By Min Chen, Nan Wang, Zhen Tian, Yingying Shen

"The enrichment behavior of phosphorus in CaO-SiO2-FeOx-P2O5 slag was studied by making an investigation on the distribution of phosphorous content in slag and 2CaO·SiO2 phase. The research results showed that the existing 2CaO·SiO2 solid particles in slag were the sites for the phosphorous enrichment. The enrichment process of phosphorus in CaO-SiO2-FeOx-P2O5 slag can be recognized as: mass transfer of phosphorus from bulk slag toward the surface of 2CaO·SiO2 particle, superficial dissolution reaction of phosphorus to 2CaO·SiO2 and diffusion of phosphorus through the product layer of 2CaO·SiO2-3CaO·P2O5 solid solution to the inner of 2CaO·SiO2 particle. Compared to the 2CaO·SiO2 particles with larger size (500µm to 1000µm), the completion time of enrichment was shorter for the particles with smaller size (less than 50µm).IntroductionDuring ironmaking and steelmaking, significant amounts of slag are produced. Contrast to the high utilization of ironmaking slag, the treatment of steelmaking slag is more difficult and challengeable, and therefore, an alternative approach is to recycle the steelmaking slag inside the ironmaking and steelmaking process itself. The main limitation to the reuse of steelmaking slag inside the process is that the refining process may be aggravated caused by the phosphorous accumulation if it is used in the blast furnace burden [1]. At the same time, the phosphorous content of steelmaking slag (approximately 1%~5% P2O5) is too low for it to be used as raw material for fertilizer [2, 3]. Moreover, owing to the diminishing supply of global iron ores with low phosphorous content, the control of phosphorus in iron and steelmaking processes has become an increasing problem, and as a result, more amounts of high phosphorus containing steelmaking slag are produced. Therefore, a valuable approach is quite appreciated in which the steelmaking slag is recycled within the ironmaking and steelmaking process and at the same time, the high phosphorus-containing phases in the steelmaking slag, suitable for use as fertilizer can be separated and recycled effectively [4]."

Jan 1, 2011

By Wenzhou Yu, Cong Zhang, Wenhui Ma, Gang Wang, Kuixian Wei

"A novel technique was successfully developed for nickel further purification by vacuum directional solidification. The removal effect of impurities in nickel was studied based on theoretical analysis and experiments. High removal efficiency of impurities in nickel can be realized according to theoretical analysis. The experimental results show that the vacuum directional solidification treatment could increase the nickel purity from 99.96% to 99.996%. Since vacuum directional solidification could effectively remove the impurities from nickel with low contamination and low cost, it is a potential route to obtain high-purity nickel for commercial application.IntroductionNickel is widely used in metallurgy, machinery, petroleum industry, chemical industry, construction industry, light industry, and other industries for its ductility, medium hardness, ferromagnetism and high chemical activity. Nickel-based alloy is an important material for the key parts of aircraft, tanks, submarines, radars, nuclear reactors and aerospace fields [1-5]. Generally, nickel contains Si, P, S, Fe, Cu, Zn, As, Cd, Sn, Sb, Pb, Bi, Al, Mn, Mg and other impurity elements, which may hinder the commercial application of nickel. Therefore, it is necessary to refine the crude nickel for the high purity nickel."

Jan 1, 2014

By Maria Leikola, Joseph Hamuyuni, Petteri Halli, Fiseha Tesfaye, Mari Lundström

In a race to save the planet of its rapidly depleting natural resources, the use of Secondary Raw Materials (SRMs) as replacements in several processes is currently intensively pursued. In fact, this is currently one of the European Union (EU)’s mandates. Valorization of SRMs is consistent with circular economy, where resource efficiency is maximized for the benefit of both businesses and the environment. In line with this mandate, this paper focuses on investigating process phenomena related to hydrometallurgical recycling of Electric Arc Furnace (EAF) dust. In the experimental study, selective dissolution of zinc and other metals is investigated to acquire a recyclable leach residue. Based on the experimental and theoretical investigations, zinc could be extracted from the EAF dust and a recyclable leach residue produced, having chemical composition suitable as a feed material into electric arc furnace.

Mar 1, 2018

By Zhongming Ren

"A new process of near net shape continuous casting of metal pipe has been put out. The specialty of the process is that no inner core is used. The principle of the process has been presented, and the effect of several factors on the thickness of the pipe has been investigated experimentally and numerically. It is shown that the temperature and the level of the molten metal, cooling intensity of the mold, and the velocity of casting influenced the thickness of the pipe apparently. In order to improve evenness of the thickness of the pipe, the mold was dedicatedly designed, and special methods were taken. By this process, a metallic material like ""bamboo"" was fabricated.IntroductionMetal pipe is a widely used material. Up to now, many processes have been put out to produce the pipe. However, the processes are usually expensive and inefficient. For instance, the welding pipe, which is most widely used, is produced through continuous casting of slab, rolling of the slab into sheet, and welding, with several times of heating and processing. Continuous casting of pipe can not produce small diameter of pipe, which is mostly needed, due to the inner core. Even though. OCC process is novel in fabricating the pipe with small diameter, it is inefficient. In this paper, the no-inner core continuous casting of pipe was proposed. With this process, pipe with small diameter can be produced efficiently. The influence of several parameters on the thickness and evenness of piper wall. With this process, a ""bamboolike"" pipe was fabricated.ExperimentThe experimental apparatus is shown in Fig. I. It is composed of mold, furnace, melt level adjuster, and dummy pipe. In the process, the level of the melt was adjusted at a proper position, then the mold along with the dummy pipe was inserted into the melt in a certain depth. The melt in the mold began solidifying, forming a solid shell. After that, the dummy pipe was pulled upward in a certain speed, drawing the solid shell out of the mold. Thus, a pipe was continuously cast."

Jan 1, 2000

By Alaina Mallard, Katie Schumacher, Jannette Chorney, Grant C. Wallace, Jerome P. Downey

Commercial ceramic carbide operations require large thermal and mechanical energy inputs in order to produce a powder product. A process that could reduce the energy requirements needed to make these materials would allow for these materials to be implemented in a greater number of industrial applications. In this study, silicon carbide (SiC), tungsten carbide (WC), and molybdenum carbide (Mo2C) were synthesized via the carbothermal reduction of activated carbon loaded with silicate, tungstate, and molybdate anions adsorbed from aqueous solutions. Carburization was carried out under reducing and inert gas atmospheres, at temperatures lower than those utilized by commercial operations. Silicon carbide “whiskers” were synthesized under H2 at 1400 °C, while molybdenum carbide and mixed crystals of WC, W2C, and W were synthesized at temperatures below 1000 °C. X-ray diffraction and scanning electron microscopy were used to characterize the carburization products, and inductively coupled plasma-optical emission spectroscopy (ICP-OES) was used to determine the degree of adsorption onto the activated carbon matrix.

Mar 1, 2018

By K. Ohmori, K. Takeya, S. Yoshizawa, A. Kawamoto, T. Ishikawa

"High performance Sm2Fe17N3 magnet powder is developed nitriding Sm2Fe17 alloy that 'is made using a reduction and diffusion method. Typical remanence, coercivity and maximum energy product of the fine powder are 1.40 T, 1.13 T and 323 kJ/m3, respectively. Decreasing samarium content, oxygen content and the amount of a-Fe are found to be the important factors to realize high-energy product.High performance injection molded Sm2Fe17N3 anisotropic magnet is also developed using the powder and an original binder system developed in order to mold at low temperature. Typical remanence, coercivity and maximum energy product obtained are 0.77 T, 0.78 T and 103 kJ/m3, respectively in the density of 4.77 Mg/m3The temperature coefficient of remanence is -0.07 %/K and that of coercivity is -0.54.%/K. The initial irreversible flux loss of the magnet that has a permeance of two is -5 % at 100 °C and the irreversible .flux loss of it is -4.4 % exposing it at 80 °C for 1000h.IntroductionSm2Fe17N3 alloy powder is expected to be very useful for a bonded magnet. The reasons are as follows. The magnetization is as large as the Nd2Fe14B alloy. Curie temperature is even higher than the alloy. The uni-axial anisotropy is comparatively higher than the alloy. Consequently it is possible to obtain high coercivity after just milling the powder and therefore possible to obtain high-energy product in a bonded magnet as it is realized in the SmCo5 bonded magnet. On the other hand, sintering is difficult because it will be decomposed into samarium nitride and a-Fe when heating it up to 500°C:"

Jan 1, 2000

By A. Andreas Hejja

Flow of slag and settling of matte in slag resistance electric furnaces are discussed in conjunction with furnace geometries, stirring action of the electrodes, buoyancy and electromagnetic effects. The rectangular electric furnace was regarded as a channel reactor and the mode of slag flow as a channel flow. The flow is affected both by buoyancy and electromagnetic forces, however the effect of electromagnetic forces is minimal. The flow velocity is made up of two components; (i) that developed by the action of the electrodes, and (ii) the bulk flow velocity determined by the smelting rate and the volume of the reactor. Slag samples were taken from various depths of the molten bath and were analyzed microscopically to determine the size and distribution of matte particles, The action of the electrodes was described by a simple mathematical formula indicating a balanced settling rate in the area of electrode action.

Jan 1, 1996

In low carbon TRIP steels, the formation of carbide-free bainitic ferrite is crucial for the stabilization of austenite. Based on experimental investigations modeling the bainite reaction is examined adopting diffusional and displacive mechanisms, as well as the semi-empirical JMAK approach. Transformation tests were carried out to study the isothermal austenite decomposition into bainitic ferrite for a model steel containing 0.6wt%C, 1.5wt%Mm and 1.5wt%Si which replicates the composition of remaining austenite at the start of the bainite reaction in a classical C-Mn-Si TRIP steel. In the diffusional approach, classical nucleation theory is employed and subsequent growth of bainite plates is modeled using the Zener-Hillert theory. In the displacive approach, the autocatalytic nucleation of bairtite plates is assumed to be rate controlling. The predictive capability of all models is evaluated for temperature ranges where different morphologies of bainitic ferrite have been detected, The shortcomings and inherent challenges associated with either of these modeling approaches will be delineated.

Jan 1, 2003

By Kiyoshi Takai

The Para-Eco Incinerator Ash Processing System for cleaning slag has been developed after a seven-year pilot plant study. The major part of the system is an electric furnace heated to 1773 K. The feed material consists of a municipal solid waste incinerator ash mixture containing a reducing agent of a coke and an inorganic flux of calcium and magnesium. With this furnace system, three kinds of products are produced. They are an inorganic molten salt that is slag, molten iron alloy absorbing non-ferrous metals, and fly ash. Due to the reducing atmosphere in the furnace, the slag does not contain any metal components as well as chlorine components just like natural rock and/or aggregate. A retreatment plant modifies this slag into a practically useful aggregate. The plant consists of a slow cooling step for crystallizing the slag as well as a water granulation step. The iron components in the ash are reduced to molten iron droplets, which concentrate at the furnace bottom. The non-ferrous metal components such as copper, chromium, and others are absorbed into the molten iron but not into the molten slag. Volatile metals such as lead, zinc, cadmium and others as well as sodium, potassium, and chlorine go back into the fly ash. A solvent extraction method and/or other appropriate procedures can be used to extract the metal components from this fly ash.

Jan 1, 2003

By Jun Deng, Daohong Wu, Zhicheng Cao, Jingkun Tang, Luxing Feng, Xun Xue

The effect of reducing temperature, H2/CO mole ratio, and reduction gas flow rate on the metallization rate of oxide pellets were investigated at laboratory scale, with ludwigite iron concentrate used as raw materials. The reducing temperature varied from 850 to 950 °C, the H2/CO mole ratio changed from 1.5 to 4.5, the range of reduction gas flow rate was from 2 to 5 L/min. The results indicate that the metallization degree of pellets increase with increase of the temperature, H2/CO mole ratio, and gas flow rate. However, after temperature rises to 850 °C, metallization degree increases slowly. The effect of H2/CO on the metallization degree is not very obviously with the ratio of H2/CO increasing from 1.5 to 4.5. When the gas flow rate was increased from 2 to 3 L/min, the metallization degree increased greatly from 72.2 to 92.1%. In the flow range from 3 to 5 L/min, the metallization degree was increased slowly. The results obtained could be useful for comprehensive utilization of ludwigite iron concentrate by gas-based direct reduction method.

Mar 1, 2017

By Th. Probst, M. Reuter, H. Orbon, U. Boin, J. Vonken, P. Vonk

Although secondary aluminum industry is well established in the world, the recycling process still requires further development to adequately control the process for a higher aluminum yield and a better product quality. In the present paper, recyclabilities of different aluminum scraps have been experimentally studied. Four types of commercial scraps were characterized and melted at 800 - 900 °C to recover 'aluminum metal with the protection salt flux of NaCl-KCl-Na3AlF6 under nitrogen atmosphere. According to the results, the difficulty of recycling aluminum scrap depends on the cleanness and the ratio of surface area to body volume. More non-metallic contaminates and higher ratio of surface area to body volume usually led to a lower metal yield. Usually cast ingots gave better results than rolling mill cuttings under similar conditions. Bottle caps can be recycled more easily than the margarine foil. The effect of temperature was not as significant as the composition of salt flux. The addition of cryolite was essential for a better metal recovery, especially for the scraps with higher surface area. Recycling

Jan 1, 2000

By Philippe Charlier

Recycling of aluminium contained in used aseptic beverage cartons is a difficult task which has nevertheless to be tackled by our modern societies. Techniques have earlier been developed by the paper and pulp industry for the recycling of the board fibres from collected post-consumer beverage cartons. A joint technical feasibility study by Granges and a leading beverage carton producer has dealt with different techniques for handling residues from repulping facilities. The aluminium obtained can be used as raw material for the production of thin gauge foil, thus closing the recycling loop.

Jan 1, 1995

By U. M. Mutnti

In order to meet the stringent market requirements for high purity cobalt, ZCCM commissioned the VIR plant in December 1982. The plant comprises a 4.1 tonne/heat vacuum induction furnace with a rated annual capacity of 2,500 MT of barstock. In the VIR furnace, molten cobalt is held under vacuum at 1600°C resulting in the removal of more volatile impurity elements by distillation. Operations todate have demonstrated that Pb, Zn and Cd have good distillation rates in excess of 95%, leading to cobalt containing 1 ppm or less of the above elements. Removal of other impurities such as Se, Bi is about 65% with the finished product still assaying around 1 ppm of each of these elements. Vacuum refining of cobalt offers an economic route for producing higher grades of cobalt from the type of concentrates and treatment processes available within ZCCM. The consistency of VIR cobalt quality has been confirmed by ZCCM and some of its alloy customers.

Jan 1, 1988

By K. Walanabe

Kosaka Smelter & Refinery has a history of more than a century as a metallurgical department belonging to Kosaka mine. It has treated for a long time the "Black Ore" or the complicated concentrates dressed from it. The "Black Ore" is composed of black sulfides. It contains not only valuable metals such as gold, silver, copper, lead and zinc but also some impurities like arsenic, antimony and bismuth. With the development of Kosaka's floatation technology, five kinds of concentrates (copper, zinc, lead, pyrite and barite) have been separated from the "Black Ore" but the separation was not complete and each concentrate contained some unfavorable impurities. In 1980s the highly appreciated yen and the drop of the metals prices forced many domestic mines to close their operations. Since then Kosaka Smelter has changed its way of operation to a custom smelter. Now more than 95% of copper concentrates are imported to take advantage of this technology of "Black Ore" treatment. It mainly treats the raw materials that contain high gold and silver like the "Black Ore". Recently, Kosaka has been working on the recycling of the metals from the printed circuit board scraps and sludge which contain some precious metals. The volume of the recycled metal is continuously increasing.

Jan 1, 2003

By Debbie Marshall

Nickel and cobalt in lateritic ores can be extracted by either a hydrometallurgical or a pyrometallurgical route. The high-iron limonitic fraction of a deposit is best processed' hydrometallurgically while the magnesium-rich transitional and saprolitic fractions are more suited for pyrometallurgical processing. During hydrometallurgical processing, it may be attractive, for economic reasons, to blend the limonitic component with transitional and saprolitic ores, which contain higher nickel levels. However, blending increases the concentration of magnesium in the feed, leading to increased acid demands. The decision on how much ore to process then becomes an economic one. Ore samples with different magnesium contents were prepared for the leach test program by blending limonitic and transitional ores. The ore samples were slurried in seawater and tested in the Falconbridge Hydrometallurgical Pilot Plant. As expected, acid consumption increased with increasing magnesium content of the ore. For target extractions of 95% nickel and 92% cobalt, the required residual free acid concentration increased from 30 g/L at 1.7% magnesium to 50 g/L at 2.7% magnesium. When the magnesium content was raised to 3.8% and 4.6% in subsequent pilot plant testing, the final free acid requirements did not increase beyond what was observed at 2.7% magnesium. Thus, the cut-off ore composition to maximize nickel units and minimize acid requirements is between 1.7- 2.7% magnesium. Keywords: high pressure acid leaching, laterites, magnesium

Jan 1, 2004

By Leonard Harris, Rosa H. Harris

"It is becoming increasingly obvious to mining and exploration companies, when operating overseas, that their activities should not conflict with the interests of the surrounding communities. The world's largest gold heap leach operation, Minera Yanacocha has installed community assistance programs in Peru concerned with health, education, electrification, agricultural assistance and road improvements. The programs are conducted with joint venture partners consisting of the company, the community people, the contractors and suppliers, government and non government organizations and a ladies association composed of the employees' wives and female staff.IntroductionThe l 990's is the decade highlighted by enormous investments in mineral exploration and mining projects in the developing world. Figure 1 illustrates the distribution of exploration spending by mining companies in 1995."

Jan 1, 1997

By Jorge A. S. Tenorio, Chuanwei Zhuo, Joner O. Alves, Yiannis A. Levendis

"The disposal of wastes is a serious environmental problem, since available landfill space is dwindling. Their treatment by pyrolysis or combustion has merit, and the corresponding fuel or power production is of technological interest. However, such processes need a rigid control of emissions. This work addresses the gaseous light hydrocarbons (LHCs) generated during sequential pyrolysis and partial oxidation of unserviceable tires, PET bottles, com wastes (DDGS) and sugarcane bagasse in a two-stage laminar-flow horizontal furnace, kept at 1000 °C. Gas chromatography was used to identify and quantify the components of the emitted gaseous light hydrocarbons. The results showed that the biomass residues generated the highest emissions of aliphatic hydrocarbons, whereas PET generated the most aromatic hydrocarbons. When stainless steel meshes were inserted in the exhaust flow, it was found that hydrocarbon emissions were curtailed; as such meshes catalyzed partial conversion of these carbon-bearing gases to carbonaceous nanomaterials.IntroductionLight hydrocarbons (LHCs) are volatile organic compounds, consisting of hydrogen and carbon with low molecular weight; the most common species are methane, ethane, propane, butane, etc. LHCs are valuable since they are a very important energy resource. However, uncontrolled release of light hydrocarbon gases to the atmosphere should be avoided [l, 2]. In this work, a development is presented for the evaluation of LHCs generated during the controlled pyrolysis/combustion of several wastes in a two-stage laminar-flow horizontal furnace. Samples of unserviceable tires, post-consumer PET bottles and waste residues from the bioethanol industry (DDGS and sugarcane bagasse) were burned. A catalyst system, consisting of stainless steel screens, was tested for its effects on the gaseous emissions."

Jan 1, 2011

By Walter Curlook

An improved process of hydrometallurgical treatment of laterite ores of the limonitic type for the recovery of nickel and cobalt using sulphuric acid has been developed and patented [I]. The major improvement is brought about by recycling a significant portion of the "mother liquor" emanating from the pressure leaching reaction back to the feed preparation stage thereby substituting for all or at least a major proportion of the fresh water that must be added. The amount of process effluent waters is correspondingly reduced. Concomitantly with the major savings in fresh water requirements, a degree of reduction in new sulphuric acid requirements is effected, along with a savings in limestone and lime required for subsequent neutralizations. Keywords: Acid pressure leaching; Nickel laterites

Jan 1, 2004

By M. M. Kim

Zn-27% Al was pressure infiltrated into a column of 20 micron diameter abrasive grade SiC particles to give billets with particle loading of 50 voli.une %. Some billets were heated to a temperature where they became semi-solid and diluted with liquid Zn-27% Al alloy to give billets with particle loadings of 12 and 16 volume %. Some of these billets were then extruded into wire with an area reduction of approximately 98%. Tensile properties of the as-cast billets were always inferior to those of the matrix alloys; however, the extruded composite samples showed at 37% improvement in ultimate tensile strength compared to their extruded conventional counterparts. The fracture surfaces of these samples are described.

Jan 1, 1990

Kosaka Smelter & Refinery has a history of more than a century as a metallurgical department belonging to Kosaka mine. It has treated for a long time the "Black Ore" or the complicated concentrates dressed from it. The "Black Ore" is composed of black sulfides. It contains not only valuable metals such as gold, silver, copper, lead and zinc but also some impurities like arsenic, antimony and bismuth. With the development of Kosaka's floatation technology, five kinds of concentrates (copper, zinc, lead, pyrite and barite) have been separated from the "Black Ore" but the separation was not complete and each concentrate contained some unfavorable impuritie. In 1980s the highly appreciated yen and the drop of the metals priees forced many domestic mines to close their operations. Since then Kosaka Smelter has changed its way of operation to a custom smelter. Now more than 95% of copper concentrates are imported to take advantage of this technology of "Black Ore" treatment. It mainly treats the raw materials that contain high gold and silver like the "Black Ore". Recently, Kosaka has been working on the recycling of the metals from the printed circuit board scraps and sludge which contain some precious metals. The volume of the recycled metal is continuously increasing.

Jan 1, 2003