By Stewart, J. B.

THE property at which this work was done consists of a large deposit of potash salts occurring in massive beds of rock salt, overlain by 600 ft. of salt-impregnated shales and marls. It is in the Province of Cataluiia, Spain, about 45 miles from the railway station of Mauresa and about a mile south of Suria. In addition to sinking the shaft, the program of construction work laid out by the European owners (not Spaniards) included a single-track narrow-gage railroad from Mauresa to the mine; one large office building and several large shop buildings, all of brick and concrete with steel truss roofs; two extensive benches for the future recovery plant; and a large village of stone dwellings for employees. The pay-roll showed approximately 1200 to 1500 men employed. After two years' operation, ending early in the autumn of 1920, the shaft had been sunk 325 ft. and still had an equal distance to go to reach the potash; all tunnels for the railroad were done and the road-bed $0 per cent completed; only a little more than the foundations were completed for all the large buildings, and the excavations of the benches were about 75 per cent done-while only a fair start had been made upon the employees' village. This was the state of affairs when the European owners decided to offer this property under a one-year option to an American syndicate, providing that they agreed to carry on the entire building program and to sink the shaft as fast as was consistent with the quality of work which they demanded, for they wished the shaft to endure at least 200 years.

Jan 1, 1926

By E. C. Lee

THE safety of mine workers has received more attention from both State and Federal law-making bodies than any other industry, a fact that shows clearly the hazardous nature of the industry. The last, but by no means the least, of the measures adopted for the protection of mine workers, is workmen's compensation legislation. This is proving to be a powerful instrument for greater safety in the industries, from the fact that special stress is laid not on how the accident happened or who may have been responsible for it, but on how badly the employee is hurt by it. The injured person does not have to employ lawyers to prove his case, because the mere fact of his employment is proof of his right to compensation. The immediate effect of such legislation is the certainty confronting the mine operator that he must pay out large sums for every accident, regardless of its cause, thus adding materially to the cost of the production of his coal. This fact furnished to the operator the strongest incentive to reduce the causes of accidents; not that the operator has ever lacked reasonable consideration for the welfare of his employees and a proper humane interest in their safety, but his engrossment in earning his daily livelihood has been so great that he has not felt that he had the time to devote to the safety of the operation. This time he must now find because of the actual-cash value of the prevention of accidents in his mines. This agency alone proved inadequate to bring about a material improvement because operators have always been willing enough to improve safety conditions when possible to do so within reasonable limits of their financial ability. The requirement in the Workmen's Compensation Laws of several of the States, that the mine operator shall insure as a guarantee of his ability to meet his compensation obligations, has furnished the needed incentive, moral and financial, necessary to the prompt and effective dissemination of a more general knowledge of the causes and

Jan 10, 1917

By Leslie F. Tedsen, Alan E. Flanigan, John E. Dorn

IT is necessary occasionally to use aluminum-alloy sheet where moderately elevated temperatures are encountered. Considerable attention has been directed toward determining the influence of "artificial aging" on the room-temperature properties of the precipitation-hardenable alloys, as testified by numerous company reports and by references 1 to 4. Investigations on the properties at elevated temperatures are few, however,5-7 and have not always covered the range of times and temperatures of greatest interest. The present investigation was instituted to overcome this deficiency. The work was done for the Office of Production Research and Development of the War Production Board, under the supervision of the War Metallurgy Committee, as a part of the "restricted" Project NRC-548. It has been released for publication by the Office of Production Research and Development. As is well known, the high-strength aluminum alloys achieve their remarkable properties as a result of precipitation-hardening. In production they are subjected to a solution heat-treatment followed by quenching, to retain the supersaturated solid solution. The solution treatment is followed by "aging" (precipitation-hardening) either at room temperature or at a suitable elevated temperature. A considerable increase in tensile and compressive yield stresses results from precipitation at room temperature ("natural aging"). Through the elevated-temperature process ("artificial aging") it is possible to obtain values of yield stress considerably higher than those attainable by natural aging. The increase in yield stress is accompanied by a smaller gain in ultimate tensile stress and by a decrease in elongation. During [TABLE I.-Sources of Materials Used in the Testing Program MATERIAL ORIGIN AND TREATMENT 24S-T Alclad.... From Lockheed stock. 24S-RT Alclad... Direct from mill. 24S-T80 Alclad.. 24S-O Alclad from Lockheed stock, solution-heat-treated (925°F., water quench) and aged at 375°F. for t0 t % hour. 24S-T8I Alclad.. 24S-T Alclad from Lockheed stock, plant stretched up t0 I per cent and aged t0 ± % hr. at 375°F. 24S-T86 Alclad.. 24S-RT Alclad from Lockheed stock aged 534 ± 34 hr. at 375°F. 6IS-W (bare).... From Lockheed stock. 6IS-T (bare) 6IS-W (bare) from Lockheed stock aged 8 hr. at 350°F. XB7SS-T Alclad. From Lockheed stock.] the first stages of artificial aging the yield stress increases steadily until it reaches a maximum value. In this condition the material is said to be "fully aged." Further exposure results in "overaging," attended by a steady decrease in yield stress. In the production of the artificially aged materials, temperatures and times are selected to achieve full aging. The following important characteristics are associated with the process: I. The higher the temperature, the more rapidly is the fully aged condition attained.

Jan 1, 1945

By AIME AIME

TWO technical sessions, an excursion through the Midwest refinery and a smoker, marked the first day of the meeting of the Petroleum Division at Casper, Wyo., on Aug. 28. Ninety-nine members and guests registered and there was an excellent attendance at 'all functions. The -local committee under the general chairmanship of J. C. Lindsay, general manager of the Western Pipe Line Co., had made every possible arrangement for the convenience and comfort of the visiting members and the Program Committee under E. L. Estabrook, vice-chairman of the Petroleum Division, had brought together a most interesting series of technical, papers. The meeting centered mainly on the various features of the Salt Creek field but there were also contributions from the technology of production in California, the Mid-Continent, and the Texas fields. The opening session was called to order by Mr. Estabrook at the Townsend Hotel on Friday morning. The members and visitors were welcomed appropriately by Ex-Governor B. B. Brooks, president of the "Rocky Mountain Oil and Gas Association, who recalled the changes that had taken place as Casper, a frontier cow town, became a thriving oil metropolis. F. Julius Fobs, chairman 'of the Petroleum Division, responded and then took the chair. He introduced H. Foster Bain, Secretary of the Institute, who expressed the regret of those members members who found it impossible to stop over en route to Salt Lake City and his own pleasure at meeting with the Division in the field. Following these introductory ceremonies the technical session began with a "Sketch of the Geological Formations of Central Wyoming," presented by J. G. Bartram of the Midwest staff. It was brief and to the point and contributed greatly to the easy under¬standing of the succeeding papers by those unfamiliar with the region. The talk was illustrated by a large scale columnar section -and a copy of the excellent, geological map of the State recently issued by the U. S. Geological Survey.

Jan 1, 1925

By Edwin H. McKee

Eruption of rhyolitic ash-flow tuffs in the area of the McDermitt (Cordero) caldera began about 17.4 million yr (m.y.) ago and continued for about 1.5 m.y. During this period of silicic eruptions, a circular area about 30 km in diameter collapsed to form a caldera that subsequently filled with sedimentary and volcanic rocks. A total of more than 200 km30f silicic rocks was erupted from the volcano. The final phase of igneous activity, about 15.0 m.y. ago, included resurgent doming and intrusion in the south-central part of the caldera. Three to 4 m.y. later (-1 2 m.y. ago), hydrothermal solutions using the northern part of the caldera ring fractures as conduits deposited silica, cinnabar, pyrite, alunite, and other minerals in tuffaceous lake beds and volcanic rocks accumulated within the caldera. The ore-forming solutions may have been a residuum from the silicic magma, or connate water, or ground water heated by the still-hot resurgent magma in the central part of the caldera. The source of the mercury and other elements has not been identified.

Jan 1, 1977

By Kyle Wightman

INTRODUCTION CRA Limited is the largest mining group in Australia by value of sales and the second largest company in Australia in terms of share market capitalisation. In the past 25 years, CRA, its predecessors and affiliates have been involved in a number of mining and further processing developments in Australia and elsewhere. Many of these have been financed using project financing techniques. These include Comalco's development of the Weipa bauxite deposits in Northern Queensland in the late 1950's, the Hamersley iron ore developments in the Pilbara region of Western Australia in the mid 1960's, the Queensland Alumina Limited alumina refinery in Gladstone, Queensland, at about the same time, and the Bougainville copper project in 1969/70. In the past three years CRA has again utilised project financing techniques to fund its Tarong steaming coal project in Queensland, the Blair Athol steaming coal project also in that State and CRA's interest in the Argyle diamond project in the Kimberley region of Western Austrlia. PROJECT FINANCE DEFINED Nevitt Definition Nevitt's is the most frequently quoted definition - "A financing of a particular economic unit in which a lender is satisfied to look initially to the cash flows and earnings of the economic unit as the source of funds from which a loan will be repaid and to the assets of the economic unit as collateral for the loan." Risk and Balance Sheet Treatment It is important to focus in more detail on two aspects of project financing, risk and balance sheet treatment. The assessment of the various elements of risk in a project and the sharing of that risk between sponsors and lenders is the most critical feature. At one end of the spectrum is full absorption of risk by the sponsor(s). This can be described as "on risk" or "on credit" or "full recourse" to the sponsor(s) and is effectively a corporate financing. At the other end of the spectrum the lenders absorb the whole risk in a non-recourse financing which is "off risk" or "off credit" for the sponsor. The other aspect is the sponsor's balance sheet treatment. If the balance sheet of the economic unit undertaking the project and the financing need not be consolidated into the balance sheet of the sponsor (because ownership does not exceed 50%) then the financing may be described as off-¬balance sheet. If consolidation is required then the financing is described as on-balance sheet. Most project financings involve some recourse to the sponsor, i.e. they are limited recourse. Very few are non-recourse or off credit to the sponsor. Limited recourse financings may be on-balance sheet although many may also be off-balance sheet insofar as consolidation is concerned. However, sponsor support may very well be a contingent liability to the sponsor and require disclosure by way of note to the balance sheet should consolidation not be required. CORPORATE FINANCE CONTRASTED A financing which is on credit or full recourse to the sponsor, whether it is directly borrowed or guaranteed by that sponsor, is a corporate financing. Lenders will tend to base their credit assessment on a historical assessment of the sponsor's activities and its financial results rather than an assessment of the project or a detailed assessment of the future activities and prospects of the sponsor. PROJECT FINANCE - A BORROWER'S PERCEPTION Although CRA could choose to arrange all finance on a corporate basis (except perhaps for the very largest projects or acquisitions), project financing techniques provide a number of specific advantages which CRA has noted and which should be carefully considered by a project sponsor. Advantages

Jan 1, 1985

By K. Osseo-Asare

The thermodynamics of solid-aqueous solution equilibria up to 200°C In the systems Me-NH3 H2 0 (Me=Cu, Ni, Co) are summarized with predominance area diagrams generated with the DIAGRAM computer program. The implications of the diagrams to ammonia hydrometallurgy are discussed.

Jan 1, 1981

By H. V. Flagg

OPERATION of a modern steel plant presents a curious anomaly. Large-scale operations, in which large volumes or heavy weights of materials are involved, are not usually subject to close control or narrow specifications. On the other hand, operations that call for a high degree of precision are usually carried out under carefully controlled conditions with delicate, precise machinery and tools, and production is made secondary to quality. In a modern steel mill both extremes are taken as a matter of course. A strip mill making auto-body sheets must supply its customers with sheets that all come within a tolerance of plus or minus 0.003 in. in gauge at any point from side to side or end to end, and without blemishes either of color or surface. Sheets that were considered par excellence as recently as ten years ago could not even find a market today. Such exacting requirements have made necessary a nicety of control that approaches the watchmaker's art. Notwithstanding this necessity for precision, the scale of operation is stupendous.

Jan 1, 1940

By J. R. Johnson

ZIRCONIUM'S corrosion rate by reactor fuel solutions increases with increasing reactor power. It is believed that the protective oxide film is affected by radiation damage. Observations of the

Jan 1, 1959

By RALPH HAYES SWEETSER

IRON ore and bituminous coal are the two basic raw materials for the whole iron and steel industry. The ore furnishes the iron and is absolutely necessary-all iron and steel products come directly or in- directly from the iron ores. The bituminous coal furnishes the carbon needed for the smelting of the ores and for the fuel used in all the processes of iron and steel manufacture. The necessary carbon could be furnished in some other form besides bituminous coal. In fact, it is only since the Civil War that bituminous coal has been the chief source of the carbon for metallurgical fuel. For many years only charcoal made from the forests furnished the carbon for smelting iron ores. About 90 years ago, anthracite coal was first used as blast-furnace fuel and for many years continued to be the chief blast furnace and steel making source for carbon. Even in my own blast-furnace experience, I have used charcoal in Canada and anthracite in Pennsylvania for smelting ores in an iron blast furnace. Bituminous coal, now almost exclusively the source for the carbon used in smelting iron ores, also furnishes most of the heat used in the steel-making processes. It is seldom used in blast furnaces in its natural condition, hut is first coked in beehive, or in by-product coke ovens; such bituminous coal is called "coking coal." Bituminous coal that is suitable for making the producer gas used in the open-hearth steel process is called gas coal. Any bituminous coals suitable for making blast-furnace coke or foundry coke, or that can be satisfactorily used for making producer gas, are classed as metallurgical coals and as such are to be considered in my proposed plan for the evaluation of metallurgical coals. According to Bureau of Mines Bulletin No. 449 these coals comprised 22 per cent of the bituminous coals mined in this country in 1923.

Jan 1, 1926

By E. T. Turkdogan, P. Grieveson

Experimental results are presented for the rate of solution of nitrogen in a iron in the temperature range 750° to 873°C and in 6 iron in the temperature range 1410° to 1470°C. It is shown that the rate controlling process is diffusion of nitrogen into the iron. The diffusiting of nitrogen in a and 6 iron is derived from the results, and the temperature dependence of the diffusivity is represented by the equation D = 7.8 x e- 18,900/RT sq cm per sec. The solubility of nitrogen in a and 6 iron, in equilibrium with 1 atm pressure of nitrogen, has been measured. Using these results and other available data, it is found that the variation of the logarithm of nitrogen solubility with the reciprocal of absolute temperature is nonlinear. In an Appendix, some results of Darken and Smith are presented for the rate of solution of nitrogen in iron using ammonia + hyidrogen mixtures. These data also support the view that diffudsion of nitrogen in iron is the rate-controlling process when ammonia + hydrogen mixtures are used. A considerable effort has been made to obtain data on the solubility1-5 and diffusivity of nitrogen in a iron6-l2 because an understanding of the effect of nitrogen on the properties of steel must be based on an accurate knowledge of the properties of nitrogen in pure iron. However, no information is available concerning the kinetics of solution of nitrogen in a and 6 iron. Recently the authors13 have investigated the rate-controlling mechanism operating in the kinetics of solution of nitrogen in y iron. This study was directed to determine the rate-controlling processes for similar reactions with a and 6 iron as well as to establish values for the solubility of nitrogen in equilibrium with nitrogen gas in a and a iron. EXPERIMENTAL The procedure used in experiments to determine the rate of solution in cylindrical iron rods was the same as that described in a previous communication.13 Ferrovac E grade iron used in all experiments contained the following impurities in weight percent: C, 0.005; Mn, 0.001; P, 0.002; S, 0.006; Si, 0.006; Ni, 0.025; Cr, 0.002; V, 0.004; W, 0.02; Mo, 0.01; Cu, 0.001; Co, 0.01; 0, 0.007. After cleaning the surface, the iron rods were treated in an atmosphere of purified hydrogen for 17 hr before the reacting gas was introduced for known experimental times. After quenching, the samples were sectioned radially and analyzed for nitrogen. In addition to experiments using rods, iron foils were used in the measurements of solution rates of nitrogen in a iron. The foils of two different thicknesses were prepared by cold rolling Ferrovac E grade iron cylindrical rod to 0.051 and 0.152 cm. Foil samples were used in a rectangular form 5 cm long and 1.25 cm wide. The specimens were thoroughly cleaned of surface oxide with fine emery cloth and degreased with carbon tetrachloride immediately before entry into the furnace. The experimental procedure was the same as that used in the study with rods. At the completion of an experiment, the foil samples of the nitrogenized iron were analyzed for nitrogen after discarding 0.3 cm from the perimeter of the specimen. Iron foils were nitrogenized and denitrogenized in the a and 6 range with a gas mixture of 95 pct N and 5 pct H for times varying from 5 min to 2 hr. Results obtained for the average composition of nitrogen in iron for these experiments are presented in Fig. 1. Prior to the denitrogenization experiments, the samples were saturated with nitrogen at 1000°C and 0.67 atm N, giving a uniform nitrogen concentration of 0.0204 pct. According to the known a-y phase boundary in the Fe-N system,14 this composition lies within the ferrite region at temperatures 750" to 850°C. Use of this initial nitrogen content insured that reaction occurred between the gas and a single solid phase, a iron. Examples of the results for the mean concentrations of nitrogen in cylindrical iron rods, 0.356 cm radius for both the a and 6 ranges are given in Fig. 2. Typical examples of the results obtained for the radial distributions of nitrogen in rods are presented in Fig. 3. It appears that the results for radial distributions can be extrapolated to constant surface compositions which agree with the equi-

Jan 1, 1964

By H. B. Pulsifer

This paper outlines a method for rapid production of flat,, granular surfaces on many of the medium hard alloys. Grinding wheels and fabrics on wheels are not used; the purpose is accomplished by rubbing on emery papers and on fine abrasives heaped on hand boards. The advantages of chromic acid in the solutions for etching nickel and copper alloys are explained. Steels may require an additional step in the mechanical smoothing owing to the lack of an ideal etchant. Chloric acid is a rapid etchant for steel. Thirty-six photomicrographs illustrate the steps in smoothing and the clearness with which structures can be rapidly exposed. New structures in low-carbon steels are announced. After a little practice, many materials can be finished within two or three minutes. CUPRONICKELS In the previous papers on the metallography of copper and magnesiurn which the author has presented to this Institute there has been an attempt to demonstrate the advantages of minimizing the mechanical work of surfacing and depending more on chemical means; the present paper continues the research into a still wider field. It is obvious that the success of a chemical method for smoothing and etching depends almost entirely on the use of a suitable reagent. The etchant must remove the surface granulations and outline the structures. A very special type of reaction between reagent and metal must be displayed. Promiscuous corrosion or the intensification of the attack about local couples formed by impurities or components must not be in evidence. There are several reagents that etch highly polished nickel and copper alloys very well. Acidified ferric chloride solutions, concentrated and dilute nitric acid solutions, and nitric and acetic acids in acetone have been used to good advantage for the purpose. However, if they are expected to etch rather deeply—that is, smooth as well as characterize— the results may be far from satisfactory. Advantages of Chromic Acid In a protracted series of experiments it has been found that the addit,ion of chromic acid may be of the most surprising benefit. The function

Jan 1, 1929

By H. B. Pulsifer

This paper outlines a method for rapid production of flat,, granular surfaces on many of the medium hard alloys. Grinding wheels and fabrics on wheels are not used; the purpose is accomplished by rubbing on emery papers and on fine abrasives heaped on hand boards. The advantages of chromic acid in the solutions for etching nickel and copper alloys are explained. Steels may require an additional step in the mechanical smoothing owing to the lack of an ideal etchant. Chloric acid is a rapid etchant for steel. Thirty-six photomicrographs illustrate the steps in smoothing and the clearness with which structures can be rapidly exposed. New structures in low-carbon steels are announced. After a little practice, many materials can be finished within two or three minutes. CUPRONICKELS In the previous papers on the metallography of copper and magnesiurn which the author has presented to this Institute there has been an attempt to demonstrate the advantages of minimizing the mechanical work of surfacing and depending more on chemical means; the present paper continues the research into a still wider field. It is obvious that the success of a chemical method for smoothing and etching depends almost entirely on the use of a suitable reagent. The etchant must remove the surface granulations and outline the structures. A very special type of reaction between reagent and metal must be displayed. Promiscuous corrosion or the intensification of the attack about local couples formed by impurities or components must not be in evidence. There are several reagents that etch highly polished nickel and copper alloys very well. Acidified ferric chloride solutions, concentrated and dilute nitric acid solutions, and nitric and acetic acids in acetone have been used to good advantage for the purpose. However, if they are expected to etch rather deeply—that is, smooth as well as characterize— the results may be far from satisfactory. Advantages of Chromic Acid In a protracted series of experiments it has been found that the addit,ion of chromic acid may be of the most surprising benefit. The function

Jan 1, 1929

By H. D. Outmans

The author applies the theory of hydrodynamic stability to fluid flow in porous media and concludes that the displacement of miscible liquids is stable if the stability coefficient, as defined by Eq. 19.2 or Eq. 27.0, is positive. The conclusion is invalid, however, since it is based on a faulty argument. To demonstrate this, the reader is referred to Eqs. 4.1 through 4.5 of the paper which describe, in differential form, the first-order disturbances c, u, v, w and p. In these same equations, cx, cz, gl, g3 and are functions of the stable concentration c. This concentration c is known and depends on x, z and t (the author assumes cy = 0). It follows that cx, cz, gl, g3 and µ are also functions of x, z and t. With this in mind, we turn to Eqs. 8.1 through 8.5 which were derived from Eqs. 4.1 through 4.5 by substituting Eq. 6.0. The significance of this substitution is that the author thereby limits the solutions of Eqs. 4.1 through 4.5 to equations of the form of Eq. 6.0. Eqs. 8.1 through 8.5 represent an infinite linear system with five unknowns: c, u, v, w and p. The coefficients cx, cz, gl, g3 and µ in this system are known at each point and at each instant; the coefficients containing derivatives of f are unknown. If this infinite linear system in c, u, v, w and p is to have a nontrivial solution, then it is indeed necessary (as the author states) that the determinant of the coefficient matrix of Eqs. 8.1 through 8.5, i.e., ( A 1, be equal to zero. This condition, however, is not sufficient. A non-trivial solution exists if, and only if, the rank of the coefficient matrix of the entire infinite system is smaller than five. In other words. all minors of order five must vanish and only if all the coefficients in Eqs. 8.1 through 8.5 are constant is this equivalent to the condition |A| =0. Constant coefficients means that gl, g3 and µ, for instance, are constant; and, since they depend on c it follows that c must be constant. We conclude that the condition I A I = 0, on which the author bases his calculations, is necessary and sufficient for a nontrivial solution only if the concentration c is constant. In other words, the author does not investigate the stability of a miscible displacement but, rather, only the stability of the flow of a homogeneous liquid. Using the initial condition and the fact that the coefficients are constant, we find

By R. I. Jaffee, H. P. Nielsen

In recent years much attention has been given to high melting alloy systems. It has been of interest in this respect to investigate the alloys of platinum and tungsten, which were known from the literature to have very high melting points up to about 50 pct tungsten, but about which little had been published on the high-tungsten side of the system. Powder metallurgical methods were used throughout this investigation for the preparation of the alloys, utilizing electrical sintering techniques such as are used for tungsten and molybdenum. In the course of the work it was found desirable to determine fusion temperatures of the alloys, and it was possible from these and other data to draw a tentative constitutional diagram (solidus, mostly) applicable to the high-temperature part of the system. No attempt was made to determine solid solubility vs. temperature data, nor to investigate the lower temperature transformations in the solid state. Data on the microstructure, hardness, and a note on oxidation resistance of the sintered alloys were obtained. Past Work Miillerl determined liquidus temperatures of platinum-rich alloys to 50 pct tungsten, using a radiation method employing a photoelectric cell, and found that the melting points increased progressively from I771 C for platinum to 2350°C for the 50 pct alloy. Microscopic evidence by Miiller that complete solid solutions exist to 50 pct tungsten was not checked by Kremer2 who, according to Vines and Wise,3 found that "although the 8 pct tungsten alloy was a solid solution, the 26 pct tungsten alloy contained a eutectic or an intermediate phase." Hultgren and Jaffee4 using X ray methods found continuous solid solutions to at least 33.6 pct tungsten (35 at. pct) after annealing in vacuum for 6 days at I000 C. Vines and WiseS report work communicated to them by E. C. Rhodes on wrought alloys to 7 pct tungsten, which showed that tungsten hardened platinum extremely rapidly, and was one of the most potent hardeners of the binary additions to platinum. Considerable quantities of 4 pct tungsten platinum wire have been produced for grids in radar tubes and for aircraft spark plugs. Some of the alloy for the latter application is made by sintering, the remainder by smelting and casting. Materials The platinum powder used in this work was kindly supplied by the Research and Development Laboratory of the Owens-Corning Fiberglas Corp., Newark, Ohio. It was prepared from scrap platinum. After dissolving in aqua regia and evaporating almost to dryness, the solution was worked up several times with concentrated HC1. The resultant platinic chloride was diluted considerably, and metallic zinc was added, which precipitated the platinum in a very finely divided form. After dissolving the

Jan 1, 1949

By Herluf P. Nielsen, Robert I. Jaffee

IN recent years much attention has been given to high-melting alloy systems, It has been of interest in this respect to investigate the alloys of platinum and tungsten, which were known from the literature to have very high melting points up to about 50 pct tungsten, but about which little had been published on the high-tungsten side of the system. Powder metallurgical methods were used throughout this investigation for the preparation of the alloys, utilizing electrical sintering techniques such as are used for tungsten and molybdenum. In the course of the work it was found desirable to determine fusion temperatures of the alloys, and it was possible from these and other data to draw a tentative constitutional diagram (solidus, mostly) applicable to the high-temperature part of the system. No attempt was made to determine solid solubility vs. temperature data, nor to investigate the lower temperature transformations in the solid state. Data on the microstructure, hardness, and a note on oxidation resistance of the sintered alloys were obtained. PAST WORK Müller1 determined liquidus temperatures of platinum-rich alloys to 50 pct tungsten, using a radiation method employing a photoelectric cell, and found that the melting points increased progressively from 1771°C for platinum to 2350°C for the 50 pct alloy. Microscopic evidence by Müller that complete solid solutions exist to 50 pct tungsten was not checked by Kremer2 who, according to Vines and Wise,3 found that "although the 8 pct tungsten alloy was a solid solution, the 26 pct tungsten alloy contained a eutectic or an intermediate phase." Hultgren and jaffee4 using X ray methods found continuous solid solutions to at least 33.6 pct tungsten (35 at. pct) after annealing in vacuum for 6 days at 1000°C. Vines and Wise3 report work communicated to them by E. C. Rhodes on wrought alloys to 7 pct tungsten, which showed that tungsten hardened platinum extremely rapidly, and was one of the most potent hardeners of the binary additions to platinum. Considerable quantities of 4 pct tungsten platinum wire have been produced for grids in radar tubes and for aircraft spark plugs. Some of the alloy for the latter application is made by sintering, the remainder by smelting and casting. MATERIALS The platinum powder used in this work was kindly supplied by the research and Development Laboratory of the Owens-Corning Fiberglas Corp., Newark, Ohio, It was prepared from scrap platinum. After dissolving in aqua regia and evaporating almost to dryness, the solution was worked up several times with concentrated HCI. the resultant platinic chloride was diluted considerably, and metallic zinc was added, which precipitated the platinum in a very finely divided form. After dissolving the

Jan 1, 1948

By W. S. CAYPLESS, H. O. Hofman, E. E. HARRINGTON

1. INTRODUCTION. AT the Lake Superior meeting, September, 1904, Messrs. A. Gibb and R. C. Philp presented a paper entitled " The Constitution of Mattes Produced in Copper Smelting,)' in which they concluded that ferrous and cuprous sulphides formed the chemical compound, 5 Cu2S, fee. They arrived at this inference from the observed fact that a matte containing Cu2S, 90.4, and Fee, 9.6 per cent (or, in round figures, Cu2S, 90, and Fee, 10 per cent.), did not contain any metallic copper, while one with more than 10 per cent of FeS readily dissolved copper, and with less than this amount retained copper in mechanical suspension. Although they determined the melting-points of five mattes containing from 32.6 to 80.1 per cent of copper, they did not draw a freezing-point curve, as the necessary apparatus was not available. A microscopical examination of 11 polished samples, gave them a grayish-black field of very uniform appearance, except that 5 of the specimens showed the presence of metallic copper. The object of the present investigation was to supplement the above paper by drawing the freezing-point curve of the series ferrous sulphide cuprous sulphide, and to see how the constitution could be further, revealed by microscopical work. The results obtained lead to conclusions very different from those of Gibb and Philp. While their paper bears the date 1904, it was published only in 1906.2 In the meantime, Bolles3 had presented his paper, "The Concentration of Gold and Silver in Iron Bottoms." The raw material which formed the basis of the research was a matte containing Fe, 61.68, and Cu, 11.20

Jan 1, 1907

By Vince Poxleitner, John Delaney

Introduction In the mining industry, comminution typically begins in the mine with a blast of explosive to break rock so that it can be handled by the avail- able equipment. Though the breaking of the rock is essential for material handling in the mine and plant, this is not the only reason for ore reduction in the mineral industry. Comminution is primarily required to liberate minerals from ore so that they can be concentrated into valuable products or to prepare minerals, such as talc, for market as mined. The size of the equipment used for comminution ranges from small to massive. Regardless of equipment size, the power required to reduce the rock is a major expense. Years ago, mineral deposits could be mined more selectively and required less grinding to produce saleable products. However, as richer deposits were depleted, it has become necessary to mine low-grade deposits, with the valuables dispersed throughout the rock. Comminution equipment evolved in physical size and capacities to meet the new mine and process requirements. A modern, modestly sized mining operation, with a capacity of 25.000 TPD may use crushers two stories high weighing over a million pounds, SAG mills 36 feet in diameter driven by dual motors putting out 10.000 horse- power, and ball mills over 16 feet in diameter . Because of the increasing size and weight of modern equipment, the builder is faced with the problems of erecting massive foundations and field assembling equipment on these foundations. As equipment costs and plant construction costs increase, builders are finding that owners are asking for more detailed progress and cost data. Comminution construction projects are generally classified as grass roots plants or expansions or modifications to existing plants. It is estimated that 60-702 of the jobs involve existing plants. Today ' s costs for construction of small, new comminution plants can reach tens of millions of dollars; larger plants can cost hundreds of millions of dollars. Modifications, on the other hand, usually run from a few thousand to several million dollars. Though many problems are common to the construction of both new plants

Jan 1, 1982

By Samuel B. Christy

At the last meeting of the Institute, several contributions were made to the subject of miners' aid funds. Such matters will always form important factors in the administration of large industrial enterprises. From the frequently remote and isolated position of mining properties, it is a subject that often forces itself upon the attention of the mining engineer. Local conditions are usually so variable that no single method can be found equally well adapted to all localities. At the same time, a study of different types is often suggestive and valuable, and it is with this in view that these notes are presented. The Miners' Fund of New Almaden is a remarkably successful example of what may be done for miners by a wise and at the same time firm management, by simply directing their own efforts and without incurring any great expense to the stockholders,—a practical consideration not without importance in most cases. The quicksilver mines of New Almaden are situated at a distance

Jan 1, 1885

By AIME AIME

EVEN though most of the program of the joint meeting at Easton, Pa., on Oct. 30 to Nov. 1. was devoted to the interests of combustion engineers rather than to coal-mining engineers, nevertheless the A.I.M.E. Coal Division was well represented, with 83, or close to one third of those in attendance giving this as their affiliation. The fuels division of the American Society of Mechanical Engineers had 108 representatives, and an equal number reported no society affiliation. Added to the men's total registration was that of some twenty ladies so the total attendance was in the neighborhood of 325, exceeding that of the last two joint meetings, at Birmingham and Columbus, and equaling the 1938 crowd at Chicago.

Jan 1, 1941