By Klaus Bauckhage

Phase-Doppler-anemometry (PDA)-measurements have to be taken from representative measuring positions from inside the spray cone, helping - with the support of simulated data of improved process models - to describe the multiphase flow situations within the spray cone - and accordingly to that - the heat transfer conditions for the rapid cooling and (partly) solidifying melt droplets before their impact onto the substratddeposit. Simulations and PDA-measurements thus give the base to confirm the hypothesis of the existence of a semisolid mixed-layer and it's influence on the resulting material structure during compaction. The dispersed particles in the spray cone exhibit a cooling and solidification process within a split of a second, which leads - as far as the particles solidify - to a dendritic structure with very short dendritic arm spacings. This causes within the particles extremely short distances for the following equalizing diffision processes taking place on a high temperature level (between liquidus and solidus) in the semisolid mixed-layer of the deposit and explaining the short residence times within this zone of only seconds up to a few minutes. This and the fact that the globular structure of the mushy zone (in the semisolid mixed-layer) leads to an unidirectional crystallization process over very short distances also explains the chemical and morphological ,homogeneity of the sprayed material. The dynamics of these process steps, the very special buffer function of the mixing layer during parameter variations as well as the controlled cooling process of the preform in order to avoid hot cracks influence the quality of the material. Due to the necessity of measuring and controlling the particle bound mass-, momentum- and enthalpy- fluxes to the deposit the PDA-technique has been adapted and modified in order to receive in-line and (in the future) also on-line data from the dynamics of the multiphase flow conditions within the spray chamber.

Jan 1, 1999

By Zhijing Zhang

Sodium borosilicate is the basic composition of coating materials, Vycor and Pyrex glasses. In the present study, viscosities of Na2O-Si02-B2O3 ternary melts were measured under various compositions and temperatures. Experiments were carried out using rotary viscometer and graphite components. Our experimental results were compared with those in literature. Based on present experimental results, the previous structure based viscosity model was modified. The predicted viscosity results are in excellent agreement with the present experimental data in the temperature range with molten state samples. The fitting ranges of the model cover the composition of XB2O3 from 0.1 to 0.6 combined with xSio2 / xNa2O = 0.5, 1,2 and 5 respectively.

Jan 1, 1998

By Y. Yang, S. Peelman, J. Sietsma, Z. H. I. Sun

The rare earth elements (REEs) present in the Kiruna iron ore mine tailings are being considered as a new REE resource for the EU. These tailings, after beneficiation, contain approximately 5000 ppm of rare earths, concentrated in apatite and monazite minerals. To economically extract the REEs from these tailings the phosphorous contained within the apatite must also be extracted and the waste production of the process should be minimal. To achieve the extraction of REEs and phosphorous HCl and HNO3 were investigated as possible leaching agents. Based on the results a leaching process using HNO3 is proposed. This process produces H3PO4 from the apatite while simultaneously dissolving the REEs. The resulting leach liquor is then cooled to remove the unwanted Ca as Ca(NO3)2. Analysis of the leach liquor reveals extraction ratios of between 75% and 100% for the heavy REE (e.g. Y, Eu, Dy, …) and below 40% from the light REEs (i.e. Ce, La). Full phosphorous extraction was also achieved.

Jan 1, 2016

By Larry B. Fiske

Elimination of dust and processing of fines for both thermal and metallurgical coals is addressed. The efficiency of treatment with lignosulfonates compares favorably to oil in thermal coal. Effect of treatment with various lignosulfonates upon cokability of metallurgical coal was determined by Free Swelling Index, Gieseler Plasticity and Arnu Dilatation.

Jan 1, 1992

By Ryokichi Shimpo, Akio Fuwa

"In order to elucidate the present status of process-control technology, survey study has been made on the present process control schemes of representative copper smelting and converting processes in Japan. Conceptual control flow diagrams have been deduced and shown on respective functional reactors, i.e. drying, smelting, converting and fire-refining units, where the objective OUTPUT items are correlated to the INPUT variables through respective CAUSE-AND-EFFECT RELATIONSHIPSFuture view has been also discussed on several feasible and desirable improvement and refinement ~n measurements and control system for better copper smelting and converting operations.INTRODUCTIONIn other to seek for the better and efficient operation in copper smelting and converting process, survey study has been first conducted on the present process-control schemes of respective functional unit processes, i.e. drying, smelting, converting and refining unit processes, of representative copper production processes in Japan. Conceptual process flow chart of control scheme has been then deduced where output items are correlated to input items through the respective cause-and-effect relationships.After this survey study, future view has been discussed on the feasible and desirable improvement and refinement in the measurement and control system in these processes. Emphasis has been placed on the better and precise measurements of temperature, oxygen partial pressures in respective furnaces and end-point in converting and refining unit operations."

Jan 1, 1989

By Georgette Smits

The gun-sprayed refractory lining of electrothermal furnaces used for the manufacture of carbon disulphide from liquid sulphur and charcoal at between 800 and l000°C are severely attacked during the process. A mineralogical study of samples of eroded refractory material disclosed that carbon disulphide had penetrated the lining, causing the precipitation of sulphides and carbon, and the decomposition of mullite, a major constituent of the lining, to corundum and amorphous silica. Calcium, iron, titanium, and chromium are undesirable cations in a refractory that is used in furnaces for the production of carbon disulphide, since they react readily with this substance. A series of tests, in which samples were exposed to different amounts of carbon disulphide for various residence times and at different temperatures, was carried out with eight types of aluminosilicate-based castable and brick refractory materials, to compare their resistance to attack by carbon disulphide. Mineralogical investigation of the test cores showed that castable refractory materials are unsuitable for this type of process because of the presence of calcium aluminates and other impurities in the cement. Of all the refractories that were tested, a mullite brick of low porosity, containing a minimum amount of impurities, appeared to be the most suitable for use in this type of operation.

Jan 1, 1989

By Pengfu Tan

In order to understand and control the formation of dioxins and furans in iron ore sinter plants and to possibly avoid expensive end-of-pipe removal stages, thermodynamic calculations on the stability of PCDD/Fs have been combined with sinter process modeling by means of kinetic simulations and computational fluid dynamics. Three thermodynamic databases of PCDD/Fs, derived using the Group Additivity approach and two computational molecular modeling methods, MNDO and PM3, respectively, combined with the SGTE database have been used to model the PCDDIF formation and the PCDD/F isomer distributions in iron ore sintering. The results show very similar conditions for the PCDD/F formation using the different databases. Concerning the isomer distributions of toxic PCDD/Fs, the calculated data derived from the MNDO method showed optimum agreement with measured values from industrial furnaces. The thermodynamic calculations also proved that the isomer distributions found in combustion processes are equilibrium values, while the concentration ratio of PCDDs and PCDFs in the wind boxes does not represent an equilibrium state. A CFD model of iron ore sintering was developed including the kinetics of 15 relevant chemical reactions with the aim of describing the temperature fields and the gas flow patterns in the sintering bed. On the basis of these information and experimental observations reported in the literature possible pathways for the PCDD/F formation in sinter plants have been identified: PCDD/Fs are formed in the critical temperature region of 250 to 450 °C below the combustion zone, are then carried downwards with the gas and condensed close to the bottom of the sinter bed. Transported to the discharge end with the solid mixture, they are again released into the gas phase when the flame front approaches the bottom. PCDD/Fs are also formed in the last wind boxes when the hot off-gases cool down and reach the critical temperature range. Consequently, methods to reduce the dioxin formation reactions are proposed including inhibitor addition to the sinter feed and off-gas quenching.

Jan 1, 2003

By W. K. Choi

Stainless steel exposed to wet environments at ambient temperature is subject to the formation of a surface biofilm. Depending upon the prevailing environmental conditions (dissolved oxygen, pH, Eh, concentration of cationic/anionic species), the biofilm may stimulate corrosion through formation of differential aeration zones and concentration cells. Corrosion significantly impacts the United States economy, since on a yearly basis, corrosion induced losses are estimated to be over $200 billion. A large portion of this corrosion is imputable to bacterial activity, and basic information is needed for a better understanding and control of the biocorrosion phenomenon. The present study has investigated the influence of Thiobacillus ferrooxidans in the corrosion of American Iron and Steel Institute (AISI) 304, 316 and 416 stainless steel samples. The formation of biofilm and microstructural changes on the surface of stainless steel samples and their weldments were assessed by microscopic examination, and the changes in the mechanical properties by stress-strain measurements. The significance of the results will be discussed.

Jan 1, 1993

By Zhou Jiemin

A mathematical model is developed to determine the economic thicknesses of refractories and insulations in rectangular furnaces, Both the heat loss cost and the lining investment are taken into account to achieve a minimum operation cost. For the sake of calculating the heat flux, the paper is particularly concerned with the simulation of the three-dimensional transient heat conduction processes in the lining and a Douglas-Rachford method is used to solve the finite difference equations, The model has been used to design an industrial electric resistance furnace operated periodically. the values of temperatures and power consumption measured from the furnace correspond with the model results.

Jan 1, 1991

By Signe Kjelstrup, Leiv Kolbeinsen, Marit Takla, Odne Burheim

"This paper presents a Seebeck-type solid state thermoelectric power generator unit, designed to investigate the possible recovery of radiant waste heat at a silicon plant in Norway where roughly 703 of the total input energy leaves the process as waste heat. The unit is 0.5 m x 0.5 m and is built of 36 commercially available thermoelectric devices based on bismuth telluride p - and n - type semiconductors. Thermoelectric devices directly convert fractions of a heat flux into an electric current (and vice versa) and may therefore be convenient for recovery of waste heat when the heat source is discontinuously available. The purpose of the thermoelectric unit is to give a proof of principle of direct thermoelectric energy conversion on a large scale. We present the initial test results for the generator. At an average temperature difference between the heat reservoir and the heat sink of 98°C, we measured an open ciruit potential of 23.44 ± 0.06 V and the matched load power output was 39.4 W. At a temperature difference of 220°C, we predict the generator open circuit potential to be 40.8 V, which corresponds to an efficient Seebeck coefficient of 242 µV /K, and matched load power output to be 120 W.IntroductionThe world's power demand increases, driven by population growth and increase in living standards and simultaneously global warming is recognized as one of our most serious environmental problems. According to the International Energy Agency[l], the industrial sector accounted for approximately one third of the total global power consumption in 2005. Increasing the energy efficiency of industrial processes thus represents a benign and substantial route for addressing environmental concerns and energy security.In accordance with the second law of thermodynamics, all real processes are associated with lost work which is energy being dissipated as heat to the surroundings[2]. Improving the energy efficiency of industrial processes is about finding the process path associated with a minimum of lost work. The more evenly the losses are distributed, the smaller are the losses [3, 4]. In addition, exploiting the unavoidable waste heat will contribute to improve the energy efficiency. The waste heat may be utilized for heating purposes and/or it can be upgraded to work for instance via some sort of heat engine."

Jan 1, 2012

By Stephen C. Britten

An in-situ amperometric slag sensor for measuring the concentration of easily dissociable oxides in slags at temperatures between 1200-1600°C is being developed. The sensor provides the same information as potentiometric sensors while also providing data on the concentration of the transition metal species and the diffision kinetics within the slag. The electrochemical technique utilized in the sensor is similar to methods utilized in aqueous voltammetry.

Jan 1, 1998

By S. P. Vanka, B. G. Thomas, S. Sivaramakrishnan

"During the continuous casting of steel, transient 'flow events can be very important to the generation of quality problems, such as shear entrainment, surface level fluctuations and bubble entrainment. These phenomena can be better predicted using Large Eddy Simulation (LES) models than the K-E models, which have been extensively studied. In this work the turbulent transient flow in a water model of a continuous caster has been both simulated using LES models and measured using Particle Image Velocimetry (PIV). The results of PIV and LES have been compared to validate the LES model and also to enhance the understanding of the prominent transient features of the flow field. The flow near the top surface in PIV was found to contain periods of 5-1 Os when the velocities were three to four times their mean values, which is of importance to the shear entrainment of the liquid flux. In both simulation and PIV the upper roll structure is found to change chaotically from a single large recirculation structure to a set of distinct vortices. The inlet swirl in PIV is seen to persist more than halfway across the mold, causing a characteristic staircase velocity vector pattern when viewed in a plane parallel to the wide faces. The lower rolls in PIV are significantly asymmetric for very long periods of time (- I-hour) and go through a repeating sequence of features. One of these features involving a short circuit between the upward and downward flow in the lower roll is also seen in the simulation and is of significance to bubble entrapment.IntroductionThe turbulent flow through the nozzle and in the mold of the continuous caster has been studied extensively using computational Reynolds Averaged Navier Stokes (RANS) models of turbulent flow [1,2]. Defects, such as internal inclusion of liquid fl4x through surface shear, pencil pipe defects due to bubble entrapment, surface defects due to level fluctuations are caused by transient flow phenomena oc'curring in the mold. These phenomena can be better predicted using transient Large Eddy Simulation [3] or ""LES"" models."

Jan 1, 2000

By R. L. Miller

Oil -bearing metal sulfide sludges produced in treatment of an industrial wastewater, which includes plating wastes, have yielded to treatment by electrooxidation and hydrogen peroxide processes. The oxidation can be controlled to be mild enough to avoid decomposition of the organic phase while oxidizing the sulfides to sulfates. The pH is controlled to near neutral conditions where iron, aluminum and chromium(II1) precipitate as hydrous oxides. Other metals, such as lead and barium, may be present as sulfate precipitates with limited solubility, while metals such as nickel and cadmium would be present as complexed ions in a sulfate solution. The oxidations were found to proceed smoothly, without vigorous reaction; heat liberation was minimal.

Jan 1, 1992

By Charles Washburn

The authors review mercury sources, and contaminant streams, with particular emphasis on mercury that is extracted from precious metal ores. The design and operation of both large and small mercury distillation facilities are detailed. The relevant properties and characteristics of mercury and mercury vapor are presented. Facility engineering with respect to industrial hygiene, area ventilation, and material handling is presented.

Jan 1, 2003

By Pertti Koukkari, Nagendra Tripathi, Karri Penttilä, Justin Salmine

ChemSheet is a thermodynamic multi‐phase multi‐component simulation software, which is used as an Add‐in in Microsoft Excel. In ChemSheet, the unique Constrained Gibbs free energy method can be used to include dynamic constraints and reaction rates of kinetically slow reactions, yet retaining full consistency of the multiphase thermodynamic model. With appropriate data, ChemSheet models can be used to simulate reactors and processes in all fields of thermochemistry. The presentation will cover off‐line modeling of Cu‐flash smelters and advanced thermochemical simulation coupled with on‐line process control of Cu‐Ni smelting. The presentation will describe an off‐line model of Cu‐smelter based on critically assessed properties of the Al-Ca-Cu-Fe-O-S-Si –system (slag, matte and liquid metal) by using the quasichemical model. A four‐stage reactor model (shaft, settler, uptake and bath) is used for optimizing process parameters and feed particle distribution. As a second example, an advanced thermochemical model of a Ni-Cu sulphide smelting plant will be given. The on‐line model covers the operation of treating Ni-Cu-S concentrate via roasters, electric furnace and converters, producing a high grade Bessemer matte product for further refining. The model integrates the thermochemistry of the roasters and electric furnace, and predicts important process parameters such as degree of sulphur elimination in the fluid‐bed roasters, matte grade, iron metallization, slag losses and the iron to silica ratio in the electric furnace slag. Both models can be used to assist process engineers and operators in calculating the addition rates of coke, flux and air for different feed scenarios.

Jan 1, 2014

By Cheng Pan, Qiugang Yuan, Xuewei Lv, Mei Liu, Enguang Guo

Land-based nickel resources include nickel sulfide and nickel laterite. With the consumption of high grade nickel sulfide, use of nickel laterite has received more and more attention. The mineralogy and sintering behavior of limonitic nickel laterite with high iron and low nickel and silica was studied to offer technical support for producing ferronickel through sintering–blast furnace route. The mineralogy results showed that the main phases in this kind of nickel laterite are goethite (FeO(OH)), gibbsite (Al(OH)3) and NiFe2O4. The TGA (Thermogravimetric Analysis) and DSC (Differential Scanning Calorimetry) revealed hydroxide minerals in addition to absorbed water. After the sintering experiments the chemical composition, phases present (XRD analysis) and physical properties of the sinter were studied. The content of FeO in the sinter increased with increasing basicity up to 1.3, and then decreased with further increase in basicity. The yield of sinter increased (from 73% to 80%) with increase in the basicity from 1.1 to 1.7, and then the yield decreased with the further increase in basicity. Mg(Ni)(Fe,Al)2O4 is the main phase in the sinter while MgCaSiO4 and Fe2SiO4 is the main binder phase when the basicity is 1.1~1.5, and MgCaSiO4, Fe2SiO4 and SFCA is the main binder phase when the basicity is 1.7~2.1.

Jan 1, 2014

By Qinmeng Wang

The oxygen bottom blown copper smelting process is a new technology which has been widely applied to the copper production in China. In this work, a computational thermodynamics model for this technology has been established, based on smelting mechanism and theory of Gibbs free energy minimization. The calculated results from the model agree well with the actual industrial data, indicating that the model can be used for the predictions under different operating conditions. The tendencies of the key parameters (such as Cu losses and Fe3O4 content in slag) and the distribution ratios of the minor elements (such as Pb, Zn, As, Sb and Bi) can be predicted by adjusting the oxygen/ore ratio charged into the bottom blown copper smelting furnace. The model can be used to monitor and optimize the industrial operations of the oxygen bottom blown copper smelting process.

By W. K. Tolley

The Bureau of Mines is investigating hydrometallurgical processing techniques to recycle metals from semiconductors and other advanced materials. Cadmium and tellurium were recovered from CdTe scrap produced in the manufacture of infrared optic devices. Sulfation, ferric chloride leaching, and oxygen-pressure leaching have been tested. Cadmium dissolution was achieved using oxygen-pressure leaching in dilute sulfuric acid. However, no satisfactory scheme for dissolution of the higher valued tellurium has been devised. Leaching the ground CdTe for 75 min at 110°C in 1.1M H2S0, under 120 psig 0, yielded 99.5% Cd extraction. Tellurium remained in the leach residue as TeO, and elemental tellurium; residual cadmium was less than 0.5%. The cadmium in the leach liquor was purified of coextracted metals such as gallium and iron by adjusting the pH. The cadmium was recovered as cadmium sulfate crystals by evaporating the solution. Recovery of by product metals, notably gallium, is possible.

Jan 1, 1991

By T. C. Goel, A. Venna, R. G. Mendiratta

"Processing of ferrites has gained tremendous importance in recent times to meet the high performance demands on ferrites in keeping with the fast emerging· technologies. The quality of ferrite powders has strong influence on ·the performance of final device. Fabrication· of high performing ferrite components requires starting ferrite powders of precise stoichiometry, purity and microstructure. It is difficult to obtain these attributes by the conventional ceramic method. The key to obtaining quality powders lies in the· solution techniques. With this in view soft ferrites have been prepared by a wet chemical process, known as the citrate precursor method, which involves the formation of citrate complexes of the constituent cations. The advantages of this process are the ease of preparation and close control of composition, homogeneity, purity and particle size. Electrical and magnetic measurements on lithium ferrites have shown resistivity higher by more than two orders of magnitude compared to that observed for samples prepared by the conventional ceramic method, and low magnetic losses, making the ferrites specially suitable for high frequency applications.IntroductionProperties of ferrites are known to be sensitive to .their processing technique. A small deviation in the compositional stoichiometry of the ferrite affects its properties greatly. Soft ferrites such as Ni-Zn, Mn-Zn and Mg-Mn. are well known ferrites covering wide-ranging applications [1,2]. Lithiiim ferrites have also assumed technological importance for microwave applications and are potential substitutes for the expensive garnets [3]. Lithium ferrites are often doped with zinc to tailor the saturation magnetization required at high frequencies. Lithium and lithium-zinc ferrites, however, present difficulty to processing due to the volatile nature of both the cation components, namely Li and Zn. These ions are volatile at temperatures > 1000°C which makes their processing difficult. One of the main considerations of high frequency performance of ferrites is the high eddy current losses which prevent the interaction of the magnetic field with the ferrite component and hence impair device performance. These losses can be reduced by having a material of high resistivity. Electrical conductivity in lithium ferrite has been attributed to electron hopping [4] between the two vaience states of iron, Fe2+ <=> Fe3+, on octahedral sites. Maintaining the + 3 valence state of otahedral- Fe ions is thus a prerequisite for achieving high resistivity. The resistivity of ferrites is normally found to be low when processed by the conventional solid-state or the ceramic method [5]. This is attributed to (a) extensive ball-milling employed in the method to mix the component oxides results in non-stoichiometric compositions due to introduction of additional Fe ions on abrasion of steel balls during milling, (b) high processing temperatures involved which result in significant volatilization of Li and Zn ions creating thereby oxygen non-stoichiometry which results in reduction of Fe3 + to Fe2 +, (c) large and non-uniform grain sizes. In the present work, preparation of Li and Li-Zn ferrites by a non-conventional method known as a citrate precursor method [6, 7] which requires lower processing temperatures and duration is reported. The method gives stoichiometric compositions on account of homogeneous atomic-scale mixing of the constituent cations via the formation of metal-citrate complexes mixed in solution state. The method is also capable of giving small grain size which aids the oxidation ofFe2+ ions."

Jan 1, 2000

By John J. J. Chen, Barry J. Welch

"The production of primary aluminium can potentially lead to metal that, with minimum treatment, meets a high purity standard. Smelters that can achieve a significant proportion of their production in this manner have a competitive edge which is of growing importance as the use grows for such items as compact discs and the like. Superimposed on the desire to produce high quality metal are stringent environmental requirements that the industry must adhere to. The environmental legislation focuses on fluoride emissions and the approach adopted is towards a zero waste management philosophy. The fluoride recycling process does, however, result in volatile impurities being captured and recycled to the cell. Aluminium has an extremely high reduction potential and this results in a significant proportion of the recycled impurities being reduced at the electrolyte metal interface and thus contaminating the metal. This paper reviews sources of impurities and the impact of the operating procedures adopted on metal treatment.IntroductionSeveral factors have contributed to the immense growth in the aluminium smelting industry. Initially the ready availability of hydro electricity provided a primary reduction energy source for the production of the light-weight metal. Because of its unique properties and innovation in the industry there has been a continued exploitation of its unique properties, especially at the high purity end of the metal. The industry has shown considerably versatility and innovation in adapting to the ever increasing demands of quality and purity. It is however a competitive industry and the ability to produce high purity grade metal (>99.9% pure) gives a competitive edge. Emerging markets such as for CD ROM disc production etc, will keep the quality demand stringent.While the industry has met the continuing demands for metal quality, it has also had to respond to stringent environmental requirements for emissions from the production plant. Like all extractive metallurgical processes carbon dioxide is an inevitable reaction byproduct. However, the volatilization and hydrolysis of the solvent electrolyte leads to fluoride emissions that are potentially harmful. Accordingly, the industry has adopted essentially a zero non-process waste management approach. All cell emissions, including reducible impurities, are recycled back to the cell. This has had a significant influence on the metal treatment processes."

Jan 1, 1996