"Coupon testing has been used to investigate stress corrosion cracking (SCC) of rockbolts in a laboratory based experimental program. This program has focused on the use of ASTM G39 three- and four-point bent beam coupon specimens, immersed in an acidified sodium chloride test solution containing hydrogen sulfide. The specimens were loaded to a range of stresses from zero, to just above the materials yield strength. It was found that only specimens above an applied stress of 580MPa failed by means of SCC, showing that rockbolts loaded to near their yield strength may be susceptible to SCC in-situ.INTRODUCTIONStress corrosion cracking (SCC) is a failure mechanism that affects material through the growth of hairline cracks when exposed to a corrosive medium while under stress (Jones and Ricker, 1999). SCC has been found to affect rockbolts in the Australian underground coal mining industry and has the capacity to cause the catastrophic failure of ground support systems, potentially leading to falls of ground in underground excavations, injury or death to mine personnel, damage or loss of equipment, and loss of productivity through the loss of roadway access (Crosky et al, 2002).Coupon testing utilises small scale samples that are intended to be indicative of the behaviour exhibited by a material in-situ (ASTM G39). The small scale, and usually high surface area to volume ratio of coupon specimens mean that they corrode at faster rate proportional to their mass, greatly reducing testing times. The small scale of the specimens allows them to be more easily prepared and handled, loaning them to mass manufacturing techniques.A previous study conducted by Vandermaat et al (2012b) into the use of three- and four-point coupon testing in-situ in an underground coal mine failed to result in SCC of the specimens. This paper serves as a follow up laboratory investigation in order to understand why these specimens did not fail. Previous studies into the SCC in rockbolts carried out by Gamboa and Atrens (2003) determined that rockbolt steel has a critical stress threshold of approximately 90% of the material ultimate tensile strength (800-900MPa). This study will focus on this critical stress threshold as a possible explanation for the lack of failure in the in-situ specimens (Vandermaat, 2012b)."

Jan 1, 2015

By H. Wilton Clark

"IntroductionTHE CANADIAN use of short-period delay-action detonators in coal shooting has been carried on for about two years, mostly in British Columbia, and this is a preliminary report on progress to date. Entire coal faces are being shot successfully with one application of electric current.The electric blasting cap came into use about the beginning of the century. The low-tension electric cap, the type most commonly used, consists essentially of a metal tube containing an initiating explosive. Two wires lead into the end of the cap and are connected inside the cap with a short 'bridge wire .of very high resistance. This •bridge wire is buried in a match-head of a readily ignitable powder composition. When current goes through the lead wires, the bridge wire becomes extremely hot and sets• off the match-head which, in turn, ignites the powder just below it in the tube. This explosion sets off the main charge of explosive. Thus, by connecting a group of caps to a source of electric .current, a number of charges could be exploded simultaneously. This immediately became of great value to mine and quarry operators. Explosives could now be used to break up large masses of material at one time, as against the older, slow method .of blasting small amounts with single charges.The next step was to develop a delay detonator which would allow charges of explosive to fire one after the other, one or two seconds apart. Such detonators allowed first blasts to relieve some rock burden before the next charge fired, giving the second charge an easier task in forcing out more rock, and so on for the rest of the series of charges."

Jan 1, 1953

By D. Kim

Kennecott operates one of the largest and most modern copper refineries in the world at Magna, Utah, USA. The inputs to the refinery are anodes produced at Kennecott Smelter, which has extremely high contents of lead and bismuth. In order to minimize undesired effects in the electrolytic refining process, unwanted impurities, especially bismuth, must be controlled. This paper describes the process development of practicing state-of-the-art quality control and presents the pilot test results of using the MRT Technology for Bi production.

Jan 1, 2007

By J. S. Redpath, W. R. Dengler

"A description of the equipment used and the electrical-mechanical problems encountered in sinking a deep shaft is given. This shaft is currently being sunk to a depth of 7,115 feet. Some of the features of the sinking plant are a 6,500-hp double-drum hoist, a Blair stage hoist, special high-capacity mucking gear, a Galloway stage, high-tensile stage suspension ropes and 12-ton sinking buckets.INTRODUCTIONIN THE EARLY FALL OF 1965, a contract was let, by The International Nickel Company of Canada, Limited, to Shaft Sinkers (Canada) Limited -J. S. Redpath Limited -Joint Venture, • to sink and equip the Creighton No. 9 shaft at their Creighton Mine proper-ty in Ontario. This paper describes the electrical and mechanical equipment used by the contractor on this project, and details various problems that were en-countered.The shaft itself is circular in section and is lined with monolithic concrete. Upon completion, it will feature twin skip compartments, a cage compartment, counterweight compartment, manway and pipe compartment. The finished diameter of this opening will be 21 feet and the shaft will bottom 7,115 feet below the collar. The present depth of the shaft (April, 1968) is 5,400 feet. The opening is concrete lined as excavation takes place and the steel will be placed in the shaft upon completion of sinking. Hoisting is done on rope guides which are part of the stage suspension system."

Jan 1, 1968

By K. Shen, A. J. Sinclair, N. Champigny

"Fluid inclusion studies from the Cinola deposit indicate low salinities and low C01 contents of the ore fluid. This supports a suggestion that the mineralizing fluids originated from pore water in the fluviatile host rock (mid-Miocene Skonun Formation). Bimodal distribution of filling temperatures suggests the existence of at least two temperature regimes centred on 160°C and 270°C during mineral deposition. Independent age and stratigraphic evidence indicates that depth of mineralization is between 1.1 and 1. 8 km, corresponding to a hydrostatic load of between 110 and 170 bars.RESUMELes donnees sur les inclusions fluides du gisement Cinola indiquent de basses salinites et basses teneurs en C01 . Ceci confirme que les fluides mineralisants ont ete derives de l'eau interstitielle prise dans les sedimentsfluviatiles hates. La distribution bimodale des temperatures d'homogenisation implique !'existence de deux regimes de temperature concentrees vers 160°C et 270°C pendant Ia mineralisation. La profondeur alaquelle le gisement s'est forme est evaluee d'etre entre 1.1 et 1.8 km a partir d'informations stratigraphiques independantes: ceci correspond a des pressions hydrostatiques de 110 a 170 bars."

Jan 1, 1982

By L. C. S. Dharmasiri, S. M. Shin, A. Senaputra, J. S. Sohn, K. H. Park, J. Avraamides

Reducing agents can be applied to leach metal values from natural and secondary resources such as laterite ores and deep sea manganese nodules and recycled materials such as spent batteries / catalysts which contain high-valent metal oxides of manganese, cobalt and iron. Selective leaching of some metals can be achieved by selecting conditions to control the saturated solubility and dissolution rates of metals from oxides or mixed metal/oxide matrices. The leaching results are rationalized on the basis of chemical species, Eh-pH diagrams and heterogeneous kinetic models. The role of reducing agents such as hydrogen peroxide, sulfur dioxide and iron(II) sulphate, in acid, alkali and in the presence of complexing ligands such as ammonia for the improvement of the leaching of metal oxides and metals is discussed. Previous studies on acid leaching of metals from nickel laterites, manganese nodules and spent catalysts/batteries in the absence or presence of reducing agents show that the rate controlling step involves the diffusion of protons through a thickening product layer on the particle being leached. It is shown that the leaching of nickel and cobalt from manganese nodules and zinc-carbon batteries in ammoniacal sulphur dioxide solutions also obey shrinking core kinetics.

Jan 1, 2014

By A. LA. Salama, D. B. Hyma

"The Western Research Centre (WRC) of CANMET located in Devon, Alberta, is a modern research facility offering services ranging from fundamental research to pilot plant investigations. Recently, a 0. 76 metre diameter by 7.9 metre high Flotaire column flotation cell was installed as a demonstration unit for Canadian coal producers. Because the column cell is intended to be used for research, development and demonstration, WRC recognized that additional sensing equipment and improved process control would be required to generate good data for subsequent column scale-up and engineering design.A low cost, personal computer based control system was, therefore, designed and installed. This paper describes the stepwise procedure in developing the control strategies, selection of system software and hardware, and installation and configuration of the system.Preliminary performance data on a western Canadian coal sample are also presented. Future testwork is planned on additional coal samples to expand upon existing database."

Jan 1, 1993

By C. Veloo

"Westmin Resources operates a mine/mill complex at Myra Falls and produces copper and zinc concentrates with minor associations of gold, silver, and lead from a polymetallic, massive sulphide orebody. Mill flotation performance has historically been plagued by periods of uncontrollably high circulating loads leading to low concentrate grades and below optimal tails. This led to a detailed examination of the flotation process. Locked cycle, and pilot plant data are presented. In addition, plant design and commissioning as well as column cell details are discussed. A comparison between actual and predicted performance is also presented. Benefits realized are higher copper and zinc concentrate grades and improved zinc recovery.PrologueMyra Falls Operations is located at the south end of Suttle Lake in Strathcona Provincial Park. Access to the mine site is provided by a 90km paved highway from Campbell River, British Columbia.The mine and facilities are nestled in the narrow Myra Valley between Mount Phillips and Mount Myra. These steep, rugged mountains rise from the valley floor at an elevation of 900 feet to summits of almost 6000 feet. The steep slopes are heavily wooded with fir, hemlock, and cedar up to an elevation of 4000 feet where a transition to alpine meadows occurs. The summits are craggy rock faces, some capped with glacial ice. Myra Creek winds its way through the valley dropping several hundred feet into Suttle Lake. Precipitation is high at over 100 inches per year, which may include up to 10 feet of snow in winter. The temperature may range from 32° C in summer to -18° C in winter.Myra Falls began production in 1965 with the Lynx Mine, supplemented by the Myra and Price Mines in subsequent years, feeding a 950 stpd mill up until the middle of 1985 when the H-W mine was brought into production. The original mill was replaced with a modern 2700 mtpd facility and in 1988 production was increased to 4000 mtpd.Both Lynx and H-W mines are currently in production producing an average of 3650 mtpd. The ore minerals are primarily sphalerite and chalcopyrite, with subordinate galena, bornite, tetrahedrite, and electrum."

Jan 1, 1992

By C. G. Bruce

"ON NOVEMBER 15th, 1950, the Department of Mines and Technical Surveys announced the discovery of vermiculite near Perth, Ontario. The announcement followed nearly a month of study to determine so far as possible the potentialities of the deposit and quality of the material from surface indications. The mineral was identified by the writer in the field among samples submitted by Mr. Arthur Powers of Stanleyville or, September 22nd, 1950. Within a week of the announcement, mining rights to properties covering a major portion of the deposit had been acquired by commercial interests.Hitherto, Canada has had to import her entire requirements of vermiculite. Prospects of .a domestic supply gave promise of considerable benefit to many industries, particularly the building industry, and to the consumer public. Should the deposit •prove large enough there was also the possibility of exporting to centres in the United States.Field and laboratory studies were continued at the Mines Branch during the winter of 1950-51 as opportunity occurred. It is the purpose of this paper to describe the results of these •preliminary investigations, to attempt to present the Stanleyville occurrence in its proper perspective with regard to similar occurrences elsewhere, and to review the salient features of the vermiculite industry.Properties and UsesVermiculite is a hydrated magnesium aluminum silicate. In appearance it resembles mica, having the same micaceous cleavage, but it differs from that mineral in being very soft, pliable, and inelastic. Colours range from black through dark olive-green and brown to almost colourless."

Jan 1, 1952

By J. W. Kramers, R. A. S. Brown

"Samples from seven test wells distributed throughout the surface-mineable area of the Athabasca Oil Sands have been evaluated to determine the amounts of heavy minerals present and the titanium and zirconium contents. The samples were treated to yield the size distribution of the titanium and zirconium minerals as well as their spatial distribution. The study has shown that heavy minerals are found throughout the surface-mineable area; concentrations range from 0.24 to 2.29 per cent (by weight), with a mean of 1.02 per cent. Titanium and zirconium contents vary throughout the area, and are found preferentially in the finer size fractions. •on the basis of preliminary calculations, the tailings streams from an oil sands plant would provide sufficient feed for a large-scale titanium pigment plant, and the tailings from one plant would provide sufficient zircon feed to satisfy Canadian demand for. metallic zirconium. Variability of the heavy mineral content and composition is such that the heavy mineral potential must be evaluated in detail for each mine site."

Jan 1, 1976

By D. R. Lentz, C. J. Beaumont-Smith, S. H. Mcclenaghan

"Abstract - The Louvicourt Au-Ag-Cu-Zn-Pb sulfide deposit is hosted by a Middle Ordovician calc-alkaline sequence of aphyric rhyolite flows and associated fragmental rocks at the top of the Flat Landing Brook Formation. The Zr/TiO2 (average = 0.110) and Y/TiO2 (average = 0.021) ratios in the footwall felsic volcanic rocks are consistent with known values for the Reids Brook member. The deposit consists of two concordant lenses of semi-massive to massive sulfides, approximately 150 m long and up to 9 m thick, which represent a fold repetition of a single exhalative horizon. The deposit contains a geologic resource of 136 000 tonnes grading 1.2% Pb, 1.0% Zn, 0.4% Cu, 90.9 g/t Ag, and 0.96 g/t Au; the deposit locally contains elevated Au (2.9 ppm) and Ag (320 ppm) contents. A laterally continuous iron formation that contains barite caps the deposit, and is gradational vertically and laterally into laminated siltstone. The exhalite confirms the stratiform nature of this deposit, but a large percentage of sulfides occur as late replacements of altered felsic fragmental rocks in the footwall. Abundant examples of colloform pyrite and perlitic and spherulitic textures in volcanic clasts are well preserved. The base- and precious-metal content of the Louvicourt deposit is atypical of the Bathurst Mining Camp (BMC). Reported assay data (n = 27) indicate an average Pb/Zn ratio of 2.6, the highest in the BMC (average = 0.39). Lead exhibits a strong Spearman Rank correlation (r' = 0.92) with base metals throughout the sequence, indicating a preponderance of galena in both the stockwork and stratiform zones. The Ag and Au contents in this deposit are among the highest in the BMC and exhibit a Au-Ag- Cu-Pb association. Barite-rich exhalative pyrite exhibits a moderate Au correlation with Ag (r' = 0.77; n = 10) and Cu (r' = 0.76) and occurs in portions of the exhalative sulfides that are enriched in Pb. Chemical exhalative rocks are conformably overlain by trachy-andesitic volcaniclastic (possibly pyroclastic) rocks that are assigned to the Little River Formation. These are enriched in Nb (average = 38.4 ppm) and P2O5 (average = 0.17 wt.%), and have much lower Zr/TiO2 (average = 0.056) and Y/TiO2 (average = 0.0062) relative to rocks higher in the hanging wall. The intermediate volcanic rocks are conformably overlain by massive to pillowed basalt flows and related hyaloclastite that have Nb/Y = 0.60 and high TiO2 contents (average = 2.8 wt.%). This chemistry is consistent with rocks of the Brunswick Mines member (Little River Formation), except that these rocks are considerably enriched in P2O5 (average = 0.82 wt.%). This syngenetic exhalative deposit is unique for the BMC with a high Pb/Zn and elevated Au and Ag contents, as well as an epithermal signature (Sb-Ag-Au-Tl-Hg), analogous to high sulfidation volcanogenic massive sulfide deposits. Its intimate relationship with an emergent felsic dome (Flat Landing Brook Formation), chlorite-silicate-oxide-sulfide exhalite (locally hematitic), and the abundance of barite are classical features of many of the Kuroko deposits."

Jan 1, 2006

By W A. James

The use of spectrographic semi-quantitative analysis has recently been of considerable value in establishing the geological relationships in a complicated orebody. The principal minerals found in the Mount Pleasant orebody are cassiterite, stannite, sphalerite, molybdenite, wolframite, chalcopyrite and galena, associated with arsenopyrite, pyrite and fluorite. In addition to the large number of minerals, a further com-plication is the non-uniform distribution of the economic minerals, with one mineral being the only one present in major amounts in one area and another mineral being predominant in another area. At the same time, all minerals are present to a minor extent throughout the deposit. This heterogeneity made it advisable to analyse all exploration samples thoroughly. Analysis by conventional means would have resulted in prohibitive costs. By the use of emission spectroscopy, however, it was possible to obtain, quickly and relatively inexpensively, a reasonably comprehensive picture of the orebody un-der investigation.

Jan 1, 1963

By D. R. Griffiths

"Oxidation of pyrrhotite prcxiuces sulphuric acid which in turn leaches out heavy metals, resulting in acidic contaminated seepages. The establishment of a marsh on top of the pyrrhotite would result in an anaerobic sediment, which should prevent further oxidation of the pyrrhotite. Initial data indicates that concentrations of sulphates and heavy metals in the seepage water are greatly reduced. Further hydrogeological studies are required however, to determine if metal and acidic loadings to the environment have increased.L'oxidation du sulfure de fer produit de l'acide sulfurique qui a son tour attaque les métaux ayant pour resultat une contamination d'acide et de métal des eaux d'infiltration. L'etablissement d'une couverture faite de boue et de vase au-dessus du depot du sulfure de fer réduit les effets de l'oxidation.Les données initiales indiquent que les concentrations de souffre et de métaux dans les eaux d'infiltration sent grandernent réduites.Des études plus poussées sent nécessaires pour déterminer si les quantités de souffre et de métaux dans les eaux d'infiltration ont augmentées.INTRODUCITONPyrrhotite tailings are readily oxidized through a combination of precipitation and atmospheric oxygen causing acidification of the unsaturated zone above the water table. This reaction is usually catalyzed by the bacteria, Thiobacillus ferooxidans. As the pH decreases, heavy metals become more soluble resulting in contaminated seepages to ground and surface waters.By creating a marshland on top of the pyrrhotite, an anaerobic intermediate layer should form between the organic covering and the tailings, preventing the oxidation process from progressing.In September 1986, Falconbridge Limited implemented a tailing reclamation project that involved creating a marshland on top of pyrrhotite tailings. The following paper will discuss and illustrate the preliminary results obtained during the sampling period of May to September 1987."

Jan 1, 1988

By John A. Herbst, Xiangjun Qiu

"Prediction of wear on a microscale level in mineral processing equipment turns out to be a challenging undertaking. This is particularly true for cases in which the objective is to use such predictions for wear parts design. The key to obtaining such predictions has turned out to be the use of physics based models along with phenomenological constitutive equations. In this paper, two components of the HFS tool set, one for particles (DEM) and one for slurry (MPF), are used for modeling. These tools are applied to the simulation of wear of SAG/AG shell lifters/plates and wear in slurry pumps. In each case wear predictions are validated with plant measurements.INTRODUCTIONHigh Fidelity Simulation (HFS) has emerged as an important tool set for mineral processing plant equipment design and optimization (Herbst and Potapov, 2003; Herbst and Nordell, 2002; Herbst and Lichter, 2006). This tool set consists of Discrete Element Modeling (DEM) of particle motion, Multi-Phase Flow (MPF) for liquid motion, discrete grain breakage (DGB) for particle fragmentation and discrete grain liberation (DGL) for mineral liberation (Campbell, Potapov and Tsuji, 1997; Ferzinger and Peric, 1997; Potapov and Campbell, 1996; Herbst and Potapov, 2005).Three sample snapshots of basic HFS illustrating the use of each of the various types of mineral processing equipment are shown below.Figure 1 shows a snapshot of a DEM simulation of ball charge motion in a commercial scale Vertimill. DEM simulation involves simultaneous solution of Newton’s Laws of Motion for 400,000 balls."

Jan 1, 2007

By Maarten van de Vijfeijken, Marco Rufli

"By using the latest generation of medium voltage frequency converters, new possibilities have arisen to improve the grinding process. Beside all the direct and indirect advantages, several dedicated functions have now been implemented for ring geared grinding mills in the minerals industry. The advanced operational functions ensure a smooth, safe and reliable operation with minimum stress for the mechanical equipment and therefore highest availability of the mill. Several papers have already been presented concerning the benefits of using this state of the art technology for mill drives (Ravani von Ow and Bomvisinho, 2010; Ravani von Ow and Gerhard, 2010). However this paper will not only show and explain the operational benefit of these functions, but will focus on the experiences gained with this kind of sophisticated ring geared mill drive system. Several measurements of different operating conditions (starting, frozen charge remover, controlled roll back, backlash, etc.) made on an installed and commissioned 2 x 5 MW dual pinion ring geared mill drive system will be shown and discussed. Also the accuracy of the load sharing between the two 5 MW motors during starting, normal operation and stopping will be demonstrated using real measurements from an operating system. Finally the inherent features of these drive systems are briefly discussed.INTRODUCTIONLooking at the demands of grinding mills, we can split them into operational, maintenance and protective demands. For smooth and safe operation, it is important that critical situations are avoided as much as possible. Maintenance functionality must be quick and easy to execute, while protection of the system is important during all operating conditions. ABB has considered all these demands during development of their dedicated mill functions. By adding an additional controller (mill controller), not only a lot of application related functionality and protection is included, but also the interface between the mill drive system and the customer’s distributed control system (DCS) is simplified."

Jan 1, 2011

By J. Keough

During industrial electrowinning of copper, uneven growth can impact current efficiency, cause short-circuits in the cell and negatively impact the final quality of the metal product. Copper electrodeposits can be made smoother by incorporating a host of additives in the electrolyte but uneven copper growth may still occur due to variations in electrolyte composition throughout the cell-house. To quantify roughness, 3D images of the surface may be combined with scaling analysis to gain further insight into the deposit structure. Moreover, scaling analysis may offer a method to predict long-term deposit structure using short-term copper deposits. In this paper, the application of Atomic Force Microscopy (AFM) and scaling analysis are used to monitor copper growth and extract surface roughness characteristics. The cathode was a 304 stainless steel disc that was polished to a mirror finish. Copper was deposited onto this surface over a range of 10, 20 and 30 minutes from an acidic sulfate solution (40 g/L Cu) at 40oC from an electrolyte that contained or was free of guar. AFM images were acquired to obtain 3D topographical information on the samples and scaling analysis was performed to extract the root-mean-squared (rms) roughness, periodicity (grain size), aspect ratio of surface features and growth mechanism. INTRODUCTION During the process of copper electrowinning, the dissolved metal ions are reduced and thereby deposited onto a cathode substrate which is later recovered by stripping the metal from the cathode surface. Although this process is widely used in the industry, the conditions of the deposition procedure may cause the growth of the metal product to be uneven which can not only impact the current efficiency and final copper product quality but may also lead to plant interruptions through short-circuits if the anode and cathode make contact. To create more uniform copper deposits, a host of additives may be included in the electrolyte which may act as brighteners, leveling agents and inhibitors which may include guar gum, glue, thiourea or polysaccharides or polyacrylamides and their industrial use has changed over time (Moats, Luyima, & Cui, 2015). As such, the electrolyte composition is often complex and subtle variations in the solution matrix throughout the cell-house may impact the surface morphology of the final copper product. In an effort to quantify the roughness of copper samples, image analysis is often applied and may include Scanning Electron Microscopy (SEM) or Atomic Force Microscopy characterization. While both are appropriate, AFM offers 3-dimensional information which may be used to both qualitatively and quantitatively characterize the surface characteristics.

Jan 1, 2019

By A. Rajan

"Drawing upon the experiences of a gold extraction plant startup in the Southern Pacific, this paper will describe the importance of the commissioning phases to the project outcomes to achieve early target production despite an overall time compression to attain full plant production. Some of the highlights of the paper include: impact of roles played by the Owner’s construction and operations representatives during project commissioning, the formation of a capable and competent “Mod Squad,” availability of trained operating personnel, control over work priorities and the scope of work needed to bring the plant to safe initial operations. The commissioning team comprised subject matter experts skilled in process technology supported by “generalists” thoroughly conversant in overall plant operations. The merits of a structured team approach to brainstorm and resolve commissioning challenges as opposed to direction from individual subject matter experts is discussed. IntroductionStartup or commissioning is a unique period in the life of a project. Each stage of a project-exploration, feasibility, design, construction, commissioning, initial operations and continuing operations-requires special talents, know-how, and practices. Each stage makes particular demands of the people involved. Initial operations are no exception.Having experienced the 1997 startup phases of oxide and sulfide facilities for a gold extraction plant at a remote island in the Southern Pacific, I can attest to the many challenges and rewards. Commissioning for both facilities was extremely successful and brought the entire project on line well ahead of the targeted completion dates. Using this specific project as an example, this paper will highlight some of the key features of project commissioning. In this paper, the term “pre-commissioning” denotes all activities that lead to mechanical completion; “commissioning” occurs when feed is introduced; and “initial operations” are defined as the duration when operations accepts the system/facility and takes over."

Jan 1, 2000

By B. Daniels, A. Tieu, W. Yan, B. Ren, M. Vijay

"Plasma or thermal sprayed coatings are becoming more widely used in a wide range of industrial applications. The preference to use thermal sprayed coatings is mainly attributed to its superior wear, and corrosion resistant properties akin to hard chrome but without the harmful health implications of chrome in the coating process. Specifically, High Velocity Oxygen Fuel (HVOF) plasma sprayed Tungsten Carbide & Cobalt (WC/Co) coatings are presently being tested on aircraft landing gear. This coating can be efficiently applied and is highly resistant to corrosion and wear. However, HVOF coating's durability also makes it difficult to be stripped for inspection and overhaul. Current coating removal methods usually involve a multi-step process whereby the coating must undergo diamond wheel grinding, chemical dipping, grit blasting, ultrahigh pressure (UHP) 380 MPa (55 Kpsi) water blasting, and subsequent chemical dipping, depending on the type and thickness of the coating. As explained by Yan, et al [l]"" a unique method has been developed for removing HVOF coatings with the use of only water. The method consists of modulating a stream of water at a pressure of only 69 MPa (10 Kpsi) with ultrasonic waves to generate a forced pulsed waterjet. The resulting cyclic loading of the hard coating due to the impact of the water pulses easily causes it to flake off the substrate. This paper will briefly describe the fundamentals of the forced pulsed waterjet technique with an emphasis on insitu applications of the removal of various plasma and HVOF coatings."

Jan 1, 2006

By J. B. Mawdsley

Introduction The writer was instructed to visit the Chibougamau region during the field season of 1927 and report on the mineral discoveries that had been made there since 1911. lt was deemed advisable to obtain detailed information regarding the rocks underlying the area in the vicinity of these recent discoveries. Accordingly an area 60 square miles in extent was mapped. The outcrops were studied along the water courses and along bush traverses spaced at half-mile intervals between these water courses. The completion of the rest of the summer's programme allowed only three weeks for this work. lt is from this small, mapped area, and this necessarily cursory survey, that the material for this paper was obtained. Location And Means Of Access The name Chibougamau district is applied loosely to an ill-defined area of about 1,000 square miles lying mostly north and west of Chibougamau lake in the Province of Quebec. The lake is approximately half way between lake St. John and James bay. It lies 150 miles north of the Canadian National railway and 40 miles south of Mistassini?lake.

Jan 1, 1928

By M. M. C. Lima, L. C. S. Solimani, M. A. Quintela

Galvanized steel scrap is recycled to B OF converters where zinc escapes from the bath and is captured by the gas control system, appearing in BOF sludge. As BOF sludge contain high iron content, it could be recycled, but due to its zinc content, it is disposed in landfills. In this study techniques were evaluated for zinc layer removal from scrap by sulfuric acid leaching. The effects of coating weight, temperature, time and sulfuric acid concentration were evaluated for three different galvanized scrap. The results showed that the behavior of each galvanized scrap was different. Nevertheless zinc removal efficiency was more than 80% with low dissolved iron in the leached solution.

Jan 1, 2011