By I. W. Wark

AN attempt has been made to compare the influences of the two most widely used depressants-alkalis and sodium cyanide-and the most widely used activator-copper sulfate-on the air-mineral contact induced by five sulfur-bearing compounds: (1) sodium di-ethyl dithio-phosphate (sodium Aerofloat); (2) potassium ethyl xanthate; (3) sodium di-ethyl dithiocarbamate; (4) potassium iso-amyl xanthate; (5) potassium di-n-amyl dithiocarbamate. Three different organic types are included in this group and for two of these types a higher and a lower homologue have been tested. The study of potassium ethyl xanthate, the preliminary results of which have been described,1 was continued until there had been obtained a comprehensive account of the influence of variations in pH value and in the concentrations of xanthate, sodium cyanide and copper sulfate on the adsorption of this xanthate by galena, sphalerite, pyrite and chalcopyrite. With concentrations of copper sulfate and collector that the work with ethyl xanthate indicated would give the most illuminating results, the other four collectors were tested in a less exhaustive way. The same general principles determine the influence of alkalis, cyanide and copper sulfate, no matter to which type the collector belongs, but there is a gradation in the quantitative measure of such influence. In the list above, the five collectors are cited in the order of their capacity to withstand the depressants, sodium Aerofloat being the least resistant, potassium di-n-amyl dithiocarbamate the most resistant. This order coincides substantially with that of the solubilities of the heavy metal salts formed by double decomposition with the collectors, those formed from sodium Aerofloat being most soluble. There is little difference between the third and fourth members of the series, and under certain conditions their positions are reversed.

Jan 1, 1934

By Thomas L. Watson

A part of the field-seasons of 1900, 1901 and 1902 mas devoted by the writer to a study of the manganese ore-deposits of Georgia. A report embodying the results of this study is rapidly nearing completion, and when finished it will be published as a bulletin of the Geological Survey of Georgia. I believe, however, the importance of these deposits warrants a separate and earlier publication than that made possible by the Survey, in which the more important results of the study are briefly set forth. It is principally for this reason that the present paper has been prepared. Previous Work.—Some of the more important deposits of manganese occurring in the Paleozoic area of Georgia were studied to some extent previous to 1890 by Dr. Penrose;t and again in the early nineties by former State Geologist, J. W. Spencer. In a recent paper published in the Transactions, on the " Geological Relations of the Iron-Ores in the Cartersville District, Georgia," Dr. Hayes briefly mentions the manganeseores of the same district. Distribution of the Manganese-Ores.—Georgia is divisible into three geologically-distinct areas which, named in order from southeast to northwest, are (a), the Coastal Plain; (b), the Crys-

Jan 1, 1904

By Clarence E. Sims

DURING the past several years the steel casting industry has made studies of heavy castings in which the test bar has been taken from heavy sections rather than from attached or separately cast coupons. It has been noted that the ductility properties of these heavy sections are often lower than those normally expected. Such lowered ductility is usually accompanied by a spotty test bar fracture and the ductility values often can be greatly improved if a low-temperature aging treatment is given to the casting. A loss of ductility of this type is considered "abnormal," since it is not accompanied by an increase of tensile strength or hardness, and "temporary" when the ductility can be restored by aging. The cure of such an abnormal condition represents a real improvement in the quality of the steel. Some hundreds of previous investigations, largely qualitative in nature, have established beyond reasonable doubt that hydrogen is normally present in newly manufactured steel and that this gas, in small amounts, can cause a temporary abnormal loss of ductility. The commonly observed association of high gas content and low ductility has given strong evidence for the presumption that hydrogen, possibly assisted by other gases, is the primary cause of the low ductility observed. Accordingly, the Steel Founders' Society of America has, since Nov. 1, 1944, sponsored investigations at Battelle Memorial Institute whose primary objective is to obtain quantitative information on the relation of the amount of hydrogen and nitrogen in steel, together with associated methods of steelmaking and treatment, to low-ductility effects and porosity.

Jan 1, 1947

By E. A. Gulbransen, K. F. Andrew

In a recent communication14 we have reported on the kinetics of the reactions of zirconium with O2, N2 and H2 as a function of the time, temperature and pressure variables. A systematic study was made and the results correlated with fundamental theories of gas-metal reactions. This paper will present a similar study for titanium. Titanium and zirconium are members of the IV group of the periodic table and possess many similar physical and chemical properties as a result of their similar electronic configuration for the outer electrons. The two metals are relatively inert to both gas and liquid phase corrosion at room temperature. However, at moderate temperatures the metals become active and react readily with the common gases including O2, N2 and H2 which are of interest in this study. A study of the kinetics of these gas-metal reactions is of interest for three reasons: (1) to understand the rate of reaction of titanium and its role in the behavior of high temperature alloys; (2) to understand the practical difficulties of the reduction, refining and working of titanium; and (3) to correlate the data with fundamental theories of gas-metal reactions and crystal structure predictions. Literature Survey Several review papers8 and books4243 exist on the preparation and properties of titanium and its alloys. THE METAL Titanium has, at room temperature, a hexagonal lattice of the zinc type. Hagg19 gives a value of 2.953A for the (a) axis, a value of 4.729 for the (c) axis and a density of 4.427 at 20°C. Burgers and Jacobs6 have observed the transformation of the hexagonal to the body-centered cubic structure at 880°C and have established a value of 3.31 for the cube edge and a density of 4.31. TITANIUM-OXYGEN Carpenter and Reavell6 using a pressure change method have studied the reaction at temperatures of 742° and 1000°C and for a pressure of one-fifth of an atmosphere. The probabilities for reaction are calculated from kinetic theory and they report a value of 10-5 for O2 at 1000°C and 10-6 at 740°C. The titanium-oxygen system has been investigated by Ehrlich.10,11 Five phases are observed. Between (TiO2 and TiO1.90) an alpha-phase, consisting ofarutile lattice, is found. A beta-phase is observed between (TiO1.80 and TiO1.70). A gamma-phase is homogeneous between (TiO1.56 and TiO1.46) and has a structure of the corundum type. The delta-phase exists between TiO1.25 and TiO0.6 and has a sodium chloride structure. From TiO0.42 to Ti the metal structure is observed. The surface oxide films have been studied by Hickman and Gulbransen.20 The rutile structure is observed in the temperature range studied, 300 to 700°C. Three crystalline modifications of TiO2 exist: rutile and anatase which are tetragonal and brookite which has an orthorhombic structure. Anatase is reported36 to exist in two forms: I and II. Anatase II changes to anatase I at 642°C. Anatase I is stable up to 915°C where rutile becomes the stable modification. At 1300°C rutile transforms to brookite which melts at 1900°C. The monoxide, TiO, may be prepared from the dioxide by high temperature reduction with carbon or magnesium. Its melting point is 1750°C. TITANIUM-NITROGEN Carpenter and Reavell6 report that at 1000°C a linear rate law is observed. The probability of reaction is given as 10-8 at 1000°C. Fast12 has studied the solubility of nitrogen and its effect on the mechanical properties of the metal. The crystal structure of TiN has been shown by several workers2'21'44 to follow the sodium chloride structure. However, the calculated density is found to differ from the pycnometric value. This is studied by Brager3,4 in detail. He has suggested that the titanium sites in the lattice are only partially filled at low temperatures. As the temperature of preparation is raised the vacant sites become occupied which expands the lattice and increases the hardness and density. An (a) value of 4.22Å is given for room temperature. TITANIUM-HYDROGEN The solubility and the crystal structures observed in this system have been reviewed in a recent book by Smith.40

Jan 1, 1950

By J. R. Szedon, T. L. Chu, G. A. Gruber

Amorphous adherent filnzs of silicon dioxide have been deposited on silicon substrates by the oxidation of silane at temperatures ranging from 650 to 1050C. Various diluents (argon, nitrogen, hydrogen) were used to suppress the formation of SiO2 in the gas phase. Deposition rates of the oxide were determined over the temperature range in question as functions of' re-actant flow rates. Etch rate studies were used for a cursory comparison of structural properties of deposited and thermally grown oxides. From electrical evaluation of metal-insulator-silicon capacitors it was determined that the interface charge density of deposited films is similar go that of dry-oxygen-grown films in the 850° to 1050 C temperature range. Deposited films exhibit several ionic instability effects which differ in detail from those reported for thermal oxides. Stable passivating films of silicon nitride over deposited oxides appear to be practical for use in silicon planar device fabrication. Such films can be prepared under temperature conditions which have less effect on substrate impurity distributions than in the case of grown oxides. AMORPHOUS silicon dioxide (silica) is compatible with silicon in electrical properties and is the most widely used dielectric in silicon devices at present. Silica films can be prepared by the oxidation of silicon or deposited on silicon or other substrate surfaces by chemical reactions or vacuum techniques. The ability of thermally grown silicon dioxide films to passivate silicon surfaces forms one of the practical bases of the planar device technology. Properly produced and treated films of grown SiO 2 can have low densities of interface charge (-1 X 10" charges per sq cm) and can be stable as regards fast migrating ionic sgecies. 1 To maintain these properties, even with an otherwise hermetically sealed ambient, the Sia layers must be at least l000 A thick. Such thicknesses require oxidation in dry oxygen for periods of 7.8 hr at 900°C or 2 hr at 1000°C. Although oxidation in steam or wet oxygen can reduce these times to 17 and 5 min, the resulting oxides must be annealed to produce acceptable levels of interface charge., Oxidation or annealing involving moderate to high temperatures for extended periods of time can be undesirable. Under some conditions, there can be changes in the distribution of impurities within the underlying substrate. A chemical deposition technique using gaseous am-bients is particularly attractive and flexible for preparing oxide films. With a wide range of deposition rates available, films can be produced under condi- tions of time and temperature less detrimental to impurity distributions in the silicon than in the case of thermal oxidation. The pyrolysis of alkoxysilanes, the hydrolysis of silicon halides, and various modifications of these reactions are most commonly used for the deposition of silica films.3 Silica films obtained in this manner are likely to be contaminated by the by-products of the reaction, organic impurities, or hydrogen halides. The use of the oxidation of silane for the deposition process has been reported recently.4 The deposition of silica films on single-crystal silicon substrates by the oxidation of silane in a gas flow system has been studied in this work. The deposition variables studied were the crystallographic orientation of the substrate surface, the substrate temperature, and the nature of the diluent gas. The electrical charge behavior of Si-SiO2-A1 structures prepared under various conditions was investigated by capacitance-voltage (C-V) measurements of metal-insulator-semiconductor (MIS) capacitors. The experimental approaches and results are discussed in this paper. 1) DEPOSITION OF SILICA FILMS The overall reaction for the oxidation of silane is: The equilibrium constants of this reaction in the temperature range 500° to 1500°K, calculated from the JANAF thermochemical data,= are shown in Fig. 1. In addition to the large equilibrium constants, the oxidation of silane is also kinetically feasible at room temperature and above. However, the strong reactivity of silane toward oxygen tends to promote the nucleation of silica in the gas phase through homogeneous reactions, and the deposition of this silica on the substrate would yield nonadherent material. The formation of silica in the gas phase can be reduced by using low partial pressures of the reactants. Argon, hydrogen, and nitrogen were used as diluents in this work. 1.1) Experimental. The deposition of silica films by the oxidation of silane was carried out in a gas flow system using an apparatus shown schematically in Fig. 2. Appropriate flow meters and valves were used to control the flow of various reactants, i.e., argon, hydrogen, nitrogen, oxygen, and silane. Semiconductor-grade silane, argon of 99.999 pct minimum purity, oxygen of 99.95 pct minimum purity, and nitrogen of 99.997 pct minimum purity, all purchased from the Matheson Co., were used without further purification. In several instances, a silicon nitride film was deposited over the silica film. This was achieved by the nitridation of silane with ammonia using anhydrous ammonia of better than 99.99 pct purity supplied by the Matheson CO.' The reactant mixture of the desired composition was passed through a Millipore filter into a horizontal water-cooled fused silica tube of 55 mm

Jan 1, 1969

By H. G. Sell, G. W. King

An investigation was made of the lensile proper-ties of recrystallized high-purity tungsten and a W-1 pel ThO2 dispersed-phase alloy over the temperature region of 800° to 2400°C. The thoria addition resulted in a modest strengthening effect over the entire temperature region. A decrease in ductility of both materials occurred above 0.5 Tm which was caused by void formation. Current theories of IT has long been recognized that a second phase of hard particles has a strengthening effect on a pure metal. At low or intermediate temperatures (<0.5 Tm), the strengthening effect is thought to arise mainly from the interaction of dislocations with dispersed particles. Above 0.5 Tm, dynamic recovery processes greatly alter the deformation mechanisms from those simply involving glide, and grain bound- strengthening by a dispersed second phase do not adequately explain the tensile results. Melallographic examination suggests that the improved strength of tire alloy results from the effect of thoria on the mierostructure. Stress-dependent thermally activated processes were found to occur high temperatures. aries may act as sources of weakness rather than strength because of grain boundary sliding. Grain boundary sliding at high temperatures has been postulated to be the primary factor giving rise to the formation of voids or cavities at grain boundaries1-3 which in turn cause premature failure and poor ductility.4 Voids, once formed, can grow by the condensation of vacancies from the equilibrium concentration&apos; or from the excess vacancies produced by the deformation.4,5 The high-temperature tensile properties of unalloyed tungsten have previously been investigated by Sikora and Ha116 and also by Taylor and Boone.7 The purpose of the present work was to investigate

Jan 1, 1965

By D. Brion, J. J. Prédali, J. Hayer

The need to grind volcanic-sedimentary ores very finely (d80 < 20 µm) so as to liberate Pb, Zn, and Cu sulfides from their pyritic gangue causes difficulties in selective flotation. The pyrite, which accounts for 70-80% of the mineral content, is insufficiently depressed by the usual pH and NaCN techniques. To determine better depressing methods, the surface evolution of pyrite during flotation was followed by ESCA spectroscopy to compare the stability range in the Eh-pH diagram. Surface iron hydroxide was formed, which is the main pyrite-depressing factor. NaCN appears to play a more restrictive part, since no ferricyanides were detected, except for very small amounts at pH 7.

Jan 1, 1980

By A. W. Hesse

Ventilation of all types of coal mines is fundamentally the same, in that sufficient air must be provided to properly dilute and remove dangerous and obnoxious gases and leave the oxygen content of the air not under 1 9 per cent in all places where men and animals must work. Perhaps animals should not be mentioned, as the speed of mechanical loading leaves livestock behind and outmoded. Since this paper has to do with the influence of mechanical loading equipment on ventilation, the problems will be confined to the splits and the coal-producing places of the mine. The removal of coal dust from the air, or its rapid transmission to the return air courses; the possible increase in the liberation of gases by the multiplication of cuts in the coal made during one shift or multiple shifts; and the additional electrical equipment at the faces, are the factors that cause the added importance to good ventilation in the permissible equipment area of gassy bituminous coal mines. Ventilation tor Mechanical Loading in Gassy Mines In gassy mines, the air currents must be maintained across the faces in such a way as to prevent short cuts to the returns and leaving pockets in which accumulation of gas might occur. To do this, two or more doors are required on almost every entry containing a track to the face, so located that in no event will a trip of cars block open the doors and permit the air to bypass some place or places on the air-approach side. This method frequently requires the use of unusual lengths of duplex cables to reach the mechanical equipment at the faces, particularly where the distances between parallel working places are 100 ft., as at the Nemacolin mine. Fig. I shows a pillar section being worked with mechanical loaders. This layout requires carrying the air in on the right and releasing it on the left, because the track clearance is on the right side and the line brattice is built on this side from the last crosscut to the face. Thus, the air travels to the face with greater velocity and gives more assurance of sweeping out the gas that might be exuding from the crevices of the coal. All working places, in driving through solid coal, are thus treated alike. They are all potentially gassy and must be swept clear of whatever may contaminate the air. Once the air starts into the working section, it is not released until it does a good job. Of course the volume of air must be large enough not only to dilute the gases but to carry away explosive fumes and fine coal dust quickly. Mechanical loading entails cutting and drilling of the coal during the same working period as the loading when two-shift and three-shift operations are employed, and all three processes create finely pulverized coal, which in itself is hazardous if not controlled by some means. If the ventilation is inadequate and gas accumulates, and a spark from defective electrical

Jan 1, 1942

By A. W. Hesse

Ventilation of all types of coal mines is fundamentally the same, in that sufficient air must be provided to properly dilute and remove dangerous and obnoxious gases and leave the oxygen content of the air not under 1 9 per cent in all places where men and animals must work. Perhaps animals should not be mentioned, as the speed of mechanical loading leaves livestock behind and outmoded. Since this paper has to do with the influence of mechanical loading equipment on ventilation, the problems will be confined to the splits and the coal-producing places of the mine. The removal of coal dust from the air, or its rapid transmission to the return air courses; the possible increase in the liberation of gases by the multiplication of cuts in the coal made during one shift or multiple shifts; and the additional electrical equipment at the faces, are the factors that cause the added importance to good ventilation in the permissible equipment area of gassy bituminous coal mines. Ventilation tor Mechanical Loading in Gassy Mines In gassy mines, the air currents must be maintained across the faces in such a way as to prevent short cuts to the returns and leaving pockets in which accumulation of gas might occur. To do this, two or more doors are required on almost every entry containing a track to the face, so located that in no event will a trip of cars block open the doors and permit the air to bypass some place or places on the air-approach side. This method frequently requires the use of unusual lengths of duplex cables to reach the mechanical equipment at the faces, particularly where the distances between parallel working places are 100 ft., as at the Nemacolin mine. Fig. I shows a pillar section being worked with mechanical loaders. This layout requires carrying the air in on the right and releasing it on the left, because the track clearance is on the right side and the line brattice is built on this side from the last crosscut to the face. Thus, the air travels to the face with greater velocity and gives more assurance of sweeping out the gas that might be exuding from the crevices of the coal. All working places, in driving through solid coal, are thus treated alike. They are all potentially gassy and must be swept clear of whatever may contaminate the air. Once the air starts into the working section, it is not released until it does a good job. Of course the volume of air must be large enough not only to dilute the gases but to carry away explosive fumes and fine coal dust quickly. Mechanical loading entails cutting and drilling of the coal during the same working period as the loading when two-shift and three-shift operations are employed, and all three processes create finely pulverized coal, which in itself is hazardous if not controlled by some means. If the ventilation is inadequate and gas accumulates, and a spark from defective electrical

Jan 1, 1942

By H. J. Wasson

Published literature regarding the nation&apos;s oil reserve has been largely concerned with the estimated quantities in sight in known producing fields. This proved reserve has never been large in relation to demand. It has been the practice to consider the total future reserve (beyond that in sight within known fields) in the light of the broad potentialities of vast areas of partially explored sedimentary rocks, which are regarded as possible oil territory. Until recently, but little attention has been given to the rate at which the unexplored potentialities may be. converted into the proved reserve classification. To a certain extent, therefore, our contemporary viewpoint on the subject of national oil reserves is characterized by a pronounced contradiction. On the one hand, we measure known reserves as sufficient for only a few years of consumption—i.e., relative scarcity; on the other hand, we are confident that millions of unexplored acres will yield many new oil fields and that countless deeper productive formations underlie many of our known productive fields—i.e., infinite abundance. Of greater significance than the quantitative measure of either of these reserve classifications is the rate at which reserve replenishment must be accomplished in order to maintain an adequate time supply of proved oil reserves. The accumulation of geological data covering broad areas supports the belief that the remaining undiscovered oil reserve is exceedingly large. The distribution of oil in sedimentary formations of practically all ages, from Cambrian to Recent, is suggestive of almost unlimited possibilities; and the relatively small proportion of these possible areas that has been intensively explored in this country is a further index of the probable magnitude of the undiscovered future reserve. The implication that may reasonably be drawn from these observations is that oil, though distributed with less regularity and concentration than its related hydrocarbon, coal, nevertheless is a relatively abundant natural commodity of which the exhaustion appears remote. Final exhaustion of our oil reserve, if not infinitely remote, is a future contin-

Jan 1, 1937

By Ta M. Li

The implementation of the Clean Air Act (CAA) Amendments of 1970 has resulted in a clean fuels deficit that has significant adverse environmental, energy and economic implications, according to the Project Independence Report. The CAA Amendments charge the Environmental Protection Agency (EPA) to establish national air quality standards as well as national standards for significant new pollution sources and for all facilities emitting hazardous substance. Section 110 of the CAA provides the framework for states to establish "emission limitations, schedules, and timetables for compliance with such limitations, and such other measures as may be necessary to insure attainment and maintenance" of ambient air quality standards. State implementation plans (SIP) are subject to EPA approval. EPA is authorized to enforce federal and state requirements by order or civil suit, including injunctive relief.

Jan 5, 1975

By J. C. Febles

HISTORY. THE use of iron for the precipitation of copper was known at least as early as the fifteenth century. Both Paracelsus and Basil Valentine refer to it in their writings, as early as 1500 A. D. It was used in Peru, for this purpose prior to 1637, and at Rio Tinto, Spain, as early as the sixteenth century. The statement has been made repeatedly that in the early history of the mining industry at Butte, the practicability of this method of recovering copper from solution was overlooked, and that enormous quantities of copper-bearing water were allowed to go to waste, the copper in which might easily have been recovered at small cost; and that this oversight on the part of the mine operators was due to ignorance of this method of recovering copper. As a matter of fact, very little copper-bearing mineral was encountered in the mines of Butte until a depth of 400 or 500 ft. bad been reached, and in many cases much greater depths were necessary to reach the copper-bearing zone. The water encountered in the upper levels (although in most cases quite highly mineralized) contained little or no copper, and it was only after considerable areas of copper-bearing ore had been uncovered and developed that copper sulphate began to. appear in the mine water in any considerable quantity. In fact, the first water that was observed to contain copper carried it in such small amounts as to be of little or no importance. It was only after years of underground work had opened extensive areas of stopes, drifts, and other underground workings, these being subsequently filled with waste, nearly all of which contained small copper values, which became oxidized by exposure to the air and were acted upon by the slowly percolating mineral water, that the recovery of copper from mine water became commercially important.

Jan 7, 1913

By W. B. Plank, A. C. Callen

WAR and normalcy do not walk hand in hand, whether it be in industry, the educational field, or in the daily lives of individuals. Schools and departments offering curricula in mineral engineering have been seriously disrupted, beginning with 1942 and reaching a low during 1944. Selective Service regulations and voluntary enlistments have effectually stopped the flow of college-trained men into the mineral industry, and the flow into the colleges is little more than a dribble. The year just closed has been a most serious one for our institutions. Until March many of our faculties had been kept reasonably intact because of the large training programs of the Army and Navy. Although the number of

Jan 1, 1945

By E. F. Ketterer, D. B. Collyer, A. B. Wilder

The microstructural stability of 59 carbon and low alloy steels after 34,000 hr exposure at 900&apos; and 1050°F, including the weld heat-affected zone, is discussed. The tensile and creep rupture properties of the parent metal of many of the steels before and after 10,000 hr exposure are presented. SEAMLESS pipe has been used for many years at elevated temperatures. When seamless first began to be used, operating temperatures and pressures were relatively low and the steel produced adequately met the existing requirements. The need for knowledge of creep properties and graphitiza-tion was nonexistent. Today the requirements for tubular products have changed considerably. Operating temperatures and pressures are increasing continually and corrosion, particularly at high temperatures, presents a problem. Carbon steels have, under these conditions, certain economic advantages particularly in oil refinery use. However, the use of low alloy steels in the generation of steam power has increased appreciably due to the influence of molybdenum on creep strength and the control of graphitization with chromium. The behavior of carbon and certain low alloy steels after long periods of exposure at 900° and 1050°F (480° and 565°C) has been investigated. The steels were examined before and after 10,000 to 34,000 hr exposure. Results obtained with material exposed at 1200°F (650°C) are not presented due to the severe oxidation and resulting decarburiza-tion after long periods of exposure. The graphitization characteristics of carbon and low alloy steels are of fundamental concern to the users of these materials. This is particularly true where welded joints are employed. In order to evaluate properly the behavior of steels at elevated temperatures, it is desirable to employ not only long periods of exposure under controlled conditions, but to use material with known properties and steelmaking practices. The purpose of this investigation has been to study the microstructure of the weld and the tensile and creep rupture properties of the parent metal after long periods of exposure at elevated temperatures. In the report&apos;.&apos; of a previous investigation data were presented on the microstructure, impact strength, hardness, and oxidation characteristics after 10,000 hr exposure at elevated temperatures. When this investigation was planned, methods for controlling the graphitization characteristics of steel were not established and, therefore, a number of special alloy steels were included in the study. During the exposure of these steels, the influence of aluminum in accelerating the rate of graphitization and the inhibiting power of chromium were established by various investigators. Also, the vanadium-bearing steels, because of their outstanding creep properties, received attention. As a result of these developments, considerable progress has been made in the field of high temperature tubular products, and the necessity for special alloys to prevent graph-itization has been restricted largely to the use of chromium. Material Chemical analysis, deoxidation treatment, and austenitic grain size of the 59 steels discussed in this paper are shown in Table I. The steels were forged to 1x1 in. bars with the exception of steels 12B, 12DX, 12DY, 12DZ, 70, 70A, 72 to 78, 82, and 83 which were machined from heavy wall pipe. All bars were surface ground before exposure. Heat treatment before exposure is shown in Table 11. The majority of the steels included were melted in either a basic open hearth or basic electric furnace; how-

Jan 1, 1955

By Franz Posepny

CONTENTS. Introduction. Part I. General Facts And Theories. [ ]

Jan 1, 1902

By W. V. Bluck, W. L. McMorris

Higher coal quality is being recognized in potentially lowering the cost of power as measured at the bus bar. Assessment of potential coal supplies for most power plants is now going beyond buying at the lowest delivered fuel cost. It is now taking into consideration other factors, such as handling, storage, pulverization cost, boiler fouling, post combustion cleanup, and waste disposal costs. New measurements of quality are being considered now by those producing and those consuming the fuel by assessing numerous variables in the total fuel cycle to achieve the lowest possible power costs.

Jan 1, 1986

By R. Stickler, A. Vinckier

An optical and electron microscope study was made on a commercial 302 stainless steel heat treated for massive carbide precipitation. Convincirg evidence was obtained that the grain boundary precipitate does not grow away from the grain boundary into the matrix, but grows as a network of large thin dendrites in between the grains. IN austenitic stainless steels the carbon in supersaturated solution precipitates when the steel is heated in the temperature range 450" to 1000°C. During such heat treatments the chromium-rich carbide occurs primarily at the grain boundaries and has adverse effects on the corrosion resistance and low-temperature ductility of the material. It has been shown that the morphology of the precipitated particles differs widely depending on the time and temperature of the heat treatment, the nature of the boundary, the misfit between the grains, and so forth.1"5 It was assumed by Mahla et al.,&apos; Streicher,&apos; and Mc Nutt&apos; that the carbide particles which nucleate in the grain boundary grow in various geometric or dendritic forms away from the boundary into the matrix. However, Kinzel,&apos; Hatwell et a, and Plateau et aL4 found that the particles nucleate in the grain boundary and grow as a network of thin dendrites in the grain boundary interface. We have made a comprehensive studyg of the precipitation occurring in a commercial 302 austenitic stainless steel heat treated for times ranging from 0.15 to 1500 hr at various temperatures from 480" to 1065"~. This study was made to elucidate the influence of heat treatments on both the mechanical and the corrosion properties of this steel. Part of this investigation which is pertinent to the morphology of the grain boundary carbides referred to above is separately reported here. We found that the particles which nucleated in the boundaries grew in the interface of these boundaries, thus supporting the viewpoints of Kinzel,&apos; Hatwell et al.,3 and Plateau et al.4 Furthermore, when carbide particles nucleated in the matrix very close to the boundaries, they possessed a morphology distinctively different from the particles growing in the grain boundaries. MATERIAL A study of metallographic samples and of fracture surfaces of a 302 stainless steel is reported in this paper. The composition and heat treatments are listed in Table I. Polished and etched samples were examined und813r the optical microscope, and carbon extraction replicas of etched micrographic samples and various fracture surfaces3&apos;8&apos;9 were examined under the electron microscope. RESULTS AND DISCUSSION A representative optical micrograph of the 302 steel, condition A, is shown in Fig. l(a). Particles can be seen on the grain boundaries but no traces can be found of particles which grow from the grain boundaries into the matrix. A carbon extraction replica of this sample shows numerous large thin dendrites, Fig. l(b). The lateral dimension of such carbide particles vary up to 100 p, and their thickness estimated from the amoun! of electron penetration i:; between 500 and 1000A. Such large dendrites are extracted from almost all grain boundaries and, if they had grown into the grains, they would definitely be revealed by etching traces in the matrix, Fig. l(a). The reason why these large dendrites on the extraction replica appear to be grown into the grain is due to the mechanism of the extraction replica process. Thus, these dendrites are supported by the carbon replica film only at the edges originally along the grain boundary trace A-A, Fig. l(b), in the polished metal section and have subsequently fallen over onto the carbon replica film during handling. Although such dendrites generally fall only to one particular side of the grain boundary trace, one finds occasionally that parts of a dendrite have fallen to both sides, as shown in Fig. l(b). Further evidence for the growth of carbide in the grain boundary can be obtained from the appearance of fracture surfaces. A small impact specimen of the 302 steel, condition A, was broken at liquid nitrogen temperature. The fracture path follows the

Jan 1, 1962

By Janshi Sen

VERTICAL-INTENSITY magnetometers, such as the Hotchkiss Superdip and the Askania vertical field balance, are now [ ] widely used, because vertical-intensity charts give definite information for the location of upper pole, dip and strike, and approximate shape of the deposit. Again, a slow and steady increase of dip over a large area indicates a large deep-lying deposit, while a large dip limited to a small area and falling away rapidly suggests a small and shallow one. The complication comes more from the richness of the ore. A large body of lean ore near the surface might produce the same vertical-intensity chart as a rich ore at depth. This paper presents a method for calculating the maximum depth of a single-pole deposit and another for a two-pole mineral body, by utilizing data of both vertical and horizontal intensities as obtained by a Thalen-Tiberg magnetometer. As shown on the left side of Fig. 1, lean ore, rich ore and a single pole produce the same magnetic field. The depth of the pole, [ ] h, can be calculated from the following relation: [h=a=tan¢=G-F h=aXFy] where G is the vertical intensity at point A due to the pole; F, the horizontal intensity of the same; and a, the distance from the point of maximum vertical intensity or the vertical projection of the pole on the surface to the point of observation A. If an entirely covered deposit is indicated by magnetic measurements and boring cost estimated from the calculated depth is so reasonable as to encourage drilling, the ore should be struck somewhere within the limit of the calculated depth by the borehole. A number of such points as A should be taken for calculation, erratic results should be rejected and the average figure used for cost estimation.

Jan 1, 1944

By C. M. Wayman, G. R. Srinivasan

A metallographic study of the isothermal products formed between 750° and 285°C was made in an Fe-7.9 wt pct Cr-1.11 wt pct C alloy, and a time-temperature-transformation diagram was determined. The study shows that the austenite decomposes into three different products: pearlite above 540°C, ferrite and carbide between 540° and 300°C, and lenticular bainite below 300°C. No upper bainite forms in this alloy. The results are discussed in terms of carbon diffusion models for upper bainite formation. AUSTENITE transforms into several products depending on the temperature, composition, and rate of cooling, and the various transformation products have been a source of controversy for a long time. Since the classical study of Davenport and ~ain&apos; extensive work has been carried out. The present study concerns the isothermal transformations in an alloy which was used for a detailed investigation of bainite crystallography and provides information supplementary to the work of Lyman and Troiano who studied austenite decomposition in steels containing 1 pct C and varying amounts of chromium. Their work showed that increasing the amount of chromium in high-carbon steels had the effect of depressing the B, temperature and of shifting the TTT curves to longer times and lower temperatures. They further found that if the chromium content is increased in a 1 pct steel to about 9 pct no bainite would form even after a period of 100 days. However, a preliminary investigation by the present authors showed that bainite plates do form in steels containing about 8 pct Cr and 1 pct C. In view of this and some results from a thin-foil electron microscope investigation of the bainite formed in the present alloy: it was considered desirable to investigate the other isothermal products as well. EXPERIMENTAL PROCEDURE The alloy used in the present investigation was obtained from a triply vacuum-melted ingot prepared from high-purity materials. Chemical analysis for the alloy verified the composition to be Fe-7.9 wt pct Cr-1.11 wt pct C. Metallographic observations were made on i by i by « in. specimens which were aus-tenitized at 12 50°C for 50 to 60 hr in evacuated quartz capsules and then water-quenched. Since the M, temperature for this alloy is below room temperature, the homogenizing treatment produced a completely austenitic structure consisting of very coarse austenite grains (ASTM #0-1). Several samples of the austenitized specimens were metallographically prepared and observed for any proeutectoid carbide separation. It was found that all the carbon was in solution. The water-quenched specimens were upquenched and given isothermal treatments at temperatures between 285" and 750°C for varying periods in molten salt or lead baths. The specimens were then water-quenched, and those showing less than 5 pct transformation were used for plotting the beginning of the austenite decomposition. To ensure the removal of the disturbed layer, the mechanically prepared specimens were electropolished in a 1:6 HzS04, CHSOH solution for 10 to 15 sec at 20 v. Final polishing was done with a vibratory polisher using 0.05-p alumina. Various etchants including nital, ferric chloride, and hot ferricyanide (Murakami&apos;s reagent) were used to bring out details in the different transformation products. The ferricyanide etch was used whenever the preferential etching of carbides was desired.

Jan 1, 1969