By J. W. Spretnak, G. W. King

THE crystallography and morphology of 0-Al,Fe precipitates in an A1 + 0.5 wt pct Fe alloy have been studied by transmission electron microscopy. The alloy was cast in cylindrical ingots, 15 cm in diameter and 60 cm in length, and cooled slowly. The measured composition was 0.527 wt pct Fe, 0.001 wt pct Mg, and 0.003 wt pct Cu. Spectrographic analysis revealed no additional trace impurities. Thin slices were cut from the ingot and reduced by more than 95 pct by rolling to a thickness of 0.1 mm with no intermediate annealing treatments. These thin sheets were then vacuum-annealed for 1 hr at 612°C and air-cooled in their capsules. Thin foils for examination in the electron microscope were prepared by electropolishing. The precipitate is found in the form of oval platelets on the (110) planes of the matrix. The major axes of the platelets are parallel to the (110) directions of the matrix, and vary in length from 1/2 to 2 p. The thickness is about 1/10 p. Examples of platelets, both in the plane of the foil and normal to the foil, are shown in Figs. l(a) and l(b), respectively. lack' found that ?-A13Fe (more correctly All13Fe4) belongs to the monoclinic system. Using Black's structural data and simultaneous electron-diffraction patterns from the matrix and precipitates, the habit planes and directions were determined to be: (00l)? || (110)Al [100]? || [001]Al The orthogonal crystallographic axes of the precipitates are accurately in the habit plane, while the measured coincidences of the directions are only within 10 deg. The major axis of the platelet is parallel to [010] in the 0. This orientation corresponds to the direction of nearest registry of the lattices.

Jan 1, 1964

By M. Kaufman, A. E. Palty

THE mechanical properties of an alloy under given test conditions are in the main determined by the grain size and the phases present, their distribution and temperature-time dependence. Alloys intended for use at elevated temperatures, especially multiphase alloys depending upon precipitation reactions for strengthening, are particularly susceptible to changes in the phases present. Unfortunately, for modern superalloys, very little published information exists which relates the mechanical properties to the basic structural variables. The present work is an effort to do this for an alloy widely used in aircraft gas turbines and related applications, Udimet 500.* The mechanical properties inves- two heats is within the normal specifications for the alloy. However, the elements which most strongly influence the phase reactions, C, Ti, Al, and Mo, are comparable in the two heats. There was no intentional addition of boron, but normal pickup is about 0.002 pct. The vacuum-melted material was received in the form of centerless ground wrought bar stock % in. diam. PHASE STUDIES A) Methods—Two methods were used to determine the phases present: X-ray diffraction measurements on electrolytically digested residues, and microscopic examination. No single commonly used electrolyte will reveal all the phases that may be present; therefore, two complementary acids were selected: HCl and H3PO4. The necessity for this will be shown below in the results. The acid concentrations used were 10 pct HC1 in alcohol and 10 pct H3 PO4 in water. The current density was maintained below 0.1 amp per sq in. Residues were rinsed and separated by centrifuga-tion. X-ray diffraction patterns were obtained in a 114 mm Debye-Scherrer type camera using cobalt radiation. A temperature of 2250°F was selected to obtain as complete solutioning of phases as possible without encountering incipient melting. Specimens were

Jan 1, 1961

By Eugene A. Stephenson

Critical analyses of the work expended in producing oil by the utilization of gas energy have appeared in the publications of Shaw,' Pierce and LewisI2 and Herold,3 authors who have ably discussed the factors which must be taken into consideration in comparing energy consumed per barrel in various wells which are flowed by means of gas-lift. However, two distinct phases of oil production are concerned with the ratio of gas energy consumed to oil produced. One of these phases is the gas-lift, which utilizes the differential gas pressures for the purpose of flowing oil, whether these pressures be natural reservoir pressures or be induced by artificial compression of gas or air. The other phase has to do with prorating oil production in pools which are operated either as units, or are subject to such restrictions as those imposed at Oklahoma City by the Corporation Commission, or by similar controlling groups in other fields. An abundance of literature is available relative to the problems of flowing wells by gas-lift, but the first suggestion that the energy of the gas within the oil and gas pool might serve as a basis for proration, appeared in the timely article by Mc Williams.4 Much of the dissatisfaction with proration in certain fields arises because some operators feel that besides the hazard to the wells which accompanies the test, the method of allocating production on the basis of the " potential" gage is inequitable and gives some operators a distinct advantage over others.5 The most severe penalty may be exacted from the most progressive operators or those who attempt to produce their oil with a minimum quantity of reservoir gas. If no difficulties ever developed in drilling, shutting off water, or in well completion, it might

Jan 1, 1931

By E. M. Bennett

HISTORY In 1923 John Campbell Miles discovered the Mount Isa deposit after finding and submitting for assay some “unusual and heavy rocks”. Six months after submission he received the assays of his original samples which indicated high lead-silver values. The deposit area was isolated and unknown geographically and not served by even a rough country road. The isolation of Mount Isa coupled with the depression years had a strong influence on the rate of development of the area. These two factors resulted in a slow amalgamation of the early individually held leases and the lack of ready finance to begin serious mining of the deposit. Initially, surface lead-silver-zinc mineralisation was proved and diamond drilling to shallow depths showed the presence of a viable orebody. Limited underground development work was initiated and open cutting associated with glory holing commenced. Due to the metallurgical problems associated with the ore and due also to unsuspected change in metallurgical conditions as the ore deepened into what is known today as the transition zone, major problems of finance were recurring at frequent intervals. Despite low metal prices the development of the mine continued due to continuing infusion of capital. During the 1939-45 war years a surplus of lead was being produced in Australia, but a grave shortage of copper was apparent. About this time copper ore had been found to the hanging wall of the then known major lead orebodies. At the request of the Australian Government, lead production ceased and copper production commenced.

Jan 1, 1970

By LeRoy Scharon

EACH year it becomes apparent that geophysical activities in the fields of mining and engineering are increasing in the number and variety of applications. Many mining companies are including, as part of their exploration programs, geophysical surveys. The value of geophysics in highway and structural foundation investigations has been realized and is now an important part of subsurface investigations in conjunction with soil and rock borings. United States of America One of the major orebody discoveries of the year is that of the Grace mine near Morgantown in Berks County, Pa. This orebody, now under development by the Bethlehem Steel Co., was discovered by an airborne magnetometer survey carried out by the Aero Service Corp. of Philadelphia. The orebody, the geological occurrence of which is similar to those existing at Cornwall, Pa., was found at a depth of 1500 ft under a cover of Triassic sediments and is reported to have a reserve of well over 100 million tons. Shaft sinking and other construction work has started at the site. Resistivity work was carried out at proposed dam sites in New York and in connection with the search for fluorspar veins in Kentucky. Spontaneous polarization investigations were pursued in the Appalachian region at various localities from North Caro¬lina up into Virginia. This work was done in connection with the search for sulphide-bearing structures. Several indications were proven by subsequent drilling to correspond to unknown sulphide deposits, a few of these occurring in the vicinity of properties long under exploitation. Refraction seismic methods applied to bedrock depth determinations as related to water problems on the Marquette Range and the extension of the. regional gravity survey on the Menominee Range to learn the major structural features of the area have been reported by, Lloyal O. Bacon. A gravity survey has been completed in the vicinity of Tioga, Bradford County, Pa. with a gravity profile being observed from Tioga east to the Delaware basin. The Indiana Geological Survey is concerned with a state-wide gravity survey. Judson Mead, University of Indiana, reports that the bulk of the State Survey's geophysical work, however, has been "seismic refraction work in connection with drift thickness problems. The survey has made almost 1000 determinations in areas of moderately thick drift. The results of this work are of interest to both the coal mining industry and to the stone industry." In the southeastern Missouri lead belt, magnetic electrical resistivity, and electromagnetic applications for the discovery of new lead deposits have been used with success. A gravity survey of the residual-barite deposits in Washington County, Mo., was made during the summer season with preliminary computations of tonnages checking with tonnages mined. Robert M. Dryer, of the University of Kansas has had considerable success in mapping structural features in southwestern Kansas with the gravity meter and is now engaged in tracing shoestring sands in eastern Kansas by resistivity surveys. Several, foundation sites were investigated in greater St. Louis using electrical resistivity and seismic refraction methods with success. A minimum amount of drilling data was available for checking and interpreting the geophysical results (Fig. 1). It is to be noted that geophysical methods are finding a place in subsurface investigations for highway and foundation problems. Interest has been so keen in this field that the American Society for Testing Materials, at its annual meeting in June of this year, devoted one session of its symposium on surface and subsurface reconnaissance to geophysical papers involving the application of the electrical resistivity and seismic refraction methods to subsurface studies. At least three major mining companies in the United States have entered the field recently in geochemistry. The program of research and development of geochemical techniques by the U. S. Geological Survey continues. Experimental field projects were conducted over lead-silver, cobalt, copper and zinc deposits in Idaho, Oregon, California, Wisconsin and Montana. Similar experiments were carried on by M. P. Nackowski in the Illinois-Kentucky fluorspar district and in the Tri-State Zinc district by R. Maurice Tripp with favorable results. Geophysical activities of the U. S. Geological Survey for 1951 were extensive and varied. About 21,000 miles of airborne magnetic and 10,000 miles of airborne radioactivity traverse were flown in 1951 by the U. S. Geological Survey. A total of 35,000 miles of aeromagnetic traverse were compiled, 57 aeromagnetic maps were published and 14 preliminary maps were placed on open file. Airborne surveys were made in Aroostook County, in the Katahdin and Dead River areas in Maine; in northwest Washington; over the Mother Lode district in California; in northeastern and northwestern Minnesota; and in the New York-New Jersey highlands. Of special interest were the surveys in Washington, where highly magnetic Eocene lavas gave information on structures in the overlying Miocene sedimentary rocks and in northeastern Minnesota over the Duluth gabbro. The latter survey was made following the discovery of nickel-copper mineralization in the gabbro near its contact with the Virginia slate. The principal ground geophysical surveys for metalliferous deposits and related purposes were made in the Colorado Plateau region, where electrical surveys assisted in prospecting; in Aroostook County, Maine, where ground magnetic surveys, following aeromagnetic surveys, have permitted tracing

Jan 1, 1952

By Frank H. Kingdon

and eventually we would have trouble. That is, these little localized overstresses may not be important if the structure is loaded a few times, but may be important if the structure is loaded many thousands of times. The existence of localized stress has been demonstrated by direct experimentation with delicate extensometers by the elaborate investigations of Coker. Localized stresses four, five, and six times those that we would get by the ordinary laws of mechanics exist in most of our structures. These stresses, ordinarily, under steady load do no damage but if they are repeated many times may start progressive failure. So far, we have seen no failure that could not be explained by localized high stress at a nick, a crack, a point where one heat treatment stopped and another began, or where there was local faulting, or any one of a dozen causes. In the case of drill rods, the actual distribution of stress must be different from that which any mathematical analysis could predict. It would seem that the spread of damage from the localized overstresses, so far as we can see now, explains the phenomenon known as fatigue. The Ideal Drill Steel By Frank H. Kingdon The essential qualities of a drill steel are: (I), It must be easily forged; (2), the forged bit end must permit easy heat treatment to obtain hardness to resist chipping; (3)) the bar or body must be stiff to resist bending or twisting and yet tough to resist shock and vibration, with resulting breakage, (4), the forged shank end must be easily heat treated to obtain hardness with great toughness. Minor requirements are that the bit and the shank are in alignment with the body; that the shank is of the proper shape and length and the shank collar or lugs of the proper diameter and length; that the hole is free from obstruction; that the striking end of the shank is flat and square; that the bit is of the proper shape, with the cutting and reaming edges formed full and to the required size; that the reaming edges are concentric with the axis of the steel, and that there are no sharp corners at the shoulder where the bit blends into the body. The essential qualities of a bit, are: That its shape be such that maximum cutting speed can be maintained for as great a distance as possible before wear of the gage and cutting edge reduces the speed of penetration to a point where a change of steel is made necessary; that the size or diameter of the drill hole corresponding to the gage of the bit can be maintained with the least possible reduction as the depth of the hole increases, and that the bit can be correctly and readily formed and heat treated. The following features of bit design require attention: Shape,

Jan 1, 1922

By S. A. Swensrud

REPORTS from smelters show that all were so occupied with the in- creased production called for during the first half of the year that little time was devoted to metallurgical developments. Improvements which have been made such as gas-firing and other alterations ill the reconstructed Hayden smelter, will require time for reporting. The labor situation at all plants held the most prominent place and put all other problems in the background. Coming events of considerable importance concerti the construction of two new smelters. The Chino unit of Nevada Consolidated which has long had its concentrate smelted at the El Paso plant of the American Smelting and Refining Co. is constructing its own smelter at the property in New Mexico. The newest Phelps Dodge development of the Clay ore body at Morenci, Ariz., will call for another new smelter.

Jan 1, 1938

By AIME AIME

AN ENGINEER with as varied geographical experience as H. J. Brown does not often specialize on one particular thing all of his professional life. For forty years he has been engaged in gypsum mining, manufacturing, plant design, construction, and operation. Not only is it his work, but he says it is his hobby as well, though membership in three yacht clubs might belie that statement. New England's new representative on the A.I.M.E. Directorate, who was born in New York, Dec. 20, 1879, went to the Lawrence Scientific School at Harvard at the turn of the century. He tried journalism for a year, with the Boston News Bureau and associated financial

Jan 1, 1940

By R. J. Lutton

Empirical data from 91 rock excavations have been used to construct a family of slope curves on a chart relating excavation height and inclination. The highest and steepest slopes from each excavation are plotted and connected by a line. The 31 1ines appear to establish one or two geometrical slope fields through which the curves are projected. The curves apparently represent a lumped eflect of many factors too complex to be considered individually. Important factors such as geological structure or ground-water conditions can dominate the picture, but where these factors do not overshadow others, the slope chart should be useful for estimating or checking optimum inclination. The U.S. Army Corps of Engineers (USAE) has been engaged since 1962 with the U.S. Atomic Energy Commission in a joint research program to develop nuclear excavation technology. The Corps is responsible for collecting the requisite data on engineering and construction problems associated with nuclear excavation. The ultimate objective is to develop a capability to use nuclear explosives as a construction tool on public works projects such as harbors and canals. The present study on empirical inclination-height curves for conventionally excavated slopes is an outgrowth of an investigation' sponsored by the USAE Nuclear Cratering Group on applicability of data from existing excavations in establishing guides for engineering judgment in crater excavation. Data were generously contributed by over 50 mining companies among other organizations. Inasmuch as several companies preferred that their contribution be anonymous, all data are treated so here. Some Factors Affecting Stability Many factors affect or are suspected of affecting the stability of excavated slopes, e.g., adverse structural orientation, degree of structural ordering, ground water, climatic conditions, mechanics of excavation, and plan-profile configuration. Such factors are lumped together in developing a slope chart. Obviously geological structure and ground water can overshadow all other factors. Where such is the case, the simplification of slope charts may give an erroneous picture (not conservative enough). A further complication results from the fact that the concept of stability may vary according to the use of the excavations. For example, slope adjustments that would be regarded as failure in a powerhouse excavation, might be tolerable in a mining operation. Mine slopes are continually being modified by further excavation, and instability that would develop in a similar permanent excavation slope over a period of years might not have time to develop in a mine. Inclination vs. Height Charts Charts of inclination vs. height for particular formations or conditions have been used in the past as an aid for designing excavation slopes. Some of these have been based upon empirical analyses of collections of data and experience. MacDonald" and Lane have presented slope tables and charts for excavated and natural slopes in relatively weak sandstone and shale. Coates' has shown an inclination-height chart for slopes in incompetent rock. Most organizations have developed slope design criteria which relate bench widths, heights, and inclinations to use in various rocks. Slope data collected in present studies can be similarly used to develop inclination-height charts; however, a plot of all slopes on such a chart shows very little because of the wide spread of the data. Reasons for the dispersion of points are: (1) many slopes are not carried at optimum inclination, particularly in mines where maintaining roadways and following irregularities of ore bodies are more important than achieving steep inclinations; (2) many engineers and geologists with varied backgrounds and viewpoints have been involved in designing these slopes; and (3) each slope is characterized by a unique combination of factors affecting stability and in turn optimum inclination. Significant curves can sometimes be constructed where the points can be grouped into related clusters from the same excavation. The essence of this approach appears when only two slopes from each excavation are considered—the highest slope and the steepest slope, connected by a line segment (Fig. 1). This reduces considerably the usable data because in many cases only one of these two slopes is available. Nevertheless, the concession seems justified. Construction of Slope Curves Ninety-one pairs of points and connecting line segments were assembled in this study. The line segments were assumed to approximate a geometrical slope field (Fig. 2), and a family of curves has been visually projected through to represent the slope field. It should be

Jan 1, 1971

By Stuart H. Ingram

The term lightweight aggregate implies material which may be substituted for the usual rock, sand and gravel commonly used as the major part of concrete, but distinguished by being much lighter in weight. Background The art of making and using concrete is old and well developed. Research and experience have pretty well determined the qualities necessary in its constituents, and time has tested theories and applications. Elaborate specifications and tests have been devised and generally adopted governing all phases of concrete work, from selection of material, through engineering design and down to mixing and placing. Standard practices have become routine to executives and laborers, and operations have been simplified and costs lowered. Though many lightweight aggregates meet the basic specifications necessary for usefulness, their physical qualities are so different that they fiequently will not pass standard tests, and some of them cannot be mixed and placed with the usual formulas for water and slump. As a rule their use produces a concrete with a lower modulus of elasticity which requires design change, and being produced in much smaller quantities than ordinary aggregate, production costs are higher. This latter works in a vicious circle to restrict their use and maintain prices that are not competitive, except as against each other. Increased Demand In spite of such handicaps consumption has grown steadily for the past two decades and is apparently growing even faster today. It is evident that lightweight concrete must have better qualities, and be sufficiently better to Overcome the higher cost and the other difficulties and disadvantages pertinent to the use of a new and different material in an old industry. Hence the study of its main ingredient should be of interest to all engineers. Our group has a double interest in the subject since most of the materials which have been used as sources of lightweight aggregate are either mined, Or are by-products of mining operations. We are directly interested in their production as well as their use, and since available supplies of materials suitable are limited, the increasing use, and rising demand, make the discovery of new Or or the development of processes to adapt other natural materials to this use, a promising field; and one in which our profession should take an active part. Recent Development Descriptions of ancient work contain references to the use of spalls of tuffs Or pumice in concrete masonry, but it is only since the nineteen twenties that serious attempts have been made to produce and market lightweight aggregates. A period of rapid advance in theory and practice in cements, mortars and con-

Jan 1, 1948

By Stuart H. Ingram

The term lightweight aggregate implies material which may be substituted for the usual rock, sand and gravel commonly used as the major part of concrete, but distinguished by being much lighter in weight. Background The art of making and using concrete is old and well developed. Research and experience have pretty well determined the qualities necessary in its constituents, and time has tested theories and applications. Elaborate specifications and tests have been devised and generally adopted governing all phases of concrete work, from selection of material, through engineering design and down to mixing and placing. Standard practices have become routine to executives and laborers, and operations have been simplified and costs lowered. Though many lightweight aggregates meet the basic specifications necessary for usefulness, their physical qualities are so different that they fiequently will not pass standard tests, and some of them cannot be mixed and placed with the usual formulas for water and slump. As a rule their use produces a concrete with a lower modulus of elasticity which requires design change, and being produced in much smaller quantities than ordinary aggregate, production costs are higher. This latter works in a vicious circle to restrict their use and maintain prices that are not competitive, except as against each other. Increased Demand In spite of such handicaps consumption has grown steadily for the past two decades and is apparently growing even faster today. It is evident that lightweight concrete must have better qualities, and be sufficiently better to Overcome the higher cost and the other difficulties and disadvantages pertinent to the use of a new and different material in an old industry. Hence the study of its main ingredient should be of interest to all engineers. Our group has a double interest in the subject since most of the materials which have been used as sources of lightweight aggregate are either mined, Or are by-products of mining operations. We are directly interested in their production as well as their use, and since available supplies of materials suitable are limited, the increasing use, and rising demand, make the discovery of new Or or the development of processes to adapt other natural materials to this use, a promising field; and one in which our profession should take an active part. Recent Development Descriptions of ancient work contain references to the use of spalls of tuffs Or pumice in concrete masonry, but it is only since the nineteen twenties that serious attempts have been made to produce and market lightweight aggregates. A period of rapid advance in theory and practice in cements, mortars and con-

Jan 1, 1948

By H. Eklund, R. T. Hukki

This article presents a simple arithmetic derivation for the relationship between sharpness of classification and circulating load, as well as world-wide industrial data which are compatible with the derived equation. It is shown that the sharpness of classification decreases with increasing circulating load. Based on the evidence available a comparison is presented between the performance of the present-day hydraulic classifiers. In a continuously operated closed circuit grinding system the tonnage and the fineness of the components may be indicated as follows: Eq. 8 expresses the relationship between sharpness of classification and circulating load in closed grinding circuits. If CL = 0, E = 100% according to the definition used. This, however, is a purely theoretical case because any apparatus to be called a classifier must produce the conventional two products. Furthermore, if CL = m, E =0%. In order to visualize the meaning of Eq. 8, the effect of factors d (fineness or percentage of under-size of classifier overflow at size x) and b (fineness or percentage of undersize of classifier sands at size x) should be studied. By the most rigid standard, factor d should be given the value of 100%. By so doing the size of classification is defined as that screen size x through which 100% of the classifier

Jan 1, 1965

By R. D. Leitch, W. P. Yant, R. R. Sayers

In 1924, the United States Public Health Service was requested to undertake a special study of stream pollution. The Public Health Service asked the United States Bureau of Mines to take up the study because the training and experience of the personnel of the former was considered not to be as well suited to this type of investigation as that of the Bureau of Mines. Under H. Foster Bain, then Director of the Bureau, field investigations were begun in the spring of 1925. Along with mine-drainage wastes, the problem of gas-house and coke-oven waste was investigated in the laboratory and a method of treatment by sodium hydrate and benzol was found to be promising. The idea was obtained by A. C. Fieldner, chief engineer of the Bureau Experiment Stations, on a trip to Germany in 1924. He saw a practical application of the process, but obtained no information as to definite chemical or mechanical processes. Because of the then pending American patent applications by the German firm, we made no attempt to develop our findings further. Shortly afterward, a similar method of treatment was developed in the United States,' and since that time we have devoted our attention entirely to mine drainage. This paper is a presentation of some general facts and information gathered during the past five years on coal-mine drainage. Scope of Work There was such a diversity of opinion at the time this work was begun, on the whole subject and apparently so little accurately known, that it was decided to undertake a basic study from which first, certain definite information might be evident, and second, what might be considered

Jan 1, 1931

By John C. McDonald

This report is a continuation of an earlier one with a similar titlell to which the reader is referred for such details of procedure as do not appear here. A brief summary will be given of the objects and methods of the research at this time. It was pointed out in the previous paper that properties of magnesium alloys, as reported by different workers, often differ. This was thought to be due to differences in the preparation of the specimens tested. The ideal way to compare alloys would be to prepare each of them in so many ways that reasonable assurance would exist that the best properties of each alloy had been developed. The alloys would then be compared on the basis of these properties. The treatment actually given the alloys of these studies is necessarily a compromise with completeness. Nevertheless, enough treatments have been given so that a considerable degree of assurance exists that the properties obtained are representative of the alloy as such, and not merely of the manner in which it was worked and heat-treated. Procedure The alloys were cast in the form of cylindrical ingots, which were extruded into bar before being rolled. Some of the ingots were made in 2-in. diameter molds whereas all of the alloys of the previous paper were cast in 4.in. molds. For the larger ingots, the extruded bar was 2 by 0.140 in.; lor the 2-in. ingots, it was I by 0.100 in. Preliminary work indicated that strip rolled from both sizes of the bars would have substantially the same properties. The bar was rolled at some temperature in the range 400' to 800°F., for a total reduction of 50 per cent. The temperature and reduction per pass were so selected that no cold cracking occurred, but were such as to leave the metal in a semihard condition. The hot-rolled metal was annealed at several temperatures in the range 400' to 800°F.; it was also cold-rolled, and given solution and aging treatments. Two standard test bars corresponding to each treatment were pulled in tension, and the average was obtained. Twelve treatments, in all, were given each alloy. The properties of the annealed specimen having the highest percentage of elongation were selected to represent the alloy in the annealed condition. The properties of the cold-rolled specimen having the highest yield strength were selected to represent the alloy in the cold-rolled condition. These properties were then plotted against percentage composition by analysis. Smooth curves were drawn among the points, thus graphically averaging the results over the entire range studied. The percentage of elongation in the cold-rolled state was not plotted, since it was always low, and varied in an irregular manner with composition. Alloys Studied Magnesium-calcium Alloys.—Fig. I presents the results on the alloys of the rnag-

Jan 1, 1941

By John C. McDonald

This report is a continuation of an earlier one with a similar titlell to which the reader is referred for such details of procedure as do not appear here. A brief summary will be given of the objects and methods of the research at this time. It was pointed out in the previous paper that properties of magnesium alloys, as reported by different workers, often differ. This was thought to be due to differences in the preparation of the specimens tested. The ideal way to compare alloys would be to prepare each of them in so many ways that reasonable assurance would exist that the best properties of each alloy had been developed. The alloys would then be compared on the basis of these properties. The treatment actually given the alloys of these studies is necessarily a compromise with completeness. Nevertheless, enough treatments have been given so that a considerable degree of assurance exists that the properties obtained are representative of the alloy as such, and not merely of the manner in which it was worked and heat-treated. Procedure The alloys were cast in the form of cylindrical ingots, which were extruded into bar before being rolled. Some of the ingots were made in 2-in. diameter molds whereas all of the alloys of the previous paper were cast in 4.in. molds. For the larger ingots, the extruded bar was 2 by 0.140 in.; lor the 2-in. ingots, it was I by 0.100 in. Preliminary work indicated that strip rolled from both sizes of the bars would have substantially the same properties. The bar was rolled at some temperature in the range 400' to 800°F., for a total reduction of 50 per cent. The temperature and reduction per pass were so selected that no cold cracking occurred, but were such as to leave the metal in a semihard condition. The hot-rolled metal was annealed at several temperatures in the range 400' to 800°F.; it was also cold-rolled, and given solution and aging treatments. Two standard test bars corresponding to each treatment were pulled in tension, and the average was obtained. Twelve treatments, in all, were given each alloy. The properties of the annealed specimen having the highest percentage of elongation were selected to represent the alloy in the annealed condition. The properties of the cold-rolled specimen having the highest yield strength were selected to represent the alloy in the cold-rolled condition. These properties were then plotted against percentage composition by analysis. Smooth curves were drawn among the points, thus graphically averaging the results over the entire range studied. The percentage of elongation in the cold-rolled state was not plotted, since it was always low, and varied in an irregular manner with composition. Alloys Studied Magnesium-calcium Alloys.—Fig. I presents the results on the alloys of the rnag-

Jan 1, 1941

By J. H. Polhems, R. B. Brackin, D. B. Grove

THE heavy media separation process plays an outstanding role in the concentration of 4000 tons of zinc ore per day at the Mascot mill of the American Zinc Co. of Tennessee. Of the total tonnage, 72 pct is treated in the heavy media separation plant to reject 56 pct of the ore as a coarse tailing, which has a ready market. Concentrates from this separation are beneficiated further by jigging and flotation. Approximately 25 pct of the total zinc concentrate production is made in the jig mill. Jig tailings are ground and pumped to the flotation circuit where the balance of the production is made. Fig. 1 shows a generalized flowsheet of the mill. The Mascot ore is a lead-free, honey-colored sphalerite in dolomitic limestone, with lesser amounts of chert and some pyrite. A mineralogical analysis is given in Table I. After 10 years of successful operation with galena medium and treatment of nearly 10,000,000 tons of ore, a decision to convert to ferrosilicon was made early in 1948 because of the increasing price of galena and consequent high operating costs. The conversion was made on Nov. 6, 1948, and the results obtained since that time have shown remarkable improvement over those made with galena. The Table I. Mineralogical Analysis of Mill Feed, Pct Calcium carbonate 49.5 Magnesium carbonate 35.2 Iron oxide and aluminum oxide 1.5 Zinc sulphide 4.5 Insoluble 9.3 100.0 Table II. Comparative Data, Galena and Ferrosilicon Ferro- Diner-Gelenaa siliconb ence Operating costs per ton milled, ct. 21.21 9.12 12.09 Medium consumption per ton milled, lb 0.80c 0.15 0.65 Reagent consumption per ton milled, lb 0.45 0.02 0.43 Tailing assay, pct Zn 0.310 0.297 0.013 Concentrate. oct Zn 12.08 10.33 1.75 Heavy medla ieparatlon recovery. pct 89.38 90.22 0.84 Mill feed rate, tons per hr 153 166 13 Heavy mesa separation feed rate. tons per hr 100 10 0 Tons milled per heavy media separation man shift 350 620 270 Mill feed to coarse tailings, pct 51.0 56.7 5.7 Lost mill time, pct 5.6 5.0 0.6 Power consumption, kw-hr per ton 2.06 1.92 0.14 a 1947. " First 6 months of 1950. c Net consumption after deducting credit for reclaimed waste galena. Consumption of new galena was 1.320 lb per ton milled. For entire life of galena operation, a credit of 40 pct of the value of the new galena added was realized from the sale of waste galena. comparisons given in this report cover the first 6 months of 1950 as representing the ferrosilicon operation, and the year 1947 as representing the galena operation. This was the last full year in which galena was used exclusively and is representative of the best work done during the 10 years of operation with this medium. After only 2 years' operating experience, with ferrosilicon and treatment of 1,807,585 tons many advantages have been revealed and are summarized in Table 11. Development Prior to the introduction of the heavy media process, all the mill feed was crushed through 5/8 in. and treated by jigging. A finished tailing assaying 0.66 pct Zn was made on rougher bull jigs, and cleaner jig tailings were ground for treatment by flotation. The first test work on the sink-and-float method of mineral beneficiation was carried out at Mascot in 1935, using a 3-ft cone and galena medium for batch tests. The following year a 6-ft cone was installed for pilot-plant work. This unit became a part of the mill circuit on March 1, 1936, and handled a gradually increasing tonnage in the next 2 years as the process developed to the point where it could treat all the + 3/8-in. material in the mill feed. Coarse jigging was then discontinued on March 1, 1939, and all coarse tailings have been made by the heavy media separation plant since that time. Feed Preparation: The original feed preparation plant consisted of a drag washer followed by two 4x10-ft Allis-Chalmers washing screens. A surge bin and two additional 5x12-ft AC washing screens were added in 1943. Use of primary and secondary washing screens was found essential to provide the cleanest possible feed for the cone and thereby avoid excessive contamination of the galena medium. Improved washing was obtained by replacing the drag washer with a 7x20-ft Allis-Chalmers scrubber, shown in Fig. 2, which has been in service since May 1944. Throughout the life of the galena operation, delivery of extremely muddy ore to the mill overloaded the medium cleaning system, and it frequently was necessary to cut off the feed and clean the medium for several hours until its normal viscosity had been re-established. The cleaning circuit

Jan 1, 1952

By A. R. Krause, C. Laird

In order to establish whether or not there is a real temperature effect in fatigue (independent of environment) , poly crystalline copper and Cu- 7.9 A1 alloy have been cycled at 298° and 7° K in vacuo and the fatigue lives compared with those in air and in liquid nitrogen. The lives of both copper and the alloy were found to be highly temperature-dependent in the absence of environment. This result casts serious doubt on the validity of the cell structure hypothesis for stage I crack propagation as presently formulated, because it predicts that there should be no such tempevnture dependence. On the other hand, the plastic blunling process is consistent with the result. Effects of environment aside, the homogenization of slip which accompanies testing at low temperature, and at low strains, seems to be the main cause for increased fatigue life. At high strain amplitudes, the fatigue lives of wavy slip materials, typically copper, are independent of temperature.' It is well-known, however, that low-strain lives greatly as as the temperature of testing is decreased. By contrast, the lives of planar slip materials, such as Cu-7.9 pct A1 alloy, increase to an even greater extent with decreasing temperature throughout both the high and low strain ranges.1'2'5 The mechanism of this temperature effect is associated with the earliest stages of fatigue failure,'" crack nucleation, and stage I growth,"' which is slow propagation along slip bands to the depth of a few grain diameters. Such life behavior has been interpreted on at least two different bases. On the one hand, those interested in the temperature effect at high strain amplitudes1 believe that stage I growth occurs by the plastic blunting process of crack propagation.7'9 They explain the effect in planar slip materials by the homogenization of slip* which accompanies fatigue testing at low temper- atures and serves both to delay crack nucleation and to decrease the rate of stage I propagation. On the other hand, Holt and Backofen,2 who have studied the effect in low strain fatigue, believe that stage I growth can be interpreted by a cell structure hypothesis.10-12 They have challenged2 the conclusion that there is a real temperature effect in this regime of fatigue testing and have interpreted the increased fatigue lives almost entirely in terms of the "environmental-protective'' effect of the liquid nitrogen and helium baths used to obtain low temperatures. This interpretation by Holt and Backofen2 may offer a means of discriminating between these two mechanisms as currently formulated and used to explain stage I growth. On the basis of the plastic blunting process applied to stage I crack propagation,7* the low strain fatigue lives of both wavy and planar slip materials should be increased with decreasing temperature. This follows because both materials show increased slip homogenization in this strain regime."13 Consequently, crack nucleation in intensified bands will be delayed and the linking of such small cracks into larger stage I cracks will be difficult. In addition, the blunting process required to lengthen a stage I crack from the order of 2 to 10 (where the strain concentration of the crack begins to overcome the slip homogenization property of the material) will also be retarded. These delays will give rise to longer lives in both kinds of material. In contrast to the blunting hypothesis, no temperature dependence has been predicted on the basis of the cell structure hypothesis, because it is well-known that materials cycled at low temperature show no differences in type of dislocation structure for a given strain amplitude.18"20 If the lives of wavy and planar slip materials do show a temperature dependence when the environment is eliminated as a variable, then it is questionable whether cell structures per se have a fundamental role in fatigue fracture. Accordingly, specimens of copper and Cu-7.9 wt pct A1 have been cycled at 298° and 77°K in vacuo and the fatigue lives compared with those in air and in liquid nitrogen, in order to establish whether or not there is a real temperature effect in low strain fatigue. Since it is difficult to measure the strains in specimens when cycled in vacuo, S-N curves have been used as the basis of comparison. In studying the influence of temperature on fatigue life in ordinary environment, Holt and Backofen2 used the superior basis of E-N curves. However, they also published S-N curves and thus established the relationship between E-N and S-N curves. This relationship is used to support the S-N comparison reported in the present investigation. EXPERIMENTAL Materials. The copper employed in this investigation was of 99.99 pct purity and the cu-7.9 pct A1 was prepared from metals of the same purity. The stock, of 3 in. initial diam, was reduced in size by rolling

Jan 1, 1969

By Harry L. Brown, Philip E. Armstrong

Young's modulus doto ore presented for W, Mo. Ta. V, Cr. Ni, Ti, and Zr as a function of temperature up to about 0.7 of the melting points. A plot of reduced temperature us reduced modulus produces a general correlation except for titanium and zirconium. Young's modudlus data for some representatiue commercial graphites are given up to 2400°C. All results were obtained from longitudinal resonance-frequency measzrrements of 4-in. long samples, corrected for simultaneously measured thermal expansion. Comparison of poly crystalline and single-crystal tungsten behavior indicates that all the observed modulus values are frequencv -dependent at the higher temperatures. STATIC measurements of elastic properties of materials at elevated temperatures are extremely difficult to make since the elastic behavior is obscured by relatively large first-stage creep effects. Dynamic methods which avoid this difficulty by utilizing the measurement of the resonance frequency of a simple vibrational mode have been described in the 1iterature.l-3 The authors have extended the operating temperature range of this type of measurement to above 2000°C and have described the equipment elsewhere.~ The Young's modulus data presented here were obtained with this equipment, using samples about 4 in. long and 1/4 in. diam, supported horizontally at the center and excited to the fundamental longitudinal resonance frequency. Young's modulus was calculated by the formula: E = 4f2f2p where E = Young's modulus, / = frequency, 1 = length, and p = density. Dilatometric data were obtained simultaneously by optical measurements of the change of length of the sample. For the metals tested, an attempt was made to obtain modulus values that would be representative of the pure, strain-free, randomly oriented material. All of the graphites studied exhibited a high degree of elastic anisotropy, while the method assumes an isotropic homogeneous material. However , when the values for Young's modulus obtained for AUC graphite were compared with those taken from static measurements at room temperature they were found to be only about 4 pet higher. This is excellent agreement considering the low precision of modulus calculations from stress-strain curves. The difficulty in using data of apparent Young's modulus for anisotropic materials arises when the attempt is made to use these data and shear-modulus data to obtain Poisson's ratio. The results are usually meaningless and sometimes absurd.' RESULTS Table I lists the sources, impurity content, thermal history, and dilatometric constants of the metal samples that were investigated. All the metal samples were tested under a vacuum of 1 to 5 x 10-5 Torr. Where our dilatometric data agreed with previously published data, the table lists the previous values and the literature reference. Where no reference is given, the constants were determined from our dilatometric data. Table II presents the modulus data in units of millions of psi as a function of temperature in degrees centigrade. The numbers were obtained from curves fitted to the experimental data. For some types of calculations, such as those attempting to correlate creep data, the slope of the modulus curve is of interest, and this information also is reported in Table 11. It is always tempting to try to fit physical-property data into some general pattern and then use this pattern to predict the behavior of other similar materials. The general pattern for an elastic modulus of a metal seems to be a linear deoro- with increasing temperature Over the range between 0.1 and 0.4 of the melting temperature, then a progressive1y decreasing value up to the melting point. Metals appear to retain finite moduli

Jan 1, 1964

By Louis A. Rosales, Kanji Ono

The anomalous behavior of hydrogen in iron is examined and a new model is proposed It is postulated that hydrogen single and di-interstitials are in equilibrium with each other. When the binding enthalpy of the di-interstitial, B, is assumed to be about 10 kcal per mole, the predicted temperature dependence of the solubility agrees reasonably well with the reported data. Effective diffusiuity is calculated assuming the di-interstitials to be immobile. Since the number of mobile single interstitials is greatly reduced at lower temperatures, the effective diffusivity is decreased. A good agreement in the temperature dependence of diffusivity between theory and experiment is provided with B - 10 kcal per mole. The predicted diffusivity is also a function of total concentration of hydrogen and this appears to be Partly responsible for the large scatter in the reported data. HYDROGEN is known to form an interstitial solid solution with iron.''' At elevated temperatures, it has been well-established that hydrogen enters iron in the dissociated form and occupies the interstices, and that diffusion of hydrogen in iron is via the interstitial mechanism. The concentration, c, permeability, P, and diffusivity, D, of hydrogen in iron have been separately determined and are consistent with each other under the steady-state condition for temperatures above approximately 400°C; that is, the relationship P = c-D holds. At lower temperatures, however, anomalous behavior of hydrogen in iron has been observed by many investigators. The results of experimental studies4-'' of the diffusion of hydrogen in iron are summarized in Fig. 1, in which the values of D are plotted against the reciprocal temperature. Although there is an increasing divergence in observed values of D with decreasing temperature, the values of D at temperatures below approximately 200°C are definitely small as compared with the extrapolation from high-temperature data. The lines shown bracket the region containing the most probable data. The observed values of c6," are plotted against the reciprocal temperature in Fig. 2, where the dashed lines represent Geller and sun's'' most probable isobars at 1 and 100 atm. At high external hydrogen pressure and low temperatures, the values of c observed are higher than those expected from high temperature data. It is generally accepted that certain trapping mechanism is responsible for the anomalies, but the nature of the trapping mechanism has not been clarified. Various types of hydrogen traps were suggested in the literature, such as "rifts" in the lattice dislocations, voids, microcracks, and so forth. However, no quantitative account of the observed behavior has been given in terms of these trapping mechanisms. Formation of methane in hydrogen-charged steel was found by ~odgurski." This appears to explain the existence of the so-called "residual" hydrogen,4 but not the observed anomalies of hydrogen in iron. McNabb and Foster' proposed a mathematical analysis in terms of a trapping mechanism. However, the physical significance of the traps was not clarified. The necessity of evaluating five parameters in their theory made comparison with experiment difficult. In the present paper, a model is proposed in which the anomalous behavior of hydrogen is attributed to the formation of hydrogen di-interstitials at lower temperatures. In this model, it is postulated that single and di-interstitials are in equilibrium with each other. (The hydrogen di-interstitial is to be distinguished from a hydrogen molecule which may exist in voids.) It can then be shown that most of the anomalies can be explained by assuming that the di-interstitials are virtually immobile and that the binding enthalpy of the di-interstitial, B, is approximately 10 kcal per mole. Predictions of the theory agree with the available experimental data reasonably well. THEORY The basic postulate of the present analysis is that single and di-interstitials are in equilibrium with each

Jan 1, 1969

By Karl L. Fetters

In the process of making steel in the open-hearth furnace the refining of the metal during the working period of the heat is largely accomplished through the agency of the slag. From the birth of the process until the present day steelmakers have recognized the importance of the slag in determining the composition of the metal and the quality of the product. The general relationships between slag composition and metal analysis have long been known, at least in a qualitative or approximate fashion. For examples, the iron oxide content of the slag is higher on lower carbon heats; the more basic slags are higher in iron oxide for a given carbon content; certain amounts of iron oxide and lime arc required for phosphorus removal and a high lime-silica ratio is needed if the sulphur content of the metal is to be diminished. In recent years a number of quantitative relationships involving these and other variables have been developed through plant and laboratory studies by numerous investigators in this country and abroad. The direct comparison of laboratory and open-hearth data involves the question of the degree to which each approaches the conditions of chemical equilibrium, a question which, from the open-hearth standpoint, we are scarcely yet in position to answer. And, although a considerable body of dependable equilibrium data has been obtained in the laboratory, this work has not yet been extended to cover the ranges of slag composition encountered in basic open-hearth practice. In the present study we shall not attempt to draw comparisons between data from the two sources; nor do we attempt to draw conclusions as to the approach to chemical equilibrium in the open-hearth furnace. Many of the operating variables that are likely to be erratic or unrecorded during the earlier stages of the heat become more consistent and arc more readily subject to observation and control during later stages. For example, undigested lime or ore gradually goes into solution, the rate of carbon drop levels off, and the temperature of the metal is brought under control. For these and other reasons a greater degree of self-consistency is likely to be found among data obtained during the

Jan 1, 1940