By Yungang Li, Hui Li, Ramana G. Reddy, Jinglong Liang

High solid corrosion protective coatings were prepared by the dust of the converter with an average particle size of 59.33 μm. The effect of different amount of benzyl alcohol diluent on the performance of high solid anti-corrosion coatings was studied. With the increase of the amount of diluent, the viscosity of high solid anti-corrosion coatings reducing, the film apparent bubble content decreasing, and film resistant to salt water corrosion ability decreased, while acid corrosion capacity enhancement. When the dosage of diluents is 15%, the coating film is more resistant to acid corrosion.

Mar 1, 2017

By D. S. Barr

Mineralogical, lithological, and metallurgical studies were conducted on various gold ore deposits currently controlled by Freeport-McMoRan Gold Company. Ore samples were first lithologically and mineralogically categorized, then subjected to chlorination, roasting, and autoclaving pretreatments to determine their effects on gold recovery in a subsequent alkaline cyanide carbon-in-leach extraction. The studies indicate that, while organic carbon and sulfide sulfur are the primary refractory components, their effect on process response must be interpreted with respect to the deposit's geology and mineralogy. This approach has proven to be an effective method for evaluating metallurgical alternatives and fore-casting future mill performance.

Jan 1, 1987

By Robert Mensah-Biney

The loading characteristics of gold-tetrabromide species onto a weak-base resin, PAZ-4, were evaluated using a completely mixed batch reaction system. The time. to attain equilibrium loading was substantial, on the order of several days. However, abnormally high loading capacity values of 15 to 20 meq Au/g dry resin (1000 to 1300 kgAu/tonne) were attainable in 24 hours. The loading of gold-bromo species by P AZ-4 was visualized as consisting of two processes: (i) the rapid adsorption of [AuBr4r species by simple ion exchange mechanisms and (ii) reduction of [AuBr4r to metallic gold by an electron exchange mechanism. Elution of gold from loaded resin was feasible provided the resin had not been loaded to high capacity values. If loading is carried to high levels, complete elution becomes impractical and the gold may be recovered by ashing the loaded resin. For the high loading capacities observed this option would appear to be cost effective.

Jan 1, 1991

By D. Bruce Wilson

The reaction of oxygen and solid aluminum produces the well-known surface coating of aluminum oxide, Al2O3. Thermodynamic properties and kinetic mechanisms of this reaction are extensively documented. Less well-defined are the corresponding liquid phase reaction and reactions which would be characterized. as 'burning' of aluminum. This paper reviews the solid aluminum-oxygen reaction as a foundation for discussing the flammability of aluminum in oxygen-enriched atmospheres. Appropriate thermodYDan3ic analysis and kinetic reaction mechanisms are developed. Available models of aluminum burning are reviewed and evaluated, The appropriate information for design of engineering applications of aluminum in oxygen atmospheres? is summarized.

Jan 1, 1996

By Hiroyuki T. Takeshita

Ca-Ni based alloys were investigated on structures, hydrogenation properties and the effect of additive elements on hydrogenation properties. CaNi, samples were decomposed to form a new hydride with a CsCl-type structure on the constituent metal atoms at high temperatures such as 673K in a hydrogen atmosphere. The candidate of the third element which was added to stabilize the original compound was investigated by using the Miedema's semi- empirical model and, as a result, Pd was chosen. The hydrogenation of CaPd was conducted with a Sieverts' type apparatus and the synthesis of Ca-Ni-Pd ternary alloys was performed by high frequency heating.

Jan 1, 2002

By Varadarajan Seshadri

The performance of mould fluxes in satisfying its quality requirements can have a significant effect on the efficiency of the continuous casting process and on the surface quality of the products. This performance is affected by various parameters including the characteristics of the mould fluxes, the quality of the steel being cast and the operational conditions of the caster. The extremely complex relationships involving the parameters mentioned above make it very difficult to have simple criteria for selecting mould fluxes for casting a certain grade of steel in a continuous casting machine. These difficulties led steelmakers and mould flux suppliers to select mould fluxes based mainly on plant trials. In the present work, a software to help in the analysis and development of mould fluxes for continuous casting was developed_ This software includes several models for prediction of mould flux viscosity and consumption. A mathematical model was also used to predict the heat flux through the mould flux. The proposed methodology was applied to continuous casting of crack sensitive steels_ Some of the results given by this software are presented, discussed and compared to plant data.

Jan 1, 2003

By Manuel Alvarado, David Nemir, Jan Beck

"Thermoelectric generation using special N-doped and P-doped semiconductors is well known as a means for direct heat energy to electrical energy conversion without the need for moving parts. The technology is used today in niche markets for low level electricity production and has been proposed as a scalable means for capturing large scale energy from waste heat streams. The choice of geometry of the thermoelements and conductors is critical to the successful implementation of a waste heat recovery system in order to manage losses due to Joule heating and diffusive heat flows. This paper describes a simulation study to define the performance impact of different aspect ratios for the active thermoelements and the electrical interconnect. The use of a finite element model that incorporates the intercoupled heat and electrical energy flows highlights some of the issues impacting scalability.IntroductionThermoelectric phenomena arise out of the intercoupled electrical and thermal currents in a material. A two-element thermoelectric generator is depicted in Figure 1. It is constructed by connecting an N-type thermoelement and a P-type thermoelement in electrical series, with both elements in thermal parallel between a heat source and a heat sink. The electrical series connection is made by attaching conductors as shown. Ideally, these series connection elements will be both good thermal conductors and good electrical conductors.The two element generator in Figure 1 is disposed between two thermal reservoirs: the heat source, which furnishes heat energy; and the heat sink, which absorbs heat energy. Heat energy flux Q, flows from the heat source to the heat sink, driven by the temperature difference between the source and the sink. As depicted in Figure 1, when a resistive load, R, is attached, electrical current, I, may be extracted from the thermoelectric generator and furnished to the load. The N-type and P-type thermoelements, are the active portions that do the actual conversion of heat energy to electrical energy. Although thermoelements may be built using conductors such as bismuth and antimony, higher efficiency thermoelectrics are built using heavily doped semiconductors. Thermoelectric devices are generally formed by connecting many pairs (couples) of N and P type thermoelements in electrical series and in thermal parallel. A commercially available module having 127 couples (254 elements) is shown in Figure 2."

Jan 1, 2011

By F. Qian

An impinging gas jet on a liquid surface is found in many industrial process systems such as electric arc furnace, welding, steel-making operation and others. Fundamental understanding of the interaction of a gas jet on a liquid pool can provide important insights into process behavior resulting in improved efficiency. A numerical model is developed for solving the flow fields of both impinging gas jet region and liquid pool below, in which the deformed interface shape is predicted simultaneously. Using curvilinear coordinates, the Navier-Stokes equations of each phase are solved separately through coupling of static pressure, shear stress and velocity at the interface. Several cases for jet distances and flowrates were investigated both numerically and experimentally with an air-water model. Favorable comparison of numerical results with experimental data confirms the validity of the present numerical approach. An existing phenomenological model for 'penetration depth' prediction was extended for smaller 3et exit height to jet diameter' ratios.

Jan 1, 1995

By Peter G. Mason

Over the last 15 years numerous Pressure Oxidation and Pressure Leach plants have been installed throughout the world. The technology is no longer regarded with awe and trepidation as plants designed to treat a wide range of feedstocks continue to be successfully brought on line. Important aspects of the design of such plants include feed preparation, slurry pumping, heating and heat recovery, pressure control and let-down, vessel design, safety and provision of associated services.

Jan 1, 1999

By Frank L. Marley

Mexican silver mining operations have existed prior to the sixteenth century. Recovery processes throughout the centuries were developed at the many mining localities and have progressed through smelting, the patio amalgamation process to cyanidation and flotation. A study of the present silver mining zones is reported in which the ores are evaluated in terms of the mineralogical constituents, their state in the matrix and the effects these are noted to impose upon the efficiency of recovery. Silver mineral identifications were by quantitative ore microscopic and scanning electron microscopic energy dispersive X-ray analysis.

Jan 1, 1982

By Linli Wu

During the measurement of contact angle, a misty band was observed near the substrate. Hsien-Nan Ho and Shinn-Tyan Wu thought this was because the oxygen atoms on the interface migrate to the droplet surface to form an oxide band near the substrate. But from our experiments misty band appeared before the drop reach to the substrate. Theoretically speaking, the oxygen partial was the same everywhere in the vacuum furnace. So there was no condition to provide enough oxygen forming oxide. This appearance would be explained more reasonably with the optics principle. Most reflected light would be absorbed by the substrate and the light cannot reach the observation area, so the misty band formed.

Jan 1, 2006

By P. M. Tait, N. A. Warner

"The refining of thermally produced zinc is currently performed using a highly energy intensive and arguably outmoded process, distilling zinc under atmospheric pressure at temperatures of 900°C to 1000°C. In order to produce refined zinc more profitably and with less environmental impact a new process has been proposed. This process is generic to all thermal zinc smelters and aims to match the purity of zinc from current technology (99.99%-99.999%). The objective is to perform all separation processes using only the heat contained in the smelter product stream. Vacuum conditions are extensively used lowering operating temperatures and enhancing separations. As part of this process zinc is distilled under vacuum from high concentration obtaining a refined product with respect to lead content. A mathematical model has been developed from fundamental principles to describe this stage, the distillation of zinc across a temperature difference between two circulating zinc streams in open channels under vacuum. Heat for the distillation is supplied by the liquid phase, necessitating a large recycle to maintain high operating temperatures, and keep zinc concentrations high. In determining this model and the operating conditions required, relationships between temperature, pressure and composition are considered.IntroductionCurrent technology (the Refluxer) used to refine thermally produced zinc is both expensive and highly inefficient. At present 80% of the worlds zinc is produced via the electrolytic process reflecting the poorer performance of the thermal route, the zinc-lead blast furnace and Refluxer. A new process is proposed to overcome the drawbacks of current processes. These drawbacks are both economic and environmental. The Refluxer requires 6.6 GJ of energy to refine one tonne of SHG zinc 1, other disadvantages of the Refluxer stem from high operating temperature, around 900°C, and liquid zinc being highly corrosive towards ferrous metals. The Refluxer is constructed from silicon carbide sections which join together by means of flat machined faces making liquid metal leaks inevitable. The Refluxer columns are very sensitive to thermal cycling, thermal shock and mechanical vibration, which easily lead to structural failure. To avoid thermal stress on the columns the feed rate and feed temperature need to be kept constant which means the feed baths to the columns must be able to accept solid and liquid feed as the Refluxer has to operate when the smelter is shut down."

Jan 1, 1998

By D. Papazoglou

This work was undertaken to investigate the thermodynamic and kinetic feasibility of using hot sulfur dioxide bearing gases from smelting processes to selectively sulfate the nickel in nickel laterite ores for subsequent extraction in water. The environmental benefits of this approach, as opposed to releasing the gas to the atmosphere, and the economic benefit of directly utilizing the SO2 rather than converting it to sulfuric acid are strong drivers for such a process. A thermodynamic analysis indicated that selective sulfation of the nickel could be feasible under appropriate conditions and these were explored through a series of laboratory scale experiments. Laterite samples were reacted at temperatures between 500 and 800°C with an equilibrated mixture of sulfur dioxide, oxygen and nitrogen in a fixed bed reactor. Tests were conducted on saprolitic ore from Bulong, Western Australia:, limonitic ore from New Caledonia and gamieritic ore from Indonesia. Nickel extractions were highest from the limonite and relatively low from the other ores. The maximum selective extraction of nickel from the limonite in a single stage sulfation was 73%. Sulfation of other elements present in the laterites was also examined. A two-stage process was also identified which involved sulfation using a strong sulfation potenrial followed by weaker sulfation potential to attempt to convert ferric sulfate formed in the first stage to ferric oxide. This increased the extraction for the limonite ore to around 84% Ni, 95% Co and 2% Fe. Direct sulfation of laterite could be feasible in locations where sulfide smelting or roasting operations are relatively close to laterite deposits.

Jan 1, 2003

By D. Papazoglou

This work was undertaken to investigate the thermodynamic and kinetic feasibility of using hot sulfur dioxide bearing gases from smelting processes to selectively sulfate the nickel in nickel laterite ores for subsequent extraction in water. The environmental benefits ofthis approach, as opposed to releasing the gas to the atmosphere, and the economic benefit of directly utilizing the S02 rather than converting it to sulfuric acid are strong drivers for such a process. A thermodynamic analysis indicated that selective sulfation of the nickel could be feasible under appropriate conditions and these were explored through a series of laboratory scale experiments. Laterite samples were reacted at temperatures between 500 and 800°C with an equilibrated mixture of sulfur dioxide, oxygen and nitrogen in a fixed bed reactor. Tests were conducted on saprolitic ore from Bulong, Western Australia, limonitic ore from New Caledonia and garnieritic ore from Indonesia. Nickel extractions were highest from the limonite and relatively low from the other ores. The maximum selective extraction of nickel from the limonite in a single stage sulfation was 73%. Sulfation of other elements present in the laterites was also examined. A two-stage process was also identified which involved sulfation using a strong sulfation potential followed by weaker sulfation potential to attempt to convert ferric sulfate formed in the first stage to ferric oxide. This increased the extraction for the limonite ore to around 84% Ni, 95% Co and 2% Fe. Direct sulfation of laterite could be feasible in locations where sulfide smelting or roasting operations are relatively close to laterite deposits.

Jan 1, 2003

By Varadajan Seshadri

Keywords: torpedo car, kinetics, physical modeling A 1:6 torpedo car physical model was built to assess the optimum refining conditions for pig iron desulfurization in the torpedo car considering the industrial parameters used in the steel plant CSBM (Companhia Siderurgica Belgo-Mineira, João Monlevade, MG, Brazil). The refining practice in this plant is through injection of a CaO-CaF2-Mg powder in the pig iron melt. Similarity between the model and prototype were established through Froude and turbulent Reynolds criteria. Mixing times were evaluated by pulse tracer addition and the kinetics of metal/slag interactions were assessed from experiments investigating iodine transfer from kerosene to water. The influence of parameters such as level of metal, gas flow rate, lance penetration, lance orientation were also evaluated.

Jan 1, 2005

By A. Andreas Hejja

Flow of slag and settling of matte in slag resistance electric furnaces are discussed in conjunction with furnace geometries, stirring action of the electrodes, buoyancy and electromagnetic effects. The rectangular electric furnace was regarded as a channel reactor and the mode of slag flow as a channel flow. The flow is affected both by buoyancy and electromagnetic forces, however the effect of electromagnetic forces is minimal. The flow velocity is made up of two components; (i) that developed by the action of the electrodes, and (ii) the bulk flow velocity determined by the smelting rate and the volume of the reactor. Slag samples were taken from various depths of the molten bath and were analyzed microscopically to determine the size and distribution of matte particles, The action of the electrodes was described by a simple mathematical formula indicating a balanced settling rate in the area of electrode action.

Jan 1, 1996

By Alaina Mallard, Jannette Chorney, David Hutchins, Grant C. Wallace, Jerome P. Downey

Current commercial processes for producing ceramic carbides require temperatures of 1400–2000 °C and often use extensive milling operations to produce a powder product. A process that could reduce the energy requirements of commercial carbide production could allow for these materials to be implemented in a greater number of applications. In this study, tungstate (WO4 2−) and silicate (SiO3 2−) anions were adsorbed onto activated carbon and converted into silicon carbide (SiC) whiskers and a mixture of tungsten and tungsten carbide (W/WC) crystals via carbothermal reduction using inert and reducing gas atmospheres at temperatures much lower than what is required by current commercial processes (950 °C for W/WC/W2C and 1200 °C for SiC). The adsorption process was statistically-optimized via a central composite response surface analysis using DesignExpert 9. Inductive coupled plasma optical emission spectroscopy (ICP-OES) was used to measure, and optimize, adsorption efficiency while the carburization products were characterized using X-ray diffraction and scanning electron microscopy.

Mar 1, 2017

By Markus A. Reuter

In this paper, the kinetics of phosphorous production in submerged-arc furnaces will be discussed as a function of temperature, as well as various ore and reductant types. Interesting positive synergetic effects on the rate of reaction could be observed when mixing different types of ores. The results will be discussed with reference to a kinetic model, microprobe analyses, etc. The effects these results have on the control of the furnace will also be discussed in detail, indicating how these could be incorporated into the electrode and metallurgical control systems for submerged arc-furnaces.

Jan 1, 2000

By W. Drummond

The cooling of smelter gases by air dilution, adiabatic evaporative cooling and indirect heat exchange is discussed with reference to the ,process, to the subsequent cleaning of the gas and to the use of the heat extracted from the gas. The method of reducing the effect of acidic ,sulphide formation on the corrosive properties of the gas and the dust and the development of surface cleaning mechanisms are discussed. The development of indirect recuperators using air, water or steam cooling, made 'possible by the control of surface fouling is traced. The application of the modern Waste Heat Boiler to the new sulphide smelting processes is discussed with respect to the natural and forced circulation concepts. Case histories are presented to illustrate mistakes made with respect to designs produced without recourse to sensitivity analysis and without an appreciation of "worst process conditions".

Jan 1, 1992

By A. W. Bryson, S. P. Fox, S. A. Godorr

"This work is an extension of a previous investigation on the development of surface roughness during electrodeposition of copper. A comprehensive model based on diffusion and migration in a force field together with surface diffusion and sticking probabilities is used to generate profiles which are compared to those produced experimentally. The roughness is characterized by using the technique of fractal geometry which is shown to describe both qualitatively and 9uantitatively the development of surface morphology during electrodeposition.The work is extended to the deposition of copper in the presence of various concentrations of thiourea. The development of roughness is observed experimentally on the edge of a thin copper disc mounted between two glass plates. This enables photographs to be taken at various stages during growth. The surface outline is digitized using an image analyzer which enables the fractal dimension to be determined as growth proceeds. As expected, the presence of thiourea at low concentrations produces a fractal dimension which is closer to unity (i.e. the surface becomes smoother).IntroductionThe development of surface morphology during electrodeposition has far-reaching implications for copper plating in the electrowinning and electrorefining processes. Short circuits as the cathode surface grows unevenly require operator intervention in a dangerous environment and imply processing delays, and the inclusion of electrolyte in small gaps in the plated cathode have implications in downstream processing of the cathode. Higher current densities are obviously desirable, as they result in greater production rates, but as shown by Ettel et. al.(l), Harvey et. al.(2), Cook (3), and Harvey et. al.(4), it is not possible to operate near the projected economically optimum conditions because the electrodeposition of copper from sulphate and acid solutions is a mass transfer controlled process. It has been shown (Ettel et. al.(l), Harvey et. al.(2)) that the closer a system operates to mass transfer limiting conditions, the poorer the resulting cathode quality. One solution is to use agitation techniques to increase the limiting current density. Another is to add surface active additives to the electrolyte which has been shown by Ettel et. al.(l), Harveyet. al.(2) and Afifi et. a1.(5) to allow higher rates of production without decreasing cathode quality. The second proposed solution is of interest in this work, since there is very little knowledge of the conditions under which these additives operate effectively, and little fundamental understanding of the mechanism by which they operate. The current work seeks to contribute to this field by correlating a simulation model with experimental results to describe the development of surface morphology in the electrodeposition process."

Jan 1, 1997