Al3Ni whisker-reinforced aluminum was found to exhibit good Charpy impact toughness and little notch sensitivity even though its room-temperature tensile elongation parallel to the whiskers is only 2 pct. This impact behavior was maintained d liquid nitrogen temperature (-196"C). It is postulated that this behavior is due primarily to the presence of the continuous aluminum matrix which provides sufficient 10calized ductility in the vicinity of the crack tip to absorb considerable energy from the advancing crack. The impact behavior of Al-Alni was found to be quite anisotropic. Of six orientations studied, the transverse orientation having the notch normal to the whisker axis was found to exhibit the lowest impact energy, whereas the transverse orientation having the notch parallel to the whisker axis was found to exhibit the highest impact energy. A significant differnce was noted between the impact behavior of material containing needlelike whiskers and that containing bladelike whiskers. Only two of the six orientations studied exhibited complete fracture for the material containing needlelike whiskers. On the other had, most of the specimens containing bladelike whiskers exhibited complete fracture. It was postulated that the bladelike whiskers block transverse flow, thus reducing the amount of plastic deformation ahead of the crack tip. One of the more significant advantages of composite materials is the prospect of combining high strength with toughness. In general, toughness is associated with materials which exhibit considerable ductility and can deform plastically in the presence of a stress concentration. Very strong materials which resist plastic deformation generally exhibit low toughness. At first glance, then, it would appear as though strength and toughness are mutually incompatible so that useful engineering materials would have to be a compromise between the two. One approach to the problem of combining the high intrinsic strength of ceramics with the toughness of metals was to mix them together to form a cermet. Unfortunately, the toughness of cermets was found to be rather disappointing. Whisker reinforcement of metals, however, appears to be a more promising approach. It has been demonstrated that whisker-reinforced metals produced by unidirectional solidification exhibit enhanced strength due to the presence of high strength nonmetallic whiskers. The total strain capacity of these composites in the direction of fiber alignment is limited to that of the fibers, the matrix being unable to carry the load once the fibers have failed. A characteristic, then, of whisker composites is low ductility in the direction of whisker alignment, on the order of a few percent elongation. This low elongation, which is usually associated with brittle behavior, should not be taken as an indication of low toughness. Such a material can exhibit significant ductility in directions other than parallel to the fibers7 and can therefore possess significant intrinsic toughness. Toughness in a fiber-reinforced metal is derived from several mechanisms. The first is due to the toughness of the matrix itself. A continuous ductile metal matrix can act as an effective crack arrest medium by undergoing localized plastic deformation. Cracks initiated from the surface of the composite or from a brittle fiber failure must travel through the matrix before reaching another brittle phase particle. A second crack arrest mechanism peculiar to fiber composites is due to the fact that, as a crack travels through the matrix and approaches a fiber, the plastic deformation ahead of the crack tip will result in loading of the fiber. This causes the matrix shear strength in the plastic zone to be apparently higher, thus extracting more energy from the crack and diverting the crack at an angle to the original direction of propagation. A third crack arrest mechanism occurs in fiber composites which exhibit a weak bond between fiber and matrix. The idea was proposed by Cook and Gordons that if a crack propagating transversely in a fiber composite were made to turn and run along the fibers by decohesion of the fiber-matrix bond, then toughness would be imparted by the blunting of the crack tip and the creation of new surfaces. The last mechanism, interfacial decohesion, is commonly noted in naturally occurring fiber composites such as wood, bone, and bamboo, and has been observed in man-made composites such as glass fiber-reinforced resins,g silica fiber-reinforced aluminum," laminated steel," and tungsten and silica fiber-reinforced electroplated copper.'' The first mechanism, crack arrest by plastic deformation in the matrix, has been noted in tungsten wire reinforced cast copper." The purpose of this investigation was to quantitatively assess the toughness of a whisker-reinforced metal as a function of orientation. Previous investigation considered only cracks propagating nominally perpendicular to the reinforcement. In this investigation, crack propagation in three mutually perpendicular directions as well as three intermediate orientations was investigated. The system chosen for study was the unidirectionally solidified A1-A13Ni eu-tectic alloy which has a microstructure consisting of 10 pct by volume of A13Ni whiskers in a matrix of aluminum This material exhibits two different kinds of whisker morphology, depending upon the rate at which it is solidified.' At low rates of solidification (less than 2 cm per hr) the whiskers are bladelike, whereas at higher rates of solidification they are

Jan 1, 1969

By Stanley M. Miller

The probabilistic nature of appropriate geologic variables can be included in analyzing the stability of potential slope failure modes. Random variables in the two-dimensional plane shear analysis of a specified structural discontinuity include the shear strength and waviness angle of the discontinuity and, in some cases, the rock mass density. Estimated probability density functions that describe these random variables are combined by Fourier analysis to produce an estimate of the safety factor probability density function, which appears to approximate a gamma distribution. The probability that sliding will occur along the specified structure is equal to the area under this density function where the safety factor is less than one.

Jan 1, 1982

By A. L. Holley

The three principal mines from which the celebrated Salisbury iron ores are obtained are called respectively the "Old Hill," "Davis," and "Chatfield" ore beds, and are situated in the town of Salisbury, Litchfield County, Conn., on the eastern slope of the Tocconuc range of hills.* The Old Hill Ore Bed is a tract of land of 100 acres, originally granted by the General Court in October, 1731, to be laid out by Daniel Bissell of Windsor. It mas Boon after surveyed and located by Ezekiel Ashley and John Pell. The descendants of Ashley are still proprietors in the mine. The supply of ore has been very abundant, and for many years was easily obtained, but latterly the cost of raising has been greatly increased. Up to about 1840 the average yield was estimated to be about 4500 tons per annum. The production has gradually increased until the average yield at present is estimated at 15,000 tons annually. The largest production in any one ymr was about 20,000 tons. The proprietors of this mine were incorporated many years ago under the style of " The Salisbury Ore Bed Proprietors." The Davis Ore Bed, named after an early owner, was originally called Hendricks Ore Bed, and was owned before the organization of the town of Salisbury by Thomas Lamb, one of the first settlers

Jan 1, 1879

By M. Allingham

This paper examines the contribution which econometric methods may be expected to make to the specification of commodity agreements, and how in turn computer methods may help in this. Starting from the specification of a model, the paper examines four activities: estimation of the unknown parameters; analysis of the properties of the model; simulation experiments with the model; and control of the model. In each of these activities the basic methodology is outlined, and the contribution of computer methods assessed.

Jan 1, 1977

By M. E. Shank, J. Wulff

At the present time, the designer of dies for metal powder pressing is handicapped by relative ignorance of stress distribution and frictional effects at the interior surface of the die. Unckell was the first to develop a method for the study of wall friction. He used three Brinell balls on which the die rested during pressing. The total frictional wall force was determined by the size of impression these balls left on a soft metal plate. Since the method does not give radial pressures, or distribution of such pressures, coefficients of friction could not be determined. Although Unckel measured density distribution, he was not able to determine radial or shear stresses. Shaler2 has proposed theoretical expressions for the stress and density distribution within cylindrical compacts during pressing, in accordance with the experimental results of Kamm, Steinberg, and Wulff.3 By application of Siebel's method,4 Kamm et a13 plotted stress trajectories for two compacts. From the stress trajectories they calculated coefficients of friction from point to point along the die wall. As pointed out by Shaler in the discussion of Ref. 3, these values are based on progressive point-to-point calculations on finite size grid squares across the compact. In the region of the die wall such calculated values may therefore have considerable cumulative error. The purpose of the present paper is to develop an experimental method by which the nonhydrostatic pressures and shears acting on the interior wall of a cylindrical die can be measured. Such measurements can then he correlated with existing data to aid in the explanation of the pressing process. The method used is based on the elastic: properties of the thick-walled tube used as the die. The principle of super-position of force systems on an elastic body is assumed to hold. Electric strain gauges were mounted in adjacent positions on the exterior die wall in order to get an exact measurement of the variation of tangential strain over the length of the die during pressing. While in this paper, measurements in terms of only tangential strains are considered, it is well to note that similar calculations may be set up for axial strains. The latter are not preferred, since they tend to be smaller than the tangential strains and therefore permit less sensitive measurements. Discussion in this work is restricted to compacts pressed from both ends, since the elastic deformation of the die is then more amenable to analysis. Before choosing the electric strain gauge method, a more direct line of attack was considered and discarded. The discarded idea was the insertion of a pressure gauge through a hole in the die wall.* The gauge would have been in the form of a small piston. If pressure were exerted against such a gauge, it would move outward along a radius of the die. One disadvantage of the scheme is its inability to measure shears along the die wall. Another more serious disadvantage is the disturbance caused by the device itself. It would serve to change the forces it was designed to measure. No matter how small the movement of the gauge, when pressure is applied a discontinuity would exist in the wall surface at that point. Due to the stress concentration caused by the hole, abnormal deflections of the die wall would occur around the gauge. During pressing, powder would be forced into the resulting depression. The depression would then become larger with increasing compacting pressure. Powder, not being a fluid, is capable of supporting shear. The ease with which it would flow into the die wall depression to further move the piston is an indication, not of the radial pressure at that point, but of the state of shear retarding the movement. Thus the "pressure" gauge is really a criterion of flowability, and of the capability of the powder to support shear. For these reasons, it was decided that the electric strain method, herein employed, was more reliable, if more indirect. The gauges and lead wires, mounted on the external die wall do not in any way affect the behavior of the metal powder or the die during pressing. Theory of the Method THE EFFECT OF RADIAL PRESSURE ON THE DIE WALL Effect of a Single Small Band of Hydrostatic Pressure Consider a die which is a thick-walled cylinder of outer radius R. and inner radius Ri. If over a small finite length L there is a normal pressure P, a tangential strain distribution at the outer wall results. This is shown schematically in Fig 1. The exact shape of the curve may he predicted by an extension of the theory of a semi-infinite beam on an elastic foundation.6 This

Jan 1, 1950

By John J. Croston

IN the closing months of 1936 the copper industry gave every evidence that it was at last on the threshold of an improved era. At the beginning of the year prices stood at 9 ¼ ¢, which in itself was a great improvement over prices prevailing for the three previous years. Industry generally was showing signs of moving forward in this country, and business was definitely good in certain foreign quarters. The threat of war and preparations for rearmament in Europe and Asia acted as a further stimulus to purchasing. By midsummer the situation had so improved and stocks had been so reduced that the cartel of foreign producers (including American producers with foreign mines) decided to increase the production quota to 75 per cent on Aug. 1. Large-scale buying gave continued strength to the price and by Oct. 1 the quota was increased to 80 per cent, and again on Oct. 15, to 85 per cent. Notwithstanding this the price of copper continued its advance and on Nov. 1, with stocks declining continuously, the cartel increased operations to 95 per cent, then to 105 per cent on Nov. 5. In the meantime the domestic producers, because of the great increase in home consumption, had increased their production by nearly one-half. At the close of the year copper sold at 12¢ per pound, and since the turn of the present year has reached 17¢. This rapid increase has not been wholly justified. Much of the increase was due to the legitimate demands of recovering industry, but rearmament orders plus accumulation of reserve stocks in case of war, purchases in anticipation of labor strikes and purely speculative activities on the London Metal Exchange accounted for the balance. Certainly in view of the state of industry and the general world price level, it appears unnecessarily high. Talk of a copper shortage is sheer nonsense, the recent condition in the market being created by overbuying, leaving but a small volume for speculative supplies. It takes some months for an increase in mine output to reach the market, but production is again overtaking apparent consumption, stocks have begun to increase, and this, together with the reopening of many small

Jan 1, 1937

By John J. Croston

In the closing months of 1936 the copper industry gave every evidence that it was at last on the threshold of an improved era. At the beginning of the year prices stood at 91/4c, which in itself was a great improvement over prices prevailing for the three previous years. Industry generally was showing signs of moving forward in this country, and business was definitely good in certain foreign quarters. The threat of war and preparations for rearmament in Europe and Asia acted as a further stimulus to purchasing. By midsummer the situation had so improved and stocks had been so reduced that the cartel of foreign producers (including American producers with foreign mines) decided to increase the production quota to 75 per cent on Aug. 1. Large-scale buying gave continued strength to the price and by Oct. 1 the quota was increased to 80 per cent, and again on Oct. 15, to 85 per cent. Notwithstanding this the price of copper continued its advance and on Nov. 1, with stocks declining continuously, the cartel increased operations to 95 per cent, then to 105 per cent on Nov. 5. In the meantime the domestic producers, because of the great increase in home consumption, had increased their production by nearly one-half. At the close of the year copper sold at 126 per pound, and since the turn of the present year has reached 17c. This rapid increase has not been wholly justified. Much of the increase was due to the legitimate demands of recovering industry, but rearmament orders plus accumulation of reserve stocks in case of war, purchases in anticipation of labor strikes and purely speculative activities on the London Metal Exchange accounted for the balance. Certainly in view of the state of industry and the general world price level, it appears unnecessarily high. Talk of a copper shortage is sheer nonsense, the recent condition in the market being created by overbuying, leaving but a small volume for speculative supplies. It takes some months for an increase in mine output to reach the market, but production is again overtaking apparent consumption, stocks have begun to increase, and this, together with the reopening of many small

Jan 1, 1937

PRODUCTION of nonmetallic mineral raw materials used by the fertilizer, ceramic, chemical, and construction industries and many others, was greater during 1953 than in any previous year. Production of fertilizer minerals was the highest in history despite somewhat decreased consumption in the second half of the year. Marketable phosphate rock production increased 10 pct to an estimated total of 13.1 million LT, valued at $78.5 million, and potash production was estimated at 1.8 million tons of K2O equivalent, valued at over $60 million. Crude gypsum output exceeded the 1952 total and approached the record of 8.66 million tons mined in 1951, with indications that 1953 will show a new all-time high. Gains and losses among gypsum products were irregular, with major gains in plate- glass and terra-cotta plasters, sanded building plasters and miscellaneous building plasters, and principal declines in base-coat plasters, prepared finishes and tile. Lath and wallboard outputs were each about 20 pct higher than in 1952.

Jan 2, 1954

By Max Boehmer

The first and most lasting impression made upon the mind of him who examines a mine or a mining district consists in the observation that in each and every case there is an intimate association of the ores with the eruptive rocks in the dietrict. The mines in the Mississippi valley seem to be the only excep-

Jan 1, 1904

By John C. Smock

While I was engaged in the preparation of a catalogue or list of mineral localities of the United States, east of the one hundredth meridian, for the U. S. Geological Survey, the thought occurred to me that an arrangement or classification of the iron-ore districts of the eastern part of our country according to their geological horizons would be an interesting topic for a paper, and would furnish a basis upon which to arrange many facts brought out by the constant development of our iron-mining districts. Our text-books of mineralogy, geology, and ore-deposits describe the iron-ores and the

Jan 1, 1884

By F. C. Newton

RefineRs of lead by the Parkes process have always been solicitous of recovering the zinc used in the desilverization, and justly so, as the loss in zinc constitutes one of the heavy costs in this method of refining. Part of this loss is due to the absorption of zinc by lead, and in the present state of knowledge is not recoverable as metallic zinc. The remainder of the zinc, which finds its way into the precious-metal-bearing crust, is recoverable and naturally engages the operators' most exacting attention. Careful elimination of the impurities in base bullion has enabled the refiner to produce a zinc crust better adapted to retorting, which reflects favorably in the zinc recovery;- and to produce a richer crust, thereby lowering the zineking cost, as the increased efficiency of the zinc results in less of it being in circulation. It is obvious that if the ratio of concentration be increased, a lessening of the amount of crust formed will ensue, throwing less work on the retorts and diminishing the amount of retort metal sent to the cupels, thus making an actual money saving in all these operations. In the effort to obtain a rich crust, the metallurgist has increased the heat to a considerable degree, upon the assumption that at the higher temperature the zinc-dver alloy could be squeezed free from the adhering lead. A further possibility for improvement suggested itself in the freezing-point curve of Prof. H. C. Carpenter, upon zinc and silver. Study of this curve disclosed the existence of a definite chemical compound, Zn3Ag2, with a freezing point of 665" C., a promising compound for practical application. In the experiment undertaken it was endeavored to force this compound into the crust, hoping thereby to obtain a higher concentration than formerly. It was recognized that in bringing a large kettle of lead to such a heat, more fuel would be used, the life of the kettle would perhaps be shorter, and other disadvantages would be experienced. AS a commercial operation, the project would have to stand on its own feet,

Jan 1, 1915

By F. G. Miller, R. C. McFarlane, T. D. Mueller

During the process of gas storage in pressure-depleted oil reservoirs, it has been observed that in some instances additional liquid oil is recovered and that the composition of the storage gas is materially altered. A mathematical study was made of the dynamic behavior of such a depleted oil reservoir undergoing gas injection. The important variable considered in this study, not included in previously published work, was that of compositional effects on the phase behavior of two-phase flow. Pressure, saturation and component composition profiles were developed for a linear, horizontal and homogeneous porous medium containing oil and gas but undergoing dry gas injection. Special new techniques were developed to overcome the problems of numerical smoothing which arise in the solution of the equations representing such systems. The method of solution includes the development of partial differential equations describing the behavior of the system, representing these equations by finite difference approximations, making certain simplifying assumptions and, finally, applying methods of numerical analysis with the aid of a high-speed digital computer. In an example calculation, results using the mathematical model are compared with field observations made on a gas storage project in Clay County, Tex. This field project involved a depleted oil reservoir used 'for gas storage and gas cycling purposes. As a result of these processes, the reservoir yielded substantial amounts of secondary oil, both in the form of stock tank oil and as vaporized products in the produced gas. The methods derived in this study may be applied to a variety of oil reservoir problems which are dependent on compositional effects. In recent years the number of oil reservoirs being used for gas storage purposes has increased greatly, and there has been at least one published account of additional oil recovery resulting from gas cycling a depleted oil reservoir after repressur-ing with dry gas for storage purposes. Additional oil recovery from oil reservoirs resulting from gas storage operations could become an important secondary recovery process. This is especially true since the use of natural gas in large metropolitan areas continues to increase and more gas storage volume near these areas is needed. These facts provided the motivation for the work reported here. This paper reports on a study of the inter-relations of composition, saturation and pressure changes which occur when hydrocarbon gas is injected into an oil reservoir system. From an understanding of the process, prediction methods may be developed for use in forecasting the secondary recovery products from gas storage operations in oil reservoirs and, consequently, .the economics of such projects can be developed. The process of storing hydrocarbon gas in an oil reservoir and the cycling process both involve the transient multi-phase flow of oil reservoir fluids with changing fluid compositions. There is a scarcity of work published on the subject. One of the first laboratory models developed to study a problem similar to the one posed here was published in 1948 by Standing, Lindblad and Parsons. l They developed a model to study gas condensate recovery by gas cycling, including the effect of heterogeneous reservoir permeability. Their results showed the compositional effects of injecting a gas of known composition into a two-phase condensate reservoir of known composition. A major finding of their study indicated that maximum oil recoveries from gas cycling projects result when low cycling pressures are used. Previous to their work it was generally considered

By H. R. Peiffer

Composite alloys of silver and alumina are shown to resist flow above the melting point of the continuous matrix. The ability to resist flow depends on the fineness of the dispersion and the oxygen content of the silver. It is believed that the oxygen influences very strongly the bond between the molten silver and the finely divided alumina. RECENT needs for materials with high strength and creep resistance at high temperatures initiated mechanical property studies on dispersed phase materials to near the melting point of the continuous matrix material. Results' of these investigations have shown that certain of these materials do have promise for high-temperature applications. Experiments performed on composite materials of silver and alumina by the author have resulted in the discovery of an interesting effect above the melting point of the silver. In these materials the silver was continuous and the alumina very finely divided (Linde B). It was observed that these materials exhibited strength and resistance to flow above the melting point of the silver matrix. The purpose of this paper will be to describe these properties. METHOD OF PREPARATION The materials were prepared by mixing the proper amount of Linde B alumina and high-purity silver oxide. The alumina content was varied from 5 to 20 wt pct alumina in silver in 5 pct steps. The materials were mixed by blending the constituents in an ordinary food blendor using ethyl alcohol as a vehicle. Enough alcohol was added to the powders to form a mixture with the consistency of a thin mud. After blending for about | hr the material was dried and the silver oxide reduced by heating to 450 OC. The material was then pressed at 25 tsi into a -in. billets 3 in. long. EXPERIMENTAL PROCEDURE The specimens were horizontally supported at either end by knife edge supports of cold-rolled steel. This holder was then placed in a "globar" furnace and a chromel-alumel thermocouple placed very close to the specimen recorded its temperature to within 10°C. Each specimen was heated rapidly to 900°C initially. The specimens were held at temperature approximately 30 min and then the temperature was raised 50 deg. The procedure was repeated until deformation was noted. Photographs were made of the specimens at various temperatures and increments of time using a Polaroid Land camera. RESULTS Fig. 1 shows the 5 pct by weight "Linde B" alumina and silver material after reaching 980 °C. Failure occurred after 15 min at this temperature. There were two points of failure and silver collected at them. No additional flow of the molten silver was noted at any other place. Fig. 2 shows a 20 pct by weight "Linde B" alumina in silver specimen. After 30 min at 1400°C, bowing of this material was observed. Other concentrations of alumina were added to

Jan 1, 1961

By Vanderlei Beisiegel, Arthur L. Bernardelli, Arthur W. Ruff, John H. Tremaine

Estimated reserves of high-grade iron ore at Serra dos Carajás total 16 billion metric tons and have an average grade of 66.7 per cent iron, 2.2 per cent combined silica and alumina, and 0.05 per cent phosphorous on a dry basis. Hematite is predominant and no significant sulfur on other deleterious elements are present. Serra dos Carajás is located in northern Brazil, about 550 kilometers southwest of Belém, Pará. It is six degrees south of the equator between the Xingu and Tocantins Rivers. Both rivers flow northward toward the Amazon River. The greater part of the area is covered by thick jungle, and the most practical means of access is by air.

Jan 1, 1974

By Edward Walsh

In the early history of the production of metallic iron from the native oxides or ores, success attended the labors of the workman according to the care he devoted to his work, and according to the degree of skill he possessed in furnishing the required amounts of fuel and ores to be acted upon by the blast propelled by the bellows, trompe, or wooden tub, and delivered into the hearths of the Persian, bloomery, or Catalan forges. The same skill may also have been of avail in the use of the lower forms of the ".Stück," "Blue,"or" Wolf"

Jan 1, 1887

By John Griffen

Methods of coal preparation in England, including usage of American units such as the Chance sand flotation process and Denver flotation cells, are compared with methods used in the United States. Problems of the coal industry in Holland are summarized.

Jan 2, 1951

By C. Chiou, D. P. Seraphim

The effect of clustering on the superconducting properties of Al-Zn alloys has been studied by the ballistic induction techniques. The superconducting critical temperature, T,, changes when zinc-rich clusters are formed. The change in T, depends on the concentration and may be positive or negative, but always correlates with an effective decrease in the solute concentration of the alloy. Reversion after clustering effectively returns a 5 at. pct Zn alloy to the quenched state. These methods might be use&lly extended to the Al-Mg system, where X-ray data are difficult to obtain. In very dilute Al-Zn alloys, as in other tin,' indium, aluminum,2 or tantalums base solid solutions, there is a decrease in the superconducting critical temperature, Tc, roughly proportional to the temperature independent resistivity, i.e., -0.2°K per pS2cm. With increasing solute concentration, the T, generally reaches a minimum and then increases4 to a value well above that for the pure solvent. The change of T, with solute concentration follows an empirical formulation involving two constants which correlate with the scattering cross section of the impurities. As will be shown below, the Al-Zn alloys more concentrated than 1or2at. pct do not follow the empiricism, probably because they are unstable even when rapidly quenched.5 However, it seems possible to study at least the later stages of solute clustering by precise measurements of the 1', following various thermal treatments. A few experiments on quenched alloys, aged alloys, and tests on reversion are reported here. The heat treatments selected for obtaining the quenched and aged states were mainly deduced from the work of Dash and Fine.6 For the quenched state, specimens were homogenized at 480°C, quenched to -160°C, and immediately transferred and mounted in liquid nitrogen. Measurements on the superconducting properties and residual resistivities were then made at helium temperatures, after which the specimens were aged at room temperature for 3 to 5 hr, i.e., much longer than the time required for clustering to be essentially completed. The superconducting properties and residual resistivities were once again examined. To reach the reverted state of the A1-5at. pct Zn alloy, the aged specimen was heated for 5 min at 200°C and then tested as above.

Jan 1, 1963

By E. S. Machlin, A. A. Hendrickson

Use was made of a recently developed surface-accumulation diffusion technique to measure the self-diffusivity of edge-type dislocation singular lines (Burgers vector along <110>) in a bent and polygonized single crystal of silver. Two factors are involved in obtaining a number for the diffusivity. One factor, the dislocation-line density, was measured by a microscopic technique recently developed, and the value of the other parameter, the effective "diameter" of a dislocation pipe, was estimated. With these parameters equal to 7.3 X 106 dislocations per sq cm and 10-7 cm, respectively, it was found that the self-diffusivity along edge-type dislocation lines was a factor of about two times the average grain-boundary self-diffusivity. The dislocation-pipe diffusivity is about 7x10-7 sq cm per sec at 450°C. THE possibility of short-circuit diffusion through imperfections in crystals has been recognized for some time. It was only recently, however, that concerted effort has been expended to obtain values of diffusivity for grain-boundary short circuits. The work, for example, of Hoffman and Turnbull1 on silver, Fisher&apos;s&apos; analysis of the grain-boundary dif-

Jan 1, 1955

By V. A. Phillips

Transmission-electron micrographs of electro-thinned samples of bulk-aged Cu-3.1 pet Co alloy show an aging sequence, supersaturated solid solution — coherent particles — quasi -coherent particles — noncoherent particles. Hardening is due to precipitation of coherent spherical fee coball-rich particles showing coherency strain fields, which are resolved at between 15 and 30A diameter. Loss of- full coherency did not occur until well into the overaged region, even with the assistance of deformation after aging. Different average particle diameters of 123, 92, and 149 ± 10Å were observed in samples aged to peak yield strength at 600°, 650°, and 700°C, respectively, indicating that there is no critical size for peak hardening. Noncoherent particles tended to develop (111) faces and became octahedral in shape. Dislocations tended to nucleate spherical coherent particles which eventually grew together forming large elongated particles. The surface energy of a noncoherent (low-angle) inter-phase boundary is estimated to he about 50 ergs per sq cm. A number of particle lining-up phenomena were observed. Overaging is principally attributed to increase in particle spacing, progressive loss of coherency, and increase in amount of discontinzdous precipitation. COPPER dissolves about 5.6 at. pet (5.2 wt pet) of cobalt at 1110oC1 and the solubility decreases to 0.75 at. petl (0.54 at. pet)2 at 650°C and to 0.1 at. pet or less at lower temperature.&apos; It has been known for many years3-5 that Cu-Co alloys are capable of age hardening. Since cobalt is fee above 417°C and its atom size is only about 2 pet smaller than that of copper, precipitation of coherent particles would be expected. The equilibrium phase precipitated at 700°C and below contains about 10 pet Cu in solution which tends to stabilize the fee structure, lowering the transformation temperature to 340oc.l The alloy is known to undergo discontinuous precipitation in addition to general precipitation; while the former can be seen with an optical microscope, the latter precipitates are not visible except in the grosly overaged condition.5, 6 Extensive use has therefore been made of the ferromagnetic properties of the precipitate in order to follow the course of aging, and it has proved possible to measure the average particle size, spacing, approximate shape, and volume fraction and to determine that the particles are coherent without ever seeing a particle (see for example Refs. 2, 7, and 8). The magnetic measurements of particle size are limited to diameters below about 120Å.7 The present study was undertaken using the techniques of transmission-electron microscopy in order to check the above conclusions, to extend the previous magnetic work to larger particle sizes, and to attempt a more detailed correlation of properties and structure. A portion of this work has already been published.9-11 The present paper is concerned with the metallographic features of precipitation in relation to aging curves. Bonar and Kelly12&apos;13 have published preliminary results of a similar study on single crystals of Cu-2 at. pet Co. EXPERIMENTAL Preparation of Alloy. A Cu-Co alloy, containing 3.12 wt pet (3.36 at. pet) Co by analysis, was prepared from 99.999 pet purity oxygen-free copper and electrolytic-grade cobalt. The alloy was melted and cast in vacuo in a high-frequency furnace using a graphite crucible and mold: Analysis showed chat 0.004 pet C was picked up during melting. The 1-1/2-lb ingot was homogenized in hydrogen for 24 hr at 1000°C. Slices were cold-rolled to 0.005 or 0.003 in. thickness, with an intermediate 650°C anneal in hydrogen at 0.080 in. thickness. Batches of six to ten strips were solution-treated in sealed-off quartz tubes in high vacuum in a vertical furnace and quenched by dropping into iced brine containing a device which snapped off the nose of the tube. Solution treatment consisted of 1 hr at 990°C or 2 hr at 965°C. The latter was employed for all mechanical-property studies, since a tendency was noted for the higher temperature to give porous material. Strips were usually aged individually in a horizontal vacuum furnace, inserting into the hot zone and withdrawing into a cold zone without breaking the vacuum. This method gave a rapid heating rate, permitting the use of short aging times. In some cases, particularly for the longer aging times at the higher temperatures, samples were sealed individually in quartz tubes in high

Jan 1, 1964

By B. J. Bayles, J. A. Ford, M. J. Salkind

Unidirecltonally sulidijied AL-A13Ni was found to exliibit excellent microstructural stability to 508°C. Above this temperature the transverse micvostructure coarsened in a manner analogous to "Ostwald Ripening", but the A13Ni whiskers did not spheroidize or foreshorlen. The coarsened whiskers reinforced the matrix as effectirely as the finer whiskevs and no reduction in room-temperature tensile strength mas noled after exposure for 90 hr at 96 pel 0-1 the absollite melling temperature of the eulectic. The slability was auribucted to the presence of low-index (and presurrlably lor-energy) cvystallographic interjaces between phases. The driving force for microstructural coursening was presumed to be the reduction of interfacial energy between the phases. Finer micvoslructures were found to coarsen more rapidly than those which weve imitally coarser. FIBER-reinforced metals have been shown to exhibit good short-time tensile properties at elevated temperatures.1-4 However, many elevated-temperature applications require long-time property retention which dictates the necessity for microstructural stability. Two types of instability are common to fiber composities. The first, chemical instability, is due to chemical reaction between the matrix and the relnforcing phase. Petrasek and weeton5 have shown that chemical reaction between tungsten wire and several copper alloy matrices resulted in degradation of the reinforcing phase and reduction in strength of the composite materials. Kreider and Leverant4 have noted similar behavior for boron-reinforced aluminum above 400°C. The second type of instability arises in systems in which the phases are essentially chemically stable with respect to each other and is characterized by spheroidization and/or agglomeration of the reinforcing phase. parratt6 has reported this type of degradation to occur relatively rapidly at moderate temperatures for nickel and cobalt alloys containing whiskers of silicon nitride, aluminum oxide, and silicon carbide and has identified it as "physicochemical" instability. Although both types of instability are the result of the differences in the chemical potential between the fibrous phase and the matrix, they may be differentiated by the fact that the second type, "physicochemi-call&apos; instability, results in little or no net change in the composition or amount of each phase present. It does, however, result in a morphological change which profoundly affects the strengthening mechanism. Chemical interaction. on the other hand, results in a change in the composition and amount of one or more of the phases present, or the appearance of a new phase. In the latter case, the appearance of the mi-crostructure, that of a fibrous phase aligned in a matrix, may remain essentially unchanged, but the chemical degradation of the fiber results in markedly reduced composite strength. This investigation was initiated in an attempt to evaluate the microstructural and related mechanical property changes of a whisker-reinforced eutectic composite after elevated-temperature exposure. The composite system chosen for this study was the uni-directionally solidified A1-A13Ni eutectic which Lemkey. Hertzberg, and Ford7,8 demonstrated to behave as a whisker-reinforced composite. The microstructure of the unidirectionally solidified material consists of aligned needles of A13Ni in a matrix of aluminum. EXPERIMENTAL PROCEDURE Eutectic ingots having a nominal composition of 6.2 wt pct Ni were produced by melting 99.99+ pct A1 and 99.99 pct Ni in recrystallized alumina crucibles in an argon atmosphere. The analyses of the starting materials are listed in Table I. These master heats were cut up? melted by induction heating, and unidirectionally solidified vertically in 1/2 -in.-ID. 6-in.-long graphite crucibles, in a dynamic argon atmosphere. Therma1 gradients in the liquid were determined by measuring the temperature in the melt as a function of apparatus travel distance, as discussed by Kraft and Albright.9 The rate of solidification was assumed to be equal to the uniform rate at which the crucible assembly was withdrawn from the furnace. Ingots representative of nominal growth rates of 2, 5, and 11 cm per hr were produced and the solidification parameters are summarized in Table 11. Ingots used for met allographic analysis were pre-

Jan 1, 1968