By Charles F. Hickey, Eric B. Kula

Thermomechanical treatments applied to the maraging steels include a) cold working in the austenitic condition at 650°F, followed by transformation to martensite and aging, b) cold working in the murtensitic condition and aging, and c) cold working in the aged condition with and without subsequent reaging. The strength increases in these steels are very small compared to the increases observed in conventional carbon and alloy steels. The changes that are observed are compatible with the strengthening mechanisms operative during thermomechanical treatment of conventional steels, however. Differences are caused by the absence of a carbide precipitate and the low work-hardening rate in both the solution-treated and the aged conditions. ThE 18 pct Ni maraging steels represent a class of steels which are finding great interest for high-strength applications.1~2 They are essentially carbon-free, and contain 7 to 9 pct Co, 3 to 5 pct Mo, and 0.2 to 0.8 pct Ti. Although austenitic at elevated temperatures, they can be air-cooled to room temperature to form a martensite, which because of the absence of carbon is relatively soft. On subsequent reheating age hardening occurs and strength levels of 250 to 300 ksi yield strength can be attained. These steels appear to be particularly suitable for studying the response to various thermome-chanical treatments for additional reasons other than the obvious one of attempting to improve their already attractive properties. Thermomechanical treatments can be defined as treatments whereby plastic deformation, generally below the recrystal-lization temperature, is introduced into the heat-treatment cycle of a steel in order to improve the properties. With an absence of intermediate transformation products on air cooling the maraging steels have good hardenability and hence can readily be cold-worked in the austenitic condition prior to transformation to martensite. Further, they can be worked in the martensitic condition prior to aging, and even can be deformed in the fully aged condition. Finally, it is of interest to compare their re- sponse to that of the more conventional alloy and carbon steels, where the role of carbides is important in the strength increase by thermomechani-cal treatments. The thermomechanical treatment of conventional steels has been the subject of a recent review.' I) MATERIALS AND PROCEDURE The steel used in this investigation was a commercially produced vacuum-melt heat, which had been rolled to 0.090 in. and mill-annealed. The composition of the alloy was as follows: 0.02 C, 0.08 Mn, 0.10 Si, 0.009 P, 0.009 S, 18.96 Ni, 7.34 Co, 5.04 Mo, 0.29 Ti, 0.05 Al, 0.004 B, 0.01 Zr, and 0.05 Ca. Unless otherwise stated the heat treatments used were the standai-d solution treatment at 1500°F for 1 hr, air cool, followed by a 900°F, 3 hr age. In this condition, the material exhibited 232 ksi yield strength and 239 ksi tensile strength. Mechanical properties were determined by Vicker's hardness measurement (20 kg) and by tensile tests on standard 1/2-in.-wide, 2-in.-gage-length sheet tensile specimens. Notch tensile tests were run using the 1-in.-wide NASA type, edge-notched specimen.4 Fracture-toughness determinations were made on 3-in.-wide, center-notched, fatigue-cracked specimens, following the recommendations of the ASTM Committee on Fracture-Toughness Testing.4 An electric-potential technique was used for measuring the crack size at the onset of rapid crack propagation5 which is necessary for calculations of Kc, the critical stress-intensity factor under plane-stress conditions. The critical stress-intensity factor under plane-strain conditions KI, was also calculated, using the stress at which the first observable crack growth occurred. 11) RESULTS A) Cold-Worked in the Austenitic Condition. The reported M, temperature for the 18 pct Ni maraging steel is about 310°F.1 Therefore, a temperature of 650°F was selected as suitable for rolling in the austenitic condition. Specimens were solution-treated at 1500°F for 1 hr, air-cooled to 650°F, and rolled varying percentages from 0 to 60 pct, at 20 pct reduction per pass. Tensile and hardness properties after aging at 900°F for 3 hr are shown in Fig. 1. The tensile strength increases from 253 to 271 ksi and the yield strength from 247 to 265 ksi as a result of a reduc-

Jan 1, 1964

By J. L. Meijering

Oxidation hardening of cylindrical and spherical specimens first decreases with depth below the surface, but then increases again as the center is approached. This is in agreement with the view that this change in hardness is mainly determined by the change in velocity of the oxidation boundary, which affects the dispersion of the oxide. WHEN a thick slab of silver containing 0.3 pct Mg by weight is internally oxidized, the hardness measured on a cross section is found to decrease considerably with distance from the surface.&apos; This phenomenon has been attributed to the diminution of the velocity of the oxidation boundary. The smaller this velocity is, the more slowly the free-oxygen concentration rises towards the concentration in equilibrium with the oxygen gas. And a small 0 concentration favors dissociation and thus conglomeration of the oxide. For instance, the hardness decreases more rapidly during long annealings in nitrogen than in air.&apos; Measurements by Gregory and Smith3 on sections through internally oxidized Al-silver wire showed a smaller variation in hardness, probably because the wire diameter was only 0.9 mm. Wood4 found a drop in hardness with depth in internally oxidized Al-copper strip, and also—by electron microscopy—the concomitant increase in Al2O3 particle size. Under certain circumstances internal oxidation leads to formation of rather irregular inner oxide films in the midst of dispersed oxide. This special sort of conglomeration—discussed in Ref. 5—is also favored by greater depth below the surface.3,5 In this paper hardness measurements in large diameter cylindrical and spherical specimens are described. Here the oxidation velocity* goes through ness initially decreases with depth but increases again towards the center. Normally, the diffusion coefficient D1 of oxygen is very large compared to D2, that of the dissolved metal. If, furthermore, the atomic fraction c2 of the latter is much larger than the O-solubility cl- but c2D2 << c1D1- the velocities in question are easily calculated2 to be: for the cylinder and for the sphere. Here p is the radial coordinate of the oxidation boundary and R the specimen radius, which in dilute silver alloys is constant, as no external oxidation occurs. These equations have been derived for a divalent solute; for nondivalent solutes c2 has to be multiplied by half the valency. The equations are not valid near the center. For which can be considered as a standard case,2 the Eqs [I] and [2] begin to yield U-values which are appreciably too high for p/R = 0.05 and 0.15, respectively. But at the v-minima they are still very good approximations. These minima lie at p = emlR= 0.37R in the cylinder and p = 1/2 R in the sphere. Other factors besides the velocity v will also influence the hardness. The oxide concentration cox is constant in a flat strip, apart from a narrow region in the middle,2 but in cylindrical and spherical specimens cox decreases steadily with depth. When C1 << c2 and c1D1 >> c2D2 one can calculate

Jan 1, 1961

By M. J. Scoble, N. Rowlands, L. Piciacchia

Pronounced non-linear behaviour of mine backfill arises from the influence of confining pressure, cementing agent content, curing time, void ratio and water content. Past research into backfill behaviour under stress is reviewed and related to the needs for constitutive laws which can be integrated into numerical modelling for mine design where structures employ backfill support. A method for representing non-linear backfill behaviour is proposed, which is based upon numerical regression treatment of triaxial laboratory data. The non-linear behaviour observed from a program of laboratory triaxial testing of cemented hydraulic backfill is presented. The particular influence of confining stress and curing duration is high- lighted. The paper concludes by considering the alternative means of accounting for such behaviour in mine design.

Jan 1, 1984

By G. E. Tardiff, A. A. Hendrickson

THE objectives of this communication are to present the solid-solution strengthening data for silver-base zinc single crystals and to evaluate the importance of strength contributions from several mechanisms through the use of this data combined with that for the silver-base aluminum case.&apos; Some features of the yield point behavior of silver-base zinc crystals were previously reported.&apos; Silver-base zinc alloys were prepared by induction melting 99.99 pct Ag with 99.9 pct Zn in high-purity graphite crucibles contained in argon-filled quartz tubes. After the first melting, the ingots were cut into short lengths, redistributed in the molds, and remelted in order to reduce solute-concentration variations. Alloy single crystals were then grown from the melt through the use of a modified Bridgeman technique which consisted of lowering the graphite crystal mold through a hot zone at a rate of 3/8 in. per hr. As in the melting operation, the molds were contained in argon-filled quartz tubes. Gage lengths 2 cm in length were introduced by both spark machining (circular cross sections) and abrading and acid etching (rectangular cross section) followed by electropolishing (a comparison of the critical resolved shear-stress values prepared by the two techniques showed no differences in strength values). The final cross-sectional areas of the crystals were approximately 5 sq mm. Prior to testing, the crystals were annealed at 600°C for 20 hr in argon atmospheres, furnace-cooled, and lightly electropolished. Crystal orientations were determined using the back-reflection method. The tensile testing was done on a Model FM Instron at a strain rate of 1(T4 per sec. Test temperatures of 77", 200°, and 400°K were attained by immersing the specimens in liquid nitrogen, dry ice-acetone mixtures, and silicone oil, respectively. The critical resolved shear-stress (CRSS) values for silver-base zinc crystals as a function of composition and testing temperature are given in Fig. 1. It will be noted that the CRSS for silver-base zinc solid solutions, as in the silver-base aluminum1 case, depends on temperature in a manner typical of fcc solid solutions: at high temperatures (-300°K and above), the CRSS is relatively temperature-independent but becomes strongly dependent on temperature at lower testing temperatures. A reasonable picture of solid-solution strengthening for silver-rich solutions at room temperature based on "direct" strengthening mechanisms3 is as follows. Since silver alloys have low stacking-fault energies, extended dislocations are expected and it is possible that Suzuki locking4 makes the major contribution to the room-temperature solute strengthening. This provides essentially temperature-independent strengthening since thermal motions of the dislocation line are not large enough to aid the dislocation in escaping the solute atmosphere extending over the fault width. An estimate of the

Jan 1, 1964

By J. R. Low, M. B. Reynolds, L. O. Sullivan

The effect of neutron bombardment upon the stability of type 347 austenitic stainless steel has been investigated by a magnetic technique. The relation of the ferrite content of a stainless steel to its magnetic properties is given, and an apparatus suitable for the measurement of the ferromagnetic saturation induction of small specimens is described. Results of measurements on irradiated specimens are tabulated. Exposure to a neutron flux was found to cause a slight increase in the ferrite content of type 347 stainless steel, the change increasing with increasing length of exposure and with increasing initial ferrite content. The similarity of the effect of irradiation to the effect of annealing is pointed out. Possible effect of irradiation upon density of austenitic stainless steel is discussed. COMMERCIAL austenitic stainless steels are alloys of iron, chromium, and nickel, plus small quantities of other elements. Although these alloys are normally used in the austenitic condition, this state is thermodynamically metastable at ordinary temperatures and transformation to a more stable state takes place under favorable conditions. In the austenitic state, these stainless steels have the face-centered-cubic crystal structure characteristic of y iron, but the stable state at room temperature is a mixture of austenite and body-centered-cubic ferrite. The transformation from the pure austenitic condition may be brought about by cold working the alloy at a temperature below that at which the aus- tenite becomes thermodynamically unstable (about 400°C), the completeness of transformation increasing with increasing severity of cold work and decreasing temperature. The behavior of the austenitic stainless steels under ordinary conditions of use is rather well known. However, use of these alloys in a nuclear reactor introduces a new variable: the effect of neutron bombardment upon the transformation from the austenitic to the ferritic state. It was with this in mind that a study of the radiation stability of austenitic type 347 stainless steel was undertaken. Magnetic Technique for Ferrite Determination Commercial austenitic stainless steels such as type 347 undergo little transformation under normal conditions of fabrication and use. In view of this fact, it seemed likely that neutron irradiation would change the ferrite content of the alloy but little. The method chosen for measurement of the effect of neutron irradiation was thus limited to one which would be quite sensitive to small changes in the ferrite content of the alloy. Of the properties of the stainless steel which can be measured, the magnetic characteristics are most sensitive to the quantity of ferrite present.

Jan 1, 1956

By T. E. SCHTVARZ

THE publication of the report by Mr. F. L. Ransome was welcomed by many engineers who had mined in the heart of the Sail Juan country, braved its long and snowy winters, climbed its lofty peaks, run the gauntlet of its snow-slides, and studied its problems of geology, while making dividends for their English or American clients. This report helps one to understand why the bonanzas occurred, and why the inevitable borrasca presents itself where least expected. The Red Mountain district of Ouray county, a very productive section from 1884 to 1893, occupies considerable space in the report mentioned.. The character of the ore-occurrence, being distinctive and presenting many features not existing elsewhere, has been deserving of special study. It is to be regretted that Mr. Ransome was .unable to observe the conditions underground, as all the principal properties, many of which I opened and developed, were closed at the time of his investigation: It has been my privilege to have contributed a few brief papers recording my observations in developing these properties ; and it is the object of the present paper to present certain sections of the Yankee Girl mine, which throw additional light on the geology of the section and make the available data more complete. The main Yankee Girl chimney or " stock" was the most productive for the first 500 ft. in depth of any chimney in the district.

Mar 1, 1905

By G. Sandoz, D. A. Meyn

The fracture surfaces of specimens of titanium a1loys which exhibited susceptibility to subcritical crack growth in a wide variety of environments, including aqueous solutions, alcohols, hydrocarbon gases, carbm tetrachloride, and dry air, were examined. The dominant and characteristic fracture mode was cleavage. which became mixed with an increasing porportion of ductile fracture modes (dimples. and so forth) as the applied KI was increased. The cleavage plane in all the alloys was oriented at 15 deg from (0001) of the a phase. No indices could be assigned to the 15 deg cleavage Plane because of uncertainty as to which zone it belonged to. SLOW crack growth and delayed fracture take place in certain titanium alloys at stress intensity (KI) lower than the critical values for complete fracture (KIc) found in short-time tests for plane strain fracture toughness.&apos; Such crack growth may take place in very dry air on sustained loading if the alloy contains a sufficient amount of hydrogen and if the stress intensity factor is higher than a threshold value designated KIH.2 Similarly, a number of environments such as water, alcohols, and hydrocarbons may cause slow crack growth provided the stress intensity factor exceeds the threshold value KISCC. In this paper it is intended to examine some fracto-graphic and crystallographic details of this subcritical crack propagation process as related to alloy composition, environment, and stress intensity. It has been previously reported that subcritical crack growth takes place in titanium alloys in aqueous environments by cleavage.2"6 The observations to be described here indicate that in the alloys investigated the mode of subcritical crack propagation is more dependent on the stress intensity during cracking than on the environment. The fracture mode is illustrated with photographs of the fracture surfaces at a wide range of magnifications. The crystallographic character of the cleavage mode is also presented and the results discussed. EXPERIMENTAL APPROACH The studies were made on four titanium alloys— Ti-8A1-1Mo-lV, Ti-5A1-2.5Sn, Ti-7Al-1Mo-lV, and Ti-0.350. Of these four alloys the first two were mill annealed and fine grained. The latter two were noncommercial and coarse grained, having been prepared for other experimental purposes. The crystallographic studies required a large-grain size. Consequently the fine-grained alloys were an- nealed in a vacuum at 1950°F and furnace cooled to produce samples for these studies. This treatment did not alter the microstructure significantly except for grain size. All the aluminum-containing alloys showed primary a with a network of ß-phase particles within the a grains; Figs. 1 and 2 show this microstructure for the specific case of fine-grained Ti-8A1-1Mo-1V. The cracks in the figures will be discussed later. Fractographic studies were made on all the alloys, but the electron fractographs displayed herein are from the Ti-8A1-1Mo-1V alloy in the fine-grained condition. Emphasis was placed on this commercial alloy because considerable information was available on the stress-corrosion cracking characteristics in a variety of environments. Sufficient supplementary studies of the alloy after the anneal to produce large grains were conducted to establish that the stress-corrosion cracking susceptibility and fractographic characteristics were not changed significantly. Thus it could be inferred that the crystallographic data obtained exclusively on large-grained specimens would apply also to fine-grained specimens. Fracture surfaces for study were obtained using precracked cantilever beam specimens loaded as described by Brown. The precracked section of a specimen was immersed in the environment of interest. Values of initial stress intensity factor Kli were chosen slightly higher than KISCC in order to obtain a fairly extensive region of slow crack growth. Fracture surfaces representative of a variety of stress intensity levels could then be examined because in the cantilever beam test KI increases as the crack propagates.

Jan 1, 1970

By R. Silverman, H. Blumenthal

It was found that despite the similarity of chemical analyses of different titanium carbides used as base materials for cermets, the physical properties, especially transverse-rupture strengths, of test bars were different. Hence this metallographic study attempts to link physical properties to micro-structures. It is shown that microstructure, grain shape, and grain growth are functions of three interrelated factors: 1—powder production procedure, 2—surface conditioning of the particles, and 3—impurities either contained in the original powder or acquired during ball milling. An explanation is offered for the "coring effect," long observed, but heretofore of unknown origin. The explanation is based on assumption of an oxide film and on chemical analyses which substantiate these findings. TITANIUM carbide has become in recent years a material of great interest in the high temperature field. Consequently, many manufacturers in the United States and Europe are producing titanium carbide for cermet applications as well as for additions to the well known tungsten carbide tools. All present commercial processes of titanium carbide production utilize the chemical reaction of titanium dioxide and carbon to form as nearly as possible stoichiometric Tic. This reaction is carried out in three ways: 1—in a menstruum of molten metal,&apos; 2—in the solid state, either in a protective atmosphere2 or in vacuum;" or 3—in an are-melting operation. In spite of the fact that the pure carbides obtained in these operations are almost identical chemically, the physical properties vary considerably when they are combined with a binder (Ni, Co) to form cermets. This fact led the authors to examine metal-lographically nickel-bonded titanium carbide in order to find the possible reasons for this behavior. Materials and Methods Five different titanium carbides were used in this investigation. They are identified in Table I. The first four materials were used in the as-received condition. Material E, received in lumps, was crushed to —100 mesh and carried through a flotation process in order to bring its graphite content in line with the other products. A Galagher flotation cell was used with pine oil as frothing agent. The chemical analyses of the investigated materials are given in Table 11. The binder used was carbonyl nickel of 9 to 14 microns particle size, supplied by A. D. Mackay. The materials were ball milled at a ball to charge ratio of 6:1 using procedures described under "Experiments and Results." All particle sizes mentioned are averages determined with a Fisher Sub-sieve Sizer. Test bars (lx0.40x0.16 in.) were prepared by 1—hot pressing to 85 to 95 pct of theoretical density at pressures between 1 and 1½ tsi and temperatures from 1600" to 1800°C, 2-—-cold presssing after 3 pct camphor had been added, or 3—wet pressing, both 2 and 3 at pressures between 5 and 10 tsi. All pressed bars were sintered in a vacuum of 105 to 10-6 mm Hg for 2 hr at 1350 °C. Transverse-rupture strengths were determined by breaking on a Baldwin Universal Testing Machine over a 9/16 in. span. Densities were measured by water displacement. The preparation of the specimens for micrographs was done according to Silverman and Doshna Luscz." All magnifications are at X1000. A sodium picrate electrolytic etch was used. Experiments and Results The influence of ball-milling procedure, ball-milling medium, pressing procedure, and sintering procedure on the microstructure of 80/20 — TiC/Ni were investigated. Ball Milling of Materials A, B, and C in a Steel Mill: Figs. 1 and 2 show microstructures of hot-pressed and vacuum-sintered test bars of materials A and B after the respective materials had been ball milled to 2.1 microns particle size in a steel mill and mixed with 20 pct Ni binder. Material A (Fig. 1) shows considerable grain growth. Also evident is a tendency of the carbide grains to coalesce. The density is 98 pct and the low transverse-rupture strength of 111,000 psi is probably caused by many large grains and an unfavorable packing factor. Almost all grains show a slight indication of "coring." Material B (Fig. 2), although showing grain growth, still has many small particles and a better distribution of binder and carbide due to the relative absence of the coalescing tendency. "Coring" can be observed in almost all grains. The high transverse-rupture strength of 179,000 psi and the density of 100 pct are believed to be due to the many small grains completely surrounded by the binder phase. There is also a preference to form spherical grains with material A, while most grains of material B preserve their angular shapes. Material C, of which no picture is given, stays between A and B in every respect. Rounding of some grains can be observed as well as coring, but the latter to a lesser degree than with material B. Its densification is good and the transverse-rupture strength obtained is 142,000 psi. Ball Milling of Materials A, B, C, and E in a WC Mill: When the Tic powders were ball milled to 2 microns particle size in a we mill, then ball-mill mixed with 20 pct Ni binder, hot pressed, and vacuum

Jan 1, 1956

By William A. Longacre

IN a previous paper1 the author discussed the problem described by the title of this paper, outlining and reviewing the Gish-Rooney method, with comparison and brief analysis of the interpretation techniques of Roman2 and Tagg.3 Some aspects of the simple type of two-layer system were reviewed from various sources.4,5,6 THE TWO-LAYER PROBLEM For the configuration shown in Fig. I, and for any electrode separation A, the apparent resistivity is a function of the relative depth [HA], the overburden resistivity pi, and a factor K defined by the equation [ ] where p2 is the resistivity of the lower bed, Thus, by the known theory of electrical images, [ ] THE MULTILAYER PROBLEM As the number of isotropic, homogeneous, horizontal layers increases, the difficulties of interpretation multiply. The theory becomes much more involved, and in view of the state of our knowledge, the general problem is virtually impossible of exact solution. However, certain types of [ ] multilayer problems can be worked out in terms of two-layer theory. Hummel,7 Pirson,8 Tagg,3 Watson,9 and others have pointed out the possibility of building up approximations of multilayer resistivity curves with suitable combinations of two-layer curves. Many three-layer curves can be constructed in this way to a good degree of accuracy, and special types of four-layer curves can be approximated. It is very likely that as the number of layers increases, the method of combination will not give good approximations except in very special cases, In the analysis of actual field data, the author has found that many obviously multilayer curves can be solved partially with a good degree of accuracy, using the theory that thin adjacent beds may be considered as one layer or zone, and applying two-layer theory to the extremities of the field curve. MODIFIED TAGG METHOD OF INTERPRETATION Tagg&apos;s second method, though superior to his first, necessitates a large number

Jan 1, 1941

By J. T. Shapland

When externally mounted sliding-gate valves are used to control the flow of metal from ladles, none of the valve components are immersed in steel. In general, the refractories used to date in sliding-gate valves have been made of a high-alumina composition. Because these refractories replace the fireclay sleeves and clay-graphite heads used to construct conventional stopper rods, they represent a major change in the use of pouring-pit refractories, Changes in the well and lining of the ladle as a result of conversion to external flow control probably will not be as severe; however, the sliding-gate valve makes it possible to preheat to a higher temperature and to decrease the turnaround time, and materials more refractory than those currently employed, such as basic brick, might be used in these areas. Another area of pouring-pit refractories that has became quite important is the tundish used with continuous casters. The use of external flow-control devices on tundishes makes it possible to use the tundish for prolonged periods of time and makes the use of better refractories necessary. In this application, high-alumina and zirconia are finding acceptance.

Jan 1, 1972

By C. A. Heiland, Tripp R. M., Dart Wantland

This paper serves to illustrate the application of geophysics to a virtually abandoned mine properly, an application that led to the discovery of an ore body and thus afforded an Opportunity to cOmpare subsequent geologic findings with geophysical data. The work herein described represents, however: more than mere &apos;&apos;case history." It demonstrates that it is possible to obtain satisfactory results by simple means and relatively inexpericnced personnel. The geophysical surveys were made by students as a part of their field assignments in the course of their regular training, and were supervised by Dart Wantland, J. E. Hawkins and R. Maurice &apos;Tripp. In the course of several seasons an appreciable amount of material was accumulated, which gave graduate students an opportunity for special studies. In this connection, the contributions by L. Massé, R. C. Hyslop, and J. E. Hawkins deserve special mention. The property owners cooperated wholeheartedly in the work, and special thanks are due messrs. J. F. Johnson and S. E. Zelenkov, of the American Smelting and Refining Co., for their interest and for permission to utilize the results of their development work for this publication. Location and Geology The Malachite mine is situated on the northcrn slope of Bear Creek Canyon, 4 miles northeast of Evergreen, I½ miles northwest of Idledale, and 4% miles west northwest of Morrison, in Jefferson County, Colorado. The location (Fig. I) is north of the center of set. 30, T. 45, R. 70 W., at an elevation of about 7500 ft, above sea level, Near the mine the terrain slopes rather uniformly southward at an angle of about 180 pigs. 3 and 7). The geology of the Malachite mine area has been described by J, underhill,&apos; W, Lindgren,2 and J. Boyd.3,4 A map showing surface outcrops and mine workings appears in Fig, 2. the Malachite mine is in an amphibolite belt enclosed in gneisses and schists of the Idaho-Springs formation (probably early Algonkian age). The highly contorted beds are nearly vertical and strike slightly north of west. A series of granite-pegmatite dikes have been intruded almost at right angles into the gneisses and schists and doubtedless are postmineral. While most of the formations are exposed at the surface, a part of the &apos;lope is covered by slide rock and float, and in the eastern portion by alluvium and creek fill. A quartz-diorite dike cuts through the amphibolite schists at a small angle with nearly vertical dip. The copper sulphides, developed in this dike by magmatic segregation, occur in lenticular form. As far as the mine workings have revealed, the ore lenses are often discontinuous in depth and

Jan 1, 1946

By Tripp R. M., C. A. Heiland, Dart Wantland

This paper serves to illustrate the application of geophysics to a virtually abandoned mine properly, an application that led to the discovery of an ore body and thus afforded an Opportunity to cOmpare subsequent geologic findings with geophysical data. The work herein described represents, however: more than mere &apos;&apos;case history." It demonstrates that it is possible to obtain satisfactory results by simple means and relatively inexpericnced personnel. The geophysical surveys were made by students as a part of their field assignments in the course of their regular training, and were supervised by Dart Wantland, J. E. Hawkins and R. Maurice &apos;Tripp. In the course of several seasons an appreciable amount of material was accumulated, which gave graduate students an opportunity for special studies. In this connection, the contributions by L. Massé, R. C. Hyslop, and J. E. Hawkins deserve special mention. The property owners cooperated wholeheartedly in the work, and special thanks are due messrs. J. F. Johnson and S. E. Zelenkov, of the American Smelting and Refining Co., for their interest and for permission to utilize the results of their development work for this publication. Location and Geology The Malachite mine is situated on the northcrn slope of Bear Creek Canyon, 4 miles northeast of Evergreen, I½ miles northwest of Idledale, and 4% miles west northwest of Morrison, in Jefferson County, Colorado. The location (Fig. I) is north of the center of set. 30, T. 45, R. 70 W., at an elevation of about 7500 ft, above sea level, Near the mine the terrain slopes rather uniformly southward at an angle of about 180 pigs. 3 and 7). The geology of the Malachite mine area has been described by J, underhill,&apos; W, Lindgren,2 and J. Boyd.3,4 A map showing surface outcrops and mine workings appears in Fig, 2. the Malachite mine is in an amphibolite belt enclosed in gneisses and schists of the Idaho-Springs formation (probably early Algonkian age). The highly contorted beds are nearly vertical and strike slightly north of west. A series of granite-pegmatite dikes have been intruded almost at right angles into the gneisses and schists and doubtedless are postmineral. While most of the formations are exposed at the surface, a part of the &apos;lope is covered by slide rock and float, and in the eastern portion by alluvium and creek fill. A quartz-diorite dike cuts through the amphibolite schists at a small angle with nearly vertical dip. The copper sulphides, developed in this dike by magmatic segregation, occur in lenticular form. As far as the mine workings have revealed, the ore lenses are often discontinuous in depth and

Jan 1, 1946

By George L. Montgomery

In a recent article Heckler, Elias, and woods1 have described an automatic computer technique for plotting of pole figures. To anyone who has constructed pole figures manually from raw X-ray data, the development of computer plotting techniques has been a very welcome development. The purpose of the present note is to describe an alternative computer plotting method which, if somewhat less precise than the method described by Heckler et al., has the advantages of being faster and of not requiring the availability of a plotter. The plot is made directly by the printer of the terminal system and, by its nature, has a good deal of visual impact. Each character of output symbolizes a level of intensity. For example the numerals 1 to 9 might represent intensities referred to some reference obtained from a randomly oriented sample. Should more levels be required (this is seldom necessary) alphabetic or other characters may be used in addition. When these are arranged in the proper fashion, the result is a pole figure such as is shown in Fig. 1. It is the purpose of the computer program to transform the data and carry out the arrangement in a suitable manner. The computation is carried out on a line by line basis in order to reduce the amount of storage required and thus keep the program "small". It is, thereby, well within the limitations of the time-sharing systems which are becoming increasingly available. The inaccuracies introduced are slight and the plot can easily be made as precise as the technique used to collect the data. Comparison of pole figures produced by this method with those constructed manually shows a high degree of equivalence. To the present, the technique has been applied to reflected X-ray data only. X-ray data are collected in a manner identical to that described by Heckler et al. That is, as the goniometer rotates the specimen, a series of counts, accumulated over a preset time, is recorded. The method by which the proper symbol, representing an intensity level, is assigned to each print position is up to the ingenuity of the programmer. Perhaps the simplest method is to section the stereograph in the fashion of a polar net, and to assign all print positions lying within each segment a symbol representing the level of intensity recorded at the data point nearest to the center of the segment, see Fig. 2. The number and arrangement of the segments are selected to conform more or less with the number of accumulated counts and the geometry of the goniometer path used to collect them. Since the angular distance between accumulated counts is usually not infinitely controllable, it is impossible to locate one reading within each segment and, at the same time, maintain symmetry in the sectioning of the stereograph. This latter requirement is essential to keep the computer program simple and flexible. As an expedient it was found that the number of data points could be increased to conform with the number of segments, with very little loss of

Jan 1, 1969

By L. W. Holm, A. K. Csaszar

A series of laboratory experiments was conducted in which oil was displaced from a porous medium by water-driven slugs of alcohols or similar solvents. The solvents used were soluble to some degree in both oil and water and covered the range of solubilities from complete solubility in oil to complete solubility in water. Displacement experiments were conducted on 2-and 3%-in. in diameter consolidated cores and 1-and 2-in. in diameter unconsolidated sand packs. The cores and sand packs ranged in length from 1 to 30 ft, and they were saturated with brine and crude or refined oils. The solvents used included ethyl alcohol, isopropyl alcohol (IPA), tertiary butyl alcohol (TBAI, secondary butyl alcohol (SBA), n-amyl alcohol (NAA), methyl ethyl ketone, acetone and others. It was found that all of the oil present in a porous medium could be miscibly displaced by injecting a slug of mutual solvent and driving it with water. The oil-recovery efficiency was dependent upon (1) the relative solubilities of the solvent in oil and water, and (2) the distance traversed by the flood. For complete oil recovery from cores, a smaller amount of a preferentially oil-soluble solvent was required, compared to the amount of preferentially water-soluble solvent needed. The size of the solvent slug required varied inversely with the linear flooding-path length raised to the 0.65 power. Water-driven dual solvent combinations (an oil-soluble solvent slug followed by a water-soluble solvent slug) were found to effect complete oil recovery with less total solvent than any single solvent used. In these dual-solvent displacement experiments, the slug size required varied inversely with length raised to the 0.55 power. Based upon the experimental results, a theory was developed to describe the displacement of oil and water by mutual solvents, and equations are presented to predict the production history in a linear system. These equations take into account the properties of the solvents and the porous medium. INTRODUCTION Oil-recovery processes which utilize displacing fluids that are miscible with the reservoir fluids have been studied extensively in recent years. Because of the poor contact efficiency and high pressure requirements of the LPG-gas displacement process there has been considerable interest in the alcohol-water process, and a number of studies have been made on the recovery of oil through the use of solvents which are mutually soluble in oil and water. An investigation by Sievert, Dew and Conleyl indicated that the use of mutual solvents would be limited because the presence of water in a porous medium would cause a phase break in the leading edge of the displacing solvent. Their study also showed that, in consolidated cores containing. only oil, the displacement of oil by a water-driven mutual-solvent slug of tertiary butyl alcohol (TBA) was affected by the viscosity ratios of the fluids involved. Gatlin and slobod3 concluded that an isopropyl alcohol (IPA) slug acts as a miscible piston, completely displacing both oil and water until the alcohol content of the mixing zone falls below the concentration necessary to maintain miscibility. Their study was conducted on uniform unconsolidated sand packs. They concluded further that IPA could be used effectively to recover oil from a watered-out sand. In a paper by Taber, Gamath and Reed4 relating an investigation on sandstone cores, it was stated that the displacement of oil by mutual solvents, particularly IPA, was not a miscible displacement and that no improvement in efficiency could be expected with increase in flooding-path length. However, their analytical analysis of the displacement mechanism using TBA is, in fact, one which indicates that the displacement is controlled by miscible mixing. They suggested that the lack of improvement in efficiency with flooding - path

By E. Brunner, E. S. Mardock

A method of measuring oil saturations in cores or sand packs by neutron scattering is described. This method permits local SatUrations to be measured in a core enclosed in a steel pressure vessel without interrupting the flow. calibration data and a saturation distribution measurement obtained with the apparatus are included by way of illustration. Introduction In laboratory flow experiments designed to study the mechanism of oil production it is frequently necessary to measure the oil saturation in a core or sand pack containing Oil, gas, and perhaps brine. It is sometimes desirable that the saturation measurement refer to a relatively small portion of the core, so as to eliminate end effects; that it be made without interrupting the flow, and that it be applicable to a core enclosed in a steel Pressure vessel capable Of withstanding the Pressures encountered in petroleum reservoirs. None of the usual methods of measuring saturation meets all Of these requirements. To measure the gas saturation by observing the apparent compressibility of the gaseous Phase1 would require the interruption of the flow and would give an average saturation for the whole core. An electrical conductivity method is available for measuring brine saturations,2,3 but it is not applicable to oil. A radioactive tracer might be used if a suitable substance could be found that would dissolve in the oil, emit gamma radiation, and not be adsorbed on the sand, the steel core holder, or in an aqueous- phase. The large gamma-ray background from the mass of radioactive oil in other parts of the apparatus might, however, be undesirable. There remain for the saturation measurement methods involving the absorption or scattering of some penetrating radiation produced outside the apparatus. It might be possible to use X-rays or gamma rays; but these radiations would be so much less strongly absorbed and scattered by the oil than by the steel walls of the core holder and by the sand that it seems doubtful that much precision could be attained. In a beam of neutrons, however, there is a radiation that is very penetrating and, moreover, its scattering by substances containing hydrogen, such as oil, is qualitatively different from that occasioned by other materials. It would seem possible, and has proved to be quite practicable, to measure oil saturations accurately under the required conditions by means of neutron scattering. The first, to our knowledge, to suggest neutron scattering as a means of measuring oil saturation were F. Brans and ,. A. Bottema,4 of the Amsterdam laboratories of the Bataafache Petroleum Maatschappij, who made a few preliminary experiments to test the method while they were engaged in exploring the possibilities of neutrons for well-logging purposes. A comprehensive account of neutrons and their behavior will be found, together

Jan 1, 1946

By E. S. Mardock, E. Brunner

A method of measuring oil saturations in cores or sand packs by neutron scattering is described. This method permits local SatUrations to be measured in a core enclosed in a steel pressure vessel without interrupting the flow. calibration data and a saturation distribution measurement obtained with the apparatus are included by way of illustration. Introduction In laboratory flow experiments designed to study the mechanism of oil production it is frequently necessary to measure the oil saturation in a core or sand pack containing Oil, gas, and perhaps brine. It is sometimes desirable that the saturation measurement refer to a relatively small portion of the core, so as to eliminate end effects; that it be made without interrupting the flow, and that it be applicable to a core enclosed in a steel Pressure vessel capable Of withstanding the Pressures encountered in petroleum reservoirs. None of the usual methods of measuring saturation meets all Of these requirements. To measure the gas saturation by observing the apparent compressibility of the gaseous Phase1 would require the interruption of the flow and would give an average saturation for the whole core. An electrical conductivity method is available for measuring brine saturations,2,3 but it is not applicable to oil. A radioactive tracer might be used if a suitable substance could be found that would dissolve in the oil, emit gamma radiation, and not be adsorbed on the sand, the steel core holder, or in an aqueous- phase. The large gamma-ray background from the mass of radioactive oil in other parts of the apparatus might, however, be undesirable. There remain for the saturation measurement methods involving the absorption or scattering of some penetrating radiation produced outside the apparatus. It might be possible to use X-rays or gamma rays; but these radiations would be so much less strongly absorbed and scattered by the oil than by the steel walls of the core holder and by the sand that it seems doubtful that much precision could be attained. In a beam of neutrons, however, there is a radiation that is very penetrating and, moreover, its scattering by substances containing hydrogen, such as oil, is qualitatively different from that occasioned by other materials. It would seem possible, and has proved to be quite practicable, to measure oil saturations accurately under the required conditions by means of neutron scattering. The first, to our knowledge, to suggest neutron scattering as a means of measuring oil saturation were F. Brans and ,. A. Bottema,4 of the Amsterdam laboratories of the Bataafache Petroleum Maatschappij, who made a few preliminary experiments to test the method while they were engaged in exploring the possibilities of neutrons for well-logging purposes. A comprehensive account of neutrons and their behavior will be found, together

Jan 1, 1946

By R. V. Norris

THE wage rates and working conditions in the anthracite. region of Pennsylvania have been governed for nearly 20 years by the award of the Anthracite Coal Strike Commission, appointed Oct. 16, 1902, by President Roosevelt. The report of this com-mission, made in March, 1903, was accepted and, with eight modifications made at various dates, has had .almost the force of law, and has kept this great indus-trial region free from strikes for almost a generation. In 1920, President Wilson appointed an Anthracite Coal Commission, and its report, accepted Aug. 30, 1920, governed wage conditions to April 1, 1922. Actually, the agreements have been for terms of two to four years, and lately, in 1916 and 1920, the employ-ees have continued at work pending the negotiation of new agreements which were made retroactive, and which have all been modifications of the original 1903 award. With the expiration, April 1, 1922, of the 1920 award approaching, Mr. Lewis, president, of the United Mine Workers of America, addressed a letter, on Feb. 20, to the operators, suggesting a meeting on March 15; this date was accepted by the latter, with the notation that the time was short. At the meeting, the Mine Workers presented 19 demands, and advised that if a satisfactory agreement was not reached by April 1.a suspension of mining would occur, contrary to the practice since 1916 of continuing work with a retro-active adjustment.

Jan 6, 1922

By R. H. Jacoby, V. J. Berry, R. C. Koeller

The experimental phase behavior of several field gas-condensate systems, one field volatile oil system, and a series of synthetic systems having gas-oil ratios from 2,000 to 20,000 scf/bbl stock tank oil was measured. The data were used to calculate the depletion performance of the field systems at their respective reservoir temperatures and of the synthetic systems at various temperatures. The results of the performance calculations were used to prepare correlations of total stock tank oil and separator gas in-place, and the amount of each recovered by primary depletion. Data needed to use the correlations are initial gas-oil ratio, initial tank oil gravity, reservoir temperature and reservoir pressure. The correlations presented should be useful for estiinating recovery from reservoirs producing volatile oils or rich gas condensates having gas-oil ratios from about 2,000 to 30,000 scf/bbl of stock tank oil. INTRODUCTION Prediction of depletion performance for gas-condensate reservoirs usually requires extensive laboratory work or lengthy phase-behavior calculations. For many small gas-condensate bearing zones the expense of such work is often not justified. Furthermore, where large holdings are involved, it is useful to have estimates of future oil and gas production in advance of the results of a laboratory analysis, even if such work is ultimately planned. For these reasons, it would be of value to have a method for rapidly estimating the depletion performance of gas-condensate reservoirs from the type of field data usually available. Few data on the reservoir depletion performance are available for the purpose of developing correlations. The increasing number of gas-condensate discoveries and the advent of high-speed computers have stimulated the development of methods for predicting performance. Such calculated performance data have been shown to be reliable and are becoming accepted as a basis for reserve estimates and for engineering studies. It therefore seems satisfactory to use results of performance predictions themselves for the purpose of developing the desired correlations. Such an approach is described in this paper. Several rich natural gas-condensate systems (gas-oil ratios of from about 3,600 to 60,000 scf/bbl) and one natural volatile oil system were studied (2,363 scf/bbl). In addition, to provide a more systematic basis for correlating purposes, a series of related, synthetic reservoir fluid mixtures was also studied (GOR&apos;s from about 2,000 to 25,000 scf/bbl). The purpose of this paper is to show how the recovery of oil and gas by primary depletion may be estimated from surface gas-oil ratio, reservoir temperature and pressure, and tank oil gravity. procedure Experiments Companion samples of gas and oil were collected from the high pressure separators in nine different fields at the time of their discovery. These samples were each recombined in accordance with the respective producing GOR to reproduce the reservoir fluids. Eight of these fluids, designated F-2 through F-9, were rich gas-condensate systems at the respective reser-

By D. J. Dunn, J. L. Huiatt, T. E. Norman

Corrosion studies in laboratory ball mills and grinding environment simulations produce corrision rates and total metal removal rates much lower than those recorded in operating production ball mills. The corrosion component of ball metal loss in many mills probably represents less than 10% of the total loss, judging from AMAX experience and recent US Bureau of Mines (USBM) tests. Such small absolute losses are consistent with ball metal loss measured in production ball mill marked ball wear tests to determine effects of corrosion and abrasion resisting properties of alloys in operating mills. These indicate that metal hardness and microstructure determine relative metal loss rates of a given situation. The combination of ore characteristics and grinding process dynamics determine metal loss severity. Alloying for corrosion resistance and modification of the milling corrosion environment yield relatively small metal loss reductions. Alloying and heat treatment to produce high hardness and microstructures of high carbon martensite and, for cast irons M7C3 carbides, produces the lowest metal losses in typical wet grinding applications.

Jan 1, 1986

By T. J. Whalen and Michael

The grain shape of the carbide in nickel-bowled ad cobalt-bonded titanium carbides was studied by microgiaphic examination, and the influcence of sintering atmosphere, sintering substl-after, ami the amount of metal binder on the grain shape was determined. If was found that the Carbide grain cross sections in the nickel and cobalt cermets ranged from round to angular, depending on the sintering conditions. The spheroidization of the carbides in both cobalt-bonded and nickel-bonded titanium carbides may be attribicted to oxygen. In the course of studies on titanium-carbide base cermets, various investigators have reported on the shape of the carbide grains, and it was noticed that grain shapes were obtained which were either spheroids, or polygons with rounded or square edges. It was also noted that the shapes of the carbide grains changed with time or composition. skolnickl showed that the titanium-carbide grains. after infiltration in vacuum with nickel tended to spheroi- dize with time. The titanium-carbide skeleton was located on a beryllia plate during infiltration. Gur-land,&apos; who studied the microstructure of titanium carbide-cobalt compacts, showed that the carbide grains are round after 1 hr at 1450oC in a hydrogen atmosphere and angular after 7 hr at the same temperature. Goetzel3 has found that the carbide grains in compacts with a high binder content. 40 to 60 pet. tend to be spheroidized. whereas Blumenthal and silverman4 pointed out that the higher binder contents could yield either round or rectangular grains with rounded edges. depending on the nature of the binder. It is the purpose of this paper to present experi-

Jan 1, 1961