By S. Arthur Krom

ThE James diagonal-plane slimer is specially adapted to handle the finest slimes, but it will also handle sands as coarse as 40-mesh. The saving efficiency of this machine is due to the original construction ,of the deck, and to the rapid reciprocating movement imparted to it by the head-motion. The deck consists of a plurality of connected planes, having a certain fixed ratio of inclination one to another. These planes intersect each other diagonally to the stroke-line of the table and are arranged so as to give the pulp on the table a double treatment. This double concentration performed by the diagonal-plane deck produces cleaner concentrates and tailings than those obtained by the operation of two separate machines. The action of the diagonal planes settles, combines, and holds all the concentrates in one compact mass, sharply defined from the gangue, and easily cut away without loss. Many slime-concentrating machines distribute the feed-pulp for a distance of 4 or 5 ft. only, and upon a very limited settling-surface. This results in a thick, heavy deposit, from which it is impossible to stratify the values and wash away the gangue, the resulting products being dirty concentrates, and tailings carrying high values. The diagonal-plane slimer distributes the feed-pulp for a distance of 10 ft., and upon a settling-surface having an area of 40 sq. ft.; in other words, it spreads the pulp thinly on the table, which allows the metallic values to settle through the gangue quickly, forming a bottom stratum from which the thinly-distributed overlying stratum of gangue is easily brushed away by the feed-water without disturbing the underlying concentrates. Referring to Fig. 1, plane A is the main settling-section of the table. The feed pulp flows gently down this plane and is

Jan 1, 1913

By T. A. Rickard

The interior of West Australia is an arid table-land, elevated 1400 feet above the sea. This plateau is flanked to the south by the Tertiary limestones which fringe the Great Australian Bight. It is bordered northward by the Carboniferous beds of the Fitzroy river and westward by the granite of the Darling hills, while to the cast this wide area, about 900 miles square, slopes downward imperceptibly into an undulating plain of sand, which stretches with dismal persistence across the boundary of South Australia. The waters of the ocean receded from this tract of land long ago; it is probably the oldest landsurface on the globe, and represents the basal wreck of a much larger continent. Fig. 1 is a map of this region. The Coolgardie and Kalgoorlie gold-fields are situated in the southwestern part of the region. The rock-formation consists of granite penetrated by diorites and andesites. The latter are occasionally associated with tuff's, which have been readily mistaken for sedimentaries. There are no fossil-bearing rocks, such as would afford a datum-line from which to measure the relative geological age of the prevailing formation. On the extreme edges of the mining territory there are, it is true, remnants of sand-rock which are considered identical with the " Desert Sandstone " of Queensland, determined by Daintree to be of Mesozoic age. But even this formation has evidently been laid down so long subsequent to the underlying rocks that it serves merely to emphasize their much greater antiquity. In their characteristics and in their relations to each other, the granite and the diorite of the Coolgardie region appear to me much to resemble the Laurentian granite and the Huronian

Jan 1, 1899

By W. C. Hardy, B. W. McArthur

The purpose of this work is to show application of laboratory data in calculating solution gas-drive performance of the Cisco K-I reservoir. Included herein is a diagram showing the graphical relationship between six variables common to all solution gas-drive mechanisms. With an iterative process one may assume existence of any of these six variables at a particular pressure and calculate the production performance likely to occur in a reservoir produced by solution gas drive. Four unique pressure values are described at which the material balance equation alone is sufficient to predict the cumulative volumes of gas produced. Information derived from these pressure points establishes a criterion for determining compatibility of the pressure-volume-temperature (PVT) analysis of the produced crude with the gas production history. Two averaging procedures are used to arrive at a relative permeability-saturation relationship which describes the field-wide performance. INTRODUCTION The Cisco K-1 reservoir is a lenticular-type sand structure lying at approximately 6,300-ft subsurface. It is located in the H. and T. C. Railroad Co. Block 97, SW 1/4 S 392 and NW 1/4 S 385, Scurry County, Tex. Correlation of data from logs indicated that the Cisco K-1 reservoir occupied approximately 3,218 acre-ft of space with a closure of from 15 to 20 ft. Analysis of the production data indicates that the initial formation pressure and temperature were 2,450 psig and 121°F, respectively. The bubble point occurred at 1,715 psig after production of 12,256 STB oil and 11,520 Mcf gas. Only traces of water have been produced since initiation of production. Successive material balance calculations from June, 1952, to June, 1957, showed that no initial gas cap or water influx has contributed to production of oil and that the Cisco K-1 reservoir originally contained approximately 1.44 X 10" STB of oil. THEORY Methods for calculating solution gas-drive perform-

By Wilbur H. Somerton

W. H. Somerton is to be commended for his application of the methods of dimensional analysis in combination with the results of laboratory drilling tests to obtain a significant formula for the rate of penetration for the process of rotary drilling. This formula is shown to be a consequence of a more general formulation developed by the discussor as a result of his investigations of the basic action of most methods of rock drilling by mechanical means—the momentary loading of a chisel-shaped tool on the surface of the rock at the bottom of the hole. Some of the author's conclusions are re-examined in the light of this general formulation. DRILLING RATE FORMULA The author selects a minimum number of the most significant variables associated with the rotary drilling process to set up his two dimensionless parameters. Only one variable is associated with the geometry of the bit —the bit diameter, D; only one variable is associated with the properties of the rock pertinent to drilling— the drilling strength, S; and only two independent variables are associated with the conditions of operation the weight on the bit. F, and the rate of rotation, N. The dependent variahle of interest is, of course, the rate of penetration, R. The results of the author's drilling tests show that the variable R that appears in the dimensionless parameter, RIND is approximately proportioned to the square of the variable, F, that appears in the other dimension-less parameter, F/D2S. This establishes the functional relationship between these two simple parameters that leads to the formulation of a third dimensionless parameter, RD1T2/NF1. This last parameter is a significant one for the rotary drilling process, in general, although the author properly limits the validity of his equations to his present test conditions. The author realizes that the numerical value of this parameter, C, is not a constant but may be a function of one or more additional dimensionless groupings of the many other variables associated with the rotary drilling process, e.g. some dimensionless measure of bit wear. The author's parameter is shown to be a special case of a more general dimensionless parameter, developed by the discussor. that is applicable to practically all methods of rock drilling by mechanical means, namely. RD2S/P. P is the rate at which mechanical work is done on the rock, and S is the drilling strength, a term originated by the discussor. S is defined as the ratio of energy input to the rock to the volume of rock broken

By Robin O. Williams

The textures which are produced by simple shear in poly crystalline samples of copper, brass, aluminum, iron, and zirconium have been determined. For the fcc materials, there are two major textures, both of which are oriented for slip on the usual slip systems. It is shown that each grain will, in general, give rise to both orientations through the production of deformation bands. This is considered a clear demonstration that such bands aye produced by the heterogeneous deformation which takes place instead of the five-slip-system model considered by Taylor. The results on iron and zirconium are more limited but would appear to exhibit certain additional complexities. It is suspected, however, that the general consideration of deformation bands may apply here also. One finds some correlation between the textures produced by this single shear and the conventional textures although it would appear- that additional data and analysis are requived to produce a strong correlation. It is somewhat remarkable that of all the texture investigations only a very few have been concerned with the action of simple shear on polycrystalline aggregates. Of these limited investigations, all used torsional strains and only in Backofen's' and Backofen and Hundy's "ork was sampling carried out so as to derive a texture in terms of the shear direction. Some rather remarkable conclusions re- sulted from Backofens'1,2work: 1) the rate of texture formation in copper is high, being almost complete at a shear strain of unity; 2) the texture does not change if the sample is sheared back, although the surface grains return to their original shape; and 3) the texture is complex in that it has four components, three of which have [110] as a shear direction. These conclusions were based on both qualitative and quantitative data. Shear deformation is intermediate in complexity between simple shear of single crystals and the usual deformation of polycrystals; hence, one might expect to learn considerable from the extension of this work. CONVENTION Deformation in simple shear has the lowest possible symmetr3, less than the other simple modes of deformation (rolling, drawing, and compression); hence, one cannot necessarily expect the textures to have the same degree of symmetry. The geometry of the process is represented by Fig. 1 along with its sltereographic projection. One has the shear plane, the shear direction, the mirror plane normal to the shear plane and containing the shear direction, and a neutral plane normal to both the shear plane and mirror plane. These planes divide the projection into four quadrants. These quadrants are not, however, identical, since all directions within the upper left and lower right are being shortened by the shear process, and the other directions are being lengthened. The first kind are called compression quadrants and the direction of greatest contraction rate, at 45 deg, is labeled with a minus sign; the corresponding direction of greatest extension rate

Jan 1, 1962

By D. Jenkins

THE Franklin Laboratory was designed mainly for the analysis of the products from the two concentrating mills situated at Franklin and Sterling Hill, the most important determinations being the zinc, iron, manganese, lime, moisture and silica contents of the ores. Within the last 4 years, however, it has been found advisable to examine most of our supplies, and therefore additional space and equipment was allotted for the examination of such substances as oils, greases, soaps, alloys, fuels, paints, explosives and water. The building as shown in elevation (Fig. 1) and plan (Fig. 2) consists of a main or routine laboratory, an experimental laboratory, a water FIG. 1.-WEST ELEVATION. analysis room and the other accessories such as stock room, library, sampling and drying rooms and office. The main laboratory is further divided into a balance room and zinc analysis room. As the greater part of our determinations are volumetric, good light is a very important factor and with this in view the interior walls of the building were constructed of white enameled brick laid in Keene cement. These also have the additional advantage that they give a clean and attractive appearance to the room. The windows are large, being 76 by 44 in. and even on very dark days the light is good throughout the whole laboratory. Our zinc titration requires a constant light and as, on many days, especially in winter, the light is variable, we installed two Artificial

Jan 8, 1917

By H. J. McQueen, G. C. Kuczynski

ThE useful properties of k6-Alfenol and the thermenol alloys (summarized by J. E. Nachman and W. J. Buehler') have encouraged research into those alloys which, having compositions near 25 at. pct Al, 75 at. pct Fe, undergo an ordering transformation between 500° and 550°C. The equilibrium diagram of the iron-rich iron-aluminum alloys was first determined by Bradley and Jay.2,3 They distinguished three structures: the disordered, which is bcc; FeAl, which is simple cubic with one Fe atom and one Al atom per lattice site; and Fe3Al, which is fcc with three Fe atoms and one Al atom per lattice site. This last structure may be conceived as eight body-centered cubes with Al atoms at the centers of alternate ones, so that Al atoms have only Fe as first and second nearest neighbors. Later, Osawa and Murata4 determined the boundaries of the different superlattice regions in the iron-rich Fe-Al solid solution by dilatometric and X-ray methods. Two of the six phases, which they found between 0 and 50 at. pct Al, were never identified by other workers. A. Taylor and R. M. ones,' concurrently with and independently of this research, redetermined this diagram by measuring lattice parameters at temperature. Further reference will be made to their results. EQUILIBRIUM DIAGRAM A) Experimental Procedure—The alloys were prepared from NRC gas-free iron (99.9 pct Fe) and 99.99 pct Al. They were melted in alumina' crucubles under vacuum in an induction furnace. If the ingots were unsound or showed more than a 3 pct weight loss, they were rejected. The ingots were homogenized at 1100°C for 24 hr before hot-rolling at 700" to 900°C from 1 in. to 0.25 in. thick. It is interesting to note that alloys containing more than 28 at. pct Al were able to take an 80 pct reduction of area in the ordered FeAl region. The dilatometer specimens and specimens for chemical analysis were cut from these plates. A Leitz dilatometer was used to measure the coefficient of linear expansion as a function of temperature. The specimens were slowly cooled from 900" to 300°C where they were annealed for 10 hr before slowly cooling to room temperature. The expansion was recorded photographically as the alloys were heated and cooled at 1.5oC per min between 100" and 1000°C. The magnetic measurements determining the Curie points were performed on the dilatometer specimens in the dilatometer, by using direct current in the furnace windings both to heat the specimen at 1.5°C per min and to serve as the primary coil. The regular specimen holder was replaced by a thin alundum tube on which was wound, as a secondary, a closely spaced coil of fine copper wire. A reversal of current in the furnace windings produced, in the secondary, an emf which was proportional to the induction in the specimen, and which could be detected on a galvanometer. In this way, it was possible to determine the Curie points of alloys to within * 5°C. B) Results and Discussion—The coefficients of linear expansion, as obtained from the dilatometer curves, are plotted as a function of temperature and composition in Fig. 1. Since in many cases the heating and cooling curves were superimposed, it was decided to measure slopes of heating curves only. Definite high peaks, due to the transformations, were observed on each curve between 400" and 520°C, and, for alloys containing more than 23 at. pct Al, a second set of smaller peaks at temperatures above 660°C. The sharpness of the peaks indicates that ordering to Fe3Al is a first-order reaction. The compositions and the temperatures of these peaks are listed in Table I. When these temperatures are plotted as a function of the composition, the result is the constitution diagram presented in

Jan 1, 1960

By A. H. Geisler, J. H. Keeler

Preferred orientations in rolled and annealed titanium sheets were determined by the Geiger counter spectrometer X-ray diffraction technique. Five annealing textures dependent upon the temperature range of annealing were found, and in order of increasing annealing temperature pendent upon the temperature range are: 1—a deformation like texture, 2—a rotated inorder a-recrystallization temperature texture, 3-a retained u-recrysraIlization texture, on annealing at lower temperatures of the ß-region, 4—a transformation texture based on recrystallized a and predicted by the Burgers' relationship, and 5—a ,ß-cube texture. These results are examined in terms of current theories of recrystallization textures. UMEROUS investigators have described the tex- ture obtained by cold rolling the hexagonal metals, titanium, zirconium, and beryllium, which have c/a ratios less than that of ideal packing, 1.633. The basal planes are rotated out of the rolling plane, about the rolling direction, so that the basal poles are tilted toward the transverse direction as shown schematically in Fig. la. In all instances but one,' it was also reported that the [1010] direction was parallel to the rolling direction (see Fig. lb). Hot rolling has been reported as causing a similar tilt of the basal poles in the transverse direction (see Fig. la) and causing the [1010] direction also to be parallel to the rolling direction as shown schematically in Fig. lb. Annealing after deformation does not appreciably change the tilt of the basal poles in the transverse direction." Beryllium2-7 continues to have the [1010] direction in the rolling direction after annealing, and similar observations for titanium and zirconium' . have been reported for annealing at fairly low temperatures, again as in Fig. lb. At higher annealing temperatures, however, the recrystallized grains of titanium" and zirconium have an orientation such that the [1120] direction is approximately in the rolling direction, although the basal poles are still inclined in the transverse direction. Figs. la and lc show the resulting orientations schematically. This change in orientation has been described as a nominally ±30° rotation of the hexagonal crystallites about the basal poles of the cold rolled texture and is apparent from the results which are summarized in Table I for investigations with the X-ray diffraction technique employing film. The angles y, , and ß are indicated in Fig. 2 which represents the stereographic projection of (1070) poles for the mean orientation of a pole figure. Texture determinations for titanium using the Geiger counter spectrometer have provided similar results except that in some instances additional components of the texture were proposed, as shown by the summary of data in the upper half of Table 11. On the other hand, the spectrometer technique, when applied to zirconium,* has revealed a splitting Recently completed studies of the textures of annealed zirconium", show zirconium to possess textures very similar to those reported here for titanium. Therefore, much of this discussion will include zirconium by virtue of its close similarity to titanium in pref erred orientations. of the intense areas of the pole figure for samples annealed at 600°C. This splitting could be described by a 7" rotation of the tilt axis about the normal to the rolling plane. Such a splitting for the annealed texture relative to the cold rolled texture was not observed in other determinations for either zirconium or titanium using the less sensitive film X-ray methoe and makes the relationship between the two types of texture more complex than the simple rotation about the (0001) pole based on film work. The more precise investigations on zirconium permit the descriptions in the lower part of Table 11, which show that the texture depends quantitatively on the temperature of annealing. When zirconium is annealed at temperatures up to 400°C, the texture is similar to the cold rolled texture, while annealing in the range 500" to 900°C produces a texture which is only approximately described as [11%] in the rolling direction. More precisely described results for zirconium show that the two types of splitting ( 1—about an axis in the rolling plane through an angle given in the second column in Table II and 2—about the normal to the rolling plane through an angle given in the third column of Table 11) depend on annealing temperature. The [1120 is the rolling direction only when the annealing temperature is in the vicinity of 900°C

Jan 1, 1957

By Magnus Troilius

For some time I have been using with great advantage, for the purpose of determining rapidly and accurately the chemical composition of gases from Siemens producers, an apparatus arranged generally like that proposed by Prof. Eggertz; * and I now take pleasure in laying before the members of the Institute a description of the apparatus and its use, hoping that some of them may find it. of practical advantage. At the end of the paper are given some results obtained and heat calculations, with the necessary data for the same. COLLECTION OF GASES. Fig. 1. Shows the arrangement for taking a sample of gas. The funnel F, which may be made of tin plate, is made to fit the test-hole. The gas passes up through the funnel and through the rubber-tubing with the glass tube K, filled with asbestos for retaining dust,, and is drawn into the upper flask by means of water flowing from the same into the lower flask. The upper flask must be completely filled with water from the beginning, so that no air remains. When filled with gas the screw-compressors are securely fastened on, and the flask disconnected from the funnel and receiver. Quart flasks, with openings at the bottom, are very suitable, and easily obtainable. COMPOSITION OF THE GASES. The ingredients found in producer gases are: carbonic acid (CO2), oxygen (0)) ethylene (C2H4), carbonic oxide (CO), hydrogen (H), and marsh gas (CH4). The nitrogen is taken by difference. CO2,O,C2H4, and CO are determined by absorption in various liquids and by observing the resulting diminution of volume. H and CH4 are determined by combustion with oxygen. Carbonic acid.—For this gas is used a solution of 16 grams of potassium hydrate in 100 C.C. of water. 4 or 5 C.C. of this solution absorb 100 C.C. of CO2.

Jan 1, 1883

By Oliver B. Hopkins

Peruvian production for the year 1935 amounted to 17,064,879 bbl., a record amount for any year, bringing the cumulative production of the country up to 188 million barrels. The 1935 figure is an increase of 785,769 bbl. over the 1934 total. The property of the International Petroleum Co. contributed 636,812 bbl. of this increase, and the Lobitos property 158,625 barrels. Exploration work in the country was again active, with attention focused on three areas, the Huallaga River, Lake Titicaca and the Coastal Zone of the Province of Tumbes. It is reported that in the Huallaga River area the Selden Breck Construction Co. has completed geological and engineering studies on its Pachitea River concessions and has ordered a drilling rig. In the Lake Titicaca region further studies in the vicinity of Pusi were made by Government geologists. During the period from 1906 to 1915, the Pirin anticline in this area produced 285,936 bbl. of low-grade crude. The Government holds 120,000 hectares of reserved lands in this area. In the Coastal Zone of the Province of Tumbes explorations by the Government were continued on the National Reserve, and a test location has been selected in the Quebrada Zapotal about 10 miles from the Port of Zorritos. An order has been placed in the United States for drilling equipment. LaBrea-Parinas Estate.—Production on the LeBrea-Parinas Estate reached an all-time high in 1935 of 14,756,914 bbl., an increase of 636,812 bbl. over the 1934 record. The total production from 1890 to 1935 was 148,541,523 bbl. During 1935 a total of 63,021 ft. was drilled in new wells and 5449 ft. in deepening existing wells; 23 wells were deepened and 29 new wells were completed, of which 27 were producers and 2 were dry holes. At the end of the year 2873 wells had been drilled on the Estate, of which 1838 were still productive. The remaining 1035 wells represent abandoned producers or dry holes. Practically all the drilling on the property has been done with cable tools, but during 1934 three strings of rotary tools were introduced. Experience with these outfits has shown that rotary equipment can

Jan 1, 1936

By Oliver B. Hopkins

Peruvian production for the year 1935 amounted to 17,064,879 bbl., a record amount for any year, bringing the cumulative production of the country up to 188 million barrels. The 1935 figure is an increase of 785,769 bbl. over the 1934 total. The property of the International Petroleum Co. contributed 636,812 bbl. of this increase, and the Lobitos property 158,625 barrels. Exploration work in the country was again active, with attention focused on three areas, the Huallaga River, Lake Titicaca and the Coastal Zone of the Province of Tumbes. It is reported that in the Huallaga River area the Selden Breck Construction Co. has completed geological and engineering studies on its Pachitea River concessions and has ordered a drilling rig. In the Lake Titicaca region further studies in the vicinity of Pusi were made by Government geologists. During the period from 1906 to 1915, the Pirin anticline in this area produced 285,936 bbl. of low-grade crude. The Government holds 120,000 hectares of reserved lands in this area. In the Coastal Zone of the Province of Tumbes explorations by the Government were continued on the National Reserve, and a test location has been selected in the Quebrada Zapotal about 10 miles from the Port of Zorritos. An order has been placed in the United States for drilling equipment. LaBrea-Parinas Estate.—Production on the LeBrea-Parinas Estate reached an all-time high in 1935 of 14,756,914 bbl., an increase of 636,812 bbl. over the 1934 record. The total production from 1890 to 1935 was 148,541,523 bbl. During 1935 a total of 63,021 ft. was drilled in new wells and 5449 ft. in deepening existing wells; 23 wells were deepened and 29 new wells were completed, of which 27 were producers and 2 were dry holes. At the end of the year 2873 wells had been drilled on the Estate, of which 1838 were still productive. The remaining 1035 wells represent abandoned producers or dry holes. Practically all the drilling on the property has been done with cable tools, but during 1934 three strings of rotary tools were introduced. Experience with these outfits has shown that rotary equipment can

Jan 1, 1936

By J. Earl Frazier, Howard A. Meyerhoff

IT is not known when silica sand was first noticed along the north coast of Puerto Rico, but the first mention of its occurrence was made in 1922, by N. L. Britton,1 who described its presence in isolated patches extending from Loiza westward beyond Manati. Further observations were made in 1925 and 1926 by Meyerhoff,2 who extended the known occurrences still farther westward to the low hill belt in the Quebradillas limestone immediately south of Hatillo. The extraordinary purity of the sands, which in most localities exhibit no contamination from the nonsiliceous materials surrounding them, was quickly appreciated, and the feasibility of utilizing them for the manufacture of glass was investigated, initially by the Committee on Mineral Resources3 and later (1936) by the Puerto Rico Reconstruction Administration and by H. C. Ray, mining engineer of the Insular Bureau of Mines. In 1934 samples submitted to the Hazel Atlas Glass Co., of Washington, Pennsylvania, were reported to have the composition as shown in the table on column two. Appreciation of the quality of the sand prompted geological and quantitative studies of the deposits, as well as commercial investigations to determine the feasibility of utilizing it locally or on the mainland for the manufacture of glass containers. [ ] DISTRIBUTION OF THE SANDS The quartz sands consistently lie within the outcrop area of the Quebradillas limestone, the youngest of the Miocene formations in the Tertiary coastal plain that fringes the northern coast of the Island. Many of the deposits are closely associated with limestone outcrops, but some appear to be embedded in lagoonal sediments at some distance from rock exposures, and at least one deposit, near Dorado, has been reworked by waves and littoral currents. With this single known exception, the deposits consist of irregular, patternless patches of white sand, which have sharply defined contacts with the surrounding material. Although patches of sand are present in a 90-km. belt that is not more than 5 km. wide, extending from Loiza to Hatillo, they attain maximum size, purity and number in the north central coastal area between Dorado and Barceloneta. Fifty separate deposits have been mapped in

Jan 1, 1945

By Paul B. Crawford, Bobby L. Landrum

An electrical model study has been mode to estimate the effect of horizontal fractures in thick reservoirs on pattern conductivity. For the patterns studied, it is shown that fracturing all the wells in the pattern in-creases the conductivity considerably more than frac-turing only single wells. For certain conditions one large fracture is more effective in increasing conductivity than several fractures of half the radius. Particularly in thick reservoirs and with large fractures, the center of the pay is found to be more responsive than other locations. For the seven-spot pattern fracturing the center well is more effective in increasing pattern con-ductivity than fracturing all outer wells with fractures of the same size. INTRODUCTION Although commercial fracturing has been used for some time very little quantitative information is known about the effects of fractures on reservoir behavior. The purpose of this work was to estimate the effect of horizontal fractures in thick reservoirs on the con-ductivity of various flooding and cycling patterns.2 Circular fractures originating at the wellbore and extending symmetrically into the pay were considered. ANALYSIS Electrical models were used in making this study. Horizontal fractures were simulated by copper sheets shaped like the fractures and of a proportional size; the wellbore was simulated by a copper wire. A dilute salt solution served as a conducting medium. A con-ductivity bridge was used to measure the conductivities of the various patterns studied. EFFECT OF HORIZONTAL FRACTURES ON CONDUCTIVITY Fig. 1 shows the effect on square and staggered line drive patterns of horizontal fractures located in the center of the pay. The model is shown schematically in the insert. The upper and lower groups of lines show the effect on conductivity when all wells are fractured, and when only one well is fractured, respectively. In general, pattern conductivities are substantially improved by fracturing all wells. Fig. 2 shows the effect of multiple horizontal frac-tures on the conductivity of a line-drive pattern. At

Jan 1, 1958

By W. T. Olsen, R. Ulcer

WHEN a liquid alloy freezes, the solid first formed usually differs widely in chemical composition from that last formed, so that there is segregation in the alloy as cast. For example in the copper-nickel system (fig. 1) the first solid formed from a liquid containing 55 atomic pct Cu may contain as little as 38 pct Cu, while the last must contain well over 55 pct. Three factors may act to decrease segregation from the maximum possible. 1. Diffusion in the cooling solid tends to make the phase homogeneous, decreasing segregation. This may be important at slow rates of cooling. 2. Segregation is impossible without diffusion in the liquid. At extremely rapid rates of cooling there may not be enough time to allow maximum segregation. 3. Supercooling delays nucleation to temperatures well below the liquidus thereby decreasing segregation. Hence the first nucleus in the copper-nickel system may contain well over 38 pct Cu. At sufficient supercooling the first nucleus may form below the solidus, in which case there is no reason to expect any segregation whatever. From these considerations, we could predict that at sufficiently low rates of cooling the alloy would be unsegregated because of factor 1 and at sufficiently high rates of cooling there should also be no segregation because of factors 2 and 3. Considerable segregation should occur only at intermediate rates of cooling. We have demonstrated experimentally that segregation can be completely suppressed by rapid rates of cooling. For the alloys studied, however, these rates are too great to be attained in any commercial practice. An alloy of 55 atomic pct Cu, 45 atomic pct Ni was frozen by cooling at varying rates. The degree of segregation in the solid was determined by X-ray diffraction photographs. Slow rates were obtained by slowly cooling the furnace containing the liquid alloy; fast rates by pouring or ejecting droplets of the alloy into water or iced sodium hydroxide solutions. The cooling rate of the droplets can be cal-culated from their dimensions by assuming reason- able values of thermal conductivity.' The experi-ments were repeated with an alloy of 16.5 pct Cu and 83.5 pct Au. A single experiment also showed a 50 atomic pct Bi-Sb alloy had no segregation at the most rapid quench. The position of back-reflection X-ray diffraction lines is a highly sensitive function of the lattice constant, which in turn depends on the chemical composition of the phase. A phase of varying composition will give broad diffraction lines. By measuring the edges of these lines and making suitable corrections for intrinsic line width, it is possible to determine the range of lattice constants represented. These can be converted to chemical compositions from a lattice constant vs. composition curve. Results are shown in table I. In the copper-nickel system the greatest segregation is found at the slowest cooling rates, where the lowest percentage of copper theoretically possible is found. In the copper-gold system, on the other hand, the degree of segregation is decidedly less at the slowest rates of cooling, being greatest at 11,100°C per sec. At no rate is the theoretically lowest percentage of copper (12 pct) found. At the rates of cooling found in sand and die castings the degree of segregation is large and depends little on the rate of cooling. Acknowledgment Most of the material in this paper is abstracted from a thesis presented by William T. Olsen, Jr. in 1948 in partial fulfillment of the requirements for the degree of Master of Science at the University of California.

Jan 1, 1951

By F. Louis Grammer

The iron industry has been so markedly the cynosure of all eyes, that a sense of weariness has overtaken many on-lookers, and a new wonder is desired. While the commercial phase of the iron industry has necessarily engrossed the public attention and probably is the more worthy of record, still the mechanical and metallurgical phases have recorded conspicuous advances and merit attention. In order to appreciate the present condition of blast-furnace practice, it is necessary before enumerating the advances made during the past decade to give a brief discussion of the tendencies in the methods of administration as well as the conditions governing supremacy, for these factors have modified the aims of the manager. It might also be well to apologize for a record of the advances made during such a short period as a decade, were it not that, for the individual, time is marked as much by the impressions recorded on the brain as by the jumps of the second hand of a watch. Furthermore, this article is written in order to carry out a project of the late Dr. Egleston, to have a record made each decade. I regret that the data collected by him, and forwarded to me, end with 1896, and therefore do not include the interesting results which followed the introduction of Mesabi ores. The perusal of the notes is melancholy reading, somewhat like the feelings we experience in going through a graveyard. It is a record made up of so many plants, which have ceased to be factors in the iron world, if they are not entirely moribund. Historically, they would be interesting, emphasizing as they do the abnormal and somewhat overestimated importance of furnace lines, taken without proper reference to volume of blast and nature of stock used. I regret, however, that the time at my disposal does not permit of this presentation.

Jan 1, 1905

By Albert Sir Kitson

THE manganese ore deposits of the Gold Coast, British West Africa, occur in very ancient rocks, of both sedimentary and metamorphic types. In. certain respects, they strongly resemble those of India and Brazil, as contrasted with those of Tertiary age in Georgia. Viewed from the present condition of the maganiferous rocks, the oldest deposits are in the sediments. Later than these are the progressively metamorphosed representatives of these sediments; youngest are the products of decay and degradation with the concentration of manganese oxide of both areas. The oldest occurrences are in argillaceous and siliceous phyllites and slates, which show only a moderate amount of metamorphism. They belong to a series which also includes mudstones, sandstones, grits, conglomerates and subordinate limestones, with tuffs and lava-flow's largely of basic types. To this series I have given the name Birrim. Its age is unknown, for no definite fossils have been discovered in it. As the characteristics of these non-fossiliferous strata at many places are the same as those of strata in many parts of the world that are suitable for the preservation of fossils and that contain them, it is assumed that the Gold Coast deposits are pre-Cambrian. These rocks of the Birrim series have normally a northeast-southwest strike and are folded, but not to any very great degree except in certain belts. From the Eastern Province of the Gold Coast they may be traversed across their strike for more than 600 miles to the extreme northwestern corner of the Northern Territories. Thence they probably extend much further into French Territory.

Jan 1, 1927

By Robert H. Richards

The object of this paper is to enlarge the field of settling velocities treated by me in my former papers, Close Sizing Before Jigging, and Sorting Before Sizing.' There seemed need of work both on coarser and on finer sizes. Messrs. A. Sidney Warren and M. L. Nagel undertook the investigation for the coarser sizes, from 12.85 mm. down to 2.05 mm. diameter. Their work, because of the closer spacing and because of the increased number of observations and consequent stronger averages, called for a revision of the former work. Messrs. G. A. Barnaby and Ralph Hayden undertook this part of the work, from 2.49 mm. down to 0.28 mm., which is near the limit of sifting. Their work covers the ground much more minutely and comprehensively than the former papers. There remained to be covered the portion of the field too fine for investigation with the sieves. This part, covering the range of grains from 0.48 to 0.03 mm., was undertaken by Mr. E. S. Bardwell. For it he used the elutriation method. 11. The First, or Coarsest, Section of the Field. The first desideratum in this investigation was a series of sieves for sizing the sands preparatory to making the tests. It became necessary, therefore, to decide on a sieve-scale for this purpose. A sieve-scale is a series of sieves in which the dimensions of the holes of the successive members form a series increasing by a definite ratio. There are three natural sieve-scales: 1, progressing by doubling the width of the hole for each suc-

Jan 1, 1908

By Sergio G. Jarpa

A mining project is, at one and the same time, capital intensive and highly risky. Besides, because of its usual long projected life, the operating cost is more difficult to predict and offtentimes exceed, during the life of the project, the first investment manifold. The objective of this study was to evaluate the applicability of cost-capacity relationships as used in the chemical industry to mining operations and, when necessary, to develop new ones. With the aid of a computer library program available at the Computation Center of the Pennsylvania State University, the total investment in mining equipment was determined to vary exponentially with production capacity, and the scaling exponents for each class of equipment, i.e., drills, shovels, trucks and earth moving equipment, as well as for the total operation were calculated. Since the scaling exponent for the whole mining operation happened to be equal to 0.94, it was concluded that more significant economies of scale are achievable in processing plants than in mining operations. From the operating cost point of view, unit material cost was found to decrease more rapidly than unit labor for the same increases in production capacity. The analysis of cost centers revealed that drilling and blasting, which are materials-intensive operational stages, were the most favorable in achieving significant economies of scale. Hauling unit cost, on the other hand, decreased only slightly when production capacity increased.

Jan 1, 1977

Jan 1, 1965

By John Croston

IN the closing months of 1936 the copper industry gave every evidence that it was at last on the threshold of an improved era. At the beginning of the year prices stood at 9 1/4¢, which in itself was a great improvement over prices prevailing for the three previous years. Industry generally was showing signs of moving forward in this country, and business was definitely good in certain foreign quarters. The threat of war and prep-arations for rearmament in Europe and Asia acted as a further stimulus purchasing. By midsummer the situation had so improved and stocks to been so reduced that the cartel of foreign producers (including American producers with foreign mines) decided to increase the produc-tion quota to 75 per cent on Aug. 1. Large-scale buying gave continued strength to the price and by Oct. 1 the quota was increased to 80 per cent, and again on Oct. 15, to 85 per cent. Notwithstanding this the price of copper continued its advance and on Nov. 1, with stocks declining con-tinuously, the cartel increased operations to 95 per cent, then to 105 per cent on Nov. 5. In the meantime the domestic producers, because of the great increase in home consumption, had increased their production by nearly one-half. At the close of the year copper sold at 120 per pound, and since the turn of the present year has reached 170. This rapid increase has not been wholly justified. Much of the increase was due to the legitimate demands of recovering industry, but rearmament orders plus accumulation of reserve stocks in case of war, purchases in anticipation of labor strikes and purely speculative activities on the London Metal Exchange accounted for the balance. Certainly in view of the state of industry and the general world price level, it appears unnecessarily high. Talk of a copper shortage is sheer nonsense, the recent condition in the market being created by overbuying, leaving but a small volume for speculative supplies. It takes some months for an increase in mine output to reach the market, but production is again overtaking apparent consumption, stocks have begun to increase, and this, together with the reopening of many small

Jan 1, 1937