Search Documents

By C. W. George, Bruce Chalmers

The authors enumerate the factors which appear, from their observations and practical experience of failure of aircraft components in Great Britain, to be responsible for causing a metal or alloy to fail by stress corrosion. The essential conditions for promoting failure by stress corrosion are: (I) tensile stress at the surface of the component, (either residual or applied), and (2) an attacking medium that may be a solution or a liquid metal. Particular attacking agents are effective only on certain metals. In all instances of stress-corrosion failure experienced, cracking of an intercrystalline form has occurred and examples of such failure in aluminum alloy, steel and copper alloys are described and illustrated. The relation between microstructure and stress corrosion is mentioned and methods of investigating the susceptibility to stress-corrosion failure of metallic materials are described. The precautions to be taken in selecting materials for particular aircraft components and the importance of adequate protection against chemical attack are considered. The authors have given a factual survey of stress corrosion and have made no attempt to advance any scientific explanation of the phenomenon.

Jan 1, 1945

By E. C. Potter

FUEL-OIL was first substituted for coal at these works in September, 1888. It was first applied in the converting-department to the battery of boilers, consisting of 14 tubular boilers, 16 feet in length by 5 feet in diameter. To operate these boilers with coal for 24 hours required 14 strikers, 3 ash-wheelers, 6 men unloading coal, and 2 water-tenders, making a total of 25 men. With fuel-oil the same boilers require for the same period 2 water-tenders and 4 men to attend to the burners, making a total of 6 men. This gives a saving of 19 men, which, at an average of $2 per day each, amounts to $38 per day. Comparing the consumption of oil with that of coal, we find that for the week ending January 5, 1889, with an ingot output of 6403 tons, 2731 barrels of fuel-oil were used as against a necessary consumption of coal for the same work of 848 tons, showing 3.22 barrels of fuel-oil to be equivalent to one ton of Indiana block-coal. Figuring oil at 60 cents per barrel, and coal at $2.15 per ton, we have as the cost of oil $1.93, as against $2.15 for its equivalent in coal. In December, 1888, the rail-mill battery of 26 boilers, of the same dimensions as those in the converting-department, was equipped for fuel-oil. For the week ending January 5, 1889, with a rail out-put of 5208 tons, 5987 barrels of oil were consumed, as against a necessary consumption of coal, to do the same work, of 1805 tons, showing 3.31 barrels of fuel-oil to be equivalent to one ton of Indiana block-coal, which at the costs named above would show $1.98 worth of fuel-oil to he equal to $2.15 worth of coal. The labor required to operate the rail-mill boilers for 24 hours, with coal as fuel,is: 26 stokers, 4 water-tenders, 6 ash-wheelers, 12 men unloading coal; total, 48 men. With oil as fuel, the same work requires 4 water-tenders and 6 men to attend to the burners; total, 10 men; a saving over coal of 38 men in 24 hours, which, at an average price of $2 per day, would be $76 per day. In the brief experience we have had with oil as fuel, we find that the efficiency of the boilers is somewhat increased and the repairs are

Jan 1, 1889

Boundary and general corrosio~z rates for higkpurity alutninum were ~rzeasured irz 16 pct HC1 at sJmllow penetrations (< 25 p). The rates for several high-angle random tilt boundaries, several [001] synzmetrical tilt boundaries, a 54-deg [010] twist, and a 15-deg randorn tw~st boundary were one-fourth to one-third higher than that of the (001) surface used as reference. Boundary attack was slower for 23 and 37-deg [001] tilt boundaries and a 16-deg [010] twist boundary. The corrosion rate for a (111) surface was roughly om-third higher than for (001) and was thus about as high as the corrosion rate of the fastest boundaries. The boundary attack did ?lot appear to parallel the variatiorz of boundavy energy. The signvicance of the anisotropy of corrosion was discussed.

Jan 1, 1966

By H. Morgolin, M. A. Greenfield, P. A. Farrar

In attempts to correlate mechanical properties with microstructure, it is desirable to determine the effect of ß grain size. Determination of 6 grain size is not a problem where a has precipitated at ß grain boundaries. However, in alloys which have been processed to produce an equiaxed a +ß structure the ß grain size is difficult to determine because ß grain boundaries do not etch. The ß grain size can sometimes be laboriously determined by searching for grains which have some a! outlining the 6 grains. This difficulty of ß grain size determination in equiaxed a + ß alloys can be overcome by heating below the ß transus temperature for a short time and water quenching. Fig. 1 shows the starting equiaxed a + ß structure of the Ti-5.25A1-5.5V-0.9Fe-0.5Cu alloy used in this investigation, and Fig. 2 shows the microstructure of the same sample water-quenched after heating 1 min at 1675"F, which is 25°F below the 0 transus. The heavily etched microstructure consists of some equiaxed a! in a structure showing considerable amounts of transformed ß. The ß grain

Jan 1, 1969

By M. A. Rigdon, R. E. Grace

The dissociation of cupric oxide to cuprous oxide and oxygen was studied with a microbalmce technique at 700" to 750°C. In this temperature range the dissociation pressure of the reaction 2CuO= Cu2O + 1/2 O2 was: The theory of near-equilibriwm reaction rates predicts a linear relationship between reaction rate and the Gibbs free-energy change for small values of AF/RT. This correlation is found to be valid for AF/RT = -0.1 or approximately 200 cal per mole away from equilibrium. THE theory of reaction rates near equilibrium as developed from classical thermodynamics suggests a small range of linear behavior between the overall reaction rate and the free-energy change accompanying the process. The extent of this linear correlation is generally unknown, even to the order of magnitude. The idea of linearity is also found in the formal mathematics of coupled transport phenomena, e.g., chemical diffusion, thermal diffusion, thermoelectricity, and so forth. The linear array of forces and fluxes which leads to various main and cross coefficients is predicated upon linearity between reaction rates and the bulk thermodynamics which govern the process. The general case in reaction kinetics is well-known: the magnitude of the free-energy change does not cor- relate with observed reaction kinetics, irrespective of whether the process occurs by diffusion or chemical reaction or both. The real need is to investigate specific reaction paths near equilibrium in order to learn of the limitations in attempting to correlate reaction rates and thermodynamics. It is the main purpose of this paper to examine the dissociation kinetics of cupric oxide under conditions of known driving force where the dissociation process is likely to occur by chemical reaction. A secondary objective is to obtain equilibrium data for the CuO-Cu20-O2 system. In a prior paper Edmiston and race&apos; investigated reduction kinetics of wustite in H2-H2O gas mixtures. The present study was carried out in oxygen according to the following reaction:

Jan 1, 1969

Twelve Directors, the Secretary, and ten guests were present. It was unanimously resolved that the sense of this body is that the name of the Institute should be changed to American Institute of Mining and Metallurgical Engineers. Messrs. J. W. Richards and Bradley Stoughton were appointed a committee to formulate the necessary steps for bringing the matter to a vote. The committee in charge of the New York meeting, with Allen Rogers, Chairman, was appointed. The rules of the American Engineering Standards Committee were approved. The Bulletin was presented to the Springfield Arsenal. The sum of $250 was appropriated to the Southern California Section. The By-laws were changed to increase the Secretary&apos;s cash from $500 to $1000. The report of the Treasurer was accepted. Sixty-eight members, thirteen associates, and forty-eight junior associates were elected. Four members were reinstated. The resignations of seven members were accepted. Thirteen members on active duty at the front had their dues remitted. Upon the recommendation of the Finance Committee, it was resolved that the clues of any members who have attained the age of seventy (70) years and have been members for a continuous period of at least thirty (30) years shall be remitted.

Jan 7, 1918

By I. S. Servi, N. F. Graves

THE etch-pit technique has long been used to reveal low-angle boundaries and, in general, the distribution of dislocations in high-purity metals. Often this technique is amenable to quantitative computations,&apos; but generally is affected by some degree of uncertainty because etch pits can be nucleated not only by dislocations, but also by inclusions and surface imperfections. In the case of high-purity zinc, Gilman&apos; reported that etch pits were produced only after adding 0.1 atomic per cent of cadmium to the crystals and aging at a proper temperature. In the course of a study of low-angle boundary behavior in zinc crystals, etch pits were produced in 99.999 pct zinc without resorting to intentional contamination, by etching in a 50:50 HNO3H2O solution. The technique consists of etching until the heat of reaction brings the solution to a boil, and in displacing the etchant rapidly with a stream of cold water, thus avoiding staining. The undesirable features of this technique are the heating effect and the removal of a considerable amount of material. A high polish is obtained if staining is controlled properly; therefore, the etch pits appear very clearly and with excellent contrast when observed under dark field illumination. This is especially helpful for cursory examinations at low magnifications. Several observations were made on zinc crystals of square cross section, having one face parallel to the basal plane and one edge parallel to a slip direction, Fig. l(a). When such a crystal was bent about 2" over a glass die and annealed at 390°C, a sharp boundary was formed only in the inner portion of the crystal. Near the two prismatic faces, perpendicular to the basal plane, the boundary was always branched into many lower-angle boundaries, Fig. 1(b). Attempts to move the main boundary by applying a shear stress to the specimen invariably resulted in curving the boundary, the branched ends remaining pinned in their original location, Fig. 1 (c). The prismatic face, when etched as indicated in the foregoing, revealed the existence of numerous (sometimes up to 30) fine boundaries, nearly parallel to each other. Pre-existing lineage boundaries, generally parallel to the direction of growth, were barriers to the formation of polygonization boundaries and interrupted the continuity of the substructure, Fig. 2. Twin

Jan 1, 1959

By Richard Moldenke

In crowding the recent mass of work on the physics of cast-iron into the compass of a short review, I cannot do better than to follow the lines of Mr. W. R. Webster&apos;s suggestion, made at the Florida meeting of the Institute, March, 1895.&apos; The classification of the properties of the metal, and the influences to which it is subjected during the various processes it undergoes, is quite complete; and as Mr. Webster gives it again in full in another paper at the present meeting, a simple reference to it now will be sufficient. I. Correspondence Between Chemical Composition, and Melting-Point, Fluidity, Shrinkage, Fracture,Chill, Micro-Structure, and Other Physical Properties. Melting-Point.—The melting-point of cast-iron had long been a subject of controversy among foundrymen. They knew that a hard iron melted faster than a soft one, but this effect was occasionally disputed, and the reasons given were unsatisfactory; but could not be well controverted. It was my good fortune to take the actual melting-temperatures of some 70 pig-irons and castings; the Le Chatelier pyrometer, suitably protected, being introduced into the interior, and the iron melted off in a specially-constructed cupola. The irons had been previously analyzed by taking the borings at the point of the intro-

Jan 1, 1905

By Henry M. Howe

The transformation which steel undergoes in slow cooling, from the condition of austenite whelk above the transformation rage into that of pearlite plus either ferrite or cementite below that range, is subject to great lag. This transformation is essentially the pearlitizing of the austenite. Indeed the hardenillg of steel is due to this lag, which is made so great by extremely rapid cooling that a very large part of the transformation itself is restrained, so that the rapid cooling catches the metal in an only partly transformed state, that of martensite, and under favorable contditions even in an almost wholly untransformed state, as in the cases of Maurer&apos;s austenitic manganese steel. Hadfield&apos;s austemtic. manganese steel, 25 per cent. nickel steel, and other anstenitic alloy steels, arc austenitic even after slow cooling. It has long been known that this lag increases (1) with the rapidity of cooling, (2) with the presence of certain retarding elements, notably manganese and nickel, and (3) with the temperature from which cooling starts. The present inquiry touches the last of these influences, but incidentally it throws light on the first also. This influence of higher heating ill increasing lag manifests itself in different ways which, though they may at first seem unrelated, are in fact hut different aspects of one and the same thing. Thus, among heatings to different high temperatures, all of them above the transformation range: the higher the temperature to which the steel is heated (1) the lower is the temperature at which the transformation occurs in cooling slowly down, (2) the shorter is the time occupied in the actual cooling from above the transformation range to the room Temperature under given external conditions, Whether of slow or

Jan 1, 1914

AT a luncheon attended by engineering leaders representing every section of the country, Col. Arthur S. Dwight, president of the American Institute of Mining and Metallurgical Engineers, and Charles F. Rand, chairman of the Engineering Foundation, past president of the Insti-tute and its present treasurer, on Thursday, July 20, were decorated with the Croix de Chevalier de la Legion d&apos;Honneur by the French Government for distinguished service in engineering tending to closer and more felici-tous relations between the two countries. The decorations were conferred by Consul General Gaston Liebert. In a speech extolling the war work of the American engineer, M. Liebert declared that Germany had been definitely foiled in her attempt to cripple France industrially for a generation by wrecking the coal mines of northern France. Three-fourths of these mines, M. Liebert said, were in full working order and the remainder will be in complete operation within two years. The Germans thought that it would take from 15 to 20 years to accomplish this. M. Liebert said that reconstruction is going on rapidly in northern France, two-thirds of whose indus-tries are now working. The French Government, he said, is planning water-power improvement on a vast scale, which will soon make unnecessary for France to import a single ton of coal. He urged that French students be sent to America to study engineering. In presenting the decorations, Consul General Liebert eulogized Colonel Dwight and Mr. Rand as personify-ing the spirit and service of the American engineer, which, he said, was a powerful factor in the victory over Germany. He spoke of the growing friendliness between the United States and France and described this ceremony as an epoch in international relations. Calvin W. Rice, secretary of the American Society of Mechanical Engineers, who presided, repeated that international unity among engineers was the dream of Andrew Carnegie, who saw in the efforts of the engineer and the scientist the hope of civilization. Mr. Rice said in part: In the Declaration of Independence occurs the statement that all men are created free and equal. Jefferson was familiar with the writings of Rousseau. In fact, he was a remarkable linguist notwithstanding that he wrote the Declaration of Independence when only 32 years of age. He was one of the very few ambassa-dors in the history of the United States who could speak the language of the country to which they were sent. The interpretation of the passage in the Declaration of Independence is that all men have equal opportunity, not that they are born with equal ability.

Jan 8, 1922

By D. T. Peters

To better understand the Co-Mo interaction in maraging steels, the precipitate reversion behavior of two alloys closely related to the 18 Ni-250 grade has been studied. The reversion experiment is carried out by aging at a low temperature, T1 (preaging temperature), for some period of time and then aging at a higher temperature, T2, called the reversion tetnperature. Aging and reversion tmzperatures used were in the range 679 to 1050°F. Reversion is marked by an increase in resistivity and a decrease in hardness. It teas found that some reversion took place at all cornbinations of T1 and T2 but that pronounced rei3ersion resulfed for an Fe-18 pct Ni-5 pct Mo-8 pcl Co alloy exposed to preagz&apos;ng&apos; temperatures at or below 850°F. A similar alloy not containing cobalt exhibited no such discontinuity in reversion behazior with TI. The results are interpreted in terms of two types of molybdenum-rich precipitates, one nucleated at dislocations and the other in the matrix. The increased supersaturation resulting from the presence oj- cobalt evidently provides sufficient energy to nucleate the matrix phase. Anotnalies in the temperature dependence of the resistivity decrease and peak hurdness in the Fe-18 pct Ni-5 pct Mo-8 pct Co alloy as a junction of aging temperature noted in an earlier study are explained on this basis. SEVERAL investigatorsl-9 have studied the details of the precipitation-hardening reaction of the maraging steels. The great majority of conclusions have been drawn from transmission electron microscopy. Although much has been learned by this method, alternate techniques which will give information earlier in the aging process are needed for a more complete understanding of the series of precipitation steps probably involved in the aging reaction. Peters and cupp&apos;&apos; have recently shown, by measurements of the kinetics of precipitation, that an 18 pct Ni-Co-Mo maraging steel shows a distinct change in precipitation behavior at aging temperatures below 850°F. The results were interpreted in terms of the existence of two types of precipitates at low aging temperatures. Only one precipitate type is present at higher aging temperatures. The low-temperature precipitate was found to be a particularly effective strengthener. No evidence for the additional low-temperature precipitate was found in the 18 pct Ni-5 pct Mo ternary alloy. The object of this investigation was to study further the characteristics of the two types of precipitates and the interaction between cobalt and molybdenum characterizing this system. Some preliminary experiments indicated a difference in reversion behavior in specimens aged above and below 850°F. This suggested that knowledge of the reversion behavior might shed some light on these two questions. Hardy and Heal11 have defined reversion as the loss of hardness, electrical conductivity, or other properties caused by heating for a very short time at temperatures above the aging temperature. The precipitate reversion referred to in this paper is entirely distinct from "austenite reversion" often referred to in maraging steel literature. This latter phenomenon could more accurately be called the diffusion-controlled formation of austenite. Much has been written about reversion in several of the aluminum-base binary and ternary alloys.&apos;2-16 Two explanations for reversion have been advanced. Based on the classical nucleation theory of Volmer-Weber-Becker-Doring,17 Konobeevski18 suggested that reversion was due to the size of the precipitate particles

Jan 1, 1968

By Russell G. Wayland

SINCE the installation at Kropfmuehl, Bavaria, of a modern flotation concentrator in 1938, the flake and fine graphite from the Passau area can now be delivered in about any normal specified carbon content of any size range up to a flake averaging about 0.7 mm. The graphite finds a wide German and export market for crucible manufacture, pencil leads, dry cells and other uses.

Jan 2, 1951

By I. Havenaar

Various methods have been proposed in the literature to calculate the pressure losses in drill-pipe and bit-nozzles, i.e., those parts of the mud-circuit where the largest pressure-losses occur. Very few data, however, are available to check the validity of these proposals. Presented in this paper are the results of pumping experiments with clay-water drilling fluids of different specific gravities and different laminar flow-properties (differential viscosity and Bingham yield value), using pipes of different diameters. In addition, a series of measurements on bit-nozzles is discussed. Two main conclusions may be drawn from this work for the flow through pipes. 1. In the laminar flow region pressure losses can be calculated from the differential viscosity and Bingham yield value of the mud. 2. In the turbulent flow region pressure losses can be calculated with good approximation from a viscosity term which is determined by the volume fraction of the dispersed phase. Calculations making use of laminar flow properties may lead to erroneous results. The effect of temperature on the pressure losses in the case of turbulent flow can be calculated from the change in viscosity of the dispersing medium, i.e., water. The main conclusions determined for the flow through bit-nozzles are that for flow conditions prevailing in the field, the pressure-drops in bit-nozzles are independent of the laminar flow properties of the mud. They are solely determined by the density of the mud and the geometry of the nozzle. INTRODUCTION The last decades have witnessed a steady increase in the depth of oil wells. This is illustrated by the increase in the drilling depth record in the USA from 8,046 ft in 1927 to 21,482 ft in 1953. This increasing depth, together with the experience that high rates of mud circulation and high fluid velocities in the bit-nozzles enhance the rate of drilling, has emphasized the importance of selecting suitable mud-pumps when starting the drilling of a deep borehole. For such a selection it is necessary to be able to calculate the pumping pressures necessary to obtain the required circulation rates. The main part of the pressure-losses in the mud circuit occur in the drill pipe and the bit-nozzles. Various methods have been proposed in the literature to calculate the pressure-losses in the drill pipe1,2,3,4. These methods do not all lead to the same results, and at the time this investigation was started insufficient basic data were available to check their validity. Moreover, to our knowledge, no data are available at all on the effect, if any, of the flow-properties of the mud on the pressure-losses in bit-nozzles.

Jan 1, 1955

By Grover J. Holt

Open-pit mining on the iron range has been in a stage of transition for several years from the standpoint of mechanization. The most radical change in open-pit mining methods was started in open-pit haulage in 1937 with the departure from the then standard system of locomotive and car transportation and the advent of the heavy duty truck as a replacement. The initial use of trucks was followed shortly by the first installation of a conveyor belt for open-pit ore haulage. The growth of the combination of trucks for gathering units delivering to a conveyor system for transportation out of the pit, has been rapid and this transition appears to have reached a peak in 1949 with locomotives and cars now being used in only a few of the largest open pits. One point which must be considered, if we assume that the maximum equipment change- over point has been reached, is that the largest pits have probably passed their peak of production. Future ore replacement must come from smaller pits wherein the truck conveyor system has done an outstanding job.

Jan 1, 1950

By Thomas T. Read

THE fact that certain types of ore-deposits have attained their present condition through the action of descending surface waters was, perhaps, first clearly pointed out by Posepny.1 The oxidizing effects of such waters were discussed by Penrose,2 and many papers dealing with this phase of the subject have subsequently appeared. That secondary enrichment of sulphide ores, however, might be produced by descending surface waters was not clearly understood until after the copper-bearing veins of the Butte district, Mont., had been carefully studied by the geologists of the U. S. Geological Survey, al¬though De Launay3 had suggested that sulphides might be transported from point to point and re-deposited in the zone above the level of ground-water. As a result of the study of the Butte district, two papers by geologists engaged in the work appeared within a short interval. The first by Weed,4 dealing with the enrichment of veins by later metallic sulphides: and the second by Ernmons,5 treating of the secondary enrichment of ore-deposits in general. In the latter paper it was pointed out that a typical vein of sulphide ores which has been subjected to the action of descending surface waters exhibits four zones,-an upper or surface zone, in which the changes have been mainly of removal, the products being typically oxides; a second zone of oxide enrichment, in which the less soluble metals brought from above have been precipitated as carbonates or oxides; a third zone of sulphide enrichment,

Mar 1, 1906

The next meeting of the Institute, the 113th meeting, will be held in Arizona in the latter part of September, 1916. All papers to be presented, at this meeting must be published in the September Bulletin or previously. Manuscripts must, therefore,&apos; be in the hands of the Secretary of the Institute not later than July 1. In case manuscripts are given by authors to members of technical committees, or others, they must be in the hands of such persons sufficiently in advance so that they may be actually in the hands of the Secretary of the Institute by the date mentioned. In the past, the Secretary has received urgent requests for special consideration regarding manuscripts that come in after the closing date. In view of the obvious unfairness of this, the Committee on Papers and Publications has instructed the Secretary not to accept for presentation at the Arizona Meeting any papers received later than July 1, 1916.

Jan 3, 1916

By F. D. Rosi, C. A. Dube, B. H. Alexander

The slip and twinning planes have been determined in deformed crystalsof titanium by an X-ray method of analysis. The slip planes are of the type {1010} and {1011}, while the twinning planes are of the type {1072}, {1121}, and (1122). In the case of the predominant (1010) slip, a type I digonal axis of indices <1120> was the effective slip direction. Microscopic observations on the appearance of the three twin types disclosed a distinct difference in their shapes, and an attempt was made to correlate this difference with the amount of twinning shear. The slip mechanism was discussed on the basis of the difference in c/a ratios for the common hexagonal close-packed metals. IT is a general rule that slip in metals occurs most easily on the planes of greatest atomic density and of the largest interplanar spacing, and that the direction of slip is a close-packed direction. Thus, of the hexagonal close-packed metals which have been investigated by the German school in the decade 1925 to 1935 (cadmium, zinc, and magnesium), it has been found that slip occurs on the basal plane (0001) and in a <1120> direction.&apos; In the case of magnesium above 225oC, slip occurs on a first-order pyramidal plane (1011) as well as on the basal plane.&apos; The hexagonal metals, moreover, deform in part by twinning, and, again with the exception of magnesium at elevated temperatures, the twinning plane has always been reported to be a second-order pyramidal plane {1012).&apos; In view of this consistency in the plastic behavior of these metals, it has been supposed that the same slip and twinning elements would be operative in the other important hexagonal close-packed metals (titanium, zirconium, and beryllium), although there are some reasons why this may not be so. Referring to the tabulation in Table I of the axial ratios of the important metals in this structural class, it may be seen that they can be categorized into three distinct groups depending on the value of their c/a ratios. In the first group are cadmium and zinc with large positive deviations from the ideal ratio for closest packing. This expansion in the direction of the c-axis would be such as to accentuate the basal plane as the slip plane, because it increases the interplanar spacing. The second group includes cobalt and magnesium, which closely approximate the ideal ratio. In the third group are zirconium, titanium, and beryllium whose axial ratios are decidedly less than the ideal. The lattice of the elements in this group is compressed along the c-axis which, in effect, tends to make the basal plane less favorable for slip inasmuch as it reduces the interplanar spacing and the atomic density of this plane. Thus, for metals in the third group, it may be said that there is a certain indefiniteness about the glide plane, in that planes other than the basal plane may be expected to operate. The fact that magnesium begins to exhibit planes other than the normal slip and twinning planes at elevated temperatures may indicate that this behavior will become more pronounced in metals of lower axial ratios. For this reason it might be expected that the slip and twinning behavior of zirconium, titanium, and beryllium would be different from that found in cadmium and zinc. One indication that there is a difference is reflected in the recent work which has been done on the deformation textures of these metals."&apos; As will be shown later, there is a significant difference between the rolling textures of cadmium, zinc, and magnesium on the one hand, and zirconium, titanium, and beryllium on the other, and this difference suggests that the mechanism of plastic flow is not the same in these two groups of metals. From these considerations, therefore, it may be seen that there are good reasons why it cannot be concluded that titanium will have the same crystal-lographic elements of slip and twinning as those exhibited by zinc and cadmium. For the complete determination of these elements it would be most advantageous to have single crystals. However, much valuable information can be obtained by using coarse grained polycrystalline specimens, provided the grains are sufficiently large to permit X-ray

Jan 1, 1954

By W. D. Robertson

The effect of a tensile stress in accelerating the corrosion-cracking of certain alloys of aluminum, magnesium and iron is widely recognized. The literature is extensive and it is only necessary to cite the recent ASTM—AIME Symposium,l There are, however, no experimental data conclusively showing the effect of an applied compres-sive stress. It has been inferred, from the generally accepted mechanism postulated for the acceleration of corrosion by an applied tensile stress, that a compressive stress would inhibit corrosion. Furthermore, it is observed that corrosion cracks invariably start on the tension side of a specimen bent as a simple beam. This observation has led to the suggestion that shot-peening of the surface would inhibit or eliminate stress-corrosion cracking in magnesium alloys and aluminum alloys. However, the degree of inhibition produced by shot-peening does not appear in the literature except for the above qualitative references which are unsupported by experimental data. Moreover, while peening undoubtedly imposes a surface compressive stress, the alteration of the surface by the severe cold-working involved complicates the interpretation of the results with respect to the effect of a compressive stress alone. If corrosion proceeds along preferential paths produced by precipitation from solid solution, it is easily understood how a component of tensile stress normal to these paths will accelerate the corrosion and lead to ultimate failure. On the other hand, if the metallurgical conditions are such as to create preferential corrosion paths, then it is difficult to understand how a compressive Stress, produced by shot-~eening Or any other method, can inhibit corrosion except in the sense that the accelerating factor is removed. Thus, if the basic corrosion mechanism remains unaltered, there should be little or no inhibition resulting from the application of a compressive stress if inhibition is defined as the reduction of the degree of corrosion below that experienced in the unstressed state. The experiment described below was performed to isolate and evaluate the effect of a compressive stress on the corrosion and stress-corrosion cracking of a high strength aluminum alloy (24-S); and, by a Comparison of the corrosion rate of &apos;pecimens subjected to an applied tensile stress, compressive stress and in the unstressed state, to clarify the role of stress in intergranular corrosion. Experimental Procedure The experiment was conducted with the aluminum-copper-magnesium alloy known as Duralumin 24-S.* Specimens, 0.064-in. thick, in the form of I-in. wide strips sheared parallel to the rolling direction,

Jan 1, 1949

By A. Dubé, G. Letendre, C. E. Beaulieu

An experimental study has been made of the time dependence of internal .friction and modulus of rigidity in- freshly quenched steels at room temperature. The effects of frequency, composition, and various thermal treatments are given. The kinetic 1aws observed cannot be fully explained by the so-called first stage of tempering and the transformation of retained austenite. It is suggested that the observed phenomena are due to the progressive immobilization of dislocations introduced by the martensitic transformation. It is generally agreed that the conversion of tetraginal martensite into cubic ferrite and ce-mentite occurs in three stages which at moderate rates of heating take place in the following temperature ranges:&apos;-3 a) The first stage involves mainly a partial loss of tetragonality of martensite and the formation of ?-carbide between 95" and 175oC. b) The second stage consists of the decomposition of retained austenite between 230 and 290&apos; C. c) The third stage covers the formation of ce-mentite between 290o and 400&apos; C. The kinetic laws of these heterogeneous reactions have also been the subject of isothermal studies. Thus, Roberts, Averbach. and cohen3 report a very low reaction rate with a eutectoid steel at room temperature. For example, less than 10 pet of the contraction associated with the first stage is observed after 50 hr at room temperature. Hollonlon, Jaffe, and Buffum4 show that under the same conditions less than 10 pet of the tetragonality is lost. These results have led to the belief that martensite is a relatively stable phase at room temperature. On the other hand, it is well known that important structural changes occur in martensitic steels during the first few minutes at room temperature after quenching. This pretempering has at least two important consequences. In the first place, freshly quenched steels have a tendency to crack at room temperature, a fact which leads to the necessity of tempering as soon as possible after the quench. Another important consequence of pretempering a steel for short periods of time at room temperature is the stabilization of the retained austenite. Thus, as shown by Cohen,5 a very pronounced stabilization is effected with holding periods of 30 min at room temperature. Since these two effects are apparently not caused by the heterogeneous reactions mentioned above, they must be related to the rearrangement of structural defects within the martensite and retained austenite. According to the modern theory of dislocations, the shears required to effect the austenite-marten-site transformation may be realized through the motion of dislocations at the austenite-martensite interface and within the martensite plates.6 In this way, a martensitic transformation closely resembles a plastic deformation. In cold-worked solids, high concentrations of dislocations are left immediately after the plastic deformation and it seems reasonable to assume that appreciable densities of dislocations should also appear in the wake of a martensitic transformation. A considerable part of the high hardness of martensite would then originate in the obstruction of dislocations in analogy

Jan 1, 1961

By C. G. Dunn, F. Lionetti

The energy associated with grain boundaries in polycrystalline aggregates is believed to play a major role in grain growth processes and, when growth ceases, to determine the final equilibrium grain boundary angles. Further, the energy of grain boundaries of recrystallization nuclei is a factor in nucleation processes. It is important to know, therefore, how the energy per unit area of a grain boundary, that is, the grain boundary surface tension y, depends on the difference in orientation of the two lattices of the grains producing the boundary. Although the problem is important, surprisingly little has been done toward a quantitative evaluation of the effect of orientation difference on grain boundary energies. C. S. Smith1 recently has discussed this problem and in addition to showing effects of orientation difference on equilibrium angles has shown a variety of interesting effects of surface tension on the appearance of microstructures. Fig 1 and the following relations expressed in Eq 1, which connect equilibrium grain boundary angles and surface tensions, illustrate equilibrium conditions which are believed to hold true in metals. ?l2 _ ?23 _ ?l3 [1] sin ?3 sin ?1 sin ?2 Clearly any two of these surface tensions can be expressed in terms of the third when the equilibrium angles ?1, ?2, and ?3 are known. Applied to the present problem for solid state equilibrium of three grains, the angles ?1,?2 and ?3 must be measured in a plane perpendicular to the line of junction of the three grains. Normally a direct determination of these angles from random microsections is impossible. Consequently Harker and Parker2 and Smith1 (except for some measurements on flat specimens) resorted to a statistical method to determine equilibrium grain boundary angles. Smith reported that grain boundaries meet the surface of a piece of metal nearly perpendicularly. He reported also, in connection with direct angle measurements on flat specimens with grains extending through the thickness, that angles varied appreciably from 120" and concluded that there was a measurable effect of orientation difference on surface tension. Another direct way of determining equilibrium angles and a method adaptable to studying particular configurations, recently suggested by Dunn,³ is to use a three-grain flat specimen with orientations of grains so chosen that the junction line of the three grains will be straight throughout the thickness and perpendicular to the surface of the specimen. Choice of orientations is possible when individual grains of each group can be grown to predetermined orientations through the reorienting and growth of " seed crystals " as described.³ Not only is it possible, for example, to have grains with the same crystallographic plane in the plane of the specimen, but a given orientation difference between two grains can be made a common factor to an unlimited number of three-grain groups while a series of orientation differences is investigated. Any effect of anisotropy of gas-solid surface tension due to grain orientation should be minimized by having all gains oriented the same with regard to crystallographic plane in the plane of the specimen. Another feature of the three-grain group is the notched grain boundaries as shown in Fig 2 for one specimen (S4). The notches serve to anchor the end positions of the grain boundaries (especially at high temperatures) while the central and junction point of the grains moves toward an equilibrium position. Final equilibrium should produce straight grain boundaries if the notches are very narrow and if changes in orientation* of the grain boundary do not alter the surface tension.† If one assumes the straight line condition and no change of surface tension with small changes in grain boundary orientation and finds the equilibrium configuration by a minimization of the grain boundary energy, one obtains the relations given in Eq 1. The approach to straight line boundaries or to minimum energy configurations in specimens containing large grains, such as those used in the present investigation, may be very slow compared with the approach to equilibrium conditions for the grain boundary angles. It may be desirable, as proved to be the case in the present investiga-

Jan 1, 1950