By Leon McCulloch

WIIen clean iron and metallic zinc dust, protected from the air, arc heated below the melting point of zinc, the iron takes on a coating that has excellent protective value. This coating is a brittle alloy of zinc and iron, and the process is called sherardizing. Although the zinc particlcs are covered with oxide and cannot touch the iron, an extremcly small amount of the zinc vaporizes and the vapor, reaching the iron, alloys with it. Other zinc then vaporizes to replace that which has been removed from the atmosphere. This process continues indefinitely at a decreasing rate, for the coating already formed permits zinc to diffuse through it to combine with the iron beneath. In this way, the coating grows outward from the surface of the iron, as the bark grows from a tree. The method of growth was clcarly seen while sherardizing small cubes of cast iron, at about 450" C., in a srnall glass-stoppcrcd bottle enclosed in a rotating drum. The dust contained about 3 per cent. iron, which prevented caking, and coatings % in. thick were grown in a few hours. After a heavy layer had been formed, the cubes mere again treated for a shorter time. The layer last formed was seen to lie next to the iron, instead of at the outer surface, showing that the growth was from the surface of the iron outward. The coatings split at the edges and corners, leaving the iron exposed there. Flakes of graphite from the iron were lifted upward and embedded in the coatings. The composition of sherardized coatings varies from the outer surface inward, as would be expected from the mode of growth. That is, the iron content increases slowly at first, then more rapidly as the iron is approached. At the surface the least amount of iron possible is 6 per cent., as the experiments described below have shown. A study was made of the effect of iron in zinc dust on the proccss and on the resulting coatings. Glass bulbs, holding the small pieces to be sherardized, together with enough zinc dust to make them two-thirds full, were heated in a small, rotating electrically heated and controlled furnacc. The bulbs had 6-in. (15 cm.) necks, of 96-in. (9.Fj mm.) tubing, plugged

Jan 1, 1923

By J. E. Tobey

BECAUSE of the wide-spread publicity given to Nylon yarn as being made from ?coal, air, and water,? the general public has become conscious of the nonfuel uses of bituminous coal. Some of these uses are as filler for fertilizer, carbon for the absorption of orders, for water supply, and for the bedding of cattle. Spectacular as are these accomplishments the fact is that only a small amount of coal is used for nonfuel purposes. It is on the utilization of coal as fuel that the industry depends. Practically all the coal mines for years to come will be used for making coke for the generation of heat. Recently much attention has been paid to the significance of ash in coal. Another study worthy the interest of metallurgists in the iron and steel industries if that of Dr, Lowry of the Carnegie Institute of Technology relative to the percentage of sulphur in coal and coke.

Jan 1, 1941

By J. R. Cahoon, W. V. Youdelis

In a previous communication by one of us,1 a theory of inverse segregation was presented by which the maximum segregation and segregation distribution throughout a unidirectionally solidified, binary-alloy ingot could be calculated. The theory, which is based on the mechanism of volume contraction and interdendritic flow, quantitatively accounts for the observed maximum segregation in the A1 (rich)-CU' and Al-Zn2 alloy systems, and for the segregation distribution along the ingot lengths for the A1-Cu system.''4 One of the drawbacks to a more extensive use of the segregation equations is their complexity, particularly for the calculation of the segregation distribution throughout the length of the ingot, involving long tedious numerical calculations to obtain the segregation. Computer pro- grams, written in Fortran II for use on an IBM 1620 computer, have been developed by the authors (and are available from them), providing quick and accurate methods for the determination of the theoretical maximum segregation in any binary-alloy system, and also for the segregation distribution in any unidirectionally solidified binary-alloy ingot. The segregation distribution is controlled by the lengths of the various solidification zones'74 which are in turn controlled by the cooling rate, and are determined from temperature-distribution curves obtained during solidification. The theoretical segregation distributions shown in Fig. 1 illustrate the effect of the zone lengths on the distribution Curve 1, indicative of a slowly cooled ingot, represents an ingot having long solidification zones, while Curve 2, indicative of a rapidly cooled ingot, represents an ingot having relatively short zones. Although these distributions are calculated for an A1-10 pct Cu ingot, the shape of the distribution would be similar for any binary-alloy ingot. These curves show clearly why early workers obtained results which indicated that the maximum (chill-face) segregation approached zero at very fast cooling rates.3 Actually, the maximum segregation is independent of cooling rate,' but even at short distances from the chill face the amount of segregation drops considerably, particularly in a rapidly cooled ingot, making it very difficult to establish the amount of segregation occurring at the chill-face. The authors would like to thank Dr. J. A. Goldak for his assistance in the preparation of the programs. The financial assistance of the Steel Co. of Canada and of the National Research Council of Canada in the form of Scholarships to one of us (J. R. Cahoon) is gratefully acknowledged.

Jan 1, 1964

By C. T. Van Winkle

MINE fires are always dangerous and are frequently accompanied by loss of life during the period of confusion which is apt to follow their discovery. In metal mines, fires may result from the accidental ignition of some combustible material, or they may be of spontaneous origin resulting from the rapid decomposition of sulphide. They occur frequently enough to demonstrate the need of some special equipment and a general plan for controlling them, in addition to measures for their prevention. Nearly all the large copper mines have had fires, and the methods of fighting them have been well described in recent papers, notably-by C. L. Berrien,1 R.. E. Tally,2 and others in discussion. The Copper Queen mine has many shafts, which are connected by underground workings. The deeper parts are ventilated by fans, but in the shallower portions natural ventilation through numerous connecting raises or shafts is sufficient. There have been several fires in the past few years, of which all are extinguished but one, and that is under control. These notes cover particularly the preparations that are being made-to check a new fire, partially or temporarily, and to facilitate the escape of workmen in the interval before a definite plan of fighting it can be established. A fire may occur in a shaft or station, or in some working father away. In case of fire in an upcast shaft, the gas would escape to the surface and the immediate result would probably not be dangerous to workmen, as they could escape by other shafts. In a downcast shaft, however, the gas would be distributed very rapidly throughout a large portion of the mine, and men might easily be trapped and asphyxiated. A fire in mine workings, drift, raise, or stope, would be dangerous in a degree, but the draft there is likely to be less strong than in a shaft and probably a smaller area would be invaded by the fire gases.

Jan 1, 1918

The American Institute of Mining Engineers, the second of the four great national engineering societies established in the United States, was organized in 15,71. Its membership is composed of men engaged in the different branches of mining, metallurgy, geology, and chemistry. It includes both those who have worked their way up from the ranks and graduates from mining schools and universities, and at all times has counted in its membership leading technical educators. By a letter ballot of the members of the Institute, it was voted, at the annual business meeting of the Institute on February 18, 1919, to change the name of the American Institute of Mining Engineers to the American Institute of Mining and Metallurgical Engineers. The vote for the amendment to the Constitution making this change was a heavy one for such matters. It is the consensus of opinion that this marks an epoch in the history and usefulness of this Institute, and it is expected that the change will presage a large and healthy growth in metallurgical fields. Many metallurgists who knew nothing about min¬ing were loath to join a society of mining engineers, despite the fact that over 35 per cent. of the papers published in our Transactions during the past five years have dealt with metallurgical subjects.

Jan 1, 1923

By R. P. Carreker, R. L. Fullman, J. C. Fisher

CREEP tests are usually constant load tests. As deformation occurs, the cross section of the specimen changes so as to maintain approximately constant volume. Until necking starts, A _ l0 A0 - 1 where A is the cross-sectional area, 1 is the specimen length, and the subscript o indicates initial values. Thus, during a tensile creep test under constant load, the stress increases in proportion to the elongation. A A, 1, where S is the stress and F the load applied to the specimen.

Jan 1, 1954

By Frederick Tickell

PETROLEUM engineers are displaying considerable interest in those fundamental properties of matter and energy that control the phenomena of oil and gas production. The subject is a difficult one to investigate by laboratory experiments for two reasons: (1) it is impossible to reproduce in the laboratory the scale of forces and dimensions that exist in the underground reservoir; (2) if we attempt to scale down the dimensions we are unable to reduce all proportionally. It is as if we tried to construct a model blast furnace for the reduction of iron ore, and reduced all lineal dimensions. We should find that the interstices between the miniature chunks of ore would not .permit rapid transfer of gases, that combustion and heat transfer would not take place as in the full size furnace and that, in short, the contraption would not work. Just so, when we attempt to make a reduced scale oil field we find we must have, not only miniature reservoir and miniature wells, but "miniature" sand, oil, gas, etc. Much valuable work, however, has been done along these experimental lines and more will no doubt follow, but investigators should bear this point in mind and strive to attain dimensional homogeneity and dynamical similarity in order that their conclusions may be translated into terms applying to the oil reservoir. As Gibson says,1 "These conditions are attained when all terms of the physical equation have the same dimensions, . . . when all corresponding particles of the two systems trace out similar paths and when the velocities are such as to make all corresponding forces acting on two such particles in the same ratio. It is the purpose of this paper to discuss the mechanics of fluid movement as it pertains to the oil pool and to point out the complexity of the laws of fluid delivery under the conditions often found.

Jan 1, 1928

By R. W. Winson

Asbestos is the generic name given to a group of fibrous mineral silicates found in nature. They are all incombustible and can be separated by mechanical means into fibers of various lengths and cross sections, but each differs in chemical composition from the others. The commercial grades of asbestos consist of a spectrum of lengths and sizes and are not definitive as are most organic fibers. It is generally recognized that there are two main groups of asbestos. The first only contains the fibrous serpentine called chrysotile and comprises about 94% of the world production of asbestos. The second group contains five minerals in the amphibole series+rocidolite, amosite, anthophyllite, tremolite, and actinolite. The latter two have no commercial importance. Properties Physical The structures of asbestos fibers have been studied intensively over a number of years. X-ray diffraction patterns have been used as a means of identification and classification. Low angle X-ray scattering techniques have shown that chrysotile fibers are "hexagonally close packed" and parallel to each other, having cross-sectional diameters varying from 18014 to 300A units, while the amphibole fibers are many times larger in cross section. Electron micrographs of the more common types of as- bestos are shown in [Figs. 1-4]. [Fig. 1] illustrates the softness and flexibility of chrysotile which make it suitable for textile-type products. For a number of years there was considerable controversy over the exact nature of chrysotile fiber, but the photographic evidence in [Figs. 5-7] clearly show that it is tubular in structure. The curvature is the result of the mismatch in the dimensions of the silica [Si,O,l and brucite [Mg(OH),] layers which are on the inside and outside, respectively, of a double sheet. This curvature had been predicted by Pauling (1930) years ago based on the molecular dimensions of the two component structures.

Jan 1, 1975

By M. V. Nevitt

In the systems Ti-Mn-O, Ti-Fe-O, Ti-Co-O, and Ti-Ni-O the bounda.r-ies of the Ti2Ni-type phases were determined at one or more temperatures and the variation of the lattice parameter with oxygen content was determined. Densities were calculated from the lattice parameters and compared with measured density values. The: results indicate that the occurrence of the phase in these systesms can be correlated qualitatively with valency electron concentration, and that the role of oxygen is that of an electron acceptor. The lower limit of oxygen solubility appears to be determined by the valencies of Mn, Fe, Co, and Ni, while the maximum oxygen concentration coincides with the filling of the 16 (c) positions of the O 7h - Fd 3m space group. THE suggestion has been made by several investigators'" that the phases having the cubic E9,-type structure, and known as 17-carbide-type, double-carbide-type and Ti,Ni-type, are members of a family of electron compounds. This concept has been given additional support by recent work8 in which new isostructural phases involving second and third long period combinations were found, and which provided further evidence of the regularity of occurrence of the phase in terms of periodic table relationships. In this laboratory attention has been focused on the isomorphs containing titanium, zirconium, or hafnium, and the role that oxygen plays in their occurrence. In some binary systems Ti,Nitype* phases occur having the formula A,B where A is the titanium group element. Based on previous workq and the present investigation, oxygen is known to be soluble in two of these binary phases, Ti,Co and Ti2Ni. It is probable that oxygen is also soluble in the other phases of this kind. In other binary systems the Ti,Ni-type phase does not occur, but does occur in the corresponding ternary systems with oxygen .3-5 The experiments described here were performed to determine whether the occurrence and composition of certain of the Ti,Ni-type phases could be related to an electronic effect and whether oxygen's stabilizing role is exerted through an influence on the electron: atom ratio. The ternary systems Ti-Mn-O, Ti-Fe-O, n-Co-O, and Ti-Ni-O were selected for study for two reasons: First, several schemes have been proposed for first long period elements which, although not in quantitative agreement, show a generally consistent trend for the variation of valency with atomic number. Although for a transition metal the term valency is difficult to define and is generally not a constant number which can be applied to all alloys, it is usually assumed to be an index of the number of electrons per atom involved in metallic cohesion. Second, the determination of the Ti2Ni-type phase boundaries was facilitated by the fact that the phase relations in several of these ternary systems have been investigated by other workers."' EXPERIMENTAL PROCEDURE___________________ The alloys were prepared by arc melting crystal-bar titanium, reagent grade TiO, and electrolytic manganese, iron, cobalt, and nickel. Each button was remelted at least three times. The metals had a minimum purity of 99.9 pct except the nickel whose purity was 99.4 pct, the major impurity in this instance being cobalt. The preparation of the manganese alloys was attended by the customary difficulties associated with the vaporization of manganese. The technique used in this case was to add approximately 10 pct extra manganese to the original charge and to continue remelting the button until the final weight was in agreement with its intended weight. At least three alloys in each system were analyzed chemically and the results, even for the manganese alloys, were in good agreement with the intended compositions. A few additional alloys in the Ti-Mn-O system were prepared by the sintering of mixed powders in evacuated quartz tubes followed in some cases by arc melting. For annealing, the alloys were wrapped in molybdenum foil and placed in fused silica tubes containing zirconium chips. The fused silica tubes were evacuated at room temperature to a pressure of 1 x l0-6 mm of Hg and sealed. These capsules were then annealed for 72 hr at an external pressure of 5 x 10-5 mm of Hg in a vacuum furnace whose temperature could be controlled to + 1°C. The success of this procedure in avoiding significant oxygen or nitrogen pickup was indicated by the bright, ductile condition of the molybdenum foil and by the complete absence of a microscopic reaction layer on the specimens. This method did not permit rapid quenching of the specimens but in no case did metal-lographic examination indicate that a solid-state transformation had occurred on cooling. Metallo-

Jan 1, 1961

By Wayne E. Glenn, R. W. French, Lincoln F. Elkins

The Lance Creek Sundance reservoir provides a case history of ro years performance of a reservoir in which unit operation has permitted effective utilization of gravity drainage augmented by primary pressure control with injection of gas into top structural wells. Detailed performance of the reservoir is presented by means of maps of Well status, reservoir pressure, individual well recovery, etc., and by pool-performance charts. Analysis of reservoir performance indicates only minor water encroachment, so that gravity, injected gas, and expansion of gas are the main oil-expulsive agents. A simplified theory of regional drainage of oil from upstructure location to downstructure location due to gravity is presented and checked by means of comparison of "reservoir" permeability and "well" permeability from the pool performance. Good order of magnitude agreement was obtained. Individual well performance and overall reservoir performance indicate possibility that maintenance of pressure makes ineffective those parts of the reservoir in which permeability is too low to permit effective drainage of oil by action of gravity. Oil from these parts can be recovered only when pressure is reduced locally by selective withdrawal or when overall reservoir pressure is finally reduced.

Jan 1, 1949

The mines of the country are called upon to bear a very large part of the enormous taxes to be raised for 1917 and later years. The Internal Revenue Bureau, which is charged with the assessment and collection of these taxes, desires that the taxation laws shall be administered in a fair and business-like way. The application to mines, however, which have wasting assets, involves questions of particular complication and difficulty. To meet this situation, there has been established in. the Income Tax Branch, a Section of Mine Valuation in which these specific problems of the industry will be handled by competent engineers. But it is realized that something more than this is required for the satisfactory application of the tax laws to the mines, namely, as complete understanding as possible between the Government and the taxpayer, a spirit of cooperation as between the two and every possible assistance and advice from mine owners and mining engineers.

Jan 9, 1919

By J. Kinkead, R. M. Sherman, E. M. Frizzel

A recent research study performed under US Bureau of Mines Contract No. J0199088 "Modular Irrigation Equipment for Reclaimed Strip Mined Lands" investigated the feasibility of irrigation as a reclamation tool in the arid and semi-arid regions of the Western United States. Review of mined land characteristics, evaluation of irrigation systems, and assistance from the mining industry resulted in the design of two strategies for the implementation of reclamation irrigation using solid set systems. It is not the intent of this paper to suggest the generalizations made on the basis of a six state area can extend to the design of an irrigation system for a specific mine site. The purpose is to present two irrigation strategies that may be implemented with solid set irrigation in this six state area. The reader should note that the following is the result of research and, therefore, original concepts were presented. The ultimate validity of these concepts will be determined by future field tests.

Jan 1, 1983

At the office of the Chief of Engineers, Washington, there is a unique collection of engineering material used and developed in the present war. It. is a most interesting group of war devices, from the special trench shovel that excavates both gas and water, to the standard gage locomotives that were sent to France so complete that they were lifted from the ships by cranes, placed on the-rails on shore, filled with water, fired up, and moved out from underneath the cranes under their own steam. Everything is exhibited either by models, or by photograph where the original samples are too large to admit of demonstration in an ordinary office. The forestry section has an interesting exhibit of the wonderful work clone in France; where, owing to the shortage of coal and the necessity for burning wood, the Forestry Unit of the A. E. F. in one month stacked up 60 mi. of cord wood (80,000 cords); also cut 6.6 mi. of timber, stacked 12 ft. long, and 10 ft. high, containing 50,000,000 hoard feet of sawed timber.

Jan 3, 1919

By Joseph Richards

THERE are two essentially different types of case-hardening processes; that using a dry mixture in which the object to be case-hardened is packed and kept for the necessary time at the necessary temperature, and the "liquid" process, employing a bath of fused, salts into which the object- is immersed and which by immediate contact case-hardens the surface of the article. The Shimer process belongs to the second class, and was a war emergency invention. Of the liquid melts used as baths, the most effective and most fre¬quently used are melted potassium cyanide and melted sodium cyanide. These may be used either pure, or mixed with salts that reduce the melting point and the percentage of cyanide present. The use of these baths since 1914 has met many commercial difficulties because of the high price and frequent commercial scarcity of the cyanide salts; at present sodium cyanide has practically entirely displaced potassium cyanide. Another trouble is the danger to the workmen handling the cyanide salts, which are extremely poisonous, and the annoying and poisonous vapors or gases given off in the workshop, unless an effective system of hoods and ventilation is provided, so as to prevent the gases from the baths mixing with the air of the room. Porter W. Shimer, of Easton, Pa., has invented a substitute for the bath of melted cyanides which case-hardens with equal or greater facility and effectiveness, gives off no poisonous vapors, and costs for chemicals materially less than the cyanide costs in the previously used baths. The process has been in use over a year in a large American works and the following statement embodies the results of practical experience in the use and operation of the process. The Shinier liquid or melted bath consists of a mixture of easily fusible salts that do not possess case-hardening properties, into which is immersed fresh calcium cyanamide, which imparts to the bath case-hardening properties. The composition of the non-case-hardening-,salts appears rather immaterial. Good results have been obtained by using a mixture of sodium chloride, calcium chloride, and barium chloride in

Jan 2, 1919

By J. W. Richards

There are two essentially different 'types of case-hardening processes; that using a dry mixture in which the object to be case-hardened is packed and kept for the necessary time at the necessary temperature, and the "liquid" proccss, employing a bath of fused salts into which the object is immersed and which by immediate contact case-hardens the surface of the article. The Shimer process belongs to the second class, and was a war emergency invention. Of the liquid melts used as baths, the most effective and most frequently used are melted potassium cyanide and melted sodium cyanide. These may be used either pure or mixed with salts that reduce the melting point and the percentage of .cyanide present. The use of these baths since 1914 has met many commercial difficulties because of the high price and frequent commercial scarcity of the cyanide salts; at present sodium cyanide has practically entirely displaced potassium cyanide. Another trouble is the danger to the workmen handling the cyanide salts, which are extremely poisonous, and the annoying and poisonous vapors or gases given off in the workshop, unless an effective system of hoods and ventilation is provided, so as to prevent the gases from the baths mixing with the air of the room. Porter W. Shimer, of Easton, Pa., has invented a substitute1 for the bath of melted cyanides which case-hardens with equal or greater facility and effectiveness, gives off no poisonous vapors, and costs for chemicals materially less than the cyanide costs in the previously used baths. The process has been in use over a year in a large American works and the following statement embodies the results of practical experience in the use and operation of the process. The Shimer liquid or melted bath consists of a mixture of easily fusible salts that do not possess case-hardening properties, into which is immersed fresh calcium eyanamid, which imparts to the bath case-hardening properties. The composition of the non-case-hardening salts appears rather immaterial. Good results have been obtained by using a mixture of sodium chloride, calcium chloride, and barium chloride in equal proportions by weight; also a mixture of one part sodium chloride

Jan 1, 1920

By W. M. Baldwin, J. T. Brown

The effect of hydrogen on the ductility, c, of SAE 1020 steel at strain rates, i, from 0.05 in. per in. per rnin to 19,000 in. per in. per rnin and at temperature, T, from +150° to —320°F was determined. The ductility surface of the embrittled steel reveals two domains: one in which and the other in which The usual "explanations" of hydrogen embrittlement are in accord with the first of these domains only. THE purpose of this investigation was a fuller A characterization of this of the investigation effects of varying temperature and strain rate on the fracture strain of hydrogen-charged steel. To be sure, it is known that low and high temperatures remove the embrittlement that hydrogen confers upon steels at room temperature,1 * see Fig. la and b, and that high strain rates have a similar effect,'-' see Fig. 2a, b, and c. However, the general effect of these two testing conditions on the fracture ductility of hydrogen-charged steels is not known, i.e., the three-dimensional graphical representation of fracture ductility as a function of temperature and strain rate is not known—only two traverses of the graph are available. The need for such a graph is not pedantic. To demonstrate this point, Fig. 3a, b, and c shows three of many three-dimensional graphs, all possible on the basis of the two traverses at hand. The important point (as will be developed in the Discussion) is that each of them would indicate a different basic mechanism for hydrogen embrittlement. It will be noted that the four types of ductility surfaces in Fig. 3a, b, and c may be characterized as follows: Material and Procedure Tensile tests were made at various temperatures and strain rates on a commercial grade of % in. round SAE 1020 steel in both a virgin state and as charged with hydrogen. The steel was spheroidized at 1250°F for 168 hr to give the unembrittled steel the lowest possible transition temperature. The steel was charged cathodically with hydrogen as follows: The specimen was attached to a 6 in. steel wire, degreased for 5 min in trichlorethylene, rinsed with water, and fixed in a plastic top in the center of a cylindrical platinum mesh anode. The assembly was placed in a 1000 milliliter beaker containing an electrolyte of 900 milliliters of 4 pct sulphuric acid and 10 milliliters of poison (2 grams of yellow phosphorous dissolved in 40 milliliters of carbon disulphide). A current density of 1 amp per sq in. was used which developed a 4 v drop across the two electrodes. All electrolysis was carried on at room temperature. Temperatures for tensile tests were obtained by immersing the specimens in baths of water (+70° to + 150°F), mixtures of liquid nitrogen and isopen-tane (+70° to —24O°F), and boiling nitrogen (-240" to-320°F). Specimens were tested in tension at strain rates of 0.05, 10, 100, 5000, and 19,000 in. per in. per min. The 0.05 and 10 in. per in. per rnin strain rates were obtained on a 10,000 lb Riehle tensile testing machine, the 100 in. per in. per rnin rate on a hydraulic-type draw bench with a special fixture, and the 500 and 19,000 in. per in. per rnin rates on a drop hammer. The fracture ductility of hydrogen-charged steel at room temperature and normal testing strain rates (-0.05 in. per in. per min) is a function of electro-lyzing time, dropping to a value that remains constant after a critical time.'* Under the conditions of • The hydrogen content of the steel continues to increase with charging time even after the ductility has leveled off to its saturated value.' this research the saturated loss in ductility occurred at approximately 30 min, see Fig. 4, and a 60 min charging time was taken as standard for all subsequent tests. After charging the steel with hydrogen, the surface was covered with blisters. These have been described by Seabrook, Grant, and Carney.' The original diameter of the specimen was not reduced by acid attack, even after 91 hr. Results The ductility of both uncharged and charged specimens is given as a function of strain rate in Fig. 5, and as a function of temperature at four different strain rates in Fig. 6. These results are assembled into a three-dimensional graph in Fig. 7. It is seen that the locus of the minima in the ductility curves of the charged steels divides the ductility surface into two domains. At temperatures below the minima,

Jan 1, 1955

By J. H. Hamilton, J. R. Lewis, J. H. Dismant, W. M. Fassell

RECENTLY this laboratory undertook the task of preparing some low carbon metallic cobalt by the carbon reduction of precipitated cobalt oxides. The oxides came in two lots and had the compositions given in Table I. Industrially, cobalt rondels' are made by the carbon reduction of cobalt oxide in small reverberatory furnaces at temperatures near but not above 1050 °C. This is a slow and tedious small batch process but does give cobalt metal which is low in carbon (1 pct C). Inasmuch as these cobalt oxides were relatively low in copper and iron it was decided to reduce them with petroleum carbon in a small three-phase electric arc furnace of about 3 to 5 Ib of metal capacity. It was hoped such a procedure would save considerable time and perhaps also indicate an improved commercially feasible process. The furnace was preheated by using small pieces of carbon electrodes to maintain the arc until a temperature of 1500°C was reached. The broken pieces of electrodes were then removed and 500 g of the cobalt oxides and 60 to 100 g of petroleum coke added. At the end of the reduction reaction, a high lime flux was added to the furnace to facilitate the removal of sulphur. Due to the fineness of the cobalt oxide powder used and also to the presence of chlorides there was considerable dust lost in charging the furnace. This was overcome by preparing briquettes composed of the cobalt oxides, charcoal, and a little bentonite to serve as a binder. The results obtained are summarized in Table 11, which shows that the cobalt metal produced in the arc furnace was high in carbon varying from 2.5 to 3.5 pct. This, of course, is much too high. For certain uses, such as in the preparation of permanent magnets, the carbon content of cobalt must be low. It was necessary therefore to find an effective method of reducing the carbon content of the cobalt that had been prepared in the arc furnace. Van Arkel3 recommends the use of Co2O3 as a means of removing carbon from cobalt. Experiments by the authors indicate that carbon is removed with difficulty by this method. Other methods used, including lancing of the molten high carbon cobalt with a jet of oxygen, proved to be ineffective. The method finally used makes use of the fact that cobalt metal is decarburized by carbon dioxide at the temperature of the molten metal. Two methods were used: 1—carbon dioxide was bubbled up through the molten cobalt, and 2— molten cobalt was maintained in a carbon dioxide atmosphere. In the first method the gas was introduced below the surface of the molten metal by means of a quartz tube. A high frequency induction furnace was used to keep the cobalt molten in both of these experiments. This kept the metal somewhat agitated and no doubt was an important factor in hastening the decarburization 'process by the second method. Both methods gave satisfactory results as shown in Table 111. An interesting observation in connection with this 'work was that a small sample of carburized cobalt metal could be decarburized by heating it with an acetylene torch adjusted to give an oxidizing flame. This may have been due to the presence of carbon dioxide in the products of combustion. Samples of molten high carbon steel were decarburized by the same method and it is suggested that nickel and perhaps manganese can be decarburized in a similar manner. Additional work, including rate studies and other theoretical aspects of this problem, is in progress in this laboratory.

Jan 1, 1953

By Wolfgang Pietsch

Direct Reduced Iron is a product obtained during solid state reduction of iron oxides into metallic iron. General chemical and physical characteristics of all direct reduced iron materials result in a noticeable reoxidation tendency and a relatively low ignition temperature. As most of the chemical reactions are exothermic, normally heating occurs and if water is present hydrogen evolves. Dry direct reduced iron deactivates quickly in air but is still reactive if it comes into contact with moisture. Because of these characteristics, special requirements are necessary for safe storage, shipment, and handling. In an effort to improve this situation passivation techniques were and still are being developed. The paper discusses the properties of direct reduced iron, presents past experience with storage, shipment, and handling of MIDREX® Iron, a direct reduced iron material produced in the MIDREX® Direct Reduction Process, and evaluates benefits derived from different passivation techniques.

Jan 1, 1978

By G. E. Karantzavelos

Anew flotation process to recover alunite from low-grade alunite ores is described. The process begins with run-of-mine ore, reduced to less than 5 mm (0.2 in.), being preconditioned with the reagents before grinding and alunite flotation. From the preconditioning step, ore particles, impregnated with reagents, form pellets that subsequently disintegrate into the pulp during grinding. The second step is basically a standard alunite flotation step. Pilot plant test results show that an alunite concentrate assaying at least 85% alunite and less than 5% silica can be produced. Laboratory and pilot plant results were in excellent agreement, indicating that the new process is a viable means of alunite beneficiation. Plant results, using the new process, were superior to results from conventional alunite flotation procedure.

Jan 1, 1986

US 4,192,852-Precipitation of iron values as a jarosite from a sulfate solution obtained as a byproduct in the hydrometallurgical processing of zinc sulfide ore The solution is cooled, partially neutralized, and clarified. The clarified solution is heated to a temperature of 80 to 100°C in the presence of sodium, potassium, or ammonium ions to precipitate substantially all of the ferric iron as jarosite The precipitate is thickened, filtered, and washed The residual solution may be processed for zinc or other nonferrous metal values R V. Pammenter and C J Haigh, assigned to Electrolytic Zinc Co of Australasia Ltd. Mar. 11, 1980. 16 pp. (423-42) Filed: 5-8-78 (903,524). Priority- Australia, 5-9-77 (PD0030) (Drawings below.)

Jan 1, 1982