By D. M. Dabbs

A static dew point technique has been used to evaluate the solubility of arsenic in ?slag and its dependency on P02 at temperatures of 1458 and 1523K. The ferrous-ferric ion ratio of the slags ranged from 3.9 to 23.8. These values correspond to partial pressures of 02 ranging from 10-8 to 10-12 atm. The solubility of arsenic in slag was found to be independent of? P02? The data indicate that elemental arsenic exists in silicate ?slags. This result was further substantiated by mass .spectrometric analysis of doped slag specimens.

Jan 1, 1983

By Murat Baydogan

Effect of retrogression and reaging treatment on hardness and stress corrosion cracking resistance of 7075 aluminum alloy was investigated. As received 7075 alloys in T6 temper condition were retrogressed at 170, 220, 240 and 380°C for different durations between 15 s and 60 min. Subsequent reaging was made at the T6 aging condition. Treated materials exhibited higher hardness and better stress corrosion cracking resistance than T6 temper in a wide range of retrogression temperature and time. The highest hardness was obtained after retrogression at 170°C for 210 s followed by reaging, corresponding to 20% hardness improvement. Improvement in stress corrosion cracking resistance of the alloy by as much as 85% was also observed. In this paper, improvements in hardness and stress corrosion cracking resistance are discussed on the basis of the microstructural changes during retrogression and reaging treatment.

Jan 1, 2006

By Joseph C. Milbourne

Tetra Technologies CCIX? (continuous countercurrent ion exchange) system has been involved in a wide range of uranium concentration, separation and purification applications over the past 40 years. Uranium ion exchange applications have ranged from the treatment of copper heap leach solution containing 5 parts per million of uranium to the treatment of high strength sulfuric acid solutions containing several thousand parts per million of uranium. The flexibility and the countercurrent mode of operation and other unique features of the CCIX? have resulted in successful uranium recovery from these solutions and many others.

Jan 1, 1995

By Tseng. B. H.

Samples of unchlorinated and chlorinated carbonaceous concentrate from a carbonaceous gold ore were analyzed by transmission electron microscopy (TEM) for organically bonded sulfur and chlorine. The concentrate assayed 1.53 oz/t gold and 6.01% organic carbon. Much of the organic carbon occurred as sizable coarse particles up to several hundred microns in size, which showed no visible evidence of reaction with chlorine after chlorination treatment. Both the untreated and chlorinated fractions of the carbonaceous concentrate were analyzed by the TEM method, which detected organically bonded sulfur in all of the carbon particles examined in the untreated sample, ranging from about 1 to 5% organic sulfur, and averaging near 3.1%. TEM analysis of 40 carbon particles in the chlorinated sample indicated that organic sulfur was reduced significantly in the carbon and replaced in part by the chlorine, as the result of chlorination.

Jan 1, 1987

By Jillian Spindura

This work investigates the carbothermic reduction of the complex sulphide mineral, pentlandite, in the presence of lime. The effects of change in temperature and the use of different carbon sources are studied and the role of these variables on the reducibility of pentlandite mineral is discussed. The microstructures of the heat-treated pellets are examined using X-ray diffraction and scanning electron microscopic techniques. The latter analytical method also allows any variation in the morphology and composition of the metallic phases formed, with temperature, to be considered. The kinetics of the reduction process is studied and the magnitude of the overall activation energy is determined from the plots of percentage reduction versus time.

Jan 1, 1996

By Chuanhong Li, Zuohua Lin, Zhancheng Guo

"Catalytic mechanism of CeO2 in combustion of coals was investigated in this paper. Catalytic combustion of four kinds of coals with different metamorphic grades by CeO2 was examined, suggesting that catalytic function of CeO2 increases with increase of metamorphic grade of the coals. One important reason for CeO2 promoting combustion of the coals is that pyrolysis of anthracite is advanced by CeO2, which not only raises the pyrolysis rate and pyrolysis conversion ratio, but increases contents of light components in pyrolysis gas; and both pore space and specific surface area of the pyrolysis char are enlarged by CeO2, which is another reason. In order to realize in situ catalysis for reducing catalyst consumption, it is crucial to increase catalyst particle number and enhance the bonding force between catalyst and coal. In addition, remarkable energy saving effect was observed when a nanometer calcium-based rare earth catalyst obtained by hydro-thermal synthesis was applied to catalytic combustion of coal injection into blast furnace.Introduction Coal combustion is acknowledged as one of the most important coal applications. Since addition of catalysts could reduce the ignition temperature of pulverized coal and accelerate the coal combustion, catalytic combustion is generally accepted as an effective measure to realize fast combustion of coal. Furthermore, different catalysts added may produce different effects on ignition temperature of coal. It is reported activity of catalysts with the same cation follows this order: OH->CO3 2->Cl->SO4 2-; while that of the catalysts which have the same anion follows: Cs+>Rb+>K+>Na+>Ba2+>Li+>Sr2+>Ca2+>Mg2+>Be2+ [1-4] .Due to the special physical and chemical structure, CeO2 plays an important role in the catalysis field. Many literatures point out that CeO2 not only has great catalytic effect on energy conversion, succeeded in catalyzing combustion of gaseous fuels such as CH4, CO, etc. but also can catalyze combustion of some liquid and solid fuels such as JP-10, black carbon, carbon deposit in the automobile exhausts and so on [5-9].Pyrolysis, the first step of combustion, directly influences ignition temperature and combustion rate of coals. So a great variety of catalysts were applied to catalyze pyrolysis of coals. And plenty of studies suggest that the alkali and alkaline-earth metal compounds inherent in the coals show apparent catalytic effect on coal pyrolysis. Meanwhile, addition of alkali and alkaline-earth metals into coal combustion process also indicates obvious catalysis effect, accelerating coal pyrolysis, improving pyrolysis conversion ratio, increasing contents of pyrolysis gases and changing composition of the pyrolysis gases [10-15].Although alkali and alkaline-earth metal compounds have good catalysis effect on coal combustion, their application in the catalysis field was limited because of their erosive attack to the combustion equipments. In contrast, CeO2, as a substitution of the traditional coal catalysts, presents widely potential application due to its good catalysis ability, non-corrosive and nontoxic. However, investigation on CeO2 catalyzing coal combustion is rarely reported. In this work, catalytic mechanism of CeO2 in coal combustion was studied, in an attempt to provide theoretical foundation for developing new catalysis technologies."

Jan 1, 2009

By I. Gaballah

Decontamination of synthetic solutions of copper acetate, chloride, nitrate and sulfate containing 10, 100 and 1000 ppm of copper, using chemically treated barks has been studied. Metal percent removal from solutions depends on the pH and the initial concentration and to some extent on the salt used. It varies from 40 to 99 % of the solution initial metallic ion's content. The maximum retention capacity of the treated bark varies from 31 to 43 mg of Cu per gram of dry modified bark. Bark loaded with copper had been analysed by Scanning Electron Microscopy and lnfra Red spectroscopy. Cu is uniformally distributed in the bulk of the bark. No copper segregation is observed. It seems that copper is bound to the acidic sites of the bark. Anions are not detected on the copper loaded bark neither with the SEM or with the IR spectroscopy.

Jan 1, 1993

By Satoshi Itoh

Phase equilibria and activities of the components in the liquid lead-antimony-oxygen temary system, which is of fundamental importance for discussing the recovery of lead and antimony from a used lead-battery, have been investigated at 1173 and 1223 K. The two liquid phases of metal and oxide were observed at the temperatures studied, and the tie lines indicating isoactivities were determined. The activities of PbO, Sb015 and Sb203 in the PbO-SbOu and PbO-Sb203 pseudo-binary systems were then obtained by applying the Gibbs-Duhem equation to the phase relation of metal-oxide equilibrium. Both in the pseudo-binary systems the activities exhibit negative deviations from Raoult's law. The vapor pressures of lead, antimony and lead oxide, antimony oxide were calculated by using the activities of the components in the lead-antimony-oxygen ternary system. As a result, an oxidation of antimony concentrated in an anode slime followed by evaporation as antimony oxide Sb406 was found to be considerably effective for the recovery of lead and antimony from a used lead-battery.

Jan 1, 2003

By Satoshi Itoh

Phase equilibria and activities of the components in the liquid lead-antimony-oxygen ternary system, which is of fundamental importance for discussing the' recovery of lead and antimony from a used lead-battery, have been investigated at 1173 and 1223 K. The two liquid phases of metal and oxide were observed at the temperatures studied, and the tie lines indicating isoactivities were determined. The activities of PbO, SbO1.5 and Sb2O3) in the PbO-SbO1.5 and PbO-Sb2O3 pseudo-binary systems were then obtained by applying the Gibbs-Duhem equation to the phase relation of metal-oxide equilibrium. Both in the pseudo-binary systems the activities exhibit negative deviations from Raoult's law. The vapor pressures of lead, antimony and lead oxide, antimony oxide were calculated by using the activities of the components in the lead-antimony-oxygen ternary system. As a result, an oxidation of antimony concentrated in an anode slime followed by evaporation as antimony oxide Sb406 was found to be considerably effective for the recovery of lead and antimony from a used lead-battery.

Jan 1, 2003

By I. S. Blair

The introduction of the 36 MVA smelting furnace at Mufulira, and the experience gained during the first five years of operation have been described previously (6). Based on this experience the furnace was rebuilt in 1977., Details of the modifications made during this rebuild are described. Subsequent to the rebuild, refractory failures, particularly in the electrode ring bricks of the sprung arch roof, continued to cause concern, and repair and improved roof control methods are described. Electrode breakages continued, but developments in casing design and electrode preparation have resulted in significant improvements. Modifications in the electric furnace gas handling system are outlined, together with details of further changes to be implemented in the near future. The systems developed for metallurgical control of the furnace and the thermo-dynamics of the process are discussed. The electric furnace at Mufulira is now operating at above design production levels, and has decisively justified the choice of this technology in situations with inexpensive electric power. The potential for further increases in production capacity from the Mufulira unit, and improvements in design for new units are discussed.

Jan 1, 1983

By Xiaobing Yang, Animesh Jha, Greg Doughty

"Successful use of inert anodes should reduce the CO2 footprint in aluminum production. The search for a “holy grail” inert anode for metal electro-winning from constituent oxides using molten salt bath as an electrolytic medium is continuing. In this article we demonstrate the engineering approaches for the fabrication of intermetallic anodes, based on a quaternary Al-Ti-Cu-M (M:Ni, Fe) system for primary aluminium production. In particular, we examine the microstructural and electrochemical properties of alloys, based on the quaternary compositions. We explain the aspects of phase stability under anodic potential, which leads to the loss of anodic materials in the temperature range of 850-1050oC. The results are analysed in the context of oxidation reaction and formation of oxide layers which readily dissolve in the cryolite melt and prevent passivation. The paper also describes the conditions under which the reduction of aluminium at the graphite cathode occurs which also strongly depends on the molten salt chemistry for the nucleation of molten aluminium at the cathode.1. IntroductionOxygen-evolving inert anodes are an alternative to the conventional consumable carbon anodes for the production of primary aluminium. In this paper the materials selection criteria chosen for the engineering of anode is based on the understanding of the thermodynamic stabilities of aluminide intermetallic phases, some of which are formed and remained stable in fluoride melts. For example, the formation Al3Ti dispersed in aluminium metal via molten-fluoride flux reaction is well known in the context of aluminium casting and grain refining [1-3]. It is for this reason in our research we concentrated on the engineering of stable intermetallic phase mixture in the Al-Ti-Cu ternary system, shown in Figure 1 [4]. In this figure two compositions in the Al3-0.5zTi1-0.5zCuz family are shown with the substitution of 7 atomic % and 11 atomic % copper. However initial investigations showed that these two compositions were unsuitable due to the formation of low-temperature liquid (~540oC) and intermetallic phase, Al2Cu along the Al-Cu binary edge during solidification. The Al2Cu phase segregated along the boundaries of Al3Ti and Al5Ti2Cu, and dissolved away when electrolysis was carried out using these anodes above 800oC. The presence of consequential porosity in the anode material increased the corrosion of the alloy through local heating due to high current density at 0.8 A cm-2. The early tests were carried out with cryolite melts, shown in Figure 2, having 3 weight percent of Al2O3 in the bath at 850oC."

Jan 1, 2010

By Esher Hsu

In Taiwan, around 8,000 tons of batteries are consumed per year but only 17% of which were collected and transported to oversea for recovery. The dumping used batteries have become a potential environment problem. How to increase the collection efficiency of used batteries is an important issue for EPA in Taiwan. Besides, some treatment plants are on process to get permission for recovering used batteries. The objective of this study is to estimate the recycling cost of spent consumer battery and explore the feasibility of recovering used consumer batteries in Taiwan based upon the principle of cost-efficiency. The recycling cost including collection cost and recovery is estimated based on a survey. Results would provide some suggestions to Taiwan EPA regarding feasibility of recovering used batteries in Taiwan.

Jan 1, 2006

By R. Hurman Eric

The flow of molten slag and matte and the estimation of the mass of settled matte in electric furnaces is discussed and the action of the electric furnace as a settler is considered. Particle size of the concentrate and its grade are major contributors to settler dimensions. Discussion on the production capacity of the electric furnace with reference to operating current, power input, furnace dimensions such as width and length and electrode diameter are given. These discussions are based on considerations derived mainly from experimentally determined properties of the slag such as its resistivity, viscosity and liquidus temperature. Extension of the design and operating considerations to circular furnace symmetry is also discussed.

Jan 1, 1995

By Xiaowen Liu

The thermal decomposition of diaspore was investigated by thermogravimetry (TG),differential scanning calorimetry (DSC), X-ray power diffraction(XRD),infrared (IR)spectrain this paper. The thermal decomposition mechanism of diaspore was discussed according to Coat-Redfer equation. It was found that the decomposition of diaspore was carried out at 500?,and the peak temperature was 530?. The electrovalent balance of diaspore was destroyed. The previous crystal structure was changed. a- Al2O3 was obtained after thermal decomposition. The activation energy is 287KJ/mol.

Jan 1, 2006

By Tiebao Yang

In high pressure die casting processes, a die plays a critical role in removing heat from the molten metal during the cavity filling and solidification stages. Proper control of die temperature is essential for producing superior quality components and yielding high production rates. This paper proposes a local temperature control scheme for die thermal management based on a computerized intelligent real-time monitoring and control system (IRMCS). In this scheme, cooling water lines are controlled by a pump and solenoid valves. A controller is designed according to the law of die temperature fluctuations. The results obtained from the experiments carried out on a laboratory die casting process simulator indicate that the controller can limit the local die insert temperatures in a given band. Hence, the desired thermal pattern of the die insert becomes achievable.

Jan 1, 2006

By Michael P. Sudbury

Non-ferrous slags are granulated and stockpiled as an alternative to pit cooling or transporting molten slag to a dump. The chemical composition of such slag is determined by the pyrometallurgical process in which it is produced, while the size distribution is set by safety concerns or a desire to reduce wear of pumps, pipelines and other equipment. Relatively few operations give consideration to the effect of granulation conditions on other properties of the granulate as the material is typically accumulated on the smelter site. It is becoming recognized that slag has many potential commercial uses and carries much of the energy applied to the smelting operation. This paper outlines the findings of extensive work to identify uses for granulated non-ferrous slag, the importance of preparation conditions on the properties, impediments to more extensive use of granulated slag, the real costs of slag stockpiling and the opportunities for further productive research.

Jan 1, 2006

By Vijaya Thangavelu

Biological leaching of low-grade nickel laterite is based on a non-traditional leaching of oxide minerals using heterotrophic micro-organisms. The organisms solubilise metals by excreting organic acids; these acids then form complexes with heavy metals. High salinity of water supplies and soils in the vicinity of nickel laterite ore bodies is a major abiotic stress to fungi and represents a major challenge in the application of bioleaching process in-situ. Salinity exposes fungi cells to Na+ toxicity and osmotic stress. This study examined the salt tolerance development of Aspergillus foetidus based on gradual acclimatization of organism, its salt threshold and the salinity effect on its metabolism. The biological leaching of weathered saprolite ore with the resulting halotolerant organism under saline conditions was assessed. It was observed that salinity stress affected the organism?s growth and energy utilization

Jan 1, 2006

By Aert Driessen

Australia has large resources of rare earths -- 4.35 Mt of contained rare-earth oxides (REO) in the demonstrated category and 1.69 Kt in the inferred category. Australia's demonstrated REO resources are contained in about equal proportions in placer deposits, which also host Australia's titanium and zircon resources, and in hard-rock deposits. The largest single deposit of rare earths, at Mount Weld in Western Australia, is contained in regolith overlying a carbonatite pipe. It has a demonstrated resource of 1.73 Mt of contained REO and yttrium oxide. The largest demonstrated resources of REOs in placer deposits are in the Murray Bash, southeastern Australia -- a total of 1.90 Mt of contained RE0 in six deposits. However, the REO-bearing minerals (monazite and xenotime) are of secondary importance and their recovery will be determined by the market for titanium dioxide and zircon. The Murray Basin and other pre-Pleistocene basins offer the greatest potential for discovering more REO resources. Australia produces about 7000 t/year of REO in monazite and xenotime nearly all from Western Australia, as by-product of mineral-sand mining; monazite production is about 12 000 t/year (6600 t REO) and intermittent xenotime production is about 50 t/year (25 t REO). About 8000 t/year of monazite containing about 4400 t REO is not recovered separately, or is lost in tailings, as is an unknown but smaller amount of xenotime.

Jan 1, 1992

By T. T. Nguyen, D. R. Gunasegaram, D. Celentano

"Heat transfer rates at the casting-mold interface are believed to be substantially reduced by the formation of an interfacial gap during the course of solidification of aluminum alloys in permanent molds. In the current work, the effect of force-cooling a permanent composite mold on (i) the initiation and growth characteristics of the gap and (ii) interfacial heat transfer rates are studied. Interesting comparisons are made with the case where no cooling is employed. Casting and mold displacements are measured using L VDTs, and the mold is force-cooled by air jets.IntroductionIn a gravity casting situation where an aluminum alloy solidifies in a permanent mold, a gap initiates and grows between the shrinking casting and the expanding mold (1). It is widely believed that the formation of this gap, customarily referred to as an 'air gap', results in a substantial reduction in the heat transfer coefficient at the casting-mold interface (2), and hence is an important factor in solidification studies.The nature of the air gap formation process is thermo-mechanical. The rate of heat loss from the casting first determines the rate of solidification, which, in turn, decides when the gap initiates. The reason for this is the requirement for the solidified casting surface 'skin' to gain sufficient thickness, and hence strength, to be self-supporting. Once the gap initiates, the gap width controls the rate of heat loss from the casting, which, again, determines the rate at which the gap expands."

Jan 1, 1997

By F. E. Wagner, L. J. Cabri, Y. G. Safonov, N. S. Bortnikov, A. D. Genkin, J. Friedl, G. N. Gamyanin

"A multidisciplinary investigation (including INAA, SIMS, EPMA, and Mossbauer Spectroscopy) was used to characterize gold in four of the largest Siberian mesothermal sulfide gold deposits. These are the Olympiada (""'750 metric tons gold) and Veduga (estimated at 75-100 metric tons gold) deposits in the Enisei Mountain Range and the Nezhdaninskoye (z500 metric tons gold) and Sentachan deposits in the Verchoyansk-Kolyma area. It was found that some of the mineralization is refractory in all four deposits, largely due to the occurrence of ""invisible"" gold in arsenopyrite as well as within pyrite, but with a lesser concentration. The gold concentration and its distribution varies considerably both within and between arsenopyrite grains, with implications for processing options such as heap leaching. The ore most likely to be amenable to heap leaching is the oxidized ore of the #4 orebody of the Olympiada deposit, but further quantitative mineralogical investigations are recommended for this orebody's sulfide ore and for the ores of the Nezhdaninskoye deposit. Following a full mineralogical characterization, it is possible that economic viability will depend on a combination of pre-concentration with or without pre-treatment, followed by heap leaching of some tailings products.Acknowledgements· The Russian authors performed this study under an ""Eco res"" Project which was financially supported by the Ministry of Science and New Technology of the Russian Federation. C.J. Stanley wishes to thank John Spratt and Terry Williams for help with EPMA. F.E. Wagner acknowledges the Deutsche Forschungsgemeinschaft for a grant supporting the Mossbauer studies. L.J. Cabri is grateful to the following: M. Beaulne, D. Carson and J.H.G. Laflamme for technical support, K.E. Haque for technical comments, and D.M. Hausen and W. Petruk for editorial suggestions."

Jan 1, 1997