"The paper describes the results of the flotation tests with complex rare metal ores from deposits in the Trans-Baikal Territory. Correlations between the quality of produced wolframite, hubnerite and mica concentrates with or without the presence of various alkaline modifiers are determined. Commonly, rare metal ores contain minerals of comparable value to main elements recovered in processing plants using gravitational methods. The paper describes the results of flotation recovery of valuable minerals – main and associated – from gravity tailings of deposits in the Trans-Baikal Territory. It was found that gravity tailings from the first deposit contained fine-grained wolframite, mica (muscovite, lepidolite etc.), feldspar; hubnerite, scheelite, beryl, fluorite, rubidium-containing muscovite from the second deposit, correspondingly. This paper presents the results of the stage flotation tests with the production of tungsten (wolframite, hubnerite), fluorite and mica concentrates from gravity tailings. Figure 1 demonstrates the flowsheet of tungsten ore minerals and mica stage flotation from gravity tailings of the first deposit.Wolframite can be floated using oleic acid with the presence of soda ash, a complexing collector (IM-50), under slightly alkaline conditions in combination with a nonpolar collector [1, 2, 3, 4]. The study included wolframite flotation using the combination of two alkaline modifiers. Flotation of wolframite was performed after pulp desliming, using tall oil saponified with soda ash. The recovery of wolframite in the concentrate of rougher flotation reached 80-85%; the concentrate contained up to 1% of tungsten oxide that can be upgraded to a saleable product using gravitational methods. This procedure was tested during flotation of wolframite, tantalite-columbite and pyrochlore, and provided high performance regardless of a season, at pulp temperatures of 8-10°C, though fattyacid collectors are significantly inefficient at such low temperatures due to low solubility, dispersion and increased collector consumption, consequently. The introduction of two alkaline modifiers in pulp appears to improve these characteristics.The first stage of the tests was focused on increase of iron-bearing tungsten ore minerals recovery from gravity tailings and stabilization of the cold pulp flotation process."

Jan 1, 2018

The major components of sylvinite ores, sylvite (KCl) and halite (NaCl), are separated by flotation. Since both these minerals are water-soluble, the process is carried out in a saturated brine, 6~7 mol/L aqueous solution of NaCl and KCl. C16~C22 primary amines, utilized as a collector, are practically insoluble in water. In commercial potash ore flotation operations these amines are melted by heating up to 70~90°C. They are then neutralized with hydrochloric or acetic acids, and such a hot emulsion/dispersion is introduced to the flotation pulp (which is at room temperature). This is immediately accompanied by the appearance of a white precipitate in the system. As our measurements indicate, the Krafft point of dodecylammonium chloride in concentrated electrolyte solutions is much higher than 80°C, and the Krafft point of C16~C22 amines is substantially higher than that. Introduction of a hot amine emulsion into a pulp, at temperature much lower than the Krafft point for the utilized amines, must cause precipitation of the amines. Some of these species are obviously flotation-active. It is interesting to observe that in summertime, when temperatures are high-er, longer chain amines perform better. It demonstrates that the colloidal amine species that precipitate serve as active species in the potash flotation. Therefore, at higher pulp temperatures, when the temperature difference between the pulp temperature and the Krafft temperature of the utilized amine is not sufficiently large, a longer chain amine, the amine with a higher Krafft point, is more efficient. The results reveal that premixing of an alcohol such as MIBC (common frother) with the amine significantly improves flotation performance of the amine. In the presence of such an alcohol the amine disperse system becomes less turbid, and the rheology of the system less non-Newtonian. All this indicates that MIBC, which does not operate as a frother in a potash flotation system, when used as a co-surfactant, enhances the dispersion of the amine colloidal system. The appearing colloidal species perform as an active form of the collector.

Jan 1, 2014

By A. P. Purgin, M. G. Viduetsky, I. F. Garifulin

"The combined treatment process for mine, tailings storage facility, quarry, circulating, and waste water in the mining and metals industry brings together the conventional chemical treatment processes and pneumatic flotation cells of the KFM series. The key principle of the process is preparing the water for treatment by saturating with finely dispersed air bubbles in the flotation cell blowers. Gas-air lift dispersers located in the lower part of the cell body additionally saturate the cell’s contents with finely dispersed air. Due to the residual content of flotation agents in the treated water, hydroxide ion-air aggregates form at the aerator outlet, supporting the efficient precipitation of hydroxide ions of heavy non-ferrous metals, calcium and magnesium ions. This process was tested in the pilot plant KFM-180 with a raw (untreated) water capacity of up to 18 m3/h per 1 m3 of the flotation cell volume using a mixture of the tailings storage facility and mine water from JSC Safyanovo Copper. The treatment process included raw water treatment with lime, aeration in KFM cells, and filtration in a sorbent bed. The content of metal ions in the treated water is lower than in the feed water by a factor of up to 170,000 and approaches the standards: aluminum 0.016-0.02 mg/l, copper 0.0043-0.0045 mg/l, zinc 0.049-0.052 mg/l. circulating water of Soryin Tailings Storage Facility at JSC Svyatogor. The treatment process included raw water treatment with lime and alkali, aeration in KFM cells, and filtration in a sorbent bed. The content of metals in the treated water is lower than in the feed water by a factor of up to 9000: copper 0.022 mg/l, zinc 0.012 mg/l, iron 0.012 mg/l, manganese 0.015 mg/l, nickel 0.132 mg/l, arsenic 0.016 mg/l. Water hardness is significantly lower: calcium - 12.6 mg/l, magnesium - 1.1 mg/l. This process can be used in the treatment of mine, quarry, tailings storage facility, and circulating water at mining and non-ferrous metals projects."

Jan 1, 2018

By Andrew T. McBride, Malcolm S. Powell, Indresan Govender

"Current empirical Semi Autogneous Grinding (SAG) mill models contain assumptions concerning the amount of energy available for particle breakage, how this energy is distributed in the mill media and the rate at which the energy is transferred. Despite these assumptions the JK SAG model is highly functional with a proven track record. DEM provides a numerical framework to greatly improve on these assumptions that were necessary due to a lack of available input data.This paper identifies key outputs of the Discrete Element Method (DEM), such as energy spectra and impact probability distribution. It describes how they can be incorporated into current mill models utilising practical rock breakage data. The rate at which energy is transferred is shown to be dependent on particle position and mill rotational speed and not once per cycle as previously assumed. Based upon this an improved energy transfer methodology is presented. The fundamental outputs of the DEM are validated against experimental three-dimensional particle tracking data, so as to establish whether the DEM produces correct energy transfer predictions on the inter-particle level, which is crucial to this work. • Effective Experimental ValidationAn automated 3D tracking technique is employed to study the motion of plastic particles deep within the charge of a 142mm diameter experimental mill. A Biplanar Angioscope is used to film the mill with X-rays in two planes simultaneously at 50 frames/s, with a shutter speed of 1/3000s. A marked ball within the charge is tracked for over 2 minutes and the resulting digital images processed by a fully automated imaging technique, which locates the 3D coordinates of the particles to within 0.2mm. With over 250 circulations, this provides statistically rigorous and accurate data for verification in the numerical modelling of mills.A series of validation techniques have been developed to compare the experimental trajectory data with the outputs of both 2D and 3D DEM simulations. The techniques describe the shape of the charge and the particle motion within mill, allowing objective comparisons to be made of key features of the charge, such as the equilibrium surface and the centre-of-circulation."

Jan 1, 2003

By Xin Tan, Changgen Li

"The floatabiliby of chelate CF-collector for zinc and lead oxide minerals was described. It found that CF-collector possesses a strong collection power for zinc and lead oxide minerals as well as excellent selectivity for the gangue minerals. A new technology of zinc and lead oxide flotation with CF reagent as a collector, lead nitrite as a activator and water glass as modifier was presented. The mechanism of interaction between reagents and minerals was discussed by means of adsorption, zeta potential, nephelometric titration, XPS and infrared spectra was investigated.CF-collector, newly developed by Beijing General Research Institute of Mining and Metallurgy (BGRIMM), is a kind of chelate collector for the flotation of oxide minerals. CF-collector mainly consists of N-nitroso-N-phenylhydroxylamine ammonium salt. The CF-collector was used for the selective flotation of scheelite in the Chinese plants.In this paper, the effects of the dosages of activator Pb(NO3)2 and depressants (sodium hexametaphosphate, polyphosphate, water glass and salified water glass) on the floatabilities of several minerals (cerussite, smithsonite, calcite, dolomite, limonite and quartz) as well as their mixtures were investigated in the presence of the CF-collector. The results show that the CF-collector is the excellent collector for selective flotation of cerussite and smithsonite. Pb(NO3)2 can selectively activate the oxides of lead and zinc resulting in a decrease of the CF-collector dosage. The sodium hexametaphosphate plus the salified water glass are the effective depressants for gangue minerals. Based on the above facts, the “CF process”, namely, used CF reagent as a collector, Pb (NO3) 2 as a activator, and sodium hexametaphosphate plus salified water glass as depressant, has been used for the flotation separation of the lead oxide mixtures or zinc oxide mixtures without disliking and heating. For the feed lead assaying 19.07%, the lead concentrate assaying 49.81% Pb at the recovery 80.69% was obtained after one step flotation. For the feed zinc assaying 12.85%, a zinc concentrate of assaying 29.56% Zn at recovery 83.87% was obtained."

Jan 1, 2003

By Bertil I. Pålsson, Sture V. Persson, Kent T. Tano

"Autogenous (AG) and semi-autogenous (SAG) mills often operate in an unstable state because of the difficulty to balance the rate of replenishment of large ore particles from the feed with the consumption in the charge. This has led to an increased interest in obtaining an accurate and direct measurement of mill load and the behaviour of the mill charge. A problem in attempting to measure those parameters is getting a sensor that is both robust and sensitive enough for continuous on-line measurement.Techniques that measure the force acting on the lifter when it hits the charge inside the mill have got an increased interest recently because of the ability to combine it with DEM modeling. This paper presents a method for the measurement of the apparent filling level in a pilot ball mill equipped with the Metso Continuous Charge Measurement system (CCM). In this technique a strain gauge sensor is mounted on a flat steel spring which is fitted into a recess underneath a lifter bar. In addition, a conductivity probe, the Boliden Grinding Measurement System (GMS), is mounted in another lifter bar with the purpose of comparing the two measurements. To visualise the behaviour of the charge a 2D DEM modelling technique is used with Metso HFS software.The pilot mill is a grate-discharge mill, equipped with 12 rubber lifters of square size 0.1 m, face angle 45 degrees. Steel balls in the size range 10-30 mm and density 8000 kg/m3, are used in the experiments. Test material is a hematite pellet feed, d50 around 45um, chosen to get stable grinding conditions with respect to feed size variations.The experiment is meant as a first test of the equipment’s performance, and to study how the sensors respond to changes in some operating variables. To get an understanding of, and distinguish between correlation and causality, experiments are performed according to a full factorial design with two levels, and in addition two replicates of the experiments at a center-point in the charge level setting."

Jan 1, 2003

By A. De1

Because of the extremely low utilization of strain energy in the breakage of solid particles, the energy efficiency prevalent in comminution technology is extremely poor. Schoenert considered that single-particle comminution under slow compression is the most energy-efficient mode of comminution and that energy efficiency should be compared to that. The usual method for grinding minerals and cement has been the ball mill, in which the hit-and-miss aspect of loose-bed comminution severely reduces energy efficiency. The fine grinding of minerals is a particularly energy-intensive process. Schoenert showed that the energy consumed in the comminution of particles in confined beds is second only to that of single-particle comminution under slow compression and developed the method of conducting particle-bed comminution continuously in a high-pressure roll mill. Since its first industrial installation in 1985, the high-pressure roll mill has established itself as the comminution device of choice for significantly improving the productivity and energy efficiency of size reduction from coarse size feeds down to products finer than 20 microns. The first of several hundred installations were in cement plants. The preliminary design and optimization of the industrial operation of high-pressure grinding roll (HPGR) systems, owing to the continuous nature of the device, cannot be efficiently done through laboratory experiments and needs to be achieved through proper system modeling. While the energetics of size reduction in high-pressure grinding rolls has been modeled very well, no model exists for the macroscopic variables in HPGR comminution. In high-pressure roll mill grinding, size reduction results from confined particle-bed comminution under compressive stresses such that the daughter particles produced are highly fractured, stressed, or otherwise weakened. This paper attempts to relate the comminution / compaction behavior for confined particle-bed under compression in a piston-die press with the macroscopic variables in HPGR comminution. A model describing the pressure-densification relationship is presented and used to accurately simulate the macroscopic variables in high-pressure grinding rolls, utilizing experimental data for particle-bed comminution with the piston-die press. The accuracy of the predictive simulations strongly suggests that, starting with a few batch-mode laboratory-scale experiments, it should be possible not only to identify the optimal operating conditions for existing operations but also to successfully design new industrial high- pressure grinding roll systems.

Sep 1, 2012

By Y. X. Yang

Bottom ash is a solid waste stream in a Waste-to-Energy (WTE) processing plant during the combustion of the municipal solid waste (MSW). In the Netherlands, bottom ash contains typically about 18% metals originated from the MSW, and current industrial practice could recover about 10% metals through magnetic and eddy current separators. The remaining 8% as the finer particles is difficult to recover through current physical separation technology. Among various alternatives, vitrification is one of the promising options to immobilize the ash and recover the remaining metals. During vitrification a homogeneous glassy slag and a Fe-Cu based alloy were obtained. In the cur-rent study, the metal alloy recovered from the bottom ash originated from a Dutch Waste-to-Energy plant contains about 82 wt% Fe, 12 wt% Cu and 6 wt% other alloying elements and impurities such as C, S, P, Ni etc. The generated alloy does not have direct commercial applications, and separation of copper from iron-based alloy is critical to obtain the market value of both copper and ferrous constituents. To find a suitable processing route of this metal alloy, various alternative approaches have been considered for an efficient removal of copper from the alloy, and the focus in the present study was on the sulphide treatment at elevated temperatures of 1400 ~ 1500oC. The tested sulphide systems include pure FeS, FeS containing sulphide mixture (such as Na2S and Al2S3), pyrite (FeS2) mineral, ZnS containing sludge as an industrial waste. It was found that the carbon saturation of the alloy is proved to be an essential condition for a proper phase separation. The results showed that FeS mixed with Na2S, ZnS containing sludge and pyrite are effective sulphide systems for copper removal with a removal efficiency of 92% by using pyrite and 95% by zinc sludge at a S/Cu ratio of around 7 times of the stoichiometry. The copper content drops from 12 wt% to about 2 wt%. However, it is still difficult to remove copper completely from the alloy in a single step, and a multi-step operation is needed. The present research is expected to contribute both to the utilization of the metal recovered from bottom ash, and to the general recycling of steel scrap where copper removal from the steel scrap is a critical issue.

Jan 1, 2014

By I. Nishkov, I. Grigorova, M. Ranchev, S. Dzhamyarov

"Chelopech concentrator (part of Dundee Precious Metals) is located in central-western Bulgaria. The current process plant utilizes conventional primary crushing and SAG mill grinding, copper and pyrite rougher and cleaner flotation stages to produce a marketable gold-rich copper and pyrite concentrates. As in the most processing plants, the pyrite depression is carried out alkaline media using lime. The subsequent activation of pyrite mineral is achieved by adding sulfuric acid, which has an adverse effect on the flotation equipment. Therefore, a series of laboratory flotation experiment for activation of lime depressed pyrite by ammonium salts, such as ammonium chloride (NH4Cl), ammonium sulfate (NH4)2SO4 and ammonium bicarbonate (NH4HCO3), have been conducted. The obtained results showed that ammonium bicarbonate proved to be the most appropriate reagent choice for pyrite mineral activation. These results are confirmed by X-ray photoelectron spectroscopy (XPS), performed to determine the surface chemistry of pyrite in its natural state, after lime treatment and subsequent treatment by NH4HCO3. The registered XPS spectra indicate that the hydrophilic phases on the pyrite surface could be efficiently removed by using the ammonium salt NH4HCO3. The industrial use of NH4HCO3 as an activator of lime-depressed pyrite is a possible alternative for sulfuric acid replacement as a most widely used pyrite activator. Flotation experiments with addition of 200, 400, 600 and 800 g/t from each of the studied ammonium salts have been conducted. Furthermore, the impact of the flotation pulp pH within the scope of 9.00 – 10.50 was also investigated. The obtained results from the laboratory flotation experiments, showed that the pyrite activation with ammonium bicarbonate is an excellent possibility for replacing the sulfuric acid as main pyrite activator reagent, in order to eliminate the gypsum accumulation during the flotation of pyrite in Chelopech concentrator.INTRODUCTION The Chelopech deposit, located about 60 km east of Sofia is one of the largest Cu-Au deposits in Europe. The ore have complicated mineralogical and chemical composition. The main ore minerals are represented by pyrite, enargite (luzonite), tennantite, chalcopyrite and bornite. The average copper content of the mined ore is about 1.1 % and the gold content is about 4.0 g/t."

Jan 1, 2018

By Junwei Han, Wenhua Li, Wenqing Qin, Fen Jiao, Wei Liu, Jiaqi Xu

"A novel technology was developed to study the process of recycling copper from waste printed circuit boards (WPCBs), which are the main source of metal production in the next decades. The chemical compositions of the WPCBs were investigated. The results indicated that the PCB powder was mainly composed of copper (38.5 wt.%), iron, aluminum, and non-metallic materials. Copper is mainly in the form of Cu and is the most valuable metal for the recycle of WPCBs. The concentrated WPCBs powder, obtained by the mechanical process, were pressed as the anode, which was directly electrolyzed to produce copper. The effects of H2SO4 concentration, Cu2+ concentration, current density, pole pitch, and liquid-to-solid ratio on the voltage, current efficiency, and copper extraction were investigated. The results indicated that the optimum conditions were liquid-to-solid ratio of 30 mL/g, current density of 571 A/m2, sulfuric acid concentration of 180 g/L, 50 g/L of copper ion, polar distance of 3 cm. Under the conditions, a desired current efficiency could be achieved. Meanwhile, about 95.62% Cu was recovered from the WPCBs. The experimental studies also revealed that the purity of copper obtained at the highest current efficiency was higher to 99.98%. Produced copper sheet were characterized by X-ray diffraction (XRD). XRD analysis indicated that the copper was the main phase. INTRODUCTION With the rapid development of electronic industry, more and more waste electronic and electrical equipments (WEEE) are generated every year (Fogarasi et al., 2012; Liang et al., 2013). The production of printed circuit boards (PCBs) is the base of electronic industry, because it is the essential part of all electrical and electronic equipments (Schlummer et al., 2007). As a result, a considerable amount of waste PCBs containing plenty of heavy metals have to be treated. In general, PCBs contain about 28% metals that are abundant non-ferrous metals such as Cu, Pb, and Sn. Printed circuit boards can be considered as a secondary resource for recycling rather than wasting. The contents of gold and silver respectively reach 80 g/t and 3300 g/t, which are much higher than that of primary ores. Copper is the main metal of PCB and its content is as high as 26.8% ( Zhang et al., 2009)."

Jan 1, 2018

By A. J. Lynch, L. Ergun, M. Oner

"A research program on modelling cement grinding circuits has been in operation at Hacettepe University, Ankara, for four years. It has concentrated so far on tube mill and air separator grinding circuits for cement clinker, with emphasis on plant sampling surveys, including axial sampling inside the tube mills. The methodology is to use plant data to build the models and to supplement this by laboratory data where necessary, for example the determination of breakage functions. The plant data come from comprehensive sampling surveys and so far 33 surveys of clinker grinding circuits have been carried out in 9 plants. The operating conditions have been• mill sizes – 3.2 to 4.8 metres diameter and 8.5 to 15 metres long,• mill feed rates – 46 to 158 tonnes per hour,• air flow through mills – 25000 to 125000 cubic metres per hour,• cement clinker work indexes – 10.3 to 18,• separator sizes – 2. to 3.1 metres diameter,• separator feed rates – 132 to 689 tonnes per hour,• separator speeds – 12.3 to 21 metres per second.The ball mill model is Whiten’s perfect mixing model and the separator model is the Tromp curve with a fish-hook. This paper emphasises on the importance of calculating the breakage rates and the discharge functions with three case studies at five different circuits which were selected for discussion because they show how particular features of circuit operation can be included in the general models. Size distributiongraphs are used to illustrate every aspect of the discussion.In case I the special emphasis on calculating the breakage rates and discharge rates separately is given in a high pressure grinding roll-ball mill-separator circuit. The tonnes of each size fraction in the mill and the calculated values of R/D, D and R are determined. The values of R per mw are also given to allow comparison with mills of other sizes. The circuit allows the comparison of the static type (V Sep) and dynamic type separators (SKS). Comparing the reduced efficiencies shows that the dynamic separator is slightly more efficient than the static one.In case 2 data are given from two compartment tube mills having the same diameter and the motor power but different ball size gradation. The breakage rate particle size variation of the second chamber of two mills indicate that having finer ball size distribution causes higher breakage rate values."

Jan 1, 2003

By Yuhe Tang, Jun Zhang, Jianguo Liu

"The nature high carbon graphite with fine particle size has low commercial value because of its narrow application range. In order to improve its value, this paper has studied the methods for nature spherical graphite. The nature spherical graphite can be used as the battery material in the field of electronic product battery and new energy automobile battery, basis on the physicochemical characteristics and particle feature of graphite. In this research, the Fixed Carbon (FC) grade of the graphite sample is more than 95.0% and the particle size of the graphite sample is from +325 mesh to -100 mesh. There are many methods for nature spherical graphite, including the fluidized bed airflow mill, the hydro-spheroidization mill and micropowder mill. The testing results indicate that the method of ACM micropowder mill is the best because the spherical shaping ratio and production yield of spherical graphite are both the best.According to the testing results of the ACM micropowder mill, the best process includes two stages of coarse crushing, four stages of fine crushing and twelve stages of shaping. And two kinds of spherical graphite products can be got, which are the product of D50=22.85 µm and the product of D50=15.43µm, and the whole yield of them is up to 54.43%. So, it lays a foundation for the high value utilization of this kind of graphite resources.INTRODUCTION Graphite is isomer of the diamond. Graphite ore resources are mainly concentrated in China, Brazil, India, followed by Czech, Korea, Mexico, Canada and other countries. Graphite ore has lots of characteristics by itself crystal structure, such as good resistance to high temperature, electrical conductivity, thermal conductivity, thermal shock resistance, good lubricity, plasticity, chemical stability and so on. So, Graphite is widely used in metallurgy, machinery, electrical, chemical, petroleum, nuclear industry, defense industry and other areas. [1,2,3] Natural graphite ore has low geological Fixed Carbon (FC) grade. FC grade should be enriched to more than 94.0% by mineral processing. [1,2] The particle size composition of this high carbon graphite affects its application value. The part of +100 mesh particle size has high application value. The part of -100 mesh particle size has low value because of its limited application field. In order to improve the value of-100 mesh particle size, this part high carbon graphite can be made into spherical graphite. And the value of the spherical graphite is great, it is more than 8 times of the feed. This paper has lots of tests for spherical graphite preparing with the fine particle size natural high carbon graphite. And it lays a foundation for the high value of this kind of resource."

Jan 1, 2018

By Fuqiang Zheng, Shuai Wang, Feng Chen, Yufeng Guo, Guanzhou Qiu, Tao Jiang

"The direct reduced iron powder and Ti-V-rich material was prepared from vanadium titanomagnetite concentrate by solid-state reduction-magnetic separation. The result indicated that under the studied conditions, adding KS can effectively improve the metallization rate of pellets. 2% KS was well mixed with vanadium titanomagnetite concentrate to make the pellets. The green pellet was preheated at 900 ? for 6 min. The preheated pellet was reduced at 1050 ? for 100 min, then crushed and ground to more than 80% was below 0.045 mm. The direct reduced iron powder and Ti-V-rich material were separated from the slurry by wet magnetic separation at 800Gs. The TFe content of magnetic material was 90.63%, and the Fe recovery rate reached 96.53%. The TiO2 and V2O5 contents of Ti-V-rich material were 28.40 % and 1.64 %, respectively. The TiO2 and V2O5 recovery rates were 69.05% and 96.82%, respectively. 1. Introduction The ilmenite and rutile are the main titanium resources which can be used in the present technical level and economic conditions[1,2]. However, with the rapid development of China’s economy, the market demand of titanium products is increasing sharply. The current supply of ilmenite and rutile cannot meet the needs of chemical industry[3]. China is rich in vanadium titanomagnetite concentrate which contains abundant titanium and vanadium resources. The TiO2 and V2O5 content of vanadium titanomagnetite concentrate are usually about 7% and 0.3%, respectively[4]. Because the TiO2 and V2O5 grades are low, it generally requires pre-concentrated to Ti-V-rich material before extracting the titanium and vanadium. Therefore, it is vital to find effective processes for pre-concentrating the titanium and vanadium in vanadium titanomagnetite concentrate. There are many methods[5-13] developed or under development to pre-concentrate Ti-V-rich material from vanadium titanomagnetite concentrate, including the blast furnace process, pre-reduction electric furnace process, to utilized vanadium titanomagnetite concentrate are direct reduction-electric furnace smelting, sodium salt roasting-direct reduction-electric furnace smelting and direct reduction-magnetic separation and so on. The blast furnace process and other methods cannot effectively utilize the titanium and vanadium resource due to the technical or environmental problems[9]. In this study, the vanadium titanomagnetite concentrate was obtained from Panxi region of China, the reserves of which account for 11.6% of vanadium and 35.17% of titanium all over the world[3]. The preparation of direct reduced iron powder and Ti-V-rich material based on reduction-magnetic separation is proposed. The process utilizes a new catalyst for titanium ore reduction in rotary kiln followed by magnetic separation. Using this novel technology, the titanium-vanadium and iron are successfully separated. Compared to the traditional reduction of Ti-bearing ore, the reduction temperature reduced to 1050 ?, leading to higher efficiency, lower energy consumption and investment, and broader applications."

Jan 1, 2018

By D. J. Borrow, K. van Netten

"A fine coal tailings feed was selectively agglomerated using a concentrated water in oil emulsion binder consisting of 95% aqueous phase and 5% organic phase. The purpose of the study was to investigate a continuous system in plug flow, providing a rapid beneficiation technique with high selectivity and recovery. The development of the novel binder was undertaken in previous work in a batch system consisting of a high-speed blender. In this previous work, it was found that agglomeration could be achieved in 3 s, providing the binder was pre-dispersed. Furthermore, it was found that, depending on the feed, only ~1 wt% of oil was required to achieve agglomeration, some 10 times less than required in traditional oil agglomeration. In a more recent study, the technique was adapted into a continuous process. Due to the rapid speed of the process using the emulsion binder it was found that a simple flow constriction within a 1 inch pipe was sufficient to achieve the selective agglomeration observed in the batch system. In this previous study, a coal feed consisting of a flotation product was agglomerated at a superficial slurry velocity of 1.3 m/s using a partially closed ball valve as the flow constriction. In the current study, a feed consisting of fine coal tailings with an ash content of 50.1% was used to establish the influence of superficial slurry velocity on the agglomeration process. The superficial slurry velocity was varied between 1.3- 4.2 m/s, while maintaining a constant pressure drop of 100 kPa across the flow constriction. The flow constriction consisted of a partially closed ball valve. It was found that increasing the superficial slurry velocity across the flow constriction reduced the amount of organic liquid required to achieve agglomeration. Under the optimum conditions, a combustible recovery of 80.4% was achieved at a product ash content of 9.6%. This work demonstrates a valuable product can be rapidly produced from tailings material using the novel emulsion binder. INTRODUCTION A significant opportunity exists to recover fine coal from material that is currently classified as waste. This waste material, also called tailings, is currently considered not economic to process due to its high ash content, low solids concentration, and the fine size of the particles. Thus, for this opportunity to be realised, a process is required that is highly selective and has the ability to economically recover fine particles at high throughputs. The technique of oil agglomeration has previously been considered as a candidate for the recovery of fine coal, as it is highly selective and has no lower limit on the size of particle that can be recovered (Capes and Jonasson, 1989). However, the cost of the oil required as the binding agent in the process has proven to be a significant barrier to any long-term applications (Swanson, Nicol, and Bensley, 1977). Recently, however, Yoon and co-workers have developed an ultrafine coal separation process that utilizes an oil phase for the recovery of the hydrophobic coal particles and have implemented an oil recycle to greatly reduce the consumption and thus cost of the oil (Yoon et al., 2016)."

Jan 1, 2018

By Y. H. Tang, H. Y. Zhang

"Tailings from lead-zinc mine contain plenty of dolomite and low-grade fine-grained barite, which is difficult to enrich by mineral processing. Since the density of barite and dolomite has some differences due to the fine dissemination size in a complex sedimentary, the gravity separation tests were conducted with no results obtained. The magnetic separation was conducted to remove the magnetic gangues, and the results were not satisfactory because of the gangue minerals such as limonite and others were low in content. The results of floatation tests showed that the mineral separation of barite and dolomite is quite difficult because that they have similar mineral floatability. Experimental research shows that the good results can be obtained by “desulfurizationbarite floatation” processing with the new depressant TS. The barite concentrate containing BaSO4 91.27%, BaSO4recovery is 70.25% when sodium dodecyl sulfonate serves as a collector and TS as the depressant.INTRODUCTIONBarite is an important mineral material. Often associated with other minerals, it usually needs to be separated by mineral processing in order to meet the application requirements. The main barite beneficiation methods include hand sorting, gravity separation, floatation, magnetic separation, acid leaching, etc. Usually barite associated with oxide ore such as fluorite dolomite, quartz ore etc. are also associated with sulfide ore such as pyrite, sphalerite and galena. The separation between barite and sulfide ore (such as pyrite) is easy. On the other hand, the separation between barite and oxide ore (such as dolomite and fluorite) is very difficult. There are quite a lot of reports on the separation between barite with fluorite dolomite however the separation between barite and dolomite is seldom discussed.The ore properties are quite complex attributable to mineral assemblage containing a large amounts of dolomite. As the density of barite and dolomite has some differences, gravity separation between them is usually easy. The gravity separation tests were conducted with no results obtained due to the fine dissemination size in a complex sedimentary. The magnetic separation was conducted to remove the magnetic gangues, and the results are not satisfactory as the gangue minerals such as limonite and others were low in content. Due to the fine dissemination and intimate association of minerals, and barite and dolomite contain the same group ions of Ba2+, Ca2+ and Mg2+, the results of flotation tests showed that the mineral separation between barite and dolomite by flotation means problematic. Previous studies have been conducted by several institutions but none to date has come up with a satisfactory process in dealing with the deposit. This may be attributable to: high cost of reagents; unsatisfactory performance. Therefore, the key to the flotation separation of barite and dolomite is the application of selective inhibitors. Based on previous test observations and years of extensive research experience in barite processing technology, with the new depressant TS has selectivity inhibition on dolomite developed and used, good results can be obtained by “desulfurization-barite flotation”, which allows barite in the lead-zinc tailings to a comprehensive recovery."

Jan 1, 2018

By X. Tong

Flotation researches of indium-beard marmatite from the Dulong multi-metallic ore in the Yunnan Province of China has been studied in order to improve the grades and recoveries of zinc and indium of the zinc concentrate in the Dulong concentration plant. The experimental results have shown that copper sulfate mixed with a chemical reagent X-1 as the activator in the marmatite flotation produced a much better beneficiation than copper sulfate alone, increasing the zinc and indium recoveries of 10% and 6%, respectively, while the concentrate grades were unchanged. Also, the new activator acted well around pH 10, allowing large savings on lime consumption in the marmatite flotation. In addition, it has been found that a sufficient activated time of activator with ore slur-ry in the flotation is needed to achieve good beneficiation of the marmatite ore.

Jan 1, 2014

By David Verrelli, Melissa Kistner, Leanne Smith, Chris Aldrich, Lidia Auret, Warren Bruckard

In this investigation, different mixtures of realgar and orpiment particles were floated in a laboratory batch flotation cell and multivariate image analysis was used to estimate the arsenic content in the froths. The analysis was based on the froth colour, as well as extraction of three groups of textural features, namely those based on grey level co-occurrence matrices (GLCMs), wavelets and local binary patterns (LBPs). Collectively, these features provided better information on the arsenic content of the froths than any one of the individual groups of features. Partial least squares models could explain approximately 78% of the variance in the arsenic by using all the features combined. The colour content, particularly the green component in the red-green-blue (RGB) features, provided almost as much information as each of the three sets of texture-base features individually.

Jan 1, 2014

By F. Burat

The present research covers the results of experiments carried out with high frequency vibration screen on dewatering of coal fines. In the tests, the addition of surface active reagents was studied employing a high frequency vibrating screen. To increase the efficiency of mechanical dewatering processes, ultrasonic treatment was applied along with surfactants and optimum dewatering conditions were obtained. The moisture content of the feed material was from 82.5% to 41% by the optimization of operation parameters including the angle of the screen, vibration frequency, feed rate and screen opening size. Optimum parameters obtained in dewatering processes carried out with the vibrating screen were kept constant and the effects of surface active reagents and ultrasonic treatment on dewatering were investigated. Finally, the moisture level of the material was further reduced from 41.0% to 37.66%.

Sep 1, 2012

By Jan Svoboda, Atsushi Shibayama, Toyohisa Fujita, Toshio Miyazaki, Kenji Murata

"The electrical disintegration (ED) method and disintegration by underwater explosion were investigated as new fragmentation techniques for the kimberlite ore and tungsten scrap of superalloy (carbide bit). The results of various breakage tests demonstrated that both fragmentation methods as new disintegration techniques for recycling were able to liberate various components of materials of different resistivity and elastic impedance.SUMMARYThe breakage of the kimberlite ore from South Africa (sample size: 15 mm x 15 mm x 6 mm) was achieved by the ED method. A relationship between the sample size, voltage, the electrical current and the energy needed for the disintegration was found from the experimental results. Kimberlite exhibited a high degree of breakage, when the high voltage of 60 kV and the pulse current of approximately 5000 A were applied to the sample by the generator during 0.2 microseconds (Fig. 1)."

Jan 1, 2003

Dielectrophoresis is a separation technique that uses a non-uniform electrical field to separate particles on the basis of their permittivity. There are many areas of mineral processing that might benefit from the application of dielectrophoresis. These include: coarse removal of gangue, recovery of ultrafine particles, upgrading of flotation concentrates or simply as a laboratory analysis technique. In order to determine the potential value of dielectrophoresis to the mineral processing industry, the response of composite particles was investigated. The electrical properties of composites involve complex relationships between the shape, distribution and permittivity of the individual grains within the rock. The relationship between mineral composition and dielectrophoretic force was measured on single particles from two ore types. The results were used to populate a model that could predict the separation characteristics of the ore. The insights gained from this model separator allowed potential applications of the technology to be examined and their performance evaluated.

Sep 1, 2012