By J. Absil, H. Dreissen

Upgrading low-concentration ores is of increasing importance today. The heavy medium cyclone process, due to strong centrifugal forces, effectively separates particles varying only slightly in specific gravity but widely in size. The paper discusses separation efficiency, assessment of that efficiency, and the influence of such factors as medium solids. The operating results of nine heavy medium cyclone plants, each handling a different mineral, are reported.

Jan 1, 1982

By A. Bleier, E. D. Goddard, R. D. Kulkarni

The influence of the collector structure on the amine (RNH2, R=alkyl) flotation of quartz has been systematically investigated using a modified Hallimond microflotation cell. This study focuses on the effect of varying chain length, branching in the alkyl group R, polyfunctionality of the collector molecule, and alkyl substitution on the nitrogen atom. In addition, adsorption at the solution/air interface and electrokinetic results for the solid/solution interface were employed to further elucidate the role ad the interrelation of the structural parameters in the flotation process. Estimates of an electrical double layer attractive energy between the bubble and the solid particle are made.

Jan 1, 1976

By A. E. Nehrenberg

R. A. Schmucker, Jr.—The writer wishes to point out that an acicular growth of austenite, similar to that described in the author's paper, was recently observed in an alloy steel of only 0.06 C content. This steel, which represents an 0.07 max C, 1.35 Cr, 0.55 Ni, 0.20 Mo analysis, combines the characteristics of minimum hardness in the annealed condition with maximum hardenability and is therefore suited primarily for cold-hobbing applications. The acicular austenite formation in this steel was observed accidentally during a determination of its Ac1 temperature. The samples used in this investigation represented as-forged bar stock which had been given a preliminary temper at 1300°F. The critical (Ac1) temperature was finally established at 1400 °F. Fig. 15 represents the microstructure of the sample which had been heated at 1450°F for ½ hr, water quenched, and tempered at 600°F for ½ hr (for the purpose of darkening the martensite). It will be observed from the distribution of the darkened areas of martensite that the parent austenite grains formed at 1450°F had grown in an acicular manner and still occupied only a small percentage of the total area. The remainder of the area contains the original equiaxed ferrite grains in which new austenite had as yet scarcely formed. However, the tiny isolated martensitic patches at several points where three or more ferrite grains intersect indicate that small austenite grains had formed and started to grow in an apparently equiaxed fashion. Fig. 16 represents the prior microstructure of an original sample in the as-forged and tempered condition, before it was heated -above the critical temperature. It is probable that there are two kinds of ferrite in this structure: (1) The equiaxed proeutectoid ferrite grains which separated from the austenite when the steel was cooled from the forging temperature, and (2) the acicular ferrite associated with the aggregate of fine carbide which is represented by the patches of

Jan 1, 1951

By E. S. Bumps

A series of macrographs are presented for the purpose of graphically recording the strain phenomenon that accompanies the energy transition in the Charpy impact testing of a mild steel that is susceptible to strain aging. STRAIN patterns in mild steel Charpy impact specimens were obtained in order to determine whether, on the first appearance of plastic strain during deformation, the initial fracture cracks appear in the region of plastic strain or in the elasti-cally deformed regions between. Although this attempt to locate the initiation of cleavage was not successful, the observed strain patterns illustrating various stress conditions in partially deformed Charpy specimens are presented along with a discussion of the possible dependence of transition energy on the yield phenomenon. Earlier work on the development of strain patterns in mild steel have been reported by Fry1 and later by Jevon.2 Harris, Rinebolt, and Raring3 observed characteristic strain markings on the surface of Charpy V-notch impact specimens fractured above and below the transition temperature which they presented schematically. It is intended that the strain figures presented here will add to the literature a graphic correlation of strain with transition energy in impact specimens. Samples of % in. round hot rolled, 0.20 pct C steel were machined to standard 0.394 in. sq, V-notch Charpy impact specimens. Preliminary testing involved determination of transition temperature, Fig. 1, using a Sontagg impact tester. These data were subsequently used to select temperatures above, within, and below the transition range at which specimens were partially deformed. Partial deformation was obtained by either varying the energy or the testing temperature, see Table I. Macroscopic strain figures shown in Figs. 2 to 19 were produced by several metallographic repolish-ing and etching steps. The macroetchant used was as follows:4 120 g HCl, concentrated; 100 ml water; and 90 g cupric chloride. Strain figures were obtained on the outer surface and on sections through the central portion of the impact specimens in order to determine an approximation of the volumetric strain pattern. In the tensile strain figures reported by Jevon, it was found that strain etching would not work immediately following strain unless the material was heated to 200°C. The impact strain patterns presented here were obtained without this heating, but the specimens were not etched until ten months after straining. This confirms a discussion of Jevon's paper, in which it was pointed out that strain figures can also be developed after aging for long periods of time at room temperature. Hardness of the strained and unstrained portions, revealed by the etched pattern, was explored using R, impressions converted to R, hardness values. Discussion of Results In the impact test, as in the tensile test, some parts of the specimen yield and deform plastically, while other regions are deformed only elastically. The plastic deformation bears a relation to the imposed stress pattern. In the strain figures presented here, the plastically deformed regions are the dark etching ones. The strain figures are always symmetrical because the stress state in the Charpy-type specimen under impact loading is symmetrical. The difficulties encountered to produce initial cracks are intimated in Figs. 2 and 4. At a temperature of —75ºF, the stress was not sufficient to pro-

Jan 1, 1953

By D. J. McAdam, G. W. Geil, R. W. Mebs

AS shown in previous papers by the authors 9-l7† the resistance of a metal to fracture, like its resistance to plastic deformation, is a function of all three principal stresses.‡ A technical cohesion limit is the technically determined resistance to fracture under a specific stress system. The technical cohesive strength thus comprises an infinite number of technical cohesion limits corresponding to the infinite number of possible combinations of the principal stresses. The technical cohesive strength, therefore, may be represented by a surface in a diagram with the three principal stresses as coordinates. As shown in previous papers, 9-I8 the technical cohesive strength increases with plastic deformation, with decrease in temperature, and with increase in the strain rate. The technical cohesion limit, therefore, is affected by the same factors that affect the flow stress, § namely, the stress system, plastic deformation, temperature, and the strain rate. More- over, the influence of each of these factors on the technical cohesion limit has been shown to be qualitatively similar to the influence of the same factor on the flow stress.9-18 Advance of knowledge about the conditions determining fracture, of metals has been retarded by the reluctance of some investigators to abandon preconceived ideas about how metals "should" behave. The incorrect idea is still prevalent that the conditions determining resistance to fracture are very different from those determining the flow stress. Attempts are still being made to express resistance to fracture in terms of a single parameter, such as a limiting value of the greatest principal stress, the maximum shearing stress, or the volume stress (one-third the algebraic sum of the three principal stresses). In these attempts, a sharp distinction is sometimes made between a ductile or "plastic fracture " and a "brittle fracture." In making this distinction, however, the meaning attached to the term "brittle fracture" sometimes is not made clear. The term could mean fracture after very little plastic deformation or it could be used to designate the type of fracture. An ordinary fracture of a ductile metal at room temperature starts as a cleavage, generally transverse to the direction of the greatest principal stress, but eventually changes to a shearing fracture. In some conditions, however, the metal fractures entirely by cleavage, with no evidence of plastic deformation during the fracture; the surface of such a fracture may have a

Jan 1, 1947

By R. W. Raymond

At the Liége meeting of the Iron and Steel Institute of Great Britain, in August, 1873, and also at the Vienna Convention of Mining and Metallurgical Engineers, at the end of August, and at the convention of German geologists, at Wiesbaden, in the first part

By W. J. Slatosky

As a means of effecting better control of endpoint temperatirres at the Jones & Laughlin basic oxygen furnace plant, a set of mathematical equations has been developed. The eqlutions are the product of a themlochemical anaysis of the process and aye designed to calculate the required scrap, lime, and hot metal additions in terms of a number of independent variables. Results of test heats have warranted adoption of this technique by the Prodrrction Department. BECAUSE of the autogeneous nature of the basic oxygen steel-making process, bath temperature can be controlled without an external fuel supply by charging the furnace with additions that are thermally balanced. The thermal requirements of the charge materials are such that, during the refining process, they throttle the heat generated by the metallurgical reactions in a manner designed to result in a speci-fied temperature at the completion of the heat. In the past, operating personnel at the basic oxygen furnace plant of Jones & Laughlin's Aliquippa Works relied on their experience and technical knowledge of the process to determine the quantities of charge additions needed to result in a finishing temperature in the range 2880"to 2920" F. (The charge consists primarily of 93 tons of scrap and hot metal plus an amount of lime sufficient to maintain a basicity ratio of 2.8 to 3.2). Estimates of these materials are based on a consideration of the effects on finishing temperature of 1) iron silicon content, having a variation of 0.8 to 1.8 pct; 2) iron temperature, ranging from 2250°to 2600°F; and 3)any excessive cooling of the furnace due to a production delay. The end temperature of the preceding heat also serves as a guide in that, if a heat was within the specified temperature range, the succeeding heat could be charged with materials of nearly the same proportions, provided the hot metal used in each of the two charges was of approximately the same temperature and composition. On the other hand, if a heat was outside the specified tapping range, or if the hot metal used in that heat was of different analysis and temperature from that of the iron to be charged, an adjustment in the proportion of additions is in order for the following heat. Due to the complex thermochemical behavior of the process and to the inexact and subjective nature of the described method of determining charge additions, consistently accurate temperature control was not to be expected. Therefore, those heats out- side the specified tapping range necessitated subsequent adjustments by either reblowing the cold heats for a suitable length of time so as to elevate the bath temperature to the desired level, or cooling hot heats with a proper amount of scrap. Because extra time is required to make these adjustments, production is delayed. In an attempt to devise a method for improving temperature control, an analysis of the thermochemistry of the process was undertaken. This, in turn, led to the development of a set of mathematical equations which enable the calculation of the quantities of scrap, lime, and hot metal needed to result in any specified tapping temperature range. The analysis was not intended to be a repetition of work done by others such as McMulkinl or ~hilbrook.' It was meant to be an extension of their work so that charge additions could be calculated not in terms of silicon alone but, rather, as a function of all independent variables. This paper presents the derivation of these relationships, their effectiveness in controlling bath temperatures, and a method of utilizing them on an operational basis. The Heat Balance—The first step undertaken in the analysis of the problem was the enumeration of the pertinent variables. A list is presented in Table I where it is noticed that these quantities have been separated into the following three categories: important variables, variables considered as constants, and variables to be neglected. The breakdown was an arbitrary one designed to facilitate the analysis; otherwise, the mathematical treatment would have been exceedingly cumbersome and complex. Fortunately, experience has shown that these simplifying assumptions do not seriously impair the accuracy of the calculations. These variables along with the limiting assumptions listed in Table n were then used to write a heat balance of the process by applying the equation of continuity, Rate of Rate of Rate of Increase = Income - Outgo PI ] of Heat of Heat of Heat.

Jan 1, 1962

The following list contains the names of members whose death notices have been printed in MINING AND METALLURGY from March 15, 1947 through March 15, 1948 Biographical sketches published in MINING AND METALLURGY are indicated in the last two columns Year of Election - Name - Date of Death - Issue Containing Biography - Page 1938 ABERNATHY, G E , (M) Feb 6, 1948 April 1948 266 1935 ARCHER, M T, (M) Oct 26, 1947 Dec 1947 633 1947 ATIKINSON, JAMES E, (S) Feb 6, 1948 June 1947 309 1940 AYRES, VINCENT L, (M) Oct 14, 1947 Jan 1948 59 1915 BABCOCK, JAMES E , (M) April 1, 1947 June 1947 309 1942 BAGGALEY, WILLIAM BLAIR, (A) Aug 28, 1947 Jan 1948 59 1897 BUIN, II POSTER, (M) Mar 9, 1948 April 1948 219 1945 BAMPFIELD, A E (M) Unknown Mar 1948 215

Jan 1, 1952

By N. J. Grant, F. B. Cuff

DURING a recent investigation of high-purity aluminum,' evidence was found for grain-boundary sliding and migration at room temperature. The investigation was concerned primarily with an electron-microscopic study of a fine (approximately 1 micron) network that appeared on the surface of chemically polished aluminum. The nature of the network will not be discussed since it serves only as markers showing relative displacements in this instance. The pertinent observation, shown in Fig. 1, was made on a flat tensile specimen which had been strained about 8 pct at room temperature. As can be seen in this electron micrograph, a grain boundary has undergone a certain amount of sliding. The reason for the existence of the two differently appearing networks is given in the foregoing reference. For present purposes, however, the transition region can be disregarded. A close study of this picture reveals that in addi- tion to sliding there is a narrow band adjacent to and above the grain boundary. Fig. 2 is a schematic drawing showing the essential features of this band.

Jan 1, 1959

By Cheri Eby, William R. Eby

This paper describes the state-of-the-art of pneumatic transport systems that are capable of conveyinq waste cuttings generated by raise drills during shaft construction projects. Additionaly other examples of applications pertaining to pneumatic transport systems qualified to convey abrasive and nonabrasive materials (&., gravel, shale, coal, ore, and limestone) will be presented.

Jan 1, 1982

By Bjorn Bolviken

Bjorn Bolviken (Geochemist, Geological Survey of Norway, Trondheim, Norway)-Under the heading "Recognition of Anomalies," the author states, "If the frequency distribution is actually log-normal, the probability of these high values being part of the background population is small (less than 0.023 and 0.0013 for 2 and 3 standard deviation, respectively)." The figures quoted seem to be the probabilities of these high values being the mean rather than part of the background population unless "background" is defined as one single concentration. If the background is considered to be a statistical distribution of concentrations,50 (which is probably the case here since the author uses the term "background population"), the probability of any observed value being part of the background may be estimated through a calculation of the number of observed values that are in excess of (or below) the number expected to belong to the background. Apparently, some confusion exists in the literature regarding this point. Many authors accept the concept of background as being a statistical distribution, but do not seem to recognize the consequences of this concept. One of these consequences would be that the background of a chemical element should comprise any concentration between zero and a theoretical maximum, which is governed by the chemistry and mineralogy of the material

Jan 1, 1974

By R. F. Nielsen, D. E. Menzie

The object of this study was to determine if crude oil could be produced successfully by a process of crude oil vaporization using carbon dioxide repressuring. This process appears to have application to highly fractured formations where the major oil content of the reservoir is contained in the non-fractured porosity with little associated permeability. Crude oil was introduced into the windowed cell and carbon dioxide was charged to the cell at the desired pressure. A vapor space was formed above the oil, and the crude oil-carbon dioxide mixture was allowed to come to equilibrium. The vapor phase was removed and the vaporized oil collected as condensate. Samples of all produced and unproduced fluids were analyzed. Tests were also performed to evaluate the amount of vaporized oil that can he produced by rocking from a high to a lower pressure. The carbon dioxide repressuring process was applied to a sand-filled cell to investigate the performance in a porous medium. A test was performed to evaluate how the condensate recovery changes as the size of the gas cap in contact with the oil changes. INTRODUCTION This study has been directed toward a relatively new process of vaporization of crude oil designed to increase ultimate production of hydrocarbons through the application of carbon dioxide to an oil reservoir. Suggested advantages of carbon dioxide repressuring of a petroleum reservoir are: (1) reduction in viscosity of liquid hydrocarbons due to the solubility of carbon dioxide in crude oil, (2) swelling of the reservoir oil into a larger liquid-oil volume with a resulting increase in production and decrease in residual oil saturation due to an increase in the relative permeability to oil, (3) displacement of more stock-tank oil from the reservoir since the residual liquid is a swelled crude oil, and (4) gasification of some of the hydrocarbons into a carbon dioxide-hydrocarbon vapor mixture. Balanced against these advantages are several detrimental factors which must be evaluated; i.e., high compression costs and corrosion of well equipment and flow lines. Some of the more outstanding contributions to the study of carbon dioxide injection have been reviewed in order to furnish a basis for a continuation of research pertaining to this method. The literature reviewed1-8 has been limited to that dealing with carbon dioxide repressuring processes or with carbon dioxide-crude oil-natural gas phase behavior. Articles relating to carbonated water injection and literature published on the use of low pressure carbon dioxide gas injection in water flooding have not been included in this study. In 1941 Pirson5 suggested the high pressure injection of carbon dioxide into a partially depleted reservoir for the purpose of causing the reservoir oil to vaporize and thus produce the oil as a vapor along with the carbon dioxide gas. By reducing the pressure on this produced mixture of hydrocarbons and carbon dioxide at the surface, it was proposed to separate the hydrocarbons from the carrier gas. He theorized that essentially all the oil in a reservoir could be produced by simply injecting enough carbon dioxide to vaporize the residual oil. This present investigation deals with the vaporization of a crude oil by carbon dioxide, the molecular weight and gravity of the vaporized oil product and the characteristics of the residual oil after several repressuring cycles with carbon dioxide. An attempt is made to evaluate the merits of a vaporization process for the crude oil rather than a flow process where the oil recovery is determined by relative permeability considerations. Such a vaporization of crude oil by carbon dioxide repressuring appears to have possible use in a highly fractured formation where the major oil content of the reservoir is contained in the non-fractured porosity with little permeability. The carbon dioxide flows into the fractures, contacts the crude oil in the matrix and vaporizes part of the crude oil; this vaporized oil is produced and recovered and the carbon dioxide is reinjected again. The specific problem of this study is to attempt to answer this question; Can crude oil be produced successfully (technically, but without economic considerations) from a petroleum reservoir by a process of vaporization of the crude oil by carbon dioxide repressuring? DEFINITION OF TERMS AS APPLIED IN THIS STUDY Carbon Dioxide Contact: One cycle in which carbon dioxide was injected and bled off. Condensate: The hydrocarbon liquid which was condensed out of the mixture of hydrocarbon-carbon dioxide vapor upon reduction of the pressure of the vapor. Hydrocarbons Produced (HCP): All the hydrocarbon!, which were vaporized by the carbon dioxide repressuring process and were removed from the cell during any specific cycle or carbon dioxide contact. Hydrocarbons Unproduced (HCU): All the hydrocarbons which were not vaporized by the carbon dioxide

By Walter Lawson

THE first plans were made in 1930 for the mining by open-pit methods of the low-grade disseminated ore body now known as the Morenci open pit. It was not until 1937, however, that final plans were completed and the decision reached to go ahead with the actual development. Many advances were made in open-pit mining equipment during that period of seven years, therefore the ways and means of attack actually used were very different from those originally contemplated. Diesel-operated bulldozers, big trucks, full-revolving electric shovels and electric churn drills constitute the major equipment finally purchased for this modern stripping operation. Neither the bulldozers nor the big trucks were considered in the early operating plans, for at that time bulldozers had not, been used in mining operations and the trucks as yet were undesigned. The full-revolving shovel and the churn drills were not new developments in open-pit equipment, but both had undergone remarkable manufacturing transition, emerging far more efficient and far more dependable than their predecessors. Even the ordinary drilling steel had been fundamentally changed. It was now threaded so that the dulled cutting bits could be detached and replaced, thus eliminating the costly transportation of long bars to the drill shop for resharpening. The decision to use trucks in the preliminary stripping operations was based on the desirability of this type of transportation to economi-cally prepare the pit for rail haulage, coupled with the success that the contractors had had with them on other big excavation jobs. There are at present no plans for the use of trucks beyond the preliminary work, inasmuch as rail haulage will give lower costs after roadbeds and benches are once established.

Jan 1, 1938

By H. Conrad, K. Janowski, E. Stofel

In a previous paper,1 the occurrence of (0001) and (0111) twins was reported for compression tests of 60-deg-oriented sapphire rods in the temperature range from 1100° to 1300° C. Subsequent to this initial work, additional tests have been conducted, and twinning has been found to occur at temperatures as high as 1500° C. Also, the temperature and strain-rate conditions for the two types of twins and for slip have been established in more detail. The present note covers this more recent work. The compression-test data are summarized in Table I. The techniques for identifying the twins are optical examination up to X1000 and X-ray analysis.' It is evident that (0711) twins are pre-

Jan 1, 1965

By L. P. Teas

The year 1931 has been one of unusual interest in Gulf Coast petroleum development, not so much because of the number of new prospects discovered, for apparently none of any present distinction have been found, but because of the discovery of so many new oil fields and the proving of so many old prospects. During the year 10 new oil fields have been found on the Coast; five in Louisiana and five in Texas. Two suspected salt domes were proven by the drill. Production dropped from a daily average of 192,000 to 162,670 bbl., or an average of 58 bbl. for each producing well, and active operations from 189 to 119. During 1931 the Coast produced approximately 48,600,000 bbl., or 44 per cent less than in 1930, when 86,500,000 bbl. were produced. The daily return at the beginning of the year was $192,000 and at the end only $126,780, the price having dropped from $1 for A grade and a range of $0.75 to $1.22 for B grade to a price range of 70 to 86c, or an average of 78c $ per barrel at the end of 1931. The average Coastal well produced 17,400 bbl. of oil during 1931. During the year development in the old fields has continued active at Barber's Hill only, although some work is in progress at Humble, Pierce Junction, Refugio and Pettus. Clear Lake is active but the large ownerships will prevent the "boom" type of field. Production is being held fairly steady at Barber's Hill and Pierce Junction, but has declined rapidly during the year at Refugio, Humble, and to a lesser degree at Pettus. The 6000-ft. production at Barber's Hill has shown a decided drop during the year and has not measured up to expectations.

Jan 1, 1932

By C. F. Rust

Experimental evidence is presented showing that reproducible formation resistivity factor measurements and resistivity index determinations on reservoir core samples map be made utilizing either the two- or four-electrode methods. Equipment is described which permits the application of either technique to the core specimen without loss of time and with a minimum amount of effort. Since electrical resistivity measurements on reservoir rocks are important not only in electric log interpretations, but also in the study of fundamental rock parameters, it was considered desirable to compare the applicability of both techniques of resistivity measurement. INTRODUCTION The techniques employed in the measurement of electrical resistivity on reservoir rocks, as practiced in the petroleum industry, may be reduced to two fundamental methods: one utilizing two electrodes only, usually referred to as the two-electrode method; the other using two additional electrodes and commonly known as the four-electrode method. In the former, the core sample whose resistivity is to be measured is mounted between two electrodes, usually metal discs, which serve to pass a current of known magnitude through the saniple. The potential drop across the sample, measured between these same two electrodes, and the core dimensions furnish the necessary data to compute he resistivity of the sample. In the four-electrode technique the end plates, again usually ol metal, still serve as current electrodes. Additional probes or electrodes dispersed along the sample are utilized to measure the potential drop. Both methods are used in practice1,2 and it is the purpose of this paper to compare the two techniques as applied to the determination of formation reiistivity factors and the resistivity index exponent n, in Archie's empirical equation I = p/po = Sw 11. To evaluate the two techniques it is desirable to point out the experimental precautions which must be taken to insure reliable results. It is evident from the electrode arrangements of the two- and the four-electrode methods that, for a given sample, the volume of sample included by the four-electrode method is less than the volume included by the two-electrode method. One of the prime difficulties associated with the two-electrode method is the possible occurrence of an abnormally high resistance between the electrodes and the brine-saturated sample, which results in erroneous resistivity values for the core sample itself. Attempts to alleviate this difficulty meet varying degrees of success. Methods used in the past employ such absorbent materials as brine-saturated Kleenex: chamois, or felt. A technique described by Morgan, Wyllie, and Fulton,1 appears to be more satisfactory. Their method consists of spraying or painting the end areas of a core sample with conductive silver paint. This technique reduces contact resistances between the porous medium and the electrodes to a value which is generally negligible as compared to the resistance of the sample itself. In the four-electrode method these requirements are not as stringent since separate probes are used to measure the potential difference acrozs a portion of the sample. In this case, contact resistance occurring at the current electrode; are of no consequence. and those appearing at the potential

Jan 1, 1952

By Alexander R. Troiano, Taylor Lyman

Studies of the transformation of aus-tenite at constant subcritical temperatures have been numerous since the work of Davenport and Rain.' Considerable information has been obtained on low-alloy steels and on high-carbon alloys containing undissolved carbide or graphite at the austenitizing temperature. Little is known of the isothermal transformation of aus-tenite containing in solution large amounts of both carbon and a single alloying element. In this investigation four steels containing one per cent carbon and with chromium in the range 3 to 9 per cent have been examined with the view to establishing the fundamental character of the isothermal reactions when all carbon and chromium are initially in solution in austenite. Experimental Procedure Alloys The chemical compositions of the steels investigated are given in Table I. The 4 per cent Cr alloy is a commercial steel. The other steels were made by the Carpenter Steel Co. as 50-lb., induction-furnace heats and rolled to 5/8 -in. round bars. Bars were softened at 650' to 700°C. before the specimens were cut. Most of the lines on the transformation diagrams presented here have been placed on the basis of the microscopic examinatioll of partially reacted specimens, Thees specimens were approximately 1/2 by 1/4 by 1/8 in. ill size, specimens of the 9 per cent cr steel were held 10 to 12 hr, at 1200°to 1225°C. before quenching to the various subcritical temperatures. The other steels were held for 2 to 2 1/2 hr. at 12ooOC. before quenching. These treatments, carried out in an atmosphere of purified nitrogen, produced an austenite grain size larger than A.S.T.M. So. I, some grains being 1 to 2 mm. in diameter. There were a few undissolved carbide particles in some specimens of the 9 per cent Cr steel. It is believed, however, that any errors in the results due to incomplete solution of carbon and chromium in austenite are negligible; that is, austenite compositions may be considered as being those listed ill Table I. X-ray Methods Constituents were identified and mar-tensite axial ratios determined from Debye

Jan 1, 1945

By Malcolm J. McPherson

INTRODUCTION The use of computers to assist the mine ventilation engineer began to grow in the early 1950s when electrical analogue devices were developed for the analysis of mine airflow systems in Europe and the United States (l,2,3). The need for quantitative planning of airflows in mines had become pressing and analogue computers fulfilled a useful purpose for over a decade. From about 1964 onwards, digital computer programs for mine ventilation network analysis became available (4,5) and, superseding the analogues, spread rapidly throughout the major mining countries. The successful implementations of such programs resulted in further research being directed towards the development of simulation programs to model the quality as well as the quantity of air flowing through underground workings. It is no understatement that digital computers have revolutionised environmental planning techniques in modern mining industries. This paper discusses the complex interaction of natural and mining factors which governs environmental hazards in underground mines and further indicates some of the simulation techniques which have entered practical usage or are at an advanced stage of development. THE PROBLEM OF ANALYSING THE MINE ENVIRONMENT The traditional methods of approaching environmental problems underground were based largely on empirical or intuitive techniques. The reason for this lay in the intricate relationships which exist between the many variables that influence the mine environment - and which limit the use of purely analytical methods to the simplest of cases. In order to illustrate the need for simulation techniques, Table 1 shows the three most widespread mine environmental hazards

Jan 1, 1977

By R. W. Armstrong, P. C. Jindal

The hardness dependence on grain size for polycrys-talline cartridge brass and a leaded brass has been measured by Brine11 and Rockwell B testing. In each case, the hardness, H, depends on the average grain diameter, 1, according to: H =Ho + kHl-1/2 where Ho and kH are experimental constants. Diamond pyramid hardness values have also been measured as a function of the indentation size and grain size to give additional information on the nature of the hardness test and the dependence of hardness on micro-structure. The hardness of polycrystalline brass depends on its grain size. Bassett and Davis' demonstrated this as early as 1919 by making Brinell hardness measurements on cartridge brass. Since then, the hardness of this type of material has been measured as a function of grain size by making Rockwell,2'3 Vickers,4 and Brinell5 tests. he hardness dependence on grain size has also been measured for other materials. Angus and summers6 investigated the grain size dependence of the Brinell hardness of polycrystalline copper and a Cu-4.5 pct Sn bronze. In other studies, nickel,? Armco iron,Big an Fe-0.07 pct C alloy,I0 and an 0.39 pct C-12.45 pct Cr stainless steel" have been investigated. In some of the preceding cases, the hardness results have been analyzed to show that the hardness varies with the average grain diameter, 1, according to an l-l\4, l-1/4 or I-2 dependence,11-13 The studies of the influence of grain size on hardness have not been based on any theoretical model. This may be because the hardness of a material is itself a complicated property. However, attempts have been made to correlate, experimentally and theoretically, the hardness of a material with its unidirectional stress-strain behavior.14-l6 On this basis, Hall" proposed that the polycrystal hardness dependence on grain size might follow directly from the Hall-Petch18,19 relation for the grain size dependence of the yield stress. Thus, the hardness-grain size relation was given as: H = Ho + kHl-1/2 [1] where Ho and kH were taken as experimental constants. The relation was applied to the measurements on brass,' copper,6 bronze,= and Armco iron.' More recently, this relation was shown by Armstrong and jindal20 to adequately describe the measurements on cartridge brass made by Bassett and Davis' and Babyak and Rhines.5 In this case, the relationship was taken a step further by independently relating the values of Ho and kH to the values of oyand ky, previously reported by Armstrong, Codd, Douthwaite, and petch21 from measurements of the yield stress dependence on grain size for this type of material. In the present investigation, new Brinell and Rockwell B hardness measurements have been made as a function of grain size for a cartridge brass and a leaded brass. In addition, diamond pyramid hardness values were measured as a function of the indentation size. All these results are applied to a further analysis of the hardness dependence on grain size. MATERIALS AND EXPERIMENTAL METHODS Cartridge brass and a leaded brass were selected for this investigation for two main reasons: it was anticipated 1) that these materials could be cold-worked and recrystallized to a wide range in grain size and 2) that the results to be obtained on these typical industrial materials could be usefully compared with previous investigations. The chemical analyses of the actual materials which were employed are given in Table I. The as-received 1/2- and 3/4-in.-thick plates were given various reductions in thickness by cold rolling. The rolled material was heat-treated at various temperatures between 330" and 850°C for differing time periods from 5 min to 9 hr to achieve a variation in the average grain diameter between 0.0339 and 0.000543 cm.22 During heat treatment, the brass was protected from zinc loss by packing it in chips or foils of the same composition material. Reasonably equi-axed grain structures were obtained in each case. The metallurgical grain sizes of the specimens were determined from measurements of the average linear intercept on a random line. Annealing twin interfaces were not counted along with grain boundaries. The

Jan 1, 1970

By W. F. Domis, F. von Gemmingen, F. Garofalo

The effect of rain size on the creep behavior of an austenitic iron-base alloy has been studied at 1300° F under conditions of constant stress. The average grain diameter varied between 9 and 190 p (ASTM 10.7-2). The subgrain size and apparent activation energy for creep were not found to depend in any systematic manner on gain size. Grain hozmdary serrations were observed in all specimens tested. The variation of the secondary-creep rate, 2,, with the pain diameter, 1, is given by: es = K(213m + 1 )/l.]; 1, is the grain diameter zohere is reaches a minimum. Results in the literature shoujthat 1,increases as the temperature increases. At low creep temperatures is is therefore proportional to 12, at intermediate temperatures <, exhibits a minimum, and at high creep temperatures is is proportional to 1/1. The dependence ofis on the stress, u, is given by: t, = A" (sinh acrln, a and n show little variation with 1. The dependence of A" on 1 is given by: A" = KA[(21k + 13)/1]. For 1 » >>lmn = 4, and at constant values 01- isat lozu stress levels, the steady-state stress is given by the Hall-Petch relation. The variation of c, with grain size is believed to he associated particularly with grain boundary generation of dislocations which becomes more important with increasing temperatures. SEEMINGLY inconsistent experimental findings have led to a certain amount of confusion concerning the effect of grain size on creep behavior. The confusion is attributed to a lack of test results obtained over sufficiently wide ranges in grain size, stress, and temperature. Experimental results presented in this paper and results available in the literature1-5 show a consistent behavior and lead to a unified concept for the dependence of secondary-or steady-state creep rate on grain size. In accordance with this concept, which is substantiated experimentally, secondary-creep rate should increase with increasing grain diameter at low creep temperatures, leading to greater creep strengths for fine-grained materials. At intermediate temperatures the secondary-creep rate should decrease to a minimum and then increase as the grain size is increased. At high creep temperatures the secondary-creep rate should decrease with increasing grain size, leading to greater creep strengths for coarse-grained materials. Whether a temperature is high or low for creep in a metal or alloy depends primarily on its melting temperature. MATERIAL AND TEST PROCEDURES The material tested was an austenitic iron-base alloy of the following composition (wt pct): C, 0.005; N, 0.017; Mn, 1.26; Ni, 14.21; and Cr, 17.18. Two 15 -lb ingots were forged and hot-rolled to 5/8-in.-diam bars which were then cold-rolled and cold-swaged to a diameter of 0.49 in. These were sectioned into 3-in.-long blanks and heat-treated at various temperatures to obtain different grain sizes. The procedures employed and the results obtained are summarized in Table I. The secondary treatment at 1400° F followed the primary treatment without intermediate cooling to room temperature. This final treatment was employed to minimize various effects arising from heating to different temperatures during the primary treatment, particularly differences in intragranular dislocation structure, segregation of interstitial atoms at grain boundaries, and density of grain boundary ledges. The intragranular dislocation structure was examined by electron transmission metallography after each of the treatments described in Table I. Isolated dislocations and a few tangles were observed but no evidence of subgrains was found after any of the treatments. No grain-size effect was evident on the density and distribution of dislocations. Stabilization of grain boundary structure is particularly important because, as will be discussed later, grain boundaries influence high-temperature creep behavior. Magnetic-permeability measurements after each treatment and

Jan 1, 1964