By Xiang-yang Zhou

Keywords: Low-Grade Dolomite, Low CaO Content, High Specific Surface Area, MgO. A low energy consumption preparation technology of magnesium oxide with low calcium oxide content and high specific surface area from low-grade dolomite has been investigated. The optimum technical conditions for the preparation of magnesium oxide are the followings: dolomite is partially calcined at 750-800° for 2 h; the optimum solid-liquid ratio range in calcined dolomite slurry is 20-30 g?l?1; carbonation temperature, carbon dioxide pressure and end point pH value of carbonation are less than 40°, 0.4-0.6 MPa and 7 respectively during carbonation process; decomposition temperature of Mg(HCO3)2 solution is near 100°; calcination temperature of the precursor (i.e. precipitated basic magnesium carbonate) is less than 850°. More than 90% of magnesium can be extracted by the technology. The MgO product (CaO < 0.38%) with a specific surface area of near 50 m2?g?1 also can be obtained by the technology.

Jan 1, 2005

By E. O. Stensholt

The Hybinette electrorefining process for production of cathode nickel was in use at Falconbridge Nikkelverk A/S, Norway, until 1975 when conversion to the new chlorine leach process was started. In 1978 the conversion to electrowinning had been completed, but further major improvements to the process have been made up to 1987. After a major expansion program in 1985 - 87 the refinery has a nickel capacity of 54 000 mt Ni/year. The main feed materials to the process are converter matte from the Falconbridge smelter in Sudbury, Ontario, Canada, and from the BCL smelter in Selebi-Phikwe, Botswana. A typical composition of the mixed feed to the refinery is: 40 - 45% Ni, 25 - 30% Cu, 20 - 22% S, 2 - 3% Fe and 1.0 - 1.5% Co. The matte is chlorine-leached in the first process step, nickel being dissolved selectively in a train of leach-cementation tanks. Essentially all copper and sulphur that was present in matte appears in the leach residue as CuS. In 1986 an autoclave treatment stage was added to the process to improve nickel extraction from the leach residue. The resulting strong nickel chloride solution is purified by the process steps (1) precipitation of iron and arsenic, (2) solvent extraction of cobalt and other minor elements and (3) precipitation of lead and the remaining impurities. The nickel solution is then fed to the tankhouse, where various nickel products are produced by electrowinning. The chlorine gas that is produced during the electrolysis is returned directly to the chlorine leaching tanks to dissolve more matte. After stripping from the loaded organic phase and solution purification cobalt is also produced by electrowinning. The copper sulphide leach residue, which contains some nickel, is dead- roasted in fluidized-bed roasters. The sulphur is recovered and sold as sulphuric acid. The calcine is leached in spent copper electrolyte, from which cathode copper is produced by electrowinning. Precious metals and the remaining base metals are recovered from the copper leach residue. The Falconbridge chlorine process is very versatile. It can accept a wide range of impurities in the feed and still produce metals of exceptional purity.

Jan 1, 1988

By Yifei Zhang, Jianzhong Li, Wenhao Zhang

Eletrochemical behavior and corrosion properties of a Ti–6Al–4V alloy fabricated by selective laser melting in artificial seawater at temperature ranges from 20 to 40 °C were investigated using electrochemical techniques, including potentiodynamic polarization, electrochemical impedance spectroscopy (EIS), and Mott-Schottky measurement, etc. Equivalent circuits were simulated to investigate alloy surface and analytic effects of temperature on interface of alloy and solution. The results showed that corrosion potential increased with temperature rise, and the EIS presented a single capacitive resistance characteristics. When the temperature reached 35 °C or above, passive current increased, while the passivation phenomenon was not obvious and corresponding radiating arc radius reduced, indicating that the resistance decreased, conductivity of surface passivation film improved, and corrosion performance improved. According to the Mott-Schottky curves, alloys exhibited n-type semiconductor characteristics. With increasing temperature, conductivity of passivation film enhanced, and alloy corrosion resistance decreased. At 40 °C, alloy possessed the worst corrosion resistance.

Mar 1, 2018

By Jennifer Mager, G. P. Martins, Dean Mussatti

"The role of lead, at low concentrations in high pH cyanide-electrolytes, on the dissolution behavior of gold, has been a topic of scientific and industrial concern for well over a century. The recent paper by Kondos et al [1] at CANMET (1995) this continuing interest and apparent importance. Nevertheless, the mechanism(s) by which this (and other heavy metal) component influences the electrodics of this electrochemical system has still not been unequivocally demonstrated. Instead, several plausible hypotheses, by pioneering researchers in this field, have been advanced and reiterated OVer the ensuing years. While it is generally accepted, based on equilibrium elctrode-potential calculations, that reduction (or co-reduction when oxygen is present in the electrolyte) of lead on the gold surface may occur due to cementation (contact reduction), the cemented lead has never been characterized. The work presented has reexamined the role of lead in this system, by delineating the species distribution of these system components and by interpreting the results of potentiodynamic studies in conjunction with SEM analyses of a gold electrode.1. INTRODUCTIONThe leaching of gold ores in cyanide electrolytes has been practiced for well over a 100 years. Research conducted on this topic has been primarily focused on the effects of operating parameters such as concentrations of oxygen and cyanide, and the pH of the electrolyte; or the leaching behavior of carbonaceous and sulfitic gold-bearing materials.Mechanisms by which pure gold is leached in alkaline cyanide media, with oxygen serving as the oxidant, have been subjected to continual examination and re-examination in the published technical literature during this century. Recently, it has been speculated that without the presence in the electrolyte of trace heavy metals, such as lead or mercury, that gold would not be leachable. Researchers who have tackled this topic, have either considered heavy metals to be a natural occurrence in these systems and ignored the role they may serve in the leaching process, or they have deliberately focussed on controlling their concentrations in the system to undetectable limits. As a result, conflicting findings have been reported for what would appear - depending on the details provided in these reports - to be identical systems."

Jan 1, 1997

By M. Pakala, Z. Fan, Ray Y. Lin

Deposition of hard chromium coatings using electrodeposition is accompanied by emission of hexavalent chromium mists which is a carcinogenic. Hence alternative chromium deposition technologies are being investigated. Sputter deposition is a strong candidate to economically deposit hard chromium coatings in an environmentally friendly way. Chromium coatings of 2-3 µ m thickness were deposited on plain carbon steel coupons using RF magnetron sputter deposition. Depositions were carried out with 0 to 22 vol% nitrogen in the plasma. Structure of the coatings was studied using x-ray diffraction analysis With increasing nitrogen contents, formation of the two nitride phases was observed. The pure chromium phase was detected in coatings with up to 7% nitrogen in the sputtering gas. The solid solution of nitrogen in the pure Cr phase coating was identified by shifts of Cr x-ray diffraction peaks to higher d-spacing. The microhardness of the coatings deposited at a substrate temperature of 200°C showed an increase in hardness with increasing nitrogen content from 600 kgf/mm2 (5.9 GPa) at 0% nitrogen to I250 kgf/mm2 (I2.25 GPa) at 9.5 % nitrogen and a subsequent decrease in hardness to I 100 kgf/mm2 (11 GPa) beyond 9.5 % nitrogen in the sputtering gas. This corresponds to the formation of the hard Cr2N phase, at 9.5 % nitrogen, and CrN phase, at I5.7 % nitrogen. The reported bulk hardness values of Cr2N and CrN are I600 kgf/mm2 (I5.7 GPa) and I 100 kgf/mm2 (11 GPa) respectively. For pure Cr phase coatings, there is a slight increase in hardness for coatings deposited at 7. I % nitrogen from that without nitrogen in the sputtering gas. This could possibly result from the solid solution strengthening of the Cr lattice by nitrogen. For films deposited at 200°C, phases of the deposited films seem to be the overwhelming factor in controlling the microhardness.

Jan 1, 1998

By Roma T. Dec

Many industrial wastes may require preliminary processing to change their particle size, density, surface properties or flowability to become more suitable for treatment and recycle. This can be achieved by pressure agglomeration using roll presses. In the following paper an overview of various roll press processing methods like briquetting, compacting, compacting-granulating or densification is presented together with basics of process and equipment design. The emphasis is focused on major factors influencing compaction process and responsible for pressure build up and final product quality. Finally, two examples of roll press application for briquetting of steel plant wastes and compaction of alumina base catalyst tailings are introduced.

Jan 1, 1996

By Russell E. Clemons

Coarse-crystalline granite, quartz syenite, syenite, meladiorite, and anorthosite in the Florida Mountains, southeast of Deming, New Mexico, were originally mapped as Precambrian. They were remapped in 1971 and some of them described as Mesozoic intrusives. Several subsequent papers presented Precambrian and Ordovician ages. Zinc, lead, copper, silver, gold, manganese, fluorite, and barite mineralization in the Florida Mountains invite more extensive exploration. Clarification of ages of rocks and periods of alteration and mineralization are necessary for efficient exploration. Field observations combined with petrographic studies strongly suggest that all the coarse plutonic rocks are Precambrian and most were altered extensively by late Tertiary hydrothermal activity.

Jan 1, 1982

By Lei Zhang, Shining Chen, Lina Wang, Pu Liu, Benquan Fu, Jiannyang Hwang

A three-dimensional (3D) electrode reactor combined with Fenton reagent was used for advanced treatment of coking wastewater from secondary biological treatment. Effects of some key factors on total organic carbon (TOC) removal rate were investigated, and the results were compared with those of the common three-dimensional electrode reactor. Experimental results showed that TOC removal rate could reach 51.7%, when optimal operating conditions were as follows: initial pH value 3.5, H2O2 dosage 17.6mmol/L, reaction time 90min and FeSO4·7H2O dosage 3.5mmol/L. Analytical results from UV absorption spectra indicated that the organic substances in the coking wastewater were well degraded by this system, which provided good experimental basis for the practical application of this process in the treatment of coking wastewater. This can be meaningful for the treatment of other kinds of wastewater.

Jan 1, 2015

By Yuanbing Ling

Keywords: Calcium sulfate, Sulfuric acid, Phase transformations, Thermodynamic analysis As part of a boarder research project, seeking the development of a cost-effective process for direct production of the high value material, -calcium sulfate hemihydrate, from sulfuric acid at atmospheric as opposed to elevated pressure conditions, the fundamental work presented here has been undertaken. This includes experimental monitoring of phase transformation reactions and thermodynamic analysis of the relationships among the various phases, namely, calcium sulfate dihydrate, hemihydrate and anhydrite in aqueous sulfuric acid solution at temperatures ranging from 20oC to boiling point.

Jan 1, 2004

By D. Pradhan, R. G. Reddy

"Electrorefining of aluminum scrap was investigated from AlCl3 –1-Ethyl-3-methyl-imidazolium chloride (EMIC) (Molar ratio 1.65) chloroaluminate electrolyte using copper cathodes at temperature of 90±3°C and cell voltage of 1.5 V. The deposits were characterized using scanning electron microscope (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD). The study was focused to determine the effect of electrode surface modification as well as deposition time on dendritic depositions of aluminum. Their effect on current density was investigated also. It was shown that the surface modification of electrodes reduced the dendritic depositions of aluminum. Pure aluminum (>99%) was deposited for all experiments with the current efficiency of 94-97%. The use of ionic liquids not only reduced the energy consumption but also minimized pollutant emissions (CO, CO2 etc.) compared to the commercial high temperature aluminum production.1. IntroductionAluminum electrorefining/recycling from aluminum scrap using ionic liquid electrolyte is an attractive process today because of the unique chemical and physical properties such as wide temperature range for the liquid phase, high thermal stability, negligible vapor pressure, low melting point and wide electrochemical window. But in conventional practice, melting of aluminum scrap and high temperature molten salt electrolysis makes this process more expensive and less energy intensive (average 13 kWh/ kilogram of aluminum) [1] . Although recycling scrap aluminum requires only 5% of the energy used to make new aluminum [1-2], but the green house emissions like CO2, CO and HF have to be counted for environmental reason. Approximately, 5.31 kilogram of CO2 emitted per kilogram of aluminum production in most of the US industries."

Jan 1, 2009

By De-qing Zhu, Feng Zhang, Jian Pan

Sintering performance of a series of sinter blends with high ratio of limonite was investigated. The metallurgical performance and mineralogy of product sinter were also examined. The results show that good sintering performance could be obtained when the ratio of limonite was below 43% in the blends of iron ore fines, while good microstructure and metallurgical properties were achieved under optimum sintering conditions. In contrast, sintering performance will rapidly deteriorate when the ratio of limonite is elevated up to 63% in the blends.

Mar 1, 2017

By Miller, Geoffrey W.

The Ravensthorpe Nickel Project (RNP) flow sheet provides for the upgrading of Ni & Co in a size based beneficiation process prior to leaching. The upgrading effect on Ni and Co makes the beneticiation process a powerful addition to the flow sheet. Multiple linear regression (MLR) analysis based on 351 individual batch tests, 52 large scale composites and 21 pilot plant tests has been used to successfully model beneticiation product grade, recovery, upgrade and mass recovery. Statistically, 83% and 96% of the variability in nickel recovery and nickel product grade respectively was accounted for. Algorithms have been developed for Ni, Co, Mg, Al and Fe, which represents the revenue and operating cost factors for the process. The algorithms have subsequently been applied to the resource model, allowing prediction of elemental grade and recovery for the development of the mine schedules based upon these parameters and not head grades alone. This has allowed optimisation of the mine schedule for improvement to the project&apos;s NPV. Keywords: Ni Laterite, Prediction, Multiple Linear Regression, Beneficiation

Jan 1, 2004

By Gavin Beer

The Chelopech Copper/Gold Mine, located in west-central Bulgaria, has been in operation since 1953 producing a low-grade copper/gold concentrate containing up to six percent arsenic by weight. The penalties and restrictions imposed on smelting this concentrate, have seen the past operators of the mine strive to find a balance between achieving acceptable metal returns from the smelters and installing novel or unproven technologies in the face of changing political and economic climates. This paper documents the colourful history of the concentrate processing alternatives that have been investigated and implemented over the 45 year life of the Chelopech Mine, culminating in the high pressure oxidation option that is now the focus of a Definitive Feasibility Study (DFS) presently being undertaken by GRD Minproc Limited. The fundamental chemistry of the preceding alternatives is outlined followed by a discussion as to why each was ultimately not employed. A detailed description of the technology proposed in the DFS is given including: pressure oxidation, arsenic fixation, SX/EW copper recovery, CIL gold recovery and AVR/SART cyanide/copper recovery processes. Keywords: Arsenic, Scorodite, HPOX, Chelopech, Dundee

Jan 1, 2005

By G. Upadhya

Considerable success has been achieved recently in modeling microstructural evolution during solidification of castings bthrough the coupling of macroscopic heat transfer with microscopic solidification kinetics models. However, a complete model for simulation of solidification in complex shaped castings involves: (i) the description of fluid flow, during and after mold filling, coupled with (ii) heat transfer to the mold and surroundings by use of a macro model, followed by (iii) a description of subsequent solidification of liquid metal by use of a micro model for solidification of the alloy under consideration. This paper describes the coupling of solidification kinetics model to a 3D, transient, fully coupled fluid flow and heat transfer model. Coupling between the macremicro models is achieved by using the latent heat method. Micro models for the eutectics of gray, white and ductile iron are discussed. This coupled code has been used for predicting the thermal history and microstructural data for shaped castings. Various applications of the model, including prediction of shrinkage defects, grain density contours, and graylwhite transition region in the casting, are presented for a relatively complex casting geometry.

Jan 1, 1992

By M. J. Bagshaw, J. D. Hunt, R. M. Jordan

"Continuous casting processes, and the roll casting process in particular, offer considerable potential to the Aluminium industry, both meatallurgically and economically.The three major limiting process problems that occur during roll casting are Centre Line Segregation', 'Sticking' where metal adheres to the rolls during casting, and 'Heat Line' formation. 'Heat Lines' are localised semi-continuous longitudinal defects, usually a few cms in width, where the cast metal leaves the roll bite partially molten. These defects occur at relatively low casting speeds when the mean slab exit temperature remains several hundred degrees below the solidus temperature. The objective of the work described here is to develop a better understanding of the roll casting process in general, and in particular, to understand the phenomenon of 'Heat Line' formation.A steady state two dimensional finite difference model has been developed to describe the roll casting process, incorporating a variable heat transfer coefficient through the roll bite. In the model the difference equations are formulated using a control volume method and latent heat is incorporated according to the Scheil equation. A Gauss-Seidel type technique is used to obtain the solution. Because the rate of heat evolution is non-linear the temperature in each box is determined by using a Newton-Raphson method. The solution for a box can be multi valued and therefore lead to instability particularly near the vicinity of the front. A stability 'criterion is presented which shows that to obtain a stable solution it is better to have long narrow boxes rather than boxes with small dimensions in both directions.The model explains why heat lines form in terms of the variable slab/roll heat transfer coefficient.Experimental measurements of slab exit temperatures are also presented. These were obtained on a Hunter twin roll caster for the binary AI-Cu system, at two compositions over as wide a range· of casting speeds as possible. The experimental results are compared with the predicted ones."

Jan 1, 1986

By Kuniaki Murase, Tetsuji Hirato, Yasuhiro Awakura

"Electrodeposition of CdTe was studied using aqueous ammonia-alkaline electrolytic baths in which Cd11-and Te1V-ions are dissolving as Cd11(NH3)/+ and Te1vol-ions, respectively. Ca-thodic polarization curves of the baths suggest the presence of strong interaction between the Cd11-and Te1V-ions; electrodeposition of tellurium is inhibited by the presence of Cd(NH3)/+ ions. The interaction makes it possible to electrodeposit CdTe films with stoichiometric composition. Polycrystalline CdTe thin film of about 1 µm thickness was electrodeposited at 343 K from ammonia-alkaline solutions (pH= 10.7) containing TeO32-(<20 mmol dm-3) and Cd(NH3)/+ ( < 60 mmol dm-3) ions. Increasing Cd(NH3)/42+/TeO32- mole ratio or decreasing total concentration of ammonia/ammonium-ion gave flat and smooth crystalline CdTe deposits at constant cathode potential-0.70 to -0.30 V vs SHE at 343 K.IntroductionCadmium telluride (CdTe) is well-known as a compound semiconductor whose band gap, i.e. 1.44 eV, is suitable for solar energy conversion with a photovoltaic cell. Various methods, such as CVD (chemical vapor deposition) and electrodeposition, of preparing CdTe thin films for solar cells have been investigated.Acidic sulfate solutions with a pH of 1-2 are usually employed for CdTe processing by electrodeposition.1-3) The electrodeposition of compound semiconductors is usually achieved (i) at a higher cathode potential than the redox potential of less-noble species, can in this case, and (ii) under the condition of diffusion-limiting current of a more noble species, Te1Y.4) There-fore, a suitable CdII/TeIV concentration ratio in the acidic electrolytic baths, resulting in the deposition of stoichiometric CdTe, is determined by the diffusion-limiting current density of TeIV- reduction, i.e. the concentration of HTeIVO2+ · Since the solubility ofTe1v species HTeIVO2+ in the acidic solutions is quite low, the rate at which CdTe is deposited from the acidic solutions is extremely slow."

Jan 1, 1998

Based on experimental and computer simulation results from our group, we report a systematic, atomic level analysis of carbon dissolution from carbonaceous materials in molten iron. Experimental results on graphite / Fe-C-S system were obtained using carbon dissolution studies, XRD and FESEM investigations and were supplemented with Monte Carlo simulations. Three basic mechanisms, namely carbon atom dissociation rate, interfacial phenomena and mass transfer in the melt were found to be responsible for the overall dissolution process. While mass transfer in the melt is governed by the concentration gradients, melt composition and temperature; impurities present in ash play a significant role in the interfacial phenomena. For less ordered forms of carbonaceous materials, carbon atom dissociation rate depends strongly on the degree of long-range order and is an important rate controlling mechanism in the overall dissolution process. A systematic comparison of dissolution rates for a variety of coal-chars, natural and synthetic graphites has been carried out in an attempt to identify rate-controlling mechanisms. The structure of the carbonaceous material appears to be an important underlying factor in the carbon dissolution process.

Jan 1, 2003

By Boxun Lu, Juan Wei, Kun Chen, Wanlin Wang, Lejun Zhou

"Slag system is an indispensable part during the continuous casting process, and playing various important roles like absorbing inclusions, modifying heat transfer rate, preventing oxidation of molten steel, etc. to ensure the smooth process and excellent slab quality. However most slags contains more than 8% fluorides which tend to introduce a series of environmental and health problems. This study involves the research of the removal of fluorine through the chemical composition optimization. Through the studies of CCT, DHTT, XRD and SEM, it has been successfully founded that the crystalline phase of Ca11Si4B2O22 discovered in this study shows very similar crystallization property as Cuspidine (Ca4Si2O7F2), which is the most important crystalline phase in the current fluorine bearing slags. Moreover, the optimized free/low fluorine slag shows the opportunity to replace conventional high-fluorine mold slag for casting medium carbon steels that is regarded as the bottleneck of green slag development for continuous casting.IntroductionMold flux has been widely used in continuous casting to control heat transfer, lubricate the strand, absorb inclusions, provide insulation and prevent oxidation of the molten steel[1-3]. It usually contains fluorides, like CaF2, NaF etc., which are used to control the viscosity and solidification temperature of mold fluxes [4-5]. However, the presence of fluoride leads to corrosion of equipment, serious environmental pollution (toxic volatiles and water pollution), and high processing cost of cooling water[6-7]. Therefore, the study of low or free fluorine mold flux is of interest and attracts worldwide attention.S. Y. Choi et al. [4] used B2O3 as a substitute for cuspidine in steel B2PB2) however, B2O3 content was extremely high (up to 30 w%). Other studies have investigated F-free mold flux by adding or optimizing components as MgO, Li2O, B2O3 et al[8-11]. However, most of these focused on the melting and viscosity issues or for low or ultra-low carbon steels, where crystallization tendency is not significantly strong. Very few studies regarding to the development of low/free Fluorine mold flux for casting medium carbon (MC) steels have been conducted, due to the difficulty of the crystallization and heat transfer control without the formation of cuspidine."

Jan 1, 2014

By Shengli Wu, Yuandong Pei, Shaoguo Chen, Zhixing Zhao, Haijun Kang, Jiangshan Shi, Wen Pan, Zhengming Cheng, Yaosheng Luo

Grate bar is the key component of the sinter machine used for loading sinter and raw materials. Bar channels are sometimes bonded into blocks, which affects the service life of bar, and more importantly reduces the effective ventilation area of the sintering, affecting the normal production of sintering, resulting in unstable negative pressure, higher electricity consumption, and lower production and quality of sinter. In order to solve this problem, the systematic study was done on bonding materials of bars, based on which bonding mechanism of sinter grate bars was obtained. The KCl is an important characterization of bonding. Control standard of blending ore that prevents bonding is K2O content below 0.06% and Cl content below 0.05%.

Mar 1, 2018

By Shoji Taniguchi, Lifeng Zhang

"In this paper, firstly the 3D single-phase turbulent steady fluid flow in a vessel with four baffles stirred by a single impeller is mathematically simulated. Turbulence is modeled by using the standard k - e model. Sliding-grid method is used to model the impeller. The flow domain is divided into two cylindrical, the inner one rotates at the same speed as the impeller, and the outer one is fixed with the baffles. Results indicate that the high-speed zone is near the paddles, and larger stirring speed generates larger fluid flow velocity. The calculated stirring intensity data are used to analyze the experimental results. Secondly the effects, such as filter pore size, gas flow rate and NaCl concentration, on bubble size are studied by experiment. For the particle removal rate by bubble flotation in this vessel, first order kinetics is adopted. The effects of initial number of the particles, gas flow rate, particle and bubble size, stirring speed and surface condition, on the removal rate constant are discussed, and an empirical equation is derived by experimental data. At last, a simple model is developed to study the particle attachment probability on bubble surface under turbulent flow conditions. IntroductionIt is well known that inclusions have a bad effect on steel quality. Trying to remove inclusions from liquid steel as many as possible is one of the main objects for the metallurgical workers. Lots of ways are developed to remove inclusions from liquid steel. Gas injection is an effective one. This technique is used to achieve homogeneity in the temperature and metal composition and to assist in the removal of second phase and dissolved impurities from molten steel. Gas injection is commonly applied to the secondary metallurgy processes and continuous casting, for example the ladle argon gas treatment, RH vacuum degassing, and the gas injection in the Submerged Entry Nozzles (SEN) of continuous casting mold, etc. The development of these processes focuses on achieving two conditions: fine bubbles and good mixing. Fine bubbles provide a large gas/liquid interfacial area and a high attachment probability to inclusions, and good mixing enhances the efficiency of impurity transfer."