By Edmund Newton

The steel industry of the United States has depended in the past almost wholly upon imports for its supplies of manganese. Many of the important domestic sources yield ores leaner in their natural condition than the foreign ores the steel industry. has been accustomed to use. To make them available, therefore, either the ores must be concentrated or the practice of the steel industry modified. Roughly 25,000 T. annually of high-grade manganese ores are used for dry batteries for chemical purpose, and in other ways; while approximately 750,000 T. are required for making steel. , By present practice, every ton of steel takes an average of about 14 lb. (1.8 kg.) of metallic manganese. This is generally added to the steel in the form of an alloy, the standard alloys being the 80-per cent. ferro-manganese and the 20-per cent. spiegeleisen, During the year 1917, 286,000 T. of ferromanganese and 193,291 T. of spiegeleisen were made in this country, the former largely from imported ores; and 45,381 T. of ferromanganese. was imported. The metallic manganese represented by these alloys was 304,000 T., the product of roughly 800,000 T. of high-grade ore and 345,000 T. of low-grade ore. Manganese Deposits in the United States Before the war manganese ore was mined in relatively small quantities in the Appalachian region, including Virginia, Tennessee and Georgia, and in Arkansas, but owing to the increase in prices during the past three years manganese mining has been undertaken also in Montana, California, Arizona, New Mexico, Nevada, Utah, and Minnesota. From data now available it appears that in this country deposits of high-grade manganese ores are usually small, while materials lower in manganese and higher in iron occur in appreciable quantities. Our total quantity of manganese-bearing material is relatively large, but on

Jan 1, 1920

By Harold S. Morgan

INTRODUCTION The Waste Isolation Pilot Plant (WIPP) is being developed in southeastern New Mexico by the United States Department of Energy as a research and development (R&D) facility to demonstrate the safe disposal in salt of radioactive wastes resulting from defense activities. As part of the WIPP R&D program, a series of in situ tests will be performed to determine the behavior of drifts and storage rooms in the creeping salt medium (Matalucci, et al. 1982). Data obtained in these tests will be used to evaluate and improve numerical models used to compute the structural response of these drifts and rooms. Stress has been proposed as one of the parameters to be measured in the tests, and borehole inclusion stressmeters have been included in the instrumentation package. Cages of this type provide an indirect measurement of stress change in that they actually monitor borehole displacements which are then related to changes in the in situ stress away from the borehole. The relationship between stress and displacement is highly dependent upon the constitutive behavior of the rock in which the gage is emplaced. This relationship is well understood for rocks with linear stress-strain behavior (Fossum, et al, 1976), but, for creeping rocks like salt, the relationship has yet to be determined. Thus, inclusion gage response in salt must be investigated fully before stress measurements from the WIPP in situ tests can be used for comparisons with computed stresses The calculations presented in this paper were performed as part of an investigation of inclusion stressmeter performance in salt. They focus on the strain gaged stressmeter (SGS) (Cook and Ames, 1979) and on a hypothetical solid cylindrical inclusion with variable stiffness Issues addressed include the effects of creep and the effects of gage stiffness on stressmeter output for various loading conditions. The

Jan 1, 1984

By W. A. Wood, W. H. Reimann

A study is made of the creep that can be induced in armco iron at room temperature by superposing small amplitudes of alternating torsion on a tensile creep load. It is shown that the creep differs from that in comparable tests on copper in being trmsient only. At the same time, though transient, the creep can produce extensions of some 10 pct under creep loads less than the tensile yield stress of the material. The creep can be largely suppressed b$ applying cyclic strain of suitable amplitude before applying the creep load and the metal thereby stabilized. At room temperature, plastic flow in a metal under steady load is normally limited by strain-hardening processes. However, if a small cyclic stress is superposed on the steady load these processes may be more or less neutralized and, as shown in recent investigations,'-4 plastic flow may continue. In this way annealed copper, for example, can be induced to creep continuously to fracture under loads as small as 1 tsi. Dislocation mechanisms possibly responsible for this room-temperature creep have been usefully reviewed by Feltner.But discussion so far has been based mainly on creep as it is found in close-packed metals initially in the annealed state, and their behavior may not be general. In fact, recent work shows that the form of creep in annealed copper is different from that even in cold-worked copper;7 the creep thus depends on the dislocation pattern already in a metal as well as on the metal itself. This paper describes the creep in annealed armco iron, tested in the same way as the above-mentioned copper. One object was to see how creep in a typical bcc metal compared with that in the annealed close-packed metals. Another object was to utilize the fact that a bcc metal like iron has a more pronounced elastic range than close-packed metals like copper and to find to what extent the creep load or superposed cyclic stress had to exceed their re-

Jan 1, 1964

By S. L. Couling, D. J-P. Adenis

i2) twinning in poly crystalline magnesium does not usually occur homogeneously but is concentrated in localized regions or bands inclined at about 45 deg to the stress axis. These bands of twinning are in many ways similar to the Luders bands seen in mild steel alzd Al-Mg alloys. Within a hand the percentage of the volume twinned may approach 100 with no twinning outside the band. Bands are not produced in specimens of grain size a3 x 10-= in. or in samples deformed at temperatures 300°F. Annealing of heavily twinned regions leads to re crystallization textures markedly different from those found in the starting material. The exact preferred orientation appears to depend on the starting grain size, the amount of compres-sive strain and the manner in which it is introduced. MAGNESIUM, with its hexagonal crystal structure, deforms plastically at room temperature by a variety of deformation mechanisms, one of the most important of which is (1012) twinning. In single crystals such twinning occurs on compression parallel to the basal plane or tension perpendicular to it. In wrought polycrystalline magnesium, such as rolled sheet, the preferred orientation is such that almost all the grains have their basal planes nearly parallel to the sheet surface. Therefore, if sheet material is deformed by cold rolling or by tension in the plane of the sheet, deformation of the grains by (1012) twinning is not favored. On the other hand, twins form readily on compression parallel to the plane of the sheet as in a compression test, on the compression side of a bent sample, or at the outer rim of a drawn cup. The first part of this paper deals with the morphology of (1012) twinning in polycrystalline magnesium. Some aspects of this subject were covered by Barrett and ~aller.' Of direct bearing on the work to be reported here are the comments of Jetter' in discussion to Ref. 1. He shows that Mg + 1.5 pct Mn alloy sheet when bent about a transverse axis develops a pattern of transverse bands on the surface of compression. A longitudinal section through the sheet shows that the bands are wedge-shaped and inclined to the rolling direction. The bands were identified as "outcrops of regions in which deformation is localized as the result of the reorientation brought about by (1012) twinning". The second part of the paper treats the recrys-tallization texture of the specimens twinned by compression. Magnesium deformed and then annealed generally recrystallizes with no change in orientation.1'3'4 This statement is true provided that the amount of (1012) twinning occurring during deformation is small. In an isolated observation, Anse15 has shown that, when deformation produces much (1072) twinning, annealing causes new maxima to appear in the pole figure. The second part of the paper elaborates on this point. I) MATERIALS AND PROCEDURES All of the experimental work to be reported was done using the commercial sheet and plate alloy AZ31B (nominal composition: 3 pct Al, 1 pct Zn, 0.4 pct Mn, balance magnesium). This alloy is available commercially in two tempers, -0 (fully annealed) and -H24 (partially annealed), and specimens of both tempers were used in various experiments. The average grain. diameter (AGD) for -0 temper 0.125-in. sheet is about 0.5 x 10- in.; where material of larger grain size was desired, anneals at elevated temperature were used to grow the grains. compression tests were made on a screw-driven "hard" machine. The specimens were clamped in a

Jan 1, 1964

By Vittal S. Bhandary, B. D. Cullity

Swaged iron wire has a cylindrical {001} <110> texture. The texture is also cylindrical after re-crystallization in the absence of a magnetic field, but <111> and <112> components are added to this texture when recrystallization occurs in a field. The mecizanical properties in tension and in torsion are not greatly altered by these changes in texture. AS shown in a previous paper,1 cold-worked wires of the two fcc metals copper and aluminum can be made relatively strong in torsion and weak in tension, or vice versa, by proper control of preferred orientation (texture). The deformation texture can be controlled by selection of the starting texture (texture before deformation), because certain initial orientations are stable during deformation. The present paper reports on similar work performed on bcc iron. In this case it was clear at the outset that there was no hope of controlling the deformation texture, which is one in which <110> directions are aligned parallel to the wire axis. (1t has usually been regarded as a fiber texture, but Leber2 has recently shown that it is a cylindrical texture of the type {001} <110>. In either case, <110> directions are parallel to the wire axis.) There is general agreement on this texture among a large number of investigators, which in itself suggests that the starting texture has no influence on the deformation texture. More direct evidence was produced by Barrett and Levenson,3 who reported that iron single crystals of widely varying initial orientations all had a single <110> texture when cold-worked into wire. Thus <110> is a truly stable end orientation for iron and probably for other bcc metals as well. Under these circumstances attention was directed to the possibility of controlling the recrystallization texture. This texture is normally <110> in iron,4 just like the deformation texture. However, it is conceivable that this texture could be modified by a proper choice of the time, the temperature, and what might loosely be called the "environment" of the recrystallization heat treatment. In the present work the environmental factor studied was a magnetic field. The effect of heating in a magnetic field ("magnetic annealing") on recrystallization texture has been investigated by Smoluchowski and Turner.5 They found that a magnetic field produced certain changes in the recrystallization texture of a cold-rolled Fe-Co alloy. The texture of this material is normally a mixture of three components, and the effect of the field was to increase the amount of one component at the expense of the other two. Smoluchowski and Turner concluded that the effect was due to magnetostriction. With the applied field parallel to the rolling direction, the observed effect was an increase in the amount of the texture component which had <110> parallel to the rolling direction. In the Fe-Co alloy they studied, the magnetostriction is low in the <110> direction and high in the <100> direction. Thus nuclei oriented with <110> parallel to the rolling direction will have less strain energy than those with <100> orientations and will therefore be more likely to grow. In a later paper on the same subject, Sawyer and Smoluchowski6 ascribed the effect to magneto-crystalline anisotropy and made no mention of magnetostriction. In the papers of Smoluchowski et al. the intensity of the magnetic field was not reported but it was presumably large, inasmuch as it was produced by an electromagnet. In the second paper6 it is specifically mentioned that the specimens were magnetically saturated. But if magnetostriction has a selective action on the genesis of stable nuclei during recrystallization, that selectivity must depend only on differences in magneto-strictive strains between different crystal orientations and not on the absolute values of those strains. Thus the saturated state does not necessarily produce the greatest selectivity, because the relative difference in magnetostrictive strains between different crystal directions may be larger for partially magnetized crystals than for fully saturated ones.7 In the present work the specimens were subjected to relatively weak fields (0 to 100 oe) produced by solenoids. MATERIALS AND METHODS Armco ingot iron rod (containing 0.02 pct C and 0.19 pct other impurities) was swaged from 0.25 in. in diam. to 0.05 in., a reduction in area of 96 pct. The mechanical properties in tension and torsion were measured as described previously.&apos; Textures were measured quantitatively with chromium or iron radiation and an X-ray diffractometer,8,1 and

Jan 1, 1962

By W. J. Keep

Cast-iron, or pig-iron, is iron which contains all the carbon that it could absorb during its reduction in the blast-furnace. As is well-known to chemists, carbon exists in cast-iron in two distinct forms. In chemical union, as "combined" carbon, it cannot be discerned, except as it may increase the whiteness of the fracture, in so-called white iron, or carburetted iron (sp. gr. about 7.72). Carbon mechanically mixed with the iron as graphite is visible, varying in color from gray to black, while the fracture of the iron, according to the color and amount of graphite it contains, ranges from a light to a very dark gray. The specific gravity of graphitic iron is about 7.40. Silicon in cast-iron is evidently to some extent combined with the iron and the carbon ; but whether it exists also in a form corresponding with graphitic carbon, mechanically mixed with the remaining mass, is a question still in dispute, which we have not in this paper endeavored to answer. It has been the opinion of many writers on metallurgy, and many foundry men, that silicon is in every way injurious to cast-iron. Yet

Jan 1, 1889

By Richard M. Foose

Most of the roofing granules produced in Pennsylvania are made by two companies at three plants. The Advance Industrial Supply Co. has three quarries and a mill at Gladhill Station, in southern Adams County. The Funkhouser Company is actively engaged in mining, quarrying and milling at Charmian, about one mile west of Gladhill Station, and at Delta, in southern York County. These three plants produced approximately 100,000 short tons of granules in 1943. The production of rooling granules in 1937 for the whole country was only about 500,000 tons, generally indicating the large growth of the industry since that time. The fundamentals of producing roofing granules were discussed comprehensively by G. W. Josephson in a paper before the Industrial Minerals Division in October 1943 (TP 1725, this volume page 460). The purpose of this paper is to describe the actual methods of mining the rock and milling it to make roofing granules, as practiced by the three Pennsylvania plants. Mining and Milling Funkhouser Company (Delta) The Funkhouser Company, near Delta, in southern York County, Pennsylvania, operates three joined quarries and a mine in the Peach Bottom slate. The joined quarries extend 1200 ft. in a northeast-southwest direction along the strike of the slate cleavage and are about 200 ft. .wide. The working face is about 45 ft. high. The quarrying operation is rather simple: Ingersoll-Rand Jackhamers, I-in. and 1 1/4-in., with hollow drill steel, are used to undercut the quarry face with 10-ft. holes. The face is "blown" and allowed to slump on the quarry floor. Loaded by a Marion electric shovel into trucks, the shattered rock is taken to the primary crusher 2500 ft. away. In addition to the normal quarrying operations, a drift into the northeast wall of the middle quarry was begun about 1935, and has advanced about 2000 ft. since then. Rooms have been driven at angles to the drift along choice beds of slate. The drifts and rooms have a roof more than 35 ft. high and the main drift and rooms are all more than 40 ft. wide. There is no cribbing at any place in the mine. Several of the rooms were driven upward on a 5&apos; slope and in some of them there was stop-ing. Ingersoll-Rand Jackhamers are used, and only wet drilling is practiced. When visited in January 1940, an electric shovel was operating at the head of the drift, scooping up the slate blasted out of the working face. This, too, is trucked to the primary crusher. Some of the better quality slate is saved for making slate shingles. The primary crusher, which is a No. 30 McCulley gyratory, receives the slate from the trucks and crushes it to about a-in. size (Fig. I). This product travels by a 30-in. belt conveyor to Niagara vibrating screens with 2-in. holes. The minus a-in. product moves to a storage silo by bucket

Jan 1, 1948

By Richard M. Foose

Most of the roofing granules produced in Pennsylvania are made by two companies at three plants. The Advance Industrial Supply Co. has three quarries and a mill at Gladhill Station, in southern Adams County. The Funkhouser Company is actively engaged in mining, quarrying and milling at Charmian, about one mile west of Gladhill Station, and at Delta, in southern York County. These three plants produced approximately 100,000 short tons of granules in 1943. The production of rooling granules in 1937 for the whole country was only about 500,000 tons, generally indicating the large growth of the industry since that time. The fundamentals of producing roofing granules were discussed comprehensively by G. W. Josephson in a paper before the Industrial Minerals Division in October 1943 (TP 1725, this volume page 460). The purpose of this paper is to describe the actual methods of mining the rock and milling it to make roofing granules, as practiced by the three Pennsylvania plants. Mining and Milling Funkhouser Company (Delta) The Funkhouser Company, near Delta, in southern York County, Pennsylvania, operates three joined quarries and a mine in the Peach Bottom slate. The joined quarries extend 1200 ft. in a northeast-southwest direction along the strike of the slate cleavage and are about 200 ft. .wide. The working face is about 45 ft. high. The quarrying operation is rather simple: Ingersoll-Rand Jackhamers, I-in. and 1 1/4-in., with hollow drill steel, are used to undercut the quarry face with 10-ft. holes. The face is "blown" and allowed to slump on the quarry floor. Loaded by a Marion electric shovel into trucks, the shattered rock is taken to the primary crusher 2500 ft. away. In addition to the normal quarrying operations, a drift into the northeast wall of the middle quarry was begun about 1935, and has advanced about 2000 ft. since then. Rooms have been driven at angles to the drift along choice beds of slate. The drifts and rooms have a roof more than 35 ft. high and the main drift and rooms are all more than 40 ft. wide. There is no cribbing at any place in the mine. Several of the rooms were driven upward on a 5&apos; slope and in some of them there was stop-ing. Ingersoll-Rand Jackhamers are used, and only wet drilling is practiced. When visited in January 1940, an electric shovel was operating at the head of the drift, scooping up the slate blasted out of the working face. This, too, is trucked to the primary crusher. Some of the better quality slate is saved for making slate shingles. The primary crusher, which is a No. 30 McCulley gyratory, receives the slate from the trucks and crushes it to about a-in. size (Fig. I). This product travels by a 30-in. belt conveyor to Niagara vibrating screens with 2-in. holes. The minus a-in. product moves to a storage silo by bucket

Jan 1, 1948

By A. Ghosh, T. B. King

The kinetics of the discharge reaction: 20&apos;- (in silicate melt) = O,(g) + 4e- at a platinum anode in lithium silicate melts have been studied al 1350°C by galvanostatic methods. Plots of the sleady-state overpotential, q, as a function of the logarithm of the current density, i, showed injlections and were linear only at high current densities. The value of the overpotential was influenced by bubbling gas through the electrolyte. The ocer potential was also studied as a function of time. The rise and decay of overpotential were very slow processes. At low current densities transport is the likely rate-controlling process but at high current densities passivation of the electrode, Presumably by an oxide film on the surface, seems to be a contributory functor. IT is well-established that molten silicates behave as electrolytes&apos;5 and, except in a few cases,6 conduction is entirely ionic. Moreover, it is supposed that a possible, and perhaps predominant, mechanism for phase boundary reactions between metals and slags is similar to that in corrosion whereby anodic and cathodic processes occur at unrelated sites, the metal serving to conduct electrons.1&apos;8 Thus electrochemical studies of some slag-metal reactions would seem to be a useful way to diagnose the rate-controlling steps in the overall reaction. The electrochemical method is, in principle, a better diagnostic tool than the direct chemical method for the following reasons: 1) The partial electrochemical reactions, which are simpler than the overall reaction, may be studied individually. 2) The rate of reaction can be controlled at will and independently of the concentrations of reactants. 3) Fast reactions can be studied by relaxation methods.&apos; Esin and his coworkers5&apos;10"12 have pioneered such studies in silicates and have deviloped some ingenious techniques. Not all of their findings, however. can be accepted without a good deal of further work. In this investigation, the kinetics of the oxygen discharge reaction: 202- (in silicate melt) = Oz(g) + 4e- [I] at a platinum electrode were studied by both steady-state and transient galvanostatic techniques. Interest in this reaction was first developed as a result of the findings of Fulton and chipman13 that the reduction of silica, in a silicate slag, by carbon, dissolved in liquid iron, is a very slow reaction. Subsequent work, for example, by Rawling and ~lliott,&apos;~ has demonstrated that the reaction under these conditions must be slow, because the rate is limited by diffusion of oxygen in the iron to the metal-crucible phase boundary at which a CO bubble may be nucleated. Further work by Tarassof,&apos;~ in which the reduction of silica by aluminum dissolved in copper was studied, has shown that under these conditions, where carbon monoxide evolution is not involved, control of the reaction rate resides in diffusion of silica in the slag phase. However, there is no practical way of inducing sufficient convection in the system to make it clear that the phase boundary reaction is indeed fast. The overall reaction of silica reduction involves the discharge of silicon ions at cathodic sites and oxygen ions at anodic sites. In the examples cited, the discharged ions are dissolved in a liquid metal. In the present study of oxygen ion discharge, gaseous oxygen may be evolved at high current densities or oxygen may simply dissolve, possibly as oxygen molecules, in the silicate at very low current densities. The discharge of an oxygen ion at an anode must, in silicates less basic than the orthosilicate composition, be preceded by a reaction in the vicinity of the electrode, such as: which makes oxygen ions available. Platinum was chosen as the working electrode since it is comparatively inert to oxygen and is, therefore, expected to come rapidly into equilibrium with the electrolyte and with gaseous oxygen. Minenko, Petrov, and Ivanova16 have measured the electromotive force at a platinum electrode in molten silicates as a function of the partial pressure of oxygen in the atmosphere, the concentration of oxide ions in the melt, and the temperature. They found platinum to behave as a reversible oxygen electrode. At two different oxygen pressures, Po2 (I) and Pq (11). the electromotive force is given by: where F is the Faraday constant, equal to 23,060 cal per v equivalent, indicating that the electrode reaction is as written in Eq. [I.]. Platinum has been similarly used in molten silicates by other inve~ti~ators. "&apos;~~ In this investigation platinum was used only as an anode, since a current deposits other elements on its surface and changes its characteristics.

Jan 1, 1970

By H. F. Webster, C. G. Dunn

Rolling md annealing procedures are described for developing the (110) preferred orientation in tantalum for use as a thermionic-emission materinl where electrodes of a uniform high work function are needed. The development of a (110) [001] annealing texture is also reported. A preferential growth process due to low (110) gas-metal surface energy is considered in explanation of the observed growth of (110) grains. ThE growth of (110)-oriented grains in thin strips of rolled zone-refined tantalum, previously discussed briefly,&apos; is reported together with more recent information on the formation of a (110)[001.] annealing texture, i.e., one where the [001] direction of each grain lies close to the rolling direction. The development of tantalum sheet with a (110) preferred orientation (position of [001 ] directions unspecified) is of importance as a thermionic-emission material in thermionic-energy converters. Since therm ionic-emission properties of cesium-coated crystals vary over a wide range depending on (hkl) a2-7 a single (hkl) preferred orientation is more useful than either several preferred orientations or none. Furthermore, the (110) preferred orientation yields the highest thermionic-emission density for a cesium coverage of less than a monolayer.5-7 A consideration of the stability of the grain structure needed at high operating temperatures suggests that the preferred orientation itself should be produced by annealing processes. Information on annealing textures in tantalum, however, is rather limited. Pugh and Hibbard 8 obtained (111)[112] and (lll)[112] components in a 1400°C recrystallization texture in 95 pct cold-rolled foil; these components were enhanced on annealing at 2500°C. Muller9 rolled 99.97 Ta to 90 pct reduction in thickness in the final stage and noted only a slight sharpening of the rolling texture, with some intensification of the (111)[112] component upon annealing at 1200°C. The experimental procedure followed in the present work stemmed from the idea of using possible differences in (hkl) surface energies to provide a small driving force for growth of grains having the lowest (hkl) surface energy.l0* This would mean using high-purity tantalum processed into thin sheet form and annealed at high temperatures either in a noncontaminating atmosphere or in one producing additional sample purification. EXPERIMENTAL Zone-Refined Tantalum. National Research Corp. tantalum in the form of 1/8-in.-diam rod and of 99.98 purity (53 ppm 0, 15 ppm N, and 8 ppm C) was zone-melted four times. The traversing speed was 4 mm per min. Such treatment increased the resistance ratio, R293k/R20K , where R293K is the resistance of the specimen at 20°C and R20K the re-resistance at liquid-hydrogen temperature, from a value of 25 for the initial rod to 175 for the zone-refined rod (the increase in the resistance ratio provides a measure of purification11,12). Part of a zone-refined rod was rolled unidirec-tionally to a strip 0.003 in. thick and 0.28 in. wide. Samples were given anneals in the range 1300" to 2100°C using ac conduction heating in an oil-free vacuum system. Recrystallization to small grains appeared to be complete at 1300°C. Large grains were formed at higher temperatures, but these were not entirely strain-free, some grains showing asterism in Laue X-ray patterns and some displaying a range in orientation. Part of the difficulty was caused by thermal expansion of the tantalum strip as it was held between fixed supports. However, in a different arrangement with the tantalum freely suspended in a tantalum can, high-frequency induction heating in vacuo at about l0-6 Torr produced

Jan 1, 1964

By N. L. Carwile, G. W. Geil

A metallographic study was made of deformation twinning (Neumann lamellae) in ingot iron slowly deformed in tension at —196O and —150°C. The results showed that twinning is initiated mainly during the initial stages of plastic deformation. However, the breadth of the twins generally increases with increase in strain up to fracture of the specimen. HE results of an investigation of the effect of low I temperatures on the flow, fracture, strain hardening, and strain aging characteristics, and the true stress-strain relationship for specimens of ingot iron deformed in tension were reported recently.1,2 In that study specimens of ingot iron, in different initial conditions, were slowly deformed in tension at various temperatures between —196" and +100°C. A phenomenon observed, but only briefly reported, was the formation of deformation twins (Neumann lamellae) in the specimens deformed at the lower temperatures. Preliminary metallographic examination of these specimens indicated that there was apparently some correlation between the deformation twinning and the strain of the specimen and that this factor merited further investigation. Some recent investigations have indicated a direct association of Neumann lamellae and the fracture of the metal. Bruckner".&apos; * postulated that the twinning immediately precedes the fracture and the latter is initiated by the stopping of the propagation of twins, either at subgrain boundaries or at other structural features. Tipper and Sullivan5 postulated that Neumann lamellae are initiated by the shock or a shock wave set up at fracture in the still highly stressed unbroken metal, and that a high rate of deformation is a necessary condition for their formation. An extensive metallographic examination, therefore, was made of many of the specimens used in the study of ingot iron at this Bureau and of additional specimens deformed to selected strains under various conditions. The present paper summarizes the effects of deformation under these conditions upon the breadth and scope of the deformation twins. Other features of twinning will be discussed in another paper. Material and Testing Procedure All of the specimens were prepared from one lot of ingot iron, as hot-rolled, of chemical composition other than iron as follows: C, 0.02 pct; Mn, 0.02; P, 0.005; S, 0.018; Si, 0.002; Cu, 0.10; 0, 0.058; and N, 0.002. Cylindrical tensile specimens with a 2 in. gage length were used. The reduced section was slightly tapered from each end; the diameter (0.438 in.) at the midsection of the gage length was about 0.003 in. less than at the ends. The specimens were finished to the final dimensions by grinding and polishing in the axial direction. The ends of the specimens were machined with 3/4 in. x 10 threads and the shoulder fillets were machined to a radius of 0.75 in. The specimens were extended slowly in tension (deformation rate less than 0.5 pct reduction in area per minute) while immersed in an appropriate cryogenic liquid maintained at the desired temperature. The minimum diameter of the specimen was measured during the test by means of a specially designed reduction of area gage accurate to 0.0001 in." A detailed description of the testing equipment and the method of maintaining the desired temperature is given in a previous paper.&apos; Each specimen, after deformation to a specified strain at a selected temperature, was sectioned longitudinally and examined metallographically. The preparation of specimens for metallographic examination was carried out in the usual manner by mechanical polishing and etching. Results and Discussion Deformation twins in specimens of ingot iron extended slowly in tension at —196" and —150°C are shown by the representative micrographs of Figs. 1

Jan 1, 1954

By B. F. Oliver, F. Garofalo

Gas-metal heterogeneous reactions and zone-lrelting were sinultarneously employed to produce several high-purity irons with low interstitial contents in a levitating- zone melter. Successive zone-tneltitzg pusses were made in carious sequences of atmospheves which included prepuvified tank hy-drogeta, water vapor hydrogen, palladiuril-purified hydrogen, and vacuunm of 2 x 10-6 Torr. Different irons ranging in purity from 99.89 to 99.996 pct with residual curbon contents of 17, 8 to 10, and 3 to 5 ppm have been Drepared. No measuvable gradient in the residual carbon content was observed along the entire zone-melted length (6-10 in.) in I-ilz.-diameter bars. The absence of a carbon-concentration gradient in the solid indicates an apparent distvihution coefficient of 1, an unusual condition. Internal friction, solid-state extraction, and hot-hardness results indicate that the level of mobile carbon in a iron depends on the gas-metal heterogeneous reactions employed. Purification under an oxidizing atmosphere resulted in the immobilization of nearly all of the carbon present at leuels of 10 ppm or less. Continuation of purification in a reducing atmosphere veturued the carbon to a state of mobility which was aguin reversed by further purification in all oxidizing atmosphere. The immobilization of curbon at "vesidual levels " is believed to be associated with a strong interaction between carbon and oxygen atoms. frons with low carbon and nitrogen contetzts which did not exhibit a hot-hardness peak were produced after zone ynelting in vacuum. CARBON, nitrogen, and oxygen have strong and well-known effects on many properties of iron. These effects persist even at concentrations of 5 to 20 ppm. The intent of the present investigation was to establish procedures for the preparation of high-purity iron with concentrations of these elements in the range of 5 to 20 ppm and lower. The results reported here deal with the procedures employed to prepare high-purity iron, and with observations on the behavior of certain elements at "residual levels": particularly carbon. The details of the (levitating) zone melter in which the final purification steps are performed and the necessary control of the pertinent solidification variables have been described previously.1,2 MATERIALS AND PROCEDURES Commercial electrolytic iron was induction vacuum-melted and cast into 30-lb ingots. Melt additions and ingot analyses for carbon, oxygen, and nitrogen are noted in Table I. All ingots were melted in stabilized zirconia crucibles conditioned with one iron wash heat. Middle sections of the ingots were forged to 1-1/4-in. rounds, machined to 1-in.-diameter bars, then cut to 36-in. lengths. The zone-melting operations were performed on six iron bars (A to F) at a freezing velocity of 2 in. per hr with the freezing interface rotating2 at 200, 300, or 400 rpm. Liquid zones were passed through the bars in various sequences of atmospheres, Table 11, including prepurified tank H2, palladium-purified Hz, wet H2, and system vacuum of 2 x 1018 Torr. Wet-Hz atmospheres were obtained by bubbling palladium-purified Hz through water exhibiting a resistance of 3 megohms. This water was heated with a platinum-immersion heater and was degassed prior to use. Zone melting in a wet-HZ atmosphere resulted in oxidation of the elements which are oxi-dizable with respect to iron. Fine oxide particles were observed on the surface of the liquid zone, and were encased in the bar surface with the passage of the molten zone. Between each zone pass, the surface of the bar was removed by filing and deep etching; this was continued until the oxide formation ceased. The filings were magnetically separated and the residues analyzed by optical spectroscopy. These were especially high in silicon and manganese. Samples were removed from the iron bars, with few exceptions, following each zone-melting operation. A 0.08-in.-thick disc was cut with an Al2O3 cut-off wheel at a point 1/2 in. above the beginning of freezing. Material from each disc was used for hot-hardness measurements, resistivity-ratio measurements, and carbon, nitrogen, and oxygen analyses. Analyses for most other elements were

Jan 1, 1965

By Harmon D. Nine

DISCONTINUITIES in the strain vs cycles to failure (S-N) fatigue curves have been reported for polycrystalline materials by Porter and Levy for copper,&apos; by Benham and Ford for mild steel,&apos; and by Williams and Stevens for 18/5 stainless steel.3 However, the considerable scatter of the points for polycrystalline materials have made a statistical analysis of the data necessary to confirm the discontinuities. By using oriented single crystals of high-purity material and low grown-in dislocation content, the reproducibility has been improved to a degree which makes statistical analysis unnecessary and clearly shows discontinuities in the S-N curves. A recent publication4 reports an abrupt change of slope in the S-N curve for ( 100) axially oriented copper single crystals fatigued in torsion. The reported discontinuities in the S-N curve, along with a different mode of failure in the two branches of the curve, have been interpreted as being due to two different amplitude-dependent mechanisms. Further work on copper single crystals of (111) axial orientation has now been completed which supports the existence of an amplitude-dependent change in the mechanism of fatigue. In the present study torsional-fatigue experiments were performed at room temperature in air on (111) axially oriented single crystals. The crystals were grown and prepared as reported in Ref. 4. Two different methods of growing the crystals also discussed in Ref. 4 produced crystals of two different perfections: Type I with dislocation density of >l06 per sq cm and Type I1 with dislocation density of <l05 per sq cm. In accordance with the accepted hypothesis that crystal flaws are primarily responsible for the scatter of fatigue lifetimes, particularly at low amplitudes, the values for the three lowest amplitudes for Type I crystal are believed to be uncertain. They are marked in braces in Fig. 1. On the other hand, at amplitudes above a surface shear strain (SSS) of *0.003, the data for both types of crystals are in agreement. Most remarkably the S-N curve for torsional fatigue of (111)-oriented single crystals is composed of three segments separated by rather large discontinuities, Fig. 1. Metallographic and X-ray measurements indicate that the lower branch corresponds to the low-amplitude (F) region of the (100) copper single-crystal results as discussed in Ref. 4, and the two upper branches correspond to the high-amplitude (H) region. The lower discontinuity in the (111) S-N curve and metallographic evidence give further support to the hypothesis that different mechanisms of failure operate for high and low strain amplitudes. Reference to the resolved shear stress diagram, Fig. 2, shows that the highest stressed systems in

Jan 1, 1965

The practice of fine-grinding is now being so succeesfully carried on in some fields, notably in West Australia, and its advisability has been so frequently pointed out,l that the matter in this paper is not put forward as new; its chief object being to call attention to the importance of fine-grinding in the treatment of comparatively low-grade oree. I&apos; have been engaged daring the last five years in the cyanide-treatment of ores in the Ohinemuri district (North Island), New Zealand, and I consider that, in the near future, extremely fine-grinding (almost sliming) will become a very im-

Jan 1, 1906

By J. L. Huitt, B. B. McGlothlin

The introduction of new fracture propping agents that are brittle but much stronger than sand created the problem of what loading strength is required for a propping agent to be effective in a given formation. It is shown that the load at which the propping agent crushes should exceed the load at which total embedment in the fracture faces is possible. Simple laboratory tests to determine loading strength of the propping agent and embedment in the fracture faces, and use of these data in selecting a propping agent for a given formation, are discussed. INTRODUCTION One of the most important factors in the design of hydraulic fracturing treatments is the selection of a propping agent that can effectively provide the fracture flow capacity needed for stimulation of a well. Sand, once generally accepted as being synonymous with propping agent in hydraulic fracturing, is now recognized as having limited effectiveness in many formations because of its low resistance to crushing. Sand particles are brittle and have relatively low strength. Because of this property, sand particles are crushed in rocks that offer high resistance to the penetration of fracture faces by the proppant particles when the fracture attempts to close under the action of the overburden load. For rocks that offer a high resistance to penetration, deform able particles are more effective propping agents than sand. However, for this same type of rock, a propping agent that does not deform, yet does not crush, is often more effective. Thus, a rigid propping agent with sufficient strength to prevent crushing is desirable. A method for determining the strength required for a rigid propping agent to function effectively in given formations is discussed. BEHAVIOR OF RIGID PROPPANTS AND FRACTURE FACES RELATED STUDIES An early qualitative description of the reaction of propping sand in fractures was given by Hassebroek et al.&apos; In discussing fracturing in deep wells, the authors mentioned that even though propping sand entered the fractures, a high flow capacity did not result due to crushing or embedding of the propping sand. Dehlinger et al.2 in discussing the reaction of propping sand surmised that, because of the hardness of sand particles, deformation occurred in the fracture faces contacting the propping sand. In later studies,3,4 methods of determining the embedment of propping sand in fracture faces of soft rock and the critical load at which propping sand is crushed by the fracture faces in hard rock were discussed. In working with de-formable proppants, Kern et al. considered proppant particles to be deformed into cylindrical disks by action of the overburden and then pressed slightly into the fracture faces by further action of the overburden. Rixie et al.&apos;0 reported on embedment pressure and presented a method of selecting a propping agent for use in given formations. The propping agents included sand, walnut shells and aluminum pellets. All these studies have contributed materially to a better understanding of propping agent behavior; however, the strength of brittle proppants (sand, glass and ceramics) required to result in embedment rather than crushing has not been discussed. This topic will be covered in the ensuing discussion. PROPPANT PARTICLE CRUSHING—-EMBEDMENT For this discussion, a rigid propping agent is considered to be one that is brittle and fails under tensile stress when loaded to a critical value. In an earlier study4 it was shown that the Hertzian4 loading theory could be applied to a spherical brittle propping agent if the propping agent and fracture faces behaved elastically. At the failure of the proppant, the ratio of the load to the square of the diameter of the particle should be constant for a given material combination, or: Lc/dp2=C ............(1) A partial derivation of this equation from proppant and formation properties is included in the Appendix. Should a rigid particle not be crushed as a load is applied, it embeds in the fracture faces. A study3 of particle embedment in fracture surfaces has been published. The embedment can be described by an equation based on Meyer&apos;s metal penetration hardness relationships: d1/dp=B 1/2[L/dp2]m/2..........(2) In Eq. 2, B and m are constants that are characteristic of the rock; the significance of the other terms is shown in Fig. 1. A STANDARD DEFINITION FOR PROPPANT LOADING STRENGTH Eq. 1 is useful in appraising propping agent strength," but it is strictly applicable only when the area of contact between a particle and a fracture face (or loading plate)

Jan 1, 1967

By S. E. Bretherton

Discussion of the paper of S. E. BRETHERTON, presented at. the San Francisco meeting, September, 1915, and printed in Bulletin No. 104, August, 1915, pp. 1595 to1599. ANTON EILERS, Brooklyn, N. Y. (communication to the Secretary*). While the advantages in the use of high-line siliceous slags in lead smelting which Mr. Bretherton discusses in this paper are obvious under certain economical conditions, he gives me credit for the introduction of such slags when it does not belong to me. It is true I did considerable experimental work, off and on, for the purpose of finding such slags, while at the Germania in 1877 and 1878, but I did not have occasion to introduce any such slags for regular work, because I had no ores which fitted the economical conditions for using high silica and high lime, except in isolated cases for very brief periods. On the contrary, the ores I had to treat were mostly very ferruginous and very low in silica, so that, economically, I was compelled to run nearly always on slags, which allowed me to use the abundant flux I had without cost. It was August Raht who first had occasion to establish and use for long periods a slag high in silica and line, and low in iron. This was when he was confronted with the task of smelting the. Horn-Silver ores at the smelting works at Franklin, Utah, with as little expenditure for fluxing material as possible. I was at that time in Leadville, Col., where, in the new works I had built, the Billings and Eilers smelters, I had occasion to use profitably many slags, but never anything as high in the earthy bases and in silica as Mr. Raht had to use.

Jan 12, 1915

By George Rice

THE A.I.M.E. Ground Movement and Subsidence Committee, pro-posed in 1920, held its first technical meeting in February 1923, under the able chairmanship of Mr. H. G. Moulton. The following list of papers and discussions, indicating the scope of the problems and relation to various conditions and method of mining, were given at that meeting by the distinguished mining engineers: J. Parke Channing, on Subsidence at Miami, Arizona; Howard N. Eavenson, on Mining an Upper Bitu-minous Seam after a Lower Seam Has Been Extracted; J. J. Rutledge, on Subsidence in Two Oklahoma Coal Mines; Benjamin F. Tillson, on Caving Cracks at the Franklin Mine, New Jersey; Dr. F. W. McNair, on the Dome Theory; William Kelly, on disadvantageous effects in Mining and Back-filling Working Upward a Steep-Pitching Iron-ore Bed; Eli T. Conner, on the good results of Back-Filling by Hydraulic Means in Preventing Destructive Subsidence in the Anthracite District; Thomas H. Claggett, on the merit of Systematic Pillar Drawing in Preventing Cracks in an Upper Seam; Henry H. Otto, successful results in the anthracite district in Mining Lower Seams before Upper Seams; Douglas Bunting, on Leading Factors Incident to Successful Mining of an Overlying Seam; Edwin Ludlow, on there being "less damage to buildings when there was complete removal of coal with complete packing than when room and pillar is used without extracting the pillars"; Edward O&apos;Toole on "bumps" in eastern Kentucky mines, which he thought were the result of geologic stresses: H. A. Buehler, on Upheaval of Surface in an Illinois Case in Advance of the Face; and R. Dawson Hall, on The Mechanics of Subsidence from Mining. The author of this paper discussed various Winds of problems of ground movement and subsidence in both metal mining and coal mining; the production of great landslides by workings near an outcrop, as at Turtle Mountain, Alberta, Canada; and general

Jan 1, 1939

By George Rice

THE A.I.M.E. Ground Movement and Subsidence Committee, pro-posed in 1920, held its first technical meeting in February 1923, under the able chairmanship of Mr. H. G. Moulton. The following list of papers and discussions, indicating the scope of the problems and relation to various conditions and method of mining, were given at that meeting by the distinguished mining engineers: J. Parke Channing, on Subsidence at Miami, Arizona; Howard N. Eavenson, on Mining an Upper Bitu-minous Seam after a Lower Seam Has Been Extracted; J. J. Rutledge, on Subsidence in Two Oklahoma Coal Mines; Benjamin F. Tillson, on Caving Cracks at the Franklin Mine, New Jersey; Dr. F. W. McNair, on the Dome Theory; William Kelly, on disadvantageous effects in Mining and Back-filling Working Upward a Steep-Fitching Iron-ore Bed; Eli T. Conner, on the good results of Back-Filling by Hydraulic Means in Preventing Destructive Subsidence in the Anthracite District; Thomas H. Claggett, on the merit of Systematic Pillar Drawing in Preventing Cracks in an Upper Seam; Henry H. Otto, successful results in the anthracite district in Mining Lower Seams before Upper Seams; Douglas Bunting, on Leading Factors Incident to Successful Mining of an Overlying Seam; Edwin Ludlow, on there being "less damage to buildings when there was complete removal of coal with complete packing than when room and pillar is used without extracting the pillars"; Edward O&apos;Toole on "bumps" in eastern Kentucky mines, which he thought were the result of geologic stresses: H. A. Buehler, on Upheaval of Surface in an Illinois Case in Advance of the Face; and R. Dawson Hall, on The Mechanics of Subsidence from Mining. The author of this paper discussed various kinds of problems of ground movement and subsidence in both metal mining and coal mining; the production of great landslides by workings near an outcrop, as at Turtle Mountain, Alberta, Canada; and general

Jan 1, 1939

By R. V. Taborelli, P. B. Bucky

This investigation was carried on by means of models and the application of the principles of similitude to determine the effects of props, props and cribs and sand filling in longwall mining. The geologic structure and rate of face retreat were kept constant and the only change introduced was in the method of support. It is not felt necessary to repeat a description of apparatus, or to explain the fact that a scalar model made in all parts of the same material as the prototype will behave similarly to the prototype when rotated at speeds such that the centrifugal force is as many times the gravitational force as the prototype dimension is a similar linear model dimension. The reader is referred to earlier papers1,2 for further information regarding these statements. All models were made of sandstone and were as in Fig. 6. They are composed of a 3/16-in. ore body bed A, overlain by a 3/16-in. bed B, a ?-in. bed C and two ?-in. beds D and E. The model was rotated at + 2350 r.p.m. equivalent to a model ratio of 1268. It was worked back ¼ in. at a time before being replaced in the centrifuge and again rotated. Table 1 gives model and prototype dimensions occurring in this discussion, the prototype dimensions being 1268 times the model dimensions. Figs. 1, 2, 3 and 4 were taken while the model was rotating at 2350 r.p.m. One was taken for each face retreat of 26.4 ft., but for obvious reasons all are not presented. Fig. 1 (A-E) shows the behavior of this type of structure with face retreats of 26.4 ft. and no artificial support. Fig. 2(A-E) shows the behavior of this type of structure where breaker and face props were used. The props were exceptionally strong, being of steel ? in. square in cross section, and capped with 1/16 in. ± of soft wood and paper, to allow for roof deflection. The face props were

Jan 1, 1940

By P. B. Bucky, R. V. Taborelli

This investigation was carried on by means of models and the application of the principles of similitude to determine the effects of props, props and cribs and sand filling in longwall mining. The geologic structure and rate of face retreat were kept constant and the only change introduced was in the method of support. It is not felt necessary to repeat a description of apparatus, or to explain the fact that a scalar model made in all parts of the same material as the prototype will behave similarly to the prototype when rotated at speeds such that the centrifugal force is as many times the gravitational force as the prototype dimension is a similar linear model dimension. The reader is referred to earlier papers1,2 for further information regarding these statements. All models were made of sandstone and were as in Fig. 6. They are composed of a 3/16-in. ore body bed A, overlain by a 3/16-in. bed B, a ?-in. bed C and two ?-in. beds D and E. The model was rotated at + 2350 r.p.m. equivalent to a model ratio of 1268. It was worked back ¼ in. at a time before being replaced in the centrifuge and again rotated. Table 1 gives model and prototype dimensions occurring in this discussion, the prototype dimensions being 1268 times the model dimensions. Figs. 1, 2, 3 and 4 were taken while the model was rotating at 2350 r.p.m. One was taken for each face retreat of 26.4 ft., but for obvious reasons all are not presented. Fig. 1 (A-E) shows the behavior of this type of structure with face retreats of 26.4 ft. and no artificial support. Fig. 2(A-E) shows the behavior of this type of structure where breaker and face props were used. The props were exceptionally strong, being of steel ? in. square in cross section, and capped with 1/16 in. ± of soft wood and paper, to allow for roof deflection. The face props were

Jan 1, 1940