By G. R. Wilms

A study has been made of the structural changes in polycrystalline high purity aluminum during the tertiary stage of creep under conditions of constant tensile load. It appears that there is no basic modification in the particular mechanism of deformation that characterized the preceding secondary stage of creep, but that the changes in crystalline structure produced during the tertiary stage are only a consequence and not a cause of the accelerated strain. Intercrystalline fissures were observed on entry into the tertiary stage, and these might supplement the accelerated rate of strain owing to local stress concentrations. There is evidence that the formation of these fissures may be associated with the presence of surface imperfections, and it is suggested that a more generalized treatment of the results may explain certain creep characteristics of commercial alloys. IN previous work'-4 a study was made of the changes produced when specimens of annealed aluminum were deformed at various temperatures and rates of strain, especially under conditions leading to creep under constant tensile load. It was shown that, as the temperature was increased or as the rate of strain was decreased, elements of the substructure produced within the grains became coarser, and with the strain rate constant at a given temperature, their size tended to an equilibrium value. The preliminary process of the breaking down of the grains into a substructure was identified with primary creep.' The subsequent equilibrium, condition was associated with secondary creep. The question then arose whether the tertiary stage corresponded to any further significant change in the substructure. The question is also of interest in view of the opinion, expressed for instance by Andrade,5 that the tertiary stage is merely an accelerated rate of strain due to the reduced area of section of a specimen under continuous tensile load, and the other opinion, as suggested by the observation by Sully, Cale, and Willoughby6 of a tertiary stage in com-pressive loading, that this third stage is a real effect in its own right. The object of this paper is to record some observations on the tertiary stage of high purity aluminum. Experimental Procedure The material was aluminum of 99.98 pct purity as previously used. The specimens had a rectangular section of l/8 x l/2 in., and extensions were measured over a 1 in. gage length. After machining to shape, the specimens were annealed to give a standard grain size of 0.2 mm and then electropolished. The general procedure involved metallographic and X-ray diffraction examination at progressive stages of elongation (marked by arrows on the curves shown in Figs. 1 and 2), the specimen being extended to fracture under constant load at a given temperature. The X-ray tests were made by the back-reflection method from a stationary specimen, using CoK radiation. The longer edge of the micrographs in the paper corresponds to the direction of applied stress. Results The previous work showed that, in the secondary stage of creep in aluminum, three basic types of structure could be developed according to the temperature and rate of strain. These were: 1—slip, which predominated at the lower temperatures and higher rates of strain and produced the finest and least perfect substructure; 2—cell structure, which superseded slip as the temperature was raised and the rate of strain decreased and which was characterized by a coarser and more perfect structure and an absence of slip lines; and 3—a stage termed "boundary microflow," which predominated at still higher temperatures and lower rates of strain when the cell size had increased and become comparable

Jan 1, 1955

By J. D. Doherty

That America's great coal deposits eventually will be our principal source of liquid as well as solid fuels is generally accepted. Moreover, the day when synthetic oil from coal will begin to supplement our petroleum supplies does not appear to be far off. The American petroleum industry has not spared effort or expenditure in its attempt to keep pace with the demand for oil, and recent production has exceeded expectations. However, the rapidly rising demand for liquid fuels plus the increasing difficulty of finding and developing the new oil needed even to maintain present production rates make it highly unlikely that oil from domestic wells can fully meet future oil requirements. Therefore, it appears that one or more of the following courses must be followed: 1. Curtail oil consumption. 2. Incr ase imports. 3. Develop new sources such as synthetic liquid fuels. All three courses may well be needed, as it is doubtful that any one of the three alternatives alone can satisfactorily solve the problem indicated by the prevailing trend in demand for oil. Curtailment of oil consumption is not a constructive policy, except where oil is being wasted or coal can be readily substituted as in stationary steam plants. Reduced oil supplies for most uses will curb our economic advancement and, in addition to inconveniencing consumers, will have a pronounced adverse effect on American industry. The oil-burner-manufacturing industry already has been dealt a hard blow. Shipments in the first 5 months of 1948 decreased 70 pct from those in the same period in 1947.1 The effect of a similar cut in the automobile industry can be imagined. A severe prolonged shortage of gasoline could seriously disturb our present economic well-being. It might be pointed out also that even the prospect of a shortage or lack of assurance for the future can discourage buyers of equipment, as occurred in the case of oil burners. An increase in our imports of oil seems to be a necessary expedient for the immediate future. Its advantages are that it will require a minimum of manpower and steel in a time of critical shortages and will conserve domestic reserves. Any major dependence upon foreign sources for our oil supplies should be avoided, however. Other nations are increasing their oil consumption more rapidly percentagewise than the United States and eventually will compete with us for the not unlimited world supplies. In peacetime, foreign countries might restrict ship- ments of oil to this country or impose exhorbitant prices. In the event of war, there is serious danger that such sources would be cut off, and American-developed oil fields overseas might even be used against us. Although synthetic fuels cannot relieve any oil shortage that might develop within the next year or two, an immediate start toward a substantial synthetics industry to supplement petroleum not only could help relieve shortages several years hence but also would help establish the much needed "know-how" for large-scale production. By assuring ample future supplies, such a start would permit sound planning by industries dependent upon oil and maintain or restore the confidence of prospective customers for oil-con-suming equipment. If it is agreed that domestic production of crude oil cannot be expected to meet future domestic demands, that oil rationing in general is undesirable. and that too great dependence on foreign oil should be avoided—and the weight of the evidence supports such conclusions—it is inescapable that commercial synthetic fuel production should be developed to supplement domestic petroleum supplies, which, of course, will furnish the bulk of our requirements for yean to come. Sources of Synthetic Oil The three principal sources of synthetic oil are natural gas, oil shale, and coal. A commercial plant using natural gas is under construction, and expansion of this industry is expected.

Jan 1, 1950

By Paul A. Farrar, Harold Margolin

The system Ti-Cr has been re investigated From 40 to 100 pct Cr. The high-temperature modification of TiCr, was found to exist in the temperature range from 1365 where it terminates in the eutectoid reaction TiCr,(TI)* — HE chromium-rich region of the Ti-Cr system was investigated by Vogel and Wenderott,' Mc Quillan,' Van Thyne et dl.,' and Cuff Duwez and Taylor determined the crystal structure of the low-temeperature modification of TiCr, to be fcc a = 6.943A and Levinger' discovered the existence of a second (high-temperature) modification of TiCr, and determited its crystal structure to be hexagonal a = 4.932A, c/a = 1.617i. No information was obtained as to the temperature range over which each modification of TiCr? existed; therefore the present investigation was initiated. I) Experimental Techniques Alloys employed for the delination of this system were prepared from iodide titanium and high-purity chromium. The purity of these materials is as follows: Iodide titanium: purity 99.99 pct; major impurities—carbon 0.0001 pct; oxygen 0 to 0.002 pct; nitrogen 0 to 0.002 pct; silicon 0 to 0.005 pct; manganese 0.001 pct; copper 0.001 pct (Foote Mineral Co., Lot 609-29). Chromium #1: metallic purity 99.997 min.; interstitial content—oxygen 0.27 to 0.46 pct; hydrogen 0.028 to 0.038 pct; nitrogen 0.0002 pct (Ave-quipo Inc.). Chromium #2: purity 99.9 pct; major impurities—carbon 0.01 pct; oxygen 0.013 pct; nitrogen 0.02 pct; silicon 0.01 pct; sulfur 0.03 pct; iron 0.01 pct (Fulmer Research Institute Ltd.). A total of sixteen alloys of thirteen different compositions was prepared in the range from 40 to 95' *All percentages are given in weight percent. pct Cr. The compositions of the alloys prepared were as follows: Ti-40, 45, 50, 60, 62, 64, 66, 68, 70, 80, 85, 90, and 95 pct Cr. Two buttons were prepared of the 66, 90, and 95 pct Cr alloys. The 40 pct Cr and one of the 66 pct Cr alloys were prepared from the chromium # 2. All the other alloys were prepared from chromium #1. The alloys were arc-melted as 25-g buttons in a copper-hearth glass-walled furnace7 under an inert atmosphere of high-purity helium. The alloys were sintered at 250 amp and melted twice at 350 amp for 30 sec with the buttons being turned over between melts. Weight losses during melting were determined and in the range 45 to 68 pct Cr they were found, in all cases, to be less than 1.25 pct of the total alloy weight. A number of the high-chromium alloys shattered during cooling from either the first or second melt, which made the weight loss considerably larger than usual. The 70 and 80 pct alloys lost approximately 5.7 pct of their total weight, the 85 pct alloys 1.5 pct, the 90 pct alloy 2 pct, and the 95 pct alloy 3 pct. However, it is felt that the actual composition of the alloys in this region is probably within approximately 1 pct of the intended composition, as a large portion of the material lost was that due to shattering after melting. Nominal compositions were therefore used in plotting data and referring to the alloys. The alloys were cut into specimens, wrapped in molybdenum sheet, and encapsuled in argon-filled quartz or Vycor tubes for heat treatment. The heat-treatment times and temperatures are given in Table I. The specimens were quenched in iced brine (I.B.Q.) following heat treatment. The standard techniques of grinding, polishing., and etching were used in preparing the specimens for metallo-graphic examination. For alloys below 68 pct Cr

Jan 1, 1963

By F. W. Jessen, N. Mungan

The plastic flow characteristics of clay water suspensions were first recognized by Binghaml in 1916 and further studied by Ambrose and Loomis' in 1931-1932. Many physical and chemical properties of clay suspensions are deeply influenced by particle size distribution as well as by the exchange cation. Separation of a number of fractions is particularly helpful in making a detailed study of a suspension. A limited amount of work has been conducted on the effects of particle size on specific properties of mud drilling fluids. A knowledge of particle size distribution is essential for a better understanding of fundamental properties of clay suspensions, particularly viscosity and gel strength. The purpose of this investigation was to study the effect of particle size on the viscosity and gel properties of clay suspensions and to determine any changes in mineral composition accompanying variation in size. EXPERIMENTAL PROCEDURE Numerous methods may be used to fractionate a poly-dispersed clay suspension into nearly mono-dispersed systems. Particles larger than 44 micron (325-mesh) may be obtained by wet screening. For sizes from 44 to 1 micron, the fractionation may be accomplished by sedimentation, elutriation plus microscopy,' or turbidimetry.6 When dealing with systems which contain a major portion of particles below l-mi-cron size, slit ultramicroscopy,7 centrifuge methods of Svedberg,5 eams,9 and McBain,l0 and X-ray methods" may be employed. The Sharples super centrifuge has been proved suitable for the economical separation of suspended particles of submicron range.12,13,14 Three-hundred and forty-five gal of 1 per cent by weight Aquagel suspension was mixed in a high-speed 5-gallon mud mixer and the suspension was allowed to stand in 5-gal glass bottles for 30 days to assure full hydration. All particles larger than 44 microns were removed by wet screening. Five fractions in the range of 44 to 1 micron were obtained by sedimentation. The Sharples super centrifuge method described by Hauser and Reed.13 Norton and Speil,14 Ha user and Lynn,15 and Hauser and Schachman,10 as employed to yield five fractions of submicron size. A super centrifuge operation chart prepared by Fancher, Oliphant, and Houssierre12 was used to determine operating conditions for the desired particle ranges. The clay suspension, after removal of all material above 1-micron size, was centrifuged. During rotation of the bowl, the particles were deposited on a thin plastic liner which fit closely inside the bowl. After passing 5 gal of suspension through the centrifuge, the liner was removed and the particles on the liner were scraped off, remixed and recentrifuged. This was repeated five times. Thus, Fractions H, I, K, and L were obtained. The finest fraction, M, remained in an approximately 0.4 per cent suspension. Water was evaporated under reduced pressure from this suspension to yield the finest particles. Results of the fractionation are included in Table 1. In order to achieve proper orientation and humidity conditions for X-ray diffraction analysis, the following procedure was employed. The dilute suspensions were placed on glass slides and allowed to dry at room temperature. This was repeated several times. Previous to measurement each sample first was placed in a water desiccator for half an hour and then allowed to stand for 15 minutes at room temperature. thus yielding an equilibrium condition of about 52 per cent relative humidity. The relative humidity of the room in which the X-ray diffraction was carried out was maintained at approximately 50 per cent so that there was no change in the spacings during the X-ray examination. Samples

By C. W. Hoffman, W. R. Hinken

Probability sizing, a fairly recent development in the field of particle separation, is now under investigation to determine its value to the mining industry. The method employed is probability sizing through a vibrating network of decreasing screen openings. While probability sizing is not new, the possibility of using it for coarse, highly abrasive ores at high tonnage rates has only recently appeared to merit practical consideration. The advantages of probability sizing vs. conventional screening methods are: (1) reduced space requirements for a high capacity unit, (2) fewer moving parts, (3) more versatile product sizing selection, (4) reduced maintenance requirements, and (5) lower power consumption. Screening is a necessary part of virtually every crushing circuit. At some stage in the process, particle separation becomes a controlling factor in the operation. The basic type of screen in use today is the vibrating unit, which usually employs a mechanical vibrator of one type or another to obtain sizing and material transportation across the screen surface. The vibrating screen has its limitations and inherent problems. Operators must live with: (1) high maintenance — worn rods, screen cloth, spacers, cross members, chutes, etc., (2) low capacity in relation to floor space requirements, (3) extreme noise levels, (4) high power consumption, and (5) structural problems in the screens and supporting steelwork. All plant operators have become tolerant of these drawbacks through the years, and little innovation has been developed in screening. The vibrating screens in use today incorporate improved metals, more efficient power sources, better lubricants, and increased manufacturing skill, but the basic machine itself remains unchanged. Screening is a relatively small part of most plants' operating expenditures and gets relatively little attention from research and development. The HiProb sizer is a new approach to the problem of particle separation on a high tonnage basis. Developed by Dr. Fredrik Mogensen (president of Fred-rik Mogensen, A. B. of Djursholn, Sweden), this unit has found its primary acceptance in the sizing of wet or dry materials in the fine ranges. Climax has been working cooperatively with Mine and Smelter Supply Company, the United States licensee, on the adaptation of the sizer to obtain consistent recovery at a high tonnage rate on a — 3/8-in. separation. This was a new application for the sizer and opened up a whole new field of problems. Dr. Mogensen's machine utilizes the control of normal probability of falling particles and is designed to eliminate some of the undesirable features of vibrating screens mentioned earlier. The machine is light, compact, consumes less power than conventional screens and has a low noise level. PRINCIPLES Probability sizing is a process designed to allow solid particles to segregate with a high ratio of the materials reporting into their respective size fractions with a minimum amount of misplaced particles. Sizing is defined in this paper as segregation of dry solid particles into fractions of comparable sizes. Probability is usually estimated as the ratio of the number of ways an event might occur vs. the total number of allowable ways. The probability process described depends upon the fact that particles falling through a network will segregate across the sizing surface even though all openings are larger than the particles. The degree of segregation is dependent upon the particle size and the trajectory applied by the sizing network to each falling particle. Specifically, the process utilizes a maze made up of screen cloth to control the path of a particle in free fall as illustrated in Fig. 1. The usefulness of this probability sizing process is dependent upon the degree of efficiency of an effective maze. Primarily, a maze must be extremely flexible to meet the multi-faceted nature of solid particles and, at the same time, the degree of control must be reproducible so that a desired separation is predictable. Dr. Fredrik Mogensen has formulated a maze that is not only flexible and easily controlled, but, mote importantly, easily adaptable to a working machine.

Jan 1, 1970

By P. K. Weimer

Coinpletely integrated thin-film circuits inco?,porating more than 1000 active and passive elements have been fabricated reproducibly in the laboratory by evaporation of- all components. A 180-stage modified shift register comprising 540 CdSe TFT's, 360 resistovs, and 180 capacitors was deposited upon a glass substrate during one pump-down of the vacuum systeitl. Experimental units have been operated for more than 5000 hr at temperatures uP to 85°C without failure of any slages. The present pupper reviews the charvactevistics of evaporated thin-film transistors (TFT's) and discusses their application to integrnted circuils. INTEGRATED circuits most widely used today are based upon silicon technology, with the circuits formed on the surface of a block of single-crystal silicon1 or on a block of sapphire 2,3 upon which a thin layer of silicon has been deposited. Transistor patterns and interconnections are defined by photographic procedures using photoresist masking. Large groups of transistors are produced in batches which undergo many processing steps, some of which are carried out at elevated temperatures. Passive elements are formed by treatment of the semiconductor surface or are deposited by evaporation alongside the active elements. The size and complexity of the circuits are limited by defects in the devices and by the size of the available single-crystal chips. Capacitative coupling to the semiconducting substrate may also limit useful size and frequency response of the circuits. An alternative approach to integrated circuits is based upon the deposition by evaporation of all circuit components upon a noncrystalline, insulating substrate such as glass.4 Thin-film field-effect transistors,1'6 known as TFT's, can be deposited in large arrays on glass or plastic substrates at the same time the associated passive elements are being deposited. Although still in the research stage the all-evaporated approach is expected to offer certain advantages for many applications. In particular, the use of thin films upon a noncrystalline substrate offers the prospect of producing complex, large-area circuits not now feasible with single-crystal silicon. Important applications of this type include memory arrays for computers and imaging devices for television. The ease with which the evaporated TFT's can be deposited may permit continuous, automated production methods not possible with high-temperature batch processing. Recent advances7'8 in the fabrication of thin-film transistors have led to greatly improved reproduci-bility and life of the TFT's. Experimental circuits having over 1000 active and passive elements deposited upon a common glass substrate are currently being produced in the laboratory. The present paper reviews recent progress in the development of the TFT and in its application to integrated circuits. I) DESCRIPTION OF THE THIN-FILM FIELD-EFFECT TRANSISTOR The TFT is a field-effect transistor of the type having the control gate separated from the semiconductor by a thin insulating spacer. Although its operation resembles that of the silicon MOS transistorg its construction is based entirely on thin-film techniques. Fig. 1 shows a cross-sectional view of an evaporated TFT deposited upon a glass substrate compared with a silicon MOS transistor deposited upon single-crystal sapphire.3 The semiconductor in the TFT is a poly crystal line layer, of a material which can be readily evaporated, such as cadmium sulfide, cadmium selenide,l0 or tellurium." Silicon monoxide layers have usually served as the gate insulator, but other oxides, sulfides, and fluorides may be used. Film thicknesses range from a few hundred to a few thousand angstroms. The source, drain, and gate electrodes in the TFT are of metal. Qpical source-drain gap dimensions are 0.0003 x 0.030 in., with a gate strip whose width slightly overlaps the source and drain. The source and drain electrodes should make low impedance contacts to the semiconductor. With cadmium sulfide films, gold is a satisfactory material for underlying electrodes, while aluminum is preferable for overlying electrodes.12 Considerable variation in design of the TFT is permissible, with the electrodes being

Jan 1, 1967

By W. S. Hyler, W. L. Bruckart

The powder metallurgy and arc-cast types of wrought molybdenum stock were studied in rotating beam fatigue. Endurance ratios of unnotched specimens after 5x10 cycles were found to be 0.74 and 0.81, respectively. Fatigue notch factors (K,) of 1.36 and 2.05, respectively, were obtained on V-notched specimens having a theoretical stress-concentration factor Kt = 3.1. MOLYBDENUM and its alloys are rapidly gaining importance as engineering materials of construction for high temperature applications. AS a wrought material, molybdenum and its alloys are outstanding above 1800°F. It is necessary, however, with molybdenum to provide elevated temperature oxidation protection. This is currently being studied by a number of investigators. Thus far, there have been no published data on the fatigue behavior of molybdenum either at room temperature or at elevated temperature. The knowledge of fatigue behavior, particularly notched fatigue behavior, becomes increasingly important as the engineering importance of a material increases, especially from the design standpoint. The work described here was directed toward determination of the notched and unnotched rotating beam fatigue characteristics of molybdenum at room temperature. Also, it was desired to learn whether any difference exists between wrought molybdenum of the powder metallurgy and the are-cast types. Fabrication History of Bar Stock For this work, bar stock was procured from Climax Molybdenum Co. (are-cast type) and from Westing-house Electric Corp. (powder metallurgy type). The processing histories of these materials are listed in Table I. The first lot of are-cast molybdenum was deoxidized by aluminum additions. The second lot was deoxidized by carbon." Both lots of the powder Microstructure A microscopic examination of these materials, as received, revealed the powder metallurgy molybdenum to be free of inclusions and to be finely fibered. On the other hand, the are-cast C molybdenum possessed numerous carbide inclusions, and the arc-cast A appeared to have coarse grained fibers. These are shown in Fig. 1. Owing to the large apparent difference in fineness of fiber between the are-cast A and the powder product and are-cast C, a check was made of the recrystallized grain sizes to determine whether these differences persisted. A series of recrystallization anneals revealed mixed grain sizes in both the are-cast A and the powder product. Variations in grain diameter of as much as 50 times were found after full recrystallization at 1200°C for 30 min. There was no distinction between the two. Arc-cast C was not checked. Room Temperature Mechanical Properties Prior to subjecting the materials to fatigue tests, room temperature mechanical properties were determined. These data, together with the tensil: strength of the notched bars, data,togetherare listed in Table tensil: There were no significant differences in the tensile strengths of the two types of molybdenum. However, the powder metallurgy material was generally more ductile and yielded at a somewhat lower stress than the arc-cast material. Tensile strengths of the notched specimens indicated a slightly greater notch strengthening effect in the are-cast C than in the powder product, lot 2. Room Temperature Fatigue Properties Sample Preparation: Specimens were prepared for use in R. R. Moore rotating beam fatigue machines. These specimens had a continuous radius test section with a minimum diameter of 0.260 in. The specimens were prepared by grinding to shape and polishing to produce a smooth unworked surface. Polishing consisted of rotating a disk in the continuous radius section on which were attached, successively, emery belts of 240, 400, and 600 grit. The specimens were slowly rotated during the operation. The belt speed was high, and rotation was such that polishing scratches were longitudinal. Unnotched Fatigue Properties: Unnotched fatigue data were obtained from a number of specimens of each of the four lots of molybdenum. The results of the tests are presented in Fig. 2. From this figure,

Jan 1, 1956

By N. Jaffee, J. E. Dorn

An activation energy of 27,400 5 1000 cal per mole was obtained for the creep of poly crystaLline aluminum over the temperature range of 273° to 350°K, at strains varying from 0.003 to 0.230. Stresses varied fronz 2250 to 6000 psi, strain rates from 0.1145 x 10-5 to 29.5 x 10~s min.-1. A strain temperature-compensated time correlatzon was oblained indicating that the structure was depedent solely upon the strain at a given stress; X-ray diffraction analyses and tensile tests on precrept specimens verified this. PREVIOUS investigations1 have revealed that the apparent activation energies for creep of high-purity polycrystalline aluminum are insensitive to the applied stress, strain, and strain rate. On the other hand, the apparent activation energy is dependent on the temperature1,2 as shown by the data reproduced in Fig. 1. Each plateau of this curve is associated with a unique rate-controlling dislocation mechanism for thermally activated creep. It is now very well-established that over the high-temperature range, where the activation energy is about 35,500 cal per mole, the creep rate is controlled by the dislocation climb mechanism. 3 Over the intermediate range of temperatures, from about 260° to 370°K, another unique activation energy, namely 28,000 cal per mole, is obtained. Current evidence strongly supports the contention that cross slip is the rate controlling mechanism for creep in this case: 1) Crystal recovery can occur by a number of mechanisms prominent among which are climb and cross slip. Astrom,4 using the Borelius micro-calorimeter, reported rapid crystal recovery of cold-worked polycrystalline A1 at 340° to 370°K giving an activation energy of 28,000 cal per mole and additional recovery at 455° to 478°K giving an activation energy of 3 6,000 cal per mole. Whereas the latter recovery process was clearly associated with the dislocation climb mechanism, the former, 28,000 cal per mole process could have arisen as a result of the cross-slip mechanism. 2) Single crystals of high-purity A1 favorably oriented for octahedral glide exhibit an activation energy for creep of about 3400 cal per mole over the range from 0° to 400°K and that of about 28,O:O cal per mole over the range from 600° to 775°K . Whereas the lower activation energy process is accompanied by the development of sharp slip-band traces, the 28,000 cal per mole process was uniquely characterized by extensive cross slip. 3) Theoretical calculations by Seeger and schoeck6 suggest an apparent activation energy for cross slip in A1 of about 24,000 cal per mole and another theoretical estimate by Friedel 7 gives the observed 28,000 cal per mole as the theoretical activation energy. It is therefore consistent with this evidence to, at least tentatively, ascribe the 28,000 cal per mole creep process in A1 to the operation of cross slip as the rate controlling mechanism. Although creep has been rather well-explored in the dislocation climb range, very little, excepting perhaps the activation energy, is known about creep in the cross slip range. This investigation was undertaken, therefore, to reconfirm the activation energy for creep in polycrystalline A1 in the intermediate temperature range and to study the strain-time relationship for creep at a constant stress in the cross slip region. EXPERIMENTAL PROCEDURE AND TECHNIQUE The three types of high-purity A1 alloy specimens described in Table I were used in this investigation. Specimens were milled from 0.100 in. thick cold-rolled sheets with their tensile axes in the rolling direction following which they were given a recrys-tallization and grain growth heat treatment at temperatures well above those which were subsequently employed in the creep tests.

Jan 1, 1962

By A. D. McMaster, M. L. Gimpl, N. Fuschillo

There is interest in the use of rhenium metal films as resistive elements in thin-film circcits, and already some zvork has been done using er)aporated rhenium films. It has been found that rheniim films protected from the atmosphere by an evaporated layer of silicon monoxide show excellent electrical stability. Unprotected films, however, are subject to aging- effects, notably the increase in electrical resistivity as a function of time. This phenomenon can be understood as primarily one of oxidation of the thin films. This paper is concerned with the study of the oxidation and crystallization behavior of such unprotected films. It has been found that the oxidation rates are a function of the substrate temperatures used during the deposition of Lhe metal films. The strictures observed in the films are correlated with the film resistivities and some data are presented to establish the existence of the various types of oxides of rhenium. ThERE is some interest in the use of thin films of rhenium metal as resistive elements in monolithic, thin-film integrated circuits. Some work has been done using evaporated films and it has been found that such films, if protected from the atmosphere by an evaporated layer of silicon monoxide, show excellent electrical stability up to temperatures of 500"." Rhenium films unprotected from the atmosphere tend to age and the electrical resistivity of the films increases as a function of time. Rhenium films, of the order of <100A thick, prepared by electron-beam evaporation techniques are found to oxidize very readily when exposed to dry air at room temperature. It would seem, therefore, that this aging phenomenon could be attributed to the oxidation of the metal films. In this investigation, the oxidation and crystallization behavior of thin films of rhenium evaporated onto silicon monoxide substrates were studied as a function of the substrate temperatures used during the evaporation. The films were examined using electron-microscopy and electron-diffraction techniques. EXPERIMENTAL RESULTS Rhenium metal was evaporated onto suitable prepared substrates which were heated to various temperatures. The evaporations were performed in a vacuum of approximately 5 x 1CT5 torr. The evaporation was carried out at a rate of approximately 10A per omin. The final film thickness was approximately lOOA and the resistance ranged from 5000 to 10,000 ohms per square. The substrates used for supporting the metal films were made by evaporating 75A of silicon monoxide onto freshly cleaved mica. The silicon monoxide film was then floated off the mica by immersing the composite in water. The film could then be picked up on a clean nickel grid. Silicon monoxide substrates were chosen because of their similarity to quartz and glass substrates commonly used for making thin-film resistors. Fuschillo, Gimpl, and McMas-ter have also shown that silicon monoxide films have only minor structural changes at temperatures up to 800°C. This fact simplified the interpretation of any changes observed in the electron micrographs or electron-diffraction patterns obtained from the deposited rhenium films. After the evaporations were completed, the substrates were cooled to room temperature, except where noted differently, before the coated substrates were removed from the vacuum system. All aging of the deposited films was done in a desiccator. The evaporated films were examined in an electron microscope equipped with a hot stage that would permit continuous observations of the samples up to temperatures of 1000°C. RESULTS A series of electron micrographs of the rhenium films deposited on the silicon monoxide substrates are shown to Figs. 1 to 3. In all cases, the metal films are approximately 100A thick and the micrographs were taken 1 hr after the deposition was completed. here was no apparent structure in the films deposited on the substrates held at the higher temperatures. The

Jan 1, 1967

By C. R. Kyle, R. L. Perrine

A transparent model of a reservoir has been used to study some characteristics of instability in miscible displacement. The linear model dimensions are 1/4 in. x 91/2 in. x 10 ft. The model is packed with spherical glass beads. Thee groups of experiments have been performed. The objectives were to measure, respectively, the rate of growth of the transition zone, flow velocity variations in the transition zone, and the effect of a graded viscosity zone on stability. All experiments were compared, where possible, with theory. The transition zone grew almost linearly with distance traveled, regardless of flow rate, where adverse viscosity ratios were used. At very adverse viscosity ratios and large distances traveled, some reduction below linear growth was noted. This could be attributed to the effects of mixing. General similarity in flow pattern was commonly shown in different tests, although exceptions occurred at the higher viscosity ratios. Injection of tracer spots permitted direct experimental measurement of velocity variations. Statistical methods were used to compare observed velocity variations with recently published theories. Surprisingly good agreement with some theoretical predictions was obtained. In the experiments using an initially graded viscosity zone, macroscopic stability was reached before predicted by theory. Under conditions theoretically considered to be slightly unstable, any fingering tendency was too slight to become observable within a 10-ft long system. The general correlation of all experiments with published theory was good, and suggests that theoretical predictions can be extended to reservoir problems. INTRODUCTION Early laboratory studies of miscible displacement demonstrated the high recovery efficiency possible with this method. Linear laboratory models showed that, under some circumstances, all in-place hydrocarbons could be recovered using as little solvent as 5 per cent of the pore volume. These results led to a series of pilot field projects. Under realistic conditions, however, other laboratory studies showed that a small solvent bank may not recover much more oil than a conventional gas drive. The cause of this lack of efficiency is unstable viscous fingering. The size of the solvent bank required to give optimum recovery is, therefore, a question of great economic significance. The object of the experiments described in this paper was the quantitative measurement of unstable flow parameters, the verification of present theories on the miscible displacement process, and correlation of these theories with ex peri mental observation. Of the theories which have been advanced, those by Dougherty, Koval and Perrine show promise of predicting reservoir performance with reasonable accuracy.l-7 The present experiments were correlated, where possible, with the theories of Koval and Perrine. Dougherty&apos;s theory was not used because of the additional computational difficulty it presented and the belief that no further information would result. EXPERIMENTAL EQUIPMENT A transparent reservoir model, consisting of a vertical reinforced plexiglass column, was used for the experiments. The column was packed with glass beads, which served as the porous medium. To induce a known velocity disturbance in the flow, a double cosine wave restriction in the transverse cross-section was placed at the top of the column. To mark the flow field and provide a means of measuring the local fluid velocity, a dye-spot injection system was provided. The column was 10 ft high by 1/2 in. wide by 1/4 in. deep. The cosine restriction was placed 16 in. from the top of the column. The glass beads were smooth and spherical and had a mean diameter of 0.0102 cm. Liquids entered the top of the column through a manifold allowing three points of entry (left, center, and right, or any combination of these). A positive-displacement pump with variable-speed drive was used to control liquid flow rates. The pump transferred viscous oil from a reservoir to an accumulator, which displaced the test liquid into

Jan 1, 1966

By G. R. Speich, D. J. Mack

The transformation of was studied by isothermal methods. At all temperatures, the ß transforms quickly to fine grained ß" which develops silver-rich striations. At higher temperatures the striations disappear, the final structure being Widmanstatten a in ß&apos;. At lower temperatures, the striated ß" is consumed by pearlite nodules of a + ß&apos; which in turn form the Widmanstatten a in ß&apos;. The transformation is unlike any previously reported for a eutectoid. AS part of a general program of study on the eutectoid reaction, the Ag-Cd eutectoid seemed particularly attractive because the ß phase which undergoes the reaction is another of the typical "electron compounds," AgCd, having the disordered body-centered cubic structure. This work deals with the eutectoid which occurs at 50.5 wt pct Ag, and not with the eutectoid which has been reported at 42.9 pct Ag.&apos; There has been no work reported specifically on the Ag-Cd eutectoid which was studied. The only information available on this eutectoid is that work done in the determination of the phase diagram. For the most part, the terminal portions of the diagram, Fig. 1, are well established; however, the region from 40 to 60 pct Cd is still somewhat in doubt. The X-ray evidence&apos;..&apos; in this region is in conflict with the results of thermal analysis. X-ray analysis3 does not show a polymorphic transformation at about 240°C as indicated by thermal analysis.1,5 Even the X-ray evidence, within itself, is confusing in this region of the diagram. One investigator2 reports the ß phase as hexagonal close-packed and has found three phases in the one-phase ß field. Other X-ray investigators"&apos; &apos; report the ß phase as body-centered cubic. The authors believe that much of the confusion resulted from incomplete homogenization of the alloys. It was found that it takes almost a week to produce a completely homogeneous two-phase structure at 370°C. Another possible source of error is the volatilization of cadmium from the surface and cracks of the specimen during annealing with the possible formation of a cadmium-poor phase. The only metallographic data available on this eutectoid alloy are those of Durrant1 and Fraenkel and Wolff.5 his information is very limited. The phase diagram chosen as most nearly correct is that in the Metals Handbook," which is almost identical with the phase diagram suggested by Durrant.1 Materials and Procedure The alloy was prepared from high purity silver (999.5 plus fine) and high purity cadmium (0.02 Pb, 0.005 Cu, trace Fe). The metals were melted in carbon under a nitrogen atmosphere. Some cadmium was lost by volatilization but by remelting several times and adding cadmium a 200 g ingot of approximately eutectoid composition was obtained. Because the CdO fumes are quite toxic, the exit gas from the furnace was led through a water trap to condense the CdO. The ingot was homogenized at 650°C for 24 hr, no attempt was made to prevent decadmiumization. This resulted in a narrow decadmiumized rim on the ingot which was removed. Filings for analysis were obtained from cross sections of the ingot. Silver was determined by the Volhard thiocyanate method,? cadmium by difference. The ingot analyzed 50.8 pct Ag at the top of the ingot and 50.7 pct at the middle and at the bottom of the ingot. This alloy was only slightly hypo-eutectoid compared to the accepted value of 50.5 pct Ag and was used for the isothermal studies. It was felt that further attempts to adjust the composition might be futile because of the volatility of the cadmium. The ingot was sectioned to specimens approximately 3/4 x 3/4 x 1/8 in. These specimens were "austeni-tized" for 3 hr in air at 650°C to yield homogeneous ß and then quenched into a salt bath held at constant subeutectoid temperatures where the transformation

Jan 1, 1954

By E. C. Barfield, D. G. McCarty

Two-dimensional analyses offer considerable promise in providing the basic information required to effect more precise control of petroleum reservoir performance. This paper describes a method for conducting some engineering analyses of this type using a high-qreed digital computer. The general approach is to (I) develop a representative numerical model of the reservoir and (2) employ a suitable numerical technique to solve the basic equation of flow and to develop the required engineering information for the particular case represented by the model. This technique has been used to calculate pattern performance in connection with several field projects involving water injection into oil reservoirs. This type of analysis involves sequentially (I) calculating the pres-&apos; sure distribution in the reservoir and (2) tracking the progress of the interface between the displaced and displacing fluids in a step-wise manner to provide a depletion history of the operation. The particular analysis presented in this discussion is subject to the restriction that the mobility of the displaced and displacing fluids be equal and assumes that the fluids are incompressible and that gravity and capillary pressure do not affect the shape of the flood pattern. Complete two-dimensional .flexibility is maintained with regard to definition of reservoir rock and fluid characteristics, placement of physical restrains and boundary conditions, investigation of flow characteristics in the reservoir, and movement of the displaced and displacing fluid interface. The results of these studies indicate that the highspeed digital computer is well suited for conducting reservoir performance studies in two-space dimensions and that dependable numerical techniques are available for making such analyses. INTRODUCTION One of the problems facing petroleum engineers is that of providing more precise engineering control over reservoir operations at all stages during the depletion cycle. The most direct approach to this problem is to simulate the reservoir with some type of physical or mathematical model and use the information developed from the behavior of the prototype to predict the performance of the actual reservoir. This principle is, of course, not new, and a variety of simulation techniques have been developed to provide information on the behavior of oil and gas reservoirs. One straightforward refinement of present reservoir analysis techniques is the progress from one-dimensional reservoir models to those where the reservoir can be represented in two- and three-space dimensions. Multidimensional reservoir analyses are desired in order to show not only what is happening in the reservoir but in addition to show where in the reservoir the various phenomena of interest are occurring. Thus far, two-dimensional analyses have been confined predominantly to potentiometric and electrolytic model studies. However, when large numbers of wells are involved and where large-scale models are required, such problems become very tedious and instrumentation problems become acute." It is possible through use of numerical methods and general purpose digital computers to avoid many of the instrumentation difficulties and to relax some of the restrictions of previous techniques. The purpose of this paper is to discuss some recent experiences with the use of high-speed digital computers for predicting pattern performance in fluid injection operations and to describe the numerical procedures which have been used for making such analyses. THE NUMERICAL MODEL The problem of representing the reservoir with an appropriate numerical model is composed of at least two important considerations. The first requires that an adequate description of the reservoir mechanism be formulated in the form of the basic differential equation describing the process. The second consideration is definition of the physical characteristics of the reservoir. The latter requires that representative basic data be obtained, examined, and interpreted to provide sufficient detailed definition of the pertinent physical properties throughout the system. The Differential Equation One of the basic assumptions made for the purpose of performing the two-dimensional studies being dis-

By W. F. Domis, F. von Gemmingen, F. Garofalo

The effect of rain size on the creep behavior of an austenitic iron-base alloy has been studied at 1300° F under conditions of constant stress. The average grain diameter varied between 9 and 190 p (ASTM 10.7-2). The subgrain size and apparent activation energy for creep were not found to depend in any systematic manner on gain size. Grain hozmdary serrations were observed in all specimens tested. The variation of the secondary-creep rate, 2,, with the pain diameter, 1, is given by: es = K(213m + 1 )/l.]; 1, is the grain diameter zohere is reaches a minimum. Results in the literature shoujthat 1,increases as the temperature increases. At low creep temperatures is is therefore proportional to 12, at intermediate temperatures <, exhibits a minimum, and at high creep temperatures is is proportional to 1/1. The dependence ofis on the stress, u, is given by: t, = A" (sinh acrln, a and n show little variation with 1. The dependence of A" on 1 is given by: A" = KA[(21k + 13)/1]. For 1 » >>lmn = 4, and at constant values 01- isat lozu stress levels, the steady-state stress is given by the Hall-Petch relation. The variation of c, with grain size is believed to he associated particularly with grain boundary generation of dislocations which becomes more important with increasing temperatures. SEEMINGLY inconsistent experimental findings have led to a certain amount of confusion concerning the effect of grain size on creep behavior. The confusion is attributed to a lack of test results obtained over sufficiently wide ranges in grain size, stress, and temperature. Experimental results presented in this paper and results available in the literature1-5 show a consistent behavior and lead to a unified concept for the dependence of secondary-or steady-state creep rate on grain size. In accordance with this concept, which is substantiated experimentally, secondary-creep rate should increase with increasing grain diameter at low creep temperatures, leading to greater creep strengths for fine-grained materials. At intermediate temperatures the secondary-creep rate should decrease to a minimum and then increase as the grain size is increased. At high creep temperatures the secondary-creep rate should decrease with increasing grain size, leading to greater creep strengths for coarse-grained materials. Whether a temperature is high or low for creep in a metal or alloy depends primarily on its melting temperature. MATERIAL AND TEST PROCEDURES The material tested was an austenitic iron-base alloy of the following composition (wt pct): C, 0.005; N, 0.017; Mn, 1.26; Ni, 14.21; and Cr, 17.18. Two 15 -lb ingots were forged and hot-rolled to 5/8-in.-diam bars which were then cold-rolled and cold-swaged to a diameter of 0.49 in. These were sectioned into 3-in.-long blanks and heat-treated at various temperatures to obtain different grain sizes. The procedures employed and the results obtained are summarized in Table I. The secondary treatment at 1400° F followed the primary treatment without intermediate cooling to room temperature. This final treatment was employed to minimize various effects arising from heating to different temperatures during the primary treatment, particularly differences in intragranular dislocation structure, segregation of interstitial atoms at grain boundaries, and density of grain boundary ledges. The intragranular dislocation structure was examined by electron transmission metallography after each of the treatments described in Table I. Isolated dislocations and a few tangles were observed but no evidence of subgrains was found after any of the treatments. No grain-size effect was evident on the density and distribution of dislocations. Stabilization of grain boundary structure is particularly important because, as will be discussed later, grain boundaries influence high-temperature creep behavior. Magnetic-permeability measurements after each treatment and

Jan 1, 1964

By J. G. Early, F. V. Lenel, G. S. Ansell

The isothermal shrinkage rates of copper-powder compacts were determined in the temperature range from 760o to 1060oC. The rates for compacts fabricated from a pure spherical copper powder were compared, on the one hand, with those fabricated from a spherical powder containing a dispersion of aluminum oxide in the copper matrix and, on the other hand, with those fabricated from a pure copper powder having irregularly shaped particles. The irregular copper-powder compacts shrank much faster than the spherical copper-powder compacts and these, in turn, shrank faster than dispersion -strengthened copper -powder compacts. The experiments were run under a small external load. By varying this load, the stress dependence of the isothermal shrinkage rate could be measured for compacts from spherical-copper powders. This stress dependence was found to be approximately proportional to the 4th (dispersion-strengthened alloys) or 4.5th (pure metals) power of the stress. It is concluded that the material-trans port mechanism is due to dislocation climb rather than to Herring-Naharro creep. In this investigation the isothermal shrinkage rates of compacts made of copper powder with an average particle size of 70 g in the temperature range from 780o to 1060°C were studied. The aim of the investigation was to determine the mechanism of material transport responsible for the shrinkage of these compacts. Since the phenomenon observed in this investigation was shrinkage of compacts at high temperatures, it will be necessary to consider all the material-transport mechanisms possible in sintering. It is unlikely that evaporation and condensation, surface diffusion, or even volume diffusion of vacancies, in which surfaces of small radius of curvature are vacancy sources and those of larger radius of curvature vacancy sinks, will materially contribute to a sintering process involving shrinkage, i.e., one in which the centers of adjacent particles move towards each other. The two principal mechanisms which were considered were the so-called Nabarro-Herring mechanism and a plastic deformation mechanism by dislocation movement. Both of these mechanisms were originally conceived to explain creep, i.e., the plastic deformation of metals at elevated temperatures under a constant applied stress. The shrinking of metal-powder compacts which was studied in this investigation can be readily treated as a creep process. This means that the shrinkage rates observed are considered as creep rates under the influence of an applied stress. It is true that the stresses in sintering experiments are generally not constant but decrease continually with time, but, by considering creep rates or shrinkage rates over a relatively short time interval, the small changes in stress during this time interval can generally be neglected. Nabarro-Herring microcreep is a high-temperature deformation mechanism which is caused by a diffusional flow of vacancies from boundaries under a tensile stress towards those under a compres-sive stress. Herring1 has shown that in this type of microcreep the strain rate e is proportional to the applied stress and follows an equation of the form ma, aexp(-Q/RT) [l| where <j is applied stress, Q is the activation energy for self-diffusion, R is the gas constant, and T is the absolute temperature This type of creep can explain the shrinkage of a porous compact. The surface of the pores are subjected to the tensile stress of surface tension, while the grain boundaries are under a compressive stress also due to surface tension. Vacancies diffuse from the pore surface through the lattice to the grain boundaries, where they are eliminated. In order to maintain vacancy equilibrium at the pore surface the vacancies leaving the region of the pore surface are replenished from the volume of the pore, which means that the pores shrink.

Jan 1, 1964

By H. Y. Hunsicker

A graphic method has been devised for three-di-mensional analysis of hot deformation and for correlating the amount and directionality of the deformation with resulting directional properties. Deformation is evaluated in terms of dimensional change ratios referred to three orthogonal axes. Since all combinations of the three ratios can be represented in a triangular coordinate field with logarithmic scales, a two-dimensional chart of extent of deformation and degree of asymetry is possible. The entire gamut of shape changes from upsetting through flat-rolling to rod-rolling is accommodated. The resulting coordinate system is a base upon which can be represented the properties of the wrought products measured in the directions of the axes employed fir evaluating the deformation. When property data are available for many types and amounts of deformation, a three-dimensional figure can be constructed, and the projection of this figure is referred to as a &apos;&apos;3d&apos;&apos; chart. Experience in using such charts to plan fabricating operations for a variety of thick-section forged and rolled products of heat-treated aluminum alloys has verified its practical value for optimizing directionality relationships. MechANICAL anisotropy of thick section products of heat-treatable aluminum alloys is recognized by producers and users of these products, and the extent of the directional differences is apparent in property tabulations included in handbooks, standards, and specifications.&apos; Attention has also been directed to the existence of important directional differences in the resistance of these products to stress-corrosion cracking. Metallurgical structure factors responsible for these directional differences include, among other possibilities, shape and alignment of grains, voids and nonmetallic inclusions (when present), volume fraction and spatial distribution of secondary phase particles and solid-state precipitates, crystal-lographic textures, and Bauschinger effect. The contributions of the individual factors vary with alloy composition, heat-treated temper, type of working process (forging, rolling, extrusion), and the amount and directional nature of the deformation. In general, the cast ingot used as the starting material for producing these wrought products exhibits only a modest degree of directionality. A monotonic and continuous transition from this nearly isotropic state with progressive hot deformation would appear probable, assuming that the working temperature is sufficiently high to cause continuous dynamic recovery. Several years ago a project was undertaken to evaluate the effects of hot deformation and metallurgical structures on the directionality of thick wrought aluminum alloy products, and the method to be described was developed as an analytical tool in this investigation. DIRECTION NOMENCLATURE The nomenclature system adopted by industry for the three mutually perpendicular directions employed in testing aluminum alloy products includes four terms: "longitudinal", "transverse", "long transverse", and "short transverse". These terms are conventionally related to the external geometry of the product but also by implication to the deformation and resulting metallurgical structure. Occasions arise in which through use of unusual fabricating methods, intentional or otherwise, the structure does not have the usual relationship to external geometry or may be very complex because of inhomogeneity of deformation throughout the piece. The longitudinal direction is generally parallel to the primary rolling direction or to the direction of extrusion. In the case of forging, it is parallel to the direction of maximum extension (not maximum "working" or "flow", as frequently stated). The term transverse is applied to any direction perpendicular to the longitudinal direction in a product having symmetry about the longitudinal axis, and generally, although not always, the deformation to produce these forms is nearly symmetrical in the transverse plane. This term then may be applied to a round, square, hexagon, or other polygonal, symmetrical shape produced by extrusion or rolling or by forging, if produced by a simple, symmetrical drawing procedure. The type of microstructure generally associated

Jan 1, 1970

By H. I. Smith

CONTENTS [PAGE Problems of Mining and Processing Mineral Aggregates (TP 1649, by NATHAN C. ROCKWOOD, Min. Tech., Nov. 1943. Discussion by H. I. SMITH, IRVING WARNER and the author) t Mica in War (TP 1749, by RUSSELL G. WAYLAND, Min. Tech., July 1944. Discussion by H. S. SPENCE) 3 Three Roofing-granule Plants in Pennsylvania (TP 1787, by RICHARD M. FOOSE, Min. Tech., Jan. 1945. Discussion by H. I. SMITH)5 Methods of Prospecting and Mining Optical Calcite in Montana (TP 1896, by E. W. NEWMAN, Min. Tech., Nov. 1945. Discussion by W. C. STOLL and FRANK C. ARMSTRONG, and the Glass Sand and a Glass Industry in Puerto Rico (TP 1939, by HOWARD A. MEYERHOFF and J. EARL FRAZIER, Min. Tech., Nov. 1945. Discussion by A. M. SHORT, the author and PHILIP The "Bonanza" Mica Operation of Purdy Mica Mines, Limited, Mattawsn Township, Ontario (TP 2154, by HUGH S. SPENCE, Min. Tech., March 1947. Author&apos;s supplement and discussion by JOHN A. BAKER, E. J. LINTNER, and the author) 7 Process for Manufacture of Dead-burned Magnesite and Precipitated Calcium Carbonate from Dolomite (TP 2155, by ROBERT D. PIKE, Min. Tech., March 1947. Discussion by 0. C. RALSTON and the author) 9] Problems of Mining and Processing Mineral Aggregates H. I. SMITH*-Mr. Rockwood has presented a very interesting paper on problems of the mineral aggregate industry in meeting specification requirements, which apparently are ever decreasing in tolerance. May I call attention to a method of mineral separation that may be of value in separating the flat aggregate particles from the more angular ones and possibly the soft particles from the hard. The method is the old Pardee spiral coal separator, extensively used many years ago in the anthracite region for separating rock and bone from anthracite coal.1 The success of the process depends on the relative coefficient of friction of the aggregate particles to be separated rather than on their relative specific gravity. The flat and the soft particles normally will slide more slowly and stay on the inner spiral until they reach the delivery spout at the bottom whereas the round and the angular pieces will work to the outer edge and fall off into a spiral of larger diameter. The capacity of the separator is increased materially by having three inner spirals, with a separate feed for each, on which the particles travel more slowly, and one outer spiral from which the more rapidly traveling pieces slide to the bottom. IRVING WARNER*-I have long been convinced that much of the equipment and methods developed for mineral dressing might be advantageously employed in the mineral aggregates industry, and more particularly in the production of sand and gravel. The two industries are not well acquainted with each other or their problems. They have separate trade publications. The difficulty with the situation is that there are few large sand and gravel plants and few provided with technical services in their own organization or by retainer. This does not refer to engineering organizations but rather to improvement of plant technic in processing.

Jan 1, 1947

Time as a Factor in the Making and Treating of Steel. By John Johnston. (Howe Lecture) (T.P. 1478) Influence of Chromium and Molybdenum on Structure, Hardness and Decarburization of 0.35 Per Cent Carbon Steel. By R. F. Miller and R. F. Campbell. (T.P. 1345) Mechanical Properties of Iron-manganese Alloys. By F, M. Walters, Jr., I. R. Kramer and B. M. Loring. (T.P. 1369) The Instability of Low-expansion Iron-nickel-cobalt Alloys. By I. R. Kramer and F. M. Walters, Jr. (T.P. 1370) The S-curve of a Chromium-nickel Steel. By B. M. Loring. (T.P. 1383) A Magnetic Determination of the A3 Transformation Point in Iron. By B. A. Rogers and K. 0. Stamm. (T.P. 1388) Rapid Tension Tests Using Two-load Method. By A. V. de Forest, C. W. MacGregor and A. R. Anderson. (T.P. 1393) Effects of Scrap in the Blast-furnace Burden. By C. L. T. Edwards. (T.P. 1270) Temperature Gradients through Composite Carbon Columns and their Application to Blastfurnace Linings. By F. J. Vosburgh and M. R. HatFIeld. (T.P. 1363) Correlations of Some Coke Properties with Blast-furnace Operation. By H. W. Johnson. (T.P. 1402) The Technical Cohesive Strength and Yield Strength of Metals. By D. J. McAdam, Jr. (T.P. 1414) Effects of Eight Complex Deoxidizers on Some 0.40 Per Cent Carbon Forging Steels. By George F. Comstock. (T.P. 1417) Significance of the Bessemer End Point. By H. T. Bowman. (T.P. 1428) Structural Diagrams of Nickel Irons and Steels. By J. T. EasE and N. B. Pilling. (T.P. 1432) Carbides in Low-chromium Steel. By Walter Crafts and C. M. OFFenhauer. (T.P. 1436) Hardenability Calculated from Chemical Composition. By M. A. Grossmann. (T.P. 1437) Recrystallization of Silicon Ferrite in Terms of Rate of Nucleation and Rate of Growth. By J. K. Stanley and R. F. Mehl. (T.P. 1438) The Solubility of Carbon as Graphite in Gamma Iron. By R. W. Gurry. (T.P. 1440) An Evaluation of the Factors Affecting Iron Oxide in the Open-hearth Bath. By J. E. Gould and H. J. Hand. (T.P. 1442) Precision in Creep Testing. By J. A. Fellows, Earnshaw Cook and Howard S. Avery. (T.P. 1443) Lattice Relationships in the Decomposition of Austenite to Pearlite, Bainite and Martensite. By G. V. Smith and R. F. Mehl. (T.P. 1459) Rate of Nucleation and Rate of Growth of Pearlite. By F. C. Hull, R. A. Colton and R. F. Mehl. (T.P. 1460) Weight Change as a Criterion of Extent of Decarburization or Carburization. By R. W. Gurry. (T.P. 1470) Observations in the Making and Use of Sulphite-treated Steels. By E. L, Ramsey and L. G. Graper. (T.P. 1476) Diffusion in Metal Accompanied by Phase Change. By L. S. Darken. (T.P. 1479) Engineering Properties of Heat-resistant Alloys. By Howard S. Avery, Earnshaw Cook and J. A. Fellows. (T.P. 1480) Distribution of Manganese and of Sulphur between Slag and Metal in the Open-hearth Furnace. By L. S. Darken and B. M. Larsen. (T.P. 1481)

Jan 1, 1942

By G. R. Love

i\ program has been written which allows fully automatic conversion of data for X-ray intensity, as a function of time, to finished conventional pole figures. The program accepts input data in the serial order in which they are taken and is therefore immediately compatible with automatic data-acquisition devices. From these data taped instructions are prepared for the Calcomp plotter to construct ink-on-paper drawings. Because both Siemens and Norelco pole figure goniometers are used in this laboratory, the program was written for pole figure data obtained from one or more interpenetrating spiral scans during which both the polar angle, @, and the equatorial angle, a, are varied simultaneously and continuously. The reference direction for a scan, that is the point @ = 0 deg, may be chosen coincident with either the normal direction (N.D. figures) or the rolling direction (R.D. figures). In either case the plotted figures are drawn with the transverse direction (a = 0 deg) at the right and the rolling direction at the top. The full, circular, pole figure is drawn as two semicircular figures labeled "front side" and "back side". As presently constituted, the program will also accept data from circular scans taken at constant values of @. In every case the angular coordinates of each intensity entry are generated in the computer from a relatively small number of auxiliary data. The X-ray intensity data are corrected for background scattering by direct subtraction of the intensity measured with 28 set appropriately "off" the Bragg angle. It is possible to enter this correction as an additional spiral scan through the a, @ space; because the background correction does not normally vary rapidly enough to warrant this detailed a determination, the background corrections are entered as one or more auxiliary data. All data are normalized to a multiple of random intensity. The data taken in this laboratory for N.D. figures are normally taken in a reflection geometry from from sheet samples and do not extend beyond <p = 75 deg; for these data random intensity must be determined from separate experiments and entered as auxiliary information. When the auxiliary information is not available, a number is chosen to give intensity values normalized to a scale of 1 to 10. In this laboratory, R.D. figures are based upon hemispherical samples for which data are taken out to @ = 90 deg; for these data random intensity is calculated by direct numerical integration of . sin @ d@ using the trapezoidal rule and the background-corrected values of the input data. Points necessary to the construction of the pole figure are identified by simple linear interpolation between adjacent data points to determine the loci of contour lines. Points lying on a given contour are connected to one another with straight-line segments and the search-calculation-drawing sequence is patterned to assure that different contour lines do not cross, that a single line does not branch, and that lines do not end in space. However, so that there be no ambiguity in the data presentation, all contour lines end at the limits of the input data. Since the curves are constructed of straight-line segments, they are not continuous in their derivatives. However,

Jan 1, 1969

By M. M. Slotnick

IT was once aptly said that a sign of approaching senility is ceasing work on a subject and beginning to talk about it. Perhaps that explains why, after many years in which part of my duties has been the training of college men in various branches of petroleum exploration geophysics, I have now begun to talk about it. In making an outline of what I believe ought to be discussed under the general heading of the title, I found it almost impossible to subdivide the ideas into an ordered set of discrete subjects. Rather, the pertinent remarks seemed to interlock almost everywhere. The consequence is that it will be necessary to start with the conclusions and then try to justify them by jumping back and forth. However, based on the types of men with whom I have had to deal, the subject naturally divides itself into two parts. In the first part, I should like to deal with the case of those undergraduates whose natural bent is toward the physical sciences and who may decide to enter the geophysical fold as a career. The other part will deal with those many men, geologists and engineers for the most part, who have drifted into exploration geophysics by one means or another, and whom it is necessary to train for geophysical work while they are occupied in their routine jobs. Here it may be in point to remark that most men in exploration geophysics at present have been developed from precisely the latter group, and that the problem of training here is of great importance even though, in this paper, it will perforce occupy the secondary place. TRAINING OF A GEOPHYSICIST The outstanding reason for the perplexing problem on the training of a geophysicist is that ideas differ on the answer to the question: "What is a geophysicist?" In any of the scientific "specialties," like physics, for example, it is relatively simple to pigeonhole a man as being qualified to call himself a physicist. That appellation applied to an individual does not mean that he has mastered only the branches of intellectual endeavor usually associated under the broad name of "physics." We expect him also to have a more than mere acquaintance with mathematics and chemistry and some understanding of most of the other sciences. But note this important point-we expect our physicist, whom we have chosen as an example, to be intelligently trained so that, if necessary, he can and will know how and where he can get the proper information on a subject in which he is not a specialist; he will know how to absorb that information and turn it to his uses. It seems to me that this is the outstanding characteristic of a man who can truly call himself a scientist: that he is a specialist in one of the broad branches of science and that he has enough training and discipline in the scientific approach so that, when called upon to do so, he can intelligently absorb knowledge from another bordering science (and all sciences not only border upon one another to some extent, but more often, overlap one another), and

Jan 1, 1941

• Pellets of concentrated iron ore have been smelted in the blast furnace by Armco and the results proved satisfactory. Various percentages of pellet burdens were tried and it has been found that charges up to 70 pct pellets are workable. •In the reorganization of the Department of the Interior, two new assistant secretaries were appointed and the work divided between the four assistant secretaries. C. Girard Davidson will head a division of mineral resources including the Bureau of Mines, Geological Survey, Division of Oil and Gas and Division of Geography. •Germanium, one of the rarest of metals and a wartime strategic material, has been discovered almost in the shadow of the Capitol. The only catch is that the scattered nature of the deposits makes profitable recovery extremely doubtful. Nevertheless, experts have tabbed the concentration in the District of Columbia area the world&apos;s second richest known concentration of the element. • Cakes of mica, weighing up to 500 lb, have been formed at the Colorado School of Mines by a new "cool hearth" method. The process avoids use of crucibles and contains the molten mica in a basin of unmelted raw mixture from which the melt was derived. Crystallization takes place in this melting basin which forms a center pool surrounded by a solid cool mass of the unmelted raw mixture. • William 1. Baxter, of the International Economic Research Bureau, predicts a period of deflation because of war-essential restrictions on consumer credit and materials use. He stated; "the recent prosperity was based mainly on the sales boom in autos, homes, and household accessories." •Two subsidiaries of United States Steel have decided to build four new ships immediately to augment iron ore and limestone carrying capacity on the Great Lakes to meet demands created by the national defense emergency. •The Norfolk and Western Railway is making a complete change over to coal to drive its locomotives. •A national roster of scientific personnel similar to the one used in the last war will be established by the Office of Education, by agreement with the National Security Resources Board. The new unit, the National Scientific Register Project, will make studies of the Nation&apos;s scientific manpower supply and recommend steps to increase the numbers of skilled personnel where needed. •National Lead Co. will start construction immediately of new facilities at St. Louis, Mo., for production of titanium pigments for paints. Producers of titanium pigments have been under considerable pressure to meet all demands from paint manufacturers, particularly for titanium dioxide. •The basic criteria for deferment of reservists in civilian occupations are (1) the Department of Labor List of Critical Occupations, and (2) the Department of Commerce List of Essential Activities, both of which were announced Aug. 3. Fundamentally, the reservist deferred must be engaged in a critical occupation which is necessary to a highly essential activity, and he will be deferred only until he can be satisfactorily replaced in that occupation. A delay in call to active duty, it was emphasized, may not be considered as an indefinite exemption from military service.

Jan 9, 1950