By Cyril Stanley Smith

BeTa brass (consisting of approximately equal atomic proportions of copper and zinc) exists as a random solid solution at high temperatures, hut at low temperature< an ordered structure is stable, with the copper and zinc atoms occupying alternate sites on the body-centered-cubic lattice. On cooling, ordering commences at a temperature of 450° to 470°C., depending on the composition. The degree of ordering progressively increases at lower temperatures until it becomes virtually complete at about 100°C. The electrical resistivity of the alloy illustrates the changes clearly (Fig. I). This type of reaction has been a favored subject for study by physicists. An excellent summary of the theory is to be found in a paper by F. C. Nix and W. Shock1ey.l All published data on electrical conductivity, specific heat and other properties agree in indicating that the ordering reaction in beta brass takes place so rapidly that it cannot be prevented or even retarded by quenching&apos; With most ordered alloys, cold-working induces disorder and

Jan 1, 1943

By Cyril Stanley Smith

BeTa brass (consisting of approximately equal atomic proportions of copper and zinc) exists as a random solid solution at high temperatures, hut at low temperature< an ordered structure is stable, with the copper and zinc atoms occupying alternate sites on the body-centered-cubic lattice. On cooling, ordering commences at a temperature of 450° to 470°C., depending on the composition. The degree of ordering progressively increases at lower temperatures until it becomes virtually complete at about 100°C. The electrical resistivity of the alloy illustrates the changes clearly (Fig. I). This type of reaction has been a favored subject for study by physicists. An excellent summary of the theory is to be found in a paper by F. C. Nix and W. Shock1ey.l All published data on electrical conductivity, specific heat and other properties agree in indicating that the ordering reaction in beta brass takes place so rapidly that it cannot be prevented or even retarded by quenching&apos; With most ordered alloys, cold-working induces disorder and

Jan 1, 1943

By D. F. Stein

In spite of the apparent usefulness of autoradiography in demonstrating segregation, it has had very limited success in demonstrating grain boundary segregation. Because of this limited success, a model system amenable to mathematical analysis was devised to determine which variables in the experiment are most important. As a result of these calculations, it was concluded that autoradiograPhy is a rather insensitive technique to measure grain boundary segregation. The range (energies) of the emitted particles (ß and a) must be low, and the concentration of the radioactive speczes at the grain boundary must be (in general) two or three orders of magnitude greater than the concentration within the grain. Because of these very restricted conditions , the limited success of the technzque is not surprising. In spite of the apparent usefulness of autoradiography in demonstrating segregation, it has had very limited success in demonstrating grain boundary segregation. Sulfur segregation in iron1 and possibly polonium segregation in Pb-5 pct B1 2 alloys are the only autoradi-ography experiments that have demonstrated segregation to grain boundaries in metals without the formation of a second phase. Segregation to a boundary without the formation of a second phase is often called Gibbs&apos; absorption and is discussed by McLean in Chapter 5 of Ref. 10. There are several394 experiments showing grain boundary diffusion of a radioisotope, but this type experiment is not representative of equilibrium between the concentration of an element at a grain boundary and that in bulk, so it will not be discussed in this paper. In an attempt to determine if temper embrittle ment of low-alloy steels was associated with segregation of antimony to grain boundaries, a program to use auto-radiography (using Sb-125) was initiated. Even though other measurements strongly suggest that segregation is occurring during embrittlement, no evidence of grain boundary segregation was observed in the auto-radiography experiments. An attempt was also made to detect segregation of carbon (using C-14) to grain boundaries in iron during slow cooling. There is again strong indirect evidence7 that segregation occurs during such a treatment, but the autoradiography experiment gave no evidence of such segregation. Because of the failure of these experiments and the general lack of success by our metallographic unit in measuring grain boundary segregation using autoradi-ography, a model system amenable to mathematical analysis was devised to determine which variables in the experiment are most important. MODEL SYSTEM The model system is illustrated in Figs. 1 and 2. It is a semi-infinite bicrystal with a single grain boundary perpendicular to the top face. The width of the grain boundary, W, is defined as the region to which segregation has occurred and it is assumed that this region is of constant composition. The assumption of an infinite dimension is for mathematical reasons but the results of such an analysis (as will be demonstrated later) are valid for even very small specimens. It also is assumed that the measurement is not limited by means of detecting the radiation (photographic emulsions, counters, and so forth) but that the means of detecting radiation is linearly sensitive to the radiation and has infinite resolving power. The distance y is the perpendicular distance from the center of the grain boundary to the point at which the background radiation is measured and x is the integration variable. CALCULATION FOR BETA PARTICLES Two values of the intensity of radiation will be calculated, the intensity at the center of the grain boundary and the intensity far from the grain boundary. The radiation at the center of the grain boundary can be calculated in the following way. Assume a grain boundary of width W having a uniform concentration equal to Cgb + Cb where CGb is the excess concentration of the element under consideration at the grain boundary and Cb is the bulk concentration. The intensity of radiation, IgB, at the center of the grain boundary, is a consequence of the amount of radioactive material, decay rate, absorption, and geometrical factors which can be represented mathematically by the following expression:

Jan 1, 1968

By Larry G. Hayes

Development of the Bowers-Campbell zinc deposit, located in the Shenandoah Valley two miles northwest of Timberville, Va., was commenced in 1956 by the Tri-State Zinc Co. The occurrence of lead-zinc mineralization in this area has been known for many years, but the first serious exploration program was initiated in 1951 by the geologic staff of Tri-State Zinc Co. Ordovician dolomites. The deposit is approximately 700 ft long, 100 ft wide, and 475 ft thick. Its projected plan has an elongated ovoid shape, where- as the profile appears boot-shaped with the upper portion outcropping. Vertical cross sections show the lense as having been thrust-faulted along certain bedding planes. The movement along these bedding thrusts varies greatly and in one case, has offset the deposit so as to divide it into an upper and lower orebody. The breccia lense strikes parallel to the N 34" E strike of enclosing strata.

Jan 9, 1960

By J. C. Smock

THE magnetic iron ores of New Jersey are found in the northern part of the State, in the Highland Mountain range, which runs from the New York line on the northeast, to the Delaware River, near Easton, at the southwest. The same range continues across Orange County to the Hudson River, and towards the southwest it is known in Pennsylvania as the South Mountain. It is more properly an elevated table-land, quite deeply furrowed by several narrow, longitudinal valleys, and shorter cross-valleys or gaps. The ridges or lines of elevation, as well as the lower valleys, conform in their general direction very closely to the general trend of the whole belt or table-land, that is, from northeast to southwest. This also agrees with the prevailing strike of the rocks. This great uniformity in the altitudes of the hills and ridges, and the direction of the lines of depression corresponding to the strike of the strata, point to an original table-land, which, through the long action of denuding agents, has been quite deeply eroded, giving rise to the present surface configuration, so that some of the former and uniform features have been partially obliterated. The very few cross-valleys or depressions are much more irregular in their course, and serve as outlets through which the drainage is carried either into the Kittatinny Valley on the northwest, or to the broad, red shale and sandstone plane bounding the highlands on the southeast. The area of this highland

Jan 1, 1874

By R. A. Sharma, F. D. Richardson

Manganese oxide acitivities and sulfide capacities have been measured at 1650°C in mixtures of MnO + A1203 and MnO + SiO2 - Al2O3. Sulfide capacities have also been measured at 165O0C for melts of MnO + SiO2, MgO + SiO2, MgO + SiO2 + Al2O3, MgO + MnO + SiO2, and SiO2 + Al2O3 and for crystalline CaO. The activity coefficients of the sulfides of manganese and magnesium have been derived where possible. It looks as though the activity coefficients of sulfides are greatest at compositions where the free energies of formation of the silicate mixtures have their maximum negative values. The amphoteric nature of alumina is reflected in the results for the binaries and ternaries in which it is present with silica. The limiting solubility of CaS in CaO at 1650°C is 6.3 x 10-4 mole fraction. THE activities of manganese oxide have been measured in a variety of silicate and aluminate melts by use of the equilibrium (MnO)slag = [Mn]pt .½O2 [l] and the experimental techniques described previously.&apos; Sulfide capacities (CS = wt pct S (PO2/PS2)½) have also been determined in a series of melts, by use of an established method2 which exploits the equilibrium (O°) + ½S2 = (S") . ½O2 [2] If CS and the activity of a metal oxide are known in a melt, the activity coefficient of the metal sulfide can be calculated by use of the equilibrium constant K, for the pure phase reaction MO i ½S2 = MS + ½O2 [3] The activity coefficient of the sulfide is then given by the equation

Jan 1, 1965

By A. C. Losekamp, R. M. Fincel, J. B. Conway

TANTALUM like several other metals exhibits a great affinity for or reactivity with certain gases. Tested in atmospheres which are not completely pure this metal becomes contaminated by certain impurities (notably nitrogen, oxygen, and hydrogen) with a resultant change in various properties. Well-known are the drastic changes in hardness, ductility, and electrical resistivity. Also previously recorded are the distortions of the lattice1,2 accompanying the increased content of oxygen and nitrogen in tantalum. This pronounced affinity for certain gases along with the significant property variations thereby produced makes it necessary to observe additional experimental precautions in making various property determinations with tantalum. Some recent measurements of the linear thermal-expansion characteristics of tantalum have made this point quite emphatically. Failure to observe the greatest precautions in reducing the contaminating influence has led to some extremely distorted results. Not only does such operation lead to different heating and cooling curves during the thermal-expansion measurements, but upon cooling to room temperature the sample is found to have suffered a permanent (actually semipermanent since the specimen can be returned to its original length by a 3-hr degassing treatment in vacuum at 2300°C) elongation. In addition, subsequent heatings will not follow the initial heating curve unless the expansion measurements are based on the actual specimen length at the beginning of the heating cycle. These thermal-expansion measurements were made by positioning the specimen horizontally at the longitudinal midpoint of a 20-in.-long, 4-in.-diam resistively heated tungsten tube furnace. The specimens were in the form of 20-mil sheet formed into a sharp U-shape about 0.3 in. in width and 0.3 in. in depth. Fiducial marks in the form of 0.010-in. holes drilled at either end of the 2.5-in.-long sheet specimens were viewed by a paired filar micrometer telescope system mounted on an Invar bar on the top of the furnace. Tests were made in helium with temperatures measured by a Pt/Pt-lORh thermocouple to 1000°C; above 1000°C temperature was measured by means of an optical pyrometer sighted into a black-body hole drilled into the specimen-holding fixture in the vicinity of the specimen. Previous tests with black-body holes drilled in a 0.25-in.-diam rod specimen had confirmed the temperature uniformity between specimens and specimen-holding fixture in this furnace. A typical thermal-expansion curve for arc-cast tantalum in helium is shown in Fig. 1 for the case where no attempt is made to remove all the impurities from the cover-gas atmosphere. The initial heating curve appears smooth and has a shape characteristic of all metals. However, it is known that the sample begins absorbing impurities at temperatures above 1000°C which are sufficient to distort the lattice and lead to specimen lengths which are somewhat larger than would be obtained in the absence of contamination. During the cooling cycle the expansion curve is seen to be significantly different from the heating curve. This is due to the impurity content causing a semipermanent (i.e., permanent until the impurities are removed by vacuum degassing) deformation which will not allow the speci-

Jan 1, 1965

By Arthur W. Rose

Statistical techniques are being widely used in geochemical exploration to answer questions involving sample spacing, analytical and sampling errors, thresholds, data smoothing, and optimum combination of several elements into one measure of favorability. The applications of sampling theory, mean and standard deviation, trend surfaces, moving averages, factor analysis, cluster analysis, discriminant analysis, and regression analysis to these questions are discussed with examples. Although the techniques are very useful as means of handling large amounts of data, they require as much geological and geochemical judgment as any other approach to data interpretation.

Jan 1, 1973

By David T. Peterson

Calcium metal was found to deoxidize thorizcm at 1000° to 1200° C. The reaction kinetics were determilled and related to the diffusion coefficients of oxygen in thorium. The solubility of oxygen in thorium, the minimum oxygen concentration, and the diffusion coefficient were determined from 1000° to 1200°C. This firocess results in the lowest oxygen concentrations zohich have been reported for thorium metal. FOR many years it has been known that calcium metal will reduce thorium oxide to thorium metal. This reaction has been the basis for several methods of preparing thorium metal. From the equations giv-by Kubaschewski and vans, &apos; AF" for the reaction Cao, + Tho,(,) - CaO(,, + Th(,) was calculated and found to be -3.4 kcal at 1000°C, -2.5 kcal at llOO°C, and -2.0 kcal at 1200°c. Thorium is very slightly soluble in liquid calcium, and the solubility of calcium in solid thorium is very low. Consequently these metals would be in essentially their reference states. If thorium containing oxygen were equilibrated with liquid calcium between 1000° and 1200°C, the oxygen content of the thorium would have to be below the solubility limit in thorium. Oxygen is one of the impurities most difficult to remove from thorium and is the most abundant impurity in metal prepared by almost all known methods. Fortunately, oxygen does not have a large influence on the properties of thorium because the solubility in solid thorium is very low. EvenT in thorium containing 100 ppm of 0, particles of thorium oxide can be observed in the microstructure. In view of the incompatibility of thorium oxide and liquid calcium and the low solubility of thorium oxide in thorium, the deoxidation of thorium by this method was investigated. For thorium containing an amount of oxygen well in excess of the solubility limit, the reaction should proceed in the following sequence. The oxygen content of the thorium matrix near the surface would be depleted by the diffusion of oxygen to the surface. At the surface, the oxygen would react with calcium to form calcium oxide. To maintain equilibrium within the thorium, thorium oxide would dissolve to keep the matrix saturated. Consequently, the thorium-oxide particles would disappear first at the surface and then the particle-free rim would grow in thickness. If the rate-controlling step were the diffusion of oxygen through this layer of thorium which was growing in thickness in direct proportion to the amount of oxygen removed, the well known parabolic time law should be observed. If the oxygen concentration at the surface of the thorium and at the inner surface of the deoxidized rim were known, the diffusion coefficient of oxygen in thorium could be calculated from the parabolic rate constant. EXPERIMENTAL PROCEDURE The thorium metal used in this study was prepared by calcium reduction of ThF, by the method described by Wilhelm.&apos; The analysis of this metal is given in Table I. The carbon was determined by combustion, the oxygen by the HC1-insoluble residue method, nitrogen by the Kjeldahl method, and the other elements by emission spectroscopy. A section of this ingot was hot rolled at 600°C to 1/4 and 1/8-in. thick plates. Specimens approximately 7/8 in. square were cut from these plates, and all surfaces of the specimens were cleaned and smoothed by filing with a clean file. Individual specimens were placed in 1-in. diam by 2-in.-long tantalum capsules. Approximately 1 g of clean, high-purity calcium was placed in the capsules and an end closure arc-welded in place. The tantalum capsules were sealed in Inconel crucibles to protect the reactive metals from oxidation. The entire loading procedure was done in a glove box filled with pure argon. The loaded crucibles were placed in a muffle furnace, controlled within 2OC of the desired temperature, for a measured length of time. After the specimen had cooled to room temperature, it was sectioned perpendicular to the large faces and through the mid-point of two of the sides. The sectioned specimen was mounted and polished through Linde A abrasive. The rim which was free of thorium-oxide particles could be clearly observed microscopically as mechanically polished. Twenty measurements of the thickness of the rim were made at equally spaced points far enough from the end of the

Jan 1, 1962

By D. J. DeLazaro, W. Rostoker, R. E. Riley, M. Hansen

At very low concentrations, carbon dissolves interstitially in molybdenum resulting in a linear expansion of lattice parameter with increase of carbon in solid solution. Geometrical consideration of the relative size of carbon atom to size of interstice approximately predicts the observed volume expansion. THE element carbon, occurring in molybdenum, either as an unavoidable impurity, or purposely added, markedly affects the mechanical properties of molybdenum. Several investigators1-" have noted the occurrence of molybdenum carbide at the grain boundaries of cast molybdenum, and Fischer and Rengstorff&apos; have shown that this intergranular constituent can induce intergranular brittleness. The appreciable change, with temperature, of the solid solubility of carbon in molybdenum, found by Few and Manning," suggests other important effects upon mechanical properties. Finally the relative atom diameters of carbon and molybdenum (the ratio of atom diameters is 0.59) are indicative, by analogy with iron (ratio of carbon atom diameter to iron atom diameter is 0.65), of a possible interstitial solid solution. If carbon dissolves intersti-tially in molybdenum, anelastic effects and age-hardening effects, similar to those observed in other body-centered cubic metals, could be expected. However, from the work of Sykes, Van Horn, and Tucker," it might be inferred that carbon forms only a substitutional solid solution with molybdenum. These considerations made it desirable to study the effect of carbon on the lattice parameter of molybdenum in greater detail than heretofore. All heat treating was done in a high temperature furnace7 built specifically for heat treatment of molybdenum. The temperatures and times of heat treatment were determined from the a solubility limit for the Mo-C system." These heat treatments were carried out in argon which was purified with respect to N, and H.!0." Purification of the argon was accomplished by passing the argon over hot (750°C) titanium and then through a magnesium perchlorate drying tower. As many as six samples were run concurrently and quenched at different times without interrupting the furnace cycle. Both the purity of the furnace atmosphere and ability to quench samples from any temperature up to 4000 °F were of prime importance in the successful heat treatment of samples for the lattice parameter investigation. Carbon Analysis The Leco Combustion apparatus was used for carbon analysis. This apparatus is capable of an accuracy of & 0.003 pct for a 1 g sample in the range below 0.10 pct. However, it is felt the degree of accuracy is somewhat better than this limit in view of the consistency evident by cross checking a number of determinations. The Battelle Analytical Laboratory consistently reported check results to within k 0.001 pct C. X-ray Measurements The molybdenum wire specimens (20 mils) were carefully filed down to about 12 mils and then etched with nitric acid to 8 mils. Carbon analyses were made on specimens before reduction in size; however, since there was no evidence of surface carburization, it is probable that the carbon was uniformly distributed throughout the sample. The resultant specimens were strain free and small enough to minimize the error in the lattice parameter determinations due to X-ray absorption. Diffraction patterns were obtained with a Debye-Scherrer powder camera 114.59 mm in diam utilizing the Straumanis type asymmetrical film mounting. Nickel-filtered copper. Ka radiation and zirconium-filtered molybdenum Ka radiation were used. Line positions on the film were measured with a traveling microscope equipped with a vernier scale permitting measurement to 0.001 cm. The average of five readings was used to determine the position of each line. The lattice parameter for each specimen was determined from the data by the extrapolation method of Bradley and Jay, Y.e., the intercept at 90" of the straight line obtained by plotting the apparent lat-

Jan 1, 1953

By C. J. Sparks, J. C. Ogle, E. A. Starke

DEFORMATION of cold-rolled fcc metals and alloys produces one or the other of two types of rolling textures, usually referred to as the copper type or the brass type. The pure fcc metals, with the exception of silver, develop the copper-type texture when rolled at room temperature. Silver, brass, and many other alloys develop the brass-type texture. Transition from one texture type to another can also occur. Solute additions to pure copper cause a transition from the copper-type to the brass-type texture.&apos; Varying the deformation temperature also produces texture transitions. Copper rolled at -196°C developed the brass-type texture2 and silver rolled at elevated temperatures, 200°C, developed the copper-type texture.374 The work of Haessner,&apos; Smallman and Green,6 and Hu and coworkers3&apos;4 seems to have established an apparent correlation between the type of rolling texture (and the texture transition) and the stacking-fault probability. Thus materials with low stacking-fault energies are thought to develop the brass-type texture while high stacking-fault energy materials develop the copper-type texture. Mikkola and cohen7 measured by X-ray diffraction techniques the stacking-fault probability, a, in the ordered and disordered fcc alloy Cu3Au. Unexpectedly, ordered specimens showed about twice the stacking-fault probability as the disordered ones. Marcinkowski and Zwe118 also found stacking faults in ordered Cu,Au, but not in the disordered CusAu. More recently, Camanzi and coworkers9 have shown that the intrinsic stacking-fault energy of Cu3Au undergoes a considerable decrease (approximately 100 ergs per sq cm) when passing from the disordered to the ordered phase. In general, deformation reduces order&apos;&apos; but some of our measurements showed that some long-range order still remains in Cu3Au after cold reduction by rolling 80 pct. From the above considerations Cu3Au offers the possibility of studying the texture transition in fcc alloys without varying either the temperature or the composition. If the stacking-fault energy correlation is correct, an initially ordered alloy should develop the brass-type texture during rolling while a disordered alloy should develop the copper-type texture. The present communication describes some initial results of experiments designed to investigate this possibility. The rolling textures of ordered and disordered Cu3Au samples were determined after various amounts of deformation. The ordered sample had an initial long-range-order parameter of S = 1, determined from X-ray diffraction. The grain size of both the ordered and disordered samples was the same, and the initial textures of both were also identical and approximately random. No obvious differences in the deformation textures of the ordered and disordered materials were detected up to 35 pct reduction and the (111) pole figures of Fig. 1 resemble that of pure copper. However, with reduction larger than 35 pct and less than 50 pct, a marked deviation from the copper texture was noted in the ordered material. The newly developed orientation was close to the (110)[i12] ideal orientations re-

Jan 1, 1970

By John R. Hutchins

1ms is a report of nickel (wire) oxidation studies designed to test the validity of Valensi&apos;s1 equation developed for the kinetics of a reaction controlled by diffusion in a continuously growing product layer on cylindrical surfaces. The equation is:

Jan 1, 1968

By Walter Weeks

LITTLE study has been made of the pressure changes and energy losses that take place when an air current is divided into splits which subse-quently unite. The discussion and the experiments that are described in this paper deal with the division of an air current into square splits of equal size, the area of each of the splits at the downstream junction being one-half the area of the main duct. APPARATUS AND SYMBOLS The duct system shown in Fig. 1 was built of Y4-in. redwood and made as smooth as possible.The section of the top over the splits and the zone of mixing was of plate glass to permit observation of the stream lines. FIG. 1-DUCT SYSTEM. Static pressures were measured by means of pinhole tubes and a precise inclined manometer. Measurements of rates of flow were .made by determining the drop in pressure through concentric square orifices in the splits. The air was supplied by a fan operated by a direct-current motor that received its current from a motor generator set. Delicate rheostats in the armature. of the motor. made possible the perfect control of the fan speed, which was indicated on an electrical tachometer. Vanes to straighten the. flow were placed at the head of the main duct.

Jan 1, 1933

I AM sure you know that it is necessary to draw the gold into wire in order to make gold cloth, gold embroidery, or gold filigree work. Just as it is beaten to form leaf for ornamenting pictures, so also can gold be drawn easily. The same is done with silver and tin, and I believe it could also be done with iron, copper, and brass. Although brass is not so

Jan 1, 1942

By W. T. Isbell

In the Parkes process of lead refining, after desilverization has been completed by means of the addition of zinc, there remains in the lead from 0.5 to 0.6 pct zinc. At this stage in the refining operations virtually all impurities are reduced to refined lead specifications except zinc and antimony. All excess copper, nickel and cobalt have been removed by the zinc additions. The silver remaining should not exceed 0.1 oz per ton. It then remains only to remove the zinc and antimony in order to produce refined lead. At the Herculaneum plant of the St. Joseph Lead Co., practice formerly was to complete the refining by means of oxidation in a reverberatory furnace. This process consisted of heating the lead to 1400O to 1500OF and allowing it to come in contact with excess air passing over the surface of the lead and periodically agitating the bath of lead with air. This procedure not only resulted in the loss of zinc but of a considerable quantity of lead converted to the oxide in the form of dross and fume. The fume, collected in the baghouse, together with the dross was returned to the blast furnace, thus adding appreciably to the circulating load on the blast furnace and refinery. In addition, operation and maintenance of the reverberatory furnace were expensive and required the performance of disagreeably hot and somewhat hazardous work. The process of dezincing with high vacuum was developed at this plant as a substitute for the oxidation process and finally led to lower operating costs, the practical elimination of dross and fume and the direct production of metallic zinc, which is very suitable for re-use in the desilverization process. Essentially this process consists of subjecting the lead to high vacuum, in a kettle provided with means for heating, a bell-shaped member open at the lower end so constructed that it can be immersed in the molten lead, and means for evacuating the interior of the bell and for sealing an agitator. Metallic zinc is thus produced and collects on the upper cooled part of the bell member. This metallic zinc is periodically removed and re-used in the desilverization process. The process is quite simple. It is conducted at a low temperature, thus permitting the use of iron equipment, and shows a material saving in refining costs over the old method. Equipment and Its Uses Degincing Machine.—The equipment employed in this process consists of a dezincing machine, a steel kettle of 120 tons capacity, a vacuum system and equipment for handling the dezincing machine (Fig 1). The dezincing machine consists of a compact assembly, suitable for handling with an overhead crane, consisting of a treating chamber and the agitating mechanism. Treating Chamber.—The treating chamber is a bell-shaped shell (4), similar in shape to a hemispherical kettle with a lid

Jan 1, 1949

By J. A. Lund, A. M. Lawson

THE structures of quenched eutectoid and hypereu-tectoid Fe-Cu alloys have been examined by X-ray diffraction and by optical and electron microscopy. The relevant portion of the Fe-Cu phase diagram is given in Fig. 1. Several values have been reported for the solubility of copper in a Fe at the eutectoid temperature, including 1.4 wt pct by orton&apos; and 2.13 wt pct by Wreidt and Darken.2 Alloys containing 4.8 and 7.5 wt pct Cu have been prepared from two batches of Ferrovac E iron (0.005C and 0.013C) and electrolytic tough pitch copper (99.90 Cu). Specimens of dimensions 0.8 by 0.8 by 0.1 in. were cut from hot-rolled material, austenitized, and quenched into brine at 25°C. Similar specimens were also cooled in the furnace, after a short soaking treatment at 1100°C, at a rate estimated to be 10°C per min in the temperature range of 900" to 500°C. X-ray diffractometry was performed on quenched and on furnace-cooled bulk specimens using iron radiation. Only a bcc phase could be detected in all samples. Lattice parameters were calculated from measurements on four lines, made up of two resolved high-angle doublets. Comparisons were made against a silicon standard. Results are shown in Table I. Based on X-ray diffraction studies of a series of alloys of lower copper concentrations, orton&apos; estimated that the tattice constant of a Fe at 25°C increases 0.0014A per wt pct Cu in solution. Extrapolating Norton&apos;s data, it may be concluded that all copper was retained in solution in the brine-quenched 4.8 pct Cu alloy, and that approximately 5 pct Cu was also held in solution on quenching the 7.5 pct Cu alloy. Typical microstructures of brine-quenched specimens, as observed by optical microscopy, are shown in Figs. 2 and 3. Precipitation of the E phase (copper-rich) occurred along the y grain boundaries on quenching the 7.5 pct Cu alloy, rendering them readily detectable in the microstructure, Fig. 3. The original boundaries in the 4.8 pct Cu specimens were gener- ally not discernible, however. This indicates that the z phase which was seen in the higher-copper alloy was probably of proeutectoid origin. Thin foils for transmission electron microscopy were obtained from bulk specimens by spark machining to 0.006 in. thickness, followed by electrolytic polishing. Typical transmission electron micrographs

Jan 1, 1967

By D. T. Peters, S. Floreen

The age hardening behavior of an Fe-8Ni-13Mo alloy was studied after the matrix had been varied to produce either ferrite, cold u~orked ferrite, or nzassive nzartensite. The aging behavior of the cold worked ferrite and murtensite structures were very similar. The martensite aging kinetics were much different from those observed in earlier studies of aging of maraging steels, even though the martensite wzatri.r had the same dislocation structure as those found in maraging steels. The results suggest that the previously observed precipitation kinetics of maraging steels ?nay have been controlled by the nucleation be-haviov, which in turn were dictated by the alloy compositions and the resultant identities of the precipitating phases. IT is well known that the rate of precipitation from solid solution depends not only on the degree of super-saturation, but also on the density and distribution of dislocations in the matrix structure. These imperfections often act as nucleation sites, and may also enhance atomic mobility. &apos;Thus, the presence of dislocations is important since the type and distribution of precipitates may be determined by them. The precipitate density and morphology in turn affects the mechanical properties of the alloy. A number of studies have been devoted to the precipitation characteristics in various types of maraging steels.&apos;-" These are iron-base alloys containing 10 to 25 pct Ni along with other substitutional elements such as Mo, Ti, Al, and so forth, that are used to produce age hardening. The carbon contents of these steels are quite low, and carbide precipitation is not believed to play any significant role in the aging reactions. After solution annealing and cooling these alloys generally transfclrm to a bcc lath or massive martensite structure characterized by elongated martensite platelets that are separated from each other by low angle boundaries, and that contain a very high dislocation den~it~.~~~~~~~~-~~ Age hardening is then conducted at temperatures on the order of 800" to 1000°F to produce substitutional element precipitation within the massive martensite matrix. Most of the aging studies to date have revealed several common traits in these alloys, regardless of the particular identity of the precipitation elements. Generally hardening has been found to be extremely rapid, with incubation times that approach zero. The agng kinetics, at least up to the time when reversion of the martensite matrix to austenite begins to predominate, frequently follow a AX/~~ = ktn type law, where x is hardness or electrical resistivity, t is the time, and k and n are constants. The values of n are frequently on the order of 0.2 to 0.5, which are well below the idealized values of n based on diffusion controlled precipitate growth models. Finally, the observed activation energy values are typically on the order of 30 kcal per mole, and thus are well below the nominal value of about 60 kcal per mole found for substitutional element diffusion in ferrite. The common explanation of these observations is that the precipitation kinetics are controlled by the massive martensite matrix structure. Thus, the absence of any noticeable incubation time has been attributed, after ~ahn," to the fact that the precipitate nucleation on dislocations may occur without a finite activation energy barrier. The low values of the activation energy are generally assumed to be due to enhanced diffusivity in the highly faulted structure. If this explanation that the precipitation kinetics are dominated by the matrix structure is correct then one should observe a distinct difference in lunetics between aging in a martensitic matrix and aging the same alloy when it has a ferritic matrix. Such a comparison cannot be made with conventional maraging compositions, but could be made with the alloy used in the present study. In addition, the ferritic structure of the present alloy could be cold worked to produce a high dislocation density so that one could determine whether ferrite in this condition would age similarly to martensite. EXPERIMENTAL PROCEDURE The composition of the alloy used in this study was 8.1 pct Ni, 13.0 pct Mo, 0.10 pct Al, 0.13 pct Ti, 0.012 pct C, bal Fe. The alloy was prepared as a 40 lb vacuum induction melt. The heat was homogenized and hot forged at 2100°F to 2 by 2 in. bar, and then hot rolled at 1900°F to $ in. bar stock. The aging lunetics were followed by Rockwell C hardness and electrical resistivity measurements. Samples for hardness testing were prepared as small strips approximately 2 by $ by 4 in. thick. Electrical resistivity was studied on cylindrical samples approximately 2 in. long by 0.1 in. diam. The method for making the alloy either martensitic or ferritic was based on the fact that the alloy showed a closed y loop type of phase diagram. At high temperatures, above approximately 24003F, the alloy was entirely ferritic. Small samples on the order of the dimensions described above remained entirely ferritic after iced-brine quenching from this temperature. In practice, a heat treatment of 1 hr in an inert atmosphere at 2500°F followed by water quenching was used to produce the ferritic microstructure. These samples were quite coarse grained and usually en-

Jan 1, 1970

By Wheeler Davey

WHEN metals are subjected to mechanical working, such as rolling, one of the phenomena that take place is a movement of the crystals of the metal into a system or systems of orientation which bear an angular relation to the direction of working. In rolled metal the crystals may orient themselves with respect to the rolling plane or the rolling direction, or both. Direct evidence of the existence of preferred orientations in rolled metal has been obtained by numerous investigators from X-ray patterns of the rolled metal. Most of these workers used a monochromatic pinhole method. Where the degree of preference for a single orientation is high the monochromatic pinhole pattern may be interpreted by a geometrical calculation based on the angular relationships of the planes in the crystal and the diffraction arcs on the X-ray pattern. This process may be aided by the geometrical construction of the locus sphere (Langenkugel), and reflection circles of Polanyi,1 Polanyi and Weissenberg,2 and Mark and Weissenberg,3 and of the plane polar figures (flachenpolfigur) of Franz Wever.4 R. M. Bozorth5 solves X-ray patterns from metals having a single preferred orientation by means of a series of charts which when placed over the X-ray pattern give directly certain angular relationships, between the crystal planes and the surface of the specimen.

Jan 1, 1929

By Elton A. Youngberg

The Holden mine operated by the Chelan Division of the Howe Sound Co. is on the east slope of the Cascade Range in north central Washington on the south slope of Railroad Creek valley at an elevation of 3500 ft. The mine may be reached by a 40 mile boat trip from the town of Chelan which is at the southern tip of Lake Chelan, to Lucerne at the mouth of Railroad Creek and an 11. mile bus ride up Railroad Creek to Holden. A11 freight and concentrate is moved over this route to Chelan Falls on the Columbia River which is on the railroad four miles below the town of Chelan. The mine is now producing 2000 tons of gold, copper, and zinc ore per day which is treated in the Holden mill. Gold-copper and zinc concentrates are made, the first of which is shipped to Tacoma, Wash., and the latter to Kellogg, Idaho, for smelting. Ore is broken by long-hole blasting using the Noranda system which has been modified to meet local conditions. Until recently, blastholes have been drilled by diamond drills. Now a partial substitution of percussion drill holes, drilled with tungsten carbide insert bits, is being made. Geology The ore body occurs as a replacement deposit in a highly metamorphosed series of sedimentary rocks, mainly gneiss and schists, in a shear zone several hundred feet in width and of undetermined length. Commercial ore has been found in mineable widths of 25 to 100 ft for approximately 2500 ft along its strike. The commercial minerals are chalcopyrite, sphalerite, and gold. During the period of mineralization considerable silicifica-tion took place giving the ore an abrasive drilling characteristic. Following the period of mineralization, numerous dikes were introduced into the ore body. The earlier ones were of granite composition having a width of a few inches up to 80 ft. These were followed by much younger, fine grained basic dikes which usually do not exceed 2 ft in width. Development of Percussion Blasthole Drilling Equipment Test work with the 1½-in. tungsten carbide bit was carried on in development headings for several months early in 1947. The short life of the bits, because of gauge loss caused by the abrasive nature of the rock, prevented its adoption for this use. However fast drilling speed and ability to drill a long uniform hole suggested its use for drilling blastholes in competition with diamond drills as diamond costs were steadily increasing and exper-ienced drillers were difficult to obtain. The 1½-in. bit was the largest available at the time initial test work was started with sectional steel. The 1½-in. hole limited the diameter of the steel thread and coupling which could be used. Type F couplings were first used but because of the small thread section excessive breakage of the steel was experienced. Type H couplings were tried next. In order to use this coupling which is 15/8 in. in outside diameter, it was reduced to 1 3/8 in. giving 1/8 in. clearance between the coupling and the hole. Rod breakage at the thread was substantially reduced but some coupling breakage was experienced, however the overall performance was considered satisfactory (see Fig 1 for illustration of coupling and thread). Early test work with the 1½ in. bit indicated machines of piston diameters larger than 255 in. would cause inserts to loosen or break. It was found however that the additional weight of the sectional steel cushioned the blow enough to prevent bit failures when 3-in. Leyners were used. Rods used with the 1½-in. bits were 7/8 in. q. o. for sectional steel and 1 in. q. o. for all chuck pieces. In May 1948, 2-in. tungsten carbide bits became available and test work was immediately started. The 2-in. hole approximated the AX (1 15/16 in.) diamond drill hole which was being used exclusively for blastholes and permitted their substitution for diamond drill holes in a ring without alteration of pattern, burden, or explosives. The 2-in. bit also gave room in the hole for larger couplings and permitted the use of heavier rods and 3½-in. machines, increasing the

Jan 1, 1950

By William R. Webster

In view of the great interest now taken in the tests of castiron and details of foundry practice, with the number of investigators at work, and recent improvements in the methods of research, it would seem that the time is ripe to attempt the solution of some of the many problems with which iron founders have to contend. Recent papers and discussions on these subjects* have opened up s large field for investigation, and have emphasized the importance of many considerations generally overlooked. With the view of promoting a comprehensive and systematic discussion, I have attempted to tabulate, in conveilient form, some of the most important points for investigation, on the general plan suggested, with such good results, by our former President, H. M. Howe, for the discussion on the Physics of Steel, at the Virginia Beach meeting, last year. This table can, no doubt, be modified or enlarged to advantage, and put in shape to serve as a guide or reminder to all who are interested in this line of work. Suggested Lines for Discussion and Investigation. I.—Correspondence between chemical composition and melting point, fluidity, shrinkage, fracture, chill, micro-structure, and other physical properties. II.—Influence of: I. Cupola mixture, use of steel and other scrap, oxidized or clean material, 2. Manner of melting, flux, etc., 3. Casting temperature, A. Fracture. 4. Manner of handling melted metal and B. Micro-structure. method of casting, C. Physical properties. 5. Size and form of casting, D. Shrinkage. 6. Kind of mould, green sand (under dif- on 1 E. Chill. ferent conditions of ramming, amount F. Residual stress. of moisture, and skin-dried), dry sand, G. Condition and quan loam, and chills, tity of carbon and 7. Rate and mode of cooling castings, other elements. 8. Manner and temperature of heating for annealing, 9. Additions of nickel or aluminum,

Jan 1, 1896