the specifications might be allowed to permit 0.4 pct iron plus silicon in the coke. For this work, the specifications were that the coal should contain less than 1 pct of ash, and the combined iron and silicon content of the coal should not exceed 0.28 pct. Heavy-liquid separations made on a number of coals showed that if certain size fractions of some coals Were separated at low specific gravities the resulting float products would meet the required specifications. The objective of this work was to develop a continuous, commercially feasible process for producing low-ash coal. After consideration of various processes, the method chosen was a float-and-sink separation using a solution of calcium chloride as the separating medium. Eagle Seam coal was used for the experiments. The —10 +35 mesh fraction was found to be the most promising feed for producing the low-ash content coal. A batch of 30 tons of — --in. coal was screened at 10 and 35 mesh; the yield of —10 +35 mesh was 20 pct of the feed. This fraction comprised the feed for the separation tests. In spite of the fact that this portion was screened a second time at 35 mesh, the coal still contained 16 pct that was finer than 35 mesh. Three-fourths of the undersize was in the —35 +48 mesh range. A representative portion of the —10 +35 mesh fraction was subjected to batch float-and-sink separations to determine the best gravity to be used in the continuous tests to obtain a high recovery of low-ash content coal. The heavy liquid used was a mixture of carbon tetrachloride and benzene which assured complete wetting of all of the particles. As usual in batch separations, adequate time was allowed for each separation so that even the near gravity particles had ample time to separate. The separations were made at increments of 0.01 sp gr from 1.25 to 1.28 and also at 1.32 and 1.59. Each specific-gravity increment was assayed for ash content. From these data it was concluded that 1.27 sp gr was best for the continuous separation of the coal. The products from the batch separation were composited into float 1.27 and sink 1.27 sp-gr fractions; these were assayed for ash, iron, and silicon. Table I shows the results of the batch separations. The composite float 1.27 fraction contained 66.04 pct of the total weight, and had an analysis of 0.79 pct ash, 0.073 pct iron, and 0.112 pct silicon, or 0.185 pct iron and silicon combined. These data are indicative of the results possible if a perfect separation is made at 1.27 sp gr under static conditions. Inasmuch as the method under investigation is a dynamic system these results could not be obtained. It remained to be determined, however, just how close to the theoretical results the actual continuous separation would be.

Jan 1, 1953

By Denton R. Wieland, Harvey T. Kennedy

The frequency of bubble formation is measured for oils from the East Texas field and the Slaughter field in cores from these fields. East Texas oil was also tested in a Slaughter core. The data checked previous results in that a definite supersatrtration may exist without the formation of bubb1es in periods of observation totaling 158 hours. Measured frequencies varied from zero at supersaturations below 14 psi to 3.1 bubbles/sec/ cu ft of rock at 40 psi supersaturation INTRODUCTION The formation of bubbles is essential in a solution gas-drive reservoir in the displacement of oil. In formations where the basic pore structure consists of fine pores or fractures connected to larger pores or crevices, bubble formation in the fine pores may be the most effective means by which the oil may be displaced, even if secondary methods are applied. The most efficient oil displacement would occur where at least one bubble would form in every pore. As the pressure decreased, the bubbles would expand, due to the gas diffusing into the bubbles, and displace the oil toward the lower pressure area around the wellbore. Kennedy and Olson' have shown that the total number of bubbles formed in a reservoir is primarily dependent upon the rate of pressure drop, the rate of diffusion of gas through oil, and surface area of the rock. The surface tension of the liquid and other characteristics of the rock may also exert an important effect, which would give a different frequency to different rocks and oils and various combinations of different rocks and oils. The purpose of this paper is to present frequency measurements on two rocks and two oils. A hydrocarbon liquid is at equilibrium with gas when it contains the maximum volume of gas in solution that it can have at the prevailing temperature and pressure. If the temperature is maintained constant and the pressure is reduced below the equilibrium pressure, the liquid is supersaturated to the extent of the difference in the two pressures until the gas comes out of solution as a free phase. As shown by previous work, and confirmed in the present investigation, the number of bubbles formed per second increases with an increase in supersaturation. Kennedy and Olson showed that a tenfold increase in the rate of pressure decline resulted in a tenfold increase in the number of bubbles formed per cubic foot of reservoir rock, e.g., for decline rates of 0.1, 1, and 10 psi/day, the number of bubbles formed per cubic foot would be 40, 400, and 4,000, respectively. For another hypothetical system, Stewart, Hunt, and Berry' estimated that for pressure declines of 0.1, 1, and 10 psi/day, the number of bubbles formed would be approximately 10, 100, and 1,000 cu ft of reservoir rock. Their value of bubbles formed is lower than given by Kennedy and Olson; however, the order of magnitude agreed satisfactorily. The rate of diffusion will also affect the number of bubbles formed. If the diffusion coefficient is high, the gas in solution in the oil surrounding a single bubble will tend to diffuse into the bubble rather than forming other bubbles. On the other hand, the formation of more bubbles will tend to occur if the diffusion coefficient is very low. In his thesis dated Aug., 1953, Wood" reports on the frequency of bubble formation in a system consisting of oil and rock from the Rangely field. In the present work, the apparatus of Wood was redesigned to allow greater precision, especially at low supersaturations, where bubble growth is slower, and detection is more difficult.

Jan 1, 1958

By Russell G. Haworth

Three companies, United States Potash Company, Potash Company of America, and International Minerals and Chemical Corporation, are now operating potash mines and reGneries in the Carlsbad, New Mexico, area. The three mines are located approximately twenty miles east of Car1sbad. The deposits have been found ideal for mechanized mining methods. This summary has been compiled from information made available by the three operating companies. Prospecting Since outcrops of potash are nonexistent, prospecting is accomplished by drilling and coring of the salt section to establish the grade, thickness, and outline of the potash beds contained in the salt deposits. Information regarding the nature of the formations in the cover of 400 to 600 ft thick over the salt and potash beds is also obtained from drill cuttings in the same operation. By proper interpretation of assembled data the best location for shafts may be determined. The overburden varies in character but consists in general of interbedded shales, sand, gravels, limestones, and anhydrite beds. Water, in unpleasant quantities, especially in the sands and limestones, often completes the geologic section. Some of the shaftas in the area have been sunk without undue difficulties, others have been delayed by flows of water. Most of the shafts are concreted from the surface to the salt section. Each of the three mines in the Carlsbad area has one shaft for hoisting ore and one for hoisting men and supplies. Mining Methods Information acquired from initial drilling and prospecting affected the choice of mining methods. Since the tabular, slightly rolling deposits were similar to coal seams, the room-and-pillar system used in coal mining was adopted by all the companies. Pillars have not been removed in any of the mines on a large scale. One company has conducted experimental robbing of pillars in one restricted area. Where it is known that overlying strata contain water in large amounts, it is not considered practical to risk flooding of the mines by removing pillars without fill. Some thought is now being directed toward development of economical methods of filling for pillar recovery. The problem is not identical at the three mines and local conditions will govern the methods employed for eventual pillar recovery. The important point is that, with large reserves, it has not been necessary to resort to mining of pillars for adequate production. The ore deposits are laterally extensive but are irregular in shape and lie at a depth of 700 to 1100 ft below the surface. The major operations of all mines are on the same bed strati-graphically, except for the langbeinite level at International Minerals and Chemical Corporation. The deposits are apparently not connected and in many parts of the deposits being mined, "salt horses" or barren zones occur. From 400 to 700 ft of salt with minor beds of polyhalite and anhydrite lie immediately above the ore horizon. The ore differs from the salt only in the potassium chloride content and color due to small amounts of iron associated with the sylvite, giving the ore a somewhat mottled red and white cast. Thickness of the ore varies from 5 to 14 ft. Rooms and break-throughs in the mines vary from 24 to 40 ft in width, the overlying salt forming an excellent roof and providing safe mining conditions. Almost no timber is used in any of the mines for roof support. Drilling is normally the first step in mining the face of a room. Electric motor driven auger drills are used in the area. Jack hammers were used to some extent when the mines were first opened but the ore is easily drilled if bits are sharp and the coal type

Jan 1, 1950

By F. W. Jessen, James N. Howell

INTRODUCTION The determination of cloud points has to date been limited to rather transparent oils, visual observation of the formation of a solid phase being the criterion for the standard ASTM D 97-47 method. The need for a quiclc and simple method for determining cloud points under dynamic conditions for opaque crude oils became necessary in a study of fundamental aspects of paraffin deposition from crude oils. PREVIOUS WORK The determination of cloud points in opaque oils by viscosity temperature curves is fairly new, Young' described a method employing the capillary tube principle. No information exists relative to the determination of cloud points of crude or refined oils under dynamic conditions. Shock' noticed that deposition of paraffin from crude oils took place at temperatures at or below the temperature at which a sharp inflection point occurred in the viscosity-temperature curve. This observation indicates a possible correlation between this temperature and the cloud point of the crude oil. Reistle and Vietti1 have reported that when crude oils containing small amounts of asphaltic materials were heated to temperatures sufficiently high to solubilize these materials and immediately cooled the pour point of the crude oil was lowered as much as 70°F. Sachanen\ asribes this effect to the action of colloidal asphaltenes in preventing the formation of the crystalline structure necessary to maintain the oil in a rigid state. At high temperatures, asphaltenes are peptized, and the paraffin crystals formed at these temperatures adsorb the colloidal asphaltenes on their surface thereby hindering further growth of the crystals. Reistle" found, however, that such heating and cooling of crude oils had no effect upon the cloud points. This latter work dealt with a crude oil of fixed composition, and the question immediately arises as to the effect of varying the concentration of asphaltic materials on the cloud point. APPARATUS AND PROCEDURE All viscosity measurements were made with a Bendix Ultra-Viscoson. The Bendix Ultra-Viscoson, which consists of a vibrating probe and an electronic computer. measures viscosity by exciting a thin alloy steel blade on the end of a probe by short electrical pulses in damped oscillation at 28 kilocycles. The blade vibrates longitudinally with an amplilude of less than 55 micron or 20 millionths of an inch. Energy to protlucc this excitation is generated in he computer and transferred to the probe through the connecting cable. The oscillating blade is magnetostric-tive, i.e., it is capable of transforming electrical energy to mechanical energy in the ultrasonic range. Ultrasonic waves are produced in the material surrounding the blade by the oscillating motion of the blade causing layers of the material to slip back and forth over one another at a known frequency. The electronic computer calculates the energy required to produce the sliding motion which is in turn proportional to the viscosity of the material. Actual values of viscosity times density (centi-poise X grams/cc) are indicated on the computer and a continuous D-C signal is provided which is fed into a type 153 Electronic Recorder (manufactured by Brown Instruments Div. of Minneapolis-Honeywell Regulator Co.) The liquid sample container was fabricated from a Lucite cylinder and jacketed by a Luicite water bath. Early experiments using glass and steel sample containers were not satisfactory. since the Ultra-Viscoson was apparently affected by the alterzltion of the magnetic fields surrounding the probe by stresses set LIP in the glass and steel as it cooled. The procedure for determining viscosity-temperature curves was relatively simple. The temperature ot the sample was raised sufficiently high to solubilize all paraffin and asphalts present. After heating, the oil sample was immediately transferred

Jan 1, 1957

By Reuel A. Cochrane, Harry H. Angst

The successful exploitation by opencut methods of the low-grade porphyry copper deposits is due to the economical handling of large tonnages. Large tonnages are possible only if the rock material is broken so that the large power shovels can operate with minimum delays. This is particularly true at the New Cornelia mine, where the dense, hard, tough rock material creates problems not encountered in most of the porphyry copper mines. The introduction of churn drills at the New Cornelia for primary drilling, in 1936, necessitated a complete change in the methods of breaking ground as formerly air drills had been used. The blasting operations are of particular interest because of the handling of great quantities of high explosives in safely and efficiently fragmenting the hard rock material. Rock Formations At the New Cornelia mine the rocks are quartz monzonite with a diorite border facies intruding a rhyolitic series. Overlying these formations is a fanglomerate formation composed of boulders of monzonite, diorite, rhyolite, and other types of rock of unknown derivation. (The word "fanglomerate" is used in this paper in referring to the local conglomerate type of rock formations.) The ore body is approximately 4800 ft. long and 2800 ft. wide, and is of the disseminated type. Mineralization occurs principally in the quartz monzonite and to some extent in the adjacent diorite and rhyolite. The principal ore minerals are chalcopyrite, bornite, and a small amount of chalcocite. Over a considerable area the quartz monzonite is extremely hard and siliceous in character, owing to pegmatitic zones of alteration. The hardness of the ground depends on the intensity of the silicification. In a small area in the pit, the monzonite contains an abundance of pyrite accompanied by sericitization and is soft and easily fragmented. This is true also in the remaining oxidized portion of the ore body. The diorite and rhyolite formations, like the monzonite, vary from extremely hard to very soft material, but on the whole are easier to fragment than the monzonite. Jointing is prevalent in all the rock formations and plays an important role in the blasting efficiencies. In the fanglomerate formation, numerous well-defined joints, widely spaced, tend to make the ground blocky when blasted. This is a deterrent to good fragmentation. In the other rocks the joints are more numerous and are closely spaced, except in localized areas where the formations are extremely hard. These descriptions indicate that the lowest blasting efficiency will be obtained in the harder formations, from which the major portion of the mine production is obtained; namely, the monzonite and rhyolite. All rock formations mined at the New Cornelia pit are so hard that excavation

Jan 1, 1943

By Earl W. Palmer, Cyril Stanley Smith

StKip of any of the metals used for deep drawing operations occasionally yields cups that are defective because of a rim that varies in height around the cup in a wave-like manner. Some such defects are traceable to tools or other press factors, but when the protuberances formed (usually four in number on brass and other copper alloys) are symmetrically disposed with respect to the rolling direction of the strip, they are invariably attributable to the metal. The effect is known as "earing" and the protuberances are called "ears." Other terms frequently heard are "tips," "scallops," and "corners." It is recognized that the effect is most commonly a result of a directional crystal structure produced by rolling and annealing operations in the manufacture of the metal strip. Numerous papers dealing with various aspects of the earing effect have appeared in the literature, those listed in the references1 being especially interesting and valuable. An investigation of the factors influencing earing of brass cups has been in progress in the laboratories of the American Brass Co. for several years, and it was thought desirable to make some of the results generally available in summarized form. The present paper discusses many factors that do and do not contribute to ear formation. In addition, a section is devoted to methods of minimizing the earing tendency of brass sheet by proper selection of the cold-rolling and annealing schedule by which it is produced. In the space available, it is impossible to quote detailed experimental procedures and numerical results. However, the authors make no statement that they do not believe to be properly substantiated, either by experimental evidence obtained under laboratory conditions or by experience in the actual production of deep-drawing brass in the brass mill. Mechanism of Ear Formation It must be clearly understood that the formation on cups of symmetrical ears, four or more in number, is attributable solely to the strip metal, and results from the strip having different deformation characteristics in different directions. The tools used in the drawing process, or the type and completeness of lubrication of the strip, have nothing to do with the problem of ears, although they do, of course, greatly affect the "drawing quality" of the strip and the general appearance of the cup. A single tip may be drawn up on the rim of a cup because of misalignment of the tools, or because the gauge of metal varies from side to side of the strip. The two-ear form that sometimes appears is also traceable to gauge variations. However, the four-ear and six-ear symmetrical forms that we are concerned with here are caused by factors inherent in the structure of the metal itself.

Jan 1, 1942

By Bernard Kopelman

The particle size of tungsten metal powder used to make tungsten wire for use in radio tubes and incandescent lamps must be closely controlled if the highly desirable feature of nonsagging is to be achieved. Our knowledge of factors affecting the particle size of tungsten powder has been limited by lack of any extensive literature on the subject. There are no publications in the English language discussing this problem in any but the most general terms. In this paper the published experimental information on this subject is reviewed. Based on the published data and some experimental data obtained by the author, a general theory of factors affecting the particle size of tungsten metal powder obtained by reduction of the oxides in hydrogen is offered. The various forms of the tungsten oxides and tungsten metal used in the experiments described were those prepared by commercial processes, so that the experimental results obtained on a laboratory scale would be more directly applicable to actual commercial reduction conditions. The effects of time of reduction, temperature. and concentration of water vapor in the hydrogen were observed by counting microscopically the particle distribution obtained. Such a method is very time-consuming, but the data obtained by this method are more reliable and more fundamental than those obtained by any of the several instruments available for measurement of particle size. Review of the Literature Until the year 1912, tungsten powder was prepared commercially by reducing tungstic oxide in the presence of carbon or one of its compounds (such as glycerin or ethylene glycol), usually by firing the mixture in a closed fire-clay crucible. The resultant powder contained about 95 per cent tungsten.' When reduction of tungsten oxides by H² was introduced Commercially,²,³ several investigators became concerned with the equilibria between tungsten metal and its several oxides in an atmosphere of hydrogen and water vapor.4-l3 While these many investigations were in fair agreement on the equilibria WO³ + H2 = WO2 + H2O and WO2 + 2H2 = W + 2H2O there arose considerable controversy as to the chemical composition of the oxide between WO³ and WO², because of very poor agreement on the equilibrium constant of this intermediate oxide reduction reaction. The controversy on this intermediate oxide has been in progress for more than 100 years. Thus Malguti,14 in 1835, decided it was WO2.56 In 1857, Riche15 proposed the formula W³O8. Usler,16 in 1865, confirmed the existence of WsO8 and further proposed W1O1l. In 1897, Desil7 agreed upon W²O8 but also found W5O14.

Jan 1, 1947

By T. Federighi, S. Ceresara, C. Panseri

The results of an exploratory investigation by means of resistivity measurements at -195ºC, on the aging characteristics of a set of Al-Mg alloys with a maximum content of 7 pct Mg, are reported. Whereas for dilute alloys (Mg < 1.5 pct) only a decrease in resistivity is observed at about 100°C (due to the elimination of quenched-in vacancies), for more concentrated alloys such a decrease is preceded by an increase in resistivity in the range between -60ºand +40°C. Following some previous suggestions, this increase is considered as good evidence for clustering of solute atoms @reprecipi-tation process). From the analysis of the results it appears that, although the process is substantially similar to that observed in other Al-rich alloys, it is characterized by a strong interaction between vacancies and zones. THE process of formation of Guinier-Preston zones, i.e., preprecipitation,1&apos;2 which occurs during the aging at about room temperature in many supersaturated aluminum-rich alloys, has been extensively investigated in the past few years by several workers.2,3 owever, a very interesting question arises when the case of Al-Mg alloys is considered: although it is very easy to supersaturate Al-Mg alloys, just in the same way as for many other aluminum alloys showing preprecipitation, only very little experimental evidence was available until a short time ago in the literature supporting the existence of "natural" aging in supersaturated Al-Mg alloys (see, for example, Refs. 4 to 6). On the other hand, as is well known, the X-ray method is not useful in this case because the X-ray scattering factors of magnesium and aluminum atoms are about the same. Recently, however, Cordier and Detert7 have stressed that during the aging at about room temperature of a supersaturated Al-Mg 10 pct alloy it is possible to detect an increase in resistivity; since, as is well known, such an increase is observed also in most alloys showing preprecipitation, the above authors have interpreted their results as evidence for the formation of magnesium-rich clusters (or Guinier-Preston zones) during the aging. In the course of or ientative investigations on preprecipitation in several aluminum-rich alloys, we also could detect a similar phenomenon in more dilute Al-Mg alloys, see Instituto Sperimentale Metalli Leggeri, Annual Report, 1959, and also Ref. 8. Since the details of our observations, although of a preliminary nature, differ from those of Cordier and Detert and allow one to draw a more advanced picture of the preprecipitation process in Al-Mg alloys, we have thought it useful to report our results in this paper and to comment on them briefly.

Jan 1, 1963

By L. C. Raymond

Valuations in the mineral industry differ from those of other enterprises because mines and oil wells have a definite life so cannot be considered a perpetuity. This requires that in any mineral-property evaluation the recovery of invested capital is necessary during the life of the property. Capital write-offs for nonextractive industries are assumed to be continuously plowed back to sustain the operation and produce yields on the capital invested. The extractive or mineral industry, however, generally attempts to return to the investor both interest and principal during the life of a property. Normally this is done currently and the dividend includes both items. Where the mineral property possesses large reserves and the life factor approximates a perpetuity, the return on investment is generally comparable to that of industrial stocks. The valuation of a mineral property, at best, is based on educated estimates and judgment factors. This is particularly true as it relates to estimating selling prices over a long term or assessing the quality of management. Also, it is possible to make various assumptions as to rapidity of working out the deposit, varying time for start-up of operations, varying earning rates, so as to obtain different results with the same basic facts. Thus it is not surprising that two engineers, irrespective of their abilities, may not agree exactly even when given the same facts, but their results should be close enough to be used in establishing a fair value for trading purposes. The valuation is no better than the source of basic data and the soundness of judgment factors. Fundamentally the basic principles of mineral valuation are similar for base metals, sulfur, oil, or any other mineral. Each mineral, however, requires an engineer to have a knowledge of such factors as its occurrence, distribution, mining and processing methods, and marketing problems in order to gather and analyze all the facts and data that have a bearing on the earning potential of the property. Present Value of a Mineral Property In essence the present value of a mineral property is a sum of money in today&apos;s dollars that future income from the property are worth. It differs from the total anticipated earnings by the amount of the interest that the unrecouped investment could be expected to earn during the period of recoupment. Thus, if one could accurately estimate what a mineral property will earn during its life, after deducting all operating, administrative, capital, interest, and tax charges, the determination of present value would be a relatively simple mathematical calculation. Normally, where the expected life of the mineral property extends beyond 20 or 25 years, the discounted value of earnings beyond this period is relatively small. The petroleum industry generally discounts the annual cash flow of an operation rather than earnings since, for tax-saving purposes, earnings are kept

Jan 1, 1976

By F. R. Archibald, C. M. Nicholson

THE present paper may be considered complementary to an earlier contribution on the same subject by F. R. Archibald and C. F. Jackson.1 It is particularly concerned with engineering and technological aspects of the operations at the Harleyville Alumina Plant during its period of operation from January 1945 to July 1946. The plant was built for and operated by Ancor Corporation, at Harleyville, South Carolina, as part of the government sponsored wartime program related to alumina production from domestic raw materials. The main purpose of the program was to secure technical and engineering data, based on actual plant experience, that might serve as a foundation for large scale production of alumina from raw materials other than bauxite. The Harleyville plant was directed specifically to treatment of clays found in very extensive deposits in the Carolinas and Georgia using the lime-sinter process developed by Ancor Corporation. It is considered that the purpose stated above has been served and this paper is to record and discuss some of the more important findings. The main factor in location of the plant at Harleyville was the presence in that locality of a rather remarkable deposit of high calcium limestone. The clay mining operation was centered near Aiken, S. C., and although a rail haul of ninety miles was involved there were, at the time, factors favorable to the Harleyville location offsetting, in part, the cost of transportation of clay. There are, no doubt, locations in the general area where clay and limestone deposits may be found in closer proximity but they had not been proven up when the project was undertaken. Availability of power from the Santee-Copper development whose high tension line skirted the property; ready access to rail and highway transportation; the promise, realized in actuality, of ample supply of soft water; and availability of labor supply were other factors of importance. Moreover, the general area has the decided advantage, for this type of operation, of a mild climate. Construction was begun in August 1943, and although stopped for a time pending review of the general situation that fall, it was resumed, albeit with less urgency, and substantially completed by the end of 1944. The total capital cost was approximately $3460,000. The first alumina was turned out in April 1945 and from then until the plant was closed down in July 1946, the operations followed a succession of periods of production alternating with periods in which minor alterations were made in conformity with experience. Steady improvement was made and at the time operations were discontinued it was considered that experience and the necessary engineering were in shape for removal of the remaining bottlenecks and a somewhat major revision in one section of the plant. Unfortunately this could not be carried out and it was necessary to discontinue the

Jan 1, 1948

By F. E. Buch

The smelter is designed for a production capacity of 10,000 short tons of blister copper per month, when operating on the present concentrate grade. The :smelter lay-out is shown in Fig I. The major units of equipment comprise two reverberatory furnaces, three 13 by 30 ft Peirce-Smith converters, two straight line casting machines, one being served by a 13 by 30 ft holding furnace and the other by a ladle tilting quadrant, two converter aisle cranes and two converter blowers. The plant is compact and the general arrangement of standard gauge railway tracks and conveyor belts provides for a smooth flow of incoming materials and metallurgical products. Concentrate is received by conveyor belts and fluxes in standard railway trucks. The local track system is covered by an electric trolley locomotive. The Smelter treats a wet (10 pet moisture) flotation concentrate containing approximately 53 pct total copper and 0.9 pet oxide copper. The predominating minerals are chalco-cite, chalcopyrite and bornite accompanied by small quantities of malachite and cuprite. The gangue is highly siliceous and requires limerock as a flux. Metallurgy would be straightforward were it not for the necessity for eliminating bismuth which occurs as an impurity in the ore along with the copper. Directly or indirectly most of the Smelter problems can be traced to the necessity for bismuth removal. Copper recovery, based on new copper treated, averages 97.5 pct. General Description Flotation concentrate, containing 10 Pet moisture, is conveyed from the filter plant to the smelter storage bins by conveyor belts, the material being weighed in transit by a revolving drum type of weigh-hopper manufactured by Samuel Denison and Son, Ltd. The weigher consists of a steel drum with dished ends carried on a horizontal shaft and rotated by an 8 hp squirrel-cage motor through a worm and Spur reduction gear. A feed mouth in the drum permits of filling and discharging. The whole unit is supported on a framework resting on weighing levers, which in turn connect to transfer levers, thence to an indicator of the steelyard type situated 16 ft from the centre line of the drum. The indicator is of the "Denison" patent equilibrium controlled ticket stamping type, insuring mistake-proof records by a combination of electrical and mechanical movements which Prevent the operator from printing until the cover enclosing the steelyard is closed and until the poise-weights have been Set correctly to the weight of the hopper and contents. The machine is capable of weighing 30 short tons at a time but the usual load is 28 tons. After obtaining the gross weight the drum is rotated and discharged into a receiving bin situated below it. The empty drum is weighed and the net weight re-

Jan 1, 1949

By P. R. Schmidt, N. J. Themelis

A study zvas made of the deoxidation of copper at 1170°C by injecting a jet of carbon monoxide vertically upwards into the melt. The effects of submersion depth (2 to 20 cm), orifice diameter (& to 5 in.), and gas velocity (100 to 3650 ft per sec) were examined. In the oxygen range 0.1 to 1.0 pct 0, the overall rate was conlrolled by gaseoLcs mass Lransfer. The results were interpreted in terms of a rate coefficient per unit depth which was found to be constant with distance along the jet axis and nearly proportional to the orifice Reynolds number in the range 1000 < NReo < 9100. AS the gas flow rate through an orifice submerged in a liquid is progressively increased, at least three regions of bubble formation may be distinguished. At very low rates, the formation of bubbles is practically a static phenomenon, depending on the orifice diameter, the liquid surface tension, and the densities of the two phases. In this region, the bubble size is constant while the frequency of bubble formation increases with gas flow rate.&apos;-3 At higher flows (500 < NR~, < 2100), the frequency of bubble formation reaches a steady value and the bubble size increases with gas flow rate; when the bubbles issuing from the orifice become so large that they start coalescing to form larger bubbles, the turbulence induced in the liquid by the passage of previous bubbles shatters them into small bubbles of varying size. Finally, for gas velocities in the intermediate and turbulent regions of flow (NR,, > 2100) a tangential separation surface is created around the jet and momentum transfer takes place between it and the surrounding liquid medium. The entrainment of liquid and the resulting deceleration of the gas-liquid dispersion causes the jet to expand forming a characteristic jet cone. The large velocity and density differences between the jet and the liquid result in a high degree of instability and the jet envelope fluctuates rapidly.The characteristic jet cone can be observed by means of time exposure photographs such as those shown in Fig. 1 for an air jet introduced vertically upwards in a water bath. High-speed photography has showns that the gas-liquid dispersion within the cone consists of small bubbles the size of which depends mainly on the jet orifice diameter and Reynolds number. In the laminar region of flow, the following correlation was obtained by Leibson: The results of Liebson et a1.&apos; are plotted in Fig. 2. It can be seen that the region 2000 < NReo c 10,000 is not well-defined experimentally. In the entrance to the fully turbulent region of flow (NR,, = 10,000), the mean bubble diameter decreased to about 0.4 cm and varied only slightly from there on according to the correlation:

Jan 1, 1968