By Clarence Zener

The internal friction of nonferrous metals vibrating at low stress amplitudes has so far always been successfully interpreted in terms of inhomogeneities of one sort or another. Examples are the fluctuation of stress across a specimen vibrating transversely,1,2,3 the stress inhomogeneities due to the elastic anisotropy and partial random orientation of the individual crystallites, localized weak regions introduced by cold-working,6'7 grain boundaries and possibly twinning planes.8'9 Perfect single crystals are, by definition, homogeneous. Actual single crystals usually, perhaps always, contains some imperfections. The present investigation was undertaken to determine whether the internal friction of single crystals may likewise be attributed to inhomogeneities. This study was made possible through the gift of a large single crystal of 70-30 alpha brass by H. L. Burghoff, of the Chase Brass and Copper Co. The specimen, 3.i in. in diameter and 10 in. long, was similar to samples previously described by Mr. Burghoff. Experimental Method The experimental method used has previously been described in institute papers.5'6'9 The measure of internal friction adopted here, I/Q, is X the logarithmic decre- ment, a measure used by some writers, and is also X the specific damping capacity, a measure used by other writers. In all measurements the stress level was kept so low that the measurements were independent of stress level. In all measurements in which the temperature was varied, observations were made as the specimen slowly cooled from its highest temperature. The specimen was vibrated transversely. Observations were made at the fundamental frequency and at the first overtone, of about 620 and 1710 cycles per second, respectively. No attempt was made to avoid acoustical losses. Experimental Results The specimen was annealed for several hours at 450°C. The temperature dependence of the internal friction was then determined from room temperature to 400°C. As shown in Fig. I, the internal friction increased by only a factor of 2 from room temperature to 300°C., then by a factor of 100 during the next Ioo° interval. These measurements are consistent with the view that the observed internal friction is the superposition of two distinct parts. One, dominant at room temperature, is nearly independent of temperature. This part may be accounted for by acoustical losses and by transverse thermal currents. It was not further investigated. The second part, when plotted in the manner of Fig. I, lies upon a straight line. Therefore it has a heat of activation H; i.e., it varies with temperature as Internal friction e-H/RT [I]

Jan 1, 1943

By J. S. Marsh

AN incomplete statistical analysis performed wearily on the morning after Thursday, Feb. 12, indicates that the unavoidable items of conversation among steelmen were the current shortage of sleeping time and the "Normandie." No analysis is needed, however, to be certain that many thousands of valuable words were uttered, both in and out of technical sessions, concerning matters of deep interest to members of the Iron and Steel Division. The opening session consisted mostly of papers that have appeared, or will appear shortly, in Metals Technology. One, however, that was not finished in time to be printed in any form, but that aroused great interest, was by E. L. Ramsey and L. G. Graper (Wisconsin Steel Works). Its subject was the production of high-sulphur steel by treatment with sulphur dioxide derived from anhydrous sodium sulphite or bisulphite added to the ladle or to the mold. The sulphide distribution in the finished steel is such that increased machinability and longer tool life result. Both items are of obvious importance in these days of mighty production.

Jan 1, 1942

By M. Kaufman, A. E. Palty

The phase structure and aging characteristics of two nickel-base alloys, Inconel 718 and 702, were investigated. Wrought and cast Inconel 718 showed ArisCb as the major hardening phase, as well as ture was positively identified. Inconel 702 had Ni3Al as the major hardening phase, as well as Cr7C3-of the phase amounts with temperature was determined. 1 HE value of phase structure and aging rate information in the utilization of alloys has been well established. As part of a continuing program, the results obtained on two nickel-base alloys, hconel 718 and Inconel 702, are presented here. Inconel 718 is a relatively new alloy considered for application in both sheet and cast form. Its novelty lies in the use of high columbium tantalum levels in a Ni-Cr-Fe base. No previous work on this type of alloy has been reported in the literature. Inconel 702 is being used now as an oxidation-resistant sheet alloy. Occasional fabrication problems spurred work on its basic structural behavior. The composition of 702 is essentially nichrome plus aluminum and titanium for strengthening and added oxidation resistance. This puts it in the basic class of other nickel-base alloys which have already been studied. The two alloys will be treated separately. INCONEL 718 Phase Study Methods. The phases present after the various conditions investigated were determined by X-ray diffraction analysis of two different elec-trolytically extracted residues and microscopic examination. The extraction methods, using 10 pct HC1 in alcohol and 10 pct H3PO, in water and the X-ray technique have been described previously.' The effect of temperature on the phase behavior was studied on sheet material using the following heat treatments: 2250°F, 2 hr, ice brine quench 1300 100 hr, water quench 2250°F, 2 hr, ice brine quench 1400°, 100 hr, water quench 2250°F, 2 hr, ice brine quench 1500°F, 100 hr, water quench 2250o 2 hr, ice brine quench 1700°F, 48 hr, water quench 2250°F, 2 hr, ice brine quench 1850°, 24 hr, water quench 2250°, 2 hr, ice brine quench 2000°F, 6 hr, water quench The high solution temperature was an attempt to dissolve as many phases as possible without causing melting. Aging exposures were made longer than normal heat treating times in order to approach equilibrium conditions more closely. Cast material was examined only in the as-cast condition and with the normal heat treatment (1700°F, 1 hr, air cool 1325oF, 16 hr,air cool). Materials. The full phase study was performed on sheet specimens approximately 1/2 in. by 2 in. by 1/16 in. The cast pieces were cut from the gating system of a vacuum-cast test piece. An all weld-metal specimen was made by running many weld beads on the sheet using filler made from the sheared edges of the sheet. All external contamination was removed by belt-sanding followed by an electro-polishing treatment. The typical composition of wrought Inco 718 is as follows: The alloy is air-melted. Cast hco 718 may have higher molybdenum. Due to the expectation of finding a Ni-Cb phase (Ni, Cb) for which no X-ray diffraction pattern was available in the ASTM Index, a special 5 Ib heat to the stoichiometric composition of this intermetallic

Jan 1, 1962

By Clarence Zener

THE internal friction of nonferrous metals vibrating at low stress amplitudes has so far always been successfully interpreted in terms of inhomogeneities of one sort or another. Examples are the fluctuation of stress across a specimen vibrating transversely,1,2,3 the stress inhomogeneities due to the elastic anisotropy and partial random orientation of the individual crystallites,4,5 localized weak regions introduced by cold-working,6,7 grain boundaries and possibly twinning planes.8,9 Perfect single crystals are, by definition, homogeneous. Actual single crystals usually, perhaps always, contains some imperfections. The present investigation. was undertaken to determine whether the internal friction of single crystals may likewise be attributed to inhomogeneities. This study was made possible through the gift of a large single crystal of 70-30 alpha brass by H. L. Burghoff, of the Chase Brass and Copper Co. The specimen, ½ in. in diameter and 10 in. long, was similar to samples previously described by Mr. Burghoff.10 EXPERIMENTAL METHOD The experimental method used has previously been described in Institute papers.5,6,9 The measure of internal friction adopted here, 1/Q, is (1/p) X the logarithmic decrement, a measure used by some writers, and is also (1/2p) X the specific damping capacity, a measure used by other writers. In all measurements the stress level was kept so low that the measurements were independent of stress level. In all measurements in which the temperature was varied, observations were made as the specimen slowly cooled from its highest temperature. The specimen was vibrated transversely. Observations were made at the funda¬mental frequency and at the first overtone, of about 620 and 1710 cycles per second, respectively. No attempt was made to avoid acoustical losses. EXPERIMENTAL RESULTS The specimen was annealed for several hours at 450°C. The temperature dependence of the internal friction was then determined from room temperature to 400°C. As shown in Fig. 1, the internal friction increased by only a factor of 2 from room temperature to 300°C., then by a factor of l00 during the next 100° interval. These measurements are consistent with the view that the observed internal friction is the superposition of two distinct parts. One, dominant at room temperature, is nearly independent of temperature. This part may be accounted for by acoustical losses and by transverse thermal currents. It was not further investigated. The second part, when plotted in the manner of Fig. I, lies upon a straight line. Therefore it has a heat of activation H; i.e., it varies with temperature as Internal friction e~H/RT [I]

Jan 1, 1942

By Clarence Zener

THE internal friction of nonferrous metals vibrating at low stress amplitudes has so far always been successfully interpreted in terms of inhomogeneities of one sort or another. Examples are the fluctuation of stress across a specimen vibrating transversely,1,2,3 the stress inhomogeneities due to the elastic anisotropy and partial random orientation of the individual crystallites,4,5 localized weak regions introduced by cold-working,6,7 grain boundaries and possibly twinning planes.8.9 Perfect single crystals are, by definition, homogeneous. Actual single crystals usually, perhaps always, contains some imperfections. The present investigation was undertaken to determine whether the internal friction of single crystals may likewise be attributed to inhomogeneities. This study was made possible through the gift of a large single crystal of 70-30 alpha brass by H. L. Burghoff, of the Chase Brass and Copper Co. The specimen, 3-s in. in diameter and 10 in. long, was similar to samples previously described by Mr. Burghoff.10 EXPERIMENTAL METHOD The experimental method used has previously been described in Institute papers.5,6.9 The measure of internal friction adopted here, I/Q, is (p) X the logarithmic decrement, a measure used by some writers, and is also (I/2p) X the specific damping capacity, a measure used by other writers. In all measurements the stress level was kept so low that the measurements were independent of stress level. In all measurements in which the temperature was varied, observations were made as the specimen slowly cooled from its highest temperature. The specimen was vibrated transversely. Observations were made at the fundamental frequency and at the first overtone, of about 620 and 1710 cycles per second, respectively. No attempt was made to avoid acoustical losses. EXPERIMENTAL RESULTS The specimen was annealed for several hours at 450°C. The temperature dependence of the internal friction was then determined from room temperature to 400°°C. As shown in Fig. i, the internal friction increased by only a factor of 2 from room temperature to 300°°C., then by a factor of 100 during the next :too' interval. These measurements are consistent with the view that the observed internal friction is the superposition of two distinct parts. One, dominant at room temperature, is nearly independent of temperature. This part may be accounted for by acoustical losses and by transverse thermal currents. It was not further investigated. The second part, when plotted in the manner of Fig. I, lies upon a straight line. Therefore it has a heat of activation H; i.e., it varies with temperature as Internal friction ~ e-HI/RT [I]

Jan 1, 1942

By Ralph W. M. Lai, D. W. Fuerstenau

This paper presents the results of a study of the principles which control the distribution of ultrafine particles between an oil phase and an aqueous phase. Alkyl sulfonates were used to control the wettability of fine alumina particles and to stabilize the water-isooctane emulsion system in the extraction process. The effects of sulfonate chain length, sulfonate adsorption, pH, and oil-water ratio on the recovery of solids in the oil phase were investigated. Higher extraction was found under conditions which yield higher hydrophobicity and large interfacial area of the oil-water emulsion. Today there is considerable interest in developing methods for the recovery of fine particles from disseminated ores. One such method might be the extraction of fine particulate solids from aqueous suspensions into an oil phase, and one example of a successful industrial process based on oil-water distribution phenomena is the emulsion flotation process used in concentrating manganese ore.' The oil agglomeration process of Farnand, Smith, and Puddington has been suggested for concentrating tin ore. Patents 3-4 for oil flotation processes extend back to that of William Haynes in 1860. The basis of all these processes is directly related to the stabilization of emulsions with solid particles. The first extensive study of oil-water emulsions stabilized by finely divided solids was made by Pickering. Later, Briggs,6 weston, 7 Chessman and King,8 and Leja and Schulman9 experimentally demonstrated how solid particles control water-oil and oil-water systems. Hildebrand10 suggested that fine particles can stabilize an emulsion because the fine particles are partially wettable by both oil and water, that is, that the contact angle must be finite. Takakuwa and Takamori 11 recently applied emulsion inversion to the study of collector adsorption in flotation systems. At the Royal School of Mines, Shergold and Mellgren12 are currently carrying out a comprehensive study of the extraction of fine particles into an organic liquid phase. In the present study of the liquid extraction or oil flotation of ultrafine particles, the recovery of hydro-philic alumina particles of 0.1-µ average diameter was determined after separating an isooctane-water mixture (emulsion) into its two phases. Alkyl sulfonates of different chain lengths were used to change the wettability of the alumina and to effect emulsifi-cation of the oil-water mixture. The effects of the oil-water volume ratio, sulfonate adsorption, and pH on the recovery of the fine particles were investigated. Since the surface charge on an oxide such as alumina is determined by the adsorption or interaction of H+ and OH- with the surface, pH control is extremely important. Furthermore, since the zero point of charge (zpc) of alumina13-14 occurs at pH 9 to 9.4, major adsorption effects with anionic collectors in these systems will occur below pH 9. The results of the foregoing investigation are discussed in terms of the recovery of the fine particles, the oil-water ratio, contact angles, surface tension, the adsorption of sulfonate onto the solid surface, and the emulsifica-tion of oil. MATERIALS AND EXPERIMENTAL METHODS Materials: The particulate solid used in all the experiments was Linde "A" alumina, a high-purity, readily available form of a-alumina. The surface area of the alumina, as evaluated from measurements of stearic acid adsorption from benzene, was 14.5 sq m per gm, based on a value of 20.5 sq Å for the cross-sectional area of stearic acid.13 All aqueous solutions were prepared from triply distilled conductivity water. Other materials included high-purity crystals of sodium alkyl sulfonates, isooctane, and, for pH adjustments, reagent grade hydrochloric acid and sodium hydroxide-Because sulfonic acids are strong acids, they are

Jan 1, 1969

By S. W. Churchill

A digital computer was used to obtain an exact numerical solution for the transient behavior of the insulation and earth adjacent to an isothermal, submerged flat surface for a single set of parametric values. Comparison of the computed results with analytical solutions for limiting conditions revealed that a complete and general solution for all parametric values could be constructed from these limiting solutions. Complete and general solutions for insulated spheres and cylinders can also be constructed from limiting solutions. The procedure is illustrated in part for an insulated spherical tank. The heat flow was found to fall rapidly to a pseudo-steady state; after some time, it then decreased slowly to zero for a flat plate and cylinder, and to a low steady-state rate for a sphere. The accumulative heat flow during the initial falling-rate period may be a significant fraction of the heat flow during the entire first year. INTRODUCTION Underground storage of liquefied natural gas and liquefied petroleum gas has received considerable recent attention. The rate of heat flow from the earth to the storage cavity and the resulting temperature field in the earth are important factors in the technical and economic evaluation of such storage facilities. The objective of this paper is to indicate how complete solutions can be developed for the transient flux and temperature field for various geometrical configurations. The representative properties and dimensions, and the resulting parameters utilized in the illustrative results, are indicated in Table 1. The results presented herein are for dry earth. The effect of the latent heat of solidification of water in the soiI will be described in a subsequent paper. The temperature field in the insulation and earth is determined by energy balances, boundary conditions and initial conditions. The physical problem can be described mathematically with virtually no idealizations insofar as physical properties are known. It appears possible to solve the equations by numerical integration on a high-speed digital computer for any geometrical configuration and conditions. For complex situations, however, the computations are expensive and the results are highly specific. Analytical solutions have been developed for a few simple but important geometrical configurations and conditions, including one-dimensional heat transfer from (or to) earth at an initially uniform temperature to (or from) flat plates, spheres and circular cylinders. The solution for an insulated flat plate has also been derived but is in the form of a slowly converging series involving taklated functions. It was planned to use a computing machine to evaluate this series for a number of representative conditions. However, upon examination of the results of preliminary computations it was discovered that a complete, general and accurate solution could be developed by interpolation between several much simpler solutions for limiting conditions. This technique then was used to develop a a complete solution for an insulated sphere. The equations presented herein are derived in Carslaw and Jaegerl and other books on applied mathematics, or they are simple extensions of these previous results. Hence, all derivations are omitted. Emphasis is instead placed on the results and their

By M. E. Volin, F. H. Erbisch, G. M. Wenberg

Bacterial leaching of copper and uranium is practiced under acidic conditions in environments furnishing sulfur and iron. However, many mineral deposits do not have these conditions; the chalcocite and native copper deposits in Michigan's Upper Peninsula are examples. Species of bacteria and fungi isolated previously from samples taken at the White Pine Copper Co. tailings pond and mine, were screened for solubilization of copper from chalcocite ore and flotation concentrate and from native copper jig concentrate. Certain Penicillium species solubilized significant amounts of copper under neutral to slightly acidic conditions in a carbon and nitrogen-enriched medium. Leaching apparently was accomplished by release of metabolites which chelated with the copper. The copper yield was highly dependent upon the medium composition and the concentration of copper in the source material. The standardized procedures which were developed in an attempt to maximize copper yield in leaching times of three to five days are described. This preliminary research indicates a biological leaching process for copper which is different from those in use, but whether it can be applied economically remains to be determined.

Jan 1, 1972

By Martin J. Gungl, J. Lyman MacInnis

None of the industry submissions could persuade the Canadian Tax Reform draftsmen that the rate of return has had as much bearing on investors' decisions to invest in Canada as the success records of Canadian ore findings. The goverment opted for the position that mining capital goes where the ore can be found. Many tax incentives which were available until the end of 1971 have been greatly reduced. However, it is still recognized that new ventures in exploration and development of natural resources deserve a break even if there is reduced recognition of the established and highly successful members of the industry unless they continue to search and develop. The latter will also get some breaks for processing beyond the prime metal stage.

Jan 7, 1972

By M. Gensamer

A RECENT paper1 described, by means of stereographic pole figures, the preferred orientations produced by cold-rolling low-carbon steel of automobile-body grade. It was found that the surface of the sheet exhibited a deformation texture significantly different from the texture possessed by the inside of the sheet. Efforts to produce the surface texture by buffing a sample exhibiting the normal or inside texture, using a copper lap, have not been successful. In view of the data collected, by Kurdjumow and Sachs2, it was suggested that the surface texture might be the result of partial recrystallization of the normal or inside texture. The recrystallization texture of cold-rolled mild steel was studied by Goss3, but he did not use the pole-figure method, so that his conclusions were in need of verification. For these reasons the work reported in the present paper was undertaken. It had two objectives: (1) to study the general behavior of cold-rolled mild steel on recrystallization below the critical temperature A,, and (2) to attempt experimentally a demon-stration of the genesis suggested above for the surface texture in cold-rolled steel. The material was that used by Gensamer and Mehl, cold-rolled to 97.5 per cent reduction in thickness. Fig. 1 is an X-ray pinhole photo-gram of this material, taken with the beam transmitted perpendicular to the plane of the sheet, using a molybdenum target at 35 kv. with no filter. It is typical of the inside texture, but in it the deformation texture is better developed than in the samples that showed a well developed difference between the inside and surface samples. Specimens from this sheet, which was 0.005 in. thick, were annealed for 5 min. at various temperatures in a lead bath. After about 0.0005 in. had been etched from both surfaces, X-ray photograms were prepared, using the technique described in the earlier paper'.

Jan 1, 1936

By David E. Van Dillen

INTRODUCTION Current design practices for deep tunnels make extensive use of plasticity solutions by Newmark (1970) and Hendron and Aiyer (1971). These solutions are applicable to a circular tunnel subjected to a hydrostatic stress state in a Mohr-Coulomb plastic medium. The role of rockbolts is introduced into these solutions as a uniform internal pressure equivalent to the yield stress of the rockbolt pattern. The application of these solutions is hampered by their inability to consider the biaxial nature of the in-situ stress field or any surcharged stress, such as due to blast loading. As a means of considering the biaxial stress field, designers have turned to relatively costly alternatives, such as the finite element method. The recent work of Detournay (1983) simultaneously provided two generalizations to the state of the art of the analysis of circular tunnels. Whereas the solution of Newmark applies to nondilatant Mohr-Coulomb materials, and that of Hendron and Aiyer applies to materials having associated flow rules, the solution of Detournay covers materials of arbitrary dilatancy. Secondly, Detournay's solution is valid for biaxial stress states, as long as the problem remains statically determinate (St. John, Detournay, and Fairhurst, 1984). The topic of this paper is an investigation of various alternatives for introducing the effects of rockbolts into simple tunnel design charts developed using Detournay's solution. The study was conducted using the BMINES finite element code, into which rockbolt elements have been added (St. John and Van Dillen, 1983). These rockbolt elements allow for plastic deformation of the bolt, bolt

Jan 1, 1984

By A. U. Seybolt

Precipitation of FeO from Fe-O solid solutions has been studied by metallographic methods. Such precipitation, which is visible, is composed largely of barely resolvable spheroidal particles. No metallographic evidence has been found for grain boundary oxide films. Oxygen diffusion into a iron does not occur chiefly by inter-granular penetration. IN an earlier communication' dealing with the solid solubility of oxygen in a iron, it was shown that under one set of conditions it was possible to show FeO precipitated from supersaturated solid solution. However, to assist in rationalizing the effect of an FeO second phase upon the mechanical properties of iron, it would be desirable to have more information on the possible modes of precipitation and on the thermal treatments required to produce precipitation.

Jan 1, 1955

By Carroll C. Bailey, William F. Boericke

Mine financing, or providing adequate capital for developing and bringing a mining property into production, is an essential requirement for a successful operation. Today it presents a different picture than even twenty-five years ago. The day appears to be gone when a mining property could pay its own way from grass roots to production. The country has been quite thoroughly combed for surface showings from which sufficient initial profit could be immediately garnered to pay for further development and production facilities. The four M's for success in mining-mineral, market, management, and money-are still essential, but doubled or tripled wage costs and steep advances in cost of equipment and supplies throw increased emphasis on adequate capital funds for converting a prospect into a producer. Consequently, the old picturesque, although seldom rewarding, grub- staking procedure where a single venturesome citizen might advance funds to a prospector on a fifty-fifty basis for whatever discovery he might find, has largely disappeared. Its place, to some degree, has been taken by the small syndicate of venturesome members who band together for furnishing funds to a group of prospectors for the same general purposes. Such a syndicate has a definite organization and is usually assured of sufficient initial funds, or flow of funds, to carry on work for several years. It is usually headed by an engineer-promoter or an entrepreneur trader who has had considerable field experience as well as personal knowledge of his prospecting crews. For the owner of a potential mining property who has ample capital, the problem is to determine (1) justification for the necessary investment in exploration and development, and (2) the economics of the enterprise as to size and degree of integration of the ha1 operating entity. If the owner of such a property has little or no capital, he also faces these same basic problems but, in addition, must be able to present the findings of fact and persuade the prospective investor that the enterprise will produce

Jan 1, 1964

By Frank E. Hauser, Philip R. Landon, John E. Dorn

The flow and fracture strengths of polycrystalline aggregates of high purity magnesium and a solid solution of aluminum in magnesium were determined as functions of temperature and grain size. Magnesium was found to obey two distinct fracture laws. Over the high temperature range, the fracture stress decreased with increasing test temperatures in a manner that closely paralleled the flow stress-temperature relationship. However, over the low temperature range, the fracture stress was independent of the test temperature though highly dependent on grain size, following the trend that is typical for the low temperature brittle fracturing of polycrystalline aggregates of body-centered-cubic and close-packed-hexagonal metals. Even at 78°K, however, plastic strains of 1 to 7 pet were obtained preceding onset of brittle fracturing. Over the brittle fracture range of temperatures, the fracture stress increased linearly with the reciprocal of the square root of the mean grain diameter, while over the entire range of temperatures investigated, the flow strength was observed to increase linearly with the reciprocal of the square root of the mean grain diameter. PREVIOUS investigations', 'have shown that deformation of coarse grained aggregates of high purity magnesium is interrupted by fracturing at very small strains. Such tendency toward brittle fracturing increased with increasing grain size and decreasing test temperature. In several respects, however, low temperature fracturing of magnesium appeared to differ from the truly brittle type exhibited by zinc, molybdenum, tungsten, and iron, so often characterized as a cleavage mode of fracturing. The absence of a well-defined cleavage mechanism for fracturing and the fact that some plastic deformation precedes fracturing might suggest that magnesium does not exhibit the same kind of brittle fracturing that is common to body-centered-cubic metals and to other close-packed-hexagonal metals. But, as will be shown, the low temperature fracture laws for magnesium are analogous to those that apply to iron, molybdenum, tungsten, and zinc in spite of differences in mechanisms and in plastic strains to fracture. In view of these observations. the low temperature fracturing of magnesium will also be called brittle fracturing. This, of course, does not imply that the brittle fracturing of metals is synonymous with the brittle fracturing of glass or other nonmetallics. Whereas the brittle fracturing of glass probably obeys Griffith's law, the low temperature brittle fracturing of metals arises from stresses induced by a series of dislocations piled up at an opaque grain boundary. Experimental Results All tests were made on tensile bars having gage sections that were 2 in. long and 0.375 or 0.25 in. wide. In order to develop a series of grain sizes, the

Jan 1, 1957

By J. J. Tietjen, D. Richman

Single-crystal Gap lms been epitaxially grow from the vapor phase at a rate oJ 3 p per nzin without encountering a7Zy low-ang-le grain boundaries or debwading- the electrical properties of the material. This growth rate exceeds any value previol~sly reported for the vapor phase growth of Gap. In pure material, mObilities ns high as 175 sq cm per U-sec at room tenzperature and 1450 sq cm per v-sec at 77°K have been obtained. These values are anLong the highest that have been attai)led for this material. For the first time, Gap possesses a number of important properties which make it well-suited for use in electro-optic modulators. First, the transverse electro-optic effect is operable in this material, which makes it possible to increase the path length of the modulated iron doping of Gap has been achieved; this results i?z resistivities of approximately 10" ohm-cm. The problelrls of residual strain and isolated shorting paths in these crystals have been partially solved. Electro-optic modulation of visible radiation has been demonstrated with this material. It is anticipated that further improvement with regard to the probleins of strain and shorting paths will result in a practical Gap electro-optic modulator. radiation without increasing the applied voltage. In addition, this permits the use of thin crystals so that relatively small voltages are needed to provide the requisite high electric fields. Second, GaP is a cubic crystal and therefore does not introduce critical optical-alignment problems associated with birefrin-gent crystals, such as ammonium dihydrogen phosphate (ADP), and potassium dihydrogen phosphate

Jan 1, 1968

By B. Post, D. Moskowitz, F. W. Glaser

Lattice parameters of various hafnium compounds, two borides, a carbide and a nitride were determined. Some physical properties were measured and comparisons with the properties of the corre-sponing zirconium compounds were drawn. A LTHOUGH borides of transition metals have A been extensively investigated in recent years, there are few references in the literature to borides of hafnium. This is not surprising, in view of the extreme scarcity and great cost of the purified metal. Becker' reported the existence of a boride, carbide, and nitride of hafnium; he listed the formulas as HfB, HfC, and HfN. However, in his work no mention was made of chemical analyses of the reaction products. In this paper results of a study of various hafnium compounds, including borides, carbides, and nitrides, are reported. It was expected, of course, that these compounds would closely resemble their zirconium analogues, which have previously been extensively investigated. Three borides of zirconium are known: ZrB,² ZrB,² and ZrB212.4 In addition, one carbide, ZrC,5 and one nitride, ZrN,5 have been reported. It should be noted that ZrB and ZrB12 are stable phases only in relatively high-temperature regions, unlike ZrB2, which is stable from room temperature to its melting point." It was felt that hafnium would yield corresponding borides, carbides, and nitrides with similar stability ranges. Experimental Procedures and Results A quantity of hafnium metal that was better than 97 pct pure, with zirconium as its major impurity, was furnished by the Argonne National Laboratories. The boron powder used was approximately 96.5 pct pure. In general, the procedure involved mixing the metal and boron powders in the desired proportions, and subsequently hot pressing them. The resulting specimens were analyzed chemically and phases present were identified by X-ray diffraction methods. A Philips Norelco Geiger counter spectrometer was used for identification of components and for measurement of lattice constants. Filtered copper radiation was used for all X-ray work. Electrical resistivity and density measurements were carried out at room temperature. The stable diboride, HfB2, will be described first. Stoichiometric quantities of boron and metal were heated to approximately 2000°C during hot pressing. The reaction product was shown by X-ray diffraction methods to be isomorphous with ZrB2 (space group Dlgh; P6/mm). Values of lattice constants of HfB2 compared with those of ZrB2 are shown in Table I. The calculated density of HfB2 is 11.2 g per cc, compared with a measured (pycnometric) value of 10.5 g per cc. HfB2 specimens prepared under a wide variety of conditions (including variations in initial Hf-B ratios) showed only insignificant variations in lattice constants, indicating a very narrow range of homogeneity. Like ZrB2,7 HfB2 is an excellent electrical conductor. The resistivity at room temperature of hot-pressed samples, approximately 85 pct dense, is 12 microhm-cm. This compares favorably with the electrical resistivity of 10 mi-

Jan 1, 1954

By E. N. Smith, J. C. Redmond

The increasing need for materials capable of withstanding higher operating temperatures for various applications such as gas turbine blading and other parts, rocket nozzles, and many industrial applications, has brought consideration of cemented carbide compositions. The well known usefulness of cemented carbides as tool materials is attributable to their ability to retain their strength and hardness at much higher temperatures than even complex alloys. However, it has been found that the temperatures encountered in cutting operations do not approach by several hundred degrees1 those involved in the applications mentioned above where the interest is in materials possessing strength and resistance to oxidation at temperatures of 1800°F and above. At these latter temperatures, the tool type compositions which are made up essentially of tungsten carbide are found to oxidize very rapidly and to produce oxidation products of a character which offer no protection to the remaining body. As a further consideration, the density of the tungsten carbide type compositions is high, from about 8.0 to 15.0. The refractory metal carbides as a class are the highest melting materials known as shown by Table 1 which summarizes the available data from the literature for the carbides of the elements which are sufficiently available for consideration for these uses. The density is also included in the table, since as mentioned above it is an important consideration in many of the applications for which the materials would be considered. It has been established that in the tool compositions the mechanism of sintering with cobalt is such as to result in a continuous carbide skeleton and that the properties of the sintered composition are thus essen- tially those of the carbide.2 On the hypothesis that this mechanism holds to a greater or less degree in cementing most of the refractory metal carbides with an auxiliary metal, it appears from Table 1 that titanium carbide compositions would offer possibilities for a high temperature material. Titanium carbide has extensive use for supplementing the properties of tungsten carbide in tool compositions. Although the literature contains several references to compositions containing only titanium carbide with an auxiliary metal,3,4,5,6 it may be inferred from the meager data that such compositions were deficient in strength and were considered to have poor oxidation resistance.7 Kieffer, for instance, reports the transverse rupture strength of a hot pressed TiC composition at 100,000 psi as compared to up to 350,000 psi for WC compositions. The work described herein was undertaken to determine the properties of compositions consisting of titanium carbide and an auxiliary metal and to improve the oxidation resistance of such compositions. It appeared possible that the inclusion of one or more other carbides with titanium carbide might improve the oxidation resistance and also that this might be more desirable than other means from the point of view of maintaining the highest possible softening point. Consideration of the available carbides in Table 1 suggests tantalum and columbium carbides because of their high melting points and general refractoriness. The work on improving oxidation resistance was concentrated on the addition of tantalum carbide or mixtures of tantalum and columbium carbide. The auxiliary metals used included cobalt, nickel and iron. It was also desired to learn the general physical properties of these compositions. Experimental Procedure The compositions used in this study were made by the usual powder metallurgy procedure applicable to cemented tungsten carbide compositions. The powdered carbide or carbides and auxiliary metal were milled together out of contact with air. In some cases cemented tungsten carbide balls and in other instances steel balls were used to eliminate any effect of tungsten carbide contamination. A temporary binder, paraffin, was then included in the mix and slugs or ingots were pressed with care to obtain as uniform pressing as possible. The ingots were presintered and the various shapes of test specimens were formed by machining, making the proper allowance for shrinkage during sintering. Thereafter the shapes were sintered in vacuum at temperatures of from 2800 to 3500°F. Final grinding to size was carried out by diamond wheels under coolant. The titanium carbide used contained a minimum of 19.50 pet total carbon and a total of 0.50 pet metallic impurities as indicated by chemical and spectrographic analysis. It was found by X ray diffraction examination with

Jan 1, 1950

By J. M. Bugbee

THE engineer and the conservationist agree that effective water drive is the desirable reservoir production mechanism. Water drive may result either from the expansion of edge water, the reservoir water bordering an oil pool, or from the artesian flow of edge water from the outcrop. Thus, the extent of the reservoir has an important bearing upon both the rate and the ultimate quantity of water influx to an oil pool. Lens-type reservoirs are generally recognizable, but the complete structure of the more important domal types, having possible limitations from crestal and synclinal faulting, is not well understood. The delineation from cores, electrical logs and exploitation phenomena of the crestal portions of reservoirs is increasingly exact. This paper suggests that inference from these factual pictures, combined with the scattered well and geophysical data of the synclines and with consideration of the dynamics of structural formation, may be applied to solving the complete geologic structure. Since faulting on the domes and in the synclines may effectively seal and thus limit the size of a reservoir and bar additional water influx, consideration of geologic structure and its possible effects is essential to complete analysis and prediction of reservoir performance.

Jan 1, 1942

By W. R. Johnson, M. Hansen, John M. Parks

AS part of a research project sponsored by the Signal Corps Engineering Laboratories, which had the objective of obtaining a magnet wire of good conductivity and low temperature coefficient of resistance, a comprehensive literature survey, supplemented by experimental work, revealed that a linear relationship exists for solid-solution alloys between the electrical conductivity, K, and the temperature coefficient, a, as expressed by the equation: k = a/ß where ß is constant for the solvent metal and a - per°C. tR0 It has long been known that the electrical conductivity at a given temperature and the temperature coefficient of resistance of binary alloys are related to their constitution by the LeChatelier-Guertler rules, as illustrated by Figs. 1 and 2: Rule 1—In alloy systems consisting of a heterogeneous mixture of two phases, the electrical conductivity and temperature coefficient vary as a straight line, if the composition of the alloys is given in volume percentage, Fig. 1. Rule 2—In solid solutions, the electrical conductivity and temperature coefficient are always lower than those of the solvent metal, and usually a considerable decrease occurs with the first small percentage additions of the solute metal, Fig. 2b. If the two components form a continuous series of solid solutions, the electrical conductivity and temperature coefficient curves take the form of a U-curve, Fig. 2a. That some kind of proportionality exists between electrical conductivity and temperature coefficient of resistance is implied by the LeChatelier-Guertler rules and by study of data such as those given by Smith and Palmer,' Fig. 3. Dellinger2 in 1910 first recognized this relationship in a number of commercial copper wires, ranging in conductivity from 94 to 100.7 pct I.A.C.S. He gave the ratio of temperature coefficient to the percentage of conductivity as a constant, C = 0.003939. A year later, Lindeck observed that the linear relationship was valid for a wider range of conductivity in "various sorts of copper," and concluded that the product of resistivity and temperature coefficient was 6.78x10-5 1.5 pct. Since then, this relationship seems to have been entirely ignored. Conductivity-Temperature Coefficient Relationship If the electrical conductivity of copper solid-solution alloys with phosphorus, silicon, arsenic, antimony, aluminum, nickel, manganese, and iron is plotted against the temperature coefficient of these alloys, the diagrams in Figs. 4 and 5 are obtained. Similar data were found with copper-rich solid solutions containing magnesium, cobalt, and titanium,'" as shown in Fig. 6. In all cases, a linear relationship exists. The point representing the highest

Jan 1, 1952

By C. G. Goetzel

Until recently porous bronzes have found many applications for self-lubricating bearings in the automotive, electrical, household appliance and general machine industries. The bulk of an annual production of several million pounds of copper powder had gone into the manufacture of these articles, of which by now more than a billion are in service. However, the war has brought severe curtailment of these bearings because of the scarcity of the two main constituents, copper and tin. The development of substitute materials of equal or superior properties has led to a large-scale replacement by products made from iron powder. In spite of the diminished interest in powdered copper-tin alloys caused by this trend, it was believed worth while to investigate some mechanical properties of these materials as a reference base for substitutes. In addition, experiments using the hot-press method were incorporated to investigate possibilities of saving vital equipment or opening new fields of applications. It must be assumed that by this time the powder metallurgy process of making porous bronzes, a development that found its first industrial applications more than 10 years ago, is well known in engineering. The patent literature and bibliography is volu- minous, most publications referring to porous, self-lubricating bronzes, containing about 10 per cent tin and I to 5 per cent graphite, with porosities in the range of 25 to 35 per cent.l-7 The excellent antifriction properties of these bearings, caused by the uniform impregnation with oil, are dependent on the interconnection of the pores and the uniform distribution of the graphite inclusions. The sintering mechanism of porous bronze, with its structural changes during the transformation of the metal powder into the sintered bearing has been shown in colored photomicrographs by Hall.* Diffusion between copper and tin was found to begin within one minute, when tin-rich transitory phases were formed. After 25 min. a homogeneous matrix of alpha was reached for an alloy containing 9.5 per cent tin and 6 per cent graphite. Price, Williams and Garrand,9 studying certain metal powder combinations in which sintering is accompanied by the cementing action of a liquid phase, including a 90-10 bronze sintered at 925°C., have found that if the treatment is carried out within the liquidus and solidus temperature range of the system, a peculiar process of alternate solution and precipitation occurs. The particles of the major solid constituent are dissolved in the minor liquid phase, but thereafter are reprecipi-tated on certain nuclei, which develop into large grains, usually rounded.

Jan 1, 1945