By Xie Gang

The leaching experiment used by bacteria on the low grade sulfide copper ore which is difficult to leach was carried out. Some leaching bacteria which have good physiological and leaching activity were isolated and domesticated, and were adapted to leaching ore. The effective domesticated method was put forward. Some technological parameters such as ore acidification, potential controlling, leaching method, ore granularity, leaching acidity, leaching liquid quantity and acid consumption were obtained by column experiment and leaching ore in situ under the ore well. The results show it could leach 30.62% of copper from the low-grade sulfide copper ore within 24 weeks by column leaching method, and the bioleaching rate of copper is 22.83% by leaching in situ under the ore well in 8 months.

Jan 1, 2006

By Kongfang Feng, Fei Ruan, Zhiyu Liu, Jieyu Zhang, Xin Hong, Shaobo Zheng, Jixu Wang, Jinyin Xie

"Mixing phenomena in smelting reduction furnaces with asymmetric side blowing were studied in this paper. Mixing phenomena in a smelting reduction furnace was represented as the mixing time by electrical conductivity measurements. Experiments were performed in a water model under various operating conditions to determine the effects of horizontal angle, radial angle, inserting depth, flow rate of the upper and the lower side nozzle, the included angle between the upper side nozzle, and the lower side nozzle on mixing phenomena in smelting reduction furnace. Comparing mixing time and mixing phenomena, the optimal conditions were obtained for an asymmetric side blowing process.IntroductionIn recent years, many countries have put forward development strategies for saving resources and environment-friendly, the development of various industries had to face its influence for resources and the environment .As we all know, the steel industry is a pillar industry of the global economy, in which ironmaking is an important part of it. In the modern ironmaking process, the blast furnace is regarded as the most important equipment and tool. But with the increasing scarcity of metallurgical coke resources and considering the environmental impact of such processes, metallurgists proposed the concept of smelting reduction. Smelting reduction processes to produce hot metal from iron ore and coal were being developed as a possible alternative to the traditional blast furnace. At present, a number of smelting reduction processes had been developed all over the world, they were mainly included COREX, HISMELT, FINEX, DIOS, etc."

Jan 1, 2012

By R. T. Jr. Faria, H. Vargas, R. Toledo, S. Cosin, V. P. Souza

"With the purpose of decrease environmental impact, caused by industrial residues (just discarded in the environment) and clay extraction in the ceramic industry, sanitary ware wastes were incorporated into clay. In contrast, it is important to evaluate not only the technological essays but also gases emissions in the ceramic firing process. The pollutant gases emitted in ceramic with residues can be in much larger concentrations than that in a pure clay ceramic firing or, on the other hand, can decrease the pollutant gas concentrations. With the aid of thermal analyses and photo acoustical techniques it was observed that sanitary ware waste can reduce the C02 emission. The gas emissions were shown as in function of firing temperature from 300 DC to 1100 DC. In order to analyze phase transformations during the firing process, clay samples and wastes were both analyzed by x-rays fluorescent chemical analysis and x-rays diffraction.IntroductionResearch works on the structural and physical changes that wastes, mainly industrially produced, cause to the final ceramic product has been rapidly expanding in these last two decades. See, for instance references in [1]. In spite of these examples of a continuous effort to incorporate wastes into clay ceramic motivated by technical and economical advantages, environmental issues are still a matter of concern. However, the gas emission due to the clay firing process and its related atmospheric pollution may be enhanced as a consequence of an incorporated waste [2]. It is known that the firing of clay ceramics in conventional furnaces using fuels such as wood, charcoal, heavy oil and natural gas generates appreciable amounts of gaseous components, mainly carbon dioxide (CO2), carbon monoxide (CO) and methane (CH4). Additionally to the atmospheric pollution, these gas sets could be harmful to the human health and can corrode equipments [3,4]."

Jan 1, 2012

By Cesimiro Fabian

The crystallite size of copper electrodeposits was determined by X-Ray powder diffraction analysis using a General Area Detector Diffraction Solution (GADDS) diffractometer. Crystallite size was calculated for copper thin films which were deposited on a 316 stainless steel rotating cylinder electrode (RCE) in the presence and absence of additive ?A?. The crystallite size was calculated from a corrected full width at half maximum (FWHM) of the [110] peak profile using the Scherrer equation. The test of significant difference on crystallite size was derived using Kruskal-Wallis method. It was found that in the absence of the additive the median crystallite size was 426, which decreased to 364 in the presence of the additive. As the additive degraded, the crystallite size increased to a size similar to that observed in the absence of additive.

Jan 1, 2003

By P. A. Metz

The Fairbanks mining district has produced in excess of 7.5 million troy ounces of placer gold and 250,000 troy ounces of lode gold since gold was discovered in the area in 1902. The Fairbanks mining district is in the northwestern part of the Yukon-Tanana Upland Schist Terrane, an area of approximately 240,000 square km that has produced in excess of 21 million troy ounces of placer gold. All lode gold production from the terrane has been from the Fairbanks mining district, and all of this production has come from high-grade gold-quartz polymetallic sulfide veins. Gold grains in the vein systems range in size from several microns to several millimeters. The veins are localized in a complex metamorphic rock assemblage which includes greenstones and felsic metavolcanic and volcaniclastic rocks, meta-exhalatives and metasediments. Gold occurs in the metamorphic host rocks in association with arsenopyrite and arsenic-antimony sulfides which occur in lenses and disseminations within the host rock. Gold grains occurring in the metamorphic host rocks range. in size from sub-micron to a few microns in diameter.

Jan 1, 1987

By Florian Kongoli

While calcium ferrite slags have been successfully used in continuous copper converting for the last 30 years, ferrous calcium silicate slag was proposed about 8 years ago as an additional alternative for copper smelting. Although both slags are normal extensions of each other their phase relations have not been completely clarified. In this paper the liquidus relations of both slags have been quantified at various areas that cover both of them. The existing experimental data have been first reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict various diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeOx-SiO2-CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO2 and Fe/SiO2 versus CaO as well as Fe/CaO versus Temperature and Fe/SiO2 versus temperature are proven to be much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams the effect of SiO2 and CaO on the melting temperature is quantified. The effect of Cu2O is also quantified through the model. Some Fe/CaO versus Cu2O and Fe/SiO2versus CaO at various copper contents are predicted and the results show good agreement with the experimental data. It is also shown that in the presence of liquid copper, Cu2O is dissolved in the slag depending on the oxidation degree of the system and might lower the liquidus temperature. Some discussions are also presented taking into account plant observations and important conclusions are drawn for copper smelting and converting

Jan 1, 2006

By Florian Kongoli

While calcium ferrite slags have been successfully used in continuous copper converting for the last 30 years, ferrous calcium silicate slag was proposed about 8 years ago as an additional alternative for copper smelting. Although both slags are normal extensions of each other their phase relations have not been completely clarified. In this paper the liquidus relations of both slags have been quantified at various areas that cover both of them. The existing experimental data have been first reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict various diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeOx-SiO2-CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO2 and Fe/SiO2 versus CaO as well as Fe/CaO versus Temperature and Fe/SiO2 versus temperature are proven to be much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams the effect of SiO2 and CaO on the melting temperature is quantified. The effect of Cu2O is also quantified through the model. Some Fe/CaO versus Cu2O and Fe/SiO2 versus CaO at various copper contents are predicted and the results show good agreement with the experimental data. It is also shown that in the presence of liquid copper, Cu2O is dissolved in the slag depending on the oxidation degree of the system and might lower the liquidus temperature. Some discussions are also presented taking into account plant observations and important conclusions are drawn for copper smelting and converting

Jan 1, 2006

By Florian Kongoli

While calcium ferrite slags have been successfully used in continuous copper converting for the last 30 years, ferrous calcium silicate slag was proposed about 8 years ago as an additional alternative for copper smelting. Although both slags are normal extensions of each other their phase relations have not been completely clarified. In this paper the liquidus relations of both slags have been quantified at various areas that cover both of them. The existing experimental data have been first reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict various diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeOx-SiO2-CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO2 and Fe/SiO2 versus CaO as well as Fe/CaO versus Temperature and Fe/SiO2 versus temperature are proven to be much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams the effect of SiO2 and CaO on the melting temperature is quantified. The effect of Cu2O is also quantified through the model. Some Fe/CaO versus Cu2O and Fe/SiO2versus CaO at various copper contents are predicted and the results show good agreement with the experimental data. It is also shown that in the presence of liquid copper, Cu2O is dissolved in the slag depending on the oxidation degree of the system and might lower the liquidus temperature. Some discussions are also presented taking into account plant observations and important conclusions are drawn for copper smelting and converting

Jan 1, 2006

By Florian Kongoli

While calcium ferrite slags have been successfully used in continuous copper converting for the last 30 years, ferrous calcium silicate slag was proposed about 8 years ago as an additional alternative for copper smelting. Although both slags are normal extensions of each other their phase relations have not been completely clarified. In this paper the liquidus relations of both slags have been quantified at various areas that cover both of them. The existing experimental data have been first reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict various diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeOx-SiO2-CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO2 and Fe/SiO2 versus CaO as well as Fe/CaO versus Temperature and Fe/SiO2 versus temperature are proven to be much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams the effect of SiO2 and CaO on the melting temperature is quantified. The effect of Cu2O is also quantified through the model. Some Fe/CaO versus Cu2O and Fe/SiO2versus CaO at various copper contents are predicted and the results show good agreement with the experimental data. It is also shown that in the presence of liquid copper, Cu2O is dissolved in the slag depending on the oxidation degree of the system and might lower the liquidus temperature. Some discussions are also presented taking into account plant observations and important conclusions are drawn for copper smelting and converting

Jan 1, 2006

By Florian Kongoli

While calcium ferrite slags have been successfully used in continuous copper converting for the last 30 years, ferrous calcium silicate slag was proposed about 8 years ago as an additional alternative for copper smelting. Although both slags are normal extensions of each other their phase relations have not been completely clarified. In this paper the liquidus relations of both slags have been quantified at various areas that cover both of them. The existing experimental data have been first reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict various diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeOx-SiO2-CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO2 and Fe/SiO2 versus CaO as well as Fe/CaO versus Temperature and Fe/SiO2 versus temperature are proven to be much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams the effect of SiO2 and CaO on the melting temperature is quantified. The effect of Cu2O is also quantified through the model. Some Fe/CaO versus Cu2O and Fe/SiO2versus CaO at various copper contents are predicted and the results show good agreement with the experimental data. It is also shown that in the presence of liquid copper, Cu2O is dissolved in the slag depending on the oxidation degree of the system and might lower the liquidus temperature. Some discussions are also presented taking into account plant observations and important conclusions are drawn for copper smelting and converting

Jan 1, 2006

By Florian Kongoli

While calcium ferrite slags have been successfully used in continuous copper converting for the last 30 years, ferrous calcium silicate slag was proposed about 8 years ago as an additional alternative for copper smelting. Although both slags are normal extensions of each other their phase relations have not been completely clarified. In this paper the liquidus relations of both slags have been quantified at various areas that cover both of them. The existing experimental data have been first reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict various diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeOx-SiO2-CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO2 and Fe/SiO2 versus CaO as well as Fe/CaO versus Temperature and Fe/SiO2 versus temperature are proven to be much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams the effect of SiO2 and CaO on the melting temperature is quantified. The effect of Cu2O is also quantified through the model. Some Fe/CaO versus Cu2O and Fe/SiO2versus CaO at various copper contents are predicted and the results show good agreement with the experimental data. It is also shown that in the presence of liquid copper, Cu2O is dissolved in the slag depending on the oxidation degree of the system and might lower the liquidus temperature. Some discussions are also presented taking into account plant observations and important conclusions are drawn for copper smelting and converting

Jan 1, 2006

By Florian Kongoli

While calcium ferrite slags have been successfully used in continuous copper converting for the last 30 years, ferrous calcium silicate slag was proposed about 8 years ago as an additional alternative for copper smelting. Although both slags are normal extensions of each other their phase relations have not been completely clarified. In this paper the liquidus relations of both slags have been quantified at various areas that cover both of them. The existing experimental data have been first reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict various diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeOx-SiO2-CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO2 and Fe/SiO2 versus CaO as well as Fe/CaO versus Temperature and Fe/SiO2 versus temperature are proven to be much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams the effect of SiO2 and CaO on the melting temperature is quantified. The effect of Cu2O is also quantified through the model. Some Fe/CaO versus Cu2O and Fe/SiO2versus CaO at various copper contents are predicted and the results show good agreement with the experimental data. It is also shown that in the presence of liquid copper, Cu2O is dissolved in the slag depending on the oxidation degree of the system and might lower the liquidus temperature. Some discussions are also presented taking into account plant observations and important conclusions are drawn for copper smelting and converting

Jan 1, 2006

By Florian Kongoli

While calcium ferrite slags have been successfully used in continuous copper converting for the last 30 years, ferrous calcium silicate slag was proposed about 8 years ago as an additional alternative for copper smelting. Although both slags are normal extensions of each other their phase relations have not been completely clarified. In this paper the liquidus relations of both slags have been quantified at various areas that cover both of them. The existing experimental data have been first reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict various diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeOx-SiO2-CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO2 and Fe/SiO2 versus CaO as well as Fe/CaO versus Temperature and Fe/SiO2 versus temperature are proven to be much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams the effect of SiO2 and CaO on the melting temperature is quantified. The effect of Cu2O is also quantified through the model. Some Fe/CaO versus Cu2O and Fe/SiO2versus CaO at various copper contents are predicted and the results show good agreement with the experimental data. It is also shown that in the presence of liquid copper, Cu2O is dissolved in the slag depending on the oxidation degree of the system and might lower the liquidus temperature. Some discussions are also presented taking into account plant observations and important conclusions are drawn for copper smelting and converting

Jan 1, 2006

By Alpagut Kara

Turkey is the fifth biggest ceramic tile exporter in the world. Considering the expectation that the Turkish tile sector continues to expand, further studies both on the improvement and the development of tile formulations are necessary in order to make the producers advantaged in the world market while maintaining the capital and running costs at reasonably competitive levels as well. In addition to such studies, waste management in tile manufacturing has also recently become an important issue. Accordingly, the industrial use of wastes in the traditional ceramic industry has been intensively investigated in the recent years. This work describes part of a detailed research project carried out jointly on the possible re-use of muds (raw production waste) from glazing and pressing lines of a local tile company in the development of new wall and floor tile formulations. In order to achieve this, the waste material was firstly investigated in function of chemical and mineralogical compositions. Then, the particular focus was given to the presence of the waste material in increasing amounts on the thermal behaviour and physico-mechanical properties of the re-formulated tile bodies. During the studies, SEM in combination with EDS, and thermal analysis techniques such as non-contact dilatometry were widely employed. The results indicated that it was possible to use the waste materials in the commercial tile production without deteriorating the relevant technological properties.

Jan 1, 2006

By L. A. André Santos

Atmospheric processing of nickel lateritic ores with low costs has been encouraged. In this work the kinetic of atmospheric acid leaching of a northern- Brazilian ore with 1.63% Ni and large amount of fine particles (d50 ≈ 0.075 mm and 40% below 0.038 mm) is presented. Chemical analysis showed a trend of Ni and Fe concentration in finer fraction (−0.075 mm) and Si and Mg in the coarsest one (−0.500 + 0.150 mm) associated to distinct mineral phases. Nickel is widespread in the mineral matrix. Distinct behaviors were observed as a function of particle size associated to the distribution of silicates and iron oxides in the ore. The kinetic modeling indicated that leaching is controlled by porous layer diffusion at 65 °C, but at 95 °C exhibits a mixed control by porous layer diffusion in initial minutes (60 min) and by chemical reaction or diffusion through the pore layer in final minutes (60–240 min) depends on metal evaluated.

By Dirk Verhulst

The Altair Hydrochloride Pigment Process is a new ?third route?, besides the established high-temperature chloride process and the older sulfate process, to manufacture TiO2 pigment from ilmenite ore. It has been tested at a scale of 5 t/day feed. The ore concentrate is digested in high-acid, high total chloride solution (+/- 39% Cl). Titanium and iron both go into solution. Iron is separated as FeCl2 crystals after reduction and cooling. Titanium is transferred by solvent extraction into a purified, high-Ti stream. It is spray-hydrolyzed to produce a TiO2 hydrate and further calcined with additives into high-quality pigment. HCl solutions generated by pyrohydrolysis and spray hydrolysis are treated by pressure-swing distillation to regenerate HCl gas for re-injection into the digestion reactor. All chloride streams are recycled. Recent work has concentrated on optimization, particularly in 3 areas: - Solvent extraction: a new organic mixture, including a new diluent, makes it possible to work at room temperature, to avoid TiO2 hydrolysis problems and to improve phase disengagement and impurity separation. - Pigment finishing: a systematic study of the parameters involved, followed by long runs in the best conditions confirm pigment quality. - Flow sheet optimization: innovative modifications of the conditions of spray hydrolysis and pyrohydrolysis, combined with re-routing of streams achieve significant energy savings. A 100 t/year pilot plant including these features as well as other process improvements is under construction.

Jan 1, 2006

By Jie E. Zhou, Yu U. Wang

"Development of crystallographic texture in polycrystals during templated grain growth process is studied by phase field modeling and computer simulation. To characterize the grain texture development, X-ray diffraction peak intensities are computed for the evolving grain structures as simulated by the phase field model, based on which Lotgering factor is further calculated as a quantitative measurement of uniaxial texturing. While the phase field modeling allows direct comparison between simulated grain structures and experimental microscopy observations, the computational diffraction allows convenient correlation between computer simulation and experimental X-ray diffraction characterization. The latter feature is especially desirable, since microscopy experiments normally require more efforts than X-ray diffraction, and diffraction is usually the preferred choice for material characterization.IntroductionThe properties of individual grains in polycrystals are generally anisotropic, while untextured polycrystalline materials with random grain orientations exhibit isotropic macroscopic properties that are independent of directions. In order to achieve anisotropic response in polycrystals, crystallographic texturing of grains is required [1]. Texture refers to the collective distribution of grain orientations towards preferred orientation in a polycrystal. To develop texture, special processing routes are needed, such as templated grain growth (TGG) for uniaxial texture [2]. TGG has been shown to provide uniaxial texture in wide variety of materials. For example, [001]-textured ferroelectric polycrystalline ceramics have been fabricated by TGG process, which exhibit enhanced piezoelectric properties [3]. Such highly textured polycrystalline materials offer better cost-performance ratio than single crystals. Thus, texture development in polycrystals is of technological importance for material applications.In this computational work, grain texture development in polycrystals during TGG process is studied. Grain structure evolution is simulated by phase field model, X-ray diffraction peak intensities for the evolving grain structures are computed, and Lotgering factor is calculated to quantitatively measure the development of uniaxial texturing. The phase field modeling allows direct comparison between simulated grain structures and experimental microscopy observations using imaging techniques such as scanning electron microscopy or optical microscopy. The computational diffraction allows convenient correlation between computer simulation and experimental X-ray diffraction characterization. The latter feature is especially desirable, because microscopy experiments normally require more efforts than X-ray diffraction, thus diffraction is usually the preferred choice for material characterization."

Jan 1, 2014

By Denise C. R. Espinosa

The amount of secondary batteries are increasing about 15% by year. Among these batteries, it can be highlighted the NiCd ones, due to their high consumption. In Brazil, the consumption of NiCd batteries grown quickly in the last 5 years, due to the dissemination of cellular telephones and other electronic devices. The first step of a process to recycle spent NiCd batteries is the pretreatment through unit operations of mining treatment. The aim of this work is to define a physical pretreatment to conditioning the waste to a pyrornetallurgical recycling process of spent NiCd batteries used in cellular telephones. Batteries were disassembled by hand to release the different components. The studied batteries are basically composed (by weight) of: 78% nucleus, 18% plastic case and 2% circuits. The grinding of the batteries was performed by knife mill and also by hammer mill. After grinding the material was screened and submitted to a magnetic separator.

Jan 1, 2001

By Jiann-Yang Hwang

Hydrogen storage is a critical issue for the hydrogen economy. Current storage technologies are not able to meet the combined gravimetric, volumetric, and system cost targets set by the Department of Energy. To solve the problem, the development of a new material - perhydride ? is proposed. Perhydrides are defined as materials that contain more hydrogen atoms in their molecules than conventional hydrides do based on the valence. This concept is supported by the versatile bonding capability of hydrogen and the recent discoveries in the chemistry of hydrogen clusters.

Jan 1, 2006

By Levente Becze

The zinc bottom dross is obtained as a by-product from hot dip galvanizing operations and contains at least 92 % zinc, which is recycled mainly by pyrometallurgical processes. The overall costs of such a treatment, however, are often relatively high, and the very strict environmental protection regulations might also cause additional difficulties for the high temperature procedures in the future. Therefore, a novel hydro-electrometallurgical process has been developed in our laboratory, by which one can reclaim zinc of high purity, while attempting to achieve low energy consumption and making allowances for all the environmental restrictions. This aqueous processing technique, based on electrolytic refining in a cell equipped with anion-exchange membrane to separate the anode and cathode compartments, allows the indirect purification of the anolyte. Zinc is dissolved from the anode along with some of the impurity elements, while the intermetallic compounds (Fe-Zn, Fe-AI- Zn) are accumulated in the anode slime.

Jan 1, 2003