By Susan B. Leiter

That oxygen in copper has been a source of trouble is well known and that that trouble has been real in the commercial world has been shown by Fuller.' Moore and Beckinsale's paper2 at the annual meeting of the Institute of Metals in London, 1921, called forth considerable discussion. Prof. T. Turner expressed the opinion that it was not necessary to have cuprous oxide present in sufficiently large quantities to form either globules or seams in order to produce a bad effect if the copper were gassed. This brought up the question of the solubility of oxygen in copper and the authors desired to know whether there were any evidence of such solubility, because their experience was that whenever there was any oxygen in copper it was present in the form of free cuprous oxide, which was practically always in the form of globules. Later Hanson, Marryat, and Ford3 stated that 'for all practical purposes cuprous oxide may be regarded as insoluble in copper. However, they found particles of the eutectic to coalesce to form much larger particles. They suggested that cuprous oxide was actually slightly soluble in copper, for it was difficult otherwise to understand the mechanism by which such coalescence could take place. W. E. Ruder, in discussing that paper, said that his experiments had led him to conclude that a slight solubility must exist to allow for the ready coalescence of oxide particles, but conductivity tests convinced him that that solubility was very small. Nevertheless, there appeared to be a state of admixture of oxide with copper that closely resembled a colloidal mixture which at first was mistaken for a true solution and which usually existed at the grain boundaries. The purpose of this paper is to give the results of some investigations, begun in September, 1921, which would seem to show that although cuprous oxide may be only slightly soluble: (1) this solubility is sufficient

Jan 1, 1926

By A. D. Brokaw

The so-called "paraffin dirt" of the Gulf Coast oil fields has been considered an indication of the possible presence of oil and gas, and not a few wells have been brought in solely on the basis of such evidence. In a sense, it may be empirically justified as evidence of the presence of oil or gas, though it cannot be said to be infallible. If the writer is correctly informed, its association with oil and gas was pointed out by Lee Hager some years ago, and while it is commonly mentioned by geologists and operators in conversation, no discussion seems to have found its way into print. The present interpretation is based on laboratory study rather than on field investigation, and is put forth with the hope of stimulating discussion which shall lead to more complete understanding. The term "paraffin dirt" has been applied to soils with a peculiar texture, which has been described as "curdy" or "rubbery." When moist, the material breaks much after the fashion of "green" cheese. It is rubbery under compression, but does not resemble rubber in tenacity or cohesion. When dry, the material ranges from hard clods to a horny mass of high tensile strength. The shrinkage in drying is very great, especially in the hornlike matter. The moist material ranges in color from dark brown in the specimens rich in organic matter to grayish in specimens containing more inorganic matter. All of the specimens studied were readily attacked by molds, which in some cases grew in great profusion on the samples. Samples exhibited a rather characteristic "swampy" or "mucky" odor when wet, and a characteristic odor of humic soils when moist. If the material is brought into suspension in water, very fine sand settles out and may be recovered by successive washing and decantation. The sand is almost entirely quartz, but contains occasional fragments of feldspar—more or less kaolinized and iron-stained. Practically all of the sand passes through a 100-mesh screen and the grains are extremely sharp —possibly below the limit of rounding. A flocculent mud, of clay and organic matter, remains in suspension for days. Some material is taken into solution in the water, imparting a slight tendency to froth when vigorously shaken. The results of partial analyses of four samples of "paraffin dirt," and, for comparison, one of a coastal plain soil are given in Table I.

Jan 1, 1920

By Elmars Ence, Harold Margolin

The partial isothermal section of the Ti-Cu-Zr system at 750°C has been studied. The crystal structure of Ti2Cu has been detevnlined as tetragonal and when expressed as face-centered tetragonal, a = 4.164, c = 3.611 A, and c/a = 0.867. TITANIUM systems in which ß-titanium decomposes eutectoidally into a and a compound rather readily are known as active eutectoid systems. Recently in active eutectoid alloys based on the Ti-Cu system, and containing additionally A1 and Zr, it has been found that zirconium may produce both moderate weakening and marked strengthening at elevated temperatures.' In order to obtain some insight into the behavior of zirconium, an attempt was made to determine whether compounds of the type Tix Zr and TixZryCu exist. Only results of the Ti-Zr-Cu studies are reported here since data on Ti-Zr alloys will be presented in a separate publication. EXPERIMENTAL PROCEDURE Alloys were nonconsumably arc melted in argon atmosphere as 15-g buttons, prepared from materials of the following purities: Bureau of Mines electrolytic Ti — Bhn 63 OFHC copper Reactor Grade Zirconium Bhn .C 150 Prior to alloy preparation the electrolytic titanium was premelted to avoid excessive spattering of the charges during melting. The weight losses during melting did not exceed 1 pct of the total weight of the charge. The alloys prepared are listed in Table I together with analyzed compositions. in cases where they were determined. Specimens for heat treatment were wrapped in molybdenum sheet, annealed in argon-filled quartz capsules, and quenched by breaking the capsules under iced brine. About 1 to 2 sec are required to remove the capsule from the furnace, drop it into the iced brine and break it. Because of the insulation effect of the quartz, this delay in quenching should not produce a large drop in temperature. In many instances, no difference or little difference has been detected between the same specimen quartz capsule quenched or directly quenched in vacuum by an impinging stream of water.' Ti-Cu-Zr alloys were homogenized for 48 hr at 825°C prior to annealing at 750°C. Annealing for 5 days at 750°C produced the same results as 11 days at temperature and it was therefore assumed that 5 days was sufficient to establish equilibrium. Titanium-copper alloys were homogenized for 40 hr at 900°C prior to heat treatment for 6 days at 750°C. Specimens for metallographic examination were electropolished and etched with the following solution:

Jan 1, 1962

By Paul L. Burkhart

THOUGH at an earlier period brief studies had been made by the Lehigh Navigation Coal Company Inc., it was not until 1924 that J. B. Warriner, then general manager, called for a comprehensive study of timber treatment, treating solutions, and related operations. Because of the impossibility of procuring accurate costs and other pertinent treating data, the American Wood Preserving Co. agreed to treat a car of mine timber at the Port Reading plant of the Reading Railroad. Fig. I shows the treating data collected at the treating plant on this timber, which was installed in two of the Lehigh mines in 1925. [ ] In the latter part of 1925, a survey of the tunnels and gangways of the company's Panther Valley mines was made to determine the proportion of gangways or tunnels timbered, cause of timber failures, approximate life of the average wood set and the approximate percentage of treated timber that it would be profitable for the company to use. Results of this survey appear in Table I. Because of the high percentage of timber that gave evidence of failure by rot, as noted in Table I, and a further study of the life of the sections where timbering was necessary, it was deemed advisable to fill 25 per cent of the yearly gangway timber requirement with treated timber. QUANTITIES AND TREATMENTS OF TREATED TIMBER PURCHASED In the early days of the program, none of the large treating companies would accept orders for small quantities of treated timber and the company was compelled to state the quantity of timber it would require at each operation in each month of the year. Table 2 is an example of the tabulation given to the various treating companies to assist them in making a yearly bid on the minimum quantity of timber required by the company during the year 1931. A bill of timber was calculated for each car, the weight of which would be between the minimum and maximum weight permitted for railroad-car loading. The treating company was paid for timber upon delivery at the operation specified. As extra cars of timber were required, they were ordered from the treating company, and payment was required on their receipt, on the basis of the piece or tonnage

Jan 1, 1942

By R. G. Knickerbocker, R. R. Lloyd, W. T. Rawles

In July 1041, the Experiment Station of the Bureau of Mines at Boulder City, Nevada, began a study of methods of producing magnesium metal from magnesium oxide, with particular emphasis upon the direct use of magnesium oxide in a molten chloride electrolyte. The program was extended to include pilot-plant study of chemical methods for the preparation of pure magnesia from dolomites and magnesites. Preliminary work on the production of magnesia from dolomite was done with the cooperation of Kobert D. Pike and the Harbison-Walker Refractories Co. These investigatipns included a cooperative arrangement whereby the Bureau tested certain steps of the Harbison-Walker-Pike process. The process finally developed by the Bureau includes the precarbonation mixing step of the H.W.P. flowsheet prepared by Mr. Pike. Two magnesium-reduction plants using MgO as a source of magnesium were being constructed in the West, and they enormously stimulated interest in various dolomite deposits as possible sources of the magnesia needed by them. This paper describes one phase of this program—the operation of a pilot plant for producing cell-grade magnesia from dolomite from Sloan, Nevada. The process developed for this purpose is an adaptation of a well-known process first proposed by Clossonl and modified by others,2"1 involving the use of calcium chloride and carbon dioxide. It is based on the following chemical reactions: MgCl2 + Ca(OH)2 = CaCl2 + Mg(OH)2 [1] Mg(OH)4 + CaCU + CO2 = MgCl2 + CaCO, + H2O [2] The first reaction proceeds almost completely to the right because of the much greater solubility of calcium hydroxide as compared with magnesium hydroxide. Under equilibrium conditions, when only the four components shown in reaction I are involved, the ratio of magnesium to calcium in solution, according to solubility-product relationship, will be: This reaction is the basis of present commercial processes for recovering magnesium from sea water and dolomite. The second reaction is, in effect, a reversal of the first reaction produced by adding COz. This reaction also proceeds nearly to completion, the solubility relationship being: Ca where P indicates partial pressure of COz, in atmospheres.

Jan 1, 1944

By Homer F. Staley, C. P. Karr

The casting alloy 88 copper, 10 tin, 2 zinc, commonly known in England as Admiralty metal and in this country as Government bronze, gun metal, or Naval Department composition G, has, at its best, many valuable properties. However, its physical properties are known to vary widely with slight changes in method of manufacture of the castings, such as slight variations in composition, variation in pouring temperature, kind of mold used, method of pouring and gating of molds, size and shape of castings, amount and kind of heat treatment, and so forth.' The microstructure of castings made from this alloy is influenced by slight variations of composition, rate of cooling, and kind and length of heat treatment. This is best understood by reference to the equilibrium diagram. The part of the diagram in which we are interested and the effect of the thermal equilibrium relations on the physical properties of the alloy 88 copper, 10 tin, 2 zinc, have been discussed by Hoyt, Campbell, Primrose, and Rawdon.2 In Fig. 1 is given the equilibrium diagram of the copper-tin alloys. Briefly stated, the relations of composition and temperature changes are as follows. Compositions between A and a consist of but one constit ent—the a bronze, which is a solid solution of copper and tin, rich in copper. On cooling from the molten state these compositions gradually crystallize, at temperatures above 790°, into a mass of interwoven treelike crystals or dendrites. The cores of the dendrites are rich in copper and the percentage of tin gradually increases as the surfaces are approached. AS cooling progresses, after a11 the metal has crystallized, no further changes occur in the crystals other than diffusion within the crystals, which tends to erase the dendritic pattern and to render the structure more homogeneous. * Metallurgical Ceramist, U. S. Bureau of Standards, Associate Physicist, U. 8. Bureau of Standards. A. D. Flinn: Iron. Age (1915) 96, 1292-3. C. P. Karr: U. S. Bureau of Standards Tech. Paper 59, Pt. 1. S. L. Hoyt: Enging. (1913) 96, 667-7, 704-5. William Campbell: Trans. Am. Inst. Met. (1912) 6, 158-172. H. S. Primrose: Metal Ind. (1916) 14, 202-4. H. S. Rawdon: U. S. Bureau of Standards Tech. Paper 59, Pt. 11.

Jan 1, 1921

By B. C. Allen

Grain boundary grooving has been studied in chromium, molybdenum, and tungsten under a variety of conditions using high vacuum techniques and tantalum -gettered argon. The average surface free energy of solid chromium, and the chromium-liquid silver interface free energy were respectively found to be 2200 ± 250 and 500 i 130 ergs per sq cm from groove formation kinetics and estimates of pertinent volume difffusion coefficients. The results for chromium were unffected by variations in interstitial content ranging from 0.003 to 0.09 pct C, or 0.003 to 0.03 pct O. Surface diffusion is the primary mechanism of groove formation in chromium under 1 atm argon at 1200" to 140O°C, and is essentially unaffected by 0.003 to 0.09 pct C, 0.003 to 0.03 pct O , metastable nitrogen contents up to -0.01 pct, and up to 2 torr Ag vapor. At higher temperatures, the major mechanism is volume diffusion in argon or evaporation-condensation in stutic vacuum. Surface diffusion occurs in molybdenum at 0.5 to 0.96 and in tungsten at 0.5 to 0.9 of the absolute melting tempera -ture by a single mechanism, possibly by the migration of single adatoms or vacancies. Results were slightly affected by up to 23 tory Sn vapor, and in molybdenum were essentially unaffected by 0.5 Ti or carbon in the range 0.002 to 0.02 pct. Volume difffusion through the liquid is the mechanism of groove formation in chromium-liquid silver at 1200" to 1400°C and in molybdenum-, Mo-0.5Ti-, and tungsten-liquid tin at 1200" to 2000°C. The solid-liquid interface free energies involved were estimated from grooving kanetics. WHEN a grain boundary intersects a solid surface, a groove tends to form along the line of intersection at temperatures above about half the absolute melting point (0.5 TM). The groove progressively grows by preferential atomic migration either by diffusion or evaporation. Establishment of a groove angle occurs in accordance with the grain boundary and surface free energies involved. The motivation for groove formation is a reduction in the total surface free energy of the system. This study is a continuation of previous work on thermal grooving of chromium, molybdenum, and tungsten.&apos; The temperature ranges were extended, and the effect of metallic and interstitial impurities was evaluated. The results were such that certain interface free energies and surface self-diffusion coefficients were deduced from the grooving kinetics. EXPERIMENTAL WORK Materials and Preparation. As indicated in Table I, the 0.05-0.08-cm-thick chromium, molybdenum, and tungsten sheet used was nominally 99.99 pct after recrystallization. Two lots of molybdenum with about the same analysis, Mo-0.5Ti,* and tungsten were ob- *Alloy compsitions are expressed in weight percent . tained commercially. Extruded chromium rod,&apos; prepared from iodide process crystals, was warm rolled to sheet at 700°C. Sheet of three Cr-0 impurity alloys containing up to 0.03 pct 0 was prepared by warm rolling arc melted, extruded, and swaged rod. Two Cr-C impurity alloys containing up to 0.09 pct C were made by equilibrating unalloyed chromium with a known amount of CH4 for 24 hr at 1150°C in previously evacuated quartz capsules. Chromium containing nominally 0.015 and 0.06 pct N was similarly prepared by equilibration with NH3. The sheet was recrystallized to give a stable grain size about equal to the sheet thickness. Molybdenum and Mo-O.5Ti were recrystallized in a tantalum resistance furnace 1 hr at 1 x lo-5 torr at 2300" and 220O°C, respectively. Tungsten was similarly annealed for 1 hr at 2500°C. Chromium and its impurity alloys were outgassed at 1100°C and recrystallized 1 hr at 1700°C under 1 atm Ar. Except for nitrogen, the impurity content stayed roughly constant. Nitrogen in both alloys was reduced to <0.001 pct. In fact, over 80 pct of the added nitrogen was lost after outgassing at llOO°C and annealing sheet 1 hr at 1300°C in argon in the presence of tantalum. Such a rapid loss can be rationalized since -2 torr N are required for equilibrium with 0.04 pct N in solution,3 while the equilibrium pressure is ~10-5 torr over tantalum at 1300°C.4 The recrystallized sheet was cut into small coupons which were metallographically ground and polished on one side with a minimum of grain boundary relief. The surface roughness was on the order of 0.01 µ. The tin and silver used were nominally 99.999 spec-trographically pure. After being outgassed at 1100°C and equilibrated in a molybdenum crucible for 0.5 hr at 1800°C in argon, the tin contained 3 ppm 0, <0.3 ppm N, and 0.1 ppm H. Following outgassing at 900°C and equilibration in a chromium crucible 1 hr at 1400°C in argon, the gas content of the silver was 1 ppm O, <0.5 ppm N, and 0.3 ppm H. Grooving Under Argon or Vacuum. All specimens were placed in unsealed containers made from rod or sheet of the same alloy, thereby enabling the polished surface to achieve gas-solid equilibrium. The annealing fixtures are shown in Fig. 1. The specimen was placed in a resistance furnace with a tantalum or Ta-10W heating element plus tantalum fixtures or radiation shields. Chromium was outgassed at 1100°C, and molybdenum and tungsten were outgassed at 1900°C to 1 x l0-5 torr or at the grooving temperature, whichever was lower. In vacuum anneals, the specimen was then heated directly to the intended grooving temperature. In argon anneals, 99.996 Ar was admitted

Jan 1, 1970

EDUCATION is a business; and, if the consumer is satisfied with the product, no one has any grounds for complaint. "Pretty well satisfied" about slims up the attitude of the mining industry toward the young graduates presently entering the field. Yet, with amazing regularity the controversy over the five-year curriculum recurs in educational circles. The educational mills grind out their products, some higher grade than others, depending on individual proclivity. The cycle continues almost without interruption. Arthur Taggart, however, takes his bowie knife to some of the sturdiest limbs of the tree of knowledge in his article on engineering education on page 770 of this issue. As all who know him might suspect, the pruning is not restrained. With one swing of the knife, such practically-labeled courses as Mine Design are stricken from the tree and transplanted to the field of Graduate Education. Emphasis on the basic sciences and the study of man through courses in history, economics, and literature are recommended to constitute an undergraduate curriculum. Such courses show the least depreciation and therefore give the student the most for his money. Partial justification for this dramatic departure from tradition is explained by the increasing number of companies giving training courses. Why make the student pay for what he can get paid for learning after graduation, the author argues. Other leading educators espouse this doctrine. Dean S. C. Hollister of Cornell, for the Committee on Adequacy and Standards of Engineering Education, recommended to ECPD in 1951 that emphasis be placed on the basic sciences. "Sifting back through the curriculum, it seems clear that instruction in the basic sciences, if taught in a manner such that knowledge of them makes available working tools, contributes the most sustaining part of the curriculum", reported the committee. Note that he would utilize practical problems from the fields of engineering in teaching the sciences. In our opinion the important thing to learn in college is how to think the engineering approach. Recitation on traditional solutions of classic problems sharpens the memory, not the ingenuity of the student. The engineering schools of the nation recognize the advantage of great emphasis on fundamentals, and the inclusion of cultural courses in the curriculum. However, industry presently requires graduates to have a substantial knowledge of the tools of the trade upon graduation. This means that the colleges are forced to pare to the bone to encompass the required studies in the time allotted. In addition, there is the limitation of student money. College educators also claim that entering freshmen are often improperly prepared in such subjects as writing and mathematics. These considerations make it difficult for the critic of the engineering graduate to make any headway with the educators. Actually with the mounting problems imposed by lower grade and more complex ores, a new breed of engineers is needed. The impetus for this new product must come from industry. If there was a concerted effort from industry for an improved type of engineer, the colleges would modify their aims to meet the demand for the kind of individual desired.

Jan 1, 1952

By T. K. Redden

Protective coatings based on the formation of a surface coating of nickel aluminide (NiAl) were applied to the nickel-base superalloys IN 100, SEL 15, and U-700. Coated specimens were exposed to an oxidizing environment at temperatures between 1600 and 2200 F for times up to 1000 hr. The oxidation resistance and stability of the coating were evaluated by weight gain measurements, metallographic examination, and X-ray diffraction study of surface oxides and coating. The composition of the coating and diffusion zone was determined by electron microprobe traverse of samples before and after high-temperature exposure. Intermediate phases formed in the coating and diffusion zone were identified by X-ray diffraction in situ and after electrolytic extraction. The outer coating was found to consist of the inter-metallic compound, NiAl, while the diffusion zone contained MC, M23C6 or M6C carbides, and a phase in a matrix of NiAl + Nidl. Oxidation resulted in formation of an A1203 n&apos;ch scale containing some Tz02. Depletion of aluminum during oxidation resulted in degradation of the outer coating to Ni3Al and the nickel alloy matrix. Diffusion of aluminum into the base metal was found to be slight and did not influence coating life significantly. The o formed in the diffusion zone during coating decomposed during elevated-temperature exposure to form stable carbide phases characteristic of the base metal. Diffusion zone phase changes were found to have no effect on the life of the aluminide coating in the oxidizing envzron?nent. THE oxidation resistance of many high-strength nickel-base superalloys is inadequate for extended exposure at temperatures above about 1600°F. In addition, some applications for these materials require that they be exposed to environments containing sulfur compounds and sodium salts which can cause surface attalk known as sulfidation or hot corrosion. In order to provide the necessary corrosion resistance to the high-strength alloys, protective coatings based on an aluminizing process have been developed. These processes, usually based on a pack cementation technique, result in the formation of a NiAl-rich outer coating layer either during the coating process or by a subsequent diffusion treatment. The performance of the aluminide coatings is affected by interactions between the coating layer and the base metal both during the coating process and during subsequent exposure at elevated temperatures. Knowledge of these interactions is required to guide the development of coatings capable of longer life and improved reliability. Goward et al.&apos; recently reported the metallurgical factors which influence coating per- formance on MAR-M200. The present work is concerned with correlating the interactions and performance of coating compositions on several representative materials. EXPERIMENTAL PROCEDURES Materials. Three cast nickel-base superalloys which are used for turbine buckets in air-breathing engines were studied: IN 100, U-700, and SEL 15. Their chemical compositions are given in Table I. The alloys were vacuum-induction-melted and cast to slabs approximately 0.3 in. thick from which rectangular specimens 0.25 by 0.5 by 1 in. were machined. Coating Procedures. The machined specimens were coated by CODEP processes which were developed at the author&apos;s laboratory. These are based on pack cementation in various media to deposit either aluminum or aluminum in combination with titanium. The coating process which deposits only aluminum is designated CODEP-C, while the CODEP-D process deposits titanium in combination with aluminum. The CODEP-D process was applied only to IN 100. Both CODEP processes are applied at 1950" or 2000°F for 4 hr without need for a subsequent diffusion treatment. An outer coating about 1 mil in thickness is produced by these processes. Test Procedures. Coated specimens were exposed to static oxidation for periods ranging from 24 to 1000 hr at temperatures of 1600" to 2200°F. Terminal weight gain measurements and visual examination were used to evaluate oxidation resistance. including oxide spalling and coating failure. Both as-coated and exposed specimens of each alloy were studied by metallographic examination, electron microprobe analysis (EMA), and X-ray diffraction analysis either of the exposed surfaces or of phases extracted from the coating and diffusion zone. RESULTS As-Coated Condition. The microstructures of as-coated conditions were generally similar, irrespective of base materials or the particular coating process. They are typified by IN 100 coated by CODEP-D as shown in Fig. 1. The predominately single-phase outer layer, area A, Fig. 1, was identified by X-ray diffraction as the intermetallic compound NiA1. The NiAl zone extended inward to the original base metal interface. The diffusion zone, area B, Fig. 1, included carbide phases, a lamellar phase oriented perpendicular to the base metal surface, and a matrix phase consisting of a mixture of NiAl and Ni3Al. The phases in the diffusion zone were electrolytically extracted using a 10 pct HCl in methanol solution at approximately 1.3 amp per sq cm. The extracted phases were found to be M6C, MC, or M=C6 carbides and o as shown in Table I1 for each of the alloys. The d spacings from a typical diffraction pattern are

Jan 1, 1969

By Nelson B. Russell, Donald C. Bond

The effects of various antifreeze agents on the formation of hydrogen sulphide hydrate have been studied. On a molar basis the relative lowering of Tm (the maximum temperature at which solid hydrogen sulphide hydrate can exist in equilibrium with the given solution) for the various agents is: sodium chloride 1.00, calcium chloride 1.71, methyl alcohol 0.57, ethyl alcohol 0.68, ethylene glycol 0.73, diethylene glycol 0.73, sucrose 0.87, dextrose 0.71. On a weight basis the relative lowering of TM is: sodium chloride 1.00, calcium chloride 0.91, methyl alcohol 1.08, ethyl alcohol 0.89, ethylene glycol 0.69, diethylene glycol 0.41, dextrose 0.23, and sucrose 0.15. Introduction The solid hydrate of hydrogen sulphide, H2S.6H20,1 is in equilibrium with water and liquid hydrogen sulphide at 85°F at a partial pressure of hydrogen sulphide approximately equal to the vapor pressure Of hydrogen sulphide at that temperature. At temperatures below 85°F, in the presence Of excess hydrogen sulphide (greater than the amount required to react with the water present) the hydrate is in equilibrium with liquid hydrogen sulphide at approximately the vapor pressure Of hydrogen sulphide. In the presence of excess water, the solid hydrate is in equilibrium with liquid water, containing dissolved hydrogen sulphide, at a pressure lower than the vapor pressure of liquid hydrogen sulphide at the same temperat~re.2 The lower the temperature, the greater the difference between the decomposition pressure of the hydrate and the vapor pressure of liquid hydrogen sulphide at that temperature. Conditions conducive to the formation of solid hydrogen sulphide hydrate may exist in wells producing a gas containing a high percentage of hydrogen sulphide under high pressure, or in the lead lines from such wells. This paper gives the results of tests made with various antifreeze agents which might be useful in decomposing the hydrate or in preventing the formation of the hydrate of hydrogen sulphide Apparatus Fig , shows a diagram of the apparatus used. The sample under observation was contained in a glass tube 34 cm long, having a 6 mm id and a wall thickness of 2.5 mm. The lower end of this tube was closed- with a plug of butyl rubber. The upper end of the tube was connected to a diaphragm gauge, with a stainless steel diaphragm, a manometer, a vacuum pump, and a cylinder of hydrogen sulphide, The tube was held nearly horizontal, with the liquid resting along the lower side of the tube. It was found that when the tube was held in a vertical position, it broke with ex. plosive violence as soon as it became filled with solid hydrate. Presumably this was caused by the expansion which occurred on solidification of the hydrate. The difficulty disappeared when the tube was held in an inclined position during the tests.

Jan 1, 1949

By E. T. Turkdogan, M. T. Hepworth, R. P. Smith

The permeability of oxygen in 0 iron in the tempera-ture range 700" to 900 C and in 6 iron at 1450°C was determined by the rate of internal oxidation of iron, containing -0.1 pct Al. The solubility of oxygen in zone-refined iron was determined by equilibration with hydrogen-water vapor gas mixtures at 1450" and 1510°C; oxygen solubilities , for iron in equi1ibriu.rn with molten oxide, are found to be 66 and 83 ppm for these two temperatures, respectively. The diffusivity of oxygen in iron at 14500C3 as calculated from the permeability and solubility data, is (4.1 * 0.6) x 10 "B sq cm per sec. OXYGEN is one of the most common impurities present in iron or steel, mainly in the form of oxide inclusions. In the study of many metallurgical problems concerning solid iron, it is often desirable to know with a reasonable accuracy the solubility and diffusivity of oxygen over a wide temperature range. The solubility of oxygen in solid iron has been the subject of numerous studies yielding highly discordant results as seen for example from the literature surveys made by Meijering &apos; and Schenck et a1.&apos; As shown by Kitchener et aL3 and by Sifferlen, the high oxygen solubilities reported by many investigators are the result of oxidizable impurities which are often present in iron. In addition, there have been experimental problems associated with icaccuracy of oxygen analysis of iron containing less than 100 ppm 0. A number of studies have been made on the permeability of oxygen in a and y iron using Fe-Si, Fe-Mn, and Fe-A1 alloys in the internal-oxidation experiments.1&apos;2&apos;5&apos;6 However, no direct measurements have been made of the diffusivity of oxygen in iron. In the present work two sets of experimental measurements were made: permeability and solubility studies at 1450" and 1510°C and permeability studies only in the range 700 to 900°C. In both sets of permeability measurements slab-shaped specimens containing small predetermined amounts of aluminum in solution were exposed at constant temperature to gas mixtures of hydrogen, water vapor, and argon for varying times. These specimens were quenched, sectioned, and examined for oxygen penetration by metallographic observation of aluminum oxide particles which formed. From these data, it is possible to calculate the ratio of the diffusivity of oxygen in iron, D, to the equilibrium constant K for the reaction Hz(g) * O (dissolved in iron) = H,O(g). EXPERIMENTAL Permeability Measurements at 1450°C. An ingot of vacuum-carbon deoxidized iron containing 0.086 pct A1 was prepared, using commercial "Type lO4A Plas-tiron"; after hot rolling, specimens were machined into slabs a by 2 by 2 in. The impurity contents were: S, P < 0.002 pct; C, Mn < 0.01 pct; each of all other Usual impurities < 0.004 pet. The amount of oxide inclusions in this material, determined by a bromine-methyl acetate extraction, corresponded to about 20 ppm 0 in the iron which agreed well with the results of vacuum-fusion analysis. Each specimen was annealed at 1450°C for 1 hr in purified hydrogen, polished to a smooth surface, and then introduced into a controlled oxidizing atmosphere in a recrystallized alumina tube at 1450°C. The constant temperature zone (*3"C) was about 3 in. in length. The gas composition was controlled by mixing argon with hydrogen (using calibrated constant-head flow meters) and passing the mixture through a column of a mixture of oxalic acid dihydrate and 10 pct anhydrous oxalic acid, to establish a required water-vapor content in the gas mixture. The temperature of the oxalic acid dihydrate column was controlled by a thermostat. The total gas flow was in the range 800 to 1000 cu cm per min. The exit gas from the reaction tube was passed through a weighing bottle containing a desiccant, to cross-check the degree of water-vapor saturation, which for all experiments was about 97 pct of those derived from the data of Baxter and Lansing.1 For a typical experiment, a specimen was introduced into the furnace in a stream of dry argon and hydrogen. The specimen was then rapidly raised by a Pt-Rh alloy wire into the hot zone and allowed to reach the reaction temperature, at which time the oxidizing gas mixture was introduced. The oxygen potentials employed were sufficient to oxidize aluminum but not to cause liquid iron oxide to form. After a specified time, the experiment was ended by dropping the specimen onto a water-cooled copper block at the bottom of the reaction tube. The depth of the internally oxidized zone, hereafter called the "case", was determined by sectioning the specimen at right angles to the long direction. The section was then examined under a microscope equipped with a micrometer stage. In general, the oxide particles were fairly uniform in size and distribution, forming a reasonably well-defined interface between the oxidized and unoxidized region. A typical cross section as observed at X30 is shown in Fig. 1. A thermal macroetch was used in one selected specimen to delineate the case. A cross section of a previously oxidized slab was polished and reheated at 1450°C in a hydrogen atmosphere for about 10 min. Upon quenching, the surface relief shown in Fig. 2 was produced; causes of this effect are unknown. Permeability Measurements Below 900°C. A slightly

Jan 1, 1967

By Alwyn Birchmore Cox, Ian William Wark

In defending the chemical theory of flotation, Taggart, del Giudice and Ziehl have criticized1 the views of those who prefer to attribute the effects of certain flotation agents to adsorption. Perhaps with some justification, they describe the latter term as the "haven of refuge of writers lost in a morass of shaky experiment and muddy thinking." We prefer to regard it, however, as a haven of refuge for writers who seek a conventional term to describe the formation of films of flotation reagents on solid surfaces, because in many cases it is not yet possible to specify the forces that hold them there. Originally, as Taggart and his associates state, adsorption connoted a concentration difference and nothing more. In recent years, workers in the field of surface chemistry have tacitly added other meanings, and they now speak of orientated adsorption of unimolecular films on a solid sub-strate, of chemi-adsorption, and of exchange adsorption. Thus the term adsorption may connote simply the Gibbs layer of excess concentration at the surface of a solution, or a unimolecular film at the surface of a solid. Perhaps this has led to the misunderstanding of Taggart, del Giudice and Ziehl concerning the relationship between surface tension and adsorption at solid surfaces. The change in "surface tension" accompanying adsorption at a liquid surface can be used as a measure of the adsorption, and the Gibbs equation as quoted by these authors correlates these two conceptions. But, to correlate two conceptions docs not necessarily imply an attempt to explain either, although sometimes such an "explanation" is carelessly inferred. Use of "surface energy per unit area" instead of the numerically equal but more difficult and less definite conception of "surface tension per unit length " would lessen many of the present difficulties. (Compare with Adam.2) At interfaces involving a solid phase, neither &apos;" surface tension " nor " interfacial tension "can have any meaning, but the conception "interfacial energy per unit area" call be understood by anyone who is familiar with the concept of free energy. While it is true that surface energy cannot be directly measured at a solid surface,

Jan 1, 1939

By W. E. Crawford

The Fresnillo Company&apos;s mill at Fresnillo, State of Zacatecas, Mexico, treats oxide ores from the Fresnillo mine, dump ores and underground ores from the Plateros district, company leases and custom ores from the Zacatecas district, custom ores from other districts and tailings from old dumps at Fresnillo. The normal capacity of the mill is approximately 2600 dry short tons per 24 hours (a ton of 2000 lb.). The final product of the mill is a precipitate containing gold and silver, which is smelted and shipped as doré bullion to the refinery of the Compania Minera de Penoles, S.A., at Monterrey, State of Nuevo Leon, Mexico. The geology of the district was described in 1923, by T. C. Baker,&apos; from whose paper the following data have been taken: The mineralization of the district was effected in the Tertiary period, following the intrusions and preceding the appearance of the flows. The area within which productive veins have been found is 1 mile long by 1/2 mile wide. The important units of each of the four general fracture systems meet in the central portion of Proano hill, which is an outcrop of graywacke, and where the rock was also intensely fractured by subsidiary movements, resulting in a shattered zone 1200 ft. long by 400 ft. wide. The mineralization was more intense in the immediate vicinity of the principal channels through which the solutions rose. The valuable metals are silver and gold, the ratio by weight of the former to the latter being 1000 to 1.5. Argentite is the predominant silver mineral, and is associated with pyrite and manganese mineral. The sulfides are primary throughout. A slight secondary action is represented by small quantities of native silver and silver halides, principally cerargyrite, which are found in the upper part of the mine. Oxidation has penetrated with great thoroughness to the lowest horizon so far exposed, this being 420 ft. below the present ground-water level. The shattered mass within the central portion of the hill and near the surface was sufficiently mineralized to produce a large stockwork

Jan 1, 1935

By Ian William Wark, Alwyn Birchmore Cox

In defending the chemical theory of flotation, Taggart, del Giudice and Ziehl have criticized1 the views of those who prefer to attribute the effects of certain flotation agents to adsorption. Perhaps with some justification, they describe the latter term as the "haven of refuge of writers lost in a morass of shaky experiment and muddy thinking." We prefer to regard it, however, as a haven of refuge for writers who seek a conventional term to describe the formation of films of flotation reagents on solid surfaces, because in many cases it is not yet possible to specify the forces that hold them there. Originally, as Taggart and his associates state, adsorption connoted a concentration difference and nothing more. In recent years, workers in the field of surface chemistry have tacitly added other meanings, and they now speak of orientated adsorption of unimolecular films on a solid sub-strate, of chemi-adsorption, and of exchange adsorption. Thus the term adsorption may connote simply the Gibbs layer of excess concentration at the surface of a solution, or a unimolecular film at the surface of a solid. Perhaps this has led to the misunderstanding of Taggart, del Giudice and Ziehl concerning the relationship between surface tension and adsorption at solid surfaces. The change in "surface tension" accompanying adsorption at a liquid surface can be used as a measure of the adsorption, and the Gibbs equation as quoted by these authors correlates these two conceptions. But, to correlate two conceptions docs not necessarily imply an attempt to explain either, although sometimes such an "explanation" is carelessly inferred. Use of "surface energy per unit area" instead of the numerically equal but more difficult and less definite conception of "surface tension per unit length " would lessen many of the present difficulties. (Compare with Adam.2) At interfaces involving a solid phase, neither &apos;" surface tension " nor " interfacial tension "can have any meaning, but the conception "interfacial energy per unit area" call be understood by anyone who is familiar with the concept of free energy. While it is true that surface energy cannot be directly measured at a solid surface,

Jan 1, 1939

By Ian Wark

IN defending the chemical theory of flotation, Taggart, del Giudice and Ziehl have criticized1 the views of those who prefer to attribute the effects of certain flotation agents to adsorption. Perhaps with some justifica-tion, they describe the latter term as the "haven of refuge of writers lost in a morass of shaky experiment and muddy thinking." We prefer to regard it, however, as a haven of refuge for writers who seek a conven-tional term to describe the formation of films of flotation reagents on solid surfaces, because in many cases it is not yet possible to specify the forces that hold them there. Originally, as Taggart and his associates state, adsorption connoted a. concentration difference and nothing more. In recent years, workers in the field of surface chemistry have tacitly added other meanings, and they now speak of orientated adsorption of unimolecular films on a solid sub-strate, of chemi-adsorption, and of exchange adsorption. Thus the term adsorption may connote-simply the Gibbs layer of excess concentration at the surface of a solution, or a unimolecular film at the surface of a solid. Perhaps this has led to the misunderstanding of Taggart, del Giudice and Ziehl concerning the relationship between surface tension and adsorption at solid surfaces. The change in "surface tension" accompanying adsorp-tion at a liquid surface can be used as a measure of the adsorption, and the Gibbs equation as quoted by these authors correlates these two con-ceptions. But, to correlate two conceptions does not necessarily imply an attempt to explain either, although sometimes. such an "explanation" is carelessly inferred. Use of "surface energy per unit area" instead of the numerically equal but more difficult and less definite conception of "surface tension per unit length" would lessen many of the present diffi-culties. (Compare with Adam.2) At interfaces involving a solid phase, neither "surface tension" nor "interfacial tension" can have any meaning, but the conception "interfacial energy per unit area" can be understood by anyone who is familiar with the concept of free energy. While it is true that surface energy cannot be directly measured at a solid surface,

Jan 1, 1936

By G. E. McElroy

Changes in existing airway and fan-installation conditions offer the most common opportunities for effecting economical operation of mine-ventilating systems, but the largest possibilities for securing this result lie in the original design of the main airways for efficient service. Formulas, and charts for their graphical solution, are presented herewith for the determination of the elements of airways design when the conditions of service are known or may be roughly approximated. Although the analyses are made with particular reference to metal-mine airways, there is no essential difference between main airways in metal and coal mines, and the methods presented are applicable to both. Little attention is paid to designing airways for maximum economy in the ventilation of metal mines. Most of the openings used as main airways are originally designed and used for transportation and other operating purposes. Even where openings are made primarily for ventilation, the possibility of their future use for other operating purposes, or even custom alone, usually results in the selection of a size and shape similar to those of existing openings. Natural conditions, such as heavy ground, often seriously limit the size of opening that can be maintained without excessive expense; and various operating factors, such as velocity limitations on traveling roads, often dictate size requirements in excess of those required for economy in ventilation only. In metal mines the main airways are, as a rule, too small rather than too large for economic service, with the general result that the quantities in circulation are often less than the mine&apos;s proper requirements over long periods, even though excessive amounts of power are applied in an effort to remedy conditions. Increasing the area of an airway increases the cost for excavation and lining practically proportionately but at the same time affects a very rapid decrease in power requirements. The balancing of these two factors of the expense to give a minimum total yearly operating cost for ventilation is mainly a matter of proper original design of the main airways of the mine, since the large volumes handled through these parts of the system involve large power costs and thus present opportunities for effecting large savings through proper design. Many of the factors

Jan 1, 1932

By A. S. Richardson

AIR conditioning, or air cooling, for the improvement of ventilation in the Butte mines has come into increasing use during the past 10 years. In part, the methods practiced have been described in previous publications of the Institute, but some improvements on earlier methods have been made and a number of new features have been developed. This paper is presented as a record of progress made, and for the sake of completeness describes all general features of the work. The need for air conditioning in the ventilation of mines in the district arises from the fact that the temperature of the ground and mine water has shown a very great increase with increase in mining depth, and has now reached a maximum of slightly over 130ºF. The most difficult part of the ventilation problem is the maintenance of temperature and humidity of a satisfactory standard in the working places, especially on the lower levels. Although ordinary ventilation is adequate to maintain good conditions in most of the working places it is subject to a number of limitations at great depth. Most important among these limitations is that with increase in depth the air becomes heated before it reaches the working places, both by compression from increase in atmospheric pressure and by heat transferred to it from rock at high temperature, so that its capacity for lowering temperatures is greatly reduced before it reaches the operating zone. Increasing depth of mining also increases the distance traveled by the air in its passage through the mine, and this causes a corresponding increase in resistance to air flow, so that there is greater difficulty in maintaining even the same volume in circulation. Thus, in the face of a demand that the ventilating system have a very much greater capacity to remove heat from the mine, the tendency is for that capacity to diminish. The only evident alternatives were (I) the opening of additional air shafts to increase the volume of air in circulation, (2) an extension of the existing system that would be subject to the same limitations, or (3) the adoption of an entirely different method such as air cooling. Fortunately for an economic solution of the problem, the mean annual temperature of the surface atmosphere at Butte is about 40°F., with very low relative humidity in summer, so that there is unlimited natural cooling power at a temperature range adaptable to air-conditioning methods. METHODS Two similar methods of air conditioning are used, as necessitated by service requirements and dependent upon the equipment available. In one, which is the more important and has the greater cooling capacity, water is circulated in a closed circuit, and, alternately, first absorbs heat from warm mine air and then dissipates it in the surface atmosphere by cooling at a cooling tower. The second

Jan 1, 1941

By David R. Mitchell, E. A. Reilly, G. R. Gardner, F. P. Lasseter

THE methods that may be applied to the treatment of slurries and water, as these are related to practical coal-preparation problems, are concerned essentially with the movements of solids suspended in water. It is assumed that there are no fundamental differences between the principles involved in the treatment of coal slurries and the phenomena encountered in general mineral-dressing practice, and the latter are-presented in some detail. Basic principles are correlated with present practice for both the anthracite and the bituminous coal fields, and methods are discussed which are designed to utilize best all the material subjected to treatment and suggest a sound approach to the solution of problems relating to the return of clear water to process or to streams. In order to approach the practical phases of the subject with sufficient understanding of the basic principles, it is necessary to discuss two types of phenomena that are applicable. The first is flocculation and the second is sedimentation. Descriptive matter is given covering the various methods and types of equipment employed to conduct these operations, with emphasis on their application to water and coal-slurry treatment. DEFINITION OF TERMS Definitions of terms are consistent with modern developments, and conform, in general, with their usage in mineral-dressing practice. Because of variations in coal-preparation methods, it is impossible to define a rigid upper limit of particle size for a coal slurry or sludge which will apply generally. Limits vary somewhat with the particular treatment method employed at a given plant. For purposes of definition, this limit is chosen as the particle size for which preparation methods such as Chance comes and jigs are usually dispensed with, and other methods, such as the Hydro-tator, tables, and froth flotation, are employed. Generally the limit will be 10 to 6 mesh.

Jan 1, 1950

By H. A. Schwartz

THE spheroidal form of the temper carbon nodules in malleable cast iron and of the graphite mottles of "mottled" cast iron suggests that in both all the graphite in a given mottle or nodule grew from a single center of crystallization or nucleus.? There is, however, a distinct metallo-graphic difference between the mottle and the nodule; the area of mother metal impoverished in combined carbon by the crystallization of graphite in a mottle is practically coextensive with the ramifications of the graphite, while the impoverished zone of metal corresponding to a given nodule is always larger, and usually much larger, than the approximately spherical mass of graphite crystals forming the nodules. Furthermore, the mottle probably is formed during freezing and the nodule almost always at a considerably lower temperature. Assuming that the nodules or mottles can be used as a measure of the existing nuclei, (capable of germination) we propose to record certain observations as to the graphitizing reaction in the light of the number and habits of growth of these nuclei. The present authors, in cooperation with others1-7, have reported upon various cognate aspects of the problem. The fact that temper carbon is a mass of flakes and not a solid granule has become well recog-nized since the introduction of an improved polishing technique8,9,10 for cast iron. The problem of deriving from the circular planar intercepts

Jan 1, 1935

By C Gunther

In the examination of an undeveloped prospect a decision must be arrived at from an inspection of the outcrops and the exposures in a few shallow pits. Prospects that are offered for sale rarely expose any important quantity of good ore, work having usually been stopped when the immediate exploration no longer yielded favorable results. It should be borne in mind, furthermore, that a great majority of prospects have been examined many times, and if of conspicuous promise, would have been acquired for development. In most cases the problem for the engineer, therefore, is to discover the traces of a valuable mineralization that has disappeared through solution, or the conditions that indicate the possibility, or probability, of underlying secondary enrichments. The available data being meager, every feature should be the subject of careful study-the condition of the outcrop, the structural relationships, the associations of minerals, the alterations of wall rocks, the chances for underlying enrichments, and so forth, as well as the actual assay value of the material exposed. It is frequently advisable to spend the time and money necessary to have trenches dug at various significant points along a promising outcrop; such exposures, even if the depth attained is slight, often disclose conditions that are not apparent at the actual surface, as for example, the existence of soft minerals and the distribution of the various minerals through the mass of the deposit. Trenches also permit samples to be taken from points that were not accessible during former examinations. Strong, persistent outcrops of uniform width may be taken to indicate the probable size and character of the underlying vein,

Jan 1, 1932