By J. Nutting, D. H. Kirkwood

The oxidation of lead sulfide in air between 200° and 350°C has been investigated by electron diffraction from thick sulfide films and from galena surfnces. It has been demonstrated that sulfate is the stable reaction product up to 570°C. Sulfate is HAGIHARA has investigated' single crystals of galena roasted in air by the reflection electron-diffraction technique, which owing to the very limited penetration of the beam into the crystal gives information of the nature of the surface only. He has shown that up to 280°C the first oxidation product is lead sulfate, followed by lead mono-oxysulfate (PbO . PbS04). At longer times and higher temperatures more complex patterns appeared which could not be analyzed. All of these patterns were of streaks or spots arising from crystals oriented on the galena surface, and it is probable that these crystals are lead compounds whose structures have not been determined, such as the other oxysulfates (2Pb0 • PbS04 and 4Pb0 . PbS04) or a number of oxides. Certain lead sulfide films, formed chemically, give ring patterns in transmission electron diffraction2 because they are polycrystalline, and should also give ring patterns of the products after oxidation. It was thought that a diffraction study would reveal the sequence of phases produced in the reactions at different temperatures, since X-ray powder patterns are available for many lead compounds. PREPARATION OF FILMS The films were prepared by passing H2S over a saturated solution of lead nitrate in water. Once a silvery film had formed on the solution surface, no further thickening was apparent. The films were transferred by a gauze to a bath of distilled water for washing and pieces of film were caught on small discs on which they were dried. The discs were formed initially on galena up to temperatures of 300°C, followed by oxide and oxysulfates in turn at longer times. The appearance of- these phases is believed to result from an inadequate rate of supply of sulfur to the top surface 01. the crystal. standard Siemens mounts, made of platinum alloy, and had seven 20-p apertures drilled through them. The parts of the film which had dried onto the disc surface were light blue in color, which is the interference color of a film about 600A in thickness. A strong pattern of lead sulfide was obtained in transmission electron diffraction through the apertures but slight broadening indicated a crystallite size of around 200A. Tilting a sulfide film in the beam produced arcing of the rings, increasing the intensities of the (Ill), (3111, and (222) rings and reducing (200) and (220). This arises from preferred orientation in the film, a [loo] direction of the crystallites being normal to the plane of the film. These specimens were oxidized in an oven maintained at the required temperature. The reported times include that taken to heat the film to the reaction temperature. STABLE PHASES FORMED IN OXIDATION The conditions in which various oxidation products of lead sulfide are stable have been considered by the authors in a previous paper.3 It was shown that in a normal atmosphere, taken as containing lo-' atm of SOs, lead sulfate would be stable up lo about 570°C. This was confirmed by oxidizing thin films of sulfide for several days, and the analysis of the transmission-diffraction pattern is given in Table 1. The fit with the patt$rn from X-rays is good, except for the missing 3.62A ring. Some disagreement in intensities of reflections given by X-rays and electrons is to be expected. Up to 570°C a spotty pattern of sulfate was still obtained, indicating grain growth, but above this temperature the film disintegrated. Probably this is associated with the decomposition to PbO . PbS04. It needs to be emphasized that the atmosphere

Jan 1, 1965

By D. L. Rainey, E. R. Goter, W. R. Hudspeth

THE area in which spodumene-bearing pegmatites occur extends from Gaffney, S. C., in a northerly direction to Lincolnton, N. C., a distance of about 16 miles. The zone averages 2 miles in width. Interest in this area was first aroused by the discovery of small amounts of cassiterite in the peg-matites and in greissen which occurs on the walls of some of the pegmatites. Attempts were made from 1880 into the 1920's to mine and concentrate cas-siterite, but there were no successful operations. In 1935 L. M. Williams became interested in the area and began prospecting by trenching and sinking several small shafts. He gradually gained control of a considerable acreage south of the city of Kings Mountain, N. C. Mr. Williams states that he produced some ore from a shaft which he shipped to the Maywood Chemical Co. in the late 1930's. In 1937 G. H. Chambers of the Foote Mineral Co. visited the area and examined several properties, but the lithium market was too small to support the necessary concentrating plant. Early in World War II the Solvay Process Co., encouraged by various federal agencies, acquired the Williams properties and leases and started a drilling program to develop reserves for spodumene mining. A study of this area was also made under T. L. Kesler by the U. S. Department of the Interior Geological Survey. Starting in 1942 a concentrating plant, water supply dams, and shops and other buildings were constructed. The Superior Stone Co., a neighboring crushed stone operator, was awarded a contract to mine and crush the pegmatite ore. Late in 1943 the plant started operations, which were continued until February 1946. A drop in demand for lithium chemicals forced it to close and remain closed for several years. In 1948 the Foote Mineral Co. became interested in assuring itself a source of lithium ore on the North American continent, to be used in the production of lithium ore chemicals, and inspected properties in Canada, South Dakota, and North Carolina. The North Carolina deposits were the most promising. In the fall of 1950 the company leased the Solvay interests with option to buy and acquired additional properties. Renovation of the mill and preparation of the quarry for mining was begun in earnest in January 1951. A new crushing plant was built and construction started in July 1951. The flotation process used was developed in the North Carolina State Minerals Research Laboratory located at Asheville, N. C. Foote is now in the process of expanding its production. The crushing plant is being revamped and much of the old milling equipment purchased from Solvay will be replaced by new. Mining equipment of suitable capacity has been received and is in use. The frontispiece is a general view of the mill. The orebodies consist of pegmatite dikes composed of fine-grained albite and quartz, with varying amounts of mica and spodumene. The latter may amount to as much as 50 pct of the rock, but the overall average is about 15 to 20 pct. Tin, columbite-tantalite, beryl, and other valuable minerals are present in varying small amounts. These dikes, which intruded into the Roan Gneiss underlying most of the Piedmont area, strike approximately N 30 E and dip about 85" to the west. The gneiss has the same strike but dips about 70" west. The dikes lie in a belt extending from Lin-colnton, N. C., to Gaffney, S. C., and passing through

Jan 1, 1954

Jan 1, 1967

By Thomas Cox

The following compilations are made from a series of investigations and are used to present the subject in an unbiased manner, as the writer does not represent any company or financial interest. The present situation is complex. The producers are hard pressed by reason of the low price of crude, while the independent refiner is little better off, because of the corresponding cut in price of refined products, except on occasional contracts. If the real costs are analyzed, it will be seen that the land speculators and the lessors—royalty owners—make the larger profits and not the struggling legitimate operator or independent refiner. The present-day (October, 1922) posted prices per barrel for crudes are Kansas, Oklahoma, Mexia, Gulf Coast, and Louisiana..... $1.25 Healdton............................................. 0.75 Northern Texas and Central Texas...................... 1 . 50 Pennsylvania......................................... 3.00 Wyoming, Elk Basin.................................. 1.25 Wyoming, Salt Creek................................ 0.70 California Base..................................... 0.60 These prices are at the well. In addition, crudes must be gathered and transported to refinery (by pipe line or tank cars), refined, and the refined products marketed. These crudes are of various gravities, ranging within a narrow margin for each field or district, so that averages are not difficult to deduce, and it is these averages that really determine the average operating conditions. In order to show the present realizations, the prices and costs now obtaining are listed against the average yields; the figures are also adjusted VOL. urn.----71

Jan 1, 1923

By Thomas Cox

The following compilations are made from a series of investigations and are used to present the subject in an unbiased manner, as the writer does not represent any company or financial interest. The present situation is complex. The producers are hard pressed by reason of the low price of crude, while the independent refiner is little better off, because of the corresponding cut in price of refined products, except on occasional contracts. If the real costs are analyzed, it will be seen that the land speculators and the lessors—royalty owners—make the larger profits and not the struggling legitimate operator or independent refiner. The present-day (October, 1922) posted prices per barrel for crudes are Kansas, Oklahoma, Mexia, Gulf Coast, and Louisiana..... $1.25 Healdton............................................. 0.75 Northern Texas and Central Texas...................... 1 . 50 Pennsylvania......................................... 3.00 Wyoming, Elk Basin.................................. 1.25 Wyoming, Salt Creek................................ 0.70 California Base..................................... 0.60 These prices are at the well. In addition, crudes must be gathered and transported to refinery (by pipe line or tank cars), refined, and the refined products marketed. These crudes are of various gravities, ranging within a narrow margin for each field or district, so that averages are not difficult to deduce, and it is these averages that really determine the average operating conditions. In order to show the present realizations, the prices and costs now obtaining are listed against the average yields; the figures are also adjusted VOL. urn.----71

Jan 1, 1923

Page Foreword—H. Foster Bain........................ 9 Letter of Transmittal—F. Julius Fohs...................11

Jan 1, 1927

AARONS, J. BOYD, Major. AGNEW, FRANK VANS. ALLEN, HERMAN H., Private, D Co., 8th -Reserve Engineers. BAINS, THOMAS M., Major, Engineer Officers' Reserve Corps. BANKS, H. R., Lieutenant, Canadian Engineers, B. E. F. BARBOUR, PERCY E., Deputy Supt. (Captain), New York State Troopers; Captain, 22d Regiment, N. Y. N. G. BARLING, H. B., Ist Lieutenant', Engineer Officers' Reserve Corps. BIGELOW, BRAXTON. BLOOMFIELD, E. C., Lieutenant. , BORROW, F. K. BROCK, R. W., Major, 19th Reserve Battalion of Canadians. BROOKS, ALFRED H., Captain, Engineer Officers' Reserve Corps. BROWNE, DE COURCY, 1st Lieutenant, Ordnance Dept., Fortress Monroe, Va.

Jan 9, 1917

AARONS, J. BOYD, Major. AGNEW, FRANK VANS. ALLEN, HERMAN H., Private, D Co., 8th Reserve Engineers. BANKS, H. R., Lieutenant, Canadian Engineers, B. E. F. BARBOUR, PERCY E., Deputy Supt. (Captain), New York State Troopers; Captain, 22d Regiment, N. Y. N. G. BARLING, H. B., 1st Lieutenant, Engineer Officers' Reserve Corps. BIGELOW, BRAXTON. BLOOMFIELD, E. C., Lieutenant. BORROW, F. K. BROOKS, ALFRED H., Captain, Engineer Officers' Reserve Corps. BROWNE, DE Courser, 1st Lieutenant, Ordnance Dept., Fortress Monroe, Va.

Jan 8, 1917

AARONS, J. BOYD; Major. AGNEW, FRANK VANS. ALLEN, HERMAN H., Private, D Co., 8th Reserve Engineers. AMBLER, HARRY A., Second Training Camp,, Ft. Sheridan, Ill. BAINS, THOMAS M., JR., Major, Engineer Officers' Reserve Corps. BANKS, H. R., Lieutenant, Canadian Engineers, B. E. F. BARBOUR, PERCY E., Deputy' Supt. (Captain), New York State Troopers; Captain, 22d Regiment, N. Y. N. G. BARLING, H. B., 1st Lieutenant, Engineer Officers' Reserve Corps. BARRETT, LESLIE P., Lieutenant, A. E. F., France. (Unattached.) BENSEL, J. A., Major, Engineers' Reserve Corps. BIGELOW, BRAXTON, Royal Engineers, B. E. F. BLOOMFIELD, E. C., Lieutenant. BORROW, F. K. BOWLES, MARTIN F., 2d Lieutenant of Infantry, Camp Funston, Kans.

Jan 11, 1917

ANDERSON, ALEXANDER, Captain, Royal Garrison Artillery. ANDERSON, GEORGE K., JR., Lieutenant, 30th Co., 3d Replacement Regiment. ARMSTEAD, H. H., Captain, Quartermaster Corps, U. S. N. A. ARMSTRONG, HAROLD KERR, Student Flight Officer, U. S. Naval Reserve Flying Corps, Dunwoody Naval Training Station, Minneapolis, Minn. BAKER, HARRY A., Captain, Co. M, 53d Pioneer Infantry. BASSETT, THOMAS E., Corporal, 340th. Field Artillery, Battery A, 89th Division, A. E. F. BATES, Wm.. T., 3d Reserve Officers' Training Camp. BAUMMGARTEN, K., 1st Lieutenant, 1st Corps School A. P. 0. 703. BAYLESS, G. E. S., Supply Dept., U. S. Submarine Base, New London, Conn. BENSEL, J. A., Major, U. S. R., Board of Control, War. Construction Activities, Norfolk, Va. BILLICK, DON C., Co. C, Ordnance. Supply School. BILLINGSLEY, PAUL, 1st Lieutenant, National Army, Statistics Branch,. General Staff. BLANDY, S. H. B., B. E. F.

Jan 8, 1918

By R. W. Raymond

That the death of Martin Coryell, which occurred at Lambertville, New Jersey, on Monday morning, November 29th, touched the sympathies of a wide circle of professional associates and personal friends, was amply testified by the gathering at the funeral services on Friday. Like his distinguished friend and neighbor, the late Ashbel Welch, Mr. Coryell was one of those pioneers in American engineering to whom we owe the great railway and canal systems which lie at the base of our national prosperity, and who have consequently enjoyed the respect and esteem of their successors of the present generation. Martin Coryell was born July 20th, 1815, at New ope, Rucks County, Pa., and was educated principally in the schools of his native town arid of Lambertville, New Jersey, to which place he returned for permanent residence fifty years later. With the exception of a brief period in youth, during which, to restore his failing health, he learned and practiced for a few months the carpenter's trade, and another brief period, later in life, when he read law for a time in the office of B. H. Brewster, of Philadelphia, afterwards Attorney-General of the United States, Mr. Coryell may be said to have spent his life as an active civil and mining engineer. Even these two episodes can scarcely be said to have been deviations from that profession, since they served to give him more thorough preparation for constructive and administrative work. The Delaware Division Canal, the Raritan Canal, and the Brunswick Canal, are among those upon which Mr. Coryell was employed. For the Raritan Canal Company, under the superintendence of Ashbel Welch, he located the greater part of the Belvidere Railroad (now the Belvidere division of the Pennsylvania Railroad), and directed its construction from Trenton to Lambertville. He was also active as a mining engineer, being one of the early pioneers of mining in the Lake Superior copper region, and had much to do with the development of the Hazleton coalfield and the railroad which has since expanded into the Lehigh Valley system. In 1862, he removed to Wilkes-Barre, where, in 1864, he became manager of the Warrior Run Mining Company. One of the editors

Jan 1, 1887

By William Fink

THE investigation of the phase relations of high-purity aluminum-base alloys is a part of the fundamental research program of the laboratories of the Aluminum Company of America. The results of a number of binary and ternary systems have previously been published in the transactions of this society. The aluminum end of the binary aluminum-titanium system has been studied. This system has received relatively little attention. To the authors' knowledge, there are two previous papers on this subject. E. van Erckelens1 determined the constitutional diagram reproduced in Fig. 1. .According, to this diagram, the liquids represents the separation of TiAl4 (Ti = 30.7 per cent.). He concluded that this is the composition of the compound, because in his work the eutectic horizontal terminated at 30.7 per cent. titanium and the metallographic examination of a sample of this composition revealed only one phase. According to the constitutional diagram developed by W. Manchot and A. Leber,2 reproduced in Fig. 2 from data given in their article, the liquidus represents the separation of the compound TiAl3 (Ti = 37.2 per cent. ). The composition of the compound was derived in a manner similar to that utilized by van Erckelens. Moreover, Manchot and Leber confirmed the composition of the compound by analysis of the constituent left as a residue after dissolving the alloys in weak sodium hydroxide solution. Although these are the only publications describing the constitution of the system, other investigators have studied the composition of the titanium compound. L. Wöhler3 says that there is a compound TiAl3 which was later confirmed by W. Manchot and P. Richter4 and by

Jan 1, 1931

By Theodore B. Comstock

The paper of Mr. S. F. Emmons on the structural relations of ore-deposits, presented at the Boston meeting in February last, having been, as I am informed, unavoidably delayed in publication, was not distributed in the preliminary edition to members until immediately before the sheets of Volume XVI. of the Transactions, containing it, were sent to press. Consequently, I saw it for the first time too late to offer any comments which might have accompanied it in that volume. This is my justification for present-

Jan 1, 1889

By Frank Clowes

This lamp has been devised to burn oil from a flat wick in the usual way for lighting-purposes ; and also to burn a hydrogen-flame of standard size instead of the oil-flame, when delicate and accurate gas-testing is to be carried out. The change from the oil-flame to the hydrogen-flame, and vice versa, can be made with great rapidity, and without opening the lamp or running any risk in the presence of gas. The oil-flame serves for illumination; and when the wick is drawn down by the " pricker," so as to abolish the light, the pale blue reduced oil-flame serves to detect fire-damp or "gas," in any propor

Jan 1, 1894

By Y. H. Liu, R. Kiessling

The chromium, iron, and tungsten borides have been treated with ammonia at different temperatures. They are attacked, forming metal nitride and boron nitride, and the results are summarized in the tables. In the tungsten-nitrogen system a new phase has been observed, closely related to the known ß phase. THE present investigations were begun to determine whether any ternary phases exist in the transition metal-boron-nitrogen systems for the metals chromium, iron, and tungsten. Attempts to prepare such phases were made by using the borides of the metals as starting materials and ammonia as the nitriding agent. Although no new ternary phases have been found to exist, the results may be of some interest with regard to the technical use of the borides. General Procedure A steady stream of dry ammonia was passed through a silica reaction tube, the central part of which was kept at the reaction temperature while its ends were water-cooled. Weighed amounts of the borides were placed in a silica or porcelain boat and heated at different temperatures for a period of 10 to 24 hr. The boat was then rapidly removed from the reaction zone to the quenching zone, the water-cooled end of the tube, by means of a simple magnetic device. The nitrogen content of the products was determined by the increase in weight of the specimens, and the phase analysis was carried out by X-ray methods. For this analysis a Guinier-type camera, constructed at this Institute, was used with a bent, ground quartz crystal monochromator. The general reaction, which occurred in all the experiments, may be summarized as: metal boride + nitrogen -* boron nitride + metal nitride For the higher temperatures pure metal was formed instead of metal nitride. It is sometimes difficult to Discussi detect boron nitride among the reaction products by X-ray methods. Prolonged exposures of some specimens showed, however, that the strongest reflections of boron nitride were present. Additional evidence for its presence was given by the increase in weight of the specimens after nitriding. This increase was always greater than that corresponding to nitride formation only and was often in close agreement with the formula given above. Finally, a white powder, which was shown by X-ray methods to be boron nitride, was left if the reaction products after nitriding Fe,B at 448°C and FeB at 768°C were dissolved in diluted sulphuric acid. Ch rom iu m - Boron - N itrogen Five phases have been found to exist in the Cr-B system,' , and all were used as starting materials. Investigations on the Cr-N system have shown the existence of two nitrides with ideal composition Cr,N and CrN.".' * The results are summarized in Table I. All the borides are attacked and decomposed into chromium nitride and boron nitride, and the kind of nitride formed depends only on the temperature and not on the boride used as starting material. The lowest reaction temperature, however, is different for the different borides. Thus the 6 phase begins to react at about 735 "C, the r phase at about 800°, the S phase at about 900°, the 7, phase

Jan 1, 1952

By K. O. Stamm, B. A. Rogers

Because it is the basis of the economically important operation of hardening steel by quenching, the A3 transformation in iron has been the subject of numerous investigations. Although the contributions to this subject are interesting, no general review will be given here. Readers who care to follow the matter further are referred to the comprehensive summary by Cleaves and Thompson,l which covers the literature to about 1935. Their references to 53 papers on the subject suggest that further investigation is hardly justifiable. However, considerable interest has devel oped recently concerning the reversibility of the transformation. From thermo-dynamic considerations, the transition ought to occur at the same point on heating or cooling, if the change of temperature is sufficiently slow. Yet all of the earlier investigators found a difference of several degrees. Burgess and Crowe,2 who used thermal methods, obtained average temperatures of 912" for Ac3 and 900°C. for Ar3 on electrolytic iron. Their data indicate a considerable range of temperature over which the change occurs, both on heating and on cooling. Terry3 measured the susceptibility in the critical range and estimated from the steepest parts of his curves that Ac3 came at 9I8° and Ar3 at 903°C. Ishiwara4 was one of the first investigators to report a shorter interval between the temperature of the change in the two directions. He measured the change of susceptibility of kaolin-coated samples of steel, in a hydrogen atmosphere, at rater of heating and cooling so low that about 3 or 4 hr. were required for the transformation to complete itself. His results show some variability between samples, but indicate that the difference between Ac3 and Ar3 is in the vicinity of 6°C. Roberts and Davey5 measured the space lattice in pure iron in the vicinity of 900°C. and concluded that a change occurs reversibly between 907' 3" and 910" 3°C., probably between 907" and 910°C. Wells, Ackley, and Meh16 made dilatometric determinations of the Ac3 and Ar3 points in samples of hydrogen-treated carbonyl iron maintained under a vacuum. They used three rates of heating and cooling: 2°, ½°, and .?°C. per min. and found the spread between the two points decreased with low rates. At the slowest rate, the Ac3 transition occurred at 909° to 909. 5°C. and the Ar3 change at 907°C. in three of the samples believed to contain the lowest percentages of alien elements. They concluded that if the rate of temperature change and the content of alien eiements were low enough, the A3 transformation would be completely reversible at 909.50 + 1°C. The question of reversibility is an interesting one and when some iron with especially small percentages of alien elements became available the opportunity to conduct an investigation was welcomed. This iron was prepared by the Division of

Jan 1, 1942

By B. A. Rogers, K. O. Stamm

Because it is the basis of the economically important operation of hardening steel by quenching, the A3 transformation in iron has been the subject of numerous investigations. Although the contributions to this subject are interesting, no general review will be given here. Readers who care to follow the matter further are referred to the comprehensive summary by Cleaves and Thompson,l which covers the literature to about 1935. Their references to 53 papers on the subject suggest that further investigation is hardly justifiable. However, considerable interest has devel oped recently concerning the reversibility of the transformation. From thermo-dynamic considerations, the transition ought to occur at the same point on heating or cooling, if the change of temperature is sufficiently slow. Yet all of the earlier investigators found a difference of several degrees. Burgess and Crowe,2 who used thermal methods, obtained average temperatures of 912" for Ac3 and 900°C. for Ar3 on electrolytic iron. Their data indicate a considerable range of temperature over which the change occurs, both on heating and on cooling. Terry3 measured the susceptibility in the critical range and estimated from the steepest parts of his curves that Ac3 came at 9I8° and Ar3 at 903°C. Ishiwara4 was one of the first investigators to report a shorter interval between the temperature of the change in the two directions. He measured the change of susceptibility of kaolin-coated samples of steel, in a hydrogen atmosphere, at rater of heating and cooling so low that about 3 or 4 hr. were required for the transformation to complete itself. His results show some variability between samples, but indicate that the difference between Ac3 and Ar3 is in the vicinity of 6°C. Roberts and Davey5 measured the space lattice in pure iron in the vicinity of 900°C. and concluded that a change occurs reversibly between 907' 3" and 910" 3°C., probably between 907" and 910°C. Wells, Ackley, and Meh16 made dilatometric determinations of the Ac3 and Ar3 points in samples of hydrogen-treated carbonyl iron maintained under a vacuum. They used three rates of heating and cooling: 2°, ½°, and .?°C. per min. and found the spread between the two points decreased with low rates. At the slowest rate, the Ac3 transition occurred at 909° to 909. 5°C. and the Ar3 change at 907°C. in three of the samples believed to contain the lowest percentages of alien elements. They concluded that if the rate of temperature change and the content of alien eiements were low enough, the A3 transformation would be completely reversible at 909.50 + 1°C. The question of reversibility is an interesting one and when some iron with especially small percentages of alien elements became available the opportunity to conduct an investigation was welcomed. This iron was prepared by the Division of

Jan 1, 1942

Jan 1, 1967

By Karl F. Peterson, H. K. Najarian, Robert E. Lund

PRIMARY products of the Josephtown smelter are zinc metal of various grades, lead-free zinc oxide pigments, cadmium metal, and sulphuric acid. Zinc concentrates of domestic and foreign origin are blended and desulphurized at the roaster plant. The equipment includes five, 12-hearth Herreshoff roasters and two modified Trail-type suspension roasters. The sulphur dioxide containing gases from the roasting operation are diverted to a four-unit contact acid plant for the manufacture of sulphuric acid. The roasted calcines are agglomerated by sintering on Dwight-Lloyd-type sintering machines; the sinter is crushed and sized within required limits; and the sized sinter is smelted in vertical shaft-type electro-thermic furnaces. Of the 13 electrothermic furnaces of various sizes now in operation, four are designed to produce American process zinc oxidc of various specifications; and the remaining nine furnaces are equipped with vacuum-type condensers and produce zinc metal. Papers describing the general smelting practice at Josephtown have been published by AIME. Since both High Grade zinc metal and lead-free zinc oxide pigments are produced direct from the electrothermic furnaces without need for subsequent refining, the elimination of impurities such as lead and cadmium has to be accomplished during roasting and sintering operations. To effect the producing of both High Grade and Prime Western zinc products, the roasting and sintering operations are on two separate circuits. A High Grade circuit produces finished sized sinter low in lead, cadmium, etc., for the High Grade furnaces; and the Prime Western circuit produces finished sinter destined for the furnaces producing Prime Western metal. Sintering at the Josephtown smelter differs in many important respects from the sintering practice in smelters operating horizontal retort zinc furnaces. Requirements of the electrothermic smelting furnaces define the physical characteristics of the sinter, while the chemical composition of the sinter is controlled according to the grade of metal and oxide to be made as final products. Three principal objectives in the sintering process at Josephtown smelter are: 1. To transform the zinc calcine from the roasting operations into a hard, yet porous agglomerate that will not crumble in the smelting furnace. 2. Crushing and sizing of the sinter to obtain a proper screen analysis which is normally —% in. down to +1/4 in. particle size. 3. To eliminate, particularly in the High Grade circuit, as much of the impurities such as sulphur, lead, and cadmium as possible. The sintering plant as originally built in 1930 was equipped with three standard 42 in. x 44 ft Dwight-Lloyd sintering machines. Each machine was equipped with a 15x60 in. sintering corporation fan driven by 150 hp, 900 rpm synchronous motor through a magnetic clutch and capable of delivering 30,000 cfm of air at 15 in. of water and 150°F. Each sintering machine was driven by 7½ hp dc motor with controllers for varying the speed of the machine from 8 to 32 in. per min. The pallets were cast iron and the grates of the herringbone type. The charge was mixed in a 4 ft diam x 8 ft Stehli pugmill and transported by belt conveyor, elevator and tripper conveyor to a small bin over each machine. Shortly after the start of operations the following changes were found necessary: 1. The herringbone grates which plugged very quickly and were difficult to keep clean were replaced by straight, narrow cast-iron grate bars running at right angles to the travel of the pallets. These grate bars are held in place by a center bar extending across the pallet on the 24 in. dimension and by removable retaining plates which form the sides of the pallets. 2. Mechanical grate knockers were developed in conjunction with new grate bars for continuously and automatically cleaning the grates. 3. As the cast-iron pallets cracked, they were replaced with cast-steel pallets. In 1938, the capacity of the sinter plant was increased with the installation of two 42 in. x 22 ft machines which were brought from the company's Herculaneum lead smelter. With a circulating load of some 250 to 300 pct, production of finished sinter on the 42 in. x 44 ft machines at this time amounted to about three tons of sized sinter per machine hour. In 1945, one of the 42 in. x 22 ft machines was replaced by a 60 in. x 44 ft machine of our own design. In 1948, as part of the plant-wide expansion program, the sinter plant not only was expanded but also divided into two separate plants; namely, Prime Western and High Grade circuits. The sinter destined for furnaces producing Prime Western zinc metal is made in a new plant comprising two 60 in. x 44 ft Dwight-Lloyd-type sintering machines, each having a 45,000 cfm Sturtevant fan at 18 in. water static pressure and served by an 8 ft diam x 12 ft long rotary charge pclletizer and auxiliary crushing and sizing equipment. The sinter destined for furnaces producing High Grade zinc metal and zinc oxide pigments is produced in the old sinter plant which was expanded to accommodate four of the 60 in. x 44 ft sintering machines, replacing the old sintering units. In the High Grade sinter circuit, two units of the 60 in. x 44 ft machines are used as preliminary soft sinter machines; and the remaining two units of the 60 in. x 44 ft machines are used to make finished hard sinter. Purification Theory Partial elimination of lead and cadmium in the sintering of zinc ores is common knowledge. However, by some manipulation and by taking advantage of the double circuit, it is possible to make zinc sinter which is nearly free of contaminators. Lead

Jan 1, 1952

By J. A. Marton, N. Brown, M. Herman

AT high temperatures a deformed polycrystalline metal shows grain-boundary displacement in preference to slip lines.' This has led to the conclusion that overall strain at high temperatures is produced chiefly by grain-boundary displacement. Detailed microscopic examinations of individual grain boundaries have shown many interesting ways by which their displacement occurs; sometimes no grain deformation was observed except possibly in the immediate neighborhood of the boundary. However, X-ray examinations show that at high temperatures subgrain formation occurs;Y he process, generally called polygonization, results from lattice bending and the subsequent climb of dislocations to form low-angle boundaries. Quantitative measures of the grain-boundary displacements show that they make a minor geometrical contribution to the overall strain; the major contribution is made by grain deformation."'" A relationship between grain-boundary displacement and grain deformation was suggested by McLean, who showed how the degree of polygonization would determine the amount of grain boundary displacement: and by Dorn, who showed that for a given creep stress, the amount of grain-boundary shear was related to the overall strain and was independent of temperature.' Although the grain-boundary displacement may make a small geometrical contribution to overall strain, it may still be the rate-controlling factor in high-temperature creep. If in general grain-boundary displacement and grain deformation are dependent quantities, then the designer of a creep-resistant metal would like to know whether it is more desirable to strengthen the matrix of the grain or to increase the strength of its boundary. The widespread interest in the relationship between temperature and grain-boundary displacement makes it desirable to test the generality of Dorn's result6 that the ratio of grain-boundary displacement to overall strain is independent of the temperature for a given creep stress. In this investigation p-brass was used because it produces sharp grain-boundary displacements above 400°C. Since B-brass undergoes an order-disorder transformation which abruptly strengthens the grain, it is an excellent metal for determining whether grain-boundary displacement or grain deformation is the rate-controlling factor in creep. The problem will be confined to the temperature range where

Jan 1, 1958