By Charles A. Sorrell

Two red muds, two fly ashes, and several aluminosilicate minerals were subjected to direct treatment with concentrated H2SO4 at temperatures of 175°C and below. X-ray analysis showed that virtually all the sulfate reaction products remained in the solid residue because of their low solubilities in x SO Substantial portions of the Al2O3 Fe2O3TiO2, Na2O, and K2O components of the materials reacted to form water soluble sulfates, which were then removed by H2O leaching at 55°C. The solid residue after water leaching consisted largely of amorphous silica and, in lime bearing compounds, CaSO4, The reaction and leaching processes were effective in removing all or nearly all the Al2O3. Fe2O3, TiO2, Na2O, and in lime components in the fly ashes, red muds, china clay, bentonites, the nephelioe fraction of nepheline syenite, and a plaster insulating brick composed of anorthite and mullite. Reaction with potassium feldspar and petalite took place, with formation of alkali aluminum sulfates, but the reaction rates and yields were extremely low. Potassium feldspar can be heated with Na2O and x O in air at 700°C for 24 hours, or with CaO at 1000°C for 24 hours, after which the reaction product kaliophilite, nepheline, and leucite-like phases, prove to be very susceptible to H2SO4, reaction and H2O leaching, providing yields near 100% of the Al2O2 content. An alternative method of H SO treatment consists of heating the sample in a silica tube and passing H2SO4 vapor over it. Preliminary results indicate that this method can be effective in enhancing the kinetics of reaction with the Al O component of potassium feldspar and offer the possibility that formation of Al2 (SO ) Fe2(SO4)3 and TiOSO4 can be accomplished selectively by taking advantage of the fact that the upper stability limits of the respective sulfates in the presence of H2SO4 vapor will be different.

Jan 1, 1982

By De-wen He

The distribution of persistent organic pollutants in the environment is studied using the multimedia environmental fugacity model, and environmental health risk assessment of POPs nearby a copper smelt enterprise is carried out. The result indicates that all are in an agreeable risk level without exception. The annual individual chronic risk index of HCB is 7.50×10-11. The annual individual risk index of 3,3',4,4'-TCB is 1.57×10-9, and the annual individual risk index of 2,3,7,8-TCDD is 6.57×10-9.

Jan 1, 2009

By Akira Yazawa, Kazuo Koike, Mitsuhisa Hino

"The vapor pressures of MS (PbS, SnS and Sb2S3) in the molten Cu2S-MS, FeS-MS pseudo-binary and Cu2S-FeS-MS ternary systems were measured by means of a transportation method in the temperature range of 1323 and 1423K to calculate MS activities in the sulfide melts. The activities of MS in these systems show negative deviation from ideal behavior except the FeS binary systems which exhibit nearly ideal behavior in the homogeneous melts. The activities of the Cu2S-FeS pseudobinary system, which is fundamentals of the copper matte, were estimated from the activity values in the ternary systems and exhibit negative deviation from ideality.The distribution behavior of tin between the ·matte and silica saturated fayalite slag was investigated under the controlled partial pressures of S02 at l 523K. It was found that, in general, tin is distributed in the both phase, while tin is concentrated to the slag phase with increasing copper content in the matte. The activity coefficient of SnO in the slag was calculated based on the distribution ratio combined with the activity coefficient in the Cu2S-FeS system.IntroductionThe thermodynamic properties related to the Cu2S-FeS system and the Cu2S-FeS-MS systems (where MS can be PbS, SnS, Sb2S3, As2S3, Bi2S3, etc.) is required to be better understanding of the copper smelting process. However, thermodynamic analysis such as the distribution of impurities among the gas, slag and matte phases is difficult due to lack of thermodynamic data. In this study, the vapor pressures of MS (PbS, SnS and Sb2S3) in the Cu2S-MS, FeS-MS. and Cu2S-FeS-MS systems were measured by a transportation method. The distribution behavior of tin between the matte and silica saturated fayalite slag was also investigated. The results in the present experiments are useful to analyze thermodynamically the behavior of component in the copper matte smelting."

Jan 1, 2000

By Xiao Yang

Calcium oxide is one of the major fluxing agents used for steel refining. Because unreacted CaO remains in slag in most cases, discharged slag is difficult to be recycled smoothly. With the growth of environmental concerns, improving utilization efficiency of CaO is required to reduce the amount of discharged slag and energy consumption. The authors have reported a resource and energy-saving process by using multi-phase flux for dephosphorization. Reaction behavior of phosphorus in multi-phase CaO–FeOX–SiO2–P2O5 flux system was investigated. Formation mechanism of P2O5-rich phases was clarified at the interface between solid CaO or 2CaO, SiO2 and molten CaO–FeOx–SiO2–P2O5 slag. Phase relationship and thermodynamic properties of 2CaO, SiO2-3CaO, P2O5 solid solution were observed to confirm the condensation of P2O5 in solid phase. Based on these results, reduction of CaO consumption, discharged slag curtailment, and energy-saving effects in the novel refining process by using multi-phase flux were discussed.

By Takayuki Watanabe, Yoshiki Shimizu, Yusuke Moriyoshi

"B-C-N nanotubes prepared by a flush evaporation method using a de arc plasma were mainly characterized by transmission electron microscopy (TEM) and electron energy· loss spectroscopy (EELS). The nanotubes obtained· were divided into three types such as carbon boron nitride and carbon or carbon nanotubes surrounded with boron nitride nanotubes. These types of nanotubes were obtained at higher temperatures than about 3000 K, however, these were not formed at lower temperatures than about 3000K. On the other hand, 11anocapsules were· formed at all the experimental temperatures and nanocapsules with a homogeneous phase were obtained at lower temperatures than about 3000 K. The effect of additives on the formation of B-C-N nanotubes was not clear. Based on these experimental data depending on temperatures and corresponding microstructures, the formation mechanisms of both nanotubes and nanocapsules were briefly .discussed 1 Introduction As reported previously, nano tubes have unique electrical properties1, 3) The preparations of nallotupes have been usually carried out by flush evaporation methods using either a de arc plasma or a laser4 -5) By these methods the reaction rate is so rarid that we have no data of intermediate products between initial raw materials and. final products of nanotubes 6-9). So, the formation mechanisms of nanotubes have been mainly speculated only from the microstructures of resultant nanoiubes. In order to have more reliable formation mechanisms, it is particularly important to have the information of intermediate products at the corresponding temperatures. From the viewpoints, we have studied about the effects of temperatures on the preparation of nanolubes. Here we report mi firstly some problems on the preparation of B-C-N nanotubes 10), secondly the effects of temperatures on the preparation of B-C-N nanotubes, and finally the formation mechanisms of nanotubes."

Jan 1, 2000

By Cheng Pan, Qiugang Yuan, Xuewei Lv, Mei Liu, Enguang Guo

Land-based nickel resources include nickel sulfide and nickel laterite. With the consumption of high grade nickel sulfide, use of nickel laterite has received more and more attention. The mineralogy and sintering behavior of limonitic nickel laterite with high iron and low nickel and silica was studied to offer technical support for producing ferronickel through sintering–blast furnace route. The mineralogy results showed that the main phases in this kind of nickel laterite are goethite (FeO(OH)), gibbsite (Al(OH)3) and NiFe2O4. The TGA (Thermogravimetric Analysis) and DSC (Differential Scanning Calorimetry) revealed hydroxide minerals in addition to absorbed water. After the sintering experiments the chemical composition, phases present (XRD analysis) and physical properties of the sinter were studied. The content of FeO in the sinter increased with increasing basicity up to 1.3, and then decreased with further increase in basicity. The yield of sinter increased (from 73% to 80%) with increase in the basicity from 1.1 to 1.7, and then the yield decreased with the further increase in basicity. Mg(Ni)(Fe,Al)2O4 is the main phase in the sinter while MgCaSiO4 and Fe2SiO4 is the main binder phase when the basicity is 1.1~1.5, and MgCaSiO4, Fe2SiO4 and SFCA is the main binder phase when the basicity is 1.7~2.1.

Jan 1, 2014

By Nobuaki Sato

The electrical conductivity, k, of pure and sodium doped sulfur melts was measured with and without ultrasonic waves at temperatures ranging from 140 to 340'C by the two probe method using an ultra high resistance meter. The k value of the pure sulfur melt with irradiation jumped at around 170°C by an order of 102 after which it mouutuniocally increased from 10-5 to10-4 A' 1 cm-1 with an increase of the temperature. The addition of the sodium metal to the sulfur melt was found to cause a larger jumping in the K value. The k value increased with the increase of Na proportion in the melt. For a 10mol% Na doped sulfur melt it was as high as max ~30 A 1cm -1 above 180 C under the irradiation of of ultrasconics.

Jan 1, 2003

By Jilai Xue, Jun Zhu, GermainKouma Ndong, Luxing Feng

High-temperature corrosion behaviors of Fe-Ni-Cr alloy as inert anodes for aluminum electrolysis have been studied. The effect of anodic overpotential on layer growth of anodic surface is specially considered. The corrosion layers on the anodes tested were analyzed using XRD and SEM-EDS to provide a fundamental understanding of the layers growth at metallic anode surface. The dissolution of the scale layers on the metal anode occurred with low overpotential, while AlxM3-xO4 spinel phase within the scale layers was found with an increased overpotential. A mixture of multiple MyO layers existed on the anode substrate. The results may be useful for understanding and controlling the corrosion behaviors of Fe-Ni-Cr anode for potential application in aluminum electrolysis.

Jan 1, 2015

By Qian Xu, Xionggang Lu, Xingli Zou, Zhongfu Zhou, Shuhua Geng, Hongwei Cheng

Herein we report an electrochemical route from oxides (SiO2, TiO2)/sulfide (MoS2)/carbon mixture precursors to Mo-Si-Ti-C composites in molten salt. The electrochemical process was carried out in molten CaCl2 at 800 °C with a potential of 3.1 V, and a graphite-based anode was used in the electroreduction process. The reaction mechanism and the influences of the stoichiometry of the initial mixture precursor on the morphology and phase composition of the final products were investigated. It has been found that Mo5Si3/MoSi2/Mo3Si/Mo, Mo5Si3/MoSi2/Mo2C/SiC, and Mo5Si3/Mo2C/Ti3SiC2/TiC/Mo composites can be electrosynthesized directly from their oxides/sulfide/carbon mixture. The preliminary experimental results suggest that the electroreduction process can be used for the controllable electrolytic production of alloys/carbide-containing composites from oxides/sulfides/carbon precursors.

Jan 1, 2016

By J. McKelliget, J. Szekely, Oreper. G. M.

"1. INTRODUCTIONThis paper is concerned with heat and fluid flow phenomena in arc welding operations. Fig. 1 shows a schematic sketch of a typical arc welding arrangement. It is seen that an arc is being struck between an inert electrode and a metal surface and that the resultant current and energy flow will case the formation of a molten weldpool.It is clearly appreciated that the weldpool shape and the nature of circulation in the weldpool may play an important part in determining the ultimate weld quality. It is known, furthermore,· that the weldpool behavior in turn will be affected by the spatial distribution of the current and the heat flux it receives from the arc. Indeed, the inherent coupling between the arc and the weldpool is a key feature of welding operations.Up to the present useful work has been done on the modelling of heat transfer and melt circulation in weldpools (1,2,3,4) and also on the description of arcs, including welding arcs (5,6,7,8). However, the coupling between these two sets of phenomena is relatively unexplored in a qualitative sense. The purpose of the present paper is to examine the interaction between welding arcs and weldpools. The actual material will be presented under the following headings:"

Jan 1, 1986

By Manjie Li, Mingrui Yang, Haijun Peng, Shuxing Qiu, Wei Liu, Shengfu Zhang

It is important to produce and utilize highly reactive coke in order to reduce the energy consumption and CO2 emissions through improving shaft efficiency in blast furnace. The present study aimed to investigate the transformation of iron minerals and properties of iron coke (the coke mixed iron ore fines). Along with the increase of iron ore fines, cold strength displayed a slight downtrend and the pore structure wasn’t inferred to be a major factor affected the properties of iron coke. During carbonization, the majority of mixed iron oxides were reduced to metallic iron by CO and H2 and the degree of metallization achieved to approximately 75%. Nevertheless, produced metallic iron was oxidized by pure CO2 during gasification. Iron coke reactivity index (ICRI) was obviously enhanced and the iron coke strength after reaction (ICSR) drastically decreases, which were also significantly influenced by crystal structure of carbon.

Jan 1, 2015

By P. Chris Pistorius

An example is presented to illustrate the joint effect of local reaction equilibria and mass transfer limitations, for reactions during ladle refining of steel. The example relies on some of the kinetic principles that David Robertson has employed to quantify many metallurgical processes. In calcium treatment of alumina inclusions in aluminum-killed steels, solid CaS forms as an intermediate reaction product. During subsequent reaction, CaS disappears and calcium aluminate forms; at the same time, aluminum and sulfur dissolve in the steel. Kinetic analysis shows that the rate of this reaction is not limited by mass transfer of dissolved aluminum and sulfur away from the reacting inclusions. The reaction rate is likely limited by transport of dissolved calcium. This example also illustrates the use of FactSage macros for kinetic modeling.

Jan 1, 2014

By B. I. Hop

The f10wfield set up by the standard Hydro gas purging unit has been predicted by a numerical model. In addition turbulent trajectories of gas bubbles released from the rotor are predicted. Here the deposition rate of inclusions on the bubble surface is allowed to depend on local conditions. Bubbles passing regions with strong pressure gradients, such as close to the rotor, will experience large slip velocities and large deposition rates. This model can deal with any distribution of bubble sizes and inclusions. The results found from the multidimensional flow predictions are discussed in relation to what can be obtained from a much simpler metallurgical engineering approach. The differences between these two approaches to predict the same process will be discussed. The model predictions are compared to experimental results for removal of SiC-particles from aluminium.

Jan 1, 1996

By Rollie E. Dutton, David A. Stubbs

"A sensor has been developed and tested that is capable of emitting and receiving ultrasonic energy at temperatures exceeding 900°C and pressures above 150 MPa. The sensor works with standard ultrasonic pulser-receivers and has demonstrated the capability of measuring workpiece deformation during hot isostatic pressing (HIP). Details of the sensor design, performance, and coupling of the ultrasound to the workpiece are described. Ultrasonic data acquired by the sensor, in situ, during HIP runs and at elevated temperatures in air are presented.INTRODUCTIONHigh temperature structural components, such as structural castings for jet engines, nickel-base superalloy turbine blades, and ceramic and metal matrix composites made from powders are often densified by hot isostatic pressing (HIP). For powder consolidification, the HIP process involves sealing the powder (and reinforcing fibers for composites) within an evacuated ""Can"" made of a material that softens at high temperatures. A hydrostatic pressure is then applied by pressurizing the inside of the HIP vessel with argon gas (up to 140 MPa). The hydrostatic pressure densities the powder through the elimination of the porosity between the powder particles.This paper presents details of the development and preliminary testing of an ultrasonic displacement sensor that can be used to monitor materials processing, in situ, at temperatures and pressures significantly higher than current ultrasonic displacement sensors. The target processing environment for this sensor is that typically found in a hot isostatic pressure (HIP) vessel, i.e., temperatures exceeding 1000°C and pressures above 138 MP a."

Jan 1, 1997

By Patrick R. Taylor

Coatings of TiCIFe have been produced by Reactive Plasma Spraying using ilmenite ore concentrate as the feedstock powder and methane as the reactive gas. A free energy minimization analysis of the ilmenite-methane system is presented. The coatings have been characterized by x-ray diffraction and SEM. The microstructure of the coatings indicates good interparticle cohesion. The composition of the coating is deficient in iron compared to the initial Fe to Ti ratio found in ilmenite.

Jan 1, 1998

By A. Kontopoulos

The extraction of nickel and cobalt from low-grade greek laterites by sulfuric acid leaching has been studied. Batch and continuous mini-plant atmospheric leaching as well as pressure leaching techniques were employed. Atmospheric leaching at temperatures as high as 95 OC generally resulted in low Ni extractions (up to 82%), high acid consumption (650-850 kg/t ore or 80-100 kg/kg Ni) and high Fe co-dissolution (30%). Pressure leaching at 260 OC increased Ni extraction to over 98%, with minimal Fe co-dissolution (2.5%); acid consumption was 300 kg/t ore (31 kg/kg Ni). Detailed experimental results and conceptual flow sheets for atmospheric and pressure leaching are presented.

Jan 1, 1991

By Kuo En Chang

Many rare earth - transition metal (RE-TM) compounds absorb/desorb hydrogen reversibly at room temperature and atmospheric pressure. For LaNi5 which is used as a battery material, the electrochemical nature of this process is well known. In the case of Nd-Fe-B which has found wide application as a powerful permanent magnet, the absorption of hydrogen has both significant advantages and disadvantages. However, a fundamental understanding of the hydrogenation process at ambient temperatures and its effect on subsequent corrosion behavior is currently lacking. This paper reports the results of the hydrogenation of NdFeB two alloys, (NdDy)15Fe78.3A10.7B6 and (NdDy)15Fe67Co5V4A12B7, which are compared with that of LaNi5. Results show that hydrogenation can be accomplished by either electrochemical methods or immersion in dilute sulfuric acid. For the latter method, the change in lattice parameter indicates that the level of hydrogen absorbed by the NdFeB particles corresponds fairly closely to an overall composition of Nd2Fe14BH2.7. Cyclic electrochemical charge/discharge experiments show that the maximum hydrogen discharge capacities of the NdFeB, NdFeB-Co-V, and LaNi5 are 40, 60, and 210 mA?h?g-1, respectively. Anodic potentiodynamic polarization measurements and calculated values of icon reveal that absorbed hydrogen in NdFeB-Co-V and the NdFeB may lead to significant increases in corrosion rates.

Jan 1, 1995

By P. D. Lee

The effect of strontium on porosity formation in aluminum-silicon alloys is not well understood and there is no consensus upon the cause of the effects observed. This paper describes a series of experiments where the effect of adding strontium on pore formation was observed directly with combination of a traditional temperature gradient stage and real time micro-focus radiography. These in situ observations provide a new insight into the effect of strontium on the nucleation and growth kinetics of porosity. The addition of strontium was found to have a minor effect on the growth of the pores in the mushy zone. However, strontium appeared to alter the nucleation and stability of hydrogen bubbles within the melt. The interaction of strontium with titanium-boride grain refiners produced an even stronger change in the nucleation and stability of the bubbles formed.

Jan 1, 2002

By A. Deepatana

Bioleaching of nickel laterite ores is based on the use of heterotrophic fungi organisms and their metabolites (organic acids) to dissolve nickel and cobalt from oxide minerals to form metal-organic complexes. Metal recovery from this process using an aminophosphonic acid based chelating resin (Purolite S950) was investigated as a function of metal concentrations, complexing agent including citric, dL-malic and lactic acids. Batch adsorptions were conducted using synthetic leachate solutions of nickel and cobalt with concentrations from 15 to 2000 mg/L prepared in 0.01 and 0.1 M organic acids. Adsorption equilibrium data were interpreted using the Langmuir, Freundlich and Dubinin-Kagner-Radushkevich (DKR) models. The results showed that equilibrium adsorption data for nickel-organic complexes followed the Freundlich model and those for cobalt agreed with the Langmuir model. It was observed that the maximum adsorption capacities of nickel and cobalt were 3.26 and 10.48 mg/g resins respectively. These were achieved in metal complexes prepared from 0.01 M lactic acid. Metal elution was conducted using 2 M nitric acid. High metal recoveries were achieved from low metal concentrations but were found to decrease with increasing metal concentration. The results suggest that effective recovery of nickel and cobalt from low concentration of metals, such as those generated from bioleaching operations, can be achieved suitably using chelating resins.

Jan 1, 2006

By Gang Qi

The solubility of nitrogen in pure molybdenum was measured over the temperature range 2173 to 2473 K and up to one atmosphere (101 kPa) of nitrogen gas pressure. Both thermochemical and kinetic aspects of this phenomenon were considered in this study. The solution of nitrogen in molybdenum may be expressed by the reaction 1/2N2(g) = {N} (Mo,s), for which the standard Gibbs energy is given by the expression {A}G° = 78,500 + 27.36T Joules/g atom N. The formation of molybdenum nitrides, specifically Mo2N, was considered. Attention was also focused on the mechanism of nitrogen solution in molybdenum. Estimates of the diffusivity of nitrogen atoms in solid molybdenum were derived from the kinetic data.

Jan 1, 1991