By Veronica Escobar

This paper presents results from a two month pilot evaluation of EMEW® technology at CODELCO Radomiro Tomic, in Chile. A prime focus in the test programme was to assess the technology?s capabilities to recover high quality copper from the Radomiro Tomic electrowinning tank house bleed stream. The EMEW® cell developed by Electrometals Technologies Ltd. tolerates substantially higher levels of contaminants than those found in conventional tankhouse, operating at high current densities while maintaining high cathode copper quality all the way down to low copper concentrations. To maintain high copper purity in a copper electrowinning (or electro-refining) tank house, a continuous bleed of solution must be taken from the tank house inventory to prevent build-up of contaminants, and resulting degradation in cathode quality. In an SX-EW operation, this bleed stream is normally recycled back to the solvent extraction circuit, but is occasionally sent to the raffinate pond to re-enter the leach circuit. Return of the bleed stream to the solvent extraction circuit creates a continually recycling load of copper in solution, which may reduce overall plant capacity and expansion potential. Return to the leach circuit has a similar effect, and methods to reduce its impact are always under consideration. The use of the EMEW® technology allows for direct and efficient recovery of near 100% of the contained copper instead of recycling. Tests were run at ambient temperature on bleed electrolyte using current densities which varied between 250 and 1100 amps per square meter, with copper concentrations between 38 and 1 g/l. A profile of maximum allowable current density with respect to concentration was developed, showing that high grade copper can be obtained at all levels of concentrations tested, by choosing an appropriate current density and electrolyte flow rate. The results of this programme show that the recirculating bleed electrolyte from an SX-EW operation can be converted into an expansion in copper production at a comparatively low investment cost.

Jan 1, 2003

By Yukihito Sasaki

Sumitomo Metal Mining Co. Ltd. planned an expansion program for the Toyo smelter and refinery in order to increase the production capacity of electrolytic copper to 450,000 tpy in 2007. Regarding the flash smelting furnace, a drastic increase in the average concentrate smelting capacity from 2,300 tpd to 3,950 tpd was required to achieve the plan. It was necessary to examine the performance of the Sumitomo concentrate burner when the feed rate was considerably increased. The authors developed a mathematical model to describe the combustion phenomena in the Toyo flash smelting furnace. This model was developed incorporating the fluid flow, heat and mass transfer, and chemical reactions of the copper concentrate and ancillary fuel. The copper concentrate was considered to mainly comprise chalcopyrite (CuFeS2). The reaction of CuFeS2 was assumed to consist of two steps, namely, the decomposition of CuFeS2 and the oxidation of the resulting pyrrhotite (FeS) and sulfur (S). The combustion phenomena in the furnace at the increased feed rate were predicted using this model. It was found that the Sumitomo burner was capable of enhancing the smelting capacity. This is attributed to the wide dispersion of the concentrate particles caused by an increase in the particle mass and a long residence time in the reaction shaft; this is due to the low temperature of the reaction air. However nonuniformity of the reaction in the reaction shaft was enhanced with the increased feed rate. In order to improve the nonuniformity of the reaction, an increase in oil-burner oxygen and an enlargement of the diameter of the dispersing cone were useful. By combining the expertise of the Toyo smelter staff and the calculation results, the concentrate smelting capacity of the Toyo smelter has been stably increased to 3,600 tpd thus far, and further improvements of the smelting performance are still being carried out.

Jan 1, 2006

By Józef Czernecki

Chalcocite-bornite concentrates of KGHM contain, similarly to chalcopyrite concentrates, 20-30 wt.% Cu but several times less iron (2-7 wt.%) and sulphur (9-12 wt.%). Another useful characteristic of KGHM concentrates is the presence of organic carbon (5.5-8.5 wt.%) in them, which serves as fuel in the flash smelting process. The main contaminants of the concentrates are lead (1.3-2.5 wt.%) and arsenic (0.05-0.4 wt.%) which require appropriate technological treatment in order to remove them from the copper pro-duct. Chalcocite-bornite concentrates are processed in KGHM by two different processes: ? a flash smelting process (Glogow 2 Smelter) ? a shaft smelting process (Glogow 1 Smelter, Legnica Smelter) The shaft smelting process used in the Glogow 1 Smelter and in the Legnica Smelter has higher production costs than the flash smelting process of HM Glogow 2. Additionally, the shaft smelting process employs several concurrently running installations (six dryers, seven briquetting lines, six shaft furnaces, nine converters), the operation of which, including maintenance, requires significant financial expenditure. Therefore, the Company is currently considering the substitution of the shaft furnace process in the Glogow 1 Smelter and in the Legnica Smelter by the one stage flash smelting process located in the Glogow Smelter, with output equaling the copper production capacity of both smelters, i.e. 320 000 ? 350 000 t/a. There are two technological options being considered which differ from each other in their man-ner of flash slag cleaning. In the first, the slag cleaning would be the same as in the existing Glogow 2 Smelter, i.e. the slag would be cleaned by pyrometallurgical reduction of the oxide copper and other metal compounds in the electric furnace in order to produce waste slag containing below 0.6 wt.% Cu. However, the other option of the flash slag cleaning would be carried out in two stages. After preliminary slag reduction in the electric furnace to 3-5 wt.% Cu, there would be flotation of the partially reduced slag.

Jan 1, 2006

By Tabbetha A. Dobbins

We report studies concerning the time frame for catalytic reactions between NaAlH4 (sodium alanate) and TiCl3 during high energy milling. Spectral features in x-ray absorption spectra were analyzed for samples milled for various times (0 minutes, 1 minute, 5 minutes, 25 minutes, and 125 minutes). A structural transition from Ti3+ to Ti0 is observed within the first 5 minutes of milling. The Ti0 structure persists for samples milled for times longer than 5 minutes?even after those samples underwent a subsequent single hydrogen desorption/absorption cycle. Samples milled for less than 5 minutes retain Ti3+. For samples milled for 1 minute, the Ti-K edge position shifts from Ti3+ to Ti0 after a single desorption/absorption cycle. However, the first coordination sphere around the Ti0 absorber occurs at longer distances for 1 minute milled sample. These results hint at the formation of Ti0 pure metallic clusters upon desorption/adsorption cycling of 1 minute milled sample. Previously reported x-ray absorption spectroscopy studies have demonstrated the structural transition from Ti3+ (in TiCl3) to Ti0(determined to be TiAl3 found at the surface of the alanate powder). Aluminum deficiency on the NaAlH4 lattice is responsible for controlling hydrogen absorption capacity. These time-resolved spectroscopy studies suggest the possibility for controlling aluminum deficiency, while still maintaining titanium activation of the alanate powder, by manipulating the coordination environment of the titanium dopant during the first five minutes of high energy milling. Specifically, a possible approach to mitigating aluminum deficiency during doping would be to introduce an alternative species to which the to Ti3+ catalyst would form a metallic bond after the TiCl3 has attached at the surface of the sodium alanate powder and before the Ti3+ forms the TiAl3 intermetallic species.

Jan 1, 2006

By Wen-Ming Chien, Vamsi Krishna Kamisetty, Amrita Mishra, Ivan Gantan, Prathyusha Mekala, Dhanesh Chandra

"The phase equilibrium and characterization studies by using high temperature X-ray diffraction (XRD) and differential scanning calorimetric (DSC) methods have been performed for binary organic thermal energy storage materials. The organic thermal energy storage materials undergo a solid-solid state phase transition before melting which stores large amounts of thermal energy. Two materials [tris(hydroxymethyl)aminomethane(TRIS) and 2-Amino-2-methyl-l, 3- propanediol(AMPL)] were used for this study. Binary samples of AMPL-TRIS were prepared to perform high temperature XRD characterization and DSC studies and the binary AMPL-TRIS phase diagram was developed. The high temperature solid-state phases of AMPL and TRIS were characterized as a disordered BCC structure. It was found there is virtually no solubility of TRIS in AMPL or vice versa below -75 °C. The maximum solubility of TRIS in AMPL is 11% TRIS at 75 °C. The eutectoid transformation was shown at 19%TRIS-81%AMPL composition and at a temperature of 75°C. Lattice expansion calculations on single phase of TRIS and AMPL have been performed.IntroductionThermal energy storage materials can store a large amount of heat due to the presence of thermal transitions from the orientationally ordered to disordered phases occurring before melting. These molecules (such as amine and alcohol derivatives of neopentane) can reorient as a whole about the central carbon atom to form orientationally disordered crystals (ODIC) and their spherical shape makes them reorient relatively easier. Thermal energy storage materials are becoming increasingly important as a renewable energy resource. These molecules undergo large changes in enthalpies at solid-solid transitions. The presence of these compounds with large enthalpy changes are identified as potential thermal energy materials and some of die applications are solar cell systems [1-3]. Binary mixtures have been found as a way to adjust the transition properties in addition to pure compounds [4]. Tris(hydroxyrnethyl)aminomethane (TRIS, C(CH2OH)3NH2) and AMPL, CH3C(CH2OH)2NH2) are two important thermal energy storage materials."

Jan 1, 2012

By Donato Firrao, Giorgio Scavino, Paolo Matteis

"The fatigue behavior of two high-strength sheet steels used to produce car bodies, a dual-phase steel and a TWIP one, both with ultimate tensile strength close to 1 GPa, is investigated.Unnotched tensile specimens are fatigue tested at room temperature with constant load amplitude and zero load ratio, in order to determine their 1 million cycles fatigue limit, both in the asfabricated sheet condition and after the resistance spot welding of one small homologous sheet square onto the calibrated length of the tensile specimen. Moreover, pre-cracked compact tension specimens are tested with load ratio 0.1 to determine the Paris fatigue crack growth curve.The fatigue results are completed with crystallographic, microstructural, tensile, and fractographic examinations, and the influence of the microstructure and of the welding processes is discussed.IntroductionCar bodies are increasingly made with high-strength weldable steels, in order to reduce vehicles' weight (to save fuel and reduce air pollution) and to improve the vehicle occupant safety in case of car crash. The main mechanical requirements of these steels in service are fracture strength and energy absorption, relevant for crashes, as well as fatigue endurance, relevant for ordinary car usage. [1]Steel sheets for car-body applications are usually made by continuous casting, hot rolling, cold rolling, continuous annealing (or other continuous heat treatment), and protective coating (in some cases). The sheets are then cold formed (deep drawn) to produce car body parts. Finally, the car bodies are built by assembling several deep-drawn parts, often consisting of different steels, usually through the Resistance Spot Welding (RSW) process, whereby two or three overlapping sheets are welded by local Joule-effect heating [2].Dual-Phase (DP) steels are widely used, low alloy steels with a microstructure consisting of ferrite and martensite, obtained from a final heat treatment which consists of heating at an intercritical temperature and then quenching. [3,4]"

Jan 1, 2012

By Shadia J. Ikhmayies

"Nanocrystalline fluorine-doped tin oxide, SnO2:F, thin films were prepared by the spray pyrolysis (SP) technique on glass substrates. The films were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), X-ray dispersive spectroscopy EDAX and transmittance measurements. X-ray diffraction patterns revealed the nanocrystalline nature of the films where the grain size was estimated based on the Sherrer formula. SEM micrographs showed that the films are uniform and totally covered with the material and they confirmed the nanocrystalline nature of the films. The absorbance was deduced from the transmittance measurements, and its first derivative was used to estimate the optical bandgap energy. Bandgaps larger than the bandgap of the bulk SnO2iF were obtained, indicating the presence of quantum dots. The hyperbolic band model was used to estimate the radii of the nanocrystallites. A comparison between the results of the different methods was performed.IntroductionTin oxide, SnO2, thin films are n-type semiconducting, transparent materials, which have numerous important applications in optical-electronic device technology. The optical transparency of SnO2, together with its chemical and mechanical stability, makes SnO2 films suitable for many other applications, such as transparent conductive coatings, gas sensors and heteroj unction solar cells [1]. In particular, SnO2 thin films have drawn much interest because of their potential application and integration with microsensor devices. Considerable attention has recently been focused on the development of solid state gas sensors based on thin films with a crystallite size smaller than the Debye length of the material, which show increased gas sensitivity and short response times [2]. In many of these applications, a doped SnO2 film is used as an active layer. Among the various dopants, fluorine is often preferred, because fluorine doping results in films with high transparency and good conductivity [1]."

Jan 1, 2012

By Selvin Yesilay, Guray Kaya, Bekir Karasu, Asli Cakir

"In this investigation, the wastes of Eti Maden Kirka Boron Company of Turkiye were evaluated in the production of diopside and anorthite-based glass-ceramic glazes suitable for porcelain tiles fast and single-fired under industrial conditions. First of all, high wear resistant frits were produced with the use of concentrator and derivative borax wastes. Second of all, pre-engobed porcelain tile bodies were coated with the standard and newly produced frit-based glazes and industrial fast single-firing was employed. Final products were undergone to the certain standard tests to determine their Vickers hardness, wear resistance, thermal expansion coefficient values, gloss and coloring parameters. The micro-structures and phase formations of the fired glazes were also studied. Consequently, it was confirmed that the utilization of borax solid wastes in fast single-fired porcelain tile glass-ceramic glazes is possible. Introduction Porcelain tiles were introduced at the end of 1980s by Friandre, one of the leading Italian porcelain manufacturers. The American National Standard Specifications for Ceramic Tile defines porcelain tiles as: dense, smooth, impervious (with water absorption value less than 0.5 %) and stain resistant [1]. The excellent technical performances for ceramic tiles, such as mechanical, wear, frost and chemical resistance that make their use possible in indoor and outdoor building applications [2-3]. In the last decade, the growth rate of the global production of porcelain tiles increased more than those of other ceramic products; in fact, the technical properties of porcelain tile, coupled with even more improved aesthetic appearance, gave it a prominent role on the tile market [2]. Glass-ceramics are composed materials of one or more crystalline phases immersed in a residual glassy phase [4-5]. Glass-ceramic technology is based on controlled nucleation and crystallization of bulk glass [6]. The concepts of controlled crystallization of glass designate the separation of a crystalline phase from the parent glass in the form of tiny crystals. Their growth rate and final size are controlled by a suitable heat treatment [7]."

Jan 1, 2008

By M. Tangstad, H. Mølnäs, J. D. Steenkamp

"Temperature affects several aspects of pyrometallurgical systems, including thermodynamics and reaction kinetics. Reliability of temperature measurements in laboratory and plant applications is thus important from process, safety and financial perspectives. This case study briefly introduces different techniques utilized for temperature validation, and demonstrates temperature validation on laboratory scale utilizing the wire-bridge method. Pt/Ptl3Rh thermocouple hot junctions were constructed by mechanically connecting thermocouple wires through a pure metal bridge consisting of copper, gold, nickel or palladium wire. When heating the wire-bridge thermocouple alongside a regular Pt/Ptl3Rh thermocouple, temperature offsets were quantified as the wirebridge thermocouple short-circuited at the melting points of the pure metals. At the melting points of gold (1064°C) and palladium (1555°C), average measured temperature offsets were -2.1°C ± 2.3°C and 0.2°C ± 0.4°C, respectively. Results from the copper and nickel wire-bridges were inconclusive. The paper concludes with a discussion on the potential industrial applications of the technique.IntroductionThermocouples are probably the simplest of all temperature sensors, but are widely utilized due to simplicity, versatility and ability to handle a variety of experimental conditions and industrial applications. Additionally, thermocouples are often the only option in research laboratories requiring high temperature measurements, and a high level of reliability is usually required from thermodynamic, kinetic as well as safety points of view.The study presented here originated from a test program where the compatibility between different types of carbon-based refractory materials and industrial slag produced in silicomanganese furnaces were investigated on a laboratory scale utilizing the static crucible test[l]. Due to the nature of the silicomanganese production process, the compatibility tests were to be conducted at 1600CC[2]. Details of the experimental set-up utilized for the compatibility tests are discussed in the Experimental Set-up and Method Statement section later in this paper."

Jan 1, 2012

By S. A. Shuey

The present industrial practice used to separate aqueous cobalt from nickel is multistage solvent extraction processing. This paper describes a different but simpler treatment technology. The proposed technology has been applied to cobalt/nickel hydroxide intermediate solids produced from the treatment of Electrochemical Machining (ECM) waste sludge, The process consists of dissolving the cobalt/nickel hydroxides in basic cyanide solutions. Cobalt and nickel form aqueous .solution metal cyanide complexes. Nickel can be selectively precipitated from the solution as a nickellic hydroxide solid. Cobalt can be recovered from the leach solution by precipitation of a cobaltous/cobaltic cyanide double salt. The double salt product can then be subsequently treated to produce an appropriate cobalt product. The process chemistry, proposed fiowsheet and preliminary reagent costs are presented and discussed.

Jan 1, 1998

By I. D. Reznik

Results of thermodynamic computations have been presented for reactions occurring in the process of segregation roasting of oxide nickel ores to describe more accurately the mechanism of the process. Under conditions of laboratory-scale roasting in combination with close-circuit flotation flow-sheets and magnetic separation, a recovery of 80-82% of nickel into 8 to 10% Ni concentrate and a recovery of up to 66% of cobalt was achieved. Process conditions have been selected for processing of both high-iron and high-magnesium ores. The feasibility of conversion of 94-98% of nickel and cobalt into solution by oxidizing pressure leaching with sulfuric acid has been demonstrated. It has been substantiated that it is reasonable to introduce double-stage segregation roasting.

Jan 1, 2003

By Antonio Huerta

The effects of potassium ethyl xanthate collector and potassium dichromate used as a depressor on a PbS mineral were studied by high frequency impedance technique. Measurements of complex permittivity, at 100 MHz suggested that is possible to obtain from isotherm adsorption the adequate industrial collector concentration being this in the range of lE-3 to 5E-3M of KEX. The e' values (320-420) in the PbS-KEX system was increased as the KEX concentration was lowered). In the other hand the PbS- K2Cr2O7 system showed higher values of e' (420-510) as the K2Cr2O7 concentration was increased. The PbS-KEX-K2Cr2O7 system was evaluated.

Jan 1, 1997

By Fumito Tanaka

The Mitsubishi Process is the sole pyrometallurgical process for the continuous production of blister copper from copper concentrates. Continuous converting originates from the application of the proven technology of a lime-ferrite slag (CaO-FeOX-Cu2O) on the Converting Furnace (C-furnace). Recent improvements on the C-furnace operation have included increasing the processing of recycled materials and the investigation of alternative fluxing agents. However, some minor oxides adversely affect C-furnace operation, with respect to magnetite behavior of the slag, with the most significant impact having been observed with the silica content of the slag. This paper will quantify the impact of silica on the lime-based slag, and discusses the controls that have been identified to sustain continuous converting operation.

Jan 1, 2005

By Ronald J. McGregor

An overview or precious metals project development and start-up, which emphasizes the process decision. Logic which determines process flowsheet, project economics, and training required to train new operators for start-up. The process decision required to successfully develop a precious metals project requires a blending of test data, environmental considerations and operations experience. Decisions to use Merrill-Crowe or carbon adsorption/ electrowinning/replating, fixed pad or multi-use pad {in heap leach) are dependent not only on technology but also on ability to train new operators. The market for experienced operators is acutely depleted and almost all new operators will have to be "home grown". Experience from the Brewer project in South Carolina as well as other projects put together in the West will be discussed.

Jan 1, 1989

By R. Gordon Bloomquist

The economic benefits of the co-production of minerals from geothermal brines far exceeds the potential revenue stream from the sale of marketable by-products such as silica, zinc, manganese, lithium and a number of rare earths. Extraction of silica can avoid scaling problems often associated with many geothermal power projects and may allow for additional power production through the use of bottoming cycles or the use of the brine in direct use applications now impractical due to scaling problems. An additional benefit of silica removal is the opportunity to use the geothermal brine as a source of water for enhanced evaporative cooling ? a technique that can significantly improve the summer power output from binary power plants employing air cooling for condensing the working fluid.

Jan 1, 2006

By R. Cheng

The kinetics of the solvent extraction of ythium from HCl solution with mono-2-ethyl hexyl phosphonic acid mono-2-ethyl hexyl ester (HEHEHP) have been studied using a rotating diffusion cell (RDC). The effects of rotation speed, pH, ymium and extractant concentrations and temperature on the rate of extraction were examined. The rate of extraction of ythium appears to be controlled by an interfacial reaction of metal ion and extractant. The concentration of the latter is determined mainly by diffusion through the membrane. The contributions of the rates of diffusion in the diffusion layer, diffusion in the membrane and chemical reaction at the interface to the overall rate have been calculated on the basis of a kinetic model.

Jan 1, 1992

By V. L. Stolyarova

The high-temperature Knudsen effusion method was used to study partial pressures of vapour species, activities of components and the Gibbs free energies in the DyF3-Dy2O3 system at the temperature (1357±5) K. Partial pressures of vapour species were obtained by the ion current comparison method, with the DyF3 partial vapour pressure over pure DyF3 as a standard. The equilibrium constant of the gaseous reaction DyF3 + DyOF = Dy2OF4 is evaluated. Thermodynamic data obtained are in a agreement with the available phase diagram of the DyF3-Dy2O3 system. Results of the present study illustrate the negative deviations from the ideal behaviour in the system.

Jan 1, 1997

By Takao Mori

Novel rare earth boron icosahedral compounds are investigated as potential high temperature thermoelectric materials. REB50-type compounds and REB22C2N compounds were synthesized and the thermoelectric properties measured. Seebeck coefficients in excess of 200 V/K are observed at temperatures above 1000 K for the REB50-type compounds. Strikingly, n-type behavior was observed for REB22C2N. Up to now, non-doped B12 icosahedral compounds have all been p-type. The discovery of an n-type compound is extremely important in terms of the potential development of this class of compounds as viable thermoelectric materials. Low thermal conductivities of < 0.03 W/cm/K at room temperature was observed for these rare earth boron cluster compounds.

Jan 1, 2006

By J. W. Matousek

Copper losses in smelter slags are :typically normalized with some form of the distribution coefficient, written as the ratio of the weight percent assays of metal in slag to the metal in matte or its inverse: L(s/m) = %(Cu)/%[Cu] or L(m/s) = %[Cu]/%(Cu) However, this simple approach ignores the dynamics of the smelting process. It overlooks the effect of the chemical work done in producing a given matte grade from concentrates of different grades -- or from a single concentrate blended with varying quantities of copper bearing precipitates or reverts. This paper examines the combined influences of matte grade and the work done in smelting on the copper content of smelting furnace slags. A simple model for the relationship is proposed.

Jan 1, 1999

By Ying-Chu Hoh

The extraction of cerium(IV) by valence change with two-phase electrolysis was studied experimentally. The results show that the electro-oxidation extraction depends mainly on the distribution of the solute between the two phases, the reaction on the electrode surface and the diffusion of the reactant and product between the electrode and aqueous interphases. The effects of various parameters on cerium extraction were also studied. The selected parameters were background current, catholyte acidity, agitation speed, operation current and voltage and surfactant addition. The electro-oxidation extraction mechanism can be divided into eight steps. In addition, Wee the rate of extraction is quite fast, the percentage extraction Ce+4 can be taken as an index to show the conversion rate of Ce+3 J to Ce+4.

Jan 1, 1989