By M. Tangstad

Keywords: Pyrometallurgy, ROMA, Norway, furnace, fines The ROMA project is a competence project on optimizing the usage of raw materials and energy in the ferromanganese, silicon, and aluminium industries. One of the items investigated in this project is the effect of fines on the furnace, and the usage of agglomerates versus lumpy ore. From lab-scale experiments it is shown, that for the charge to agglomerate in the furnace, the charge has to be exposed to a temperature higher than about 1200°C, independent of fines content. The fines less than 1 mm also showed higher agglomeration properties, compared to 2?4 mm, which showed no agglomeration property at all. The properties of agglomerates are very dependent on the pre-treatment of the agglomerate. Sinter and pellets, which have been heated to high temperatures, show a better strength, but also a lower CO reactivity. Sinter also shows a lower melting temperature compared to the ore.

Jan 1, 2011

By D. van Rensburg

Jointed rock slopes are generally stable, as there is no freedom of movement for blocks of rock. In an open- pit mining environment, blasting opens up space into which blocks of rock can fail, resulting in the common occurrence of slope failure. Prior to the blasting of a trim pattern, the immediate highwall is scaled, where loose rock material is removed by means of a mechanical scaler. As mining of the pit progresses, the height of the scaled highwall from the pit floor progressively increases. These highwalls are never scaled again for the remainder of the pit life, and time-dependant deterioration contributes to these highwalls becoming subject to rockfall and, sometimes, slope failure. This paper documents the development of a South African innovation, a remote-controlled mechanical highwall scaler, a world first for the mining industry. The scaler will enable open-pit highwalls to be scaled from crest to toe whenever the need arises. It will reduce the risk associated with highwalls and deliver on the Anglo American promise of producing safe, profitable platinum.

Jan 1, 2012

By G. Tranell, L. Kolbeinsen, S. Gaal, J. Safarian

The effect of carbon material properties on the rate of MnO reduction from ferromanganese slag by solid graphite was investigated. A sessile drop technique was used to study the reduction rate of a synthetic slag containing 45 wt% MnO at 1500 and 1600 ºC. Different types of graphite substrates were used and the con-tact angle between slag droplets and substrate were measured in-situ. Moreover, the slag droplet volume during the interaction with the graphite substrates was calculated and normalised. The mathematical relationship between the slag density during the reduction and the normalised slag droplet volumes during the reduction were derived and the MnO reduction curves were then calculated. A method for measuring the slag reactivity of solid carbon was defined and used to qualify the propensity of the different graphites to react with the liquid slag. Some supplementary studies such as manganese evaporation measurement and EPMA analysis for determining the extent of MnO reduction were also carried out. It was observed that there is nota significant difference in the wetting angle of the graphite substrates by the slag, and the wetting is not changed within the temperature range of 1500-1600ºC. However, the changes in the contact angle during the slag reduction at 1600ºC are more than at 1500ºC. The kinetics of MnO reduction is dependent on the type of graphite and it is more dependent on the graphite properties at lower temperatures. On the other hand, the dominant properties of graphite on the reduction rate vary with temperature. A multivariate analysis on the graphite properties and the parameters related to the slag reactivity indicated that the kinetics of MnO reduction is mainly dependent on the temperature, and then on the graphite properties. It was also found that at1500 ºC the surface area and the CO2 reactivity are the most important graphite properties for the slag reduction, suggesting that the reactivity of carbon is rate controlling at 1500 ºC. However, the porosity related parameters are the most important graphite properties at 1600 ºC, suggesting that CO gas desorption is rate controlling at high temperatures.

Jan 1, 2007

By Z-B. Cheng, X-J. Liu

"Intensive mining of shallow coal seams tends to result in severe subsidence of the ground surface. Surface subsidence is a complex dynamic spatiotemporal process that constantly changes as mining advances. With Liangshuijing coal mine as a case study, 3DEC numerical software was used to simulate the development of the moving subsidence field from open-off cut to full subsidence on the working face. The results demonstrate that the formation of a subsidence field is directly related to the coal seam depth H and the extent of the mine workings. Taking the advance distance of the working face as the unit of scale, the process of surface subsidence can be divided into four stages: micro-change (H/ p), the development of surface subsidence (2H/ p), the formation of a movement subsidence field (3H/ p), and dynamic balance (4H/ p). The changing movement of a subsidence field can be fully described by the characteristics of surface subsidence value, curve slope, and the inflection position. The results provide important technical support for predicting surface subsidence and the temporal–spatial evolution features of mining subsidence. IntroductionChina’s coal output was about 3.52 Gt in 2017 (China National Coal Association, 2018), making it the largest coal producer in the world, accounting for almost half of total world coal production. Coal production and distribution play a vital role in the energy industry of China. However, entire overlying strata, from coal seam to surface, are disturbed as a result of long-term, high-intensity and large-scale mining, causing surface subsidence. This results in groundwater loss, surface desertification, vegetation loss, and mud-rock flows. These issues have become topics of common concern throughout society. According to related research results (Liu 2008), the area of surface subsidence caused by coal mining in China has reached about 600 000 ha, some 0.2 ha (and up to 0.42 ha) of surface subsidence for every 10 000 t of coal produced. Surface subsidence disasters not only damage buildings, water conservancy, transportation infrastructure, and farmland, but also cause adverse effects on individual and community lifestyles, environmental hygiene, and economic development. Deterioration of the ecological environment in mining areas has a long history and is very harmful (Lu, 2015)."

Feb 1, 2019

By X. Goso

Laboratory-scale tests were conducted at Mintek for the production of titanium powder from particulate Kroll sponge by the hydrogenation-dehydrogenation (HDH) process. The aim of this work was to produce titanium powder for powder metallurgical consolidations. The work involved the production of titanium powder at optimized conditions, which included hydrogenation in a horizontal tube furnace at 600°C for 2 hours, milling using planetary and roller mills, and dehydrogenation in a vacuumed retort fitted in a muffle furnace running at 700°C for 36 hours. The titanium powder produced in this project matched the elemental specifications of commercially available titanium powder, except for high carbon content. Nevertheless, the powder has been tested further in mechanical alloying and has been found suitable for the production of powder metallurgical compacts. Keywords Powder metallurgy, titanium components, HDH process, ball milling.

Jan 1, 2011

By Austin Whillier, Duncan Mitchell

The problem of heat stress underground in the gold mines is approached on the basis of the heat transfer between the human body and the underground environment. Experimental measurements of radiant and convective heat transfer and a theoretical calculation of maximum evaporative heat transfer enable the maximum cooling power of an environment to be calculated in terms of the dry-bulb and wet-bulb temperature, the mean radiant temperature, the wind speed and the barometric pressure. For most underground applications the cooling power can be expressed as a function of wet-bulb temperature and wind speed only. The relative importance of wind speed and wet-bulb temperature can be assessed: in working places where wind speed is low additional cooling of workmen can be achieved better by increased wind speed than by decreased wet-bulb temperature. The wet kata reading proves to be of limited value as an index of heat stress because environments with equal wet kata do not necessarily have the same cooling power. Finally, thermal equilibrium with the environment is possible when cooling power equals or exceeds the rate of metabolic heat generation. The rates of metabolic heat generation for various underground tasks are indicated.

By L. J. Su, J. Y. Zhang, P. W. Gu, J. F. Xu

Surface tension of mold flux is a key factor affecting optimum casting conditions. A thermodynamic model was developed to determine the surface tension of mold flux containing fluoride based on the ion and molecule coexistence theory of slag structure and Butler’s equation. The relationship between composition and surface tension was investigated by this model. Results indicated that the calculated values showed good agreement with literature data, and the average error was 8.19%. The surface tension value of the CaO–Al2O3-based mold flux was larger than that of the CaO– SiO2-based mold flux. The surface tension in a multi-component system decreased with increasing contents of SiO2, CaF2, and Na2O, which are considered surface-active components. This trend was more significant in the CaO–Al2O3-based mold flux.

Dec 11, 2024

By M. K. Roberts

The approximately 2800 Ma old Ventersdorp Contact Reef is a unique Witwatersrand orebody, from which about 6% of the world?s gold production is derived. A major portion of this production is mined at depths exceeding 2500 m and deepest levels of mining are at about 3600 m. The orebody?s hangingwall consists of volcanic rocks. This differs from the older Witwatersrand orebodies, which have quartzitic hangingwalls. The thickness of the Ventersdorp Contact Reef is generally about 1.20 m, but is highly variable, at an average dip of about 18°. A pronounced unconformity beneath this orebody is also expressed by varying footwall rock type characteristics and frequent rolling of the reef plane. These rolls follow topographic variations of the palaeo-surface. More geological than rock mechanics studies were performed on the Ventersdorp Contact Reef prior to 1992. Recently, however, a multidisciplinary team comprising various rock engineering and geological disciplines has delineated geotechnical areas by a novel technique. Geotechnical areas are defined by distinct footwall/hangingwall rock assemblages. The presence of three footwall and two hangingwall rock types results in the definition of six geotechnical areas across a distance exceeding 60 km, including about 10 gold mines. Distinct rock mass behaviour has been documented in three of the six geotechnically defined areas. Different rock mass behaviour is expressed by features such as mining-induced fracturing, closure rates, fall of ground characteristics and seismic character. Some geological features override the rock mass behaviour as defined for the individual geotechnical areas. These are undulations of the orebody or the frequency, characteristics and attitude of major discontinuities. It is concluded that the concept of geotechnically subdividing orebodies is not only important for facies delineation and the associated grade, but also needs to be considered for safety aspects, in determining factors such as the appropriate support to be employed.

Jan 1, 1999

By G. Kang

The ferroalloys industry has generated historically substantial solid waste. The accumulated waste causes serious problems to the environment. However, it is possible to transform the solid waste into an environment-friendly resource to serve the human being. Consequently, the construction of plants that are ?environment-friendly? and that accommodate ?recycling? has become a target of most ferroalloy producers in the world to ensure sustainable development. This paper introduces the practice of Shanxi Jiaocheng Yiwang Ferroalloys Works, the biggest manganese metal producer in China, in the development of an ?environment-friendly and recycling? process. The process includes power generation using coal gangue, waste from local coal mines; hollow bricks manufacture using slag and fly ash from the power station; cement production using slag from ferroalloy smelting; recovery of ferrous and non-ferrous elements in the dust from the furnace gas cleaning system; application of silica dust in construction and so on. The final objective of the plant is to realize zero discharge of solid waste. The profit of the ?environment-friendly and recycling? process compensates in part for the operational expense of the environment facilities.

Jan 1, 2004

By P. van der Heever

The genesis of Simrac?s technology transfer practices and future initiatives are discussed in this report. Simrac produces a relatively large volume of research-based health and safety outputs that must be communicated to its tripartite stakeholders and to other interested and affected parties. The wide spectrum and complexity of the transferables, together with the diversity of end-user needs and skills of the recipient population, necessitate customizing of technology transfer practices. In an attempt to optimize this process, a variety of practices are employed. Information is transferred by means of publication and dissemination of a variety of reports (paper, website and CD).Knowledge transfer is directed to health and safety practitioners by means of workshops, seminars, best practice booklets, handbooks and textbooks. Promotion of recently completed projects is directed at targeted recipients by means of project launches. Only isolated cases of piloting and implementation of technologies have been undertaken due to lack of resources and past organizational focus. It is anticipated that Simrac?s new organizational structure and management system, together with end-user involvement by industry champions, from project inception to implementation, will enhance the effectiveness of the technology transfer process.

Jan 1, 2002

By V. Riihimäki, M. Luotamo

The Unit of Toxicological Risk Assessment of the Finnish Institute of Occupational Health (FIOH) is conducting a 'Health Risk Assessment for Metallic Chromium and Trivalent Chromium' under the sponsorship of the International Chromium Development Association (ICDA) and the International Stainless Steel Forum (ISSF). This risk assessment will be conducted in accordance with the current European Union legislation in force (Council Regulation 793/93/EEC, Commission Regulation 1488/94/EEC, Dir. 67/548/EEC), but also to meet the regulatory obligations as set out in the European Commission REACH legislation proposal (Consultation Document, the Registration, Evaluation, Authorisation and Restrictions of CHemicals). Further aims include outlining the criteria for the setting of occupational exposure limits for metallic chromium and trivalent chromium compounds. Human Health Risk Assessment according to the current legislation shall entail hazard identification of the toxic end points (acute toxicity, irritation/corrosivity, sensitisation, repeated dose toxicity, mutagenicity, carcinogenicity, reproductive toxicity) including, as appropriate, dose (concentration) - response assessment, and derivation of the N(L)OAELs (No (Lowest) Observed Adverse Effect Level) and/or DNELs (Derived No Effect Level). Exposure assessments for workers, consumers and humans exposed via the environment take into account all the known intended uses. Risk characterisation will compare the typical and/or reasonable worst case exposure estimates to the N(L)OAELs or DNELs to determine Margins of Safety (MOS) for all human populations by each exposure scenario and type of effect, followed by conclusions about the presence or absence of risk. Although all of the key elements of existing legislation remain in REACH, the principal change is that, the burden of proof will be transferred from the member state authorities to industry. The new proposed format of Chemical Safety Report (CSR) will include Risk Management Measures (RMM) as an essential part of the report in addition to the risk assessment. The RMM plays a role in the evaluation of further testing needs and advocating reasons for possible waiwer of requirements. The research programme started in March 2002 and will be completed within the time frame of two years.

Jan 1, 2004

By G. Coetzer

"Prior to operating a non-recovery coke pilot plant oven, it was essential to ascertain coal cake stability during the loading of a 1 m3 (1 m × 1 m × 1 m) coal cake into the cold pilot-plant oven by a pusher mechanism. Previously established laboratory-scale compaction parameters, to obtain coal cakes with sufficient stability, were employed during the loading tests of the coal cakes. Two different coals were evaluated, namely Waterberg semi-soft coking coal (sscc) and Oaky North hard coking coal.It was demonstrated that lower applied compaction forces (14%) can be utilized during 1 m3 compaction, in comparison to laboratory-scale tests, to obtain similar wet cake densities, owing to differences in the effect of frictional forces. Wet cake densities for Waterberg sscc improved slightly (3%) to 1.13 t/m3 when utilizing 79 t/m2 applied force for a 1 m3 coal cake, in comparison to laboratory-scale tests. Similar results were obtained for Oaky North hard coking coal, with a 6% density increase to 1.27 t/m3 at a similar applied force. Porosities decreased by 13% and 32% for Waterberg sscc and Oaky North coal, respectively, when 1 m3 compaction was compared to laboratory-scale tests. An opportunity exists to further decrease the porosities of Waterberg sscc during compaction, whereas acceptable compaction parameters were achieved for Oaky North hard coking coal. Most major vertical cracks and the partial collapse of coal cakes were mitigated, and high-stability coal cakes were obtained that could be successfully loaded into the pilot-plant coke oven by a pusher mechanism.Factors contributing to the instability of the coal cake during loading into the oven, such as vertical cracks, are (i) the cubic geometry (1 m3) of the coal cake, (ii) friction exerted by the oven floor, and (iii) mechanical problems, such as a misalignment between the pusher machine feeder plate and the oven floor. IntroductionOperation of the stamp-charging horizontal 1 t electrically heated coke pilot-plant oven at Exxaro Resources requires coal cake stability during the loading of a 1 m3 compacted coal cake into the oven. In this case, a pusher plate is utilized to push the coal cake into the oven over the oven floor. This is in contrast to a ‘spoon’ or bottom plate feeding mechanism as found in industrial horizontal coke ovens. The pusher plate loading mechanism dictates that the coal cake should possess high stability and inherent strength owing to frictional forces exerted by the oven floor. In order to obtain a coal cake of acceptable stability for the 1 t coke oven, various compaction parameters need to be verified and established."

Apr 1, 2019

By A. du Plessis

The study summarized in this paper focused on expanding existing South African mine closure cost calculation models to provide a new model that incorporates risks, which could have an effect on the closure costs during the life cycle of the mine. This research is important because currently there are a number of mines that do not have sufficient financial provision to close and rehabilitate the mines. The magnitude of the lack of funds could be reduced or eliminated if the closure cost calculation is done in a more risk-orientated manner. The model consists of an expansion of existing closure cost calculation models, by applying the Monte Carlo risk simulation technique to model influences of external and internal changes affecting closure costs. It is shown that the proposed risk-based model provides a way to understand better the implications of uncertainty on the closure costs.

Jan 1, 2006

Where is Your Advertisement

By S. J. Baumgartner

The ferromanganese industry is under pressure to deal with the slag arising from the production of ferromanganese, which is discarded in landfills or slag heaps. This material poses an environmental and health risk to surrounding ecosystems and communities, and disposal costs are increasing. Ferromanganese slag contains an appreciable amount of residual manganese metal, which can be exploited. Previous work has shown that the slag can be leached fully, while rejecting the silica to a residue. The methods that were investigated to recover manganese from the leach solution included hydroxide precipitation to upgrade the leach solution followed by manganese carbonate precipitation to produce a pure manganese carbonate product or a manganese carbonate furnace feed material, which would be recycled to increase manganese recoveries in the production of ferromanganese. In addition, electrowinning of electrolytic manganese dioxide from the leach solution was studied. The methods were compared in terms of selectivity, costs, and product quality. Co-recovery of the leach residue, which is a potential cement additive, is discussed. Among the methods investigated to upgrade the pregnant leach solution, hydroxide precipitation utilizing ammonia to adjust the pH appears to be the most effective in removing major impurities such as iron, aluminium, and silica to less than 1 ppm. The manganese carbonate and impure manganese carbonate furnace feed products met quality specifications. However, although the production of these materials was technically viable, the large amounts of base reagent that were required to raise the pH, and the associated high operating costs, rendered the process uneconomic. An optimization study was therefore carried out with the primary objective to determine the ideal acid amount to be utilized in the waterstarved digestion stage, thereby decreasing acid and base consumption while optimizing the quality of the pregnant leach solution, and producing a leach residue that contained <1% Mn. The outcome was an economically viable process. Additional benefits included an increase in the manganese content of the impure manganese carbonate furnace feed material, and a substantial reduction in the dilution of the pregnant leach solution, thereby maintaining high manganese concentrations that rendered the solution viable for electrowinning of electrolytic manganese dioxide, the production of which yielded a current efficiency of 74%.

Jan 1, 2014

By Z. W. Nkosi, M. Sephton, J. H. Potgieter

The exhaust system is a complex assembly of various components performing important tasks in harsh environments. Carbon steels have been used extensively in exhaust systems, but pressure for lower cost, increased fuel efficiency; lower hazardous emissions, weight savings and increased life expectancy have shifted the emphasis to stainless steels. In response to the growing consumption of stainless steels in automotive exhaust systems, the need to properly evaluate their corrosion resistance properties in order to ensure their appropriate use, has increased substantially. This paper evaluated the most common corrosion and oxidation tests developed that are used and applied it to four common stainless steels often employed in hot end exhaust components. In a summary considering the weight loss of an alloy, it general corrosion rate and pitting resistance under all the test conditions for hot end exhaust components, results indicate that 434 was by far the most corrosion resistant alloy, followed by 1.4509 and 321, and lastly 304 was the least corrosion resistant. In general, the ferritic stainless steels, especially 434, outperformed the austenitic ones under all the test conditions.

Jan 1, 2006

The kinetics of cyanide loss were found to be first order under any given set of conditions, allowing rate constants to be easily determined. At room temperature and in the absence of activated carbon, some cyanide is lost by hydrolysis to hydrogen cyanide, but this does not occur to any significant extent at pH values higher than about 10. A higher rate of hydrolysis occurs when air agitation is used. When activated carbon is present, an additional carbon-catalysed oxidation reaction is responsible for a fairly high loss of cyanide. The evidence indicates a reaction mechanism that consumes oxygen and produces cyanate ion. Some of the cyanate thus produced decomposes to form a mixture of ammonia, carbonate, and urea, depending on the solution conditions. Additional cyanide is lost as a result of the adsorption of sodium cyanide by the activated carbon. At high temperatures, an additional hydrolysis reaction, which involves the formation of ammonium formate as an intermediate, occurs an/j is responsible for. a high loss of cyanide, leading ultimately to the formation of ammonia, hydrogen, and carbon dioxide. The presence of activated carbon has no effect on the rate of this reaction.

Jan 1, 1990

The paper provides a brief review of a multivariate uniform conditioning and a localized multivariate uniform conditioning (LMUC) technique, and presents a production reconciliation case study based on a porphyry copper-gold deposit in Peru. The reconciliation study compares the longterm LMUC mineral resources model (typical of new mining projects, which are invariably based on drilling data on a relatively large grid) to the corresponding production blast-hole grade control model, as well as the final plant production.

Jan 1, 2014

By F. T. Cawood

The distinction between real estate ownership and that of interests in the property is fundamental to the appraisal of mineral properties. This distinction affects the nature and understanding of security of tenure and, consequently, the perception of what constitutes fair value. Legal matters are a particular concern because of their influence on security of tenure, ownership definition and use restrictions. The dynamics of the market and the complex interrelationships between the factors of production define value at a specific point in time for the bundle of rights, interests and assets that constitute a mineral property. Because each mineral property is unique, physically immobile and of a wasting nature, its usefulness to its owner and society must be optimized. The US Appraisal Institute (2001) classified the forces that affect land use as the cultural, political and economic attitudes of society. These forces culminate in laws that often dictate the purposes for doing appraisals. Once the legal definition of the asset is understood, valuers can decide on the valuation process that will support the final valuation approach.

Jan 1, 2004

By M. Ndabeni, J. H. van Vreden, M. Le Roux, Q. P. Campbell

It is not uncommon for gold slurry ponds or screen oversize dumps to contain several different types of carbon-rich contaminants. These contaminants act as robbers of dissolved gold which has a detrimental effect during the downstream carbon-in-leach (CIL) or carbon-in-pulp (CIP) processes. With a renewed interest in the reprocessing of contaminated gold waste ponds and dumps, preconcentration of the feed to either the CIL or CIP process becomes important to maximise profits from these resources. An added advantage in removing these resources, which were once thought of as being uneconomical, is the availability of land that can further be rehabilitated for community development projects. For gravity separation, an example of suitable technology is the Reflux Classifier (RC), which can be used for the separation of materials of different densities and can be used as a pre-concentration step. In this project, a laboratory-scale Reflux Classifier was used to pre-concentrate a gold-bearing sample obtained from a waste dump situated to the east of Johannesburg, South Africa. The material had an average gold grade of 1.9 g/ton and a carbon content of 10%. This material was first fed to a semi-batch Reflux Classifier that was used to fractionate it into several different density intervals by varying the fluidisation water feed rate, followed by continuous runs at fixed water flow rates. The results showed that a cumulative gold recovery of 60%, carbon recovery of 85%, and mass pull of 41% was possible for a fluidisation water feed rate of 15 L/min, while a rate of 20 L/min resulted in a gold recovery, carbon recovery and mass pull of 83%, 92% and 79% respectively, which translated into a concentrate gold grade above the set target of 3 g/ton. Continuous operation at 20 L/min yielded an underflow stream with 84% gold recovery at a grade of 5.4 g/ton. Keywords: Reflux Classification, gold recovery

Jan 1, 2020