Keywords: Wasted catalyst, Hydrodesulfurization, Ammonium vanadate, Ammonium molyb-date, Hydrometallurgical process. The fundamental reactions have been investigated in order to develop a hydrometallurgical process for recovery of molybdenum and vanadium from wasted catalysts generated in the hy-drotreating desulfurization of heavy oil. The principal steps of the process are a mild oxidation roasting of the waste catalysts at temperature around 500°C, leaching of the target metal components with dilute ammoniacal aqueous leachates, selective precipitation of vanadic acid, and ammonium molybdate precipitation. The selective recovery of vanadium as vanadic acid is successfully performed using ammonium sulfate as a salting-out agent. Recovery of ammonium molybdate is based on large dependence of solubility of ammonium molybdate in ammoniacal solutions upon temperature and ammonium salt concentration. In this process, the solution after recovery of vanadium and molybdenum is recycled to the leaching stage of the roasted materials, and the ammonium salts in the process liquor is in the repeated use. Employment of am-moniacal system makes it possible to operate the roasting at much lower temperature than that for the currently operating process.

Jan 1, 2005

By Sylvie C. Bouffard

The need for a better understanding of the heap biooxidation pretreatment of pyritic refractory gold ores has prompted us to develop a rigorous mathematical model of the process. The hydrological structure of the model takes the form of lateral stagnant pores in contact with a uniformly distributed gas stream and connected to vertical plug flow channels, as suggested by the results of an independent study of column hydrology. A model of pyrite oxidation kinetics was derived based on electrochemical leaching theory and the results of potentiostatic stirred tank and column tests. The growth rates of attached and planktonic iron- and sulfur-oxidizing cells are modeled with separate Monod expressions over three separate temperature ranges corresponding to mesophiles, moderate thermophiles, and extreme thermophiles. Isothermal column tests validate the model simulations. Excellent fits of several leaching indicators (potential, extent of sulfide oxidation, iron concentration, cell numbers) reveal the rate-limiting step to shift from particle kinetics to oxygen gas/liquid mass transfer with increasing temperatures and pyrite head grades. Competition for oxygen between sulfur- and iron-oxidizing microorganisms lowers potentials and slows down pyrite oxidation. This modeling tool may assist engineers in the design and operation of heaps to give more complete gold liberation in a shorter time.

Jan 1, 2003

By Omid Lashkari

Keywords: SEED, SSM materials, Microstructural evolution, Rheology, Swirling Speed SEED (Swirled Enthalpy Equilibration Device) is established itself as a new technology amongst the many Semi-Solid Metal (SSM) processes, where swirling of the mush plays an important role in modifying the dendritic structure of as-cast parts. A range of semi solid metal structures, dendritic, rosette and/or globular morphology of primary phase, can be prepared using SEED. The current article reports on the application of rheological tests in characterizing microstructural evolution during SSM processing of 356 Al-Si foundry alloy. A simple parallel plate test machine, designed and constructed at our labs, was used to determine viscosity values for each structure and identify the optimum structure with superior die filling characteristics. Such findings have important technological and economical implications during high pressure die casting of semi- solid metals. The strain-time graphs for 356 Al-Si foundry alloy indicated lower viscosity values for globular microstructure, i.e. improved die filling.

Jan 1, 2005

By Mitsuhiro Ito

"To allow various wastes containing high levels of chlorine to be used as alternative raw materials for Portland cement, two practical methods of chlorine removal were developed. In the first method, chlorine is extracted from the wastes during the cement manufacturing process. In the second, ash-dust waste with high chlorine content is first washed and then dehydrated to cake before being introduced to the cement manufacturing process. This cake can be used as an alternative for some cement raw materials. By combining the two methods, various wastes previously considered unsuitable for recycling due to their chlorine content can often now be used in cement manufacturing plants. As such, these methods represent a major contribution to environmental protection as well as a solution to problems relating to the diffusion of heavy metals and dioxins from cement plants.1. IntroductionWaste generation levels have risen rapidly in recent years. in both the consumer and industrial sectors and today, the need for effective, efficient waste management is one of the most pressing and serious problem of today's society.The Japanese cement industry has reacted to the increase in waste generation by using certain materials as alternative raw inputs or fuels for cement production, in an effort to contribute to society and conserve energy resources.These wastes often contain non-negligible levels of chlorine and heavy metals, however, both of which are unsuitable for cement production. Depending on the element content, Heavy metals have a particularly negative effect -on cement quality; in addition, they can be released into the environment. Chlorine, on the other hand, is contained in large amounts in incinerated ash from household wastes as well as in certain plastics. Both substances are considered impediments in cement-production, not only because they reduce the quality of the cement produced but also because they impair operating safety on cement production lines.To address this problem, two practical technologies have been established for separation and recovery of chlorine components during cement pre-processing and production. This paper introduces the application of these technologies with a special focus on incinerated ash from urban wastes, a representative form of waste material having notably high concentrations of chlorine, heavy metals, and dioxins. We also outline the technologies enabling this material to be used as an alternative input to cement production."

Jan 1, 2000

By Hideki Yamamoto, Shigeno Matsumoto, Junji Shibata

"Some fundamental studies were carried out in order to produce composite powders comprising of two or three metal oxides ~y using liquid-liquid extraction and to develop the control technology of the particle size. The combination of samarium and cobalt was selected as the two component composite powders. Both stripping and crystallization occurred at the same time by emulsifying the organic phase loading the two metals extracted with Versatic Acid 10 and the aqueous solution containing oxalic acid. The effect of aqueous pH, oxalic acid concentration and agitation speed was examined on some properties such as crystallization percent, particle size and shape of each metal oxide powders obtained in this process. The analysis by using EDX showed that the two metal oxides were distributed uniformly.IntroductionComposite metal and metal oxide powders with high purity are indispensable as industrial materials in the fields of electrical engineering, electronics and metallurgy. It is difficult to mix metal powders or metal oxide powders uniformly for the production of alloy powders. If insoluble metal salts are allowed to collect as crystallization products in the crystallization-stripping process, the conventional melting and crushing process can be avoided. After mixing of the organic phase containing metals in fixed composition, fine metal and metal oxide powders of alloy composition are produced by using a crystallization-stripping method. Versatic Acid 10 and D2EHPA, both acidic extractants, were chosen in this experiment, and the metal oxide powders were produced by using oxalic acid as a crystallization reagent. Mixed metal oxalates containing samarium and cobalt were precipitated from the mixed organic phase containing these metals. Furthermore, the physical properties of the powders, such as particle size, shape and thermal decomposition, were measured in order to evaluate them for industrial purposes."

Jan 1, 2000

By Artur Camposo, Rômulo. L. Loiola, Frederico M. Margem

"The growing interest for natural materials as an environmentally friendly alternative for the substitution of energy intensive and non-sustainable synthetic materials, has motivated the use of lignocellulosic fibers as reinforcement of biocomposites. The sisal fiber, a relatively unknown lignocellulosic fiber with potential for composite reinforcement, still needs to characterize for possible engineer applications. Therefore, the present work analyzed the sisal fiber by means of Fourier Transform Infra-red (FTIR) spectroscopy. The sisal fiber FTIR spectrum revealed main absorption bands typical of any lignocellulosic fiber. However, some specific bands as well as bands broadening and intensity suggested particular activities for functional molecular groups in the sisal fiber.IntroductionIn recent decades, environmental issues related to worldwide pollution and climate changes, mainly the global warming, are motivating new paradigms for the development of our society. Among these, the use of natural materials in substitution for non-sustainable synthetic materials, obtained from non-renewable ores and petroleum, is increasingly being considered. In particular, natural fibers extracted from plants are, in this 21st century, experiencing a surge as composite reinforcement [1-11 ], following their replacement by synthetic fibers, specially the glass fiber, during the second half of the 20th century [1-2-8].In addition to environmental benefits [12-13] the lignocellulosic fibers present economical advantages, such as worldwide abundance and comparatively low costs as well as some technical properties associated with flexibility and toughness[ll], which contribute to the performance of automobile components fabricated with natural fibers composites[14-16].Among the less common lignocellulosic fibers that only recently have been investigated[l 7], the fibers extracted from the stem of the sisal plant, shows in Fig 1, reveals a potential for polymer composite reinforcement."

Jan 1, 2013

By M. Vijayalakshmi, S. Saroja, C. Sudha, T. N. Prasanthi

"Ti-5Ta-2Nb alloy and 304L austenitic stainless steel were joined by explosive cladding process. Investigations on 'as received' explosive clad revealed high hardness very near the interface due to martensitic transformation of 304L steel base plate. To improve ductility, explosive clads were heat treated in the temperature range of 823 to 1073 K for 1 to 20 h. Consequent change in the microstructure and microchemistry of the clad interface was studied. No change in the interface microstructure was observed for heat treatment at 823 K. Increase in temperature lead to the formation of various reaction zones at the interface, their number and width increase with temperature and time of thermal exposure. Growth kinetics of the reaction zones was monitored and activation energy required for formation was calculated. From elemental redistribution profiles, effective inter-diffusivities of alloying elements were calculated as a function of concentration and activation energy required for inter-diffusion was evaluated.IntroductionFor engineering components exposed to highly oxidizing and corrosive environments, a titanium based alloy i.e Ti-5Ta-2Nb (Ti-Ta-Nb) is often chosen as a structural material [1,2]. For economic consideration, vessels and piping exposed to non-oxidizing conditions are fabricated from 304L austenitic stainless steel (304L SS). Hence, dissimilar joint of Ti-5Ta-2Nb alloy and austenitic stainless steel becomes unavoidable. Fusion welding processes are not suitable for joining Ti and Fe based alloys due to the propensity for the formation of intermetallic phases and subsequent reduction in the bond strength [3,4]. Hence, explosive cladding, a solid state welding technique, was used to achieve high integrity, corrosion resistant joints between the two alloys."

Jan 1, 2012

By Masaru Imaizumi, Hiroyuki Nomura, Mitsuharu Takita

"Cast iron possesses many superior characteristics caused from precipitated graphite structure, for example, castability, wear resistance, solid lubrication, damping capacity. But the more graphite hyper-eutectic cast iron contains, the lower its mechanical strength becomes, because graphite gives a negative effect to strength of cast iron. In addition, primary graphite tends to segregate during solidification, so uniform materials are difficult to be produced.In this study, authors introduced semi-solid processing in developing new and high quality cast iron. A series of semi-solid processing experiments were carried out to clarify the effect of stirring condition; solidification temperature and etc. on microstructures and characteristics of cast iron. In particular much attention is paid to the appearance of ternary eutectic zone at the final stage of solidification. As the results advanced hyper-eutectic cast iron was obtained with high quality of both the mechanical strength and wear resistance. As for the mechanical strength, 300MPa and 0.60% are obtained as the tensile strength and the elongation values, respectively, under the controlled stirring condition. This indicates that semi-solid processed hyper-eutectic cast iron is used prospectively without spheroidization.IntroductionCast iron has various good properties such as wear resistance, solid lubrication, damping capacity and machinability. The characteristics of cast iron are mainly decided by graphite structure, namely graphite shape and its distribution in the matrix. Mechanical strength of cast iron is large in the case of small quantity of graphite particles which are precipitated uniformly, however, it becomes small in the case of large quantity of graphite precipitated flakily."

Jan 1, 2000

By Seksak Asavavisithchai, Natthida Jareankieathbovorn, Areeya Srichaiyaperk

"Recycling of ADC12 alloy scraps for fabrication of open-cell aluminium foams has been conducted via pressure infiltration method of replication process. The scrap, up to 50 wt.%, was melted with pure aluminium billet, followed by infiltration in a replicated mold of polyethylene foam structure. Compared with the pure aluminium foam, the compressive strength and hardness are higher for the foams with recycled scraps. The increase in foam mechanical properties is due to the presence of Si hard phase in Al matrix. The strength and hardness of the foams also increase with increasing contents of the scraps.IntroductionRecently, open-cell metallic foams have been brought to considerable attention of many industries due to their superior properties; such as large surface area, high specific strength, thermal conductivity, high service temperature and excellent anti-microbial activity, that cannot be found in conventional materials [1, 2]. Typically, open-cell foams are used in functional applications for which a requirement of high strength materials is not demanded. Good examples of such applications include heat exchangers, bone-replacement implants, interconnects, catalyst supports, and sound insulators.Among all types of open-cell metallic foams, aluminium (Al) is the most widely used base metal, due to low material cost, low density, low melting temperature and good corrosion resistance. To improve mechanical properties of Al foam, modification of foam microstructure with addition of alloy elements or ceramic particles is commonly carried out [3, 4]. ADC12 alloy is a typical die-casting Al alloy with high content of silicon (Si) close to the eutectic point in Al-Si binary phase diagram. The alloy is extensively used in the casting industry, due to high wear and corrosion resistance, low coefficient of thermal expansion and excellent castability [5]. The mechanical properties of Al-Si alloy are strongly dependent of Si content."

Jan 1, 2012

By T. Ikeda, M. Maeda, K. Mita

Galvanized steel sheet is the major product for the automobile industry. Therefore, automotive recycling results in zinc-containing scrap that should be remelted in EAFs. Naturally, the EAF dust is a very important source of zinc for zinc recycling processes. The thermodynamic properties of the Fe-Zn intermetallic compounds formed on the surface of galvanized steel sheet should be clarified to make clear the evaporation mechanism of zinc; however, there are few reports on these compounds because of difficulties in their synthesis. There are various intermetallic compounds in the Fe-Zn system. We synthesized them at about 673K. A specimen was examined chemically and X-ray diffraction was applied to ensure the formation of intermetallic compounds. Material containing two phases was placed in a Knudsen type effusion cell and the mass spectrum studied to evaluate the vapor pressure of zinc. The thermodynamic property of intermetallics was then evaluated through measured intensity.

Jan 1, 2000

By Tian Sugui

By means of the long-term aging treated, creep properties measuring and microstructure observation, an investigation has been made into the microstructure and creep behavior of the casting and rolling GH4169 superalloy after long-term aged. Results show that, after the casting and rolling GH4169 superalloy treated by long-term aged, significant amount of " phase are dispersedly precipitated within the grains of the alloy, and some of the NbC, Cr7C3 carbide are distributed along the grain boundaries. In the range of the applied stresses and temperatures, the creep activation energies and stress exponents of LTA GH4169 alloy during steady state creep are calculated to be Q=541.1kJ/mol and n=16.2, respectively. During creep, the deformation mechanism of LTA GH4169 is thought to be the twinning and dislocation slipping within the twinning regions, and the damaging mode of the alloy is the intergranular fracture, and the non-smooth crystal surface is displayed in the fracture regions of the alloy. Thereinto, the carbides film formed along the grain boundaies has a few effect on the strength between the boundaries, which is a main reason of resulting in the alloy possessing a longer creep lifetimes.

Jan 1, 2009

By Hongbo Zhu, Kun Yang, Jingyan Jia, Jinhui Peng, Libo Zhang, Yi Xia

"Titanium dioxide is broadly considered as the most potential useful photocatalytic material. In this work, titanium dioxide was synthetized by microwave solid-state method and characterized by thermogravimetry-differential scanning calorimetry (TG-DSC), X-ray diffraction (XRD) and scanning electron microscopy (SEM). The result demonstrates that through microwave solid-state synthesis, we can obtain uniform size and anatase TiO2 photocatalyst, with the precursor being Ti(C2O4)2·2H2O. And its degradation kinetic parameter of MO can reach to 0.21232.IntroductionSince Fujishima and Honda found the photovoltaic property of titanium dioxide TiO2 [l], it has been widely used in the field of pollutant degradation, virus killer and environment protection [2-5]. Compared to other semiconductors, TiO2 has the advantage of low toxicity/cost, chemical stability, excellent photocatalytic activity, and long lifetime of electron/hole pairs, thus it is considered to be a most potential useful photocatalyst material [ 6]. Solid-state synthesis of oxide nanoparticle is a new method developed in recent years, which not only overcomes the shortcomings of easily aggregation existing in traditional hydrometallurgical process, but also fully demonstrates the unique technologic advantages of without solvents, high yield, easy control, less environmental pollution in solid-state reaction [7-11]. Researches show that the new method of microwave synthesis shows a lot of advantages such as fast reaction rate, efficient, high purity of product, uniform morphology, energy-efficient, and nonpolluting [12-15].In this work, we associated microwave heating and solid-state synthesis to prepare TiO2 photocatalyst material. Its photocatalytic activity was studied in the degradation of MO queous solution. Meanwhile, the formation process as well as the crystal structure and morphology of the synthesized powders were characterized by means of chermogravimetrydifferential scanning calorimetry (TG-DSC), X-ray diffractometry (XRD) and scanning electron microscopy (SEM) techniques."

Jan 1, 2014

By Duck Jae Lee, Kwan Ho Kim, Ji Whan Ahn

"In Korea, reutilization of constructions waste is gaining an increasing attention as generation of construction waste is projected to increase continuously. In current practices, the concrete waste is simply crushed and used as a low application such as paving, back filling, etc. In this study, a new process was developed comprising of heat pretreatment, autogenous milling, and density separation for complete reutilization of concrete waste. Firstly, the concrete waste was crushed using autogenous milling. The coarse size fractions from autogenous milling have a density of 2.5g/cm3 and a water absorption ration 3.0%, which meet the specification of the first class of KS F 2573. The fine size fractions were further separated using a hindered-settling column into two products 1) underflow, 2) overflow. The underflow sample was a high quality fine recycled aggregate which can be used for concrete making, and the overflow sample was an enriched cement material can be also used for CO2 sequestration by mineral carbonation. Introduction Kwan Ho Kim1, Ji Whan Ahn2, Duck Jae Lee1, Hee Chan Cho1 Recently, the importance of resource recycling is gaining a greater attention due to the increasing price of natural resource. Recycling is beneficial for not only the management of waste, but also the reducing of consumption of natural resources and huge energy consumption to treat of natural resource. The construction and demolition waste comprises the major industrial waste generated in Korea. It increased to 54 million tons in 2004, and is projected to increase to over 300 million tons in 2020, as many buildings reach the end of their 30 years life. Among total waste, the proportion of concrete waste was about 30% in Korea. Due to its large volume, recycling of concrete waste is the most important aspect of the waste management. In the current practices, the concrete waste is simply crushed and used as a recycled aggregate. The recycled aggregate has a low quality and most of them are down cycled for usage as paving material, back-filling material, concrete bricks, etc. It cannot be reused for replacement of natural aggregates because cement mortar is not separated perfectly from aggregates. These kinds of recycled aggregates tent to be weaker, more porous and have a higher value of water absorption. When these aggregates are used in concrete making, there are problems of higher total water demand, low compressive strength and durability [1-5]. And recycled fine aggregate is not almost recycled due to its low quality. In this study, a new processing circuit is developed to produce not only highquality recycled coarse aggregates but also fine aggregates and cement material from concrete waste."

Jan 1, 2008

By Shenghui Guo, Ying Lei, Wei Li, Jinhui Peng, Libo Zhang, Yu Li

"Abstract: In this work, low temperature carbothermic reduction of Panzhihua low grade ilmenite after ball milling were investigated. The ball milling of ilmenite and graphite were processed in a ball mill. The milling process can attenuate the particle of ilmenite, and the ilmenite characteristic peak were broadened and weakened. The reduction temperature and behaviors are studied on the thermo gravimetric apparatus; lower temperature and higher reaction rate were obtained for the reduction of ilmenite with graphite after milled. The reduction temperature and times of ilmenite decreased to 1000-1025°C and 40-60min via milled for 4 or 8h; Low down the reduction temperature can eliminate the solution of Mg2+ and FeTi03 in a certain degree; the reduced ilmenite has an obvious loose structure, can favored the subsequent procedure such as leaching.1 IntroductionThere is about 9.66 billion tons of Vanadic Titan-magnetite deposited in Panzhihua, China. In this reserve, there is about 8.73x108 t ofTi02, Accounting for 90.54% of the Chinese reserves, and 35.17% of the international reserves and ranking first in the world. [JJ Titanium mineral deposits major classified into Rock type and Placer type. Rock type is the igneous mineral, which have great content of FeO (Relative to Fe20 3) and gangue. The rock textures are compact and almost are complex ore. Rock type Titanium mineral major are ilmenite and titan magnetite ore, difficult to separate the metal ore and gangue. l.21 Thus, the Ti02 grade of Rock type ilmenite much lower than the Placer type (Table land 11). Panzhihua ilmenite are the typical Rock-type, due to the higher contents of MgO, CaO and Si02 and the complex mineralogy in ilmenite in Panzhihua region, making its direct reduction progressively more difficult. Mechanical activation, usually carried out by energetic milling or ball milling, was reported to significantly decreased the reduction temperature and accelerate the reaction rate of reduction of ilmenite with carbon, silicon and Magnesium. f3·(>J It reported that the process temperature were decreased to 600-1000°C and the annealing time were reduced to 30-120min after milled for 50-400 h. Shorter milling time involved was imported for else procedure such as direct leaching. 171 Hardly any research had referred to the carbothermic reduction reactivity of ilmeite milled for a short time as 1-1 Oh. In the present work, the aim is to investigate the reactivity and reaction temperature of carbothermic reduction of Panzhihua ilmenite. The Phase composition and micro morphology of samples are characterized."

Jan 1, 2011

By J. -S. Park, H. -S. Jeon

This study has been carried out to develop a relatively simple hydrometallurgical process for recovering nickel as nickel sulfate from the spent nickel-cadmium battery residue in which cadmium was removed by vacuum distillation. This residue is composed of 36 % nickel, 20 % iron, and other metals such as cobalt. First, crushing and selective classification were performed to separate iron to produce a nickel-rich product (over 40 % nickel). This product was dissolved in sulfuric acid to obtain a nickel sulfate solution. During the dissolution, nitric acid and air were added to the system to enhance the iron oxidation reaction rate. The free acid remaining in the dissolved solution was neutralized by adding nickel carbonate. Iron was precipitated as iron hydroxide and removed from the solution. The nickel sulfate solution was then fed to a vacuum evaporator to concentrate the solution by evaporation of water and crystallized at around 45°C to obtain nickel sulfate hexahydrate. A recrystallization process could remove other impurities such as zinc and manganese.

Jan 1, 2000

By Norihiro Murayarna

Hydrothermal synthesis of K type zeolite was carried out by using coal fly ash as a raw material and KOH as an alkali source. The change in various physical properties of the obtained zeolite, such as the kind of zeolite crystal, cation exchange capacity, surface structure of zeolite and particle size distribution were investigated through the overall reaction of zeolitization. The reaction mechanism of K type zeolite from coal fly ash was investigated from these results in this study

Jan 1, 2002

By Rodney T. Jones

DC arc furnaces were first used industrially for the reductive smelting of chromite fines to produce ferrochromium thirty years ago. Since then, they have been used for a variety of applications, including the smelting of ilmenite to produce titania slag and pig iron, the recovery of cobalt from non-ferrous smelter slags, and the smelting of nickel laterite ores to produce ferronickel. The power of these furnaces has increased from 12 MW to 72 MW for ferrochromium, and to 80 MW for ferronickel. The largest of these furnaces requires two electrodes to carry sufficient current to generate this much power. A review is presented of various DC arc furnaces in use, along with a discussion of the likely ways in which furnace power might be increased further in the future.

Jan 1, 2014

By Jinfu Xu, Youqing Cao, Yuting Lv, Hang You, Peng Jiang

"In present work, we reported the fabrication of composites consisted of M42 powder metallurgy high speed steel and 45 steel at one step via spark plasma sintering (SPS) technology. The interface microstructure, compositions and microhardness with the interface forming mechanism were investigated. The results show that the morphology and microhardness within the M42/45 steel interfaces exhibit a gradient distribution. The interfaces possessed a transition layer up to 10.2 ?m with few distortions and microcracks. The formation of M42/45 steel interfaces were driven by both fusion and diffusion processes. The former one was primary at the early sintering process, while the later one becomes dominant over the followed sintering process.IntroductionPowder high-speed steels have been widely used in cutting tools, cold-hot tools and dies, as well as in cut materials and structure parts with wear resistance and high-temperature resistance, due to its high hardness, good wear resistance, desirable cutting toughness and favorable hot hardness [1-2]. For materials of some parts in practical production, not only the favorable toughness is required to resist the impact action, but also the high hardness and exceptional wear resistance are demanded. According to the functional requirements and working conditions, bimetal composite materials are prepared in a certain mode, proportion and distribution, by designing two metals with different chemical and physical properties [3-6]. Considering the composites exhibit different properties in different positions of the parts with a combination of the advantages of two metals, they can obtain enhanced properties that the single one can not achieve."

Jan 1, 2012

By I. C. Howard, E. J. Palmiere

"Heat transfer and friction in hot flat rolling have traditionally been characterised by an average heat transfer coefficient (h) and an average friction coefficient (p.). However, the presence of oxide scales and asperities at the interface question the use of such averages. The apparent irregularity and lack of pattern of interactions at the interface has prompted this present investigation to move away from averaged h and 11 values, and to study their local evolution based on probabilistic rules. The approach is based on the probability of finding the workpiece surface in a specific configuration at a particular instance of time in the roll gap. These rules are based on observations of surface phenomena such as scale behaviour during hot rolling. The model is implemented using user-subroutines integrated with the commercially available finite element program ABAQUS™. The results show the strong dependence of h and u on the local scale interactions. In particular, the effect of scale thickness, material behaviour and processing conditions on the evolution of hand 11 are discussed. Finally, the development of a Cellular Automata based Finite Element (CAFE) model is proposed to model the combined interfacial phenomenon of friction and heat transfer at the tool-work piece interface.IntroductionIntricate interactions between process variables in hot rolling of steels make it a challenge to the modelling community. For a given material and geometry combination, reducing interfacial power losses can increase the efficiency of the rolling process. The roll-strip interface, therefore, forms the critical zone and is currently the domain of intense investigation, especially to characterize interfacial frictionl • 2 and heat transfer3 • 4 . These interfacial phenomena are inter-related and cannot be studied in isolation. However, very few mathematical models4 • 5 combine an analysis of friction and heat transfer and deformation of the strip-roll interface taking into account the role of asperities and oxide scales."

Jan 1, 2001

By Hong N. Vu, Jitka Jandova

"Gypsum and limestone methods were examined in this study to process zinnwaldite wastes originating from dressing Sn-W ores mined in the Czech Republic. These wastes containing 0.20-0.30% Li and 0.10-0.20% Rb were subjected to magnetic separation to obtain a zinnwaldite concentrate with 1.36% Li and 0.94% Rb. It was observed that processing of the zinnwaldite concentrate with gypsum resulted in almost 96% recovery of Li into aqueous liquors, whilst rubidium extraction was only 25%. At the same time, it is possible to extract almost 92% Li and Rb from the identical zinnwaldite concentrate if the concentrate is processed by limestone method. Lithium carbonate, a final product of both methods was recovered from the refined sulphate solution using K2CO3 as a precipitation agent and/or from unrefined hydroxide solution using gaseous CO2. In the continuation of this study, rubidium will be separated from carbonate solutions after Li2CO3 precipitation as RbAl(SO4)2, an intermediate for Rb2CO3 production. IntroductionLithium is used as an alloying constituent in lightweight alloys, as a heat transfer medium in nuclear reactors and as a component in primary and secondary batteries. With the development of a new generation of electric vehicles, the lithium demand will dramatically grow. Lithium chemicals find extensive application in many industrial branches such as metallurgical, glass, ceramic and pharmaceutical industries. Rubidium compounds are predominantly used in psychiatry and medicine, in magneto-optic modulators, solid-state lasers, phosphors and components of electrolytes for fuel cells. The four most important lithium minerals are amblygonite, spodumene, petalite, and lepidolite. Spodumene LiAlSi2O6 (6.0-7.5% Li2O) and petalite LiAlSi4O10 (3.5-4.5% Li2O) belong to aluminosilcate minerals. Lepidolite (Li.Al)3(Al.Si)4O10(F.OH)2 (3.30-7.74% Li2O), lithium mica, is the most important representative of the mica minerals, a subgroup of the aluminosilicates. It frequently contains 3–5% Rb2O and eventually caesium. Zinnwaldite, which has the general formula K(Li.Al.Fe)3(Al.Si)4O10(F.OH)2 (2-5% Li2O), is regarded as a variety of lepidolite with a high iron content. Commercial amblygonite is a complex phosphate (Li.Na)Al(F.OH)PO4 (up to 9.88% Li2O), however, its deposits have not been commercially exploited because of their small size. Natural brines with a high lithium chloride content are important in the industrial production of lithium [l]"

Jan 1, 2008