By Toshihiro Kuzuya

A hydro metallurgical process has been developed for the recovery of metal values such as Co, Ni and rare earths from the electrode materials of spent nickel metal-hydride(Ni-MH) secondary battery. MmNis_xCo. (Mm : Misch metal) intermetallic compound could be separated from the electrode materials mixture by sedimentation. A typical chemical composition of MmN5-xCox was approximately, in mass%, 56.0%Ni, 13.4%Ce, 10.6%La and 7.9%Co. The time dependency of leaching intermetallic compound with sulfuric acid solution was examined with processing factors such as sulfuric acid concentration, temperature and agitation intensity, The leaching of rare earth metals proceeded very rapidly, reaching completion in less than 1.8ks. On the other hand, the slow leaching of nickel was observed. The percent of nickel leached at 328K could only reach about 70%.

Jan 1, 2003

By Batric Pesic

Solvent extraction of nickel and cobalt from the real leach solutions was studied by using a novel extraction system. The extraction system was a mixture of 2,6-bis-[5-n-nonylpyrazol-3¬y]] pyridine (BNPP) and dinonylnaphthalene sulfonic acid (DNSSA). The BNPP represents a novel molecule, which was designed and synthesized in our laboratory. Real solutions for the study were prepared by leaching of two different cobalt-nickel bearing concentrates, cobaltite [CoAsS] concentrate from Blackbird Mine, Idaho, and siegenite [(Ni,Co)3S4] concentrate from Missouri Lead-Belt. The major strength of the system was the selectivity of extraction toward nickel and cobalt from iron containing solutions. Other metals such as Mn, Mg, Ca, Al and As were not extracted. Due to the irreversibility of copper extraction, its removal from solution was required prior to the extraction of nickel and cobalt. Zinc was not as strongly extracted (i.e. its stripping was readily achieved) as was copper . Flowsheets for the recovery of nickel and cobalt were also developed.

Jan 1, 1997

By M. C. Ruiz

This work outlines the results of leaching studies on a copper concentrate containing chalcocite (Cu2S) and digenite (Cu9S5) with an acid saline solution of cupric chloride oxygenated at ambient pressure. The variables studied included the stirring speed, concentration of cupric ions, concentration of HCI, concentration of chloride ions, oxygen flow rate, temperature and time. The leaching system was found to be very effective for the dissolution of the concentrate. Over 95% of the copper was dissolved in 30 minutes with negligible dissolution of iron. The dissolution of copper increased with the stirring speed up to about 400 rpm and depended little on the total chloride concentration. The oxygen flow rate affected the dissolution of copper only below 0.1 1/min. The concentration of HC1 did not influence the dissolution providing its was sufficient to avoid the precipitation of copper oxychloride. The study of the effect of the temperature showed a maximum in copper dissolution around 90 "C

Jan 1, 1997

By M. C. Ruiz

The leaching behavior of chalcopyrite concentrate in acidic CuC12-NaCI-O2 solutions was investigated. Experiments were conducted under continuos flow of oxygen at atmospheric pressures. The results indicated that among the variables temperature has the largest influence on the dissolution of chalcopyrite in this medium, and high copper extraction can only be obtained at temperatures near the boiling point of the solution. It was also found that the stirring speed did not influence appreciably the dissolution of chalcopyrite. An increase in the oxygen flow rate up to 0.1 1/min increased the copper extraction. The total chloride concentration affects the dissolution of chalcopyrite up to about 4 M. Copper extraction of 93 % was obtained in leaching chalcopyrite of size fraction -400 # Tyler at 105 OC in 2 hours.

Jan 1, 1997

By K. R. Robilliard

Ausmelt Technology has been developed to process copper concentrates containing significant levels of lead, arsenic and antimony. A process was developed aimed at smelting these concentrate materials to remove the contaminants to fume and produce a clean copper product. The production of clean copper and the potential economic benefits of this process step over the sale of impure concentrates is discussed.

Jan 1, 1995

By A. Lanterne, J. A. Bones, E. Øvrelid, Y. Hu, M. Di Sabatino, F. W. Thorsen

This study presents a new testing method to analyze the bubble content and distribution in quartz crucibles for monocrystalline silicon ingots. Two different types of silica (SiO2) crucibles have been investigated, before and after use during Czochralski (Cz) silicon ingot production for solar cells. Samples have been cut from three different positions along the crucible wall and then investigated by X-ray tomography, optical microscopy and scanning electron microscopy. The unused samples were heat-treated at 1400 °C for 4 h in Ar at 15 mbar. It is observed that the crucible bubbles grow in size and density during the Cz process. More bubbles are detected closer to the inner part of the crucible wall after use in the Cz process. The results also indicate that there are some differences in quality between different crucible producers and that bubble formation and growth are significantly affected by the Cz process parameters, such as temperature and time.

Mar 1, 2017

A strategy is presented for a relatively. "low-tech" means for decontamination of streams . containing .low concentrations of toxic metals. Metal ion solutions were . circulate through fluidized beds of activated carbon which support bio-films ?of bacteria .that naturally excrete exopolysaccharides. The attached 'biomass is shown to significantly enhance nickel, cadmium and silver extraction from dilute solutions (5- l00mg/l). By heat treating (at 300º C) the metal/biomass/carbon particles, bio-sorbed silver was subsequently fixed to the carbon surface. This approach to metal decontamination may therefore also provide a route for dispersing and fixing catalytic metal particles over an activated carbon surface.

Jan 1, 1991

By Isadora Dias Perez, Denise C. Romano Espinosa, Flávia P. Cianga Silvas, Jorge A. Soares Tenório, Mónica M. Jiménez Correa

In view of the rising generation of wastewater containing metals, sustainable and clean techniques to recover them are being researched. This study investigated the adsorption of aluminum, cobalt, chromium, copper, iron (III), magnesium, manganese, nickel and zinc presents in a synthetic ef fluent by chelating ion exchange resin Dowex XUS43605. The resin was tested in columns experiments and was analyzed the flow rate (0.45, 0.66 and 1.11 BV/h), at pH 1.5 and 20 °C. After loading the column, the elution experiments occurred with 1 M of H2SO4 and 4 M of NH4O. The concentration of the metals in solution was obtained by X-ray fluorescence spectrometry energy dispersive (EDX). The results showed that the breakthrough experimental curves demonstrated that the main metals (aluminum, cobalt, manganese and zinc) were immediately broken through just after the initiation of the feeding, while the breakthrough of copper began later. Therefore, the study showed that the chelating resin could be used to treat contaminated effluents with metals.

Mar 1, 2017

By Klas G. Hultbom

Mercury is present as trace contaminant in many raw materials for metallurgical plants. When such materials are treated with pyrometallurgical processes the mercury is volatilised. Mercury has a high vapour pressure, even at low temperatures, and therefore it is removed only partly by normal gas cleaning processes. The Boliden Norzink scrubbing process removes elemental mercury by converting it to calomel. It is widely used in the base metals industry. This paper gives examples of the application, and also outlines the background for the development of the process. Another technology developed by Boliden for mercury removal is the Selenium filter. This is a fixed bed filter based on the reaction between elemental gaseous mercury and selenium, by which mercury selenide, HgSe, is formed. The mercury selenide is a highly stable compound with extremely low solubility in water and very low vapour pressure. Mercury is removed selectively without any side reactions. Special applications for the selenium filter technology include mercury removal from gases containing sulphur dioxide and geothermal off-gases.

Jan 1, 2003

By R. Stefaniuk, T. Le, J-Y Huôt, H. Henein

"One of the most important process variables in gas atomization is the gas to metal (G/M) mass ratio as it has a direct effect on the mean particle size of the atomized powder. If this ratio can be controlled during the atomization process, the powder produced would be more uniform and the d50 more predictable. Thus, atomization using a tundish or gravity feed from a crucible would be more stable. In gas atomization, the gas flow rate can be easily monitored; while it is very difficult to determine the molten metal flow rate. This research paper presents a new method of recording the molten metal height with time using a conducting metal height detector. The metal height recorded in real time during atomization was used to characterize using a model the friction losses in the metal delivery system. It is found that the integrity of the metal delivery tube and the cleanliness of the melt play a key role in the maintaining a stable metal feed.IntroductionIn the gas atomization process, molten metal is normally fed to the system either continuously using a tundish or in most cases a certain amount of metal is melted in a crucible and flows into the atomizing chamber under gravity. In the first case, the metal flow rate is believed to be constant during the atomization process despite the presence of slag or dross on the molten metal surface. In the second case, the amount of molten metal is depleted with time and the rate at which the metal flow decreases with time varies from test to test in a seemingly unpredictable fashion.' Furthermore, most atomization systems are confined units and the metal level in the crucible cannot be detected by a visualization method. In industry as well as in laboratories, the metal flow rate is normally calculated on either the mass of input material or the mass of total production divided by the duration of the test. This figure is not accurate enough and obviously cannot be used as a control parameter for the gas to metal ratio as it is only determined after the completion of an atomization run. The need exists for a metal flow rate measurement and control methodology; thereby the d50 of the powder produced may be estimated and controlled in real time. Clearly, the smaller the variation of the G/M ratio during the atomization process the more uniform the powder produced and hence the size of the particles can be predicted."

Jan 1, 1994

By Shanlu Yang

In this study, laser-GTAW hybrid welding was used to the lap joint of galvanized dual-phase (DP) 980 steel in a gap-free configuration. The effects of welding parameters such as the laser power, the distance between the laser beam and the electrode torch, the arc current on the quality of hybrid welds were fully studied. The reason for the formation of different weld defects arises from the development of the highly-pressurized zinc vapor at the interface of two metal sheets. Experimental results demonstrated that the elongated molten pool introduced by the GTAW can suppress the formation of spatters to some extent. However, the hybrid laser-arc welding process still suffers from a large amount of spatters that degrade the weld quality. Furthermore, it was found that the weld quality was enhanced with the increase in the laser beam-arc distance and welding current.

Jan 1, 2009

By T. S. Bannos

Section 1417 of the Safe Drinking Water Act Amendments enacted by the O.S. Congress prohibits the use of lead containing solders for potable water systems in new construction or when making repairs. The legislature defines "lead-free" solder as containing less than 0.2% lead. In the development of a new solder it was recognized in addition to the lead free requirement, the alloy should perform as well as the popular 50/50 tin lead solder, both in application and properties. Another objective was to have only nontoxic elements. This led to the development of a 4.0% copper, 0.5% silver and 95.5% tin solder. Review of the merits of other alloy systems and the development of the physical properties along with test data are presented for the lead free tin. rich alloy.

Jan 1, 1990

By Chidchai Loyprasert, R. A. Stoehr

"A computer model has been developed to predict grain structures in alloys solidified under unidirectional flow using a combination of three techniques -- solution of the equations for flow of an incompressible fluid bounded by curved surfaces by the SOLA-SURF algorithm, calculation of heat flow by a finite difference method, and simulation of grain formation by a two-dimensional cellular automaton (CA) model. The changing rigid surface has been taken into account. Heterogeneous and homogeneous nucleation are considered, and the growth kinetics of a dendrite tip are evaluated by the Kurz-Giovanola-Trivedi (KGT) model. These calculations were applied to solidification of an Al-4.5% Cu alloy flowing over a chill on the bottom of a channel, a system for which experimental results were available. Using a variety of flow rates and superheats, agreement between the computed and experimental results were very good including transitions between columnar and equiaxed grains, the aspect ratio of the grains, and the inclination of the grains to the flow.IntroductionModeling of casting and solidification processes has developed over the years along two distinct tracks: (1.) modeling of macroscopic heat transfer and fluid flow for design purposes, and (2.) modeling of microscopic processes such as nucleation and growth in order to improve the scientific understanding of the phenomena involved. The present work is an attempt to combine the macroscopic and microscopic approaches for the solidification of an alloy flowing over a chill. The specific case chosen is that of an aluminum-4.5 % copper alloy flowing linearly over a water-cooled copper chill for which experimental results were available over a range of flow rates and superheats. For the macroscopic calculations, the SOLA-SURF algorithm for solution of the twodimensional fluid flow equations was combined with the finite difference method (FDM) for calculating heat transfer. For the microscopic calculations, heterogeneous and homogeneous nucleation were considered, and the growth kinetics at the dendrite tips were evaluated. The cellular automaton (CA) technique was used to apply the microscopic kinetics to the temperature and .flow conditions."

Jan 1, 1999

By Feng Wang, Guojing Shi, Yangyang Xie, Zizong Zhu, Qiang Wu

The coal chars from northwestern part of China are characterized with high reactivity and low strength after reaction. Four type of coke-making coals selected from northwestern part of China were studied by proximate analysis, ultimate analysis, vitrinite reflectance analysis, and FTIR with curve-fitting analysis to obtain information on their chemical composition and chemical structure. The results show that the studied coals have relatively high values of final contraction of coke residue index (x) and relatively low values of maximum thickness of plastic layer (y) and average vitrinite reflectance. Based on the curve-fitting analysis of FTIR spectra, the aliphatic carbon (Cal), the aromatic carbon (Car), and the molecular structural parameters such as CH2/CH3, fa, Hal/Har, and (R/C)u are determined. The results of curve-fitting analysis indicate that the studied coals are characterized by a large amount of oxygen-containing functional groups and aliphatic side chains.

Mar 1, 2018

By Waraporn Piyawit

Grinding sludge from the sintered neodymium-iron-boron (NdFeB) magnets production process was enriched with critical rare earth elements (neodymium, dysprosium and praseodymium), which can be up to 30% in the magnets. The demand of NdFeB magnets are simultaneously growing. Therefore, rare earths recovered from waste residue would reduce the demand of rare earth elements from primary sources. In this study, the feasibility of recycling rare earths through a hydrometallurgical process was investigated. The selective leaching of Nd from grinding sludge can successfully raise the rare earths concentration to 70%. The necessity of an oxidation pretreatment to improve the selectivity between Nd and Fe will be described.

By Jing Zhan, Gui Li, Wei-feng Li, Li-Hua Jiang, Chuan-fu Zhang, Jian-yang Hwang

Thermodynamics analysis for processing the charge with lead concentrate and lead sulfate-containing materials in bottom blowing smelting furnace was conducted. The results show that the technology of large-scale processing PbSO4- containing materials with PbS concentrate in bottom blowing furnace under the condition of using high-iron slag type, batch heat supplement, high temperature and rich oxygen is thermodynamically feasible. The exploration test and industrial experiment confirm the results. When S content in mixed ore is 16~17% with coke foam content of about 5%, the lead paste amount can be increased up to 40%.

Jan 1, 2015

By K. V. Sreenivas Rao

Solidification experiments have been conducted to study the effect of interface heat flux and air gap formation on cooling rate of the casting during solidification of Al-4.5wt%Cu alloy. The thermal history of the casting and mold during solidification is recorded using thermocouples connected to computer interfaced data logger. The measured temperatures in the mold are used as input to the IHCP (inverse heat conduction problem) algorithm for simulating multiple heat flux components at the boundary. It is observed that the filling effects induce spatial variation in the thermal field in the mold and casting regions and greatly influence the cooling rate of the casting. The study demonstrates the use of IHCP and in-situ measured thermal profile in analyzing the cooling rate and microstructure.

Jan 1, 2008

By Masayuki Kudoh, Kiyotaka Matsuura

"Molten aluminum and nickel cast onto a steel block exothermically react and produce molten nickel monoaluminide, NiAI, which is simultaneously joined to the steel. The heat of the exothermic reaction is transferred to the steel block, and steel near the surface of the block is melted. The depth of the melted steel increases with both the initial temperature of the steel block and the thickness of the produced NiAI. Iron from the melted steel dissolves in the molten NiAI, and an intermetallic compound of NiAI-Fe pseudo-binary system is produced. During solidification of the intermetallic compound, it is strongly joined to the steel. The Ni.Al-Fe intermetallic compound has an excellent resistance to oxidation and corrosion.IntroductionAn intermetallic compound of nickel monoaluminide, NiAl, offers many advantages over conventional superalloys, such as higher melting temperature, lower density, greater specific modulus and higher thermal conductivity [1]. NiAl also exhibits excellent high-temperature oxidation resistance when doped with zirconium or hafnium, and excellent high-temperature corrosion resistance when doped with chromium or yttrium, that are superior to existing high temperature alloys or coating materials [1-4]. On the other hand, NiAI is significantly brittle at temperatures below 600 K [5-7], which is the most sigriificant disadvantage of NiAI. A possible way to overcome the disadvantage and to utilize NiAl as an environmental-resisting high-temperature structural material may be joining of NiAl to a ductile material."

Jan 1, 2000

By Yun Guo, Min-Min Lin, Bing Xie, Hong-Yi Li

The extraction of vanadium from vanadium-containing APV-precipitated wastewater by W/O microemulsion system was studied. In the N263/n-heptane/isoamyl alcohol/NaCl microemulsion system, N263 played double functions of cationic surfactant and extractant to form microemulsion in n-heptane, and isoamyl alcohol was added in the microemulsion as a cosurfactant. The extraction of vanadium by W/O microemulsion systems effectively accelerated the extraction and improved the extractatability because of the enormous increase in the micro-interfacial surface area. Due to ion association with extractant, vanadium was extracted into the microemulsion phase. The influence of different parameters on the extraction ratio (E%) were investigated, including the volume ratio of aqueous phase to microemulsion, surfactant concentration, pH value of the feed solutions, cosurfactant concentration, extraction time as well as temperature. In optimum conditions, the extraction ratio (E%) can reach 97.2%.

Mar 1, 2018

By M. C. Furerstenau

Adsorption behavior of various surfactants on sulfide minerals is very much affected by the nature of the surface of the mineral. Since sulfides are naturally meta-stable, oxidation occurs when they are exposed to air, especially in aqueous environments. As a result. oxygen assumes a major role in sulfide flotation. Mechanisms of adsorption of various thiol collectors on sulfide minerals have been reviewed. The electrochemical behavior of various sulfide minerals has also been reviewed. Flotation behavior of galena, chalcocite, sphalerite, pyrite, chalcopyrite and pentlandite has been presented together with the. flotation of copper sulfide- nickel sulfide ore.

Jan 1, 1993