By Richard A. Queeney, Lance G. Peterson

ESTIMATES of the stacking fault free energy of copper reported in the literature show an extensive divergence of results. Based on measurements of dislocation node radii, Thornton et al.7 find the lower limit of stacking fault energy to be 60 ergs per sq cm: Jossang and coworkers4 estimate the same value should be less than 40 ergs per sq cm. Assuming stacking fault free energy to be twice the coherent twin boundary free energy, Valenzuela8 reports 72 ergs per cm, while Inman and Khan2 cite a value of 24 ergs per sq cm. which can no doubt be accounted for by almost complete absence of interstitials in solution. However, the minute concentration was sufficient to permit observable recovery of dislocation damping. Assuming a dislocation density of 1010 CM -2 and an average loop length of 0.5 , a concentration of interstitials as low as 0.01 at. ppm is sufficient to reduce dislocation damping by more than a factor of ten. The concentration of interstitial solute atoms in Ferrovac E-0.15 pct Ti was thus estimated at 0.01 at. ppm < (C + N) < 2 at. ppm. The absence at elevated temperature of strengthening due to interstitials, Fig. 1, was therefore anticipated in the titanium alloy. The temperature dependence of the flow stress below 300°K was unaffected by addition of either titanium&apos; or zirconium.&apos; Observed, however, was an initial difference in the absolute value of the flow stress below 320oK, Fig. 1. Grain size may account for the difference; the grain diameter of Ferrovac E was 30 to 45 µ and that of Ferrovac E-0.15 pct Ti 65 to 90 µ. Although second phase particles in the form of titanium carbides and nitrides precipitated in the Ferrovac E-0.15 pct Ti alloy, the spacing was too large to produce any strengthening effect. The mechanical properties measured, therefore, were inherent to the bcc lattice. 1W. C. Leslie and R. J. Sober: Trans. ASm, 1967, vol. 60, pp. 99-111. 2 H. Conrad: Journal of Metals, 1964, vol. 16, pp. 582-88. 3 A. S. Keh and W. C. Leslie: Materials Science Research. H. H. Stadelmaier and W.W.Austin, eds., vol. 1.pp. 208.50, Plenum Press, New York, 1963. 4A. S. Keh, Y. Nakada, and W. C. Leslie: Dislocation Dymmics, Rosenfield, Hahn, Bement, Jr., and Jaffe, eds., pp. 381-406, McCraw-Hill Book Co., New York, 1968. &apos;W. J. Bratina, J. T. McCrath, and H. E. Rosinger: Can. Met. Quart., in press. 6 W. J. Bratina, J. T. McGrath, and D. Mills: Suppl. Trans. Japan Inst. Metals. 1968, vol. 9, pp. 436-43. &apos;H. E. Rosinger and C. B. Craig: Can. Met. Quart., In press. %. Mills. J. T. McGrath. and W. J. Bratina: ScriptaMet,, 1968, vol. 2, pp. 311-13. The purpose of this note is to present the results of a direct measurement of the stacking fault free energy in copper. The present method avoids both the question of interaction forces of nodal dislocations and the assumption that the coherent twin boundary free energy is one-half that of a stacking fault. Fig. 1 shows a transmission electron micrograph of a stacking fault intersecting a high angle grain boundary in copper: Fig. 2 is a schematic representation of the intersecting interfaces. To produce the specimen, pure copper was rolled to 0.002 in. thickness and annealed for several hours at 875°C. These foils were strained in tension to l04 µ in. per in., and rean-nealed to 8 min. Recrystallization and/or grain growth were not observed during the second anneal, indicating that intersections such as Fig. 1 are equilibrium configurations. Many such stacking faults were observed, but few were noted as intersecting grain boundaries in well-illuminated areas. The intersection of Fig. 1 was well away from the specimen edge. Since similar defects have not been observed in fully recrystal-lized and annealed copper, it is felt that this defect is due to the tensile straining. Electron transmission

Jan 1, 1970

By H. E. Cline, T. H. Alden

A study zvas made of rate-sensitive plastic deformation and superplasticity in alloys of lead and tin. These alloys (lead, PO-19 pct Sn, Sn-38 pct Pb, Sn-2 pct Pb, tin) were extruded, aged at room temperature, or melted and resolidified to produce a variety of ~nicrostrnctures. Flow stress us strain rate data were obtained frorn tension tests for strain rates between 10-6 and 1 min-1. The curve log o .us log £ was S-shaped jor fine-grained materials and approxinzately linear for coarse-grained nzaterials. At constant grain size, the behavior was relatively insensitive to conposition. High rate sensitivity (d log o/d log k) and superplasticity occurred at intermediate strain rates in fine-grained materials and are believed to be associated with a transition with strain rate in the mode of plastic flow. This transition was shifted to higher strain rates with increasing temperataire or decrensing grain size. The high rate rneclzanisrn is presunzed to be slip, while rnetallographic evidence sug-gests that the low rate lnechanism is pain boundary sliding. PEARSON&apos; discovered that extruded eutectic alloys of Pb-Sn and Bi-Sn could be elongated as much as 2000 pct in tension. The ability for stretching decreased with aging time or annealing to increase the grain size. At high strain rates, or if the material was in the cast condition, normal ductility was observed. Following deformation of the extruded Pb-Sn eutectic at low rates, Pearson observed an equiaxed granular structure on an initially flat surface, while rapid straining produced elongated grains. He attributed the large deformation in the extruded alloys to the persistence of extremely small grains to a temperature sufficiently high for inter granular flow. Avery and backofen2 measured the strain rate sensitivity of the flow stress, m = d In old In 6, in the Pb-Sn eutectic and established a correlation between m and the tensile elongation. In the extruded eutectic alloy the strain rate sensitivity was 0.1 to 0.2 at rapid rates and the elongation was small, while at low rates m increased to 0.4 to 0.6 and superplastic elongation was observed. They also noted a grain size effect. In the case of the cast Pb-Sn eutectic the strain rate sensitivity remained at 0.1 over the range of strain rates of their experiment (3 x 10"3 to 2 min-I). These authors suggested that diffusional (Nabarro-Herring) creep was the mechanism by which deformation occurred at low strain rates, while climb-controlled creep occurred at high rates. Two predictions of this model are that, at low strain rates, the strain rate sensitivity approaches 1, i.e., Newtonian viscosity, and that the strain rate at constant stress varies as D/L2, where D is the coefficient of self-diffusion and L the grain size. More recently, a mechanical and microstructural investigation of the dilute superplastic alloy, Sn-5 pct Bi, has been done.3 The results show that the high strain rate sensitivity is associated with a transition with strain rate of the mechanism of plastic flow. At low strain rates, grain boundary sliding and its associated accommodation processes were evident, while at high strain rates quasi-uniform slip was concluded to be the dominant deformation process. The following experiments were performed to extend our knowledge of the phenomena of superplasticity to a larger range of strain rates, compositions, temperatures, and microstructures in the Pb-Sn alloy system. The question of why a cast structure does not exhibit viscous behavior although it appears to have a fine microstructure2 was investigated.

Jan 1, 1968

By W. W. Cotter, W. R. Clark

WEBSTER tells us the word "extrude" means to "force, press or push out; to protrude." As applied to the metal industry, the process consists largely of forcing plastic elements (plasticity usually obtained by preheating), through dies of predetermined profiles, into constant sections of considerable length and weight. Most of the "virgin" metals are quite malleable under this process, likewise many of the commonly used "alloys" in various industries, when basic elements are proportioned or combined within the natural laws and limits of good metallurgy. Several of the foundry alloys, both ferrous and nonferrous, together with some of the heat-treatable light metal mixtures, are decidedly weak and hot short at ordinarily plastic ranges, and consequently are troublesome or quite incapable of commercial extrusion. DEVELOPMENT OF PROCESS This process was conceived some time before 1800 and during its first century was employed almost entirely in making lead pipe, plumbing fittings and coating electrical cables. As a result of contact and experience with the lead industry and presses, Alexander Dick, of London, England, is credited with first having applied the principles of extrusion to brass, and in 1894 brought out a 500-ton horizontal press powered by hydraulics. A duplicate of this unit was imported by one of the Connecticut brass mills and was in experimental operation by 1900. During the first five years of operation, this press proved the value of the method to American industry, as it immediately revolutionized and converted the manufacture of brass rod from a 15-pass cold-rolling operation, with elimination of several intermediate anneals and cleanings, to an extrusion and a finishing draw. Likewise, ornamental brass and bronze moldings formerly cast and machined were produced in one squeeze on the extruder. The extrusion operation, being entirely that of compression, deforms the material without tensile stresses and can be used on delicate mixtures under heat, which cannot be hot-worked by straight hot-rolling or roller piercing. Base slabs of clock-brass strip were early in line of development or improvement, as were the brass bronzes (Naval brass, Muntz metal, manganese bronze, and others), popular as engineering materials for bolt stock, as well as structural shapes for marine and other mild conditions of corrosion. By 1910, American engineers undertook to design tube shell extruders, but were unsuccessful. The first World War began before fabricators could procure the more substantial designs of tube extruders produced in Germany; and it was not until the middle twenties that better models of the Universal extruders (double-actioned presses), equipped with hydropneumatic accumulator systems and other modern equipment, were available in the United States.

Jan 1, 1945

By J. L. Rodda, R. L. Wilcox, E. C. Truesdale

IN recent years various problems in connection with research work on the preparation and properties of zinc-base alloys have required reliable information concerning the constitution of the zinc-rich portion of the iron-zinc equilibrium diagram. On numerous occasions rather positive indications were obtained that, for example, the solubility of iron in zinc was incorrectly represented on .the current equilibrium diagrams.. A careful study of all the available literature relating to the iron-zinc system led to the conclusion that much of the early work was unsatisfactory as measured by present standards of experimental accuracy, and as a result it was decided to redetermine the location of the liquidus curve and of adjacent portions of the diagram. Part I. of this paper comprises a description of the experimental methods and a summary of the results by means of which the zinc-rich end of the iron-zinc diagram has been revised in the following ways: 1. Measurements of the solubility of iron in liquid zinc by several different sampling methods, leading to a relocation of the liquidus curve. 2. Microscopic, conductivity, and X-ray studies of the solid solubility of iron in zinc, which, together with thermal analyses, have resulted in new values for the solid solubility and the eutectic temperature and composition. 3. Heating and cooling curves, obtained by a refined differential method, leading to new locations for the two peritectic horizontals. In Part II of the paper the attempt is made to review all of the published work having a bearing on the constitution of the iron-zinc system, and to correlate the present results, and some recently published data

Jan 1, 1935

By E. C. Truesdale

IN recent years various problems in connection with research work on the preparation and properties of zinc-base alloys have required reliable information concerning the constitution of the zinc-rich portion of the iron-zinc equilibrium diagram. On numerous occasions rather positive indications were obtained that, for example, the solubility of iron in zinc was incorrectly represented on the current equilibrium diagrams. A careful study of all the available literature relating to the iron-zinc system led to the conclusion that much of the early work was unsatisfactory as measured by present standards of experimental accuracy, and as a result it was decided to redetermine the location of the liquidus curve and of adjacent portions of the diagram. Part I of this paper comprises a description of the experimental methods and a summary of the results by means of which the zinc-rich end of the iron-zinc diagram has been revised in the following ways: 1. Measurements of the solubility of iron in liquid zinc by several different sampling methods, leading to a relocation of the liquidus curve. 2. Microscopic, conductivity, and X-ray studies of the solid solubility of iron in zinc, which, together with thermal analyses, have resulted in new values for the solid solubility and the eutectic temperature and composition. 3. Heating and cooling curves, obtained by a refined differential method, leading to new locations for the two peritectic horizontals. In Part II of the paper the attempt is made to review all of the pub-lished work having a bearing on the constitution of the iron-zinc system, and to correlate the present results, and some recently published data

Jan 1, 1935

By E. H. Sellards

Phosphate rock like other mineral substances is found in nature in varying degrees of purity.

Jan 1, 1915

By Benjamin L. Miller

THE essential differences expressed by the different speakers participating in this symposium concern merely the relative emphasis placed on the subjects that are commonly included under the term "geophysics" and the branches of science that form the basis for investigations in this field. In order to appreciate the present situation it may be profitable to briefly refer to a few historical matters. One can find almost countless descriptions of geological phenomena long antedating the introduction of the title of "geology," which has been credited to Richard de Bury in the fourteenth century. Interpretations, when they were offered, were generally pure speculation. Only toward the close of the eighteenth century do we find theories developed as the result of observations and tested by additional observations. It is difficult to select and give proper credit to the individual who was particularly responsible for turning geology into a distinctly observational science. William Smith, who has been called the "Father of English Geology," certainly represents the period when observation was the only method used. As he traveled through the British Isles, "sometimes 10,000 miles in a year," he was continually making notes of his observations. Geikie says: "His plain, solid, matter of fact intellect never branched into theory or speculation, but occupied itself wholly in the observation of facts." William Smith, with others of his time, definitely laid firmly the foundations on which modern geology has been built. Field and laboratory observations can no longer be said to constitute the sole basis for geologic contributions but we have not laid aside the methods of Smith and his followers. It is folly to underestimate the fundamental value of the observational part of geology in the present. The objection to purely observational geology is that it is mainly qualitative and not quantitative, general and not specific. No one can deny this charge and probably there are few who do not welcome every method or process whereby we can put aside generalities for definite established values. Physics is the science that has particularly come to the aid of the geologist in this respect. CONTRIBUTIONS OF PHYSICS It is not the intent of the writer to enumerate or to evaluate all of the contributions to geologic advance in the field of physics. A few only are used for the purpose of illustration. When Clarence King, Director of the United States Geological Exploration of the Fortieth Parallel, invited Ferdinand Zirkel to study 2500 thin sections of rocks collected from the western United States, the use of the microscope came into general use. Zirkel&apos;s report was published in 1876. He was not the first to use transmitted light for microscopic rock determination, some work having been done by Henry Clifton Sorby and others some years earlier, but he was the first to put into general use this method. We may well claim that this

Jan 1, 1941

Mr. Raden has described the practical problems associated with fines in phosphate rock beneficiation. In this discussion, a colloid chemical viewpoint is given to the problem of separating phosphate values from phosphatic clay slurries. The phosphatic clays are predominantly colloids of a complex mixture of many minerals (1). The constituents are typically 25% apatite, 40-50% clays, and various amounts of wavellite, quartz, dolomite, fluorite, and other minerals. The clays are montmorillonite, attapulgite, and illite, with some kaolinite. The various mineral colloids in the slurry are heterogeneously coagulated in the as-produced state. Dispersion of the coagulated state is evident from the fact that dispersing agents (certain polyelectrolytes) cause a large reduction in the viscosity of the slurry (2). The as-produced slurry settles from 4 to 8% solids within a week, but thereafter settles much more slowly in the form of a sediment of flocs. The supernatant liquid is often clear because of the cooperative action of the mutual interaction of particles during settling. Mineral segregation during settling has not been observed for the same reason. The initial slow settling rates indicate that the coagulated assemblies are very small. Efforts to separate apatite from the other minerals would be complicated by the heterogeneous coagulation state. Somehow the apatite must be "liberated" from its association with the other minerals before it can be physically separated. One approach for liberating apatite is to disperse the entire suspension. While this is feasible technically, for example by using certain polyelectrolytes (2), the reagent costs based on present

Jan 1, 1979

By T. V. Moore, H. D. Wilde

In many of the important problems of the petroleum engineer, it is necessary to know accurately the laws governing the flow of gas and liquid mixtures in vertical pipes. Although much work has been done along these lines, no satisfactory solution to the problem has been found. A good theoretical discussion of the energy balance in a gas-lift has been published by Versluys.1 One of the most important factors affecting the efficiency of the flow of oil and gas mixtures is slippage, and in most of the experimental work that has been done no provision has been made for the measurement of this quantity. As Versluys pointed out, since there is no method now known to estimate it from the data usually taken, slippage must be determined empirically. This paper presents the results of some work carried on to measure slippage in short experimental gas-lifts. As shown herein, slippage can be easily calculated in a vertical pipe carrying a mixture of oil and gas if the fractions of the pipe occupied by liquid and gas respectively are known. In this work, the fraction of the pipe occupied by the liquid was measured under a wide variety of conditions and the relationship between this fraction and other quantities, which are easily measured in ordinary work, was determined. It was hoped that the quantitative relationship obtained from this work could be used for making accurate calculations in flowing or gas-lift wells, but unfortunately it did not check satisfactorily when applied to actual wells. Apparently flow in long flow pipes is more efficient than in the short ones used for the experimental work. Nevertheless, it is felt that the data themselves arc of interest; that the method of attack may be of value in future work and that the relationship derived between slip and the relative velocities is a contribution toward the solution of the gas-lift problem.

Jan 1, 1931

The report of the Comittee on Nominations was received and ordered to take the statutory course. Thereupon the chairman was authorized to appoint a committee of three members to report at the next meeting of this Board regarding the suggestions made by the Nominating Committee. The following vote of thanks was then passed to the members of the Arizona Committees and others: "WHEREAS, the Board of Directors of the American Institute of Mining Engineers has a deep appreciation of the splendid success of the Arizona Meeting and WHEREAS, the Board is aware that this success was brought. about by the generous and efficient efforts of the members of the Local Committees, therefore it is

Jan 12, 1916

By Jerry M. Thornton, Richard W. Cannon, Don C. Rotherham

The orebodies of Gibraltar Mines Ltd. (N.P.L.) are located on the western slope of Granite Mountain, central British Columbia. The area in and around Gibraltar Mines has a moderate topographic relief with elevations between 3500 and 4100 ft. The property is 95% covered by overburden which varies in depth from a few feet to 230 ft. Early History and Geology The present Gibraltar Mines property before amalgamation consisted of the Pollyanna property (Duval-Canex) and the Gibraltar property (original Gibraltar Mines) as well as some Coast Silver and McLeese Lake Copper claims.

Jan 9, 1972

By Charles Wert

THE diffusion and precipitation of carbon and nitrogen in a iron have previously been investigated using the internal friction as a measuring tool.&apos; Most of this work has been done on rather pure iron; no effect was observed which would indicate that either of these phenomena is affected by the rather small amounts of impurity found in these samples of iron. Fastz observed, however, that both the diffusion rate and the aging properties of nitrogen in iron were sensibly changed by the addition of Vz pet Mn. The diffusion rate at a given temperature is reduced and the nucleation of nitrides is apparently changed somewhat. He observed no such changes for carbon in this alloy. Later Dijkstra and Sladek" extended these observations on nitrogen to other alloys of iron. They found that metals other than manganese also influence the behavior of nitrogen in iron; chromium, molybdenum and especially vanadium affect the diffusion and precipitation of nitrogen even more than manganese does. Their results have been verified in all essential details by this author, who finds in addition that small additions of nickel have about the same effect on the diffusion of nitrogen as the same amount of manganese. The present work was undertaken to study the effect on carbon in iron of these alloying elements. The alloys used had two sources. The material used as a "standard" (designated Fe in this paper) in the measurements was some iron supplied by J. K. Stanley, of Westinghouse Electric Corp., who reported 0.01 pct 0, as the only major impurity. He also made up an alloy of 0.26 pct Ni and one of 0.9 pct Mo using this same iron as a base. They were supplied by him in 2 lb billets, which were sawed into rods and cold formed into 0.030 in. wires for measurement. The alloys of chromium, manganese, and vanadium were prepared by the metallurgy section of the Institute for the Study of Metals, University of Chicago, by adding these metals in turn to vacuum melts of National Research Corp. iron. The small castings prepared in this way were also cold formed into 0.030 in. wires. After these wires had been prepared they were decarburized for 30 min at 730°C in wet Hz. After this treatment, no trace of carbon (as measured by internal friction) could be found. All specimens were then carburized for about 15 min at 710°C and water quenched. By this treatment the internal friction at 40°C was raised to a Q-&apos; ~ 0.015. The diffusion of carbon in these alloys was studied by observing the shape and position of the internal friction peak at 0.9 cycles per sec. These measurements were made using a torsional pendulum in a manner described earlier.&apos; The data are plotted in Fig. 1. It is seen that there is no apparent difference in internal friction between the various alloys. This is in marked distinction to the broadening and shift-

Jan 1, 1953

By Barry K. McMahon

The fundamental problem in rock mechanics is accounting for the discontinuous and anisotropic nature of the jointed rock mass. It is this problem that makes rock mechanics distinct from the mechanics of steel, glass, or concrete. Existing mathematical models explain much of the behavior of rock cores in the laboratory but, in civil engineering at least, the rocks that matter are the ones that are already broken. On the other hand, the basically descriptive methods now used in engineering geology do not lend themselves easily to mathematical analysis. A set of indices of geological properties related to the strength and deformation characteristics of jointed rock is needed. Like the index properties used in soil mechanics these will probably not have precise mathematical meaning, but once correlations are established with large scale tests they can form a basis for the transfer of test results, obtained in one area under one set of conditions, to the prediction of rock behavior in another area under another set of conditions. Indices of rock properties are even more important in rock mechanics than in soil mechanics as the cost of testing is much higher. To be useful, these indices must be easily and quickly measured and give reproducible results when measurements are made by different people. In this paper the word "joint" means all naturally occurring rock fractures with less than 3 in. of clay or other soft coating material. EXISTING INDICES OF ROCK PROPERTIES A comprehensive review of indices of rock properties for intact rock is given by Deere and Miller.&apos; They provide charts ". . . for estimating the strength or modulus properties for intact rock from the numerical indices obtained by either the Schmidt hammer, the Shore Scleroscope,

Jan 1, 1968

By Robert L. Dean, Michael Hoch, Samuel M. Wolosin, Chung K. Hwu

The general shape of the 1450°C isotherm of the Ti-TiO-ZrO2-Zr region was evaluated from the surrounding binary phase diagrams and from thermo-dynamic data on the metal-oxygen binaries. The phase boundaries were accurately determined using X-ray and metallographic techniques. At 1450°C the system shows a large bcc ß field, which extends from the two metal-oxygen binary systems as a Gaussian error function, and is stable up to 30 at. pct 0 when Ti and Zr are present in equal amounts. At higher O Concentrations, the ß field is in equilibrium with t-ZrO . The following four regions, with three solid phases, are present: two a ß t-ZrO,, a TW t-ZrO,, and TiO t-ZrO2 c-ZrO2. On cooling the ß phase transforms into the a phase, going through the w transition phase. The isotherm at 1500°C for the region TiO-TiO,-ZrO, was obtained by using X-ray diffraction. At 1500°C a large c-ZrOz region is present as well as a large two-phase field, Ti0 c-ZrO,. The following regions, with three solid phases in equilibrium, were found These regions are relatively small. The solidus and liquidus relationships were determined by observing samples suspended in a tungsten crucible by means of a fine tungsten wire and heated in vacuum. Eleven univariant points were found. C-ZrO, decomposes through a peritectic reaction into liquid t-ZrO2. The activities of Ti and TiO in the TiO t-ZrOz and in the two a ß t-ZrO regions were measured using the Knudsen effusion method. In the a TiO t-ZrO, region the activities of Ti and Ti are the same, as in the a — Ti TiO binary. In the two a t-ZrO, regions, the Ti activity is high and the Ti0 activity very low, although all phases present contain at least 30 at. pct 0. This indicates a short-range order in the solid phases, Zr atoms being preferentially surrounded by 0. 1 HE system Ti-Zr-0 is of interest because of the wide ranges of solid solubility exhibited by the boundary systems; as titanium and zirconium both belong to the same group of the periodic table, large single-phase regions should occur within the system, with a great variation of properties (as the composition changes within the single-phase region). Furthermore, the possibility of modifying ZrO, to make it a more usable refractory by the addition of other metals makes this system also of interest. Because of the high affinity of titanium and zirconium for oxygen, the oxygen partial pressure is very low at all compositions; thus, there exists a ternary metal-metal-oxygen system in which the oxygen pressure is not an important variable, so long as it is low enough. When a sample is heated in vacuum to a temperature high enough for vaporization to occur, the vapor phase will consist of metal and metal-oxide gas, the oxygen concentration being very low. The phase relationships in the surrounding binary systems have already been reported in the literature; therefore, the study of the ternary diagram

Jan 1, 1962

By Edwin Berry

THE consideration of the present value of a mine is of great importance when planning for the operation of a property,, and it is particularly so in the case of mines that have large ore reserves. At various times during the past 15 years, the writer has had occasion to make rather thorough studies of the subject, and has been greatly impressed by certain important points which these studies have brought out, points which, though they may be well known, are often lost track of in the rush to obtain low mining costs and high daily tonnage output. . It is the object of this paper to present briefly, and in a general way, some of these points, and especially those which have to do with the relationship which (1) ore reserves and plant capacity, (2) grade of ore mined, and (3) ore losses in mining, bear to the present value. Present value, sometimes called present worth or actuarial value, means the value today of the future earnings of an enterprise. Great industrial, manu-facturing or railroad enterprises, if properly handled, go on indefinitely and their value is directly dependent on their estimated annual earnings. Mines, or oil properties, on the other hand, have an earning capacity only until the ore or oil is exhausted, and their present value is dependent not only on their annual earnings but also on their life, which is the length of the period over which they can produce at a profit. A mine, or an oil property, is a "wasting asset," while an estab-lished manufacturing business is not, or should not be. In other words, the present value of a mining property. represents a sum of money on which there could be paid from operating profits a determined rate of interest, say 8 per cent., and in addition an amount which, if invested at compound interest as received, would at the end of the life of the mine pay back the present value. In his "Wealth and Income of the American People," Walter Renton Ingalls says: "The fundamental principle of mine valuation is the present worth of an annual dividend accruing during the period of years corresponding to the life of the mine."

Jan 7, 1922

By J. Greenspan

The anisotropy of fracture and slip, that is, the brittleness and ductility of the beryllium single crystal, is characteristic also of po1ycrystalline beryllium in which the grains are oriented in a preferred manner. Beryllium with grain orientations resulting from hot working either unidirectionally or bidirectionally is ductile or brittle in directions given by the anisotropy and orientation of the grains. Textures developed from various hot-working sequences are given, and tensile results are correlated with textures. Not only texture, but fine grain size is necessary for obtaining high tensile elongation. Ultimate tensile strength and elongation are both correlated with grain diameter. Of particular interest is the case in which unusually high tensile elongations of 30 to 40 pct are obtained when basal planes are oriented to carry THE beryllium crystal (of nominal purity) is probably unique among metals with respect to its unusually acute anisotropy of slip and fracture. While extensive slip can occur on the system (1010) [ll20] starting at about 19,000 psi, the (0001) plane is particularly vulnerable to fracture at 4500 psi or less. Fracture occurs also on the (11zo) plane at about 26,000 psi.1"3 Further, there seems to be no other slip System which contributes significantly to

Jan 1, 1960

By B. K. Miller, R. S. Bradley

THE principal producing areas of fire clay in Missouri are: (I) the east central district, which includes Audrain, Callaway, Montgomery, Warren, and Boone Counties [ ] (Fig. I); (2) the St. Louis district, which includes St. Louis and St. Louis County; (3) the north central Ozark district, which includes Franklin, Gasconade, Osage, Maries, Phelps, and Crawford Counties. Most of the semiplastic[$] fire clay is found in Audrain, Callaway, Montgomery and St. Louis Counties, and in St. Louis. Flint fire clay is found in Callaway, Audrain, and Montgomery Counties and in most of the north central Ozark district. High-alumina diaspore clay is found only in the north central Ozark district, except a few deposits found in Montgomery County. This paper is concerned with the semiplastic fire clay that occurs in the east central Missouri district near Mexico, Audrain County, Missouri, which is mined by the open-pit method as practiced by the A. P. Green Fire Brick Co. About one-fourth of the semiplastic fire clay in that district is mined in shaft mines, and three-fourths in open pits.

Jan 1, 1941

Most of the early coal production in Tennessee was for iron-making, and here, contrary to the usual custom, coal was used in the early furnaces before charcoal was. There was no salt industry of any volume. A considerable quantity of the coal used in the state before the Civil War was brought down the Cumberland River from eastern Kentucky, and both Pittsburgh coal and coal from the river mines in Kentucky was brought up the Tennessee River. The Memphis market was supplied almost entirely by river from Pittsburgh seam mines until the end of the period. The available data did not permit the production by counties to be estimated. [ ]

Jan 1, 1942

By Seymour G. Epstein

Using a modified capillary-reservoir technique, electromigration of dilute solutions of silver in liquid bismuth has been measured with relatively good precision. The effects of experiment duration, temperature. current density, and silver concentration have been investigated. Chemical diffusion coefficients of silver in liquid bismuth were also measured at temperatures ranging from 300°to 600°C. The effective valence of silver in bismuth was calculated as a function of temperature from a comparison of electric mobilities and diffusion coefficients. In an alloy containing 1 wt pct Ag, the electric mobility of silver increased from 1.65 x X sq cm per v-sec at 300°C to 2.38 x 10-4at 600°C; the diffusion coefficient in-creased from 3.0 to 17.5 x 10-5 sq cm per sec over the same temperature range. Calculated values of effective valence decreased from 0.28 at 300°C to 0.10 at 600°c. ALTHOUGH there has been considerable progress in the theoretical treatment of electron-transport properties in liquid metals, the mechanisms of mass-transport phenomena in liquid metals are still not clearly understood. This is especially true for the case of electro migration, alternatively termed elec-trotransport or electrodiffusion, which is mass transport induced by an applied electric field. A thorough knowledge of the mechanisms governing electromigration will considerably aid in understanding the electronic state of an impurity atom in a liquid metal. Electromigration has been long observed and studied in liquid metals and alloys. However, no satisfactory theory to explain the observed effects has been developed. The disparity in the present theoretical treatments, summarized by Verhoeven,1 has been attributed to the difficulty in describing the momentum transfer between electrons and ions and to the lack of precise measurements in liquid metals, especially at elevated temperatures. Prior to the last decade most of the electromigration studies were qualitative, in that only the direction of migration of alloy constituents was determined with any degree of reliability. These results have been summarized by schwarz,2 who was able to measure the electric mobility of several elements in mercury. More recently electromigration in liquid metals has been measured by a variety of techniques, with a varying degree of success. Mangelsdorf3,4 made precise measurements on dilute amalgams at room temperature, using a technique relating changes in composition to changes in alloy resistivity, but was unable to make measurements at elevated temperatures. Using a modification of this technique, Verhoeven and Hucke5 measured electromigration and resistivities in liquid Bi-Sn alloys. However, the resistivity technique is not sensitive to small composition changes and is impractical for very dilute alloys. Verhoeven and Hucke6 also measured electromigration of several solutes in liquid bismuth by adapting the capillary-reservoir method for determining diffusion coefficients in liquids. The reported precision of these measurements was poor, however, primarily due to the large uncertainties in the chemical analyses to determine concentration changes. Belashchenko7 has summarized the recent Russian investigations of electromigration, many of which, however, are of questionable accuracy. The present study was initiated to develop an experimental technique which would be both versatile and sufficiently sensitive to yield precise measurements of electromigration of solutes in dilute metal alloys at elevated temperatures. Using this technique, a comprehensive study of silver in liquid bismuth was made to determine the effects of experimental variables on the apparent electric mobilities. Chemical diffusion coefficients of silver in liquid bismuth were also measured over the same temperature range for comparison with the electromigration data. EXPERIMENTAL TECHNIQUE Electromigration Measurements. Electromigration of silver in liquid bismuth was measured by the capillary-reservoir technique, similar to that used by Verhoeven and Hucke,6 but modified to yield more

Jan 1, 1967

Discussion of the paper of Frederic P. Dewey, presented at the Cleveland Meeting, October, 1912, and printed in Bulletin -No. 70, October, 1912, pp. 1075 to 1101. EDWARD KELLER, Perth Amboy, N. J. (communication to the Secretary *) :-Mr. Dewey, in his paper, offers a liberal addition of new data to those already to be found in the technical literature on this subject. However, now as before, the work issuing from the U. S. mints and assay-offices conveys the impression that systematic sampling in those institutions is more or less a secondary consideration, the chief attention being given to the principle of producing approximately homogeneous bars; recourse being taken to remelting or refining the bullion. This practice has been definitely rejected in the realm of copper-bullion sampling, for the reason that in such operations there are always unaccounted losses. Does not the same objection hold true for gold-bullions; although, perhaps,in a lesser degree ? Differences of opinion would seem justified on the following statements made by Mr. Dewey: 1. "Only two classes of alloys can form homogeneous bars-those that are solid solutions, and the eutectics."

Jan 3, 1913