By H. Sigurdson, T. V. Cherian, C. H. Moore

The phenomenon of recovery of cold-worked metals is interesting not only because of its practical importance but also because of its fundamental significance in solid state reactions. Although extensive investigations1,2 have already been made in an attempt to discover the mechanics of the recovery process, many of the observations have not yet been satisfactorily correlated to provide a completely consistent model for the process. The wide differences in the recovery rates of various properties can be cited as a typical example of one of the difficulties that are encountered. Frequently, for example, the electrical resistance will have almost completely recovered before any recovery in tensile strength can be detected. Of course, such differences in the recovery rates of different properties might be explained by assuming that each property is a unique function of the work-hardened state, and consequently each property exhibits its own unique recovery rate. The assumption that different properties are uniquely related to the work-hardened state cannot be denied. On the other hand, the properties that recover at different rates often exhibit more or less parallel changes upon work-hardening. This suggests that the microstructural changes attending recovery are not exactly the reverse of the changes attending work-hardening. Several types of imperfections must be postulated in order to account for this apparent anomaly. The different recovery rates for various properties, then, are due to the different recovery rales of the type of imperfection to which each property is most sensitive as well as the unique dependence of each property on the cold- worked state. This concept assumes that a simple model of the work-hardened state consisting only of one type of imperfection, such as Taylor's type of dislocation patterns, is inadequate to cope with the diversified phenomena attending work-hardening and recovery. Although current models for the work-hardened state are not useful for describing all aspects of the recovery process, the general trends of the recovery of each postulated type of imperfection as a function of time and temperature should be at least qualitatively deducible from the rather well developed laws of kinetics of reactions in the solid state. Consequently, recovery data might prove useful for elucidating some aspects of the complexities of the work-hardened state of metals. A preliminary attempt to study work-hardening by investigating recovery rates of cold-worked metals is outlined in the following pages of this report. Experimental Procedure Many properties recover when cold-worked metals are annealed below their recrystallization temperature. Therefore, electrical resistivity, thermal electromotive force, X ray diffraction line widths, X ray diffraction line intensities, elastic spring back, density and other physical and chemical properties have been used to study the recovery process. Major interest, however, has generally been directed toward the recovery of the mechanical properties such as hardness, yield strength, and tensile strength. But a search of the literature suggests that the effect of recovery on the true stress-true strain curve has been neglected, in spite of the current recognition of the fundamental importance of such an investigation. An investigation on the effect of recovery treatment on the true stress-true strain curves in tension, therefore, was undertaken in the present study. Commercially pure aluminum (99. + pet Al) in the form of 0.100 in. thick rolled sheet of 2S-O aluminum alloy was selected as the material for this investigation because rather extensive correlatable data are already available on the recovery of some of its properties. Tensile specimens having a 6 in. long gauge section and a uniform reduced section width of 0.500 in. were machined from the sheet in accordance with a design that has previously been reported.3 All specimens were selected with their axes aligned in the rolling direction. In order to eliminate the effects of previous work-hardening and the effects of machining, the specimens were annealed for 15 min. at 750°F before testing. During tensile testing the loads were measured by means of a proving ring (sensitive to 1/2 lb) in series with the specimen.4 Strains were determined from the extension of a rack and pinion strain gauge sensitive to a strain of + 0.0001. The stress was recorded as the true stress, namely

Jan 1, 1950

By S. A. Mersol, C. T. Lynch, F. W. Vahldiek

The room-temperature Knoop hardness of single -crystal titanium diboride has been determined. Variations in microhardness have been correlated with orientation and structural imperfections in the crystals. Maximum differences in hardness values of 750 kg per sq mm with respect to orientation and 450 kg per sq mm with respect to substructure were found. The effects of etchants, load on indenter, and degvee of cracking of indentation were studied. The average hardness was determined as 2800 kg per sq mm on the as-grown crystals. Annealing increased the average hardness to 3375 kg per sq mm. ThE microhardness of polycrystalline titanium diboride approximating the stoichiometric composition TiB, has been studied by several investigators. The values for the Knoop hardness number range from 2710 kg per sq mm (Khn = 2710 kg per sq mm) to 3400 kg per sq mm.'-4 Samsonov et al.' reported a Vickers hardness number of 3400 kg per sq mm (Vhn = 3400 kg per sq mm) at 120-g loads for a 98 pct Ti + B material of 96 pct theoretical density. Recently Dunegan measured the Vickers hardness and obtained 2060 kg per sq mm with a 10-g load (Vhnlo = 2060 kg per sq mm), 1425 kg per sq mm for Vhnloo, and 1320 kg per sq mm for Vhnlooo. We have obtained a Khnloo = 3000 * 350 kg per sq mm for hot-pressed polycrystalline TiB2 that was 99.1 pct Ti + B and 96.6 pct of theoretical density. The present investigation has been made on single-crystal titanium diboride boules, and is believed to be the first such study on TiB, crystals of known orientation. EXPERIMENTAL The single crystals were prepared by a Verneuil-type process using an electric arc by the Linde Division of Union Carbide Corp. The largest specimens were 6 mm in diameter by 12 mm long. The crystals were of theoretical density (4.50 g per cm3) with a Ti + B content of 99.8 pct. The major impurities present were: 0.03 pct (by weight) 0, 0.06 pct C, 0.01 pct Si, 0.05 pct Fe, 0.01 pct Cr, and 0.01 pct Ni. The crystals were boron-rich, the average boron content being 31.S7 wt pct (stoichiometric value is 31.12 wt pct), and titanium-poor, the average titanium content being 68.2 wt pct (stoichiometric value is 68.88 wt pct). Titanium was determined gravimetrically by cupferron precipitation and boron by titration of H3B03 from a NaOH-fused specimen after removal of titanium with BaC03. The outer edge of the boule accounted for some of the excess boron. An electron-microprobe analysis showed that the titanium content increased from 60.0 wt pct at the edge to 68.5 wt pct at D, ~ 1000 p, where D, = distance from outer edge (see Fig. 5). X-ray measurements indicate that the boules are single crystals with considerable substructure. Upon etching this structure is seen in the form of a Widmanstatten-type rhombohedral line pattern in the basal (c) plane and a parallel "lines" pattern in the prism (a) planes. A typical WidmanstHtten-type pattern is seen in in Fig. 1. Electron microscopy reveals that the lines are less than 1 p across, which does not allow direct electron probe or microfocus X-ray determination of their composition. The identity of the second phase has not been established. It might be a higher boride or a nonstoichiometric TiB2. On annealing above 2200°C the precipitate is dispersed and dissolves in the matrix. The best etchants found were HF/HNO/HO, KF(CN)$NOH/HO (Murakami's Etch), and A large number of other etchants were previously Studied. The acidic etchant produced an acicular or "needles" pattern in the (a) planes which is an etchant effect on the "lines" pattern.

Jan 1, 1965

By C. D. Hall

This paper may be divided into two main parts: (1) analysis and data to show that Eq. 6 adequately correlates the authors' experimental data, and (2) the assertion that Eq. 20 "should permit scale-up with data taken from one pipe diameter for Newtonian, inelastic non-Newtonian, and viscoelastic fluids, such as dilute polymer fracturing fluids, which produce considerable pressure reductions." The authors might well recommend that this broad grouping of fluid types could be correlated by using Eq. 6 (requiring data from at least two pipe diameters). On the other hand, Eq. 20 is only shown to be adequate for conditions within the range of the present data set. Specifically, predictions by Eq. 20 for diameter scale-up to casing sizes would give larger deviations than implied in Table 2, and scale-up for some other fluids that give large drag reduction could be grossly in error. The description of a class of fluids "which produce a diameter family of straight parallel lines on a log (d?p/4L) vs log (8 v/d) plot. . ." defines a necessary condition for using Eq. 6; i.e., that s shall be constant for each fluid. The proposal that Eq. 20 is applicable to turbulent flow of such fluids is equivalent to saying that the spacing of these parallel lines, with A being constant, will be found to correspond to m = -1.20 for all such fluids. Table 1 shows the values of m derived from data on 16 non-Newtonian fluids. The key statement of this paper is that the diameter exponents "do not vary significantly from . . . -1.20." In statistical terms, this says that the m value for each fluid, which was obtained from all the measurements made on that fluid. has not been shown to be different from the arithmetic mean of the m values for the 16 fluids tested. This implies that the group mean, -1.20, is a more reliable value to use for an individual fluid than is the m value derived from the data on that fluid alone. No statistical test is described to support the key statement that the diameter exponents do not vary significantly from -1.20. Such a test would have to take into account that each individual m value is shown to correlate the pressure gradients for its fluid, with only about 3 percent standard deviation over the diameter range covered. That is, the m value is not the result of a single independent measurement. Thus, it would not be sufficient, or valid, to compare the deviation of one of the m values with the variance of the 16 values of m about their mean. An alternative interpretation of the key statement is that the diameter exponents do not vary appreciably from -1.20; i.e., that using -1.20 does not cause serious inaccuracy. Table 2 seems to be offered in support of such an assertion. However, such a statistical treatment (1) is unnecessary and (2) cannot lead to any valid scale-up generalization. The amount of error introduced by using a 1"wrong" value of diameter exponent — i.e., -1.20 instead of m — is determined by Eq. 6. The ratio of the pressures predicted by Eqs. 6 and 20 for scale-up from ds in small pipe to d, in casing is The pressure for 30-percent calcium carbonate slurry (m = -1.112) in 10-in. ID pipe would be predicted 30 percent higher by Eq. 6 than by Eq. 20, if based on tests in 0.5-in. ID pipe. The data set tested in Table 2 represents only a limited sample of pipe diameters (ratio of about 4:l) out of the population of diameters that would

Jan 1, 1970

By M. L. Hammond, G. M. Bowers

Silicon dioxide films have been prepared on silicon wafers by the oxidation of SiH, near 400°C. Results previously reported by Goldsmith and Kern7 have been qualitatively corrobovated using a system of different geometry, and significantly greater deposition rates have been achieved. The deposition rate is independent of thickness and nearly independent of the O2/SiH, ratio over a wide range; however, the rate is strongly temperature-dependent. The structure of the deposit depends upon the cleanliness of the substrate, and the electrical field strength of the deposited oxide depends upon the nature of the electrodes. MULTILEVEL interconnects in integrated circuits using aluminum metallization require an insulator that can be deposited at low temperature. Because the A1-Si eutectic is only 577°C, the maximum deposition temperature must be below about 500°C to prevent reaction of the aluminum with the silicon and with other materials in the integrated circuit. Many methods of depositing insulating films of SiO, and other dielectrics have been reported'-6 but the technique described by Goldsmith and Kern7 offers the simplest method of preparing SiO, films. The technique involves the reaction of SiH, and 0, to form SiO, films in the 300" to 500°C temperature range. Previous work using this gas system has been reported8 and the initial development work at Philco Microelectronics was done at the East Coast R&D Laboratories. 9 This paper corroborates some of the results of Goldsmith and Kern,7 shows that much higher deposition rates can be obtained than previously reported, and presents some observations on the structure of deposited SiO, films. EXPERIMENTAL CONDITIONS Fig. 1 is a schematic drawing of the apparatus used in this study. It differs from that of Goldsmith and Kern in that 1) the gases are mixed before they enter the reaction chamber, 2) there is no fritted glass diffuser, and 3) the wafers are stationary during deposition. The control thermocouple was in a well located 0.06-in. from the substrate, and three gas supplies were used: 1 pct SiH4 in N 2, O 2, and N 2. Water vapor must be excluded from the plumbing to prevent the formation of colloidal SiO, and the SiH4 must be diluted with an inert gas because SiH4-0, mixtures are extremely flammable above about 4 pct SiH The wafer temperature was determined by attaching a thermocouple to a test wafer and the temperature was maintained to +5 C. The conditions used in this investigation are listed in Table I. The temperature range was chosen for compatibility with the A1-Si system. The volume ratio of 0, to SiH4 is the actual volume of 0, delivered to that of SiH4, taking into account the initial dilution of the SiH4. This ratio, which was used by Goldsmith and Kern,7 is a useful indicator of the experimental conditions. The active/inactive ratio is the ratio of the volume of active gases, SiH4 and O2, delivered to the volume of dilution gas. The active/inactive ratio is an important parameter to specify for deposition rate determinations since it determines the amounts of reactants that arrive at the sample per unit time. Fairly high dilution ratios were necessary to achieve uniform deposits of SiO,. Most of the process characterizations were performed on the polished (111) face of 3 to 5 ohm-cm, n-type silicon wafers which were 0.009 in. thick; but the data approximately apply to deposition of SiO, on thin films of aluminum. It is difficult to obtain accurate deposition rate data over aluminum films because of coarsening the aluminum surface during exposure to 300" to 400°C. The deposited SiO, film fol-

Jan 1, 1969

By S. J. Matas, R. F. Hehemann, R. H. Goodenow

The hot-stage metallographic method has been employed to determine radial growth rates of upper and lower bainite. Lower bainite appears to grow as individual plates that increase in both length and thickness while upper bainite grows as sheaves of closely spaced plates or needles. A discontinuity in the temperature dependence of the growth rate appears to be associated with the transition from upper to lower bainite and stepped quenching experiments suggest that lower bainite will not continue to grow when the temperature is raised to the upper range. Thus, a single process does not appear to control the growth of both upper and lower bainite. A tentative model based on the forces acting on a dislocation interface is proposed to account for the slow growth of bainite. It has been recognized since the early studies of Davenport and Bain that a close relationship exists between the martensite and bainite transformations in steels. However, diffusion of carbon during the transformation has lead to considerable controversy concerning the reaction mechanism.1-7 Many studies4,5,7-9 have emphasized the structura and kinetic aspects of the bainite reaction and, in particular, the difference observed between the two forms of bainite—frequently termed upper and lower bainite. A kinetic difference between the two types of bainite has been revealed in the activation energy determined from the overall reaction;4,5 however, many difficulties arise in an interpretation of these activation energies since a number of temperature dependent factors contribute to the kinetics of the overall reaction. The displacive surface relief10 accompanying the bainite reaction permits a separation of the nuclea-tion and growth contributions to the reaction and allows the kinetics of the growth process to be examined. Several investigations of this type have been conducted; however, they have been restricted to the low temperature range.3'6'11 Here, bainite plates are observed to grow slowly in both length and width. The present investigation extends such studies to include the upper bainite range. MATERIALS AND PROCEDURE Materials. The composition of the steels studied in this investigation are presented in Table I. The range of composition permitted a study of the effect of carbon content on the growth rate of upper bainite in the 9 pct Ni steels and consideration of both upper and lower bainite in the higher carbon steels. These steels were received as hot-rolled rounds and were forged to approximately 1/2 in. thick plates for preparation of metallographic specimens. In order to produce an essentially zero carbon steel, Steel A was decarburized in wet hydrogen at 1550°F for 15 days with the result tabulated as Steel AD. Experimental Procedure. In order to study the slow growth of the displacive transformation product, a commercially available Leitz hot stage was modified to permit heating of the specimen by its own resistance in a manner similar to that employed by other investigators.6 The furnace chamber was maintained at a pressure of 2 to 3 X 10-5 mm Hg prior to austenitizing at 2000° ± 12° F for 5 min. Samples could be cooled from the austenitizing to the transformation temperature in approximately 15 sec and the progress of transformation was recorded with a 9 cm by 12 cm single frame camera or a 16 mm movie camera. RESULTS AND DISCUSSION Growth Characteristics. The general growth characteristics observed in this investigation were analogous to those reported previously.3,6,11 Typical growth sequences for the high temperature and low temperature forms are illustrated in Figs. 1 to 5. In both temperature ranges, bainite plates increase in length at slow, temperature dependent rates until interrupted by a grain boundary, another plate, or

Jan 1, 1963

By B. L. Averbach, Morris Cohen, S. A. Kulin

The martensitic transformation can be initiated by elastic stresses at temperatures above M. in a steel containing 20 pct Ni and 0.5 pct C. Shear strains and normal tensile strains acting on a potential habit plane promote the transformation but compressive strains oppose it. THE strain sensitivity of the martensitic transformation has long been recognized. It is now well known that martensite formation can be induced by plastic deformation at temperatures below, and not too far above, the M, point.' However, the exact role of elastic vs. plastic strains and of the concomitant stresses has proved to be a very elusive matter. Many investigators2-' of the steel hardening reaction have made use of the stresses resulting from volume changes to account for such observations as the existence of retained austenite and its variation across the section of a bar, the change in the amount of retained austenite with quenching rate, and the self-stopping nature of the transformation when the cooling is stopped. The effect of applied strain as an independent variable has been studied in 70 pct Fe-30 pct Ni alloys by Scheil7 and McReynolds.8 Some data are also available for lithium and Li-Mg alloys,9 Cu-Zn,10 Cu-Sn and Cu-A1 alloys," and aus-tenitic stainless steels."-" It has been found that martensite formation can be induced isothermally, even at temperatures above M,, by mechanical deformation of the parent phase. The competitive nature of plastic yielding by slip and by the martensitic reaction has been depicted by Scheil.7 Basically, Scheil postulated that: 1—at temperatures not too far above M, (where austenite is less stable than martensite), a critical resolved shear stress (within the elastic range) is required to promote the transformation to martensite; 2—at and below M,, the austenite lattice becomes mechanically, as well as thermodynamically, unstable and shears over spontaneously into martensite without the application of external stress; and 3—at temperatures sufficiently far above M8, the critical resolved shear stress for martensite formation increases to a level above that required for slip, and plastic flow then supersedes the transformation when external stress is applied. Scheil's concepts were tested by McReyno1ds8 ho found no change in the elastic moduli (measured both statically and dynamically) of 71 pct Fe-29 pct Ni alloys in the vicinity of the M, temperature. Since the moduli did not approach zero or become negative on cooling to M,, it was concluded that the austenite lattice does not become mechanically unstable at M2, as postulated by Scheil. McReynolds also reported that M, is not raised by elastic stresses. Accordingly, plastic deformation was considered to stimulate the transformation by generating martensite nuclei in the distorted regions of the parent phase. The above issues with regard to the role of applied stress require clarification, if a basic understanding of the martensitic transformation is to be obtained. For example, in the reaction-path theory,'"," it is postulated that strain embryos exist in the austenite that provide part of the activation energy for the nucleation process. These embryos are visualized to be regions of localized strain in which the atoms in the austenite lattice are displaced part way along the path to their ultimate positions in the martensite. Consequently, it would

Jan 1, 1953

In reply to inquiries and comments which have reached me since the publication of this paper, and in explanation of some seeming discrepancies between my statements in the text concerning the amount of displacement of the faults, on one hand, and certain figures in the plates on the other hand, I give here, with some additional remarks, my measurements of the displacements in the different sections, which it originally seemed unnecessary to print : By displacement, I mean neither the throw, i.e., the vertical distance apart of the two edges of a faulted bed (what Mr.

Jan 1, 1896

By Arthur B. Yates

Diamond drilling has advanced and expanded during the past few yean. Along with this increase there has been a marked trend to rely more and more upon drilling for the outlining of ore for reserve purposes. This is especially true underground, where men have not been available for opening up ore by crosscuts, drifts and raises. During the recent heavy call upon known ore reserves, more drilling has been done for exploration and it has become expedient to drill longer lateral holes from underground and deeper holes both from surface and from exploration headings in the mines. Furthermore, these deeper holes have to be drilled closely enough to warrant calculation of "probable" if not "proven" ore, from the results obtained therefrom. Interpretation of diamond-drill results has become more precise and reliable with the growing knowledge and understanding of the geologic structures that control the geometry of ore distribution, and this has broadened the field of usefulness of the drill. All of this has created a necessity and a demand for more accurate control of the hole as to direction, a more precise and reliable method of surveying for position, and a need for better and more complete core recovery, as well as larger cores, to provide an adequate sample. At depth the control becomes more difficult and, at the same time, more important. Control A close study of drilling in various parts of the world for a period of more than 20 years has brought to light one definite rule, practically invariable; namely, that diamond-drill holes tend to deviate into a position normal to any structure existing in the rocks, such as bedding, schistosity, gneissosity, or even parting or jointing— even if the hole is started at almost any angle other than parallel with the structure. It also appears that the better developed the structure is, the more quickly will the hole get into a position perpendicular to it. It has often been said that there is a tendency for holes to "drift" in the direction of rotation. This is obviously untrue, for in a vertical hole the measure of deviation would depend upon the azimuth chosen as zero, and there is an infinite number of choices. It has been proved. however, that in homogeneous rocks there is a tendency for the hole to corkscrew, and that the direction of the spiral is the same as the direction of rotation. This may account for the belief that holes drift in that direction. Some tests have been made using right-hand and left-hand rods, and these show that no matter what the direction of rotation the hole will swing into a position perpendicular to the structure. Methods of Control The foregoing empirical rule may be used as an indirect method of control. If the prevailing structure is known, it may be advantageous to start the hole as nearly normal to it as possible, for the

Jan 1, 1946

By Charles S. Barrett

The experiments reported in this paper have been fruitful in disclosing the mechanism of the deformation of iron in compression. They have established the nature of "deformation bands," "etch bands," or "X-bands," that have been a recognized but little understood feature in the structure of cold-worked metals since the early days of metallography, and have shown the role of the bands in the development of preferred orientations by cold-working. The work has also shown the relation of the orientation of individual grains to the preferred orientation of the aggregate. Some of the methods previously used in the determination of the indices of slip planes and slip directions are shown to be untrustworthy in the presence of deformation bands. The conclusion is reached that many slip planes and slip directions must operate during each stage in the compression of a single crystal, and that theories failing to take account of this require revision. In conducting the experiments a method of compression has been used by which extreme reductions can easily be reached, even to the limit set by the metal's capacity to deform without fracture. The work is a portion of a research program on the plastic properties of iron and steel. It is being used as a foundation for studies of orientntions resulting from recrystallization and is being extended to other metals and other types of deformation. Previous Work The previous experiments are few and have given confusing results Onol compressed a polycrystalline alpha-iron specimen between two flan plates of a testing machine and found that severe deformation oriented the crystals into a duplex preferred orientation, one set of crystallites having a cube diagonal of the body-centered cubic lattice parallel to the compression axis, and another set having a cube axis parallel to the compression axis. We shall speak of this structure as a double fiber texture of the type [111] + [100]. Wever2 also made an X-ray determination of the texture

Jan 1, 1939

By Charles S. Barrett

The experiments reported in this paper have been fruitful in disclosing the mechanism of the deformation of iron in compression. They have established the nature of "deformation bands," "etch bands," or "X-bands," that have been a recognized but little understood feature in the structure of cold-worked metals since the early days of metallography, and have shown the role of the bands in the development of preferred orientations by cold-working. The work has also shown the relation of the orientation of individual grains to the preferred orientation of the aggregate. Some of the methods previously used in the determination of the indices of slip planes and slip directions are shown to be untrustworthy in the presence of deformation bands. The conclusion is reached that many slip planes and slip directions must operate during each stage in the compression of a single crystal, and that theories failing to take account of this require revision. In conducting the experiments a method of compression has been used by which extreme reductions can easily be reached, even to the limit set by the metal's capacity to deform without fracture. The work is a portion of a research program on the plastic properties of iron and steel. It is being used as a foundation for studies of orientntions resulting from recrystallization and is being extended to other metals and other types of deformation. Previous Work The previous experiments are few and have given confusing results Onol compressed a polycrystalline alpha-iron specimen between two flan plates of a testing machine and found that severe deformation oriented the crystals into a duplex preferred orientation, one set of crystallites having a cube diagonal of the body-centered cubic lattice parallel to the compression axis, and another set having a cube axis parallel to the compression axis. We shall speak of this structure as a double fiber texture of the type [111] + [100]. Wever2 also made an X-ray determination of the texture

Jan 1, 1939

By Charles S. Barrett

THE experiments reported in this paper have been fruitful in disclosing the mechanism of the deformation of iron in compression. They have established the nature of "deformation bands," "etch bands," or "X-bands," that have been a recognized but little understood feature in the structure of cold-worked metals since the early days of metallography, and have shown the role of the bands in the development of preferred orientations by cold-working. The work has also shown the relation of the orientation of individual grains to the preferred orientation of the aggregate. Some of the methods previously used in the determination of the indices of slip planes and slip directions are shown to be untrustworthy in the presence of deformation bands. The conclusion is reached that many slip planes and slip directions must operate during each stage in the compression of a single crystal, and that theories failing to take account of this require revision. In conducting the experiments a method of compression has been used by which extreme reductions can easily be reached, even to the limit set by the metal's capacity to deform without fracture. The work is a portion of a research program on the plastic properties of iron and steel. It is being used as a foundation for studies of orientations resulting from recrystallization and is being extended to other metals and other types of deformation. PREVIOUS WORK The previous experiments are few and have given confusing results. Ono1 compressed a polycrystalline alpha-iron specimen between two flat plates of a testing machine and found that severe deformation oriented the crystals into a duplex preferred orientation, one set of crystallites having a cube diagonal of the body-centered cubic lattice parallel to the compression axis, and another set having a cube axis parallel to the compression axis. We shall speak of this structure as a. double fiber texture of the type [111] + [100]. Wever2 also made an X-ray determination of the texture

Jan 1, 1938

By Charles O. Thompson

WHEN a wire rod of iron or of steel is immersed in a hot. solution of common salt, allowed to remain long enough to bring the metal to the temperature of the brine, and withdrawn, the surface of the rod is irregularly covered with a deposit of crystals of salt. These crystals adhere to the cod with great firmness, in consequence, doubtless, of a thin film of ferric hydrate, which is formed between them and the rod as the water dries tiff. The rod can now be re¬duced, by successive passes through a dic or draw-plate, without any

Jan 1, 1881

By F. L. Wolf

The catenary system of line construction possesses so many desirable characteristics from the operating standpoint that it has wide application for all types of electric traction. Many steam roads are electrifying sections of their lines, and in most cases are operating both steam and electric locomotives over the same track. This means that the overhead catenary system is subjected to the severe corrosive action of locomotive smoke, and data concerning the resistance of various alloys to this form of corrosion are very desirable from every point of view. Reliable and specific information and data on the subject of corrosion due to steam and smoke from locomotives are extremely meager and, on this account, extensive service tests, together with accelerated tests, have been made on a number of commercial metals and alloys. The observations and data recorded in this paper are the result of a preliminary test which was started in 1923 and which has been carried on to the present time. The recognition of the need for even more detailed and accurate data has resulted in the undertaking of another test which has been in progress for about a year. The result of this test will be published in due course. Some years ago The Ohio Brass Co. was asked by one of the large steam railroad companies to furnish data on construction details for a catenary system which it was considering for one of its divisions. The selection of materials which would give the necessary physical characteristics as well as withstand the severe corrosive action of locomotive gases caused electrical railroad engineers considerable concern. At that time, there were available no specific or authentic data on these important questions: no systematic investigation of the problem appeared to have been made, even though it's importance was generally recognized. Such observations as had been made were crude in that they had been limited largely to visual inspection which too frequently is most misleading. However, the scattered information which was collected gave important clues as to how best to start an investigation. Technical literature was studied, metallurgical experts were consulted, and the problem was discussed with engineers who were in close contact

Jan 1, 1930

By L. A. Wilson, N. H. Harrison, R. R. Clay, R. L. Reed. D. W. Reed

Experiments have been performed in a linear near-adiabatic system for the purpose of extending data on reverse and forward combustion from atmospheric pressure to 1,000 psig. Results obtained from reverse combustion appear to conform qualitatively with the existing description of the process when reaction kinetics are suitably modified to account for the increase in pressure, i.e., increasing tbe pressure decreases the peak temperature and increases the combustion zone velocity. Forward combustion appears to be a fuel dominated process wherein peak temperature and combustion zone velocity are not very sensitive to changes in pressure. The moderate effects of pressure that do exist at low flux virtually disappear at high flux providing all oxygen is consumed. With this provision. increasing the pressure decreases the frontal velocity and increases the peak temperature. Results me shown graphicaIIy which demonstrate the effects of presswe on peak temperature, rate of advance, oil recovery, air/oil ratio, carbon oxides produced and temperature distributions. INTRODUCTION Numerous field tests of oil recovery using the technique of underground combustion are now in progress. Operating pressures used are always substantially in excess of atmospheric pressure. Nevertheless, the literature contains no laboratory data pertaining to the effects of pressure except for those of Martin, Alexander and Dew.1 Unfortunately, these data appear to reflect heat losses which may have obscured some of the effects of increased pressure. The underground combustion processes are exceedingly complex, and general concepts relating to them have necessarily been described in relatively simple terms. Particularly with regard to forward combustion, the interaction between multiphase fluid flow, heat transport and various rate mechanisms is so involved that to date a rigorous treatment is not available. In this paper a linear near-adiabatic system is described which was found capable of operating at pressures up to 1,000 psig and temperatures of at least 1,100 F. Using this equipment, experiments on both forward and reverse combustion were accomplished at elevated pressures and the data presented as a function of air flux or temperature. It will be assumed that the reader is familiar with the papers of Wilson, Wygal, Reed, Gergins and Henderson on forward combustion and that of Reed, Reed and Tracht3 on reverse combustion, so that it is not necessary to repeat the details of the two processes. EQUIPMENT AND PROCEDURE It was decided to study the effects of pressure over the interval 0-1,000 psig using a near-adiabatic system. Since satisfactory operation of such a system requires very thin tubing walls, it proved necessary to insert the entire combustion tube and heater assembly into a high pressure jacket in such a way that the internal tube pressure could be counterbalanced by pressurizing the annulus. This meant that the numerous heater and thermocouple wires had to pass through gas-tight seals that required considerable effort to maintain effective. An unexpected difficulty arose in connection with the nature of the annulus pressuring gas. It turned out that the composition of this gas critically affected the functioning of the adiabatic control system. Operation of the equipment at elevated pressures was not particularly difficult. The problems that did arise were a direct consequence of the large numbers of connections and seals involved. EQUIPMENT The equipment consisted of the combustion tube which fitted within the pressure jacket. This jacket was in turn mounted on a wheeled carriage which facilitated movement and provided for rotation of the

By J. Washburn

Two simple types of dislocation distribution were introduced into zinc crystal specimens and the effect of each on the stress-strain curve was investigated. Quantitative results were obtained for simple edge dislocation arrays and for an array of screw dislocations lying in the slip plane. A CCORDING to present knowledge, the disloca-tions present in large annealed metal crystals can be divided into two somewhat arbitrary groups: 1—single dislocation lines distributed more or less at random or forming elements of a three-dimensional network in which the distance between adjacent dislocations is of the order of 10 2 to lo-' cm and 2— widely separated planar arrays of edge dislocations forming dislocation walls or small angle boundaries within which adjacent dislocation lines are spaced at much smaller distances (lo-' to 10- hm). The former can be considered as a dislocation interpretation of the mosaic crystal proposed by Darwin and Ewaldl, ' 40 years ago to account for anomalously high integrated intensities of X-ray diffraction maxima. Small angle boundaries, although now known to be present in most single crystals used for mechanical testing, were not generally recognized by the early workers. This was partly due to the fact that only recently have improved X-ray and metal-lographic techniques been available for checking the macroscopic perfection of crystals."" It has long been known that changes in growth conditions and in annealing procedure, which might logically be expected to cause variations in the structural details of both the dislocation network and of dislocation boundaries, produce marked variations in some mechanical properties such as yield strength." However, no quantitative experimental correlations between changes in dislocation distribution and changes in mechanical properties have yet been made. Such a correlation has been difficult to obtain because, even when great care is exercised to keep the histories of a number of single crystal specimens identical, it usually has not been possible to avoid considerable variation in macroscopic per- fection.' The number and orientation of dislocation boundaries vary from specimen to specimen. This has probably been an important contributing factor to the large scatter in the results of most mechanical measurements on pure single crystals. Some recent experiments"% ith single crystals of zinc have shown that the presence of dislocation boundaries in a specimen can increase its resistance to deformation by slip. With polycrystalline aluminum and nickel, there is also evidence that dislocation boundaries within the individual grains of the aggregate can increase the resistance of the material to plastic deformation, either as measured by tension tests at room temperature or by creep tests at higher temperatures.'" " Although the foregoing observations seem to have established the fact that substructure can have a strengthening effect, the test conditions were too complex to give much information concerning the mechanism. In the foregoing cases, a network of intersecting boundaries having various orientations and boundary angles were present. Before their apparent strengthening effect can be understood, it will be necessary to isolate and study separately the effect of a number of variables: 1—boundary angle, 2—boundary orientation with respect to the active slip direction, 3—number of boundaries, 4—intersections of boundaries, 5—detailed structure of the boundaries, and 6—interaction of impurity atoms with dislocations in boundaries. The object of the present work was to study the effect of dislocation boundaries on flow stress under the following simple experimental conditions: 1— substantially pure shear deformation and 2—boundaries of controlled angle, orientation, and number. In this way, it might be possible to distinguish the important variables from the relatively unimportant ones. Experimental Procedure Stress-strain curves of hexagonal metals are generally nearly linear even out to very large strains."

Jan 1, 1956

By Roy Lindgren

Since the year 1643, when the first blast furnace in America for treating iron ore was built at Saugus, Mass., out of mica schist quarried in the neighboring district, the procurement of a suitable refractory for furnace lining has been a problem of concern to the operators of furnaces. The stacks built of mica schist continued to smelt iron ore until about 1836, when, according to F. H. Norton, the first firebrick were produced1, at Queens Run, Pa. Other writers speak of brick having been molded and burned in Massachusetts about the year 1834. In 1841, Andrew Russell began to produce medium refractory plastic clay brick near East Liverpool, Ohio, that were used for lining blast furnaces1. The well-known Kentucky clay-producing district was not opened up until the year 1871, but since then it has produced a large percentage of the linings for iron blast furnaces. While some strides have been made by the refractories industry during the 100 years that have passed since the first firebrick were produced, it has been only during the last two decades that any real progress has been made towards bettering the product, even though the method of production had improved. Perhaps the fault lies with the user of the brick rather than with the producer, for not sooner demanding a supe¬rior product. During the past 15 years the tonnage produced per lining has increased from 500,000 gross tons to 1,000,000 gross tons, and now some furnaces are producing 1,600,000 gross tons and better on a single lining. It is true that enlarged capacity of furnaces and improved practice have accounted for some of this increase in tonnage, nevertheless better quality in firebrick must be given credit for its share. However, we are not yet ready to say that we have reached a maximum life of furnace lining. We believe that a better product can be produced and that the refractories industries of America will, through their extensive research depart-

Jan 1, 1936

A. G. Cockbain—The paper by Burlingame, Bitsianes and Joseph is of great interest in extending the work done on high grade sinters, particularly that of Hessle, and the development and application to them of the technique of McBriar, Johnson, Andrews and Davies on ironstone sinters. In this laboratory the work of McBriar et al. has also been continued and extended to cover high grade sinters, and a sectioning technique similar to that used by McBriar et al. was attempted on sinter cakes made in the laboratory sinter unit, using magnetite concentrates (containing 64 pct Fe). In these experiments no attempt was made to flush out the products of combustion with nitrogen before cooling. It was considered that free air penetration would occur on only a limited scale with the size of sinter cake made (14 in. sq x 12 in. deep). Chemical analyses of the zones showed generally similar features of those described by Burlingame et al. and especially the FeO rich region at and just behind the flame front, i.e. zones of ignition and combustion. This seems to indicate that the nitrogen atmosphere does not materially affect the states of oxidation in the sinter cake or at least that special care is not required unless the sinter cake is small. Burlingame et al. consider that FeO present has some significant part to play in the mechanism of sintering. This view does not find favor with the author. The reduction of iron oxides in the presence of red hot coke is a well known phenomenon, whether conducted in an atmosphere of nitrogen or in a crucible in air, and in view of the presence of some carbon in the hot sinter, especially just at the ignition zone, cessation of the progress of the flame front will in no way affect the reduction of iron oxides near hot coke. Even in a nitrogen atmosphere some CO and CO, will be generated by reduction and by continual oxidation and reduction of CO as the transfer agent, the oxidation state of the iron oxides can be lowered quite rupidly so long as free carbon exists with enough heat. Knowing the composition of the gas at the flame front (obtainable by probes), it would be possible to calculate the static oxidation state of Fe2O3/Fe3O2 in equilibrium with it and hence obtain a check on the chemical analyses to see if in fact direct reduction of the Fe2O3/Fe2O1 to FeO has taken place. Have the authors attempted this? It appears to this writer that what is required is some means of reducing rapidly the heat content of the ignition zone and immediately behind, and at the same time insuring no oxidation by the air. In ironstone sinters the difficulty of oxidation state of the iron did not arise on account of the very large slag bulk. However, in high grade sinters knowledge of this, and also the mechanism whereby high oxidation states can be obtained in the final sinter, is of great interest. R. D. Burlingame (author's reply)—The question has been raised as to whether the high FeO content found in high-fuel sinters is due to actual reduction at the advancing flame front or due to unavoidable direct reduction during the quenching period. For such direct reduction to have taken place in the freshly-formed sinter, a considerable amount of solid carbon would have had to escape combustion and be available throughout the hot sinter zone during the quenching period. A simple stoichiometric calculation with the limited data available indicates that a zone of freshly-formed sinter over 2 in. wide must have averaged roughly 2 pct C to accomplish the amount of reduction found. Furthermore, the presence of this amount of carbon would indicate that the fuel in the charge had not burned over a narrow front but over a zone at least 2 in. thick. In contrast to such a condition, the data of the present investigation indicate that the combustion of fuel is confined mainly to a narrow front in which high temperatures and reducing conditions favor. the formation of excess ferrous iron.

Jan 1, 1959

By J. J. Gilman

THEORIES of fracture in metals have been based primarily on the dependence of fracture strength on grain size. This dependence was first observed by Masing and Polanyi.l These workers, as well as 0rowan12 and Davidenkov and Wittman,' thought the grain size could be equated with the crack size in the Griffith condition for crack propagation.4 In this way they could account for the observed proportionality between fracture stress and the reciprocal square root of the grain size. The chief results of recent investigations of the fracture strength of polycrystals are summarized in Fig. 1. Low for iron,5 Petch for iron,' Greenwood and Quarrel for zinc, Petch and Zein for zinc,' and Hauser, Landon, and Dorn for magnesium'' have all found that the fracture stress of a polycrystal is proportional to the reciprocal square root of the grain size. Also, they find that, for large grain sizes, the fracture stress lies near the extrapolation of the yield-stress curve determined at small grain sizes; where measurable plastic strain precedes fracture. Low9 has gone a step further and shown that, in Range 1, the fracture stress in tension is almost identical to the yield stress in compression for a given grain size. Homes and Gouzou, 10 and Low also have shown that, in Range 2 of Fig. 1, microcracks form when the yield stress is reached, but they do not cause failure until the stress reaches a much higher value. The fact that yielding always precedes fracture suggests that fracture is induced by plastic flow. A mechanism by which this might occur was first proposed by Zener.11 He pointed out that blocked dislocations would cause stress concentrations which might cause fracture. The blocking would be caused by grain boundaries. This idea has been developed by Eshelby, Frank, and Nabarro,12 by Koehler,13 and by Stroh.14 By means of etchpits blocked dislocations have been observed in brass by Jacquet,15 in zinc by Gilman,16 and in lithium fluoride by Gilman and johnston. The blocked-dislocation theory and the experiments that bear on it have been summarized by Mott.18 One of the strong points of the blocked-dislocation theory is that it can explain the grain-size dependence of the fracture stress in a natural way. However, Low9 has pointed out that the theory is not satisfying when it is considered quantitatively. Gilman10 also has criticized the theory and presented an alternative interpretation of the relation between fracture stress and grain size. Since the blocked-dislocation theory is not the only theory that can explain in the grain-size effect, it is necessary to find other evidence either to support or deny it. In this investigation the following points were studied: 1) If blocked dislocations normally cause fracture, then the fracture stress ought to be very high in the absence of plastic glide. Is it? 2) If dislocations must be blocked in order for metals to fracture, then certain types of grain

Jan 1, 1959

By F. L. Wolf

THE catenary system of line construction possesses so many desirable characteristics from the operating standpoint that it has wide application for all types of electric traction. Many steam roads are electrifying sections of their lines, and in most cases are operating both steam and electric locomotives over the same track. This' means that the overhead catenary system is subjected to the severe corrosive action of locomotive smoke, and data concerning the resistance of various alloys to this form of corrosion are very desirable from every point of view. Reliable and specific information and data on the subject of corrosion due to steam and smoke from locomotives are extremely meager and, on this account, extensive service tests, together with accelerated tests, have been made on a number of commercial metals and alloys. The observations and data recorded in this paper are the result of a, preliminary test which was started in 1923 and which has been carried on to the present time. The recognition of the need for even more detailed and accurate data has resulted in the undertaking of another test which has been in progress for about a year. The result of this test will be published in due course. Some years ago The Ohio Brass Co. was asked by one of the large steam railroad companies to furnish data on construction details for a catenary system which it was considering for one of its divisions. The selection of, materials which would give the necessary physical characteristics as well as withstand the severe corrosive action of locomotive gases caused electrical railroad engineers considerable concern. At that time, there were available no specific or authentic data on these important questions: no systematic investigation of the problem appeared to have been made, even though its importance was generally recognized. Such observations as had been made were crude in that they had been limited largely to visual inspection which too frequently is most misleading. However, the scattered information which was collected gave important clues as to how best to start an investigation.

Jan 1, 1930

By R. M. S. B. Horta, W. T. Roberts, D. V. Wilson

Evaluation of results obtained by the Harris method for inverse pole figures is discussed. Two existing analyses and a new approach are compared. In the most frequently used analysis, different reflections are accorded equal weight. A second method involves area-weighting of reflections, mainly to take account of nonuniformity of Pole distribution. In the new method, reflections are weighted according to their multiplicity factors. Intensity ratios obtained from a sample of steel sheet by the three methods are compared. INVERSE pole figures offer a convenient method of depicting the proportions of material with various orientations referred to a unique specimen axis. The technique was first applied to fiber textures, but it is now frequently used as a description of texture in sheet metal, the unique axis in this case usually being the sheet normal. The Harris method' for the determination of inverse pole figures has the great merit of simplicity. It suffers certain intrinsic limitations, but provided that these are borne in mind, the results allow useful conclusions to be drawn regarding the effects of texture components on certain mechanical properties. Much thought has been given to alternative methods of texture description, aimed at eliminating the ambiguity in the simpler methods.2"6 Refinements in the method of description are obtained at the price of increasing complexity, and it seems clear that a simple method, such as that of Harris, will continue to find application. The original derivation by Harris1 has been corrected by Morris7 and later by Mueller, Chernock, and Beck.2 Since the latter reference is more accessible, it is referred to more frequently than the work of Morris. Most users of the inverse pole figure method present their results on the basis of the treatment by Mueller et al., and it is the purpose of the present communication to comment on this treatment and to suggest a simple modification to the method of presentation which enhances the meaningfulness of the results. It will be convenient first to summarize the Mueller analysis as follows: The intensity Ihkl of a hkl reflection from a textured specimen is: Ihkl=CI0AL\Fhkl\2NhklPhkl [1] where C is a constant for a given sample I, is the intensity of the incident beam A is an absorption factor. With usual diffrac-tometer geometry and a flat specimen, A is inversely proportional to the density of the specimen. L is the Lorenz polarization factor Fhkl is the structure factor for the hkl reflection Nhkl is the multiplicity factor phkl is the fraction of crystals in the polycrystal-line aggregate with any particular (nkl) plane parallel to the surface. The corresponding equation for a specimen with randomly oriented grains is lR,hkl=CRl°ARL\fnkl\2Nnklk [2] the subscripts R indicating the factors that are different for the random sample, which will, in general, have a density different from that of the textured one. The intensity ratio is hkl , c A Phkl [3] IR,hkl CR AR PR The constants are eliminated by summing over all the measured reflections ^iRMi °R AR PR ljPkkl and from Eqs. [3] and [4] T IR,hkl The only unknown in Eq. [5] is Yj phkl and before this can be evaluated, it is necessary to adopt some form of normalizing procedure. Mueller et al. assume that when a large number, n, of reflections is used, the average value of p as defined by Eq. [6] below will be unity ? = £j**l3l [6] and the final result of their analysis follows: hkl Pkkl = i I&Jf~ [7] ±y* Ihkl ^ in,hki The normalizing procedure used by Mueller et al. involves an unrealistic assumption since it gives equal weight to each of the hkl reflections. Other normalizing procedures can now be examined with a view to selecting a more appropriate one. For an infinite number of reflections, the function p can be averaged over a continuous range of orientations covering the complete solid angle 4p by the integral relation: p =1 jp(a)dQ = l [8] This is the only exact procedure, but in practice a

Jan 1, 1970